JPH03186309A - Air filter - Google Patents
Air filterInfo
- Publication number
- JPH03186309A JPH03186309A JP1324723A JP32472389A JPH03186309A JP H03186309 A JPH03186309 A JP H03186309A JP 1324723 A JP1324723 A JP 1324723A JP 32472389 A JP32472389 A JP 32472389A JP H03186309 A JPH03186309 A JP H03186309A
- Authority
- JP
- Japan
- Prior art keywords
- zeolite
- antibacterial
- filter layer
- air
- filter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、空気を殺菌するエアーフィルター及び空気の
殺菌清浄化方法に関する。DETAILED DESCRIPTION OF THE INVENTION [Field of Industrial Application] The present invention relates to an air filter that sterilizes air and a method for sterilizing and purifying air.
本発明のエアーフィルターは、空気殺菌の持続性に優れ
ている。さらに、本発明の空気の殺菌清浄化方法によれ
ば、長時間安定して空気を殺菌清浄化することができる
。The air filter of the present invention has excellent sustainability in air sterilization. Furthermore, according to the air sterilization and purification method of the present invention, air can be stably sterilized and purified for a long period of time.
エアーコンディショナーのフィルタ一部及び空気供給部
は、温湿度が微生物の繁殖に適した状態になることが多
く、細菌、カビ等が発生、増殖する。細菌等の繁殖は、
感染症や悪臭の原因となり、衛生上、これらを殺菌除去
する必要がある。The temperature and humidity of a part of the filter and the air supply section of an air conditioner are often in a state suitable for the growth of microorganisms, and bacteria, mold, etc. occur and multiply. The proliferation of bacteria, etc.
These can cause infections and bad odors, and for hygiene reasons, it is necessary to sterilize and remove them.
また、近年バイオテクノロジー分野、半導体、精密機器
、薬品等の製造分野で広く使用されているクリーンルー
ムに設置されている空調装置では特に優れた殺菌除去法
が必要とされている。Furthermore, in recent years, air conditioners installed in clean rooms, which are widely used in the biotechnology field, semiconductor, precision equipment, pharmaceutical manufacturing fields, etc., require particularly excellent sterilization and removal methods.
空調装置は、定期的に運転を停止し、清掃、ホルマリン
燻蒸、オゾンガス殺菌または紫外線照射して殺菌除去す
るのが一般的である。しかし、この方法では手間が掛か
る。Generally, air conditioners are shut down periodically and sterilized by cleaning, formalin fumigation, ozone gas sterilization, or ultraviolet irradiation. However, this method is time-consuming.
そこで、人体に対して安全性が高い銀ゼオライトをエア
ーフィルターに含めることが提案されている〔特開昭５
９−６６３２１号、特開昭６１−１３７５６４号〕。銀
ゼオライトを含むエアーフィルターを用いれば、−々運
転を停止する必要はない。Therefore, it has been proposed to include silver zeolite, which is highly safe for the human body, in air filters.
No. 9-66321, JP-A-61-137564]. If an air filter containing silver zeolite is used, there is no need to stop operation.
ところが、本発明者らの検討により、単に従来のエアー
フィルターに銀ゼオライトを含めただけでは、運転中に
銀ゼオライト表面に塵、ゴミ等が徐々に付着して、遂に
は抗菌力が失効してしまうことが明らかになった。However, the inventors' studies have revealed that if silver zeolite is simply included in a conventional air filter, dust, dirt, etc. will gradually adhere to the surface of the silver zeolite during operation, and the antibacterial activity will eventually lapse. It became clear that it would go away.
そこで本発明の目的は、銀ゼオライト等の抗菌性ゼオラ
イトを用いたエアーフィルターの抗菌力の持続性を向上
させる方法及び抗菌力の持続性を向上させたエアーフィ
ルターを提供することにある。Therefore, an object of the present invention is to provide a method for improving the sustainability of the antibacterial activity of an air filter using antibacterial zeolite such as silver zeolite, and an air filter with improved sustainability of the antibacterial activity.
本発明は、抗菌性ゼオライトを含有するフィルター層の
一方または両方の面に静電気帯電フィルター層を有する
エアーフィルター及び静電気帯電フィルター層を通過し
た空気を抗菌性ゼオライトを含有するフィルター層に導
入する空気の殺菌清浄化方法に関する。The present invention provides an air filter having an electrostatically charged filter layer on one or both sides of the filter layer containing antibacterial zeolite, and an air filter that introduces the air that has passed through the electrostatically charged filter layer into the filter layer containing the antibacterial zeolite. Concerning sterilization and cleaning methods.
以下本発明について詳細に説明する。The present invention will be explained in detail below.
本発明に用いる抗菌性ゼオライトを含有するフィルター
層とは、抗菌性ゼオライトを含有する通気性シートであ
る。本発明において通気性シートとは、圧損が１ｗｕｉ
ＨｔＯ以下、好ましくは０．８ ｗ ＨｔＯ以下である
シートを言う。通気性シートとしては、例えば不織布を
挙げることができ、本発明の抗菌性ゼオライトを含有す
るフィルター層として、抗菌性ゼオライトを含有する不
織布を例示することができる。通気性シートのその他の
例として、織物等を挙げることができる。通気性シート
を構成する材料としては、樹脂が一般的であり、ポリエ
チレン、ポリプロピレン、ポリエステル、ポリカーボネ
ート、ポリアミド、アクリル樹脂、アセテート樹脂、ポ
リビニルアルコール系樹脂等を挙げることができる。The filter layer containing antibacterial zeolite used in the present invention is a breathable sheet containing antibacterial zeolite. In the present invention, a breathable sheet has a pressure loss of 1 wui.
Refers to a sheet that is below HtO, preferably below 0.8 w HtO. Examples of breathable sheets include nonwoven fabrics, and examples of the filter layer containing antibacterial zeolites of the present invention include nonwoven fabrics containing antibacterial zeolites. Other examples of breathable sheets include woven fabrics and the like. The material constituting the breathable sheet is generally a resin, and examples thereof include polyethylene, polypropylene, polyester, polycarbonate, polyamide, acrylic resin, acetate resin, polyvinyl alcohol resin, and the like.
抗菌性ゼオライトは、結晶性アルミノケイ酸塩であるゼ
オライトのイオン交換可能なイオンの一部または全部を
銀、銅、亜鉛、水銀、錫、クロム、カドミウム等の抗菌
性金属イオンで置換したものである。Antibacterial zeolite is made by replacing some or all of the ion-exchangeable ions of zeolite, which is a crystalline aluminosilicate, with antibacterial metal ions such as silver, copper, zinc, mercury, tin, chromium, and cadmium. .
本発明において「ゼオライト」としては、天然ゼオライ
ト及び合成ゼオライトのいずれも用いることができる。In the present invention, as the "zeolite", both natural zeolite and synthetic zeolite can be used.
ゼオライトは、一般に三次元骨格構造を有するアルミノ
シリケートであり、一般式としてＸＭ２／□０・Ａ１．
Ｏ，・ＹＳｉＯ□・ＺＨ，０で表示される。Zeolite is generally an aluminosilicate having a three-dimensional skeleton structure, and has a general formula of XM2/□0・A1.
It is displayed as O,・YSiO□・ZH,0.
ここでＭはイオン交換可能なイオンを表し、通常は１ま
たは２価の金属イオンである。ｎは（金属）イオンの原
子価である。Ｘ及びＹはそれぞれの金属酸化物、シリカ
係数、２は結晶水の数を示す。Here, M represents an ion exchangeable ion, which is usually a monovalent or divalent metal ion. n is the valence of the (metal) ion. X and Y represent respective metal oxides, silica coefficients, and 2 represents the number of crystal water.
ゼオライトの具体例としては、Ａ型ゼオライト、Ｘ型ゼ
オライト、Ｙ型ゼオライト、Ｔ型ゼオライト、高シリカ
ゼオライト、ソーダライト、モルデナイト、アナルサイ
ム、クリブチロライト、チャバサイト、エリオナイト等
を挙げられる。但し、これらに限定されるものではない
。Specific examples of zeolites include A-type zeolite, However, it is not limited to these.
これら例示したゼオライトのイオン交換容量は、Ａ型ゼ
オライト： ７ ｍｅｑ／ｇ、 Ｘ型ゼオライト６．４
ｍｅｑ／ｇ、 Ｙ型ゼオライト５ ｍｅｑ／ｇ、 Ｔ型
ゼオライト３、４ ｍｅｑ／ｇ、ソーダライト１）．５
ｍｅｑ／ｇ、モルデナイト２．６ ｍｅｑ／ｇ、アナ
ルサイム５ ｍｅｑ／ｇ、クリブチロライト２．６ ｍ
ｅｑ／ｇ、チャバサイト５ ｍｅｑ／ｇ、エリオナイト
３．８ ｍｅｑ／ｇであり、いずれも銀イオン等の抗菌
性金属イオンでイオン交換するのに充分の容量を有して
いる。The ion exchange capacity of these exemplified zeolites is 7 meq/g for A-type zeolite and 6.4 meq/g for X-type zeolite.
meq/g, Y-type zeolite 5 meq/g, T-type zeolite 3, 4 meq/g, sodalite 1). 5
meq/g, Mordenite 2.6 meq/g, Analcyme 5 meq/g, Cributyrolite 2.6 m
eq/g, chabasite 5 meq/g, and erionite 3.8 meq/g, all of which have sufficient capacity for ion exchange with antibacterial metal ions such as silver ions.
また、ゼオライトの平均粒子径は、０．５〜３．０μｍ
の範囲とすることが、抗菌性ゼオライトとした場合に少
量で充分な抗菌力を発揮できるという観点から好ましい
。In addition, the average particle diameter of zeolite is 0.5 to 3.0 μm
It is preferable to set the amount within the range of 1, from the viewpoint that when used as an antibacterial zeolite, sufficient antibacterial activity can be exhibited with a small amount.
本発明で用いる抗菌性ゼオライトは、上記ゼオライト中
のイオン交換可能なイオン、例えばナトリウムイオン、
カルシウムイオン、カリウムイオン、マグネシウムイオ
ン等の一部又は全部を抗菌性金属イオン、または抗菌性
金属イオンとアンモニウムイオンとで置換したものであ
る。抗菌性金属イオンとしては、銀、銅、亜鉛、水銀、
錫、ビスマス、カドミウム、クロム及びタリウム等を例
示でき、特に、銀、銅及び亜鉛であることが好ましい。The antibacterial zeolite used in the present invention includes ion exchangeable ions in the zeolite, such as sodium ions,
Part or all of calcium ions, potassium ions, magnesium ions, etc. are replaced with antibacterial metal ions, or antibacterial metal ions and ammonium ions. Antibacterial metal ions include silver, copper, zinc, mercury,
Examples include tin, bismuth, cadmium, chromium, and thallium, with silver, copper, and zinc being particularly preferred.
ゼオライトに含まれる抗菌性金属イオンの含有量は、抗
菌性を考慮すると、０．５〜３０％、好ましくは１〜２
０％であることが適当である。尚、ゼオライトについて
のパーセント（％）とは、１）０℃乾燥基準の重量％を
いう。The content of antibacterial metal ions contained in zeolite is 0.5 to 30%, preferably 1 to 2%, considering antibacterial properties.
It is appropriate that it be 0%. Note that the percentage (%) for zeolite refers to 1) weight % on a dry basis at 0°C.
本発明で用いる抗菌性ゼオライトは、公知の方法（例え
ば、特開昭６３−２６５８０９号に記載の方法）により
、ゼオライトを抗菌性金属イオンによりイオン交換して
製造することができる。The antibacterial zeolite used in the present invention can be produced by ion-exchanging zeolite with antibacterial metal ions by a known method (for example, the method described in JP-A-63-265809).
抗菌性ゼオライトを含有するフィルター層の製造方法を
、抗菌性ゼオライトを含有する不織布である場合を例に
して以下に説明する。A method for producing a filter layer containing antibacterial zeolite will be described below, taking as an example a case where the filter layer is a nonwoven fabric containing antibacterial zeolite.
抗菌性ゼオライトを紡糸段階で樹脂に練り込んで抗菌性
ゼオライトを含有する繊維を得、この繊維を常法により
不織布化する。紡糸方法は、従来より知られている湿式
法または乾式法等の種々の方法を用いることができる。The antibacterial zeolite is kneaded into the resin during the spinning stage to obtain a fiber containing the antibacterial zeolite, and this fiber is made into a nonwoven fabric by a conventional method. As the spinning method, various conventionally known methods such as a wet method or a dry method can be used.
本発明に用いる抗菌性ゼオライトを含有するフィルター
層は、抗菌性ゼオライトを０．１〜３０重量％、好まし
くは０．３〜５重量％含有することが適当である。尚、
紡糸の形状は、表面に高密度に抗菌性ゼオライトを分散
できると言う観点から、最外層にのみ抗菌性ゼオライト
を含有するコンジュゲート糸とすることが好ましい。ま
た、紡糸口型の断面形状を波型等の多角形にすることが
糸の表面積を大きくするという観点から好ましい。The filter layer containing antibacterial zeolite used in the present invention suitably contains 0.1 to 30% by weight, preferably 0.3 to 5% by weight of antibacterial zeolite. still,
The spinning shape is preferably a conjugate yarn containing antibacterial zeolite only in the outermost layer, from the viewpoint that antibacterial zeolite can be dispersed at high density on the surface. Further, it is preferable to make the cross-sectional shape of the spinneret shape polygonal, such as a wave shape, from the viewpoint of increasing the surface area of the yarn.
本発明において用いる静電気帯電フィルター層は、一定
量の表面電荷密度を長期間維持できるものであればよい
。例えば、強誘電性セラミックを含有する通気性シート
または強誘電性高分子体製通気性シートを挙げることが
できる。The electrostatically charged filter layer used in the present invention may be any layer as long as it can maintain a certain amount of surface charge density for a long period of time. For example, a breathable sheet containing a ferroelectric ceramic or a breathable sheet made of a ferroelectric polymer can be used.
強誘電性セラミックとしては、チタン酸バリウム、チタ
ン酸鉛、チタン酸マグネシウム、ニオブ酸リチウム、ニ
オブ酸ガリウム、タンタル酸リチウムを例示できる。ま
た、強誘電性高分子体としては、例えばポリフッ化ビニ
リデン、フッ化ビニリデン−三フッ化エチレン共重合体
、フッ化ビニリデン−四フッ化エチレン共重合体、シア
ン化ビニリデン−酢酸ビニル共重合体等を挙げることが
できる。Examples of the ferroelectric ceramic include barium titanate, lead titanate, magnesium titanate, lithium niobate, gallium niobate, and lithium tantalate. Examples of ferroelectric polymers include polyvinylidene fluoride, vinylidene fluoride-ethylene trifluoride copolymer, vinylidene fluoride-ethylene tetrafluoride copolymer, vinylidene cyanide-vinyl acetate copolymer, etc. can be mentioned.
ここで、通気性シートとは、圧損が１ｍａＨｔＯ以下、
好ましくは０．８ ｍｍＨｔｏ以下であるシートである
。強誘電性セラミックを含有する通気性シートとしては
、例えばこれら強誘電性セラミックを樹脂に練り込んだ
繊維からなる不織布及び強誘電性高分子体からなる不織
布を挙げることができる。Here, the breathable sheet means a sheet with a pressure loss of 1 maHtO or less,
Preferably, the sheet is 0.8 mmHto or less. Examples of breathable sheets containing ferroelectric ceramics include nonwoven fabrics made of fibers in which these ferroelectric ceramics are kneaded into resin, and nonwoven fabrics made of ferroelectric polymers.
強誘電性セラミックを練り込む樹脂としては、ポリエチ
レン、ポリプロピレン、ポリエステル、ポリカーボネー
ト、ポリアミド、アクリル樹脂、アセテート樹脂、ポリ
ビニルアルコール系樹脂等を例示できる。Examples of the resin into which the ferroelectric ceramic is kneaded include polyethylene, polypropylene, polyester, polycarbonate, polyamide, acrylic resin, acetate resin, and polyvinyl alcohol resin.
静電気帯電フィルター層は、高集塵性とうい観点から、
表面電荷密度１０−１０クーロン／ ｃｔ１以上である
ことが好ましい。表面電荷密度をｒｏ−１）１ク一ロン
／ｄ以上にすれば、静電気帯電フィルター層の捕集効率
を９６％以上にすることができる。From the viewpoint of high dust collection, the electrostatically charged filter layer is
The surface charge density is preferably 10-10 coulombs/ct1 or more. By setting the surface charge density to ro-1) 1 coron/d or more, the collection efficiency of the electrostatically charged filter layer can be made to be 96% or more.
静電気帯電フィルター層は、表面電荷密度１０−”クー
ロン／ ｃａｒ以上を有し、しかも安価に製造できるこ
とから、チタン酸バリウムまたはチタン酸マグネシウム
を含有するポリエチレンまたはポリカーボネートから製
造することが好ましい。The electrostatically charged filter layer is preferably made from polyethylene or polycarbonate containing barium titanate or magnesium titanate because it has a surface charge density of 10-'' coulombs/car or more and can be manufactured at low cost.
強誘電性セラミックの樹脂への添加量は、各セラミック
の誘電率により適宜流めることができ、例えばチタン酸
マグネシウムの場合には、含有率を１０〜４０重量％と
することが、所定の表面電荷密度を得るという観点から
適当である。The amount of ferroelectric ceramic added to the resin can be adjusted as appropriate depending on the dielectric constant of each ceramic. For example, in the case of magnesium titanate, the content should be 10 to 40% by weight. This is appropriate from the viewpoint of obtaining surface charge density.
静電気帯電フィルター層は、公知の湿式法または乾式法
により、強誘電性セラミック含有樹脂または強誘電性高
分子体を繊維化し、一定の長さに切断し、不織布に成形
することにより得られる。The electrostatically charged filter layer is obtained by forming a ferroelectric ceramic-containing resin or a ferroelectric polymer into fibers, cutting them into predetermined lengths, and forming them into a nonwoven fabric using a known wet method or dry method.
低圧損性及び高集塵性を付与するという観点から、繊維
径は５〜６０μｍ１目付は５〜１２０ｇ／ｒｄとするこ
とが好ましい。From the viewpoint of providing low pressure loss properties and high dust collection properties, it is preferable that the fiber diameter is 5 to 60 μm and the basis weight is 5 to 120 g/rd.
得られた不織布は、常法により帯電させる。帯電方法と
しては、例えばコロナ放電法、誘電性ぺルトに挟み込ん
で放電する方法等を挙げることができる。The obtained nonwoven fabric is charged by a conventional method. Examples of the charging method include a corona discharge method and a method of discharging by sandwiching the material between dielectric pelts.
本発明のエアーフィルターは、抗菌性ゼオライトを含有
するフィルター層の一方または両方の面に静電気帯電フ
ィルター層を有するものである。The air filter of the present invention has an electrostatically charged filter layer on one or both sides of the filter layer containing antibacterial zeolite.
通常の除塵及び殺菌には、抗菌性ゼオライトを含有する
フィルター層の一方の面にのみ静電気帯電フィルター層
を設ければ充分である。但し、高い除塵性を付与する場
合には、抗菌性ゼオライトを含有するフィルター層の両
面に静電気帯電フィルター層を設けることが好ましい。For normal dust removal and sterilization, it is sufficient to provide an electrostatically charged filter layer only on one side of the filter layer containing antibacterial zeolite. However, when imparting high dust removal properties, it is preferable to provide electrostatically charged filter layers on both sides of the filter layer containing antibacterial zeolite.
抗菌性ゼオライトを含有するフィルター層と静電気帯電
フィルター層は、ニードルパンチ法、サーマルボンディ
ング法、パウダーボンディング法、水流絡合法等の公知
の方法により積層されてエアーフィルターとすることが
できる。The filter layer containing antibacterial zeolite and the electrostatically charged filter layer can be laminated to form an air filter by a known method such as a needle punching method, a thermal bonding method, a powder bonding method, a hydroentanglement method, or the like.
本発明のエアーフィルターは、バイオ分野、半導体、精
密機器、薬品等の製造分野で使用されるクリーンルーム
の空調装置に使用することができる。さらに、病院手術
室、種子保管室等の微生物による空気汚染の予防を必要
とされる多くの分野に適用できる。The air filter of the present invention can be used in clean room air conditioners used in the biotechnology field, semiconductor, precision equipment, pharmaceutical manufacturing fields, and the like. Furthermore, it can be applied to many fields where prevention of air contamination by microorganisms is required, such as hospital operating rooms and seed storage rooms.
本発明のエアーフィルターは、■空気の給気部及び排気
部物のフィルタ一部における微生物の繁殖及び通過を防
止し、■この効果を長期間維持でき、■構造が簡単であ
り、メインテナンスが容易であり、さらに■人体に対し
て安全性が高い。The air filter of the present invention: 1) prevents the growth and passage of microorganisms in the filter part of the air supply and exhaust parts, 2) maintains this effect for a long time, and 2) has a simple structure and is easy to maintain. Furthermore, it is highly safe for the human body.
以下、本発明を実施例及び参考例によりさらに詳細に説
明する。Hereinafter, the present invention will be explained in more detail with reference to Examples and Reference Examples.
参考例１ （抗菌性ゼオライト含有不織布の調製）シナ
ネンニューセラミック社製のＡ型ゼオライ） （Ｎａｔ
Ｏ” Ａｌｔｏｓ ” ２．０３ｉＯｔ ’ ＺＨｔＯ
：平均粒子径１、２ μｍ） 、Ｙ型ゼオライト（Ｎａ
ｔＯ＠ Ａｌｔｏｓ ” ４゜１Ｓｉ０１ＺＨ！０：平
均粒子径０．８μｍ）の２種類のゼオライトを使用して
、特開昭６３−２６５８０９号に記載の方法に準じて４
種類の抗菌性ゼオライトを得た。Reference Example 1 (Preparation of antibacterial zeolite-containing nonwoven fabric) Type A zeolite manufactured by Sinanen New Ceramics) (Nat
O" Altos "2.03iOt' ZHtO
: average particle diameter 1, 2 μm), Y-type zeolite (Na
tO@Altos" 4゜1Si01ZH!0: average particle size 0.8 μm) using two types of zeolites according to the method described in JP-A-63-265809.
Various antibacterial zeolites were obtained.
次いで、抗菌性ゼオライトを０．５〜５重量％配合した
ポリエチレン（昭和電工製ショウレックスＦ５０１２Ｍ
）混合物を２６０℃の成形温度で５０μｍ繊維径のモノ
フィラメントを溶融紡糸した。繊維長を１５ｍｍに切断
し、スパンボンド不織布加工機にて目付１０ｇ／ｒｔｒ
の抗菌性フィルター部材を得た。各抗菌性フィルタ一部
材に用いた抗菌性ゼオライトの性状及び各抗菌性フィル
タ一部材の特性を表１に示す。尚、Ｎｏ、 Ｚ −０は
、抗菌性ゼオライトを含まない。Next, polyethylene containing 0.5 to 5% by weight of antibacterial zeolite (Showa Denko's Showa Rex F5012M) was used.
) The mixture was melt-spun into monofilaments with a fiber diameter of 50 μm at a forming temperature of 260°C. The fiber length was cut to 15mm, and the fabric weight was 10g/rtr using a spunbond nonwoven fabric processing machine.
An antibacterial filter member was obtained. Table 1 shows the properties of the antibacterial zeolite used in each antibacterial filter member and the characteristics of each antibacterial filter member. Note that No. and Z-0 do not contain antibacterial zeolite.
参考例２（高誘電性セラミック含有不織布の調製）市販
のチタン酸バリウム（平均粒径３．５μｍ）をｌＯ〜２
５重量％配合したポリエチレン（昭和電工製ショウレッ
クスＦ５０１２Ｍ）混合物または市販のチタン酸マクネ
シウム（平均粒径４．２μｍ）を３５重量％配合したポ
リカーボネート（三菱瓦斯化学型Ｅ２００１）を２６０
℃の成形温度で３５μｍ繊維径のモノフィラメントを溶
融紡糸した。繊維長を３５ｍｍに切断し、スパンボンド
不織布加工機にて日付４０ ｇ／ｒｒｉとし、コロナ放
電法により帯電化させた。このようにして得た静電気帯
電フィルタ一部材の特性を表２に示す。尚、Ｎ１）Ｅ−
０は、上記加工を施さないものである。Reference Example 2 (Preparation of highly dielectric ceramic-containing nonwoven fabric) Commercially available barium titanate (average particle size 3.5 μm) was mixed with lO~2
A mixture of polyethylene (Shorex F5012M, manufactured by Showa Denko) containing 5% by weight or polycarbonate (Mitsubishi Gas Chemical Type E2001) containing 35% by weight of commercially available magnesium titanate (average particle size 4.2 μm) was used at 260% by weight.
Monofilaments with a fiber diameter of 35 μm were melt-spun at a forming temperature of °C. The fibers were cut to a length of 35 mm, processed using a spunbond nonwoven fabric processing machine at a rate of 40 g/rri, and charged using a corona discharge method. Table 2 shows the characteristics of the electrostatically charged filter member thus obtained. In addition, N1) E-
0 means that the above processing is not performed.
実施例（エアーフィルターの製造）
参考例１及び２で得た不織布をニードルパンチ法により
静電気帯電フィルター（厚さ０．３ｍ）／抗菌性ゼオラ
イト含有フィルター（厚さ５．０ ｔｎｍ ）／静電気
帯電フィルター（厚さ０．３ｍｍ）の順に積層化した。Example (manufacture of air filter) The nonwoven fabrics obtained in Reference Examples 1 and 2 were needle-punched to produce an electrostatically charged filter (thickness: 0.3 m)/antibacterial zeolite-containing filter (thickness: 5.0 tnm)/electrostatically charged filter. (thickness: 0.3 mm) were laminated in this order.
さらに、家庭用エアーコンディショナーの給気フィルタ
一部及び排気フィルタ一部に設置できるように適当な大
きさ（例えば、７００Ｘ４２０Ｘ７閣、１５０Ｘ６００
Ｘ７ｍｍ）に切断して設置した。In addition, it has an appropriate size (for example, 700 x 420 x 7 cabinets, 150 x 600
It was cut to 7mm x 7mm and installed.
試験例１（抗菌性試験）
上記エアーフィルターを設置した家庭用エアーコンディ
ショナーを１か月運転し、設置直後、１０日及び３０日
日の室内に排出される空気（１０ｄ）中の一般細菌数並
びに３０日日の両フィルター内部の一般細菌数を測定し
た。結果を表３に示す。Test Example 1 (Antibacterial Test) A household air conditioner equipped with the above air filter was operated for one month, and the number of general bacteria in the air (10d) discharged into the room immediately after installation, 10th and 30th days, and The number of general bacteria inside both filters was measured on the 30th day. The results are shown in Table 3.
Claims (2)
または両方の面に静電気帯電フィルター層を有するエア
ーフィルター。(1) An air filter having an electrostatically charged filter layer on one or both sides of the filter layer containing antibacterial zeolite.
ゼオライトを含有するフィルター層に導入する空気の殺
菌清浄化方法。(2) An air sterilization and purification method in which air that has passed through an electrostatically charged filter layer is introduced into a filter layer containing antibacterial zeolite.