JPH02279750A - Resin composition for sealing material - Google Patents
Resin composition for sealing materialInfo
- Publication number
- JPH02279750A JPH02279750A JP9984289A JP9984289A JPH02279750A JP H02279750 A JPH02279750 A JP H02279750A JP 9984289 A JP9984289 A JP 9984289A JP 9984289 A JP9984289 A JP 9984289A JP H02279750 A JPH02279750 A JP H02279750A
- Authority
- JP
- Japan
- Prior art keywords
- component
- resin
- easy
- weight
- ethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
（産業上の利用分野）
本発明は、プリン、ヨーグルトなどの液状あるいは固形
状の食品を収納する、ポリオレフィン系イージーオープ
ン容器と蓋との間に使用するイージーオープン容器のシ
ール材用樹脂組成物に関するものであシ、ヒートシール
加工の温度範囲が広く、開封時のイージーピ・−ル性お
よび剥離面の外観が優れたイージーオープン容器のシー
ル材用樹脂組成物に関する。Detailed Description of the Invention (Field of Industrial Application) The present invention relates to an easy-open container used between a polyolefin easy-open container and a lid for storing liquid or solid foods such as pudding and yogurt. The present invention relates to a resin composition for sealing materials, and relates to a resin composition for sealing materials for easy-open containers, which can be heat-sealed over a wide temperature range, has excellent easy peelability upon opening, and has excellent appearance of the peeled surface.
（従来の技術）
プリン、ヨーグルトなどの乳製品やインスタント食品な
どを完全密封し、且つ開封時には蓋や容器を破損せずに
手で容易に開封できる特性（イージーピール性）を持っ
たイージーオープン容器は、食品包装容器として広く使
用されている。(Conventional technology) Easy-open containers that completely seal dairy products such as pudding and yogurt, instant foods, etc., and that have the characteristic (easy peelability) that they can be easily opened by hand without damaging the lid or container when opened. are widely used as food packaging containers.
容器の材料としては、適度な硬度、保温性、加工成形の
容易さの点からポリスチレンあるいはポリオレフィンが
多用され、イージーピール性を持たせるために蓋と容器
のシール部に用いるシール材に種々の工夫がこらされて
いる。Polystyrene or polyolefin is often used as a material for containers due to its appropriate hardness, heat retention, and ease of processing and molding. Various innovations have been made to the sealing material used for the seal between the lid and the container to provide easy-peel properties. is being strained.
例えば、ポリスチレン容器用シール材としては、エチレ
ン酢酸ビニル樹脂とスチレンブタジェンブロック共重合
体およびポリスチレン樹脂からなる組成物（特開昭５４
−１２９０７５号）や低結晶性ポリエチレン−αオレフ
インランダム共重合体とスチレン系炭化水素とのブロッ
ク共重合体からなる樹脂組成物（特開昭５４−１２０６
５８号）などが提案されている。For example, as a sealing material for polystyrene containers, a composition consisting of an ethylene vinyl acetate resin, a styrene butadiene block copolymer, and a polystyrene resin (Japanese Patent Laid-Open No. 54
-129075) and a resin composition comprising a block copolymer of a low-crystalline polyethylene-α olefin random copolymer and a styrene hydrocarbon (JP-A-54-1206).
No. 58) have been proposed.
しかしながら、これらの樹脂組成物をポリオレフィン系
容器に応用した場合、シール材と容器との接着強度が大
きすぎイージーピール性が発現せず、また剥離面の外観
も悪く、これらはいずれもポリオレフィン系容器には適
さない。However, when these resin compositions are applied to polyolefin-based containers, the adhesive strength between the sealing material and the container is too high, and easy peelability is not achieved, and the appearance of the peeled surface is also poor. Not suitable for
また、ポリオレフィン系イージーオープン容器のシール
材としては、従来よシポリプロピレンとポリエチレンの
混合物、ポリエチレンとエチレン酢酸ビニル共重合体の
混合物あるいはポリプロピレン、ポリエチレン、エチレ
ン酢酸ビニル共重合体等の積層フィルムなどが、多く使
用されている。Conventionally, sealing materials for polyolefin-based easy-open containers include a mixture of polypropylene and polyethylene, a mixture of polyethylene and ethylene-vinyl acetate copolymer, or a laminated film of polypropylene, polyethylene, ethylene-vinyl acetate copolymer, etc. Used a lot.
しかし、これらはいずれも容器とシール材の融着界面で
の剥離によってイージーピール性を持たせようとするも
のであるため、融着温度の影響を大きく受け、イージー
ピール性を保持させるための加工温度幅が狭く、加工時
の厳密な温度管理が必要となる。また開封時の剥離は、
シール材と容器との界面およびシール材と蓋との界面の
両者で起こるため、剥離面にシール材の剥離片が膜状の
大きなヒゲあるいは毛羽立ちとなって発生するとともに
、これらの剥離片が容器内へ脱落するという欠点を有し
ている。However, these methods all attempt to provide easy-peel properties by peeling off at the fused interface between the container and the sealant, so they are greatly affected by the fusion temperature, and processing to maintain easy-peel properties is required. The temperature range is narrow, requiring strict temperature control during processing. In addition, peeling when opening the package,
This occurs at both the interface between the sealant and the container and the interface between the sealant and the lid, so peeled pieces of the sealant form large film-like whiskers or fluff on the peeled surface, and these peeled pieces can cause damage to the container. It has the disadvantage of falling out.
（発明が解決しようとする課題）
本発明は、従来のポリオレフィン系イージーオープン容
器のシール材用樹脂組成物の上記問題点を解消し、広範
囲のヒートシール加工温度において、イージーピール性
を持ち、且つ剥離面にひげ、毛羽立ちの発生が少なく、
剥離外観に優れたイージーオープン容器のシール材用樹
脂組成物を提供することを目的とする。(Problems to be Solved by the Invention) The present invention solves the above-mentioned problems of conventional polyolefin-based resin compositions for sealing materials for easy-open containers, and has easy-peel properties over a wide range of heat-sealing temperatures. There is less occurrence of whiskers and fuzz on the peeled surface,
An object of the present invention is to provide a resin composition for a sealant for an easy-to-open container that has an excellent peel appearance.
（課題を解決するための手段）
本発明者たちは、上記目的を達成するため鋭意研究した
結果、ポリオレフィン系樹脂と、これに対して非相斉也
であるポリスチレン系樹脂とを所定量混合することによ
って得られる組成物は、それ自身に層剥離性を有し、そ
の組成物をシール材として用いると、融着界面から剥離
せずに、シール材の内部で層剥離するため、広範囲のヒ
ートシール加工温度において安定したイージーピール性
を有し、また、剥離面の外観の優れた、イージーオープ
ン容器のシール材用樹脂組成物となることを見い出し、
この知見にもとづき本発明を完成した。(Means for Solving the Problem) As a result of intensive research to achieve the above object, the inventors of the present invention have determined that a predetermined amount of a polyolefin resin and a polystyrene resin, which is non-compatible with the polyolefin resin, are mixed together. The composition obtained by this process has delaminating properties in itself, and when used as a sealing material, the composition does not peel off from the fusion interface but delaminates inside the sealing material, so it can be heated over a wide range. We have discovered that a resin composition for sealing materials for easy-open containers has stable easy-peel properties at sealing processing temperatures and has an excellent appearance on the peeled surface.
The present invention was completed based on this knowledge.
すなわち、本発明はポリプロピレン系樹脂（成分ａ）、
ポリエチレン系樹脂（成分ｂ）、ポリスチレン系樹脂（
成分Ｃ）および共役ジエン−スチレンブロック共重合体
の水添物（成分ｄ）とからなり、全重量に対する各成分
の割合がそれぞへ成分ａが１０〜６０重量％、成分すが
１０〜７０重量％、成分Ｃが１０〜４０重！−％、成分
ｄが３〜２０重量係であシ、成分Ｃの配合量が成分ｄの
配合量の１．５倍以上７倍未満であることを特徴とする
ヒートシール性、イージーピール性および開封時の剥離
面の外観の優れたイージーオープン容器９シール材用樹
脂組成物である。That is, the present invention uses a polypropylene resin (component a),
Polyethylene resin (component b), polystyrene resin (
It consists of component C) and a hydrogenated product of a conjugated diene-styrene block copolymer (component d), and the ratio of each component to the total weight is 10 to 60% by weight for component a and 10 to 70% by weight for component A. Weight%, component C is 10 to 40 weight! -%, component d is 3 to 20% by weight, and the amount of component C is 1.5 times or more and less than 7 times the amount of component d. This is a resin composition for an easy-open container 9 sealing material that has an excellent appearance on the peeled surface when opened.
以下に、本発明を具体的に説明する。The present invention will be specifically explained below.
囚 ポリプロピレン系樹脂
本発明で成分ａとして用いられるポリプロピレン系樹脂
は、プロピレン単独重合体、エチレン−プロピレンラン
ダム共重合体、エチレン−プロピレン−ブテンランダム
共重合体、エチレンープロピレンブロック共重合体また
はこれらの二以上の混合物のいずれでもよい。Polypropylene resin The polypropylene resin used as component a in the present invention is a propylene homopolymer, an ethylene-propylene random copolymer, an ethylene-propylene-butene random copolymer, an ethylene-propylene block copolymer, or a combination thereof. It may be a mixture of two or more.
本発明の組成物中の成分ａの割合は１０〜６０重量％で
あるが、１０重ｉ％未満であると、容器および蓋とのヒ
ートシール強度不足のため、食品の運搬時等に内容物が
漏れる可能性があるため不適当であり、また６０重量％
を越える量であるとイージービール性が低下し開封が困
難となるため不適当である。The proportion of component a in the composition of the present invention is 10 to 60% by weight, but if it is less than 10% by weight, the heat sealing strength with the container and lid will be insufficient, so that the contents may be lost during transportation of food. It is inappropriate because there is a possibility of leakage, and 60% by weight
If the amount exceeds the above, the easy-beer property will deteriorate and opening will become difficult, which is inappropriate.
（Ｂ） ポリエチレン系樹脂
本発明で成分すとして用いられるポリエチレン系樹脂は
、高密度ポリエチレン、低密度ポリエチレン、あるいは
直鎖状低密度ポリエチレンとして市販されているものを
適宜選択して用いればよい。(B) Polyethylene resin The polyethylene resin used as a component in the present invention may be appropriately selected from those commercially available as high-density polyethylene, low-density polyethylene, or linear low-density polyethylene.
本発明の組成物中の成分すの割合は１０〜７００〜７０
重量％特に好ましい割合は４０〜６０重量％である。成
分すの割合が１０重量％未満では、イージ・−ビール性
は発現するものの、ヒートシール加工の温度範囲が狭く
なるため不適当であり、また７０重量％を越えるとヒー
トシール強度が低くなシ、食品の運搬時等に内容物が漏
れる可能性があるため不適当である。The proportion of the components in the composition of the present invention is 10-700-70
A particularly preferred percentage by weight is 40 to 60% by weight. If the proportion of the component is less than 10% by weight, easy-to-beer properties will be achieved, but the temperature range for heat sealing will be narrow, making it unsuitable. If it exceeds 70% by weight, the heat sealing strength will be low and the seal will be unsuitable. This is inappropriate because the contents may leak during food transportation.
（Ｑ ポリスチレン系樹脂
本発明で成分Ｃとして用いられるポリスチレン系樹脂は
、スチレン単独重合体、ゴム変性ポリスチレン、アクリ
ロニトリル−ブタジェン−メチ１／ン共重合体、もしく
はこれらの二以上の混合物のいずれでもよく、例えばス
チレン単独重合体としては、無化成工業■製スタイロン
６０５、スタイロン６６６などを、ゴム変性ポリスチレ
ンとしては、無化成工業■製スタイロン４７０などをあ
げることができ、またアクリロニトリル−ブタジエン−
スチレン共重合体としては、鐘淵化学工業■製カネエ−
ｘｙｘｕＨＥ−１５００などをあげることができる。(Q Polystyrene Resin The polystyrene resin used as component C in the present invention may be a styrene homopolymer, a rubber-modified polystyrene, an acrylonitrile-butadiene-methylene copolymer, or a mixture of two or more of these. For example, styrene homopolymers include Stylon 605 and Stylon 666 manufactured by Mukasei Kogyo ■, rubber-modified polystyrene such as Stylon 470 manufactured by Mukasei Kogyo ■, and acrylonitrile-butadiene-
As a styrene copolymer, Kane-E manufactured by Kanebuchi Chemical Industry ■
Examples include xyxuHE-1500.
本発明の組成物中の成分Ｃの割合は１０〜４０重ｉ％で
あシ、特に好ましい割合は１５〜３０５〜３０重量％成
分Ｃの割合が１０重量％未満であると、本発明の特徴で
ある層剥離性が低下し、そのためイージーピール性が失
われ、また４０重墓係を越えると剥離面のヒゲや毛羽立
ちの発生が多くなるためいずれも不適当である。The proportion of component C in the composition of the present invention is 10 to 40% by weight, particularly preferably 15 to 305 to 30% by weight.The characteristic of the present invention is that the proportion of component C is less than 10% by weight. The peelability of the layer decreases, resulting in a loss of easy peelability, and if the layer thickness exceeds 40 layers, the peeled surface becomes more prone to beards and fuzz, which are both unsuitable.
（Ｄ） 共役ジエン−スチレンブロック共重合体の水
添物
本発明で成分ｄとして用いられる共役ジエン−スチレン
ブロック共重合体の水添物は、公知の方法（例えば特公
昭６０−５７４６３号公報など）で得られているゴム状
物質である。このような共役ジエン−スチレンブロック
共重合体の水添物は、通常市販品ではスチレン−エチレ
ン・ブチレンブロック共重合体として、シェル化学■製
クレイトン（Ｋｒａｔｏｎ ） （登録商標） Ｇ−１
６５０、Ｇ−１６５２を、またスチレン−エチレン・プ
ロピレンブロック共重合体として、シェル化学■製クレ
イトン（Ｋｒａｔ、ｏｎ ） （登録商標）Ｇ−１７０
１Ｘなどをあげることができる。(D) Hydrogenated product of conjugated diene-styrene block copolymer The hydrogenated product of the conjugated diene-styrene block copolymer used as component d in the present invention can be prepared by a known method (for example, Japanese Patent Publication No. 60-57463, etc.). ) is a rubbery substance obtained from Such hydrogenated conjugated diene-styrene block copolymers are usually commercially available as styrene-ethylene-butylene block copolymers such as Kraton (registered trademark) G-1 manufactured by Shell Chemical Company.
650, G-1652, and as a styrene-ethylene propylene block copolymer, Krat, on (registered trademark) G-170 manufactured by Shell Chemical Company.
1X etc. can be given.
本発明の組成物中の成分ｄの割合は３〜２０重ｉ易であ
り、特に好ましい割合は５〜１０重量％である。成分ｄ
の割合が３重量％未満では、剥離時にヒゲや毛羽立ちが
激しくなるため不適当であり、２０重量％を越えるとヒ
ートシール強度が高くなシすぎイージーピール性が発現
しなくなるので不適当である。The proportion of component d in the composition of the invention is usually 3 to 20% by weight, with a particularly preferred proportion being 5 to 10% by weight. component d
If the proportion is less than 3% by weight, it is unsuitable because whiskers and fuzz will become severe during peeling, and if it exceeds 20% by weight, the heat seal strength will be too high and easy peelability will not be expressed, so it is unsuitable.
また、ポリスチレン系樹脂（成分Ｃ）の配合ｌは、共役
ジエン−スチレンブロック共重合体の水添物（成分ｄ）
の配合量の１．５倍以上７倍未満でなければならない。In addition, the blend l of the polystyrene resin (component C) is a hydrogenated product of a conjugated diene-styrene block copolymer (component d).
It must be at least 1.5 times and less than 7 times the blended amount.
成分Ｃの特に好ましい配合割合は、成分ｄの３〜５倍で
ある。成分Ｃの量が成分ｄの量の１．５倍未満では、イ
ージーピール性が失われ、開封が困難となり、また７倍
を越える量では、ヒゲや毛羽立ちの発生が激しくなり剥
離面の外観が劣るため不適当である。A particularly preferred blending ratio of component C is 3 to 5 times that of component d. If the amount of component C is less than 1.5 times the amount of component d, the easy-peel properties will be lost and it will be difficult to open the package, and if the amount exceeds 7 times, the appearance of the peeled surface will be severe and hairs and fuzz will occur. It is inappropriate because it is inferior.
本発明の組成物は、各配合成分の所定量をヘンセルミキ
サーニ商品名）、スーパーミキサーなどの混合装置に入
れて数分間、例えば３分間、撹拌混合し、該混合物を通
常の単軸押出機、２軸押比機などで溶融混線温度１８０
℃〜３００℃で、好ましくは２００℃〜２６０℃で、溶
融混線しぺ１ノツト化することによシ製造することがで
きる。The composition of the present invention can be prepared by putting a predetermined amount of each ingredient into a mixing device such as a Hensel mixer (trade name) or a super mixer, stirring and mixing for several minutes, for example, 3 minutes, and then extruding the mixture by conventional single-screw extrusion. The melt crosstalk temperature is 180 with a machine, twin-screw press ratio machine, etc.
It can be produced by melt-mixing and forming a single knot at a temperature of 300°C to 300°C, preferably 200°C to 260°C.
かくして製造された本発明の組成物は、常法のＴダイフ
ィルム法や常法のインフレーションフィルム法等により
フィルム状とし、イージーオープン容器の蓋または容器
側シートに常法のサーマルラミ法を用いてラミネートし
て使用でき、または蓋側樹脂、容器側樹脂と共に、常法
の共押出法を用いて複合多層フィルム、多層シートとす
る等によって、イージーオープン容器のシール材として
使用することができる。The composition of the present invention thus produced is formed into a film by a conventional T-die film method or a conventional blown film method, and then laminated onto the lid of an easy-open container or a container side sheet by a conventional thermal lamination method. Alternatively, it can be used as a sealing material for easy-open containers by forming a composite multilayer film or multilayer sheet together with a lid side resin and a container side resin using a conventional coextrusion method.
また、本発明の樹脂組成物からなるフィルムは他のプラ
スチックフィルムまたはアルミニウム箔と積層してイー
ジービール接着剤として使用することもできる。Furthermore, the film made of the resin composition of the present invention can be laminated with other plastic films or aluminum foil and used as an easy beer adhesive.
（発明の効果）
本発明による樹脂組成物を、ポリオレフィン系のイージ
ーオープン容器に、シール材として使用すると、広範囲
なヒートシール加工温度においてヒートシール性とイー
ジーピール性に優れ、且つ剥離外関性の良いイージーオ
ープン容器のシール材となるため、各種の食品収納カッ
プ等に幅広く使用することができる。(Effects of the Invention) When the resin composition of the present invention is used as a sealing material in polyolefin-based easy-open containers, it exhibits excellent heat-sealing properties and easy-peel properties over a wide range of heat-sealing temperatures, and has excellent peelability. Since it is a good sealing material for easy-open containers, it can be widely used in various food storage cups, etc.
（実施例）
以下、実施例および比較例によυ、本発明を具体的に説
明する。(Examples) Hereinafter, the present invention will be specifically explained with reference to Examples and Comparative Examples.
なお、実施例および比較例において用いた評価方法は次
の方法によった。The evaluation method used in the Examples and Comparative Examples was as follows.
ポリプロピレン系樹脂（成分ａ）、ポリエチレン系樹脂
（成分ｂ）、ポリスチレン系樹脂（成分ｃ）、共役ジエ
ン−スチレンブロック共重合体の水添物（成分ｄ）の各
成分を、各表に記載の配合割合に配合し、ヘンセルミキ
サー（商品名）で３分間撹拌混合したのち、該混合物を
単軸４０ｍｘφ押出機を用いて、溶融混線温度２２０℃
で溶融混線押出し、ペレット状の組成物を得た。Each component of polypropylene resin (component a), polyethylene resin (component b), polystyrene resin (component c), and hydrogenated product of conjugated diene-styrene block copolymer (component d) was added as shown in each table. After stirring and mixing for 3 minutes using a Hensel mixer (trade name), the mixture was heated to a melt mixing temperature of 220°C using a single-screw 40m x φ extruder.
The mixture was melt mixed and extruded to obtain a pellet-like composition.
得られた組成物を６０ｊ＋ｍφ押出機を用い、温度２６
０℃で常法のでダイ法により厚さ３０μｍのシール材フ
ィルムとした。The obtained composition was heated to 26°C using a 60j+mφ extruder.
A sealing material film having a thickness of 30 μm was prepared by a conventional die method at 0°C.
該シール材フィルムを厚さ２５０μｍのポリプロピレン
単独重合体シート（ＭＦＲ０，５，９／１０分）に重ね
合わせ、２４０℃で常法のサーマルラミ法を用いて積層
シートを作成した。The sealing material film was laminated on a polypropylene homopolymer sheet (MFR 0, 5, 9/10 minutes) having a thickness of 250 μm, and a laminated sheet was prepared using a conventional thermal lamination method at 240° C.
得られた積層シートのシール材側と単層ボリプ定するこ
とによシ、ヒートシール性、イージーピール性、剥離面
のヒゲ・毛羽立ちの発生の有無を調べた。By comparing the sealing material side of the obtained laminated sheet with a single layer, heat sealability, easy peelability, and the presence or absence of hairs and fuzz on the peeled surface were examined.
ヒートシールは、バー型ヒートシーラーで行ないシール
温度は１２０℃〜２６０℃、シール圧力１に９／ｃｒｉ
ｌ、シール時間５秒で実施した。ヒートシール強度の測
定は、引張試験機を用い、テストピース幅１５ｊＩｘ、
剥離スピード３００朋／ｉで行なった。Heat sealing is done with a bar type heat sealer, sealing temperature is 120℃ ~ 260℃, sealing pressure is 1 to 9/cri.
1. The sealing time was 5 seconds. The heat seal strength was measured using a tensile tester with a test piece width of 15jIx,
The peeling was carried out at a peeling speed of 300 mm/i.
イージーピール性
１８０℃のヒートシール温度におけるヒートシール強度
よシ判定し、判定基準は以下の通りとした。Easy peelability The heat sealing strength at a heat sealing temperature of 180° C. was evaluated, and the criteria for evaluation were as follows.
ヒートシール強度５００〜１５００ ｊｉ ／ １５
Ｂの範囲の物をイージーピール性良好とし、Ｏ印で示し
た。またヒートシール強度５００ Ｅ ／ １５ ｊｃ
ｔ幅未満の物を密封性不良としＸ印で示し、１５００１
／ １５ ｍ幅を越える強度の物をイージーピール性
不良としｘ印で示した。Heat seal strength 500-1500 ji/15
Items in the range B were considered to have good easy peelability and were marked with an O mark. Also, heat seal strength is 500E/15JC
Items with a width less than t are considered to have poor sealing performance and are marked with an X mark, 15001
/ Items with a strength exceeding 15 m width were considered to have poor easy peel properties and were marked with an x.
ヒートシール性
１２０〜２６０℃のヒートシール温度範囲において、イ
ージーピール性良好を示すの温度範囲が５０℃以上と広
い物をヒートシール性良好とし○印で示した。またイー
ジーピール性良好を示すの温度範囲が５０℃未満と狭い
物をヒートシール性不良としＸ印で示した。Heat-sealability In the heat-sealing temperature range of 120 to 260°C, those exhibiting good easy peelability in a wide temperature range of 50°C or higher are considered to have good heat-sealability and are marked with a circle. In addition, those exhibiting good easy peelability but having a narrow temperature range of less than 50°C are marked with an X as having poor heat sealability.
剥離面の外観 剥離面の外観の判定基準は、以下の通りとした。Appearance of peeled surface The criteria for determining the appearance of the peeled surface were as follows.
ｘｘ：肉眼判定において、大きなヒゲ・毛羽立ちが認め
られる。xx: Large whiskers and fuzz are observed by visual inspection.
Ｘ：肉眼判定において、小さなヒゲ・毛羽立ちが認めら
れる。X: Small whiskers and fuzz are observed by visual inspection.
Δ：肉眼判定において、微細な毛羽立ちが認められる。Δ: Fine fluff is observed when visually judged.
○：肉眼観察でヒゲ・毛羽立ちの発生が認められない。○: No occurrence of whiskers or fuzz is observed by naked eye observation.
Δ印およびＯ印を、剥離面の外観良好とした。The Δ mark and the O mark indicate that the appearance of the peeled surface was good.
実施例および比較例で用いたポリプロピレン系樹脂の（
ａ−１）は、常法で重合されたエチレン含有量４．０重
量％、ブテン含有量４．５重量％で、メルトフローレー
ト５．０＃／１０分のエチレン−プロピレン−ブテンラ
ンダム共重合体で６．Ｄ、 （ａ−２）は、常法で重合
されたエチレン含有量２．０重量％で、メルトフローレ
ート８．０．９／１０分のエチレン−プロピレンランダ
ム共重合体、（ａ−３）は、常法で重合されたメルトフ
ローレート５．０ｇ／１０分のポリプロピレン単独重合
体である。Polypropylene resin used in Examples and Comparative Examples (
a-1) is an ethylene-propylene-butene random copolymer polymerized by a conventional method with an ethylene content of 4.0% by weight, a butene content of 4.5% by weight, and a melt flow rate of 5.0#/10 min. Combined with 6. D, (a-2) is an ethylene-propylene random copolymer with an ethylene content of 2.0% by weight and a melt flow rate of 8.0.9/10 min, polymerized by a conventional method, (a-3) is a polypropylene homopolymer having a melt flow rate of 5.0 g/10 min, polymerized by a conventional method.
ポリエチレン系樹脂の（ｂ−１）は日本ユニカー−製直
鎖状低密度ポリエチレンＮＵＣＧ−５２１１（密度０．
９２０、Ｍｌ １゜Ｏ）であシ、（ｂ−２）は高密度ポ
リエチレンでちるチッソポリエチＭ８５０ （ａ密度０
、９６５、Ｍｌ５．０）を使用した。The polyethylene resin (b-1) is linear low-density polyethylene NUCG-5211 (density 0.
920, Ml 1°O), (b-2) is Nissopolyethylene M850 (a density 0
, 965, Ml5.0) was used.
ポリスチレン系樹脂の（ｃ−１）は旭化成工業■製スチ
レン単独重合体でおるスタイロン（登録商標）６０５で
あり、（ｃ−２）はゴム変性ポリスチレンであるスタイ
ロン（登録商標）４７０を使用した。The polystyrene resin (c-1) was Styron (registered trademark) 605, a styrene homopolymer manufactured by Asahi Kasei Kogyo ■, and (c-2) was Stylon (registered trademark) 470, a rubber-modified polystyrene.
共役ジエン−スチレンブロック共重合体の水添物の（ａ
−１）はスチレン−エチレン・ブチレンスチレンブロッ
ク共重合体であるシェル化学■製のクレイトン（登録商
標）Ｇ−１６５２を、（ａ−Ｚ）はスチレン−エチレン
・プロピレンブロック共重合体であるシェル化学■製の
クレイトン（登録商標）Ｇ−１７０１Ｘをそれぞれ使用
した。Hydrogenated product of conjugated diene-styrene block copolymer (a
-1) is a styrene-ethylene/butylene-styrene block copolymer, Shell Chemical Co., Ltd.'s Kraton (registered trademark) G-1652; (a-Z) is a styrene-ethylene/propylene block copolymer, Shell Chemical Co., Ltd. Kraton (registered trademark) G-1701X manufactured by (1) was used in each case.
実施例を実験番号１〜１１に、また比較例を実験番号１
２〜２７に示した。Examples are shown in experiment numbers 1 to 11, and comparative examples are shown in experiment number 1.
2 to 27.
結果を第１表および第２表に示した。The results are shown in Tables 1 and 2.
第１表及び第２表のデータから、以下のことが明白であ
る。From the data in Tables 1 and 2, it is clear that:
実験番号１〜６では、ヒートシール性、イージービール
性に優れ、また剥離面のヒゲ・毛羽立ちも少なく、イー
ジーオープン容器シール材用樹脂組成物として適してい
ることがわかる。In Experiment Nos. 1 to 6, it was found that the resin compositions had excellent heat-sealing properties and easy-to-beer properties, and there were few whiskers and fuzz on the peeled surface, making them suitable as resin compositions for easy-open container sealing materials.
実験番号１２では、ポリプロピレン樹脂（ａｌが少ない
丸め、１８０℃のヒートシール強度が低く不適当である
。In Experiment No. 12, the polypropylene resin (rounded with low Al content and low heat sealing strength at 180°C is inappropriate).
実験番号１３．１４．１５では、イージーピール性及び
剥離面の外観性は良いが、ヒートシール性に劣る。In experiment numbers 13, 14, and 15, the easy peelability and the appearance of the peeled surface were good, but the heat sealability was poor.
実験番号１６では、ポリスチレン系樹脂が少ないため、
イージービール性に劣シネ適当であるｄ実験番号１７．
１８では、イージーピール性は発現するが、ヒートシー
ル性及び剥離面の外観性に劣るため不適当である。In experiment number 16, since there was little polystyrene resin,
Experiment number 17.
Sample No. 18 exhibits easy peelability, but is unsuitable because it has poor heat sealability and poor appearance of the peeled surface.
実験番号１９では、イージービール性は発現するが、ヒ
ートシール性に劣るため不適当である。In Experiment No. 19, easy beer properties were exhibited, but heat sealability was poor and therefore unsuitable.
実験番号２０，２１．２２では、ポリスチレン系樹脂（
Ｃ）と、共役ジエン−スチレンブロック共重合体１ｄ）
の配合割合が、本発明で規定した範囲を越えているため
、イージーピール性は発現するものの、剥離面に大きな
ヒゲ・毛羽立ちが発生するので不適当である。In experiment numbers 20, 21 and 22, polystyrene resin (
C) and conjugated diene-styrene block copolymer 1d)
Since the blending ratio exceeds the range specified in the present invention, although easy peelability is achieved, large hairs and fuzz occur on the peeled surface, which is inappropriate.
実験番号２３は、ポリスチレン系樹脂（Ｃ１と共役ジエ
ン−スチレンブロック共重合体ｆｄ）の配合割合が、本
発明で規定した範囲に達していないため、イージーピー
ル性に劣シネ適当である。In Experiment No. 23, the blending ratio of the polystyrene resin (C1 and conjugated diene-styrene block copolymer fd) did not reach the range specified in the present invention, so the easy peelability was poor and the film was suitable for use as a cine.
実験番号７は、実験番号１と同一配合比で、ただしポリ
プロピレン樹脂としてエチレン−プロピレンランダム共
重合体（ａ−２）を使用し、まだ実験番号８は同様に、
ポリプロピレン系樹脂としてプロピレン単独重合体（ａ
−３）を使用したものであるが、エチレン−プロピレン
−ブテンランダム共重合体（ａ−１）を用いた場合と同
様に、優れたイージービール性、ヒートシール性を示し
ている。Experiment No. 7 had the same blending ratio as Experiment No. 1, except that ethylene-propylene random copolymer (a-2) was used as the polypropylene resin, and Experiment No. 8 had the same proportions as Experiment No. 1.
Propylene homopolymer (a
-3), it shows excellent easy beer properties and heat sealability, similar to the case where ethylene-propylene-butene random copolymer (a-1) is used.
実験番号９は、ポリエチレン系樹脂として高密度ポリエ
チレン（チッソポリエチＭ８５０）を使用したものであ
るが、直鎖状低密度ポリエチレンを使用した場合と同様
のイージーピール性を示し、剥離面の外観性も良好であ
る。Experiment No. 9 used high-density polyethylene (Chisso Polyethylene M850) as the polyethylene resin, and showed the same easy-peel properties as when linear low-density polyethylene was used, and the appearance of the peeled surface was also improved. In good condition.
実験番号１０では、実験番号１と同一配合比で、ただし
共役ジエン−スチレンブロック共重合体の水添物として
スチレン−エチレン・プロピレンブロック共重合体（シ
ェル化学■製クレイトンＧ−１７０１Ｘ ）を使用した
ものであるが、スチレン−エチレン・ブチ１／ンスチレ
ンブロック共重合体に比較して、剥離面の外観性が僅か
に劣るが、実用上問題なく、イージーオープン容器シー
ル材用樹脂組成物として使用可能である。In Experiment No. 10, the same blending ratio as in Experiment No. 1 was used, except that styrene-ethylene propylene block copolymer (Krayton G-1701X manufactured by Shell Chemical ■) was used as the hydrogenated product of the conjugated diene-styrene block copolymer. Although the appearance of the peeled surface is slightly inferior to that of the styrene-ethylene butylene 1/styrene block copolymer, there is no practical problem and it can be used as a resin composition for easy-open container sealing materials. It is possible.
実験番号１１では、ポリスチレン系樹脂としてゴム変性
ポリスチレン（スタイロン４７０）を使用したものであ
るが、スチレン単独重合体を使用した場合と比較して、
剥離面の外観性が僅かに劣るが、実用上問題なく、イー
ジーオープン容器シール材用樹脂組成物として使用可能
である。In Experiment No. 11, rubber-modified polystyrene (Styron 470) was used as the polystyrene resin, but compared to using styrene homopolymer,
Although the appearance of the peeled surface is slightly inferior, there is no practical problem and it can be used as a resin composition for an easy-open container sealing material.
実験番号２４では、ポリプロピレン系樹脂とエチレン酢
酸ビニル共重合体のブレンド系であシ、また実験番号２
５は、ポリエチレン系樹脂とエチレン酢酸ビニル共重合
体のブレンド系であるが、これらはいずれもイージーピ
ール性は有するものの、ヒートシール性、剥離面の外観
性に劣るため不適当である。In experiment number 24, a blend system of polypropylene resin and ethylene vinyl acetate copolymer was used, and experiment number 2
No. 5 is a blend of polyethylene resin and ethylene-vinyl acetate copolymer, but although they all have easy peelability, they are unsuitable because they are poor in heat sealability and appearance of the peeled surface.
実験番号２６．２７では、ポリプロピレン樹脂とポリエ
チレン樹脂のブレンド系であるが、ポリプロピレン樹脂
の多い系では、イージーピール性を示さず、また、ポリ
エチレン樹脂の多い系では、イージーヒール性は有する
ものの、ヒートシール性、剥離面の外観性に劣るため不
適当である。In experiment numbers 26 and 27, a blend system of polypropylene resin and polyethylene resin was used, but the system with a large amount of polypropylene resin did not show easy peel properties, and the system with a large amount of polyethylene resin showed easy heel properties, but it was difficult to heat. It is unsuitable because the sealing performance and appearance of the peeled surface are poor.
以上that's all
Claims (4)
系樹脂（成分ｂ）、ポリスチレン系樹脂（成分ｃ）およ
び共役ジエン−スチレンブロック共重合体の水添物（成
分ｄ）とからなり、全重量に対する各成分の割合がそれ
ぞれ成分（ａ）が１０〜６０重量％、成分（ｂ）が１０
〜７０重量％、成分（ｃ）が１０〜４０重量％、成分（
ｄ）が３〜２０重量％であり、成分（ｃ）の配合量が成
分（ｄ）の配合量の１．５倍以上７倍未満であることを
特徴とするイージーオープン容器のシール材用樹脂組成
物。(1) Consists of polypropylene resin (component a), polyethylene resin (component b), polystyrene resin (component c), and hydrogenated product of conjugated diene-styrene block copolymer (component d), based on the total weight. The proportion of each component is 10 to 60% by weight for component (a) and 10% by weight for component (b).
~70% by weight, component (c) 10-40% by weight, component (
d) is 3 to 20% by weight, and the amount of component (c) is 1.5 times or more and less than 7 times the amount of component (d). Composition.
レン単独重合体、エチレン−プロピレンランダム共重合
体、エチレン−プロピレン−ブテンランダム共重合体、
エチレン−プロピレンブロック共重合体またはこれらの
二以上の混合物であるイージーオープン容器のシール材
用樹脂組成物。(2) The composition of claim (1), wherein component a is a propylene homopolymer, an ethylene-propylene random copolymer, an ethylene-propylene-butene random copolymer,
A resin composition for a sealing material of an easy-open container, which is an ethylene-propylene block copolymer or a mixture of two or more thereof.
ポリエチレン、低密度ポリエチレン、もしくは直鎖状低
密度ポリエチレンであるイージーオープン容器のシール
材用樹脂組成物。(3) A resin composition for a sealing material for an easy-open container, which is the composition of claim (1), wherein component b is high-density polyethylene, low-density polyethylene, or linear low-density polyethylene.
ン単独重合体、ゴム変性ポリスチレン、アクリロニトリ
ル−ブタジエン−スチレン共重合体、もしくはこれらの
二以上の混合物であるイージーオープン容器のシール材
用樹脂組成物。(4) A seal for an easy-open container of the composition according to claim (1), wherein component c is a styrene homopolymer, a rubber-modified polystyrene, an acrylonitrile-butadiene-styrene copolymer, or a mixture of two or more thereof. Resin composition for materials.