JPH02255606A - 歯科用セメント材料 - Google Patents
歯科用セメント材料Info
- Publication number
- JPH02255606A JPH02255606A JP1074591A JP7459189A JPH02255606A JP H02255606 A JPH02255606 A JP H02255606A JP 1074591 A JP1074591 A JP 1074591A JP 7459189 A JP7459189 A JP 7459189A JP H02255606 A JPH02255606 A JP H02255606A
- Authority
- JP
- Japan
- Prior art keywords
- dental cement
- aqueous
- cement material
- solution
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
[産業上の利用分野]
本発明は補綴物の合着剤として使用される他、充填材や
裏装材等にも使用される歯科用セメント材料に関し、殊
に硬化性および生体親和性に優れた燐酸カルシウム−水
性練和液系歯科用セメント材料に関するものである。
裏装材等にも使用される歯科用セメント材料に関し、殊
に硬化性および生体親和性に優れた燐酸カルシウム−水
性練和液系歯科用セメント材料に関するものである。
[従来の技術]
歯科用セメント材料は補綴物の合着剤として使用される
他、充填材、裏装材としても使用されており、歯科分野
の修復材料として様々な歯科用セメント材料が開発され
ている。
他、充填材、裏装材としても使用されており、歯科分野
の修復材料として様々な歯科用セメント材料が開発され
ている。
従来の歯科用セメント材料の代表例としては、燐酸亜鉛
セメントが広く使用されている。この歯科用セメント材
料は、酸化亜鉛を主成分とし、その他酸化マグネシウム
、酸化アルミニウム、シリカ等を含んだ粉末剤を、燐酸
を主剤とする液剤と混練することによって反応させ、主
に水に不溶性の第3燐酸亜鉛[Zns (PO4)*
・48xO]を生成させるものである。しかしながらこ
の歯科用セメント材料は口腔内の唾液によって徐々に溶
解する他、歯買に対する接着性や親和性がほとんど無い
ため、適用部位に対する固着状態は機械的保持力に頼る
ものとなっていた。
セメントが広く使用されている。この歯科用セメント材
料は、酸化亜鉛を主成分とし、その他酸化マグネシウム
、酸化アルミニウム、シリカ等を含んだ粉末剤を、燐酸
を主剤とする液剤と混練することによって反応させ、主
に水に不溶性の第3燐酸亜鉛[Zns (PO4)*
・48xO]を生成させるものである。しかしながらこ
の歯科用セメント材料は口腔内の唾液によって徐々に溶
解する他、歯買に対する接着性や親和性がほとんど無い
ため、適用部位に対する固着状態は機械的保持力に頼る
ものとなっていた。
上記燐酸亜鉛セメント以外のセメントとして、酸化亜鉛
粉末とポリアクリル酸の水溶液を混合したカルボキシレ
ートセメントや、アルミノ珪酸塩粉末とポリアクリル酸
を混合したグラスアイオノマーセメント等が知られてい
る。これらの歯科用セメント材料は生体に対する為害作
用が少なく、接着性もある程度期待できるが、上記燐酸
亜鉛セメントと同様生体親和性が不十分であるという欠
点を有していた。
粉末とポリアクリル酸の水溶液を混合したカルボキシレ
ートセメントや、アルミノ珪酸塩粉末とポリアクリル酸
を混合したグラスアイオノマーセメント等が知られてい
る。これらの歯科用セメント材料は生体に対する為害作
用が少なく、接着性もある程度期待できるが、上記燐酸
亜鉛セメントと同様生体親和性が不十分であるという欠
点を有していた。
こうしたことから生体親和性の優れた各種燐酸カルシウ
ム系歯科用セメント材料も開発されており、例えば(、
I )第3燐酸カルシウム−硬化液剤系(開開、上野、
特許第1103653号;開開、後藤、特許第1343
300号;楠ら、特願昭62−83348)、(Iり第
4燐酸カルシウム−第2燐酸カルシウム−燐酸水溶液系
(土井ら、歯科材料・器械、6,53 、1987)、
(III)第2燐酸カルシウム−炭酸カルシウム−水系
(開開、窯業協会誌、95,284;1987 )等が
知られている。
ム系歯科用セメント材料も開発されており、例えば(、
I )第3燐酸カルシウム−硬化液剤系(開開、上野、
特許第1103653号;開開、後藤、特許第1343
300号;楠ら、特願昭62−83348)、(Iり第
4燐酸カルシウム−第2燐酸カルシウム−燐酸水溶液系
(土井ら、歯科材料・器械、6,53 、1987)、
(III)第2燐酸カルシウム−炭酸カルシウム−水系
(開開、窯業協会誌、95,284;1987 )等が
知られている。
[発明が解決しようとする課題]
これまで開発されてきた歯科用セメント材料はそれぞれ
一長一短があり、その用途に応じて使い分ける必要があ
るが、歯科用セメント材料としては硬化性が十分である
ことおよび生体親和性が良好なことの2点が共通の要求
特性であり、これらを両方とも十分に満足するものが望
まれている。
一長一短があり、その用途に応じて使い分ける必要があ
るが、歯科用セメント材料としては硬化性が十分である
ことおよび生体親和性が良好なことの2点が共通の要求
特性であり、これらを両方とも十分に満足するものが望
まれている。
本発明はこうした技術的課題を解決する為になされたも
のであって、その目的は、補綴材や充填材として要求さ
れる十分な硬化性を有すると共に、生体親和性にも優れ
た歯科用セメント材料を提供する点にある。
のであって、その目的は、補綴材や充填材として要求さ
れる十分な硬化性を有すると共に、生体親和性にも優れ
た歯科用セメント材料を提供する点にある。
[課題を解決する為の手段]
上記目的を達成し得た本発明の歯科用セメント材料とは
、α型第3燐酸カルシウムと第2燐酸カルシウム2水和
物を主成分とする粉末と、水性練和液からなる点に要旨
を有するものである。
、α型第3燐酸カルシウムと第2燐酸カルシウム2水和
物を主成分とする粉末と、水性練和液からなる点に要旨
を有するものである。
[作用]
本発明者らは上記要求を満足する歯科用セメント材料の
開発を0指して種々研究を重ねた結果、α型第3燐酸カ
ルシウム(以下、α−TCPと略記することがある)と
第2燐酸カルシウム2水和物(以下、DCPDと略記す
ることがある)を主成分とし、これらが所定の比率とな
る様に混合すると共に、該粉末に硬化液としての水性練
和液を混和することによって、硬化性および生体親和性
のいずれの点においても優れた歯科用セメント材料が実
現できることを見出し、本発明を完成した。
開発を0指して種々研究を重ねた結果、α型第3燐酸カ
ルシウム(以下、α−TCPと略記することがある)と
第2燐酸カルシウム2水和物(以下、DCPDと略記す
ることがある)を主成分とし、これらが所定の比率とな
る様に混合すると共に、該粉末に硬化液としての水性練
和液を混和することによって、硬化性および生体親和性
のいずれの点においても優れた歯科用セメント材料が実
現できることを見出し、本発明を完成した。
本発明で用いる粉末はα−TCPとDCPDを主成分と
する混合粉末であるが、この混合割合はCa / Pモ
ル比で1.20〜1.47の範囲となる様に調整するの
が好ましい、当該モル比が1.20未満若しくは1.4
7を超えると、凝固硬化時間が長くなり、歯科用材料と
して好ましくない、また第3燐酸カルシウムはα型であ
ることが必要であり、β型第3燐酸カルシウムを使用す
ると上記と同様に凝固硬化時間が長くなる。
する混合粉末であるが、この混合割合はCa / Pモ
ル比で1.20〜1.47の範囲となる様に調整するの
が好ましい、当該モル比が1.20未満若しくは1.4
7を超えると、凝固硬化時間が長くなり、歯科用材料と
して好ましくない、また第3燐酸カルシウムはα型であ
ることが必要であり、β型第3燐酸カルシウムを使用す
ると上記と同様に凝固硬化時間が長くなる。
一方硬化液としての水性練和液の種類については特に限
定するものではないが、例えば生理食塩水、有機酸水溶
液、無機酸水溶液、水溶性高分子溶液等が挙げられる。
定するものではないが、例えば生理食塩水、有機酸水溶
液、無機酸水溶液、水溶性高分子溶液等が挙げられる。
尚上記有機酸水溶液とは、例えば不飽和脂肪族カルボン
酸の単独重合体や共重体、或はこれらの酸と他の不飽和
脂肪族単量体の共重合体等を含んだ水溶液の意味であり
、この水溶液を用いる場合はその濃度が80%未満であ
ることが好ましい。これは80%を超えると粘度が著し
く増大し、粉末と練和液とを混合するのが困難となり、
物理的および機械的性質が低下するからである。また上
記水溶性高分子溶液とは、例えばポリビニルアルコール
、ヒドロキシプロピルセルロース、カルボキシメチルセ
ルロース等の高分子を含んだ溶液である。但し、水性練
和液は、水だけを使用する場合を含まない排除する趣旨
であり、水単独を練和液として使用しても歯科用セメン
ト材料として必要とされる物性を得ることは困難である
。
酸の単独重合体や共重体、或はこれらの酸と他の不飽和
脂肪族単量体の共重合体等を含んだ水溶液の意味であり
、この水溶液を用いる場合はその濃度が80%未満であ
ることが好ましい。これは80%を超えると粘度が著し
く増大し、粉末と練和液とを混合するのが困難となり、
物理的および機械的性質が低下するからである。また上
記水溶性高分子溶液とは、例えばポリビニルアルコール
、ヒドロキシプロピルセルロース、カルボキシメチルセ
ルロース等の高分子を含んだ溶液である。但し、水性練
和液は、水だけを使用する場合を含まない排除する趣旨
であり、水単独を練和液として使用しても歯科用セメン
ト材料として必要とされる物性を得ることは困難である
。
この様にして、α−TCPとDCPDを混合した粉末を
適切な水性練和液と混和することによって最適な強度を
有する歯科用セメント材料ができる。これは夫々単独で
は硬化性の低いα−TCPとDCPDが水性練和液の作
用によってアパタイトやオクタカルシウムホスフェート
を容易に形成し、あるいは酸成分とキレート反応し、こ
れが十分に硬化する為と考えられる。尚α−TCPとD
CPDの混合比は上記範囲内で適宜調整することによフ
て硬化時間を調整でき、使用する練和液は所望する物性
を発揮させるために任意に選択すればよい。また混合粉
末と練和液との混合割合については特に限定するもので
はないが、臨床上の修復操作を考慮した場合、1:2〜
3:1程度が適当である。
適切な水性練和液と混和することによって最適な強度を
有する歯科用セメント材料ができる。これは夫々単独で
は硬化性の低いα−TCPとDCPDが水性練和液の作
用によってアパタイトやオクタカルシウムホスフェート
を容易に形成し、あるいは酸成分とキレート反応し、こ
れが十分に硬化する為と考えられる。尚α−TCPとD
CPDの混合比は上記範囲内で適宜調整することによフ
て硬化時間を調整でき、使用する練和液は所望する物性
を発揮させるために任意に選択すればよい。また混合粉
末と練和液との混合割合については特に限定するもので
はないが、臨床上の修復操作を考慮した場合、1:2〜
3:1程度が適当である。
本発明は上述の如く構成されるが、必要によりヒドロキ
シアパタイト、第4燐酸カルシウム、非晶質燐酸カルシ
ウム等を含ませることも可能である。
シアパタイト、第4燐酸カルシウム、非晶質燐酸カルシ
ウム等を含ませることも可能である。
以下本発明を実施例によって更に詳細に説明するが、下
記実施例は本発明を限定する性質のものではなく、前・
後記の趣旨に徴して設計変更することはいずれも本発明
の技術的範囲に含まれるものである。
記実施例は本発明を限定する性質のものではなく、前・
後記の趣旨に徴して設計変更することはいずれも本発明
の技術的範囲に含まれるものである。
[実施例]
実施例1
a−Ca3 (PO4)2 :310gとCaHP
O4” 2H20: 172gを混合してCa / P
モル比が1.33である混合粉末とした。これに、イタ
コン酸(351量%)とアクリル酸(65!量%)から
製造された平均分子量的18000のポリカルボン酸4
0!!量%と酒石酸10重量%および水50重量%から
なる硬化液を、1.5(粉末):1(硬化液)の割合で
加えて37℃に保持したところ、硬化時間5分で24時
間後の圧縮強度が920 Kg/cm2の硬化物が得ら
れた。
O4” 2H20: 172gを混合してCa / P
モル比が1.33である混合粉末とした。これに、イタ
コン酸(351量%)とアクリル酸(65!量%)から
製造された平均分子量的18000のポリカルボン酸4
0!!量%と酒石酸10重量%および水50重量%から
なる硬化液を、1.5(粉末):1(硬化液)の割合で
加えて37℃に保持したところ、硬化時間5分で24時
間後の圧縮強度が920 Kg/cm2の硬化物が得ら
れた。
実施例2
α−TCP:310gとDCPD : 43gを混合し
Ca / Pモル比が1.44の混合粉末とした。これ
にクエン酸0.2重量%とカルボキシヌルセルロースナ
トリウム1重量%を含んだ水性練和液を、2.5(粉末
):1(練和液)の割合で混和したところ、硬化時間6
分、圧縮強度が850kg/CID2であワた。
Ca / Pモル比が1.44の混合粉末とした。これ
にクエン酸0.2重量%とカルボキシヌルセルロースナ
トリウム1重量%を含んだ水性練和液を、2.5(粉末
):1(練和液)の割合で混和したところ、硬化時間6
分、圧縮強度が850kg/CID2であワた。
次に、X線により硬化物を同定したところ、ハイドロキ
シアパタイトとオクタカルシウムホスフェートが生成し
ていることが確認された。
シアパタイトとオクタカルシウムホスフェートが生成し
ていることが確認された。
更に、この歯科用セメントを3週令つィスター系ラット
の大腿骨部2カ所に穿孔した骨髄腔に充填し、3力月後
に切り出して違法に従い研磨薄片を作製して検鏡したと
ころ、セメントの周りを一層の新生骨が取り囲んでいる
ことが認められ、生体親和性の点でも優れていることが
確認された。
の大腿骨部2カ所に穿孔した骨髄腔に充填し、3力月後
に切り出して違法に従い研磨薄片を作製して検鏡したと
ころ、セメントの周りを一層の新生骨が取り囲んでいる
ことが認められ、生体親和性の点でも優れていることが
確認された。
[発明の効果]
以上述べた如く本発明によれば、α型第3燐酸カルシウ
ムと第2燐酸カルシウム2水和物を適切な割合で混合し
た粉末と適切な水性練和液と混和することによって、硬
化性が十分であり且つ生体親和性にも優れた歯科用セメ
ント材料が実現できた。
ムと第2燐酸カルシウム2水和物を適切な割合で混合し
た粉末と適切な水性練和液と混和することによって、硬
化性が十分であり且つ生体親和性にも優れた歯科用セメ
ント材料が実現できた。
Claims (3)
- (1)α型第3燐酸カルシウムと第2燐酸カルシウム2
水和物を主成分とする粉末と、水性練和液からなること
を特徴とする歯科用セメント材料。 - (2)粉末の混合割合が、Ca/Pモル比で1.2〜1
.47である請求項(1)に記載の歯科用セメント材料
。 - (3)練和液が、生理食塩水、不飽和脂肪族カルボン酸
の単独若しくは共重合体水溶液、有機酸単量体水溶液、
無機酸水溶液および水溶性高分子溶液からなる群から選
択される1種または2種以上の混合溶液である請求項(
1)または(2)に記載の歯科用セメント材料。