JPH01168607A - Polishing composition - Google Patents
Polishing compositionInfo
- Publication number
- JPH01168607A JPH01168607A JP32790487A JP32790487A JPH01168607A JP H01168607 A JPH01168607 A JP H01168607A JP 32790487 A JP32790487 A JP 32790487A JP 32790487 A JP32790487 A JP 32790487A JP H01168607 A JPH01168607 A JP H01168607A
- Authority
- JP
- Japan
- Prior art keywords
- wax
- polishing composition
- polymerization
- silicone resin
- low degree
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
[産業上の利用分野]
本発明は三次元網目構造を有する有機シリコン樹脂、低
重合度シリコン油分、及び炭化水素系ワックスを配合し
てなる、グロス光沢に優れ、軽い使用性で、且つベタツ
キの少ないつや出し用組成物に関する。[Detailed Description of the Invention] [Industrial Application Field] The present invention is a light and excellent gloss product made by blending an organic silicone resin with a three-dimensional network structure, a low polymerization degree silicone oil, and a hydrocarbon wax. The present invention relates to a polishing composition that is easy to use and has less stickiness.
[従来の技術]
つや出し用口紅組成物(リップグロス)は単品で使用し
たり、リップスティックを塗った上から塗ワたりして、
唇に光沢(グロス感)を付与するものであり、スティッ
ク状、ポット状と、種々の形態で市販されている。[Prior art] A glossy lipstick composition (lip gloss) can be used alone or applied over lipstick.
It gives gloss to the lips and is commercially available in various forms such as sticks and pots.
グロス効果を付与する油分としては、通常、口紅に好ん
で使われるヒマシ油、オリーブ油、ラノリン類、ポリブ
テン、更にはシュークローズアセテートイソブチレート
のようなシュゴーエステル類等の高粘度油分があげられ
る。しかしいずれの油分も高粘度ゆえに、そのグロス効
果とは背反に、使用性が重く、塗布後にベタツキを感じ
きせるものであった。Examples of oils that impart a glossy effect include high viscosity oils such as castor oil, olive oil, lanolins, polybutenes, and sugar esters such as sucrose acetate isobutyrate, which are commonly used in lipsticks. However, due to the high viscosity of both oils, contrary to their glossy effect, they were difficult to use and felt sticky after application.
軽い使用性で、きっばりした感触のリップグロスは口紅
愛用者にとって待望久しいものであった。Lip glosses that are lightweight and have a firm feel have been long awaited by lipstick users.
このような背反する目標を達成する手段として当業者で
あれば、高粘度のシリコン油分(例えばジメチルポリシ
ロキサンの5000c、s、以上の油分)の配合を思い
付くのは容易である。しかしシリコン系の高粘度油分は
、軽い使用性で、きっばりした感触を示し、グロス効果
のあるものの、通常口紅のメインのワックスである炭化
水素系ワックスときわめて相溶性が悪く、又色材の濡れ
も悪いため、製品化するのが難しく、とりわけリップグ
ロス市場の大半を占めるスティック状、ポット状への応
用は、保型性が得られないため、きわめて難しかった。One skilled in the art can readily envision the formulation of high viscosity silicone oils (eg, dimethylpolysiloxane oils of 5000 c, s or higher) as a means of achieving these contradictory goals. However, although silicone-based high viscosity oils are easy to use, have a firm feel, and have a glossy effect, they are extremely incompatible with hydrocarbon waxes, which are the main waxes used in lipsticks, and are also difficult to use as colorants. It is difficult to commercialize lip gloss because of its poor wettability, and in particular, it has been extremely difficult to apply it to stick and pot shapes, which account for the majority of the lip gloss market, because it does not retain its shape.
[発明が解決しようとす問題点]
本発明は、その重合方向が線状でな(、三次元方向であ
り、従って炭化水素系ワックスと相溶性のよい有機シリ
コン系樹脂を、やはり同様に炭化水素系ワックスと相溶
性の良い低重合度のシリコン油分に溶解し、適度の粘性
(好ましくは5ooo〜20000c、s)をもった溶
液をつくり、それを主基剤として配合することにより、
軽い使用性で、きっばりした感触で、グロス効果のある
スティック状、若しくはポット状のリップグロスを得る
ことを目標としている。すなわち炭化水素系のワックス
を溶解する高粘度のシリコン油分を開発したところから
本発明はスタートする。[Problems to be Solved by the Invention] The present invention is directed to carbonizing an organic silicon resin whose polymerization direction is not linear (or three-dimensional) and is therefore highly compatible with hydrocarbon waxes. By dissolving in silicone oil with a low degree of polymerization that has good compatibility with hydrogen wax and creating a solution with an appropriate viscosity (preferably 500 to 20,000 c, s), and blending it as the main base,
The aim is to obtain a stick-shaped or pot-shaped lip gloss that is light in use, has a firm feel, and has a glossy effect. That is, the present invention starts from the development of a high viscosity silicone oil that dissolves hydrocarbon wax.
[問題点を解決するための手段]
すなわち本発明は、平均式(A)の単位からなる有機シ
リコン樹脂と、一般式(B)で示される低重合度シリコ
ン油分と、炭化水素系ワックスとを必須成分とすること
を特徴とするつや出し用組成物である。[Means for Solving the Problems] That is, the present invention comprises an organic silicone resin consisting of units of average formula (A), a low degree of polymerization silicone oil represented by general formula (B), and a hydrocarbon wax. This is a polishing composition characterized by containing the present invention as an essential component.
(A) Rn S i O(4−n)/2(Rは炭素数
1〜6のアルキル基又はフェニル基を表し、nは1.0
〜1.8までの値を示す)(nは1〜20の整数、Rは
炭素数は1〜6までのアルキル基及びフェニル基を表わ
す)以下、本発明の構成について詳述する。(A) Rn S i O(4-n)/2 (R represents an alkyl group having 1 to 6 carbon atoms or a phenyl group, and n is 1.0
-1.8) (n is an integer of 1 to 20, R represents an alkyl group having 1 to 6 carbon atoms and a phenyl group) Hereinafter, the structure of the present invention will be explained in detail.
本発明で用いる有機シリコン樹脂はR35iO単位、R
25iO単位、R31O単位及びSiO□単位の適当な
組合せからなり、その割合は平均式Rn5iO(nは1
.0〜1.8までの値を示す。)を満足するように選ば
れる。分子量は1500〜200000までが望ましい
。The organosilicon resin used in the present invention has R35iO units, R
It consists of an appropriate combination of 25iO units, R31O units and SiO□ units, and the ratio is determined by the average formula Rn5iO (n is 1
.. Indicates a value from 0 to 1.8. ) is selected to satisfy the following. The molecular weight is preferably from 1,500 to 200,000.
上記有機シリコン樹脂はベンゼンに可溶であり、各種の
方法で製造しうる。−例を挙げると、一般式R35iX
、 R25iX2、R51X3及びSiX+ (X ハ
加水分解しうる基、例えば塩素、臭素、弗素、アルコキ
シ例えばメトキシ、エトキシ等の基、アシロキシ基をし
めす。)で示される化合物を、目的とする樹脂組成に応
じて、トルエン、ベンゼン、キシレンなどの適当な溶媒
に添加し、次いでこの溶媒を適当な酸性溶媒中における
希望する加水分解および共縮合を得るに十分な量の水中
に加える。こうして得られた二相系から水相を除去し、
残留する樹脂状物質を重炭酸ナトリウムあるいは他のア
ルカリ性物質の十分量を用いて中和し、溶媒を留去すれ
ば目的の有機シリコン樹脂が得られる。The above organosilicon resin is soluble in benzene and can be produced by various methods. -For example, general formula R35iX
, R 25iX 2 , R 51 and a suitable solvent such as toluene, benzene, xylene, etc., which is then added to a sufficient amount of water to obtain the desired hydrolysis and cocondensation in a suitable acidic solvent. removing the aqueous phase from the two-phase system thus obtained;
The remaining resinous material is neutralized with a sufficient amount of sodium bicarbonate or other alkaline material, and the solvent is distilled off to yield the desired organosilicon resin.
本発明における有機シリコン樹脂の配合量は、樹脂の組
成によっても異なるが、つや出し用組成物全量中10〜
90′重量%、好ましくは30〜60重量%である。The blending amount of the organosilicon resin in the present invention varies depending on the composition of the resin, but is 10 to 10% of the total amount of the polishing composition.
90'% by weight, preferably 30-60% by weight.
本発明における低重合度のシリコン油分はジメチルポリ
シロキサンおよびメチルフェニルポリシロキサンの一般
式においてnの値が20以下、好ましくは3〜15のも
のである。nが20より大きくなると、炭化水素系ワッ
クスとの相溶性が悪く、相分離を生じたり、保型性を保
てなかったりする。The low degree of polymerization silicone oil in the present invention has a value of n of 20 or less, preferably 3 to 15 in the general formula of dimethylpolysiloxane and methylphenylpolysiloxane. When n is larger than 20, compatibility with hydrocarbon waxes is poor, resulting in phase separation or failure to maintain shape retention.
本発明における有機シリコン樹脂と低重合度のシリコン
油分の割合は、樹脂の組成、分子量、油分の重合度等に
より異なり、その混合粘度が3000〜200000c
、s、に調整きれていれば良い。The ratio of organic silicone resin and silicone oil with a low degree of polymerization in the present invention varies depending on the composition of the resin, molecular weight, degree of polymerization of the oil, etc., and the mixed viscosity is 3000 to 200000c.
, s, as long as it is properly adjusted.
本発明における炭化水素系ワックスは、一般に化粧料等
に用いられるものであれば何でもよく、マイクロクリス
タリンワックス、ポリエチレンワックス、セレシンワッ
クス等が挙げられる。炭化水素系ワックスの配合量は、
油分に対する固化力によっても異なるが、つや出し用組
成物全量中の0゜5〜25重量%、好ましくは3〜10
重量%である。0゜5重量%未満であると、保型性が保
てず、25重量%を越えると、グロス光沢が失われる。The hydrocarbon wax in the present invention may be any wax that is generally used in cosmetics, and examples thereof include microcrystalline wax, polyethylene wax, ceresin wax, and the like. The amount of hydrocarbon wax is
Although it varies depending on the solidifying power for oil, it is 0.5 to 25% by weight, preferably 3 to 10% by weight based on the total amount of the polishing composition.
Weight%. If it is less than 0.5% by weight, shape retention cannot be maintained, and if it exceeds 25% by weight, gloss is lost.
本発明のつや出し用組成物には発明の効果を損なわない
範囲で、必要に応じ、ワックス、油分、水、保湿剤、界
面活性剤、顔料、樹脂、粘土鉱物、酸化防止剤、防腐剤
、紫外線防止剤、香料等を配合することかで伊る。The polishing composition of the present invention may contain wax, oil, water, humectants, surfactants, pigments, resins, clay minerals, antioxidants, preservatives, and ultraviolet rays, as necessary, to the extent that the effects of the invention are not impaired. This can be done by adding inhibitors, fragrances, etc.
[発明の効果]
本発明のつや出し用組成物は、有機シリコン樹脂、低重
合度シリコン油分、および炭化水素系ワックスを配合し
た、のびが軽<、すつばりき等の感触に優れたスティッ
ク状、若しくはポット状のつや出し用組成物である。[Effects of the Invention] The polishing composition of the present invention contains an organic silicone resin, a low degree of polymerization silicone oil, and a hydrocarbon wax, and is in the form of a stick that spreads easily and has an excellent feel such as smoothness. Or it is a pot-shaped polishing composition.
[実施例]
次に実施例によって本発明を更に詳しく説明する。本発
明はそれによって限定されるものではない。配合量は重
量%である。実施例に先たち効果試験方法及び評価基準
について説明する。[Example] Next, the present invention will be explained in more detail with reference to Examples. The invention is not limited thereby. The blending amount is in weight%. The effectiveness test method and evaluation criteria will be explained in Examples.
11 ◆
単品及び組合せた油分中、10%濃度にてワックスを仕
込み、90℃に加熱し溶解する。その際ワックスと透明
に溶けあうものを01不透明もしくは二層分離を示すも
のを×で示した。11 ◆ Add wax at a concentration of 10% to the oil components alone or in combination, and heat to 90°C to dissolve. In this case, those that dissolve transparently with wax are shown as 0, and those that are opaque or exhibit two-layer separation are shown as x.
王且庄
べたつき、きっばりざ、使用性の軽ざについて18〜3
5才までの女性50名による官能評価を行なった。各項
目とも5段階評価とし、50人の平均が4.2以上のも
のを0,4.1〜3.5までを口、3.4〜2.6まで
をΔ、2.5以下を×とした。About stickiness, stiffness, and lightness of usability 18-3
Sensory evaluation was conducted by 50 females aged up to 5 years. Each item is evaluated on a 5-point scale, with the average of 50 people being 4.2 or higher as 0, 4.1 to 3.5 as Δ, 3.4 to 2.6 as Δ, and 2.5 or less as ×. And so.
−グユLス」l良
サンプルを硫酸紙上に塗布し、日本電色工業KK製グロ
スメーターにより測定し、基準光沢板に比べての光沢度
を%で示す。A good sample of "Guyu L" was coated on parchment paper and measured using a gloss meter manufactured by Nippon Denshoku Kogyo KK, and the degree of gloss compared to a standard glossy plate is expressed in %.
実施例1、比較例1,2
表−1に示す処方に基づきリップグロスを調製し、相溶
性、使用性、グロス効果について評価した。Example 1, Comparative Examples 1 and 2 Lip glosses were prepared based on the formulations shown in Table 1, and evaluated for compatibility, usability, and gloss effect.
(以下余白)
表−1かられかるようにグロス感についてはいずれのサ
ンプルも十分にあるが、ラノリンやポリブテンを配合し
た比較例1のリップグロスは、ベタツキがあり、のびが
重い。又、ジメチルポリシロキサン(n = 500)
を配合したリップグロスは炭化水素系ワックスと相溶性
が悪く、製品の形態をなきない。本発明によるリップグ
ロスは、炭化水素系ワックスと油分の相溶性がよく、シ
リコンの特徴である、ざっばりざ、軽い使用性を十分に
具現化したものであり、従来のリップグロスの°“ツヤ
ツヤだけどベタベダ゛の概念を一掃するものであった。(The following is a blank space) As can be seen from Table 1, all the samples have sufficient glossiness, but the lip gloss of Comparative Example 1 containing lanolin and polybutene is sticky and spreads easily. Also, dimethylpolysiloxane (n = 500)
Lip glosses containing this product have poor compatibility with hydrocarbon waxes, and the product loses its shape. The lip gloss according to the present invention has good compatibility with hydrocarbon wax and oil, and fully embodies the smoothness and lightness of use that are characteristic of silicone, and has the same gloss and gloss of conventional lip glosses. However, it was something that wiped away the concept of stickiness.
実施例2 ペースト状リップグロス
マイクロクリスタリンワックス 12.0ワセリ
ン 20.0シリコンKF
56 ※−120,0有機シリコン樹脂 ※−24
7,0
雲母チタン 0.9香料
0.1計
ioo、。Example 2 Paste lip gloss microcrystalline wax 12.0 Vaseline 20.0 Silicone KF
56 *-120,0 Organic silicone resin *-24
7.0 Mica titanium 0.9 Fragrance
0.1 total
ioo,.
※−1信越化学KK製 ジメチルポリシロキサン※−2
約3000の分子量を有し、且つ(C)13) 3si
01/2単位:5i02単位= 0.8 :1からなる
平均式(CH3) 1.33siO+、 34で表され
る有機シリコン樹脂。*-1 Dimethylpolysiloxane manufactured by Shin-Etsu Chemical KK *-2
has a molecular weight of about 3000, and (C)13) 3si
An organic silicone resin represented by the average formula (CH3) 1.33siO+, 34 consisting of 01/2 units: 5i02 units = 0.8:1.
(製法)有機シリコン樹脂をシリコンKF56に溶解し
、粘性のある透明の溶液を得る。ついで、ワックスを添
加して90℃にて溶解する。更に雲母チタン、香料を添
加し、85℃で分散混合する。脱気後、チューブ状容器
に充填する。実施例2は表−2のスコアが示すように、
べたつきがなり、キっばりした感触で、使用性も軽く、
グロス効果も十分であった。(Manufacturing method) An organic silicone resin is dissolved in silicone KF56 to obtain a viscous and transparent solution. Then, wax is added and melted at 90°C. Further, titanium mica and fragrance are added and dispersed and mixed at 85°C. After degassing, fill into a tube-shaped container. As shown in the scores in Table 2, Example 2
It is sticky, has a firm feel, and is easy to use.
The gloss effect was also sufficient.
(以下余白)
(製法)
実施例2に準じる。製造後、所定のスティック容器に充
填する。(Left below) (Manufacturing method) According to Example 2. After manufacturing, it is filled into designated stick containers.
実施例3は表−2のスコアが示すように、べたつきがな
く、ざっばりした感触で、使用性も軽く、グロス効果も
十分であった。しかし比較例3は、ざっばりした感触で
はあるが、ワックスがメインオイルであるシリコンKF
98Hに溶解しないため、均一な組成になりえない。又
、比較例4はグロス効果はあるものの、重い使用性であ
り、ベタツキを感じるものであった。As shown by the scores in Table 2, Example 3 had no stickiness, had a smooth feel, was easy to use, and had a sufficient gloss effect. However, Comparative Example 3 has a rough feel, but silicone KF whose main oil is wax.
Since it does not dissolve in 98H, it cannot have a uniform composition. Although Comparative Example 4 had a gloss effect, it was difficult to use and felt sticky.
実施例4 乳化リップグロス
ポリエチレンワックス 6.0セレシン
ワツクス 5.0ジメチルポリシ
ロキサン(n=1〜2) 10.0有機シリコン
樹脂※−170,0
精製水 5.0ラポナイ
トXLG ※−21,0
シリコンKF945 ※−30.5dl−ピロリド
ンカルボン酸 0.3グリセリン
0.7酸化鉄赤
0.2二酸化チタン
0.5青色1号 0.
1エチルパラベン 0,3ジブ
チルヒドロキシトルエン 0.1香 料
0.3
計 100
.0※−1約分子量5000、(CH3)3siOt/
2単位: (CsHs) 2SiO単位” (CsHs
)Si02/3単位: 5i02単位= 0.9 :
0.1 : 0.2 : 1.0からなる平均式%式%
機シリコン樹脂
※−2英国ラボルテ社製合成へクトライト※−3信越化
学製ポリエーテル変性
ジメチルポリシロキサン
(製法)
有機シリコン樹脂にジメチルポリシロキサンを加え、ペ
ースト化し、ワックス、顔料、防腐剤、酸化防止剤、更
にシリコンKF945を添加し、90℃にて分散する。Example 4 Emulsified lip gloss polyethylene wax 6.0 Ceresin wax 5.0 Dimethylpolysiloxane (n=1-2) 10.0 Organic silicone resin *-170.0 Purified water 5.0 Laponite XLG *-21.0 Silicone KF945 *-30.5dl-pyrrolidonecarboxylic acid 0.3glycerin
0.7 iron oxide red
0.2 titanium dioxide
0.5 Blue No. 1 0.
1 Ethylparaben 0,3 Dibutylhydroxytoluene 0.1 Fragrance 0.3
Total 100
.. 0*-1 approximately molecular weight 5000, (CH3)3siOt/
2 units: (CsHs) 2SiO units” (CsHs
)Si02/3 unit: 5i02 unit = 0.9:
Average formula % formula consisting of 0.1 : 0.2 : 1.0 Machine silicone resin *-2 Synthetic hectorite manufactured by Laborte, UK *-3 Polyether-modified dimethylpolysiloxane manufactured by Shin-Etsu Chemical (manufacturing method) Organic silicone resin Dimethylpolysiloxane is added to form a paste, wax, pigment, preservative, antioxidant, and silicone KF945 are added and dispersed at 90°C.
次いでラポナイトを加え、同様に分散する。85℃にて
水、保湿剤を徐々に添加し、ホモミキサーにて分散する
。脱気後、香料を添加し、ゆるやかに撹拌する。80℃
にて、所定スティック状容器に充填、同化きせる。Laponite is then added and dispersed in the same manner. Water and a humectant were gradually added at 85°C and dispersed using a homomixer. After degassing, add the fragrance and stir gently. 80℃
Fill it into a designated stick-shaped container and assimilate it.
実施例4は表−2のスコアが示すように、べたつ沙がな
く、ざっばりした感触で、使用性も軽く、グロス効果も
十分なスティック状リップグロスであった。As shown by the scores in Table 2, Example 4 was a stick-like lip gloss that was not sticky, had a smooth feel, was easy to use, and had a sufficient gloss effect.
尚、比較例3は、相溶性が悪いため、化粧料としての形
態をとれない。Note that Comparative Example 3 cannot be used as a cosmetic because of poor compatibility.
特許出願人 株式会社 資生堂Patent applicant: Shiseido Co., Ltd.
Claims (1)
、一般式(B)で示される低重合度シリコン油分と、炭
化水素系ワックスとを必須成分とすることを特徴とする
つや出し用組成物。 (A)RnSiO_(_4_−_n_)_/_2(Rは
炭素数1〜6のアルキル基又はフェニル基を表し、nは
1.0〜1.8までの値を示す) (B)▲数式、化学式、表等があります▼ (nは1〜20の整数、Rは炭素数は1〜6までのアル
キル基及びフェニル基を表わす)(1) A polishing composition characterized by containing as essential components an organic silicone resin consisting of units of average formula (A), a low degree of polymerization silicone oil represented by general formula (B), and a hydrocarbon wax. thing. (A) RnSiO_(_4_-_n_)_/_2 (R represents an alkyl group having 1 to 6 carbon atoms or a phenyl group, and n represents a value from 1.0 to 1.8) (B) ▲ Formula, Chemical formulas, tables, etc. are available▼ (n is an integer from 1 to 20, R represents an alkyl group or phenyl group with carbon numbers of 1 to 6)