JPH01165665A - Rubber-asphalt composition for underlying material - Google Patents
Rubber-asphalt composition for underlying materialInfo
- Publication number
- JPH01165665A JPH01165665A JP32490387A JP32490387A JPH01165665A JP H01165665 A JPH01165665 A JP H01165665A JP 32490387 A JP32490387 A JP 32490387A JP 32490387 A JP32490387 A JP 32490387A JP H01165665 A JPH01165665 A JP H01165665A
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- asphalt
- paper
- tar
- underlying material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】
（技術分野）
この発明は、下地材用ゴム・アスファルト組成物に関す
るものである。さらに詳しくは、この発明は、高温時の
バインダー性能が良好で、施工性に優れ、かつ施工後の
釘穴からの漏れに対する耐水シール性も良好な下地材用
ゴム・アスファルト組成物に関するものである。DETAILED DESCRIPTION OF THE INVENTION (Technical Field) This invention relates to a rubber/asphalt composition for base material. More specifically, the present invention relates to a rubber/asphalt composition for base materials that has good binder performance at high temperatures, excellent workability, and good water-resistant sealing properties against leakage from nail holes after construction. .
（背景技術）
従来より、屋根や外装材の下地材としてアスファルトフ
ェルト紙、タール含浸クレープ紙、軟質ポリ塩１ヒビニ
ルシート、不織布等にアスファルトまたはゴム・アスフ
ァルトバインダー層を配設して積層したものや撒布砂の
層を設けたものなどが知られている。(Background technology) Conventionally, materials such as asphalt felt paper, tar-impregnated crepe paper, soft polysalt 1-hibinyl sheet, and nonwoven fabrics with asphalt or a rubber/asphalt binder layer arranged and laminated or sprayed have been used as base materials for roofs and exterior materials. Some examples include those with a layer of sand.
特に、ゴム・アスファルト混合物からなるバインダーは
、アスファルトに粘弾性を付与し、上記の各種の紙、レ
ート、砂、不織布等の被着体の剥離、離脱を防止するこ
とを目的に開発されたものである。In particular, binders made of rubber and asphalt mixtures have been developed with the purpose of imparting viscoelasticity to asphalt and preventing the peeling and detachment of adherends such as the various papers, plates, sand, and nonwoven fabrics mentioned above. It is.
しかしながら、この従来のゴム・アスファルトを用いた
下地材の場合でも、高温（７０〜８０℃）時には粘接着
力が急激に低下し、下地材としての機能を失うという問
題があり、これを改善するための対策が強く求められて
いた。However, even with this conventional base material using rubber and asphalt, there is a problem that the adhesive strength rapidly decreases at high temperatures (70 to 80 degrees Celsius) and it loses its function as a base material. There was a strong need for countermeasures.
たとえば、添付した第１１図に示した下地材においては
、タールをき浸させたクレープ紙（ア）をゴム・アスフ
ァルトバインダー層（イ）を介して軟質ポリ塩化ビニル
シート（つ）を積層一体止しているが、この下地材を屋
根に用いる場合には、真夏時にはその温度は７０〜８０
℃もの高温にな、す、この高温条件によって下地材のゴ
ム・アスファルトバインダー層（イ）の粘接着力は急激
に低下する。このためタール含浸クレープ紙（ア）およ
び軟質ポリ塩化ビニルシート（つ）は剥離、脱落してし
まう。For example, in the base material shown in the attached Figure 11, tar-soaked crepe paper (A) is laminated with a soft polyvinyl chloride sheet (2) through a rubber/asphalt binder layer (B). However, when this base material is used for roofs, the temperature is 70 to 80 degrees in midsummer.
When the temperature is as high as ℃, the adhesive strength of the rubber/asphalt binder layer (a) of the base material decreases rapidly due to these high temperature conditions. As a result, the tar-impregnated crepe paper (A) and the soft polyvinyl chloride sheet (T) peel off and fall off.
また、下地材施工後には、第５図に示したように、粘接
着力の急激な低下によって針穴（１）部の耐水シール性
能は著しく低下し、夏の夕立ち時などにはこの針穴から
の漏水が避けられない。In addition, after the base material is installed, as shown in Figure 5, the water-resistant sealing performance of the needle hole (1) part decreases significantly due to a sudden drop in adhesive strength, and during summer showers, etc. Water leakage is unavoidable.
このため、従来の下地材においては、ゴム・アスファル
トバインダーの高温時の粘接着力の低下と、それによる
耐水シール性能、さらには施工性の低下を防止するため
の改善策が必要とされていた。For this reason, in conventional base materials, improvement measures were needed to prevent the decline in the adhesive strength of the rubber/asphalt binder at high temperatures and the resulting decline in water-resistant sealing performance and workability. .
（発明の目的）
この発明は、以上の通りの事情に鑑みてなされたもので
あり、従来の下地材、特にゴム・アスファルトバインダ
ーの欠点を改善し、高温時の密着強度の低下を防止し、
耐水シール性能を向上させた、改良された下地材用のゴ
ム・アスファルト組成物を提供することを目的としてい
る。(Objective of the Invention) This invention was made in view of the above-mentioned circumstances, and aims to improve the drawbacks of conventional base materials, especially rubber and asphalt binders, prevent the decrease in adhesion strength at high temperatures,
The purpose of the present invention is to provide an improved rubber/asphalt composition for base materials that has improved water-resistant sealing performance.
（発明の開示）
この発明の下地材用組成物は、上記の目的を実現するた
めに、高分子エラストマーを配合して変性したゴム・ア
スファルトからなることを特徴としている。(Disclosure of the Invention) In order to achieve the above object, the base material composition of the present invention is characterized in that it is made of rubber/asphalt modified by blending a polymer elastomer.
以下、この発明の下地材用ゴム・アスファルト組成物に
ついて詳しく説明する。Hereinafter, the rubber/asphalt composition for base materials of the present invention will be explained in detail.
この発明の組成物である変性ゴム・アスファルトは、ゴ
ム・アスファルトに高分子エラストマーを配合したもの
であるが、そのための高分子エラストマーとしては、エ
チレン−エチルアクリレ−１−（ＥＥＡ）、エチレン−
酢酸ビニル（ＥＶＡ）、ウレタン等のエラストマーの１
種または２種以上を用いることができる。もちろん、こ
れ以外の高分子エラストマーも用いることができるが、
下地材の高温時の性能の向上の面では、このＥＥＡ、Ｅ
ＶＡ、ウレタンの高分子エラストマーは好ましいもので
ある。The modified rubber/asphalt that is the composition of this invention is a rubber/asphalt blended with a polymer elastomer. Examples of the polymer elastomer for this include ethylene-ethyl acrylate-1-(EEA), ethylene-ethyl acrylate-1-(EEA),
1 of elastomers such as vinyl acetate (EVA) and urethane
A species or two or more species can be used. Of course, other polymer elastomers can also be used, but
In terms of improving the performance of the base material at high temperatures, EEA and E
VA, urethane polymeric elastomers are preferred.
これらの高分子エラストマーは、ゴム・アスファルトに
対して、全配合物のおよそ３〜２０重量％程度の割合で
配合し、ゴム・アスファルトを変性することが好ましい
。より好ましくは５〜１５重量％で配合する。These polymeric elastomers are preferably blended into the rubber/asphalt at a ratio of about 3 to 20% by weight of the total composition to modify the rubber/asphalt. More preferably, it is blended in an amount of 5 to 15% by weight.
このような変性ゴム・アスファルトバインダーは、その
実際の使用にあたっては、タール含浸クレープ紙、軟質
ポリ塩化ビニルシート、アスファルトフェルト紙、ター
ル含浸フェルト紙等の被着体に、バインダーの変性ゴム
・アスファルトを塗布し、次いで、その上に同種または
他の紙、布等を配したものとすることができる。その実
際の例を示したものが第１図および第２図である。When such a modified rubber/asphalt binder is actually used, the modified rubber/asphalt binder is applied to an adherend such as tar-impregnated crepe paper, soft polyvinyl chloride sheet, asphalt felt paper, or tar-impregnated felt paper. It can be applied and then the same or other paper, cloth, etc. can be placed thereon. Actual examples thereof are shown in FIGS. 1 and 2.
第１図に示した例の場合には、タール含浸クレープ紙（
１）に高分子エラストマーの配合によって変性したゴム
・アスファルトバインダー層（２）を配設し、その上に
軟質ポリ塩化ビニルシート（３）を設けている。この下
地材の場合には、変性ゴム・アスファルトバインダー層
（２）を設けていることから、高温時の粘接着力低下に
よるタール含浸クレープ紙（１）および軟質ポリ塩化ビ
ニルシート（３）の剥離はない、下地材の施工後の針穴
からの漏水も防止される。In the example shown in Figure 1, tar-impregnated crepe paper (
A rubber/asphalt binder layer (2) modified by blending a polymer elastomer is provided on 1), and a flexible polyvinyl chloride sheet (3) is provided on top of the layer (2). In the case of this base material, since the modified rubber/asphalt binder layer (2) is provided, the tar-impregnated crepe paper (1) and the soft polyvinyl chloride sheet (3) will peel off due to a decrease in adhesive strength at high temperatures. It also prevents water from leaking from the needle holes after the base material is installed.
また、第２図は、タール含浸フェルト紙（４）および変
性ゴム・アスファルトバインダー層（２）の上に、不繊
布（５）を配設した例を示している。Furthermore, FIG. 2 shows an example in which a nonwoven fabric (5) is disposed on the tar-impregnated felt paper (4) and the modified rubber/asphalt binder layer (2).
この場合にも、高温時の下地材の性能低下は効果的に防
止されることになる。In this case as well, deterioration in the performance of the base material at high temperatures can be effectively prevented.
次にこの発明の実施例を示し、さらに詳しくこの発明の
下地材について説明する。Next, examples of the present invention will be shown, and the base material of the present invention will be explained in more detail.
（実施例１〜４）
タール含浸クレープ紙に、表１の高分子エラストマーに
よって変性したアスファルトをあらかじめ２００〜２３
０°Ｃで、３０〜６０分間かけて溶融させ、ロールコー
タ−にて含浸塗布し、７０〜９０μｍのＪＷさとした後
にただちに第１図と同様に軟質塩化ビニルシート（０，
１１３−０，２８１１ｍ ）をラミネートした。(Examples 1 to 4) Tar-impregnated crepe paper was coated with asphalt modified with the polymer elastomer shown in Table 1 in advance at 200 to 23
After melting at 0°C for 30 to 60 minutes and impregnating and coating with a roll coater to obtain a JW of 70 to 90 μm, a soft vinyl chloride sheet (0,
113-0,2811m) was laminated.
得られたラミネート品を常温で放置して接着強度と漏水
に対する性能を評価した。その結果も表１に示した。The resulting laminate was left at room temperature and its adhesive strength and performance against water leakage were evaluated. The results are also shown in Table 1.
比較のために変性ゴム・アスファルトを用いない場合に
ついても同様にしてその性能を評価した。For comparison, the performance was evaluated in the same manner when no modified rubber or asphalt was used.
、表１に示した結果から明らかなように、この発明の場
合には接着強度は良好である。As is clear from the results shown in Table 1, the adhesive strength of the present invention is good.
また、漏水に対するシール性能もこの発明の場合には極
めて良好である。Furthermore, the sealing performance against water leakage is also extremely good in the case of the present invention.
なお、密着強度は、各温度（５０℃、６０℃、７０℃）
での剪断強度の測定を行って評価した。In addition, the adhesion strength is determined at each temperature (50°C, 60°C, 70°C).
The shear strength was measured and evaluated.
また、漏水は、第３図に示したように、ラミネート品を
１０１１／ｌＩコンパネに３６ ｍ／ｎの釘で打ちつけ
、常温と８０℃で水のシャワーを１分間放水後の打部の
漏水状態を目視で観察し、釘（６）を中心とする同心円
上の漏水浸透幅（Ｊ ）を測定して評価した。In addition, as shown in Figure 3, water leakage was determined by nailing the laminated product to the 1011/lI control panel with a 36 m/n nail, and checking the leakage state of the striking part after showering with water for 1 minute at room temperature and 80°C. was visually observed, and the water leakage penetration width (J) on a concentric circle centered on the nail (6) was measured and evaluated.
表１
（注）
１）モノマー含量 ７％
２）モノマー含量 １８％
３）モノマー含ＪＬ １５％
４）クレープ紙／軟質ポリ塩１ヒビニルシート間の剪断
強度
（実施例５〜１２）
実施例１〜４と同様にして、表２の配合量で高分子エラ
ストマーを配合して変性したゴム・アスファルトを用い
、剪断強度と漏水状態を評価した。Table 1 (Note) 1) Monomer content 7% 2) Monomer content 18% 3) Monomer-containing JL 15% 4) Shear strength between crepe paper/soft polysalt 1 hibinyl sheet (Examples 5 to 12) Examples 1 to 4 In the same manner as above, shear strength and water leakage state were evaluated using rubber asphalt modified by blending a polymer elastomer in the blending amount shown in Table 2.
その結果を表２に示した。The results are shown in Table 2.
高温時においても剪断強度が極めて良好であることがわ
かる。また、エラストマーの配合割合は、ゴム・アスフ
ァルトに対して、全配合量のおよそ５〜１５重量％程度
が好ましいこともわかる。It can be seen that the shear strength is extremely good even at high temperatures. It can also be seen that the blending ratio of the elastomer is preferably approximately 5 to 15% by weight of the total blending amount relative to the rubber/asphalt.
表２
（実施例１３〜１６）
実施例１〜４と同様にして、第２図に示したタール含浸
フェルト紙および不織布（０，２ａｍポリエステル）と
、変性ゴム・アスファルトのラミネート品を作成した。Table 2 (Examples 13 to 16) In the same manner as Examples 1 to 4, laminates of the tar-impregnated felt paper and nonwoven fabric (0.2 am polyester) shown in FIG. 2, and modified rubber/asphalt were created.
６０℃、７０℃での剪断強度と漏水状態を評価した。ま
た比較のために、変性ゴム・アスファルトを用いない場
合についても同様に評価した。The shear strength and water leakage state at 60°C and 70°C were evaluated. For comparison, a case in which no modified rubber or asphalt was used was also evaluated in the same manner.
表３にその結果を示した。Table 3 shows the results.
この発明のラミネート品の性能は良好であり、特に、漏
水状態は向上している。The performance of the laminate product of this invention is good, and in particular, the water leakage condition is improved.
表３
＊：不織布破壊
（発明の効果）
以上詳しく説明した通り、この発明の高分子エラストマ
ーによって変性したゴム・アスファルトは、高温時の紙
、シート、砂等の接着強度を向上させ、耐水シール性能
についても良好なものとする。Table 3 *: Destruction of nonwoven fabric (effects of the invention) As explained in detail above, the rubber/asphalt modified with the polymer elastomer of this invention improves the adhesive strength of paper, sheets, sand, etc. at high temperatures, and has excellent water-resistant sealing performance. It shall also be in good condition.
この発明の組成物は、従来の下地材の欠点を改善し、高
性能な下地材が提供される。The composition of the present invention improves the drawbacks of conventional base materials and provides a high-performance base material.
第１図は、この発明の一実施例を示した断面図である。
第２図は、他の実施例を示した断面図である。
第３図は、漏水評価の方法を示した平面図である。第４
図および第５図は、従来の下地材の例を示した断面図で
ある。
１・・・タール含浸クレープ紙
２・・・変性ゴム・アスファルトバインダー層３・・・
軟質塩化ビニルシート
４・・・タール含浸フェルト紙
５・・・不織布 ６・・・釘
第 １ 図
第 ３ 図
第 ４ 図
つ
第 ５ 図FIG. 1 is a sectional view showing one embodiment of the present invention. FIG. 2 is a sectional view showing another embodiment. FIG. 3 is a plan view showing a method of water leakage evaluation. Fourth
FIG. 5 is a sectional view showing an example of a conventional base material. 1...Tar-impregnated crepe paper 2...Modified rubber/asphalt binder layer 3...
Soft vinyl chloride sheet 4...Tar-impregnated felt paper 5...Nonwoven fabric 6...Nails Figure 1 Figure 3 Figure 4 Figure 5
Claims (2)
スファルトからなることを特徴とする下地材用ゴム・ア
スファルト組成物。(1) A rubber/asphalt composition for base materials, characterized by comprising rubber/asphalt modified by blending a polymer elastomer.
全配合物の３〜２０重量％配合した特許請求の範囲第（
１）項記載の下地材用ゴム・アスファルト組成物。(2) Claim No. 3 in which the polymer elastomer is blended in an amount of 3 to 20% by weight of the total blend with rubber and asphalt (
1) Rubber/asphalt composition for base material as described in item 1).