JP7413857B2 - ゴム組成物 - Google Patents
ゴム組成物 Download PDFInfo
- Publication number
- JP7413857B2 JP7413857B2 JP2020045112A JP2020045112A JP7413857B2 JP 7413857 B2 JP7413857 B2 JP 7413857B2 JP 2020045112 A JP2020045112 A JP 2020045112A JP 2020045112 A JP2020045112 A JP 2020045112A JP 7413857 B2 JP7413857 B2 JP 7413857B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- weight
- monomer
- rubber composition
- aliphatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
1)樹脂原料
ジシクロペンタジエン:富士フィルム和光純薬製試薬。
スチレン:富士フィルム和光純薬製試薬。
インデン:富士フィルム和光純薬製試薬。
トルエン:富士フィルム和光純薬製試薬、超脱水グレード。
ペンタン:富士フィルム和光純薬製試薬。
イソプレン:富士フィルム和光純薬製試薬。
ピペリレン:富士フィルム和光純薬製試薬。
所定の組成となるように重合に用いる原料を調製した。原料の組成を表1に示す。なお、表1中のDCPDはジシクロペンタジエンの略記である。
シクロペンタジエンはジシクロペンタジエンを200℃で熱分解し使用した。
重合触媒:三フッ化ホウ素ブタノール(ステラケミファ製)。
重合触媒:三フッ化ホウ素フェノール(ステラケミファ製)。
天然ゴム:伸工貿易社製、(商品名)RSS3号。
カーボンブラック:旭カーボン社製、(商品名)旭#70。
炭酸カルシウム:丸尾カルシウム社製、重質炭酸カルシウム。
プロセスオイル:出光興産社製、(商品名)ダイアナプロセスオイルAH-16。
酸化亜鉛:堺化学工業製、酸化亜鉛。
ステアリン酸:キシダ化学社製、ステアリン酸。
硫黄:鶴見化学工業社製、(商品名)サルファックス5。
加硫促進剤(MBTS):大内新興化学工業社製、(商品名)ノクセラーDM-P。
<脂肪族単量体-芳香族単量体共重合樹脂中の芳香族単量体残基成分含量>
JIS K-0114(2000年)に準拠してガスクロマトグラフ法により重合前後の油中のモノマー量の測定を行い、モノマー転化率より共重合組成を算出し、芳香族単量体残基成分の算出を行った。
JIS K-2207に従って測定。
標準ポリスチレンを標準物質としてゲル浸透クロマトグラフィーにより、数平均分子量(Mn)及び重量平均分子量(Mw)を測定した。
粘弾性測定装置(ユービーエム社製、(商品名)Rheogel E-4000)を使用し、周波数10Hzでtanδを測定し、50℃、75℃の値を制振性の指標とした。この値が大きい程、制振性が良好であると判断した。
市販の原料を用いて所定の濃度に調製し、芳香族単量体の混合物(混合油)として芳香族油a,芳香族油b、脂肪族単量体の混合物(混合油)として脂肪族油a,脂肪族油bを調製した。芳香族油a,bの組成を表1に示す。脂肪族油a,bの組成を表2に示す。
下記に示す方法により、芳香族油a,芳香族油b,脂肪族油a,脂肪族油bを用い、脂肪族単量体単独重合樹脂a、脂肪族単量体-芳香族単量体共重合樹脂b~g(以下、単に樹脂a~樹脂gと記す。)のそれぞれを製造した。
天然ゴム100重量部に対し、樹脂a70重量部、樹脂b50重量部、カーボンブラック40重量部、炭酸カルシウム10重量部、プロセスオイル10重量部、酸化亜鉛5重量部、ステアリン酸2重量部を、バンバリーミキサー(東洋精機製(商品名)BR600)にて、混練りした。続いて硫黄2重量部、加硫促進剤(MBTS)1重量部を添加し、仕上げ練りを行った後、8インチロールを用いてシーティングして未加硫ゴム組成物を得た。
ゴム組成物の配合剤及び配合量を表5に示す通りとした以外は、実施例1と同様の方法にて、未加硫ゴム組成物、加硫ゴム組成物を製造し、その評価を行った。その結果を表5に示す。
ゴム組成物の配合剤及び配合量を表5に示す通りとした以外は、実施例1と同様の方法にて、未加硫ゴム組成物、加硫ゴム組成物を製造し、その評価を行った。その結果を表5に示す。
Claims (6)
- 天然ゴム(A)100重量部に対し、少なくとも、芳香族単量体残基成分が30wt%未満である脂肪族単量体重合樹脂又は芳香族単量体残基成分が30wt%未満である脂肪族単量体-芳香族単量体共重合樹脂である樹脂(B)5~100重量部と芳香族単量体残基成分が70wt%以上である脂肪族単量体-芳香族単量体共重合樹脂(C)5~100重量部とを含むものであり、樹脂(B)及び脂肪族単量体-芳香族単量体共重合樹脂(C)が石油樹脂であることを特徴とするゴム組成物。
- 樹脂(B)が、その構成としての脂肪族単量体がイソプレン,ピペリレン,シクロペンタジエン,メチルシクロペンタジエン,ジシクロペンタジエン,メチルジシクロペンタジエン,ジメチルジシクロペンタジエン,石油類の熱分解により得られる沸点範囲が20~110℃の留分から選択される1種以上、芳香族単量体がスチレン,ビニルトルエン,α-メチルスチレン,β-メチルスチレン,インデン,メチルインデン,石油類の熱分解により得られる沸点範囲が140~280℃の範囲にある留分から選択される1種以上であり、標準ポリスチレン換算値の重量平均分子量500~6000、軟化点90~120℃を有するものであることを特徴とする請求項1に記載のゴム組成物。
- 脂肪族単量体-芳香族単量体共重合樹脂(C)が、その構成としての脂肪族単量体がイソプレン,ピペリレン,シクロペンタジエン,メチルシクロペンタジエン,ジシクロペンタジエン,メチルジシクロペンタジエン,ジメチルジシクロペンタジエン,石油類の熱分解により得られる沸点範囲が20~110℃の留分から選択される1種以上、芳香族単量体がスチレン,ビニルトルエン,α-メチルスチレン,β-メチルスチレン,インデン,メチルインデン,石油類の熱分解により得られる沸点範囲が140~280℃の範囲にある留分から選択される1種以上であり、標準ポリスチレン換算値の重量平均分子量500~8000、軟化点100~140℃を有するものであることを特徴とする請求項1又は2に記載のゴム組成物。
- 天然ゴム(A)100重量部に対し、さらに無機充填剤(D)5~200重量部を含むものであることを特徴とする請求項1~3のいずれかに記載のゴム組成物。
- 無機充填剤(D)が、カーボンブラック、シリカ、炭酸カルシウム、タルク、クレー、マイカ、アルミナ及び水酸化アルミニウムからなる群より選択される少なくとも1種であることを特徴とする請求項4に記載のゴム組成物。
- 請求項1~5のいずれかに記載のゴム組成物を構成材とすることを特徴とする制振材。