JP7406936B2 - 樹脂組成物及びその成形品 - Google Patents
樹脂組成物及びその成形品 Download PDFInfo
- Publication number
- JP7406936B2 JP7406936B2 JP2019145616A JP2019145616A JP7406936B2 JP 7406936 B2 JP7406936 B2 JP 7406936B2 JP 2019145616 A JP2019145616 A JP 2019145616A JP 2019145616 A JP2019145616 A JP 2019145616A JP 7406936 B2 JP7406936 B2 JP 7406936B2
- Authority
- JP
- Japan
- Prior art keywords
- aromatic
- rubber
- mass
- polymer
- modified graft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
しかし、特許文献1では、乳化重合法により製造されたゴム変性グラフト重合体を用いつつ耐湿熱老化性を向上させることについて何ら検討されていない。
〔2〕前記芳香族カルボジイミド化合物(C)の含有量が、前記ポリカーボネート系樹脂(A)と前記ゴム変性グラフト重合体(B)との合計質量に対して0.1質量%以上である、前記〔1〕の樹脂組成物。
〔3〕前記ポリカーボネート系樹脂(A)が、芳香族ポリカーボネート及び芳香族ポリエステルカーボネートからなる群から選ばれる少なくとも1種である、前記〔1〕又は〔2〕の樹脂組成物。
〔4〕前記ゴム変性グラフト重合体(B)が、ゴム質重合体の存在下にビニル系単量体成分を乳化重合して得られたものである、前記〔1〕~〔3〕のいずれかの樹脂組成物。
〔5〕前記〔1〕~〔4〕のいずれかの樹脂組成物を含む成形品。
本明細書において、「(メタ)アクリル」は、アクリル及びメタクリルを意味し、「(メタ)アクリル酸エステル」は、アクリル酸エステル及びメタクリル酸エステルを意味し、「(共)重合体」は、単独重合体及び共重合体を意味する。
数値範囲を示す「~」は、その前後に記載された数値を下限値及び上限値として含むことを意味する。
本発明の樹脂組成物は、ポリカーボネート系樹脂(A)と、ゴム変性グラフト重合体(B)と、芳香族カルボジイミド化合物(C)とを含む。
本発明の樹脂組成物は、必要に応じて、本発明の目的を損なわない範囲で、他の熱可塑性樹脂や添加剤をさらに含んでいてもよい。
ポリカーボネート系樹脂(A)は、主鎖にカーボネート結合を有する樹脂である。
ポリカーボネート系樹脂(A)としては、特に限定されず、芳香族ポリカーボネート、脂肪族ポリカーボネート、脂肪族-芳香族ポリカーボネート、芳香族ポリエステルカーボネート等が挙げられる。これらのポリカーボネート系樹脂は、末端がR-CO-基又はR’-O-CO-基(R及びR’は、いずれも有機基を示す。)に変性されたものであってもよい。これらのポリカーボネート系樹脂は、1種単独で又は2種以上組み合わせて用いることができる。
2つのベンゼン環の間に炭化水素基を有する化合物としては、ビスフェノールA、2,2-ビス(3,5-ジブロモ-4-ヒドロキシフェニル)プロパン、2,2-ビス(4-ヒドロキシフェニル-3-メチルフェニル)プロパン、2,2-ビス(3-tert-ブチル-4-ヒドロキシフェニル)プロパン、2,2-ビス(3、5-ジメチル-4-ヒドロキシフェニル)プロパン、ビス(4-ヒドロキシフェニル)メタン、1,1-ビス(p-ヒドロキシフェニル)エタン、2,2-ビス(p-ヒドロキシフェニル)ブタン等が挙げられる。これらは、1種単独で又は2種以上を組み合わせて用いることができる。これらの中では、ビスフェノールAが特に好ましい。
芳香族ポリエステルカーボネートとしては、ポリ-4,4’-イソプロピリデンジフェニルカーボネート等が挙げられる。
ポリカーボネート系樹脂(A)のMvは、溶融粘度により求めた値である。
ゴム変性グラフト重合体(B)は、ゴム質重合体の存在下にビニル系単量体成分を重合(グラフト重合)して得られたものであり、ゴム質重合体とビニル系重合体とを含む。
ビニル系単量体成分は、1種以上のビニル系単量体からなる。ビニル系重合体は、ビニル系単量体成分の重合体であり、ビニル系単量体に基づく構成単位を含む。
ゴム質重合体としては、エチレン・α-オレフィン系ゴム質重合体、ジエン系ゴム質重合体、アクリル系ゴム質重合体等が挙げられる。これらは、1種単独で又は2種以上を組み合わせて用いることができる。
ゴム質重合体としては、耐衝撃性の観点から、エチレン・α-オレフィン系ゴム質重合体及びジエン系ゴム質重合体からなる群から選ばれる少なくとも1種が好ましく、成形品同士が互いに接触したときの軋み音を低減する観点から、エチレン・α-オレフィン系ゴム質重合体がより好ましい。
エチレン・α-オレフィン系ゴム質重合体とジエン系ゴム質重合体とを併用してもよい。この場合、樹脂組成物の成形品が、例えば-30℃といった非常に低温の環境下においても、衝撃破壊時に延性破壊するようになるため、樹脂組成物が、安全性が要求される成形品(自動車用部品等)の成形品の成形材料として好適なものとなる。
α-オレフィンとしては、例えば、炭素数3~20のα-オレフィンが挙げられ、具体的には、プロピレン、1-ブテン、1-ペンテン、1-ヘキセン、4-メチル-1-ペンテン、1-ヘプテン、1-オクテン、1-デセン、1-ドデセン、1-ヘキサデセン、1-エイコセン等が挙げられる。これらのα-オレフィンは、1種単独で又は2種以上を組み合わせて用いることができる。
α-オレフィンの炭素数は、好ましくは3~20、より好ましくは3~12、さらに好ましくは3~8である。炭素数が20以下であれば、エチレンとの共重合性が良好で、樹脂組成物の成形品の表面外観がより優れる。
非共役ジエンとしては、1,4-ヘキサジエン、1,5-ヘキサジエン、5-エチリデン-2-ノルボルネン、ジシクロペンタジエン等が挙げられる。
エチレンに基づく構成単位とα-オレフィンに基づく構成単位との合計質量に対する非共役ジエンに基づく構成単位の割合は、10質量%以下が好ましく、5質量%以下がより好ましく、3質量%以下がさらに好ましく、0質量%が特に好ましい。すなわち、非共役ジエンに基づく構成単位を含まないことが特に好ましい。
エチレン・α-オレフィン系ゴム質重合体は、1種単独で又は2種以上を組み合わせて用いることができる。
ムーニー粘度は、JIS K 6300に規定された方法に従って測定した値である。
エチレン・α-オレフィン系ゴム質重合体がTmを持つことは、該ゴム質重合体が結晶性部分を有することを意味している。ゴム質重合体中に結晶性部分が存在すると、スティックスリップ現象の発生が抑制される為、軋み音の発生が抑制されるものと考えられる。
Tmは、示差走査熱量計(DSC)を用い、1分間に20℃の一定昇温速度で吸熱変化を測定し、得られた吸熱パターンのピーク温度を読みとった値であり、詳細は、JIS K 7121:1987に規定されている。なお、DSCの測定において、吸熱変化のピークを明瞭に示さないものは、実質的に結晶性がないものであり、Tmを持たないものと判断する。
Tgは、Tmの測定と同様に、DSCを用い、JIS K 7121:1987に規定された方法に従って測定することができる。
上記重量平均分子量は、ゲルパーミエーションクロマトグラフィー(GPC)により測定される標準ポリスチレン換算の値である。
ジエン系ゴム質重合体は、架橋重合体であってよいし、未架橋重合体であってもよい。
ジエン系ゴム質重合体は、共役ジエン系化合物よりなる単位を含む(共)重合体を水素添加してなる(共)重合体であってもよい。該ジエン系ゴム質重合体に対する水素添加率は、典型的には95%以上、好ましくは98%以上である。
ジエン系ゴム質重合体は1種単独で又は2種以上を組み合わせて用いることができる。
ビニル系単量体成分を構成するビニル系単量体としては、芳香族ビニル化合物、シアン化ビニル化合物、(メタ)アクリル酸エステル、これらの化合物と共重合可能な他のビニル系単量体が挙げられる。他のビニル系単量体としては、マレイミド系化合物、不飽和酸無水物、カルボキシ基含有不飽和化合物、ヒドロキシ基含有不飽和化合物、オキサゾリン基含有不飽和化合物、エポキシ基含有不飽和化合物等が挙げられる。これらは1種単独で又は2種以上を組み合わせて用いることができる。
ビニル系単量体成分の総質量に対する芳香族ビニル化合物の割合は、40質量%以上が好ましく、55質量%以上がより好ましい。該割合は100質量%であってもよい。
なお、ビニル系単量体成分の総質量に対する芳香族ビニル化合物の割合は、ビニル系重合体を構成する全ての構成単位の合計質量に対する芳香族ビニル化合物に基づく構成単位の割合とみなすことができる。シアン化ビニル化合物の割合も同様である。
ゴム変性グラフト重合体(B)は、ゴム質重合体の存在下にビニル系単量体成分を重合することにより得られる。
重合方法としては、乳化重合法、溶液重合法、塊状重合法、懸濁重合法等が挙げられる。これらのなかでも、ゴム成分の含有率を高くでき設計の自由度が大きいこと、得られる成形品の外観が優れること、過度の熱劣化によるゴム質重合体の劣化、着色が低いこと、小ロット単品種生産にも対応できること等から、乳化重合法が好ましい。すなわち、ゴム変性グラフト重合体(B)は、ゴム質重合体の存在下にビニル系単量体成分を乳化重合して得られたものであることが好ましい。
ゴム質重合体のラテックスは、公知の方法により製造できる。ラテックスを製造する方法としては、溶融状態のゴム質重合体を水中で攪拌剪断力によって、均質化処理(ホモジナイズ)する方法や、乳化剤の存在下で、重合性モノマーを乳化重合する方法等が知られている(特公平4-30970号公報、特許第3403828号、特開平11-269206号公報等参照)。
重合には、重合開始剤、連鎖移動剤(分子量調節剤)、乳化剤等を用いることができる。
重合開始剤の使用量は、単量体成分全量100質量部に対し、好ましくは0.1~1.5質量部、より好ましくは0.2~0.7質量部である。
連鎖移動剤の使用量は、単量体成分全量100質量部に対し、好ましくは5質量部以下、より好ましくは3質量部である。
乳化剤の使用量は、単量体成分全量100質量部に対し、例えば0.3~5質量部である。
乳化重合により得られたラテックスからゴム変性グラフト重合体(B)を回収する方法としては、特に制限されるものではないが、前記ラテックスを凝固剤水溶液等に投入して凝固し、重合体を回収する方法、凝固剤水溶液を前記ラテックスに投入して凝固し、重合体を回収する方法、凝固工程を低温から高温に温度勾配をつけ二段階以上に分けて凝固し、重合体を回収する方法、凝固工程を弱酸性から強酸性に又は強酸性から弱酸性に酸性度勾配をつけて二段階以上に分けて凝固し、重合体を回収する方法、前記ラテックスに凝固剤水溶液を混合してペーストとした後、細孔から温水中へ押出して凝固し、重合体を回収する方法等が挙げられ、これらの方法から二種類以上を選択して組み合わせることにより、回収することもできる。凝固剤としては、例えば、硫酸、リン酸、硝酸等の無機酸、酢酸、乳酸等の有機酸、硫酸マグネシウム、塩化カルシウム、塩化マグネシウム、塩化ナトリウム等の無機塩等から選ばれた1種以上を用いることができる。
この後、公知の方法、例えば遠心脱水機、流動乾燥機を使用して、脱水・乾燥して重合体を回収することができる。なお、この際、必要に応じて、ラテックスに予め各種酸化防止剤、各種安定剤を添加してもよく、さらにこれらを乳化して添加してもよい。
グラフト率(質量%)={(S-T)/T}×100 ・・・(1)
上記式中、Sは、ゴム変性グラフト重合体(B)1gをアセトン20mLに投入し、25℃の温度条件下で、振とう機により2時間振とうした後、5℃の温度条件下で、遠心分離機(回転数;23,000rpm)で60分間遠心分離し、不溶分と可溶分とを分離して得られる不溶分の質量(g)であり、Tは、ゴム変性グラフト重合体(B)1gに含まれるゴム質重合体の質量(g)である。このゴム質重合体の質量は、重合処方及び重合転化率から算出する方法、赤外線吸収スペクトル(IR)、熱分解ガスクロマトグラフィー、CHN元素分析等の方法により得ることができる。
まず、ゴム変性グラフト重合体(B)のアセトン可溶分をメチルエチルケトンに溶解させ、濃度の異なる測定用試料5点を作製する。次に、ウベローデ粘度管を用い、30℃における各濃度の測定用試料の還元粘度を測定した結果から、極限粘度[η]を求める。単位は、dL/gである。アセトン可溶分は、ゴム変性グラフト重合体(B)の1gをアセトン20mLに投入し、25℃の温度条件下で、振とう機により2時間振とうした後、5℃の温度条件下で、遠心分離機(回転数;23,000rpm)で60分間遠心分離し、不溶分と可溶分(アセトン可溶分のアセトン溶液)とを分離し、可溶分を乾燥(アセトンを除去)して得られる。
芳香族カルボジイミド化合物(C)は、分子中に芳香環及びカルボジイミド基(-N=C=N-)を有する化合物である。
芳香族カルボジイミド化合物(C)としては、カルボジイミド基を1つ有する芳香族モノカルボジイミド化合物、カルボジイミド基を2つ以上有する芳香族ポリカルボジイミド化合物が挙げられる。
「カルボジイミド量の最小含有量」とは、芳香族モノカルボジイミド化合物100質量%中のカルボジイミド基の質量の割合である。
芳香族ポリカルボジイミド化合物の重量平均分子量の上限は特に限定されないが、例えば50000である。
芳香族カルボジイミド化合物(C)としては、耐湿熱老化性、耐加水分解性の観点から、芳香族ポリカルボジイミド化合物が好ましい。
他の熱可塑性樹脂としては、例えば、ポリエチレンテレフタレート(PET)樹脂、ポリブチレンテレフタレート(PBT)樹脂等のポリエステル樹脂、ポリウレタン(PU)樹脂が挙げられる。これらの熱可塑性樹脂は、1種単独で又は2種以上を組み合わせて用いることができる。
他の添加剤としては、紫外線吸収剤、耐候剤、充填剤、酸化防止剤、老化防止剤、帯電防止剤、難燃剤、防曇剤、滑剤、抗菌剤、粘着付与剤、可塑剤、着色剤等が挙げられる。これらの添加剤は、1種単独で又は2種以上を組み合わせて用いることができる。
ポリカーボネート系樹脂(A)とゴム変性グラフト重合体(B)との合計質量に対するポリカーボネート系樹脂(A)の割合は、30~80質量%が好ましく、40~70質量%がより好ましい。ポリカーボネート系樹脂(A)の割合が上記下限値以上であれば、耐衝撃性、耐熱性がより優れる。ポリカーボネート系樹脂(A)の割合が上記上限値以下であれば、機械的強度、成形性がより優れる。
芳香族カルボジイミド化合物(C)の含有量は、衝撃性の観点では、樹脂組成物の総質量に対して3.0質量%以下が好ましく、2.0質量%以下がより好ましい。
MFRは、ISO 1133に規定された方法に従って測定した値である。
各成分の混合順序は特に制限されず、一部の成分を混合した後、残部を混合してもよく、全成分を一括に混合してもよい。各成分を混練するに際して、各成分を一括して混練してもよく、多段、分割配合して混練してもよい。充填材のうち繊維状のものは、混練中での切断を防止するためにサイドフィーダーにより押出機の途中から供給する方が好ましい。溶融混練温度は、通常200~300℃、好ましくは220~280℃である。
本発明の成形品は、本発明の樹脂組成物を含む。
本発明の成形品は、例えば、本発明の樹脂組成物を成形することにより製造できる。
成形方法としては、特に制限はなく、例えば、射出成形法、射出圧縮成形法、ガスアシスト成形法、プレス成形法、ブロー成形法、異形押出成形法、カレンダー成形法、Tダイ押出成形法等の公知の方法が挙げられる。
<MFR>
樹脂組成物のペレットについて、ISO 1133に規定された方法に従って、温度240℃及び荷重98Nの条件でMFRを測定した。
樹脂組成物のペレットを、射出成形機((株)日本製鋼所社製「J110AD-180H」)を用い、シリンダー温度240℃の条件で射出成形して試験片A(成形品)を得た。得られた試験片Aについて、ISO 179-1に規定された方法に従って、23℃におけるIMPを測定した。
樹脂組成物のペレットを、射出成形機((株)日本製鋼所社製「J110AD-180H」)を用い、シリンダー温度240℃の条件で射出成形して試験片B(成形品)を得た。得られた試験片Bについて、ISO 527に規定された方法に従って、23℃におけるTEを測定した。
熱可塑性樹脂組成物を東芝機械製IS-170FA射出成形機によりシリンダー温度250℃、射出圧力50MPa、金型温度60℃にて射出成形し、縦150mm、横100mm、厚さ4mmの射出成形プレートを得た。このプレートから、縦60mm、横100mm、厚さ4mmの試験片及び縦50mm、横25mm、厚さ4mmの試験片をディスクソーで切り出し、番手#100のサンドペーパーで端部を面取りした後、細かなバリをカッターナイフで除去し、大小2枚のプレートを試験片として用いた。
大きな試験片と小さな試験片をジグラー(ZIEGLER)社製スティックスリップ試験機SSP-02に固定し、温度23℃、湿度50%RHの雰囲気下で荷重5N、40N、速度1mm/秒、10mm/秒の4条件にて振幅20mmで3回擦り合わせたときの異音リスク値を測定した。そして、異音リスク値が最も大きい条件の数値を抽出して測定値とした。異音リスク値が大きいほど軋み音の発生リスクは高くなり、以下の基準で判断した。
○:異音リスク値が3以下でリスクが低く良好とした。
×:異音リスク値が3を超えてリスクが高いとした。
<ポリカーボネート樹脂(A)>
三菱エンジニアリングプラスチックス社製「ノバレックス7022PJ-LH1」(Mv18,700(カタログ値)の芳香族ポリカーボネート)を使用した。
UMG ABS社製「B501N」(ジエン系ゴム質重合体の存在下にアクリロニトリル及びスチレンを乳化重合して得られたABS樹脂)を使用した。
ランクセス社製「スタバクゾール(Stabaxol)P100」(芳香族ポリカルボジイミド、分子量15,000g/mol)を使用した。
日清紡ケミカル社製「カルボジライトHMV-15CA」(脂肪族ポリカルボジイミド)を使用した。
表1記載の成分を表1に記載の配合割合(部)でヘンシェルミキサーにより混合した後、ベント付き二軸押出機(日本製鋼所社製、TEX44、バレル設定温度260℃)を用いて溶融混練し、樹脂組成物のペレットを得た。得られたペレットについて、前記した方法によりMFRを測定した。また、前記した方法により試験片を成形してIMP及びTEを測定し、耐軋み音性を評価した。
MFRの上昇率(%)={湿熱処理後のMFR-初期のMFR}/初期のMFR×100
IMPの保持率(%)=湿熱処理後のIMP/初期のIMP×100
TEの保持率(%)=湿熱処理後のTE/初期のTE×100
実施例3における芳香族カルボジイミド化合物を非芳香族カルボジイミド化合物に置換した比較例2の樹脂組成物は、実施例3に比べて、IMP及びTEの保持率が低く、MFRの上昇率が高くなっており、耐湿熱老化性に劣っていた。このことから、カルボジイミド化合物のなかでも芳香族カルボジイミド化合物が、ポリカーボネート系樹脂(A)及びゴム変性グラフト重合体(B)を含む樹脂組成物の耐湿熱老化性の向上効果に優れることがわかる。
Claims (5)
- ポリカーボネート系樹脂(A)と、ゴム変性グラフト重合体(B)と、芳香族カルボジイミド化合物(C)とを含み、
前記ゴム変性グラフト重合体(B)が、ゴム質重合体の存在下にビニル系単量体成分を乳化重合して得られたものであり、
前記ポリカーボネート系樹脂(A)と前記ゴム変性グラフト重合体(B)との合計質量に対する前記ポリカーボネート系樹脂(A)の割合が、40~70質量%であり、
前記芳香族カルボジイミド化合物(C)が、重量平均分子量が3000以上である芳香族ポリカルボジイミド化合物であり、
前記芳香族カルボジイミド化合物(C)の含有量が、前記ポリカーボネート系樹脂(A)と前記ゴム変性グラフト重合体(B)との合計質量に対して0.1~3.0質量%である、樹脂組成物。 - 前記芳香族カルボジイミド化合物(C)の含有量が、前記ポリカーボネート系樹脂(A)と前記ゴム変性グラフト重合体(B)との合計質量に対して0.1~0.5質量%である、請求項1に記載の樹脂組成物。
- 前記ポリカーボネート系樹脂(A)が、芳香族ポリカーボネート及び芳香族ポリエステルカーボネートからなる群から選ばれる少なくとも1種である、請求項1又は2に記載の樹脂組成物。
- 他の熱可塑性樹脂の含有量が、前記ポリカーボネート系樹脂(A)と前記ゴム変性グラフト重合体(B)との合計質量に対し、0~30質量%である、請求項1~3のいずれか一項に記載の樹脂組成物。
- 請求項1~4のいずれか一項に記載の樹脂組成物を含む成形品。