JP6871294B2 - 積層体及び画像表示装置 - Google Patents
積層体及び画像表示装置 Download PDFInfo
- Publication number
- JP6871294B2 JP6871294B2 JP2019056689A JP2019056689A JP6871294B2 JP 6871294 B2 JP6871294 B2 JP 6871294B2 JP 2019056689 A JP2019056689 A JP 2019056689A JP 2019056689 A JP2019056689 A JP 2019056689A JP 6871294 B2 JP6871294 B2 JP 6871294B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- film
- sensitive adhesive
- pressure
- adhesive layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[1] 前面板と、両面粘着剤層付円偏光板とを備え、前記前面板の厚みをa[μm]とし、前記両面粘着剤層付円偏光板の厚みをb[μm]とし、前記前面板の温度23℃での最大弾性エネルギーをc[106N/m2]としたとき、下記式(1)を満たす、積層体。
[(b/a)×c]>0.72 (1)
[2] 前記cは下記式(2)を満たす、[1]に記載の積層体。
c≧0.7 (2)
[3] 前記前面板は、ポリアミドイミド系樹脂フィルムを含む、[1]又は[2]に記載の積層体。
[4] 前記前面板はハードコート層を有する、[1]〜[3]のいずれかに記載の積層体。
[5] 前記両面粘着剤層付円偏光板は、第1粘着剤層と、直線偏光板と、位相差層と、第2粘着剤層とをこの順に有する、[1]〜[4]のいずれかに記載の積層体。
[6] [1]〜[5]のいずれかに記載の積層体を備える、画像表示装置。
図1は、本発明の一実施形態による光学積層体の概略断面図である。図1に示す光学積層体100は、前面板10と、両面粘着剤層付円偏光板20とを備える。
[(b/a)×c]>0.72 (1)
[(b/a)×c]≧1.0 (1a)
[(b/a)×c]≧1.1 (1b)
[(b/a)×c]≧1.5 (1c)
[(b/a)×c]≧2.0 (1d)
また、積層体100は、下記式(1e)を満たすことが好ましい。
[(b/a)×c]≦5.0 (1e)
前面板10は、光を透過可能な板状体であることができる。前面板10は、1層のみから構成されてよく、2層以上から構成されてもよい。その例としては、樹脂製の板状体(例えば樹脂板、樹脂シート、樹脂フィルム等)、ガラス製の板状体(例えばガラス板、ガラスフィルム等)等が挙げられる。前面板は、表示装置の最表面を構成する層であることができる。
c≧0.7 (2)
c≧0.75 (2a)
c≦3.0 (2b)
中でも、前面板を構成する熱可塑性樹脂としては、可撓性、強度及び透明性の観点から好ましくは環状ポリオレフィン系樹脂、ポリイミド系樹脂、ポリアミド系樹脂、ポリアミドイミド系樹脂であり、より好ましくはポリアミドイミド系樹である。ポリアミドイミド系樹脂の具体例としては、特開2018−119141号公報に記載のポリアミドイミドフィルム等が挙げられる。
両面粘着剤層付円偏光板20は、第1粘着剤層と、直線偏光板と、位相差層と、第2粘着剤層とをこの順に含むことが好ましい。この実施形態において、両面粘着剤層付円偏光板20の厚みは、第1粘着剤層における直線偏光板側とは反対側の表面から、第2粘着剤層における直線偏光板側とは反対側の表面までの距離であることができる。直線偏光板の吸収軸と位相差層の遅相軸とが所定の角度となるように直線偏光層と位相差層とが配置された円偏光板は、反射防止機能を発揮することができる。位相差層がλ/4板を含む場合、直線偏光板の吸収軸とλ/4板の遅相軸とのなす角度は、45°±10°であることができる。直線偏光板と、位相差層とは後述の貼合層により貼合されていてよい。以下、第1粘着剤層及び第2粘着剤層を総称して粘着剤層ともいうことがある。
直線偏光板としては、吸収異方性を有する色素を吸着させた延伸フィルム若しくは延伸層、又は吸収異方性を有する色素を塗布し硬化させたフィルムを偏光子として含むフィルム等が挙げられる。吸収異方性を有する色素としては、例えば、二色性色素が挙げられる。二色性色素として、具体的には、ヨウ素や二色性の有機染料が用いられる。二色性有機染料には、C.I.DIRECT RED 39等のジスアゾ化合物からなる二色性直接染料、トリスアゾ、テトラキスアゾなどの化合物からなる二色性直接染料が包含される。
まず、吸収異方性を有する色素を吸着させた延伸フィルムを偏光子として備える直線偏光板について説明する。偏光子である、吸収異方性を有する色素を吸着させた延伸フィルムは、通常、ポリビニルアルコール系樹脂フィルムを一軸延伸する工程、ポリビニルアルコール系樹脂フィルムを二色性色素で染色することにより、その二色性色素を吸着させる工程、及び二色性色素が吸着されたポリビニルアルコール系樹脂フィルムをホウ酸水溶液で処理する工程を有する、及びホウ酸水溶液による処理後に水洗する工程を経て製造することができる。かかる偏光子をそのまま直線偏光板として用いてもよく、その片面又は両面に後述する熱可塑性樹脂フィルムを貼合したものを直線偏光板として用いてもよい。偏光子の厚みは、好ましくは2μm以上40μm以下である。
必要に応じて、基材フィルムを偏光子から剥離除去してもよい。基材フィルムの材料及び厚みは、後述する熱可塑性樹脂フィルムの材料及び厚みと同様であってよい。
熱可塑性樹脂フィルムは位相差を有していても、有していなくてもよい。
熱可塑性樹脂フィルムは、例えば、接着剤層を用いて偏光子に貼合することができる。
吸収異方性を有する色素を塗布し硬化させたフィルムを偏光子として備える直線偏光板について説明する。偏光子として用いられる、吸収異方性を有する色素を塗布し硬化させたフィルムは、液晶性を有する二色性色素を含む組成物、又は二色性色素と液晶化合物とを含む組成物を基材に塗布し硬化して得られるフィルム等が挙げられる。当該フィルムは、基材を剥離してまたは基材とともに直線偏光板として用いてもよく、またはその片面又は両面に熱可塑性樹脂フィルムを有する構成で直線偏光板として用いてもよい。
配向膜は、上記基材と液晶性を有する二色性色素を含む組成物、又は二色性色素と液晶化合物とを含む組成物の硬化物の層との間に配置されることができる。配向膜は、その上に形成される液晶層を所望の方向に液晶配向させる、配向規制力を有する。配向膜としては、配向性ポリマーで形成された配向性ポリマー層、光配向ポリマーで形成された光配向性ポリマー層、層表面に凹凸パターンや複数のグルブ(溝)を有するグルブ配向膜を挙げることができる。配向膜の厚みは、例えば10nm以上500nm以下であってよく、10nm以上200nm以下であることが好ましい。
保護層は、偏光子の表面を保護するために用いることができる。直線偏光板が熱可塑性樹脂フィルムを含む場合、保護層は、偏光子の熱可塑性樹脂フィルムとは反対側に配置されることができる。保護層としては、上記の熱可塑性樹脂フィルムの材料として例示をした樹脂フィルムから形成されてもよいし、コーティング型の保護層であってもよい。コーティング型の保護層は、例えばエポキシ樹脂等のカチオン硬化性組成物や(メタ)アクリレート等のラジカル硬化性組成物を塗布し、硬化してなるものであってよく、ポリビニルアルコール系樹脂等の水溶液を塗布し、乾燥してなるものであってよく、必要により可塑剤、紫外線吸収剤、赤外線吸収剤、顔料や染料のような着色剤、蛍光増白剤、分散剤、熱安定剤、光安定剤、帯電防止剤、酸化防止剤、滑剤等を含んでいてもよい。
位相差層は、1層または2層以上の位相差層を含むことができる。位相差層としては、λ/4層やλ/2層のようなポジティブA層、およびポジティブC層であることができる。位相差層は、上述の熱可塑性樹脂フィルムの材料として例示をした樹脂フィルムから形成されてもよいし、重合性液晶化合物が硬化した層から形成されてもよい。位相差層は、さらに配向膜や基材を含んでいてもよい。位相差層の厚みは、例えば1μm以上50μm以下であってよい。
第1粘着剤層は、両面粘着剤層付円偏光板20が有する粘着剤層である。第1粘着剤層は、両面粘着剤層付円偏光板20と、前面板10とを貼合するために配置される。第2粘着剤層は、両面粘着剤層付円偏光板20が有する粘着剤層である。第2粘着剤層は、両面粘着剤層付円偏光板20と、後述する背面板とを貼合するために配置される。粘着剤層は、粘着剤組成物を用いて形成することができる。粘着剤層は、単層構造であっても多層構造であってもよいが、好ましくは単層構造である。第1粘着剤層及び第2粘着剤層はそれぞれ、同種の粘着剤層から構成されてよく、又は異種の粘着剤層から構成されてもよい。
積層体100は、第2粘着剤層を介して、背面板が貼合されていてもよい。背面板としては、タッチセンサパネル、有機EL表示素子等の表示素子又はこれらの組合せ等が挙げられる。
貼合層50及び62は粘着剤層又は接着剤層であり、粘着剤組成物や接着剤組成物を用いて形成することができる。貼合層は、単層構造であっても多層構造であってもよいが、好ましくは単層構造である。粘着剤組成物としては、上述の粘着剤層の説明において例示したものと同一であってよい。
画像表示装置としては特に限定されず、例えば、有機エレクトロルミネッセンス(有機EL)表示装置、無機エレクトロルミネッセンス(無機EL)表示装置、液晶表示装置、タッチパネル表示装置、電界発光表示装置等を挙げることができる。本実施の形態の画像表示装置は、屈曲可能な積層体を有するため、フレキシブルディスプレイに好適に用いることができ、特に有機EL表示装置に好適に用いることができる。
接触式膜厚測定装置(株式会社ニコン製「MS−5C」)を用いて測定した。ただし、偏光子層、位相差層および配向膜については、レーザー顕微鏡(LEXT、オリンパス株式会社製)を用いて測定した。
JIS K7161に準拠して、UTM(Universal Testing Machine、オートグラフAG−X、株式会社島津製作所)を用いて引張試験を行い、応力[MPa]を縦軸、ひずみ[%]を横軸とした座標系において応力ひずみ曲線を取得した。延伸条件は、常温(温度23℃)で速度4mm/分、幅10mm、標点距離50mmとした。得られた応力ひずみ曲線において降伏点が確認される場合、図3(a)に示すように、原点、降伏点、及び降伏点から横軸に降ろした垂線と横軸との交点の3点で囲まれる面積(斜線部)を最大弾性エネルギーとして求めた。得られた応力ひずみ曲線において降伏点が確認されない場合、図3(b)に示すように、原点、荷重を除去した際に元の長さに戻らず0.2%の残留ひずみが生じる点(以下、a点という)、及びa点から横軸に降ろした垂線と横軸との交点の3点で囲まれる面積(斜線部)を最大弾性エネルギーとして求めた。
各実施例および比較例で得られた積層体に、積層体が備える粘着剤層を介して、ポリエチレンテレフタレート(PET)フィルムを貼合し、試験片を得た。PETフィルムは、画像表示素子を模したものであり、その厚みは100μmであった。試験片をレーザーカットし、下記条件で常温屈曲試験を施した後、屈曲部のうねりを干渉顕微鏡を用いて測定した。うねりは、積層体の前面板が上方になるように干渉顕微鏡に設置し、干渉顕微鏡により積層体の屈曲部の前面板側表面に観察される凹凸のうち、最も高い箇所と最も低い箇所との高低差の平均値(n=6)として求めた。
(常温屈曲試験)
積層体を前面板側を内側にして曲率半径1mm(1R)で屈曲した状態で、温度23℃で10日間放置した。
うねり評価後の積層体を、屈曲した状態を開放して平面状態にした。この積層体を蛍光灯下に前面板側が上方となるように設置し、積層体表面に映り込んだ蛍光灯の像を観察した。折り曲げた部分において蛍光灯の像に歪みが視認されない場合を○とし、蛍光灯の像に歪みが視認される場合を×とした。
(ポリアミドイミドフィルム)
窒素ガス雰囲気下、撹拌翼を備えた1Lセパラブルフラスコに、2,2’−ビス(トリフルオロメチル)ベンジジン(TFMB)14.67g(45.8mmol)および水分量を200ppmに調製したN,N−ジメチルアセトアミド(DMAc)233.3gを加え、室温で撹拌しながらTFMBをDMAcに溶解させた。次に、フラスコに4,4’−オキシジフタル酸二無水物(OPDA)4.283g(13.8mmol)を加え、室温で16.5時間撹拌した。その後、4,4’−オキシビス(ベンゾイルクロリド)(OBBC)1.359g(4.61mmol)およびテレフタロイルクロリド(TPC)5.609g(27.6mmol)をフラスコに加え、室温で1時間撹拌した。次いで、フラスコに無水酢酸4.937g(48.35mmol)と4−ピコリン1.501g(16.12mmol)とを加え、室温で30分間撹拌後、オイルバスを用いて70℃に昇温し、さらに3時間撹拌し、反応液を得た。
得られた反応液を室温まで冷却した後、メタノール360gおよびイオン交換水170gを加えてポリアミドイミドの沈殿を得た。それをメタノール中に12時間浸漬し、濾過で回収してメタノールで洗浄した。次に、100℃にて沈殿物の減圧乾燥を行い、厚み50μmのポリアミドイミド(PAI)樹脂を得た。
HC層形成用組成物1は、多官能アクリレート(Miramer M340、Miwon Specialty Chemical製)30質量部と、ナノシリカゾルのプロピレングリコールモノメチルエーテル分散体(12nm、固形分40%)50質量部と、エチルアセテート17質量部と、光重合開始剤(Irgacure−184、Ciba Corporation製)2.7質量部と、フッ素系添加剤(KY1203、信越化学株式会社製)0.3質量部とを含む。
上記HC層形成用組成物をポリアミドイミドフィルムの一方の面に塗工し、得られた塗膜を温度80℃で5分間乾燥し、UV照射装置(SPOT CURE SP−7、ウシオ電機株式会社製)を用いて、露光量500mJ/cm2(365nm基準)のUV光を照射してHC層1を形成した。硬化後の厚みが10.0μmになるように塗工した。以上のようにして、HC層1/ポリアミドイミドフィルムの構成を有する前面板1を得た。
前面板1のポリアミドイミドフィルムの調製においてOPDA4.283gに代えて4,4’−(ヘキサフルオロイソプロピリデン)ジフタル酸二無水物(6FDA)6.140gを用い、TFMB14.67g(45.8mmol)に代えてTFMB8.809g(27.5mmol)および2,2’−ジメチルベンジジン(MB)3.889g(18.3mmol)を用いた以外は、前面板1のポリアミドイミドフィルムの調製と同様にして、厚み40μmのポリアミドイミド樹脂を得た。
シクロオレフィン(COP)フィルム(厚み40μm、日本ゼオン株式会社製)を準備した。
トリアセチルセルロース(TAC)フィルム(厚み40μm)を準備した。
(重合性液晶化合物)
重合性液晶化合物は、式(1−6)で表される重合性液晶化合物[以下、化合物(1−6)ともいう]と式(1−7)で表される重合性液晶化合物[以下、化合物(1−7)ともいう]とを用いた。
二色性色素には、下記式(2−1a)、(2−1b)、(2−3a)で示される特開2013−101328号公報の実施例に記載のアゾ色素を用いた。
偏光子層形成用組成物は、化合物(1−6)75質量部、化合物(1−7)25質量部、二色性染料としての上記式(2−1a)、(2−1b)、(2−3a)で示されるアゾ色素各2.5質量部、重合開始剤としての2−ジメチルアミノ−2−ベンジル−1−(4−モルホリノフェニル)ブタン−1−オン(Irgacure369、BASFジャパン社製)6質量部、およびレベリング剤としてのポリアクリレート化合物(BYK−361N、BYK−Chemie社製)1.2質量部を、溶剤のトルエン400質量部に混合し、得られた混合物を80℃で1時間攪拌することにより調製した。
下記の表1に示す各成分の割合にて粘着剤層1を形成する粘着剤組成物を調製した。この粘着剤組成物を離型処理されたポリエチレンテレフタレートフィルム(厚み38μm)の離型処理面に、アプリケータを利用して乾燥後の厚みが25μmになるように塗布した。塗布層を100℃で1分間乾燥して、粘着剤層1を備えるフィルムを得た。その後、粘着剤層1上に、離型処理された別のポリエチレンテレフタレートフィルム(厚み38μm)を貼合した。その後、温度23℃、相対湿度50%RHの条件で7日間養生させた。
表1中の単量体の欄における記号は以下の意味を表す。
BA:アクリル酸ブチル
MMA:アクリル酸メチル
EHA:アクリル酸2−エチルヘキシル
AA:アクリル酸
表1中の架橋剤及びシランカップリング剤は以下のものを用いた。
架橋剤:コロネートL(東ソー株式会社製)
シランカップリング剤:KBM−403(信越化学工業株式会社製)
乾燥後の厚みが5μmになるようにしたこと以外は、粘着剤層1と同様にして粘着剤層2を備えるフィルムを得た。
下記の表1に示す各成分の割合にて粘着剤層3を形成する粘着剤組成物を調製した。この粘着剤組成物を離型処理されたポリエチレンテレフタレートフィルム(厚み38μm)の離型処理面に、アプリケータを利用して乾燥後の厚みが5μmになるように塗布した。塗布層を100℃で1分間乾燥して、粘着剤層3を備えるフィルムを得た。その後、粘着剤層上に、離型処理された別のポリエチレンテレフタレートフィルム(厚み38μm)を貼合した。その後、温度23℃、相対湿度50%RHの条件で7日間養生させた。
トリアセチルセルロース(TAC)フィルム(厚み25μm)を準備した。
(HC層形成用組成物2)
18官能のアクリロイルオキシ基(アクリル基ということがある)を有するデンドリマーアクリレート(Miramer SP1106、Miwon Speciality Chemical社)2.0質量部、6官能のアクリル基を有するウレタンアクリレート(Miramer PU−620D、Miwon Speciality Chemical社)10.0質量部、3官能のアクリル基を有するアクリレートモノマー(M340、Miwon Speciality Chemical社)8質量部、光重合開始剤(イルガキュア(登録商標)184、BASF社製)2質量部、及びレベリング剤(BYK−UV3530、ビックケミー・ジャパン株式会社)0.1質量部を、メチルエチルケトン(MEK)70質量部に溶解させて攪拌混合し、ハードコート層形成用組成物2を得た。
上記HC層形成用組成物2をシクロオレフィン(COP)フィルム(厚み13μm)の一方の面に塗工し、得られた塗膜を温度80℃で5分間乾燥し、UV照射装置(SPOT CURE SP−7、ウシオ電機株式会社製)を用いて、露光量500mJ/cm2(365nm基準)のUV光を照射してHC層2を形成した。硬化後の厚みが2μmになるように塗工した。以上のようにして、基材2を得た。
垂直配向膜形成用組成物として、2−フェノキシエチルアクリレートと、テトラヒドロフルフリルアクリレートと、ジペンタエリスリトールトリアクリレートと、ビス(2−ビニルオキシエチル)エーテルとを1:1:4:5の割合で混合し、重合開始剤としてLUCIRIN TPOを4%の割合で添加した混合物を用いた。
上述の位相差層1と位相差層2とを、基材フィルム側の表面とは反対側の表面が貼合面となるように粘着剤層3を介して貼り合わせて、基材フィルム/水平配向膜/λ/4層//粘着剤層3/ポジティブC層/垂直配向膜/基材フィルムの構成を有する位相差層を得た。
まず、基材1を準備した。基材1上に、配向膜形成用組成物をバーコート法により塗布した。塗膜を80℃で1分間乾燥した。次いで上記UV照射装置およびワイヤーグリッドを用いて、塗膜に偏光UVを照射し、塗膜に配向性能を付与した。露光量は100mJ/cm2(365nm基準)であった。ワイヤーグリッドは、UIS−27132##(ウシオ電機株式会社製)を用いた。このようにして、配向膜を形成した。配向膜の厚みは100nmであった。
実施例1において前面板1を用いたことに代えて前面板2を用いたこと以外は、実施例1と同様にして、実施例2の積層体を得た。結果を表2示す。
実施例1において前面板1を用いたことに代えて前面板3を用いたこと以外は、実施例1と同様にして、実施例3の積層体を得た。結果を表2示す。
実施例1において前面板1を用いたことに代えて前面板4を用いたこと、基材1を準備し、基材1上に配向膜形成用組成物を塗布したことに代えて、基材2を準備し、基材2のHC層2上に配向膜形成用組成物を塗布したこと、及び粘着剤層1を備えるフィルムを用いたことに代えて粘着剤層2を備えるフィルムを用いたこと以外は、実施例1と同様にして、比較例1の積層体を得た。結果を表2示す。
Claims (5)
- 前面板と、両面粘着剤層付円偏光板とを備え、前記前面板の厚みをa[μm]とし、前記両面粘着剤層付円偏光板の厚みをb[μm]とし、前記前面板の温度23℃での最大弾性エネルギーをc[106N/m2]としたとき、下記式(1)及び(2)を満たす、積層体。
2.37×10 6 N/m 2 ≧[(b/a)×c]≧1.0×106N/m2 (1)
1×10 6 N/m 2 ≧c≧0.7×106N/m2 (2) - 前記前面板は、ポリアミドイミド系樹脂フィルムを含む、請求項1に記載の積層体。
- 前記前面板は、ハードコート層を有する、請求項1又は2に記載の積層体。
- 前記両面粘着剤層付円偏光板は、第1粘着剤層と、直線偏光板と、位相差層と、第2粘着剤層とを含む、請求項1〜3のいずれか一項に記載の積層体。
- 請求項1〜4のいずれか一項に記載の積層体を備える、画像表示装置。