JP6772402B1 - 偏光子の製造方法、偏光フィルムの製造方法、積層偏光フィルムの製造方法、画像表示パネルの製造方法、および画像表示装置の製造方法 - Google Patents
偏光子の製造方法、偏光フィルムの製造方法、積層偏光フィルムの製造方法、画像表示パネルの製造方法、および画像表示装置の製造方法 Download PDFInfo
- Publication number
- JP6772402B1 JP6772402B1 JP2020536897A JP2020536897A JP6772402B1 JP 6772402 B1 JP6772402 B1 JP 6772402B1 JP 2020536897 A JP2020536897 A JP 2020536897A JP 2020536897 A JP2020536897 A JP 2020536897A JP 6772402 B1 JP6772402 B1 JP 6772402B1
- Authority
- JP
- Japan
- Prior art keywords
- polarizer
- film
- polyvinyl alcohol
- polarizing film
- roll
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
本発明の偏光子の製造方法は、ポリビニルアルコール系フィルムに、少なくとも、染色工程、架橋工程、および延伸工程を施した後に、乾燥工程を施して得られる偏光子の製造方法であって、前記染色工程、架橋工程、および延伸工程の少なくとも1つの処理浴は、亜鉛イオンを含有し、前記乾燥工程は、亜鉛を含有するポリビニルアルコール系フィルムを複数のロールにより搬送しながら乾燥させて、厚さが20μm以下であり、かつ水分率が13重量%以上19重量%以下である偏光子を製造する工程であり、前記複数のロールは、ポリビニルアルコール系フィルムの搬送方向の最上流側に設けられた第1ロールと、ポリビニルアルコール系フィルムの搬送方向の最下流側に設けられた第2ロールと、前記第1ロールと前記第2ロールの間に設けられた1つ以上の第3ロールを含み、前記1つ以上の第3ロールのうち、少なくとも1つのロールは、当該ロールと前記ポリビニルアルコール系フィルムとの抱き角が90°以下である。
前記染色工程は、ポリビニルアルコール系フィルムを、染色浴(ヨウ素溶液)に浸漬する処理工程であり、ポリビニルアルコール系フィルムに、ヨウ素または二色性染料等の二色性物質を吸着・配向させることができる。前記ヨウ素溶液は、通常、ヨウ素水溶液であることが好ましく、ヨウ素および溶解助剤としてヨウ化物を含有する。なお、前記ヨウ化物としては、ヨウ化カリウム、ヨウ化リチウム、ヨウ化ナトリウム、ヨウ化亜鉛、ヨウ化アルミニウム、ヨウ化鉛、ヨウ化銅、ヨウ化バリウム、ヨウ化カルシウム、ヨウ化錫、ヨウ化チタン等が挙げられる。これらの中でも、ヨウ化カリウムが好適である。
前記架橋工程は、前記染色工程にて染色されたポリビニルアルコール系フィルムを、ホウ素化合物を含む処理浴(架橋浴)中に浸漬する処理工程であり、ホウ素化合物によりポリビニルアルコール系フィルムが架橋して、ヨウ素分子または染料分子が当該架橋構造に吸着できる。前記ホウ素化合物としては、例えば、ホウ酸、ホウ酸塩、ホウ砂等が挙げられる。前記架橋浴は、水溶液が一般的であるが、例えば、水との混和性のある有機溶媒および水の混合溶液であってもよい。また、前記架橋浴は、ヨウ化カリウム等のヨウ化物を含むことができる。
前記延伸工程は、ポリビニルアルコール系フィルムを、少なくとも一方向に所定の倍率に延伸する処理工程である。一般には、ポリビニルアルコール系フィルムを、搬送方向(長手方向)に1軸延伸する。前記延伸の方法は特に制限されず、湿潤延伸法と乾式延伸法(ロール間延伸方法、加熱ロール延伸方法、圧縮延伸方法等)のいずれも採用できるが、本発明では、湿潤式延伸方法を用いるのが好ましい。前記延伸工程は1回だけ実施されてもよく、必要に応じて複数回実施されてもよい。前記延伸工程は、偏光子の製造において、いずれの段階で行われてもよい。
前記膨潤工程は、ポリビニルアルコール系フィルムを、膨潤浴中に浸漬する処理工程であり、ポリビニルアルコール系フィルムの表面の汚れやブロッキング剤等を除去でき、また、ポリビニルアルコール系フィルムを膨潤させることで染色ムラを抑制できる。前記膨潤浴は、通常、水、蒸留水、純水等の水を主成分とする媒体が用いられる。前記膨潤浴は、常法に従って、界面活性剤、アルコール等が適宜に添加されていてもよい。
前記洗浄工程は、ポリビニルアルコール系フィルムを、洗浄浴中に浸漬する処理工程であり、ポリビニルアルコール系フィルムの表面等に残存する異物を除去できる。前記洗浄浴は、通常、水、蒸留水、純水等の水を主成分とする媒体が用いられる。また、前記洗浄浴にヨウ化カリウム等のヨウ化物を使用することができ、この場合、前記洗浄浴中、ヨウ化カリウム等のヨウ化物の濃度は、1〜10重量%程度であることが好ましく、2〜4重量%程度であることがより好ましく、1.6〜3.8重量%程度であることがさらに好ましい。
前記乾燥工程は、亜鉛を含有するポリビニルアルコール系フィルムを複数のロールにより搬送しながら乾燥させて、厚さが20μm以下であり、かつ水分率が13重量%以上19重量%以下である偏光子を製造する工程であり、前記複数のロールは、ポリビニルアルコール系フィルムの搬送方向の最上流側に設けられた第1ロールと、ポリビニルアルコール系フィルムの搬送方向の最下流側に設けられた第2ロールと、前記第1ロールと前記第2ロールの間に設けられた1つ以上の第3ロールを含み、前記1つ以上の第3ロールのうち、少なくとも1つのロールは、当該ロールと前記ポリビニルアルコール系フィルムとの抱き角が90°以下である。
水分率(重量%)={(初期重量−乾燥重量)/初期重量}×100
本発明の偏光フィルムの製造方法は、前記偏光子の少なくとも片面に接着剤層を介して透明保護フィルムを貼り合わせる工程を含む。
本発明の積層偏光フィルム(光学積層体)の製造方法は、前記偏光フィルムに光学層を貼り合わせる工程を含む。
本発明の画像表示パネルの製造方法は、画像表示セルに、前記偏光フィルム、または前記積層偏光フィルムを貼り合わせる工程を含む。また、本発明の画像表示装置の製造方法は、前記画像表示パネルの偏光フィルムまたは積層偏光フィルム側(視認側)に、透明板を設ける工程を含む。
<偏光子の製造>
平均重合度が2,400、ケン化度が99.9モル%、厚みが45μm、幅が2600mmであるポリビニルアルコールフィルムを用意した。ポリビニルアルコールフィルムを、周速比の異なるロール間で、28℃の膨潤浴(水浴)中に30秒間浸漬して膨潤しながら搬送方向に2.4倍に延伸し(膨潤工程)、続いて、25℃の染色浴(ヨウ素濃度が0.03重量%、ヨウ化カリウム濃度が0.3重量%である水溶液)中で45秒間浸漬して染色しながら元のポリビニルアルコールフィルム(搬送方向に全く延伸していないポリビニルアルコールフィルム)を基準にして搬送方向に3.7倍に延伸した(染色工程)。次いで、染色したポリビニルアルコールフィルムを、40℃の架橋浴(ホウ酸濃度が3.0重量%、ヨウ化カリウム濃度が3.0重量%、硫酸亜鉛が3.6重量%(亜鉛イオン濃度が1.5重量%)である水溶液)中で20秒間浸漬して元のポリビニルアルコールフィルムを基準にして搬送方向に4.2倍まで延伸した(架橋工程)。さらに、得られたポリビニルアルコールフィルムを、65℃の延伸浴(ホウ酸濃度が4.0重量%、ヨウ化カリウム濃度が5.0重量%、硫酸亜鉛濃度が5.0重量%(亜鉛イオン濃度が2.0重量%)である水溶液)中で50秒間浸漬して元のポリビニルアルコールフィルムを基準にして搬送方向に6.0倍まで延伸した(延伸工程)後、27℃の洗浄浴(ヨウ化カリウム濃度が2.5重量%である水溶液)中で5秒間浸漬した(洗浄工程)。洗浄したポリビニルアルコールフィルムを、図2に示すようなロールの配置(ロールの全数が10個;第3ロール中、最大の抱き角が43°)を有するオーブンを用い、25℃で2分間乾燥して偏光子を作製した。ポリビニルアルコールフィルムの第3ロールに対する接触距離と、ポリビニルアルコールフィルムの全搬送距離との比(接触距離/全搬送距離)が0.09であった。また、オーブン内の複数のロールにおけるロール間の最大距離(LMAX)と、乾燥工程前の前記亜鉛を含有するポリビニルアルコール系フィルムの幅(W1)との比(LMAX/W1)が0.21であった。得られた偏光子の厚みは18μmであり、偏光子の水分率は17.2重量%であり、W2/W1は0.97であった。
接着剤として、アセトアセチル基を含有するポリビニルアルコール樹脂(平均重合度が1,200、ケン化度が98.5モル%、アセトアセチル化度が5モル%)とメチロールメラミンとを重量比3:1で含有する水溶液を用いた。この接着剤を用いて、第2透明保護フィルムとして、上記で得られた偏光子の一方の面(画像表示セル側表面)に、(メタ)アクリル系樹脂(ラクトン環構造を有する変性アクリル系ポリマー)からなる厚み30μmの透明保護フィルム(飽和吸水量が0.2g/m2、透湿度が125g/(m2・24h))、(以下、このフィルムを「透明フィルムA」と称する)、また、第1透明保護フィルムとして、他方の面(視認側)に、ハードコート層を有する厚み40μmのトリアセチルセルロースフィルム(透湿度が342g/(m2・24h)、コニカミノルタ製、商品名「KC4UYW」)(以下、このフィルムを「透明フィルムB」と称する)をロール貼合機で貼り合わせた後、引き続きオーブン内で加熱乾燥(温度が88℃、時間が10分間)させて、偏光子の両面に透明保護フィルムが貼り合わせられた偏光フィルムを作製した。
上記で得られた偏光フィルムを、偏光子の吸収軸が長辺となるように150×50cmのサイズに切断し、偏光フィルムの一方の面(透明フィルムA側の面)に、厚み20μmのアクリル系粘着剤層を介してガラス板(疑似画像表示セル)を貼り合わせ、偏光フィルムの他方の面(透明フィルムB側の面)に厚み200μmのアクリル酸モノマーフリー粘着剤(日東電工(株)製、商品名「LUCIACS CS9868」)を介して別のガラス板を貼り合わせて、疑似画像表示装置を作製した。
上記で得られた偏光フィルムの外観を目視にて以下の基準にて評価した。結果を表1に示す。
〇:外観に異常がない、もしくは10個/m2未満の偏光ムラが発生する。
×:10個/m2以上の偏光ムラが発生する。
上記で得られた偏光子の外観を目視にて以下の基準にて評価した。結果を表1に示す。
〇:視認可能な偏光子の折れが発生していない。
×:視認可能な偏光子の折れが発生している。
上記で得られた疑似画像表示装置を、温度95℃の熱風オーブン内に500時間静置し、投入(加熱)後の外観を目視で以下の基準で評価した。結果を表1に示す。
○:外観に異常がない。
×:偏光子に視認可能なムラが発生する。
<偏光子、偏光フィルム、疑似画像表示装置の作製>
偏光子の作製において、乾燥工程での乾燥温度を35℃にしたこと以外は、実施例1と同様の操作にて、偏光子を作製した。得られた偏光子の厚みは17μmであり、偏光子の水分率は14.3重量%であり、W2/W1は0.95であった。得られた偏光子を用い、実施例1と同様な操作にて、偏光フィルム、疑似画像表示装置を作製した。
<偏光子、偏光フィルム、疑似画像表示装置の作製>
平均重合度が2,400、ケン化度が99.9モル%、厚みが30μm、幅が2600mmであるポリビニルアルコールフィルムを用意した。ポリビニルアルコールフィルムを、周速比の異なるロール間で、20℃の膨潤浴(水浴)中に30秒間浸漬して膨潤しながら搬送方向に2.4倍に延伸し(膨潤工程)、続いて、25℃の染色浴(ヨウ素濃度が0.045重量%、ヨウ化カリウム濃度が0.45重量%である水溶液)中で45秒間浸漬して染色しながら元のポリビニルアルコールフィルム(搬送方向に全く延伸していないポリビニルアルコールフィルム)を基準にして搬送方向に3.7倍に延伸した(染色工程)。次いで、染色したポリビニルアルコールフィルムを、40℃の架橋浴(ホウ酸濃度が3.0重量%、ヨウ化カリウム濃度が3.0重量%、硫酸亜鉛が3.6重量%(亜鉛イオン濃度が1.5重量%)である水溶液)中で20秒間浸漬して元のポリビニルアルコールフィルムを基準にして搬送方向に4.2倍まで延伸した(架橋工程)。さらに、得られたポリビニルアルコールフィルムを、65℃の延伸浴(ホウ酸濃度が4.0重量%、ヨウ化カリウム濃度が5.0重量%、硫酸亜鉛濃度が5.0重量%(亜鉛イオン濃度が2.0重量%)である水溶液)中で50秒間浸漬して元のポリビニルアルコールフィルムを基準にして搬送方向に6.0倍まで延伸した(延伸工程)後、20℃の洗浄浴(ヨウ化カリウム濃度が3.0重量%である水溶液)中で5秒間浸漬した(洗浄工程)。洗浄したポリビニルアルコールフィルムを、図2に示すようなロールの配置(ロールの全数が10個;第3ロール中、最大の抱き角が43°)を有するオーブンを用い、18℃で2分間乾燥して偏光子を作製した。ポリビニルアルコールフィルムの第3ロールに対する接触距離と、ポリビニルアルコールフィルムの全搬送距離との比(接触距離/全搬送距離)が0.09であった。また、オーブン内の複数のロールにおけるロール間の最大距離(LMAX)と、乾燥工程前の前記亜鉛を含有するポリビニルアルコール系フィルムの幅(W1)との比(LM AX/W1)が0.20であった。得られた偏光子の厚みは12μmであり、偏光子の水分率は17.6重量%であり、W2/W1は0.97であった。得られた偏光子を用い、実施例1と同様な操作にて、偏光フィルム、疑似画像表示装置を作製した。
<偏光子、偏光フィルム、疑似画像表示装置の作製>
偏光子の作製において、乾燥工程での乾燥温度を25℃にしたこと以外は、実施例3と同様の操作にて、偏光子を作製した。得られた偏光子の厚みは12μmであり、偏光子の水分率は14.5重量%であり、W2/W1は0.95であった。得られた偏光子を用い、実施例1と同様な操作にて、偏光フィルム、疑似画像表示装置を作製した。
偏光子の作製において、乾燥工程で図5に示すようなロールの配置(ロールの全数が8個;第3ロール中、最大の抱き角が88°)を有するオーブンを用い、28℃で3分間乾燥して偏光子を作製したこと以外は、実施例1と同様の操作にて、偏光子を作製した。ポリビニルアルコールフィルムの第3ロールに対する接触距離と、ポリビニルアルコールフィルムの全搬送距離との比(接触距離/全搬送距離)が0.09であった。得られた偏光子の厚みは18μmであり、偏光子の水分率は15.0重量%であり、W2/W1は0.92であった。また、オーブン内の複数のロールにおけるロール間の最大距離(LMAX)と、乾燥工程前の前記亜鉛を含有するポリビニルアルコール系フィルムの幅(W1)との比(LMAX/W1)が0.82であった。得られた偏光子を用い、実施例1と同様な操作にて、偏光フィルム、疑似画像表示装置を作製した。
<偏光子、偏光フィルム、疑似画像表示装置の作製>
偏光子の作製において、乾燥工程での乾燥温度を45℃にしたこと以外は、実施例1と同様の操作にて、偏光子を作製した。得られた偏光子の厚みは17μmであり、偏光子の水分率は12.5重量%であり、W2/W1は0.91であった。得られた偏光子を用い、実施例1と同様な操作にて、偏光フィルム、疑似画像表示装置を作製した。
<偏光子、偏光フィルム、疑似画像表示装置の作製>
偏光子の作製において、乾燥工程での乾燥温度を17℃にしたこと以外は、実施例1と同様の操作にて、偏光子を作製した。得られた偏光子の厚みは18μmであり、偏光子の水分率は19.1重量%であり、W2/W1は0.98であった。得られた偏光子を用い、実施例1と同様な操作にて、偏光フィルム、疑似画像表示装置を作製した。
<偏光子、偏光フィルム、疑似画像表示装置の作製>
偏光子の作製において、乾燥工程で図3に示すようなロールの配置(ロールの全数が18個;第3ロール中、最大の抱き角が176°)を有するオーブンを用い、28℃で5分間乾燥して偏光子を作製したこと以外は、実施例1と同様の操作にて、偏光子を作製した。また、オーブン内の複数のロールにおけるロール間の最大距離(LMAX)と、乾燥工程前の前記亜鉛を含有するポリビニルアルコール系フィルムの幅(W1)との比(LMA X/W1)が0.82であった。得られた偏光子の厚みは17μmであり、偏光子の水分率は14.3重量%であり、W2/W1は0.84であった。得られた偏光子を用い、実施例1と同様な操作にて、偏光フィルム、疑似画像表示装置を作製した。なお、ポリビニルアルコールフィルムの第3ロールに対する接触距離と、ポリビニルアルコールフィルムの全搬送距離との比(接触距離/全搬送距離)が0.13であった。
<偏光子、偏光フィルム、疑似画像表示装置の作製>
偏光子の作製において、乾燥工程で図4に示すようなロールの配置(ロールの全数が6個;第3ロール中、最大の抱き角が134°)を有するオーブンを用い、31℃で3分間乾燥して偏光子を作製したこと以外は、実施例1と同様の操作にて、偏光子を作製した。得られた偏光子の厚みは17μmであり、偏光子の水分率は14.3重量%であり、W2/W1は0.88であった。また、オーブン内の複数のロールにおけるロール間の最大距離(LMAX)と、乾燥工程前の前記亜鉛を含有するポリビニルアルコール系フィルムの幅(W1)との比(LMAX/W1)が0.98であった。得られた偏光子を用い、実施例1と同様な操作にて、偏光フィルム、疑似画像表示装置を作製した。なお、ポリビニルアルコールフィルムの第3ロールに対する接触距離と、ポリビニルアルコールフィルムの全搬送距離との比(接触距離/全搬送距離)が0.08であった。
<偏光子、偏光フィルム、疑似画像表示装置の作製>
偏光子の作製において、乾燥工程でロールを有しないオーブンにて、25℃で2分間乾燥したこと以外は、実施例1と同様の操作にて、偏光子を作製した。得られた偏光子の厚みは18μmであり、偏光子の水分率は17.4重量%であり、W2/W1は0.81であった。得られた偏光子を用い、実施例1と同様な操作にて、偏光フィルム、疑似画像表示装置を作製した。
<偏光子、偏光フィルム、疑似画像表示装置の作製>
偏光子の作製において、架橋浴および延伸浴中に硫酸亜鉛を用いなかったこと以外は、実施例1と同様の操作にて、偏光子を作製した。得られた偏光子の厚みは18μmであり、偏光子の水分率は17.2重量%であり、W2/W1は0.96であった。得られた偏光子を用い、実施例1と同様な操作にて、偏光フィルム、疑似画像表示装置を作製した。
<偏光子、偏光フィルム、疑似画像表示装置の作製>
平均重合度が2,700、ケン化度が99.9モル%、厚みが75μm、幅が2600mmであるポリビニルアルコールフィルムを用意し、染色浴の濃度を、ヨウ素濃度が0.02重量%、ヨウ化カリウム濃度が0.2重量%に調整し、乾燥工程で図3に示すようなロールの配置(ロールの全数が18個;第3ロール中、最大の抱き角が176°)を有するオーブンを用い、45℃で5分間乾燥して偏光子を作製したこと以外は、実施例1と同様の操作にて、偏光子を作製した。また、オーブン内の複数のロールにおけるロール間の最大距離(LMAX)と、乾燥工程前の前記亜鉛を含有するポリビニルアルコール系フィルムの幅(W1)との比(LMAX/W1)が0.82であった。得られた偏光子の厚みは28μmであり、偏光子の水分率は14.5重量%であり、W2/W1は0.86であった。得られた偏光子を用い、実施例1と同様な操作にて、偏光フィルム、疑似画像表示装置を作製した。
R ロール
θ 抱き角の角度
L1 空走距離
Claims (10)
- ポリビニルアルコール系フィルムに、少なくとも、染色工程、架橋工程、および延伸工程を施した後に、乾燥工程を施して得られる偏光子の製造方法であって、
前記染色工程、架橋工程、および延伸工程の少なくとも1つの処理浴は、亜鉛イオンを含有し、
前記乾燥工程は、亜鉛を含有するポリビニルアルコール系フィルムを複数のロールにより搬送しながら乾燥させて、厚さが20μm以下であり、かつ水分率が13重量%以上19重量%以下である偏光子を製造する工程であり、
前記複数のロールは、ポリビニルアルコール系フィルムの搬送方向の最上流側に設けられた第1ロールと、
ポリビニルアルコール系フィルムの搬送方向の最下流側に設けられた第2ロールと、
前記第1ロールと前記第2ロールの間に設けられた1つ以上の第3ロールを含み、
前記1つ以上の第3ロールのうち、少なくとも1つのロールは、当該ロールと前記ポリビニルアルコール系フィルムとの抱き角が90°以下であることを特徴とする偏光子の製造方法。 - 前記乾燥工程において、前記亜鉛を含有するポリビニルアルコール系フィルムの前記第3ロールに対する接触距離と、前記亜鉛を含有するポリビニルアルコール系フィルムの全搬送距離との比(接触距離/全搬送距離)が、0.1以下であることを特徴とする請求項1記載の偏光子の製造方法。
- 前記複数のロールにおけるロール間の最大距離(LMAX)と、乾燥工程前の前記亜鉛を含有するポリビニルアルコール系フィルムの幅(W1)との比(LMAX/W1)が、2以下であることを特徴とする請求項1または2記載の偏光子の製造方法。
- 前記偏光子は、乾燥工程前の前記亜鉛を含有するポリビニルアルコール系フィルムの幅(W1)と、乾燥工程後に得られた前記偏光子の幅(W2)との比(W2/W1)が、0.9以上1未満であることを特徴とする請求項1〜3の何れかに記載の偏光子の製造方法。
- 請求項1〜4の何れかに記載の偏光子の製造方法で得られた偏光子の少なくとも片面に接着剤層を介して透明保護フィルムを貼り合わせる工程を含むことを特徴とする偏光フィルムの製造方法。
- 前記接着剤層を形成する接着剤は、水系接着剤であることを特徴とする請求項5記載の偏光フィルムの製造方法。
- 前記透明保護フィルムは、透湿度が200g/(m2・24h)以下であることを特徴とする請求項5または6記載の偏光フィルムの製造方法。
- 請求項5〜7の何れかに記載の偏光フィルムの製造方法で得られた偏光フィルムに光学層を貼り合わせる工程を含むことを特徴とする積層偏光フィルムの製造方法。
- 画像表示セルに、請求項5〜7の何れかに記載の偏光フィルムの製造方法で得られた偏光フィルム、または請求項8記載の積層偏光フィルムの製造方法で得られた積層偏光フィルムを貼り合わせる工程を含むことを特徴とする画像表示パネルの製造方法。
- 請求項9記載の画像表示パネルの製造方法で得られた画像表示パネルの偏光フィルムまたは積層偏光フィルム側に、透明板を設ける工程を含むことを特徴とする画像表示装置の製造方法。