JP6646636B2 - 改良された化学的および機械的耐久性を有するアルカリ土類アルミノケイ酸ガラス組成物 - Google Patents
改良された化学的および機械的耐久性を有するアルカリ土類アルミノケイ酸ガラス組成物 Download PDFInfo
- Publication number
- JP6646636B2 JP6646636B2 JP2017168242A JP2017168242A JP6646636B2 JP 6646636 B2 JP6646636 B2 JP 6646636B2 JP 2017168242 A JP2017168242 A JP 2017168242A JP 2017168242 A JP2017168242 A JP 2017168242A JP 6646636 B2 JP6646636 B2 JP 6646636B2
- Authority
- JP
- Japan
- Prior art keywords
- mol
- glass
- glass composition
- composition
- alkali
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
Claims (7)
- ISO720−1985試験規格に準じて試験されてクラスHGA1耐加水分解性を有するアルカリアルミノケイ酸ガラスから形成されるガラス本体を含むガラス医薬品パッケージであって、前記アルカリアルミノケイ酸ガラスが、
65モル%〜75モル%のSiO2と、
6モル%〜12.5モル%のAl2O3と、
2.5モル%〜12モル%のNa2Oと
0モル%〜2.5モル%のK2Oと、
1モル%〜2.0モル%のSrOと、
3モル%〜7モル%のCaOと、
を含み、
前記ガラスはイオン交換による強化に対し感受性を有し、
前記ガラスはホウ素およびホウ素化合物を含まない、
ことを特徴とするガラス医薬品パッケージ。 - 前記ガラスがさらに、5モル%〜12モル%のアルカリ酸化物を含むことを特徴とする請求項1に記載のガラス医薬品パッケージ。
- 前記ガラスがさらに、少なくとも2つのアルカリ酸化物を含むことを特徴とする請求項3に記載のガラス医薬品パッケージ。
- 前記ガラスがさらに、2モル%〜7モル%のMgOを含むことを特徴とする請求項1に記載のガラス医薬品パッケージ。
- 二価カチオンの濃度の合計に対するMgOの濃度の比(MgO;ΣRO)が0.3未満であることを特徴とする請求項1に記載のガラス医薬品パッケージ。
- 65モル%〜75モル%のSiO2と、
6モル%〜12.5モル%のAl2O3と、
5モル%〜12モル%のアルカリ酸化物と
1モル%〜2.0モル%のSrOと、
3モル%〜7モル%のCaOと、
を含むガラス組成物であって、
二価カチオンの濃度の合計に対するMgOの濃度の比(MgO;ΣRO)が0.3未満であり、
前記ガラス組成物がホウ素を含まず、
前記ガラス組成物がBaOを含まず、
前記ガラス組成物がイオン交換による強化に対し感受性を有する、
ことを特徴とするガラス組成物。 - 前記ガラス組成物が、8モル%〜15モル%のアルカリ土類酸化物を含むことを特徴とする請求項6に記載のガラス組成物。