JP6582606B2 - スピネル−マグネシア−カーボン質煉瓦 - Google Patents
スピネル−マグネシア−カーボン質煉瓦 Download PDFInfo
- Publication number
- JP6582606B2 JP6582606B2 JP2015126283A JP2015126283A JP6582606B2 JP 6582606 B2 JP6582606 B2 JP 6582606B2 JP 2015126283 A JP2015126283 A JP 2015126283A JP 2015126283 A JP2015126283 A JP 2015126283A JP 6582606 B2 JP6582606 B2 JP 6582606B2
- Authority
- JP
- Japan
- Prior art keywords
- spinel
- magnesia
- mass
- raw material
- carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
以下に実施例及び比較例を提示して、本発明のマグネシア−スピネル−カーボン質煉瓦を説明する。なお、本発明は以下の例示に限定されるものではない。
弾性率変化率=(試験前弾性率−試験後弾性率)/試験前弾性率×100 (1)
弾性率変化率の数値が小さいほど耐熱スポーリング性は良いと評価することができる。なお、弾性率変化率が40%以下であれば実用上問題なく使用可能であり、弾性率変化率が20%以下であることがより好ましい品質である。そのため、弾性率変化率が40%より大きい場合を不適合と判定している。
(実施例2)
実施例3、11、13の煉瓦と比較例1の煉瓦を、300トン転炉の底吹き羽口周辺の炉底煉瓦に適用した。2658チャージ使用後に回収し、残厚から損傷速度を比較した。実施例3、11、13の煉瓦の損傷速度は、それぞれ0.45mm/チャージ、0.43mm/チャージ、0.37mm/チャージであるのに対し、比較例1の煉瓦の損傷速度は0.52mm/チャージであった。すなわち、実施例13の煉瓦は比較例1の煉瓦よりも約28%損傷が小さいという優れた結果であった。
Claims (2)
- カーボン原料を3質量%以上かつ17質量%以下含有するスピネル−マグネシア−カーボン質煉瓦であって、
スピネル原料とマグネシア原料との和を100質量部とした場合、スピネル原料の含有量が50質量%以上かつ95質量%以下であり、マグネシア原料の含有量が5質量%以上かつ50質量%以下であるとともに、前記スピネル原料が、理論組成スピネル又はアルミナリッチスピネルであり、前記スピネル原料に含まれる、粒子径10μm以下のスピネル粒子の量が、スピネル原料、マグネシア原料及びカーボン原料の全量に対して2質量%以上15質量%以下であるスピネル−マグネシア−カーボン質煉瓦。 - 前記マグネシア原料の粒子径が0.3mm以上である請求項1記載のスピネル−マグネシア−カーボン質煉瓦。