JP6466871B2 - Foreign matter removing lubricating composition, foreign material removing lubricating composition coating member, and method of using foreign matter removing lubricating composition - Google Patents
Foreign matter removing lubricating composition, foreign material removing lubricating composition coating member, and method of using foreign matter removing lubricating composition Download PDFInfo
- Publication number
- JP6466871B2 JP6466871B2 JP2016039081A JP2016039081A JP6466871B2 JP 6466871 B2 JP6466871 B2 JP 6466871B2 JP 2016039081 A JP2016039081 A JP 2016039081A JP 2016039081 A JP2016039081 A JP 2016039081A JP 6466871 B2 JP6466871 B2 JP 6466871B2
- Authority
- JP
- Japan
- Prior art keywords
- foreign matter
- matter removing
- lubricating composition
- fluoropolyether
- containing compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
この発明は、異物除去潤滑組成物、異物除去潤滑組成物の塗布部材、及び、異物除去潤滑組成物の使用方法に関する。 The present invention relates to a foreign matter removing lubricant composition, an application member of the foreign matter removing lubricant composition, and a method of using the foreign matter removing lubricant composition.
ドアロック機構、ウインドレギュレータ、シートレール、及び、サンルーフ等の自動車部品、及び各種機器における摺動部を備えた部材には、潤滑油、或いは、グリースが使用されている。 Lubricating oil or grease is used for members having sliding parts in door parts, window regulators, seat rails, sunroofs and other automobile parts and various devices.
ところで、粉塵、砂等の異物が潤滑油、或いは、グリースに混入すると、摺動部材の摩耗が促進し、場合によっては異音を発生させてしまうという問題点があった。 By the way, when foreign matters such as dust and sand are mixed in the lubricating oil or grease, there is a problem that the wear of the sliding member is promoted and abnormal noise is generated in some cases.
従来の技術として、例えば、高架橋樹脂添加グリース組成物による潤滑性の向上が知られている(特許文献1参照)。 As a conventional technique, for example, improvement of lubricity by a highly crosslinked resin-added grease composition is known (see Patent Document 1).
しかしながら、上記高架橋樹脂添加グリース組成物には、粉塵、砂等の異物を除去する作用がないため、摩耗、異音を抑えることはできなかった。 However, since the above-mentioned highly crosslinked resin-added grease composition has no action of removing foreign matters such as dust and sand, it has not been possible to suppress wear and noise.
そこで本発明は、上記問題に鑑みてなされたもので、異物除去効果が高く、潤滑性を従来に比べて向上させることが可能な異物除去潤滑組成物、異物除去潤滑組成物の塗布部材、及び、異物除去潤滑組成物の使用方法を提供することを目的とする。 Accordingly, the present invention has been made in view of the above problems, and has a high foreign matter removing effect and a foreign matter removing lubricating composition capable of improving the lubricity as compared with the prior art, an application member of the foreign matter removing lubricating composition, and Another object of the present invention is to provide a method of using the foreign matter removing lubricating composition.
本発明における異物除去潤滑組成物は、ドアロック機構、ウインドレギュレータ、シートレール、及びサンルーフの各自動車部品に適用される異物除去潤滑組成物であって、フルオロポリエーテル含有化合物と、潤滑油或いはグリースの潤滑成分と、を含み、前記フルオロポリエーテル含有化合物は、フッ素原子よりも、前記潤滑成分への親和性が高い官能基を有することを特徴とする。 The foreign matter removing lubricating composition in the present invention is a foreign matter removing lubricating composition applied to automobile parts such as a door lock mechanism, a window regulator, a seat rail, and a sunroof, and includes a fluoropolyether-containing compound and lubricating oil or grease. And the fluoropolyether-containing compound has a functional group having a higher affinity for the lubricating component than a fluorine atom .
本発明では、前記フルオロポリエーテル含有化合物は、前記異物除去潤滑組成物を100重量部としたとき、0.01重量部以上10重量部以下の範囲で含有されることが好ましい。 In the present invention, the fluoropolyether-containing compound is preferably contained in the range of 0.01 parts by weight or more and 10 parts by weight or less when the foreign matter removing lubricating composition is 100 parts by weight.
また本発明では、下記一般式(1)又は(2)で表される前記フルオロポリエーテル含有化合物を含有することが好ましい。 Moreover, in this invention, it is preferable to contain the said fluoro polyether containing compound represented by the following general formula (1) or (2).
また、本発明における異物除去潤滑組成物は、フルオロポリエーテル含有化合物と、潤滑油或いはグリースの潤滑成分と、を含み、前記フルオロポリエーテル含有化合物は、フッ素原子よりも、前記潤滑成分への親和性が高い官能基を有し、前記官能基は、カルボキシレート、アルキルアミド、カルボキシレートトリエタノールアミン、ジニトロベンゼン、メチルエステル、エトキシル化アルコール、アルキルアミド、ポリアミド、アルコキシシラン、ホスフェート、ウレタンメタクリレート、及び、ウレタンアルキレートのうち、少なくともいずれか1種を備えることを特徴とする。
或いは、本発明における異物除去潤滑組成物は、フルオロポリエーテル含有化合物と、潤滑油或いはグリースの潤滑成分と、を含み、前記フルオロポリエーテル含有化合物は、フッ素原子よりも、前記潤滑成分への親和性が高い官能基を有し、下記一般式(1)又は(2)で表される前記フルオロポリエーテル含有化合物を含有することを特徴とする。
Alternatively, the foreign matter removing lubricating composition in the present invention includes a fluoropolyether-containing compound and a lubricating component of a lubricating oil or grease, and the fluoropolyether-containing compound has an affinity for the lubricating component rather than fluorine atoms. It has a highly functional functional group and contains the fluoropolyether-containing compound represented by the following general formula (1) or (2).
また本発明では、前記潤滑成分として、鉱物油、合成炭化水素油、ジエステル油、ポリオールエステル油、エーテル油、グリコール油、シリコーン油、及び、フッ素油のうち、少なくともいずれか1種から選択されることが好ましい。 In the present invention, the lubricating component is selected from at least one of mineral oil, synthetic hydrocarbon oil, diester oil, polyol ester oil, ether oil, glycol oil, silicone oil, and fluorine oil. It is preferable.
また本発明では、前記グリースに含まれる増ちょう剤は、リチウム石けん、カルシウム石けん、ナトリウム石けん、アルミニウム石けん、リチウム複合石けん、カルシウム複合石けん、アルミニウム複合石けん、ウレア化合物、有機化ベントナイト、ポリテトラフルオロエチレン、シリカゲル、ナトリウムテレフタラメートのうち、少なくともいずれか1種から選択されることが好ましい。 In the present invention, the thickener contained in the grease includes lithium soap, calcium soap, sodium soap, aluminum soap, lithium composite soap, calcium composite soap, aluminum composite soap, urea compound, organic bentonite, polytetrafluoroethylene. , Silica gel, and sodium terephthalate are preferably selected from at least one of them.
また本発明では、前記フルオロポリエーテル含有化合物と、前記潤滑油とを含む前記異物除去潤滑組成物に対し、JIS Z 8901に定められた、少なくとも7種或いは8種を備えた異物を加えた場合に、前記異物の沈降が観測されることが好ましい。 Further, in the present invention, when a foreign matter having at least 7 or 8 types as defined in JIS Z 8901 is added to the foreign matter removing lubricating composition containing the fluoropolyether-containing compound and the lubricating oil. In addition, it is preferable that sedimentation of the foreign matter is observed.
また本発明では、前記フルオロポリエーテル含有化合物と、前記グリースの潤滑成分とを含む前記異物除去潤滑組成物に対し、JIS Z 8901に定められた少なくとも、1種或いは2種を備えた異物を加えて測定した摩擦係数は、前記フルオロポリエーテル含有化合物を含まず、前記異物を加えた潤滑組成物の摩擦係数に比べて小さいことが好ましい。 Further, in the present invention, a foreign substance having at least one or two kinds defined in JIS Z 8901 is added to the foreign substance removing lubricating composition containing the fluoropolyether-containing compound and the lubricating component of the grease. The friction coefficient measured in this manner preferably does not include the fluoropolyether-containing compound and is smaller than the friction coefficient of the lubricating composition to which the foreign matter is added.
また本発明では、前記フルオロポリエーテル含有化合物と、前記グリースの潤滑成分とを含む前記異物除去潤滑組成物に対し、JIS Z 8901に定められた、少なくとも1種或いは2種を備えた異物を加えて測定した初期時の摩擦係数をμ1、前記異物を加えずに測定した初期時の摩擦係数をμ0としたとき、{(μ1−μ0)/μ0}×100で示される前記摩擦係数の変化率(%)は、40%未満であることが好ましい。 Further, in the present invention, a foreign substance having at least one or two kinds as defined in JIS Z 8901 is added to the foreign substance removing lubricating composition containing the fluoropolyether-containing compound and the lubricating component of the grease. When the initial friction coefficient measured by the above is μ1, and the initial friction coefficient measured without adding the foreign matter is μ0, the rate of change of the friction coefficient represented by {(μ1-μ0) / μ0} × 100 (%) Is preferably less than 40%.
また本発明では、上記に記載の前記異物除去潤滑組成物が、塵埃を含む環境下に置かれることを特徴とする。 Moreover, in this invention, the said foreign material removal lubricating composition as described above is placed in an environment containing dust.
本発明では、前記塵埃は、前記異物除去潤滑組成物の50%以下の体積比率とされることが好ましい。 In the present invention, it is preferable that the dust has a volume ratio of 50% or less of the foreign matter removing lubricant composition.
また本発明では、前記塵埃には、SiO2が主成分として含まれることが好ましい。 In the present invention, the dust preferably contains SiO 2 as a main component.
また本発明における異物除去潤滑組成物の塗布部材は、上記に記載の前記異物除去潤滑組成物を塗布した部材が、塵埃を含む環境下に置かれることを特徴とする。 Moreover, the application member of the foreign matter removing lubricating composition in the present invention is characterized in that the member applied with the foreign matter removing lubricating composition described above is placed in an environment containing dust.
また本発明における異物除去潤滑組成物の使用方法は、上記に記載の前記異物除去潤滑組成物を塗布した部材が、塵埃を含む環境下にて使用されることを特徴とする。 Further, the method for using the foreign matter removing lubricating composition in the present invention is characterized in that the member coated with the foreign matter removing lubricating composition described above is used in an environment containing dust.
本発明の異物除去潤滑組成物は、フルオロポリエーテル含有化合物を含有することで、異物除去効果を高めることができ、従来に比べて潤滑性を向上させることができる。 By containing the fluoropolyether-containing compound, the foreign matter removing lubricating composition of the present invention can enhance the foreign matter removing effect and improve the lubricity as compared with the conventional one.
以下、本発明の一実施の形態(以下、「実施の形態」と略記する。)について、詳細に説明する。なお、本発明は、以下の実施の形態に限定されるものではなく、その要旨の範囲内で種々変形して実施することができる。 Hereinafter, an embodiment of the present invention (hereinafter abbreviated as “embodiment”) will be described in detail. In addition, this invention is not limited to the following embodiment, It can implement by changing variously within the range of the summary.
本発明者らは、ドアロック機構、ウインドレギュレータ、シートレール、サンルーフ等の自動車部品、及び各種機器における摺動部を備えた部材に対して、潤滑油、或いは、グリースに各種の添加剤を配合し、粉塵、砂等の異物を含有した際の潤滑性を試験した。 The present inventors blend various additives in lubricating oil or grease for automobile parts such as door lock mechanisms, window regulators, seat rails, sunroofs, and members with sliding parts in various devices. Then, the lubricity when containing foreign matters such as dust and sand was tested.
その結果、固体潤滑剤については、一般的に固体で物理的な接触を防ぎ(摩耗)、転がり作用、分子間の滑り作用によって摩擦の低減及び固体で衝撃緩和をもたらす。しかしながら、摩耗、異音の発生を抑制することができず、異物混入時の潤滑性を飛躍的に向上させることはできなかった。また、スラッジを除去する作用のある清浄分散剤についても、異物の分散効果が発揮されるものの摩耗、異音の発生を抑制することができず、異物混入時の潤滑性を飛躍的に向上させるには至らなかった。 As a result, solid lubricants generally prevent solid physical contact (abrasion), and reduce friction and impact relaxation with solids by rolling and intermolecular sliding. However, the generation of wear and noise cannot be suppressed, and the lubricity when foreign matter is mixed cannot be improved dramatically. In addition, the cleaning dispersant that acts to remove sludge also exhibits the effect of dispersing foreign matter, but cannot suppress the occurrence of wear and abnormal noise, and dramatically improves the lubricity when foreign matter is mixed. It did not reach.
そこで本発明者らは、異物除去潤滑組成物について誠意研究した結果、フルオロポリエーテル含有化合物を含有した潤滑組成物を用いることで、従来に比べて効果的に、潤滑性を向上させることができることを見出した。 Therefore, as a result of sincere research on the foreign matter-removing lubricating composition, the present inventors can effectively improve the lubricity by using a lubricating composition containing a fluoropolyether-containing compound as compared with the conventional one. I found.
本実施の形態における異物除去潤滑組成物は、フルオロポリエーテル含有化合物を含有することを特徴とする。フルオロポリエーテル含有化合物は基本骨格として含まれる。基本骨格とは、繰り返し単位を意味し、フルオロポリエーテル含有化合物の一部が他の置換基で置換された状態のものも含む。「フルオロ」とは、炭素原子に結合した水素原子の少なくとも一部がフッ素原子に置換された状態のものであり、全てフッ素に置換された「パーフルオロ」も含まれる。 The foreign substance removing lubricating composition in the present embodiment is characterized by containing a fluoropolyether-containing compound. Fluoropolyether-containing compounds are included as the basic skeleton. The basic skeleton means a repeating unit, and includes one in which a part of the fluoropolyether-containing compound is substituted with another substituent. “Fluoro” refers to a state in which at least a part of hydrogen atoms bonded to carbon atoms are substituted with fluorine atoms, and “perfluoro” in which all are substituted with fluorine is also included.
フルオロポリエーテル含有化合物を含有した異物除去潤滑組成物を用いた際の、異物除去のメカニズムについては、以下のように推測される。 The foreign matter removal mechanism when using the foreign matter removing lubricating composition containing the fluoropolyether-containing compound is presumed as follows.
図1は、グリース中のフルオロポリエーテル含有化合物の挙動を示す模式図である。図1に示すように、異物除去潤滑組成物としてのグリースG中に含まれるフルオロポリエーテル含有化合物Sは、フッ素原子Fの電気陰性度が最も高いため、δ−に帯電し、官能基Rは、δ+に帯電している。 FIG. 1 is a schematic diagram showing the behavior of a fluoropolyether-containing compound in grease. As shown in FIG. 1, since the fluoropolyether-containing compound S contained in the grease G as the foreign matter removing lubricating composition has the highest electronegativity of the fluorine atom F, it is charged to δ−, and the functional group R is , Δ + are charged.
フッ素原子Fは、グリース(潤滑油)への親和性が官能基Rより小さいため、図1に示すようにグリース表面から外方に向けてフッ素原子Fが配列しやすくなる。なお図示していないが、フッ素原子Fは、グリースGを塗布する塗布面1を備える部材側でも配列している。また、グリース内部では、できる限り表面エネルギーを小さく保とうとするために、フッ素原子Fを内側に官能基Rを外側としたミセル構造にて配列している。 Since the fluorine atom F has a smaller affinity for grease (lubricating oil) than the functional group R, the fluorine atom F is likely to be arranged outward from the grease surface as shown in FIG. Although not shown, the fluorine atoms F are also arranged on the member side including the application surface 1 on which the grease G is applied. In order to keep the surface energy as small as possible inside the grease, the grease is arranged in a micelle structure with the fluorine atoms F on the inside and the functional groups R on the outside.
図2は、異物が混入されたグリース中のフルオロポリエーテル含有化合物の挙動を示す模式図である。図2は、異物CがグリースG内に混入した様子を示す。異物Cは、例えばSiO2を主成分とし、異物Cの表面はδ−に分極している。このため図2に示すように、異物Cには、電気的に中和するように、官能基(δ+)Rが吸着している。よって、フッ素原子Fが異物Cの外側(吸着側とは反対側)に配列した状態とされる。外側にフッ素原子Fが配列された異物Cは、グリースGとの親和性が小さい。その結果、異物Cは、グリースG中に浮遊しているような状態になり、グリースG表面方向に移行する作用が生じる(図2の矢印にて示す)。これにより異物Cは、グリースGの外部へ除去されやすい状態におかれる。そして、グリースGから除去された異物Cは、グリースGとの親和性の低いフッ素原子Fに外周面が覆われた状態となるため、グリースG中に混入しにくくなる(図2の×印を参照)。 FIG. 2 is a schematic diagram showing the behavior of the fluoropolyether-containing compound in the grease mixed with foreign matter. FIG. 2 shows a state in which the foreign matter C is mixed into the grease G. The foreign matter C has, for example, SiO 2 as a main component, and the surface of the foreign matter C is polarized δ−. For this reason, as shown in FIG. 2, the functional group (δ +) R is adsorbed on the foreign matter C so as to be electrically neutralized. Therefore, the fluorine atoms F are arranged outside the foreign substance C (on the side opposite to the adsorption side). The foreign matter C in which fluorine atoms F are arranged on the outside has a low affinity with the grease G. As a result, the foreign matter C is in a state of floating in the grease G, and an action of moving toward the surface of the grease G occurs (indicated by an arrow in FIG. 2). As a result, the foreign matter C is easily removed to the outside of the grease G. The foreign matter C removed from the grease G is in a state in which the outer peripheral surface is covered with the fluorine atoms F having low affinity with the grease G, and therefore, it is difficult for the foreign matter C to be mixed into the grease G (marked with a cross in FIG. 2). reference).
上記した異物除去作用は、例えば、部材同士が大きく移動するレールとスライダーのような摺動関係にある場合には、特に効果的である。すなわち、半固形状のグリースであっても、摺動により流動化し、フッ素原子で覆われた異物(図2参照)は、速やかにグリースの表面に移動し、外部へ排出されやすくなっている。また、フルオロポリエーテル含有化合物自体も、摺動面と接する表面に被膜を形成するため、異物除去潤滑組成物に潤滑性をより効果的に付与することが出来る。 The foreign matter removing action described above is particularly effective when, for example, there is a sliding relationship such as a rail and a slider in which members move greatly. That is, even in the case of semi-solid grease, foreign matter (see FIG. 2) that is fluidized by sliding and covered with fluorine atoms quickly moves to the surface of the grease and is easily discharged to the outside. Moreover, since the fluoropolyether-containing compound itself forms a film on the surface in contact with the sliding surface, it is possible to more effectively impart lubricity to the foreign matter removing lubricating composition.
本実施の形態において、フルオロポリエーテル含有化合物は、異物除去潤滑組成物を100重量部としたとき、0.01重量部以上10重量部以下の範囲で含有されることが好ましい。フルオロポリエーテル含有化合物の含有量が0.01重量部よりも少ないと、異物除去効果が低減し、潤滑性向上の効果が不十分である。また、フルオロポリエーテル含有化合物の含有量が10重量部を超えると、異物除去潤滑組成物中に占めるフルオロポリエーテル含有化合物の含有量が多すぎて、潤滑組成物が持つ本来の潤滑性能が低下してしまう。また、フルオロポリエーテル含有化合物をこれ以上多く含有しても、含有量に応じた目的の効果の更なる向上が得られず、価格も高価となるために実用的ではない。また、フルオロポリエーテル含有化合物は、0.05重量部以上10重量部以下の範囲で含有されることがより好ましい。 In the present embodiment, the fluoropolyether-containing compound is preferably contained in the range of 0.01 parts by weight or more and 10 parts by weight or less when the foreign matter removing lubricating composition is 100 parts by weight. When the content of the fluoropolyether-containing compound is less than 0.01 parts by weight, the effect of removing foreign matter is reduced and the effect of improving lubricity is insufficient. In addition, if the content of the fluoropolyether-containing compound exceeds 10 parts by weight, the content of the fluoropolyether-containing compound in the foreign matter-removing lubricating composition is too much, and the original lubricating performance of the lubricating composition is reduced. Resulting in. Moreover, even if it contains more fluoropolyether containing compounds than this, the further improvement of the target effect according to content is not acquired, and since price also becomes expensive, it is not practical. The fluoropolyether-containing compound is more preferably contained in the range of 0.05 parts by weight or more and 10 parts by weight or less.
(フルオロポリエーテル含有化合物)
本実施の形態では、例えば、以下のフルオロポリエーテル含有化合物を提示することが出来る。
(Fluoropolyether-containing compound)
In the present embodiment, for example, the following fluoropolyether-containing compounds can be presented.
すなわち、本実施の形態では、下記一般式(1)又は(2)で表されるフルオロポリエーテル含有化合物を含有することができる。 That is, in this Embodiment, the fluoro polyether containing compound represented by the following general formula (1) or (2) can be contained.
なお、Xの両方が官能基である場合、官能基Xは、同じでも異なっていても良いが、通常は同じとされる。上記に挙げたフルオロポリエーテル含有化合物は、単独で或いは2種以上を組み合わせて用いることができる。このとき、混合比率、使用量は限定されず、塗布適性に応じて適宜調整することが出来る。 When both X are functional groups, the functional groups X may be the same or different, but are usually the same. The above-mentioned fluoropolyether-containing compounds can be used alone or in combination of two or more. At this time, the mixing ratio and the amount used are not limited and can be appropriately adjusted according to the coating suitability.
また、フルオロポリエーテル含有化合物の粘度(20℃)は、50cSt〜30000cSt程度とされる。 The viscosity (20 ° C.) of the fluoropolyether-containing compound is about 50 cSt to 30000 cSt.
(潤滑油タイプ、グリースタイプ)
本実施の形態の異物除去潤滑組成物は、フルオロポリエーテル含有化合物と、潤滑油或いはグリースの潤滑成分と、を含むことを特徴とする。すなわち、潤滑油タイプとしては、フルオロポリエーテル含有化合物と、潤滑成分としての潤滑油と、を含む。また、グリースタイプとしては、フルオロポリエーテル含有化合物と、潤滑成分としての基油及び増ちょう剤と、を含む。
(Lubricant type, grease type)
The foreign matter removing lubricating composition of the present embodiment is characterized by containing a fluoropolyether-containing compound and a lubricating component of lubricating oil or grease. That is, the lubricating oil type includes a fluoropolyether-containing compound and a lubricating oil as a lubricating component. The grease type includes a fluoropolyether-containing compound and a base oil and a thickener as lubricating components.
フルオロポリエーテル含有化合物の含有量や、潤滑成分量は、使用用途に応じて、フルオロポリエーテル含有化合物を、0.01重量部〜10重量部とした含有量の範囲内で適宜、調整することができる。 The content of the fluoropolyether-containing compound and the amount of the lubricating component should be appropriately adjusted within the range of the content of 0.01 to 10 parts by weight of the fluoropolyether-containing compound, depending on the intended use. Can do.
潤滑成分として、鉱物油、合成炭化水素油、ジエステル油、ポリオールエステル油、エーテル油、グリコール油、シリコーン油、及び、フッ素油のうち、少なくともいずれか1種から選択されることが好ましい。これら潤滑成分は、単独で又は2種類以上を組み合わせて用いることができ、その使用量は特に限定されず、塗布適性に応じてその量を選定することができる。潤滑成分は広温度範囲で使用できる点、ゴム・樹脂への適合性、添加剤との相溶性から、ポリαオレフィン及びエチレンαオレフィンオリゴマーが特に好ましい。 The lubricating component is preferably selected from at least one of mineral oil, synthetic hydrocarbon oil, diester oil, polyol ester oil, ether oil, glycol oil, silicone oil, and fluorine oil. These lubricating components can be used alone or in combination of two or more, and the amount used is not particularly limited, and the amount can be selected according to the coating suitability. As the lubricating component, poly α olefins and ethylene α olefin oligomers are particularly preferable from the viewpoint that they can be used in a wide temperature range, compatibility with rubbers and resins, and compatibility with additives.
本実施の形態のグリースに含まれる増ちょう剤は、リチウム石けん、カルシウム石けん、ナトリウム石けん、アルミニウム石けん、リチウム複合石けん、カルシウム複合石けん、アルミニウム複合石けん、ウレア化合物、有機化ベントナイト、ポリテトラフルオロエチレン、シリカゲル、ナトリウムテレフタラメートのうち、少なくともいずれか1種から選択されることが好ましい。増ちょう剤は、せん断安定性から、ステアリン酸リチウム、及び/又は、12−ヒドロキシステアリン酸リチウムであることが好ましい。リチウム石けんは、脂肪酸又はその誘導体と水酸化リチウムとのけん化反応物である。用いられる脂肪酸は、炭素数が2〜22の飽和又は不飽和の脂肪酸及びそれらの誘導体からなる群から選ばれる少なくとも1種である。また、前記の脂肪酸又はその誘導体と水酸化リチウムとを反応させた「石けん」が市販されており、これを用いることもできる。 The thickener contained in the grease of the present embodiment is lithium soap, calcium soap, sodium soap, aluminum soap, lithium composite soap, calcium composite soap, aluminum composite soap, urea compound, organic bentonite, polytetrafluoroethylene, It is preferably selected from at least one of silica gel and sodium terephthalate. The thickener is preferably lithium stearate and / or lithium 12-hydroxystearate from the viewpoint of shear stability. Lithium soap is a saponification reaction product of a fatty acid or a derivative thereof and lithium hydroxide. The fatty acid used is at least one selected from the group consisting of saturated or unsaturated fatty acids having 2 to 22 carbon atoms and derivatives thereof. Further, “soap” obtained by reacting the above fatty acid or derivative thereof with lithium hydroxide is commercially available, and this can also be used.
また、必要に応じて、酸化防止剤、防錆剤、金属腐食防止剤、油性剤、耐摩耗剤、極圧剤、固体潤滑剤などを添加することができる。これら添加物の含有量は、0.01重量部〜30重量部程度の範囲内に収められる。酸化防止剤としては、ヒンダードフェノール、アルキル化ジフェニルアミン、フェニル−α−ナフチルアミン等から選択することができる。防錆剤としては、ステアリン酸などのカルボン酸、ジカルボン酸、金属石鹸、カルボン酸アミン塩、重質スルホン酸の金属塩、又は多価アルコールのカルボン酸部分エステル等から選択することができる。金属腐食防止剤としては、ベンゾトリアゾール又はベンゾイミダゾール等から選択することができる。油性剤としては、ラウリルアミンなどのアミン類、ミリスチルアルコールなどの高級アルコール類、パルミチン酸などの高級脂肪酸類、ステアリン酸メチルなどの脂肪酸エステル類、又はオレイルアミドなどのアミド類等から選択することができる。耐摩耗剤としては、亜鉛系、硫黄系、リン系、アミン系、又はエステル系等から選択することができる。極圧剤としては、ジアルキルジチオリン酸亜鉛、ジアルキルジチオリン酸モリブデン、硫化オレフィン、硫化油脂、メチルトリクロロステアレート、塩素化ナフタレン、ヨウ素化ベンジル、フルオロアルキルポリシロキサン、又は、ナフテン酸鉛等から選択することができる。また、固体潤滑剤としては、黒鉛、フッ化黒鉛、ポリテトラフルオロエチレン、メラミンシアヌレート、二硫化モリブデン、硫化アンチモン等から選択することができる。 Moreover, antioxidant, rust preventive agent, metal corrosion inhibitor, oiliness agent, antiwear agent, extreme pressure agent, solid lubricant, etc. can be added as needed. The content of these additives is within the range of about 0.01 to 30 parts by weight. The antioxidant can be selected from hindered phenol, alkylated diphenylamine, phenyl-α-naphthylamine and the like. The rust preventive agent can be selected from carboxylic acids such as stearic acid, dicarboxylic acids, metal soaps, carboxylic acid amine salts, metal salts of heavy sulfonic acids, or carboxylic acid partial esters of polyhydric alcohols. The metal corrosion inhibitor can be selected from benzotriazole or benzimidazole. The oily agent may be selected from amines such as laurylamine, higher alcohols such as myristyl alcohol, higher fatty acids such as palmitic acid, fatty acid esters such as methyl stearate, or amides such as oleylamide. it can. The antiwear agent can be selected from zinc, sulfur, phosphorus, amine, ester, and the like. The extreme pressure agent should be selected from zinc dialkyldithiophosphate, molybdenum dialkyldithiophosphate, sulfurized olefin, sulfurized fat, methyltrichlorostearate, chlorinated naphthalene, benzylidated, fluoroalkylpolysiloxane, lead naphthenate, etc. Can do. The solid lubricant can be selected from graphite, graphite fluoride, polytetrafluoroethylene, melamine cyanurate, molybdenum disulfide, antimony sulfide, and the like.
(異物除去効果)
本実施の形態において、異物を特に限定するものでないが、例えば異物は、SiO2(二酸化ケイ素)を主成分としている。SiO2は、中心にSi4 +があり、その周囲に4個のO2が取り囲むSiO4四面体が連結した結晶構造を構成する。Siの電気陰性度は1.8であり、Oの電気陰性度は3.5であり、両者には1.7の電気陰性度の差がある。このため、SiO2は、陰性(δ−)に分極している。
(Foreign matter removal effect)
In the present embodiment, the foreign matter is not particularly limited. For example, the foreign matter is mainly composed of SiO 2 (silicon dioxide). SiO 2 has a crystal structure in which Si 4 + is in the center and SiO 4 tetrahedrons surrounded by four O 2 are connected to each other. The electronegativity of Si is 1.8, the electronegativity of O is 3.5, and both have a difference in electronegativity of 1.7. For this reason, SiO 2 is polarized negatively (δ−).
本実施の形態では、後述の実験にて詳述するように、フルオロポリエーテル含有化合物と、潤滑油とを含む異物除去潤滑組成物(潤滑油タイプ)に対し、少なくとも、JIS Z 8901に定められた7種或いは8種を備えた異物を加えた。JIS Z 8901に定められた7種及び8種は、いずれもSiO2を主成分として含んでいる。そして、異物を混入しても、本実施の形態の潤滑油では、異物の沈降が観測された。すなわち本実施の形態の異物除去潤滑組成物では、異物が潤滑組成物内に取り込まれず、異物除去効果が確認された。 In the present embodiment, as described in detail in an experiment described later, at least JIS Z 8901 is defined for a foreign matter removing lubricating composition (lubricating oil type) containing a fluoropolyether-containing compound and a lubricating oil. Foreign substances with 7 or 8 species were added. Both 7 types and 8 types defined in JIS Z 8901 contain SiO 2 as a main component. Even if foreign matter is mixed in, the sedimentation of the foreign matter was observed in the lubricating oil of the present embodiment. That is, in the foreign matter removing lubricating composition of the present embodiment, foreign matter was not taken into the lubricating composition, and the foreign matter removing effect was confirmed.
また、後述の実験にて詳述するように、フルオロポリエーテル含有化合物と、グリースの潤滑成分とを含む異物除去潤滑組成物(グリース)に対し、JIS Z 8901に定められた少なくとも1種或いは2種を備えた異物を加えて摩擦係数を測定した。その結果、本実施の形態のグリースは、フルオロポリエーテル含有化合物を含まず、異物を加えた従来の潤滑組成物の摩擦係数に比べて小さいことがわかった。JIS Z 8901に定められた1種及び2種は、いずれもSiO2を主成分として含んでいる。 Further, as will be described in detail in an experiment to be described later, at least one or two or more of those defined in JIS Z 8901 are used for a foreign matter removing lubricating composition (grease) containing a fluoropolyether-containing compound and a lubricating component of grease. The foreign material with seeds was added and the coefficient of friction was measured. As a result, it was found that the grease of the present embodiment does not contain a fluoropolyether-containing compound and is smaller than the friction coefficient of the conventional lubricating composition to which foreign matters are added. Both 1 type and 2 types defined in JIS Z 8901 contain SiO 2 as a main component.
また、後述の実験にて詳述するように、フルオロポリエーテル含有化合物と、グリースの潤滑成分とを含む異物除去潤滑組成物(グリース)に対し、JIS Z 8901に定められた少なくとも1種又は2種を備えた異物を加えて初期の摩擦係数μ1を測定した。また、異物を加えない状態での初期時の摩擦係数μ0も測定した。そして、{(μ1−μ0)/μ0}×100で示される摩擦係数の変化率(%)を求めたところ、本実施の形態のグリースでは、初期時の摩擦係数の変化率が、40%未満にできることがわかった。ここで「初期時」とは、往復摺動回数を、5回以上50回以下とした摺動条件を指す。また、本実施の形態では、変化率が、30%未満であることがより好ましく、20%未満であることが更に好ましい。 In addition, as will be described in detail in the experiment described later, at least one or two or more of those defined in JIS Z 8901 are used for a foreign matter removing lubricating composition (grease) containing a fluoropolyether-containing compound and a lubricating component of grease. The initial friction coefficient μ1 was measured by adding a foreign substance with seeds. Further, the initial friction coefficient μ0 in a state where no foreign matter was added was also measured. Then, when the change rate (%) of the coefficient of friction represented by {(μ1-μ0) / μ0} × 100 was obtained, the change rate of the initial friction coefficient was less than 40% in the grease of the present embodiment. I understood that I can do it. Here, the “initial time” refers to a sliding condition in which the number of reciprocating sliding operations is 5 to 50 times. In the present embodiment, the rate of change is more preferably less than 30%, and even more preferably less than 20%.
本実施の形態の異物除去潤滑組成物を用いることで、異物除去潤滑組成物を潤滑面に塗布し、摺動部材を摺動させた際、異物除去効果により、摩擦係数を安定して低い状態を保つことが出来る。このため、本実施の形態の異物除去潤滑組成物を用いることで、従来に比べて、安定して高い潤滑性を得ることが出来る。 By using the foreign matter removing lubricating composition of the present embodiment, when the foreign matter removing lubricating composition is applied to the lubricated surface and the sliding member is slid, the friction coefficient is stably reduced due to the foreign matter removing effect. Can be kept. For this reason, by using the foreign matter removing lubricating composition of the present embodiment, it is possible to stably obtain high lubricity as compared with the conventional case.
なお、後述の実験に示すように、JIS Z 8901に定められた1種、2種、7種及び8種のうち少なくとも2種類以上を所定の割合で混合させた異物を用いて、上記した異物の沈降観察や摩擦係数の実験を行うことが出来る。このときの混合割合は特に限定されるものではない。例えば、後述する実験に示すように、JIS Z 8901に定められた1種、2種、7種及び8種を1:1:1:1の割合で混合することが出来る。 In addition, as shown in the experiment to be described later, the foreign matter described above is used by using a foreign matter obtained by mixing at least two types of one, two, seven, and eight types defined in JIS Z 8901 at a predetermined ratio. Observation of sedimentation and experiment of friction coefficient. The mixing ratio at this time is not particularly limited. For example, as shown in an experiment to be described later, one, two, seven and eight kinds defined in JIS Z 8901 can be mixed at a ratio of 1: 1: 1: 1.
本実施の形態の異物除去潤滑組成物は、塵埃を含む環境下に置かれても、異物除去効果により高く安定した潤滑性を保つことができる。「塵埃を含む環境下」とは、例えば、塵埃が、異物除去潤滑組成物の50%以下の体積比率にて含まれる環境下である。すなわち本実施の形態の異物除去潤滑組成物であれば、塵埃が、異物除去潤滑組成物の体積比率で50%程度まで含まれていても、異物除去効果が適切に発揮されうる。本実施の形態では、塵埃が、異物除去潤滑組成物の体積比率で0.01%程度以上含まれた環境下において、従来の潤滑組成物とは、明らかに摩擦係数が低くなる等、異物除去効果が顕著に現れる。 The foreign matter removing lubricating composition of the present embodiment can maintain highly stable lubricity due to the foreign matter removing effect even when placed in an environment containing dust. “In an environment containing dust” is, for example, an environment in which dust is contained at a volume ratio of 50% or less of the foreign matter removing lubricant composition. That is, with the foreign matter removing lubricant composition of the present embodiment, the foreign matter removing effect can be appropriately exhibited even if dust is contained up to about 50% in the volume ratio of the foreign matter removing lubricant composition. In the present embodiment, in an environment where dust is contained in an amount of about 0.01% or more by volume ratio of the foreign matter removing lubricant composition, the foreign matter removal such as the friction coefficient is clearly lower than that of the conventional lubricating composition. The effect is noticeable.
また、本実施の形態の異物除去潤滑組成物は、ドアロック機構、ウインドレギュレータ、シートレール、及び、サンルーフ等の自動車部品、及び各種機器における摺動部を備えた部材には、潤滑油、或いは、グリースとして使用される。このような自動車部品及び摺動部を備えた部材が、上記した塵埃を含む環境下に置かれても、本実施の形態の異物除去潤滑組成物を用いることで、異物除去効果が適切に発揮され、従来に比べて、安定して高い潤滑性を得ることができる。 In addition, the foreign matter removing lubricating composition of the present embodiment includes a lubricant, or a member having a sliding part in a door lock mechanism, a window regulator, a seat rail, a sunroof, and various other devices. Used as grease. Even if such a member having an automobile part and a sliding part is placed in an environment containing dust as described above, the foreign matter removing effect can be appropriately exhibited by using the foreign matter removing lubricating composition of the present embodiment. Thus, it is possible to stably obtain high lubricity as compared with the conventional case.
以下、本発明の効果を明確にするために実施した実施例により本発明を詳細に説明する。なお、本発明は、以下の実施例によって何ら限定されるものではない。 Hereinafter, the present invention will be described in detail with reference to examples carried out in order to clarify the effects of the present invention. In addition, this invention is not limited at all by the following examples.
[潤滑油タイプ]
以下の表1、表2、及び表3に示す配合で、潤滑油タイプとしての実施例1〜実施例10、比較例1〜比較例3を調製した。使用した原料は以下の通りである。
[Lubricant type]
Examples 1 to 10 and Comparative Examples 1 to 3 as lubricant types were prepared with the formulations shown in Table 1, Table 2, and Table 3 below. The raw materials used are as follows.
(実施例1)
フルオロポリエーテル含有化合物A(製品名:Fomblin(登録商標、以下同じ) DA305):1.0重量部
潤滑油 ポリαオレフィン(動粘度(40℃):30mm2/s):97.8重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤(下記の一般式(3)参照):0.2重量部
Example 1
Fluoropolyether-containing compound A (Product name: Fomblin (registered trademark, the same shall apply hereinafter) DA305): 1.0 part by weight Lubricating oil Polyalphaolefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 97.8 parts by weight Antioxidant Hindered phenol antioxidant (see the following general formula (3)): 0.2 parts by weight
粉塵(JIS Z 8901 1種、2種、7種、8種を1:1:1:1で混合):1.0重量部 Dust (JIS Z 8901 1 type, 2 types, 7 types, 8 types mixed at 1: 1: 1: 1): 1.0 part by weight
(実施例2)
フルオロポリエーテル含有化合物B(製品名:Fomblin DA306VAC):1.0重量部
潤滑油 ポリαオレフィン(動粘度(40℃):30mm2/s):97.8重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
粉塵(JIS Z 8901 1種、2種、7種、8種を1:1:1:1で混合):1.0重量部
(Example 2)
Fluoropolyether-containing compound B (product name: Fomblin DA306VAC): 1.0 part by weight lubricating oil Polyalphaolefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 97.8 parts by weight antioxidant hindered phenol Antioxidant: 0.2 part by weight dust (JIS Z 8901 1 type, 2 types, 7 types, 8 types mixed at 1: 1: 1: 1): 1.0 part by weight
(実施例3)
フルオロポリエーテル含有化合物B(製品名:Fomblin DA306VAC):0.01重量部
潤滑油 ポリαオレフィン(動粘度(40℃):30mm2/s):98.8重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
粉塵(JIS Z 8901 1種、2種、7種、8種を1:1:1:1で混合):1.0重量部
(Example 3)
Fluoropolyether-containing compound B (Product name: Fomblin DA306VAC): 0.01 parts by weight Lubricating oil Polyalphaolefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 98.8 parts by weight Antioxidant Hindered phenol Antioxidant: 0.2 part by weight dust (JIS Z 8901 1 type, 2 types, 7 types, 8 types mixed at 1: 1: 1: 1): 1.0 part by weight
(実施例4)
フルオロポリエーテル含有化合物B(製品名:Fomblin DA306VAC):5.0重量部
潤滑油 ポリαオレフィン(動粘度(40℃):30mm2/s):64.8重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
粉塵(JIS Z 8901 1種、2種、7種、8種を1:1:1:1で混合):30.0重量部
Example 4
Fluoropolyether-containing compound B (product name: Fomblin DA306VAC): 5.0 parts by weight lubricating oil Polyalphaolefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 64.8 parts by weight antioxidant hindered phenol Antioxidant: 0.2 parts by weight Dust (JIS Z 8901 1 type, 2 types, 7 types, 8 types mixed at 1: 1: 1: 1): 30.0 parts by weight
(実施例5)
フルオロポリエーテル含有化合物C(製品名:Fomblin DA308):1.0重量部
潤滑油 ポリαオレフィン(動粘度(40℃):30mm2/s):97.8重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
粉塵(JIS Z 8901 2種、8種を1:1で混合):1.0重量部
(Example 5)
Fluoropolyether-containing compound C (product name: Fomblin DA308): 1.0 part by weight lubricating oil Polyalphaolefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 97.8 parts by weight antioxidant hindered phenol Antioxidant: 0.2 parts by weight Dust (JIS Z 8901 2 types, 8 types mixed at 1: 1): 1.0 parts by weight
(実施例6)
フルオロポリエーテル含有化合物D(製品名:Fomblin DA410):1.0重量部
潤滑油 ポリαオレフィン(動粘度(40℃):30mm2/s):97.8重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
粉塵(JIS Z 8901 2種、7種を1:1で混合):1.0重量部
(Example 6)
Fluoropolyether-containing compound D (product name: Fomblin DA410): 1.0 part by weight lubricating oil Polyalphaolefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 97.8 parts by weight antioxidant hindered phenol Antioxidant: 0.2 parts by weight Dust (JIS Z 8901 2 types, 7 types mixed 1: 1): 1.0 parts by weight
(実施例7)
フルオロポリエーテル含有化合物E(製品名:Fluorolink(登録商標、以下同じ) E10H):1.0重量部
潤滑油 ポリαオレフィン(動粘度(40℃):30mm2/s):97.8重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
粉塵(JIS Z 8901 1種、2種、7種、8種を1:1:1:1で混合):1.0重量部
(Example 7)
Fluoropolyether-containing compound E (Product name: Fluorolink (registered trademark, the same shall apply hereinafter) E10H): 1.0 part by weight Lubricating oil Polyalphaolefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 97.8 parts by weight Antioxidant Hindered phenolic antioxidant: 0.2 parts by weight Dust (JIS Z 8901 1 type, 2 types, 7 types, 8 types mixed at 1: 1: 1: 1): 1.0 parts by weight
(実施例8)
フルオロポリエーテル含有化合物F(製品名:Fluorolink S10):1.0重量部
潤滑油 ポリαオレフィン(動粘度(40℃):30mm2/s):97.8重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
粉塵(JIS Z 8901 1種、2種、7種、8種を1:1:1:1で混合):1.0重量部
(Example 8)
Fluoropolyether-containing compound F (product name: Fluorolink S10): 1.0 part by weight lubricating oil Polyalphaolefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 97.8 parts by weight antioxidant hindered phenol Antioxidant: 0.2 part by weight dust (JIS Z 8901 1 type, 2 types, 7 types, 8 types mixed at 1: 1: 1: 1): 1.0 part by weight
(実施例9)
フルオロポリエーテル含有化合物A(製品名:Fomblin DA305):0.005重量部
潤滑油 ポリαオレフィン(動粘度(40℃):30mm2/s):98.8重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
粉塵(JIS Z 8901 1種、2種、7種、8種を1:1:1:1で混合):1.0重量部
Example 9
Fluoropolyether-containing compound A (Product name: Fomblin DA305): 0.005 parts by weight lubricating oil Polyalphaolefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 98.8 parts by weight antioxidant hindered phenol type Antioxidant: 0.2 part by weight dust (JIS Z 8901 1 type, 2 types, 7 types, 8 types mixed at 1: 1: 1: 1): 1.0 part by weight
(実施例10)
フルオロポリエーテル含有化合物B(製品名:Fomblin DA306VAC):0.005重量部
潤滑油 ポリαオレフィン(動粘度(40℃):30mm2/s):98.8重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
粉塵(JIS Z 8901 1種、2種、7種、8種を1:1:1:1で混合):1.0重量部
(Example 10)
Fluoropolyether-containing compound B (Product name: Fomblin DA306VAC): 0.005 parts by weight Lubricating oil Polyalphaolefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 98.8 parts by weight Antioxidant hindered phenol Antioxidant: 0.2 part by weight dust (JIS Z 8901 1 type, 2 types, 7 types, 8 types mixed at 1: 1: 1: 1): 1.0 part by weight
(比較例1)
潤滑油 ポリαオレフィン(動粘度(40℃):30mm2/s):98.8重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
粉塵 (JIS Z 8901 1種、2種、7種、8種を1:1:1:1で混合):1.0重量部
(Comparative Example 1)
Lubricating oil Poly α-olefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 98.8 parts by weight Antioxidant Hindered phenolic antioxidant: 0.2 parts by weight Dust (JIS Z 8901 1 type, 2 types 7 types and 8 types mixed at 1: 1: 1: 1): 1.0 part by weight
(比較例2)
清浄分散剤A 過塩基性金属Caスルホネート(粘度(100℃)52cSt):1重量部
潤滑油 ポリαオレフィン(動粘度(40℃):30mm2/s):97.8重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
粉塵 (JIS Z 8901 1種、2種、7種、8種を1:1:1:1で混合):1.0重量部
(Comparative Example 2)
Detergent Dispersant A Overbased metal Ca sulfonate (viscosity (100 ° C.) 52 cSt): 1 part by weight lubricating oil Poly α-olefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 97.8 parts by weight antioxidant hinder Dophenol antioxidants: 0.2 parts by weight Dust (JIS Z 8901 1 type, 2 types, 7 types, 8 types mixed at 1: 1: 1: 1): 1.0 parts by weight
(比較例3)
清浄分散剤B コハク酸イミド(粘度(100℃)570cSt):1重量部
潤滑油 ポリαオレフィン(動粘度(40℃):30mm2/s):97.8重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
粉塵 (JIS Z 8901 1種、2種、7種、8種を1:1:1:1で混合):1.0重量部
(Comparative Example 3)
Detergent Dispersant B Succinimide (viscosity (100 ° C.) 570 cSt): 1 part by weight lubricating oil Polyalphaolefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 97.8 parts by weight antioxidant hindered phenol Antioxidant: 0.2 part by weight dust (JIS Z 8901 1 type, 2 types, 7 types, 8 types mixed at 1: 1: 1: 1): 1.0 part by weight
表1〜表3に示す○は、スクリュー瓶の底に粉塵の分離沈降が観察された。一方、△は、スクリュー瓶の底に粉塵の分離沈降が見られるものの、粉塵を同じ量だけ添加した○の評価の実施例よりも粉塵の沈降量が少なかった。×は、スクリュー瓶の底に粉塵の分離沈降が観察されなかった。 In the circles shown in Tables 1 to 3, separation and sedimentation of dust was observed at the bottom of the screw bottle. On the other hand, Δ indicates that although the dust settled and settled at the bottom of the screw bottle, the amount of dust settled was smaller than that of the example in which the same amount of dust was added. X: no separation and settling of dust was observed at the bottom of the screw bottle.
図3は、比較例1と実施例1の各試料の異物の混合状態を示す写真である。図4は、図3の模式図である。図3、図4に示す左側の写真及び模式図は、比較例1であり、右側の写真及び模式図は、実施例1である。図3、図4に示すように、比較例1は、溶液全体が濁った状態になり、異物除去がなされていないことが観察された。このように濁った状態になるのは、JIS Z 8901のうち粒径が小さい7種や8種が潤滑油内で混合した状態を保つためである。一方、図3、図4に示すように、実施例1は、溶液全体が半透明な状態になっており、異物は潤滑油から排除されて底に沈降していることが確認された。表2に示す「粉塵の分離沈降」が△の評価の実施例9、及び実施例10では、○の評価の実施例よりも異物の沈降量が少なかった。 FIG. 3 is a photograph showing a mixed state of foreign matters in each sample of Comparative Example 1 and Example 1. FIG. 4 is a schematic diagram of FIG. The left photograph and schematic diagram shown in FIGS. 3 and 4 are Comparative Example 1, and the right photograph and schematic diagram are Example 1. FIG. As shown in FIGS. 3 and 4, in Comparative Example 1, it was observed that the entire solution became cloudy and no foreign matter was removed. The reason for becoming cloudy in this way is to maintain a state in which seven or eight kinds of JIS Z 8901 having a small particle diameter are mixed in the lubricating oil. On the other hand, as shown in FIGS. 3 and 4, in Example 1, it was confirmed that the whole solution was in a translucent state, and foreign matters were excluded from the lubricating oil and settled to the bottom. In Example 9 and Example 10 in which “separation and settling of dust” shown in Table 2 was evaluated as Δ, the amount of foreign matter settled was smaller than that in the example evaluated as ○.
[グリースタイプ]
以下の表4に示す配合で、グリースタイプとして、実施例11〜実施例13、比較例4を調製した。使用した原料は以下の通りである。
[Grease type]
Examples 11 to 13 and Comparative Example 4 were prepared as grease types with the formulation shown in Table 4 below. The raw materials used are as follows.
(実施例11)
フルオロポリエーテル含有化合物A(製品名:Fomblin DA305):1.0重量部
基油 ポリαオレフィン(動粘度(40℃):30mm2/s):77.8重量部
増ちょう剤 リチウム石けん(12−ヒドロキシステアリン酸リチウム):7.0重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
固体潤滑剤A ポリテトラフルオロエチレン(平均粒径6.5μm):5.0重量部
固体潤滑剤B メラミンシアヌレート(平均粒径3.1μm):5.0重量部
固体潤滑剤C 超高分子量ポリエチレン(平均粒径30μm):5.0重量部
粉塵 (JIS Z 8901 1種、2種、7種、8種を1:1:1:1で混合):2.0重量部
(Example 11)
Fluoropolyether-containing compound A (Product name: Fomblin DA305): 1.0 part by weight base oil Polyalphaolefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 77.8 parts by weight Thickener Lithium soap (12 -Lithium hydroxystearate): 7.0 parts by weight Antioxidant Hindered phenol antioxidant: 0.2 parts by weight Solid lubricant A Polytetrafluoroethylene (average particle size 6.5 μm): 5.0 parts by weight Solid lubricant B Melamine cyanurate (average particle size 3.1 μm): 5.0 parts by weight Solid lubricant C Ultra high molecular weight polyethylene (average particle size 30 μm): 5.0 parts by weight Dust (JIS Z 8901 1 type, 2 Seeds, 7 kinds, 8 kinds mixed at 1: 1: 1: 1): 2.0 parts by weight
(実施例12)
フルオロポリエーテル含有化合物B(製品名:Fomblin DA306VAC):0.5重量部
基油 ポリαオレフィン(動粘度(40℃):30mm2/s):77.3重量部
増ちょう剤 リチウム石けん(12−ヒドロキシステアリン酸リチウム):7.0重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
固体潤滑剤A ポリテトラフルオロエチレン(平均粒径6.5μm):5.0重量部
固体潤滑剤B メラミンシアヌレート(平均粒径3.1μm):5.0重量部
固体潤滑剤C 超高分子量ポリエチレン(平均粒径30μm):5.0重量部
粉塵 (JIS Z 8901 1種、2種、7種、8種を1:1:1:1で混合):2.0重量部
(Example 12)
Fluoropolyether-containing compound B (product name: Fomblin DA306VAC): 0.5 part by weight base oil Polyalphaolefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 77.3 parts by weight Thickener Lithium soap (12 -Lithium hydroxystearate): 7.0 parts by weight Antioxidant Hindered phenol antioxidant: 0.2 parts by weight Solid lubricant A Polytetrafluoroethylene (average particle size 6.5 μm): 5.0 parts by weight Solid lubricant B Melamine cyanurate (average particle size 3.1 μm): 5.0 parts by weight Solid lubricant C Ultra high molecular weight polyethylene (average particle size 30 μm): 5.0 parts by weight Dust (JIS Z 8901 1 type, 2 Seeds, 7 kinds, 8 kinds mixed at 1: 1: 1: 1): 2.0 parts by weight
(実施例13)
フルオロポリエーテル含有化合物B(製品名:Fomblin DA306VAC):10.0重量部
基油 ポリαオレフィン(動粘度(40℃):30mm2/s):67.8重量部
増ちょう剤 リチウム石けん(12−ヒドロキシステアリン酸リチウム):7.0重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
固体潤滑剤A ポリテトラフルオロエチレン(平均粒径6.5μm):5.0重量部
固体潤滑剤B メラミンシアヌレート(平均粒径3.1μm):5.0重量部
固体潤滑剤C 超高分子量ポリエチレン(平均粒径30μm):5.0重量部
粉塵 (JIS Z 8901 1種、2種、7種、8種を1:1:1:1で混合):15.0重量部
(Example 13)
Fluoropolyether-containing compound B (Product name: Fomblin DA306VAC): 10.0 parts by weight Base oil Polyalphaolefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 67.8 parts by weight Thickener Lithium soap (12 -Lithium hydroxystearate): 7.0 parts by weight Antioxidant Hindered phenol antioxidant: 0.2 parts by weight Solid lubricant A Polytetrafluoroethylene (average particle size 6.5 μm): 5.0 parts by weight Solid lubricant B Melamine cyanurate (average particle size 3.1 μm): 5.0 parts by weight Solid lubricant C Ultra high molecular weight polyethylene (average particle size 30 μm): 5.0 parts by weight Dust (JIS Z 8901 1 type, 2 Seeds, 7 kinds, 8 kinds mixed at 1: 1: 1: 1): 15.0 parts by weight
(比較例4)
基油 ポリαオレフィン(動粘度(40℃):30mm2/s):79.8重量部
増ちょう剤 リチウム石けん(12−ヒドロキシステアリン酸リチウム):10.0重量部
酸化防止剤 ヒンダードフェノール系酸化防止剤:0.2重量部
固体潤滑剤D 超高分子量ポリエチレン(平均粒径10μm):10.0重量部
粉塵 (JIS Z 8901 1種、2種、7種、8種を1:1:1:1で混合):2.0重量部
(Comparative Example 4)
Base oil Polyalphaolefin (kinematic viscosity (40 ° C.): 30 mm 2 / s): 79.8 parts by weight Thickener Lithium soap (lithium 12-hydroxystearate): 10.0 parts by weight Antioxidant Hindered phenol Antioxidant: 0.2 parts by weight of solid lubricant D Ultra high molecular weight polyethylene (average particle size 10 μm): 10.0 parts by weight of dust (JIS Z 8901 1 type, 2 types, 7 types, 8 types 1: 1: 1: 1 mixing): 2.0 parts by weight
基油の存在下、リチウム石けんを合成し、攪拌しながら温度を上昇させた。次いで、80℃以下に冷却した後、各種添加剤を処方して、三段ロールミル、ディスパーミルやコロイドミル等を使用することにより均一なグリース組成物を得ることができた。 Lithium soap was synthesized in the presence of base oil and the temperature was raised with stirring. Next, after cooling to 80 ° C. or lower, various additives were formulated, and a uniform grease composition could be obtained by using a three-stage roll mill, a disper mill, a colloid mill, or the like.
混和ちょう度は、280〜310の間にて調整した。なお、試験方法はJIS K 2220に基づく。混和ちょう度調整後に、規定量の粉塵をグリース中に混合した。 The mixing penetration was adjusted between 280 and 310. The test method is based on JIS K 2220. After adjusting the blending consistency, a specified amount of dust was mixed into the grease.
<グリースの評価方法>
グリースは粘ちょう状物質であるため、潤滑油のような粉塵の沈降で評価することはできない。そのため、摩擦係数にて評価した。
<Grease evaluation method>
Since grease is a viscous substance, it cannot be evaluated by sedimentation of dust such as lubricating oil. Therefore, the friction coefficient was evaluated.
<摩擦係数の実験条件>
試験片:PA66GF30ピン(φ4mm)/Al板
荷重:1000gf
グリース塗布膜厚:0.2mm
試験温度:室温
摺動速度:10mm/sec
摺動幅:20mm/片道
摺動回数:10往復
<Experimental conditions for friction coefficient>
Test piece: PA66GF30 pin (φ4 mm) / Al plate load: 1000 gf
Grease coating thickness: 0.2 mm
Test temperature: room temperature sliding speed: 10 mm / sec
Sliding width: 20 mm / one-way sliding: 10 reciprocations
図5は、往復摺動試験方法を説明するための模式図である。図5に示す符号3は、固定ピンを示し、符号4は、Al板を示す。そして、Al板4を、A方向に往復摺動させた。 FIG. 5 is a schematic diagram for explaining the reciprocating sliding test method. Reference numeral 3 shown in FIG. 5 indicates a fixed pin, and reference numeral 4 indicates an Al plate. The Al plate 4 was slid back and forth in the A direction.
各試料において、粉塵添加前と粉塵添加後の各動摩擦係数を測定し、下記の計算式で摩擦係数の変化率を算出した。 In each sample, the respective dynamic friction coefficients before and after the addition of dust were measured, and the rate of change of the friction coefficient was calculated using the following formula.
すなわち、10回往復摺動後における粉塵混合後動摩擦係数を、μ1とし、10回往復摺動後における粉塵混合前動摩擦係数をμ0とした。そして、摩擦係数変化率(%)を、{(μ1−μ0)/μ0}×100にて求めた。その実験結果が以下の表4に示されている。 That is, the dynamic friction coefficient after dust mixing after 10 reciprocating slides was μ1, and the dynamic friction coefficient before dust mixing after 10 reciprocating slidings was μ0. Then, the coefficient of friction change (%) was determined by {(μ1-μ0) / μ0} × 100. The experimental results are shown in Table 4 below.
ここで、表4に示す「変化率」欄の○は、変化率が40%未満を示し、×は、変化率が40%以上であることを示す。 Here, “◯” in the “change rate” column shown in Table 4 indicates that the change rate is less than 40%, and “x” indicates that the change rate is 40% or more.
表4に示すように、初期時における摩擦係数の変化率は、実施例では40%未満に抑えることができるとわかった。ここで、摺動回数を10往復させた状態で摩擦係数を測定しており、すなわち初期状態を少しだけ摺動させた状態としたのは最初の数回は、摺動部材とグリースとのなじみが低く、摩擦係数のばらつきが大きいためである。 As shown in Table 4, it was found that the rate of change of the friction coefficient at the initial stage can be suppressed to less than 40% in the examples. Here, the coefficient of friction was measured with the number of sliding times reciprocated 10 times, that is, the initial state was slightly slid for the first few times. This is because the variation in the friction coefficient is large.
次に、実施例11及び比較例4の各試料を用いて、摺動速度を10mm/sと変化させた際の、往復摺動回数と摩擦係数との関係について調べた。なお摩擦係数の実験条件は、上記の摺動速度回数及び摺動回数を除いて同じとした。 Next, using the samples of Example 11 and Comparative Example 4, the relationship between the number of reciprocating sliding operations and the friction coefficient when the sliding speed was changed to 10 mm / s was examined. The experimental conditions for the friction coefficient were the same except for the above sliding speed and sliding times.
図6は、実施例11と比較例4との摺動速度に対する、異物を含まない状態での、往復摺動回数と摩擦係数との関係を示すグラフである。一方、図7は、実施例11と比較例4との摺動速度に対する、異物を含んだ状態での、往復摺動回数と摩擦係数との関係を示すグラフである。 FIG. 6 is a graph showing the relationship between the number of reciprocating slides and the coefficient of friction with respect to the sliding speed between Example 11 and Comparative Example 4 in a state in which no foreign matter is included. On the other hand, FIG. 7 is a graph showing the relationship between the number of reciprocating slides and the coefficient of friction with respect to the sliding speed between Example 11 and Comparative Example 4 in a state including foreign matter.
図6に示すように、異物を含まない状態では、実施例11及び比較例4ともに、摺動速度によって摩擦係数は大きく変化しないが、実施例11のほうが比較例4に比べて、摩擦係数を低く抑えることができるとわかった。 As shown in FIG. 6, in a state in which no foreign matter is included, in both Example 11 and Comparative Example 4, the friction coefficient does not change greatly depending on the sliding speed, but in Example 11, the friction coefficient is higher than that in Comparative Example 4. I found that I could keep it low.
次に図7に示すように、異物を含んだ状態でも、実施例11では、摺動速度によって摩擦係数は大きく変化しないことがわかった。これに対して、比較例4では、特に摺動速度が低速になるほど摩擦係数が不安定になることがわかった。 Next, as shown in FIG. 7, it was found that the friction coefficient did not change greatly depending on the sliding speed in Example 11 even in the state including foreign matter. On the other hand, in Comparative Example 4, it was found that the coefficient of friction becomes more unstable as the sliding speed becomes lower.
本発明における異物除去潤滑組成物を、ドアロック機構、ウインドレギュレータ、シートレール、及び、サンルーフ等の自動車部品、及び各種機器における摺動部を備えた部材の潤滑油、或いは、グリースとして好ましく適用することができる。 The foreign matter removing lubricating composition in the present invention is preferably applied as a lubricating oil or grease for a member having a sliding part in a door lock mechanism, a window regulator, a seat rail, a sunroof and other automobile parts, and various devices. be able to.
1 塗布面
3 固定ピン
4 Al板
1 Application surface 3 Fixing pin 4 Al plate
Claims (15)
フルオロポリエーテル含有化合物と、潤滑油或いはグリースの潤滑成分と、を含み、前記フルオロポリエーテル含有化合物は、フッ素原子よりも、前記潤滑成分への親和性が高い官能基を有することを特徴とする異物除去潤滑組成物。 A foreign matter removing lubricating composition applied to door lock mechanisms, window regulators, seat rails, and sunroof automobile parts,
A fluoropolyether-containing compound and a lubricating component of a lubricating oil or grease, wherein the fluoropolyether-containing compound has a functional group having a higher affinity for the lubricating component than a fluorine atom. Foreign matter removing lubricating composition.
前記官能基は、カルボキシレート、アルキルアミド、カルボキシレートトリエタノールアミン、ジニトロベンゼン、メチルエステル、エトキシル化アルコール、アルキルアミド、ポリアミド、アルコキシシラン、ホスフェート、ウレタンメタクリレート、及び、ウレタンアルキレートのうち、少なくともいずれか1種を備えることを特徴とする異物除去潤滑組成物。The functional group is at least one of carboxylate, alkylamide, carboxylate triethanolamine, dinitrobenzene, methyl ester, ethoxylated alcohol, alkylamide, polyamide, alkoxysilane, phosphate, urethane methacrylate, and urethane alkylate. A foreign matter removing lubricating composition comprising:
下記一般式(1)又は(2)で表される前記フルオロポリエーテル含有化合物を含有することを特徴とする異物除去潤滑組成物。 A foreign matter removing lubricating composition comprising the fluoropolyether-containing compound represented by the following general formula (1) or (2).