JP6420215B2 - 消耗電極式ガスシールドアーク溶接方法 - Google Patents
消耗電極式ガスシールドアーク溶接方法 Download PDFInfo
- Publication number
- JP6420215B2 JP6420215B2 JP2015148988A JP2015148988A JP6420215B2 JP 6420215 B2 JP6420215 B2 JP 6420215B2 JP 2015148988 A JP2015148988 A JP 2015148988A JP 2015148988 A JP2015148988 A JP 2015148988A JP 6420215 B2 JP6420215 B2 JP 6420215B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- wire
- filler
- arc
- welding method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
0≦WC+BC×FWR−WC×FWR≦0.15 (1)
FWR=−0.8×FWw/TWw+0.7 (2)
WC=AWC×AWw/TWw+FWC×FWw/TWw (3)
(式(1)〜(3)中、BC、FWR、WC、FWC、AWC、FWw、AWw及びTWwはそれぞれ以下を表す。
BC:母材中の炭素含有量[質量%]
FWR:フィラーワイヤの重み係数
WC:ワイヤ炭素量の加重平均[質量%]
FWC:フィラーワイヤの炭素含有量[質量%]
AWC:アークワイヤの炭素含有量[質量%]
FWw:フィラーワイヤの溶加量[g/分]
AWw:アークワイヤの溶着量[g/分]
TWw:フィラーワイヤの溶加量とアークワイヤの溶着量の和[g/分])
FWR=−0.8×FWw/TWw+0.7 (2)
WC=AWC×AWw/TWw+FWC×FWw/TWw (3)
BC:母材中の炭素含有量[質量%]
FWR:フィラーワイヤの重み係数
WC:ワイヤ炭素量の加重平均[質量%]
FWC:フィラーワイヤの炭素含有量[質量%]
AWC:アークワイヤの炭素含有量[質量%]
FWw:フィラーワイヤの溶加量[g/分]
AWw:アークワイヤの溶着量[g/分]
TWw:フィラーワイヤの溶加量とアークワイヤの溶着量の和[g/分]
−0.015FWw2+4FWw+50≦I≦450 (4)
実施例1〜31及び比較例1〜16について、溶接後の試験板の溶接金属中央部分から炭素分析用の切粉を採取し、炭素・硫黄分析装置(HORIBA社製のEMIA−920V)を用いて炭素含有量を測定した。その結果を表6及び7に示す。
実施例1〜31及び比較例1〜16について、溶接後の試験板から断面観察用の試験片を4つずつ切り出し、各試験片に発生した割れを、デジタル顕微鏡(KEYENCE社製のVHX900)を用いて50倍の倍率で観察して、1断面当たりの割れ総長さの平均値を算出した。その結果を表6及び7に示す。ここで、割れ総長さの平均値が1.00mm以下の場合に、合格と判定した。
係数A=(DC―WC)/(BC―WC) (5)
DC:溶接金属の炭素含有量[質量%]
WC:ワイヤ炭素量の加重平均[質量%]
BC:母材中の炭素含有量[質量%]
WC=AWC×AWw/TWw+FWC×FWw/TWw (3)
FWC:フィラーワイヤの炭素含有量[質量%]
AWC:アークワイヤの炭素含有量[質量%]
FWw:フィラーワイヤの溶加量[g/分]
AWw:アークワイヤの溶着量[g/分]
TWw:フィラーワイヤの溶加量とアークワイヤの溶着量の和[g/分]
y=−0.8x+0.7 (6)
0≦WC+BC×FWR−WC×FWR≦0.15 (1)
FWR=−0.8×FWw/TWw+0.7 (2)
WC=AWC×AWw/TWw+FWC×FWw/TWw (3)
(式(1)〜(3)中、BC、FWR、WC、FWC、AWC、FWw、AWw及びTWwはそれぞれ以下を表す。
BC:母材中の炭素含有量[質量%]
FWR:フィラーワイヤの重み係数
WC:ワイヤ炭素量の加重平均[質量%]
FWC:フィラーワイヤの炭素含有量[質量%]
AWC:アークワイヤの炭素含有量[質量%]
FWw:フィラーワイヤの溶加量[g/分]
AWw:アークワイヤの溶着量[g/分]
TWw:フィラーワイヤの溶加量とアークワイヤの溶着量の和[g/分])
2 アークトーチ
3 アークワイヤ送給装置
4 溶接電源
5 アーク
11 フィラーワイヤ
12 フィラーガイド
13 フィラーワイヤ送給装置
14 フィラー電源
101 切欠きを有する鋼板(母材)
102 鋼板(母材)
B 母材
M 溶接金属
P 溶融池
Claims (11)
- 炭素を0.20〜1.00質量%含有する炭素鋼を母材として用いる消耗電極式ガスシールドアーク溶接方法において、下記式(1)〜(3)を満足する条件でフィラーワイヤを送給する、消耗電極式ガスシールドアーク溶接方法。
0≦WC+BC×FWR−WC×FWR≦0.15 (1)
FWR=−0.8×FWw/TWw+0.7 (2)
WC=AWC×AWw/TWw+FWC×FWw/TWw (3)
(式(1)〜(3)中、BC、FWR、WC、FWC、AWC、FWw、AWw及びTWwはそれぞれ以下を表す。
BC:母材中の炭素含有量[質量%]
FWR:フィラーワイヤの重み係数
WC:ワイヤ炭素量の加重平均[質量%]
FWC:フィラーワイヤの炭素含有量[質量%]
AWC:アークワイヤの炭素含有量[質量%]
FWw:フィラーワイヤの溶加量[g/分]
AWw:アークワイヤの溶着量[g/分]
TWw:フィラーワイヤの溶加量とアークワイヤの溶着量の和[g/分]) - 前記フィラーワイヤをアークの進行方向後方から挿入する、請求項1に記載の消耗電極式ガスシールドアーク溶接方法。
- 前記フィラーワイヤがソリッドワイヤであり、前記ソリッドワイヤはその全質量を基準として、
C:0〜0.02質量%、
Si:0〜1.10質量%、
Mn:0〜2.10質量%、
P:0〜0.020質量%、及び、
S:0〜0.020質量%を含有し、
残部がFe及び不可避不純物である、請求項1又は2に記載の消耗電極式ガスシールドアーク溶接方法。 - 前記フィラーワイヤとしての前記ソリッドワイヤが、さらに、Cu:0.10〜0.40質量%、及び、Ti+Zr:0.02〜0.30質量%からなる群から選ばれる少なくとも1種を含有する、請求項3に記載の消耗電極式ガスシールドアーク溶接方法。
- 前記フィラーワイヤがメタル系フラックス入りワイヤであり、前記メタル系フラックス入りワイヤはその全質量を基準として、
C:0〜0.02質量%、
Si:0〜1.00質量%、
Mn:0〜1.70質量%、
P:0〜0.020質量%、及び、
S:0〜0.020質量%を含有し、
残部がFe及び不可避不純物である、請求項1又は2に記載の消耗電極式ガスシールドアーク溶接方法。 - 前記アークワイヤがソリッドワイヤであり、前記ソリッドワイヤはその全質量を基準として、
C:0.02〜0.15質量%、
Si:0.20〜1.10質量%、
Mn:0.40〜2.10質量%、
P:0〜0.030質量%、及び、
S:0〜0.030質量%を含有し、
残部がFe及び不可避不純物である、請求項1〜5のいずれか1項に記載の消耗電極式ガスシールドアーク溶接方法。 - 前記アークワイヤとしての前記ソリッドワイヤが、さらに、Cu:0.10〜0.40質量%、及び、Ti+Zr:0.02〜0.30質量%からなる群から選ばれる少なくとも1種を含有する、請求項6に記載の消耗電極式ガスシールドアーク溶接方法。
- 前記アークワイヤがメタル系フラックス入りワイヤであり、前記メタル系フラックス入りワイヤはその全溶着金属の質量を基準として、
C:0.02〜0.15質量%、
Si:0.20〜1.10質量%、
Mn:0.40〜2.00質量%、
P:0〜0.030質量%、及び、
S:0〜0.030質量%を含有し、
残部がFe及び不可避不純物である、請求項1〜5のいずれか1項に記載の消耗電極式ガスシールドアーク溶接方法。 - 前記アークワイヤとしての前記メタル系フラックス入りワイヤが、さらに、Ni:0.10〜0.80質量%、及び、Mo:0.05〜0.30質量%からなる群から選ばれる少なくとも1種を含有する、請求項8に記載の消耗電極式ガスシールドアーク溶接方法。
- 前記アークワイヤがスラグ系フラックス入りワイヤであり、前記スラグ系フラックス入りワイヤがその全溶着金属の質量を基準として、
C:0.02〜0.15質量%、
Si:0.20〜1.10質量%、
Mn:0.40〜2.00質量%、
P:0〜0.030質量%、及び、
S:0〜0.030質量%を含有し、
残部がFe及び不可避不純物である、請求項1〜5のいずれか1項に記載の消耗電極式ガスシールドアーク溶接方法。 - 前記アークワイヤとしての前記スラグ系フラックス入りワイヤが、さらに、Ni:0.10〜0.80質量%、及び、Mo:0.05〜0.30質量%からなる群から選ばれる少なくとも1種を含有する、請求項10に記載の消耗電極式ガスシールドアーク溶接方法。