JP6364660B2 - 吸着フィルム - Google Patents
吸着フィルム Download PDFInfo
- Publication number
- JP6364660B2 JP6364660B2 JP2014064961A JP2014064961A JP6364660B2 JP 6364660 B2 JP6364660 B2 JP 6364660B2 JP 2014064961 A JP2014064961 A JP 2014064961A JP 2014064961 A JP2014064961 A JP 2014064961A JP 6364660 B2 JP6364660 B2 JP 6364660B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- adsorption layer
- adsorption
- layer
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明で使用する基材フィルムは、各種のプラスチックからなるフィルムであれば、特に限定されない。例えばポリオレフィン、ポリエステル、ポリアミド、ポリカーボネート、トリアセチルセルロース、フッ素樹脂、ポリフェニレンオキサイド、ポリイミド、ポリアミドイミド、アクリル系樹脂、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリアクリロニトリル等よりなるフィルムが例示されるが、これらに限定されるものではない。シリコーンゴムの熱架橋時の取り扱い性、コストの面からポリエステルフィルムやポリカーボネートフィルムが好ましい。透明性の点では、ポリエステルフィルム、特にポリエチレンテレフタレートが好ましい。基材の厚みは、用途に応じて適宜選択すればよいが、通常5〜400μm、特に20〜250μmの範囲であるのが好ましい。
本発明の吸着層に用いるシリコーン樹脂の性状としては、透明性が高く、ゴムのような柔軟性を持っていて被着体の表面に対しても、吸着層の面が被着体表面に沿うことがもとめられる。さらに剥離の際には、小さい剥離力で、容易に剥離できることが求められる。また、少なくとも厚み10μm以上で、目付け加工の方法を用いることなく、塗布及び加熱処理だけで架橋吸着層を設けるためには、シリコーン組成物の硬化反応に際して、白金触媒等のもとで、150℃以下の低温短時間で深部まで架橋し、透明で耐熱性、圧縮永久歪み特性に優れかつ低粘度で液状タイプである、1分子中に2個以上のアルケニル基を有するポリオルガノシロキサンと架橋剤としてSiH基を有するオルガノハイドロジェンシロキサン−オルガノシロキサンコポリマーとの付加反応により熱架橋する付加反応型液状シリコーン組成物の使用が好ましい。
本発明の吸着フィルムを構成する吸着層のゴム硬度は、アスカーFP型硬度計(高分子計器株式会社製)を使用して測定する。アスカーFP型硬度計使用で90〜100ポイントを示す場合は、FP型より硬い材料を測定するアスカーCSC2型硬度計(高分子計器株式会社製)を使用して測定する。
。
本発明の吸着フィルムを構成する吸着層のゲル分率は、所定の大きさにカットした吸着フィルムを24時間トルエンに浸漬させ、浸漬前後での吸着層の重量比として求められる。
ゲル分率の測定は、まず、吸着フィルムを所定の大きさにカットし、その試験片に積層されている吸着層の重量を測定する(その重量をG1とする)。次に、その試験片を50mlのトルエンに浸漬した後、25℃で1日放置する。続いて、試験片及びトルエン溶液を濾過した残渣を105℃で2時間乾燥させ、試験片に積層された吸着層の乾燥後の重量、及びトルエン溶液を濾過した残渣の乾燥後の重量を測定する(その合算重量をG2とする)。その後、ゲル分率=(G2/G1)×100により算出する。
本発明においては、基材フィルムと吸着層との接着力の向上、および被着体への自己貼着性フィルムの貼着後、前記自己貼着性フィルムを再剥離する際に、前記吸着層と基材フィルム間で剥離することなく、被着体からスムーズに剥離できることを目的として、前記基材フィルムと吸着層との間にアンカー層を設けてもよい。
はできるだけ平滑であることが必要である。表面の凹凸が大きいとシリコーン吸着層が凹凸に追従することが難しくなり、密着することができなくなる。
プラズマ処理された厚み75μmのポリエチレンテレフタレートフィルムの片面に、下記アンカー層塗工液をグラビアコーターで塗工、乾燥して、厚み2.0μmのアンカー層を形成した。
アクリルポリオール樹脂 20部
(東レファインケミカル製、コータックスLH455、固形分:50%)
ポリチオフェン 27部
(信越ポリマー製、セプルジーダOC−SC100、固形分:3%)
MEK 40部
トルエン 13部
前記のアンカー層の上に、表1の成分を、表中の塗布厚みの吸着層を設けた後、オーブンにて150℃、100秒で架橋させて本発明の吸着フィルムを作製した。
(ゴム硬度)
直径が60mmのアルミ製カップに、表1の実施例、比較例の吸着層用塗工液を、所定量流し込み、ギヤオーブンにて150℃、100秒で架橋させて、厚さ約10mmのゴム硬度測定用の試験片を作製した。ついで、アスカーFP硬度計、またはアスカーCSC2硬度計(ともに高分子計器株式会社製)を用いて、前記硬度計の測定部に試験片を挟み込み、各サンプルのゴム硬度を測定した。
吸着層のゲル分率の測定は、まず、上記作製した吸着フィルムを50mm×50mmの大きさにカットし、その試験片に積層されている吸着層の重量を測定する(その重量をG1とする)。次に、その試験片を50mlのトルエンに浸漬した後、25℃で1日放置する。続いて、試験片及びトルエン溶液を濾過した残渣を105℃で2時間乾燥させ、試験片に積層された吸着層の乾燥後の重量、及びトルエン溶液を濾過した残渣の乾燥後の重量を測定する(その合算重量をG2とする)。ゲル分率=(G2/G1)×100により算出した。
上記作成した吸着フィルムを25mm幅にカットし、前記吸着フィルムの吸着層を厚み2mmのソーダ石灰ガラス板に2Kgのローラーを1往復させる方式で圧着し、圧着後室温で約24時間放置した。次に、引っ張り試験機を用いて、180°の剥離角度、剥離速度:1200mm/minで剥離し、吸着フィルムのアクリル板剥離力(mN/25mm)を測定した。
リワーク性の評価基準
◎:アクリル板剥離力が25mN/25mm以上、150mN/25mm未満
○:アクリル板剥離力が150mN/25mm以上、400mN/25mm未満
×:アクリル板剥離力が25mN/25mm未満、400mN/25mm以上
上記作成した吸着フィルムを50mm×50mmにカットし、直径4mmのガラスビーズを間に挟み込んで厚み2mmのアクリル板に貼着した。次に前記吸着フィルムを前記アクリル板から剥離して前記ガラスビーズを取り除き、前記吸着フィルムを前記アクリル板に再び貼着して、直径4mmの気泡を巻込んだ積層体を作成した。前記積層体の直径4mmの気泡を、指を用いて1.8〜2.0kgの荷重で10秒押し、気泡の有無を確認した。
評価基準
◎:気泡が全くない
○:気泡が殆どなし
×:気泡が消失せず、残っている
Claims (1)
- 基材フィルムの少なくとも片面に、シリコーン樹脂を主成分とする吸着層を積層した吸着フィルムにおいて、前記吸着層が、1分子中に2個以上のアルケニル基を有するジオルガノポリシロキサンと、オルガノハイドロジェンシロキサン−オルガノシロキサンコポリマーからなるシリコーン組成物を、付加反応により硬化してなるものであり、前記1分子中に2個以上のアルケニル基を有するジオルガノポリシロキサンの重量平均分子量は540,000であり、前記吸着層のアスカーFP硬度が40以上又は、アスカーCSC2硬度が5以下であり、かつ前記吸着層のゲル分率が60%以上、80%以下であり、かつ前記吸着層の厚みが10〜40μmであることを特徴とする吸着フィルム。