JP6312185B1 - コンクリート用含浸剤 - Google Patents
コンクリート用含浸剤 Download PDFInfo
- Publication number
- JP6312185B1 JP6312185B1 JP2017233514A JP2017233514A JP6312185B1 JP 6312185 B1 JP6312185 B1 JP 6312185B1 JP 2017233514 A JP2017233514 A JP 2017233514A JP 2017233514 A JP2017233514 A JP 2017233514A JP 6312185 B1 JP6312185 B1 JP 6312185B1
- Authority
- JP
- Japan
- Prior art keywords
- concrete
- impregnating agent
- compound
- aminosilane
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
[1]ケイ酸リチウム系化合物と、アミノシラン系化合物と、カリウムメチルシリコネートと、溶媒と、を含む、コンクリート用含浸剤。
[3]前記溶媒が、水である、[1]または[2]に記載のコンクリート用含浸剤。
[4]前記アミノシラン系化合物を、0.1質量%以上含む、[1]〜[3]のいずれかに記載のコンクリート用含浸剤
以下に示す各材料を準備した。
・ケイ酸リチウム系化合物:日本化学工業社製 ケイ酸リチウム溶液 75
・アミノシラン系化合物1:信越化学工業社製 アミノシランカップリング剤 KBM602
・アミノシラン系化合物2:信越化学工業社製 アミノシランカップリング剤 KBM603
・カリウムメチルシリコネート:旭化成ワッカー社製 カリウムメチルシリコネート水溶液
・純水
ケイ酸リチウム系化合物と、アミノシラン系化合物と、カリウムメチルシリコネートと、を表1に示す割合となるように混合し、コンクリート用含浸剤を得た。下記表における、ケイ酸リチウム系化合物およびカリウムメチルシリコネートの量は有効成分量である。また、表1には、各コンクリート用含浸剤の性状も併せて記載する。
JIS R5201(セメントの物理試験方法)で規定されるモルタルを、3分間低速で練り混ぜた。練り混ぜたモルタルを、140mm×140mm×160mmの3連の枠型、および100mm×100mm×10mmの3連の型枠に、それぞれ打設し、評価用コンクリートを作製した。なお、評価用コンクリートは、24時間後に脱型し、温度20℃、湿度60%の試験室で7日間養生させた。
上記コンクリート用含浸剤に浸漬させた評価用コンクリート、および浸漬なしの評価用コンクリートについて、それぞれ摩耗試験、ならびに曲げおよび圧縮強さ試験を行った。また、既存のコンクリート構造物に対するアルカリ性回復の評価も行った。
各評価用コンクリートに対して、JIS K7204(プラスチック−摩耗輪による摩耗試験方法)に準じて、摩耗試験を行った。なお、摩耗輪はH−22を使用し、荷重は9.8N、回転数は200回転とし、摩耗質量および厚さの減少率を各3回測定した。結果を表2に示す。
各評価用コンクリートに対して、JIS R5201に準じて、曲げ強さ試験を各3回、圧縮強さ試験を各6回行った。なお、各評価用コンクリートの材齢は28日とした。結果を表3に示す。
上述の実施例1および実施例2のコンクリート用含浸剤に浸漬させた評価用コンクリートに、水を滴下し、撥水性を評価した。水を滴下した後の写真を図1A(実施例1)および図1B(実施例2)に示す。図1Aおよび図1Bに示されるように、いずれの評価用コンクリートに水を滴下した場合にも、水が弾かれた。つまり、実施例1及び実施例2のコンクリート用含浸剤を浸漬させた評価用コンクリートでは、内部に水が浸透し難く、十分な撥水性を有することが明らかであった。
上述のコンクリート用含浸剤(実施例1および実施例2)を、細骨材として海砂を用いた、築35年、平均中性化深さ2.7cmの鉄筋コンクリート構造物に7m2/kg塗布した。その後、中性化深さを測定したところ、いずれも中性深さ0cmとなった。つまり、アルカリ性が回復されたことが確認された。なお、中性化深さの確認は、構造物の切断面にフェノールフタレイン1質量%エタノール溶液を噴霧して測定した。
Claims (4)
- ケイ酸リチウム系化合物と、アミノシラン系化合物と、カリウムメチルシリコネートと、溶媒と、を含む、コンクリート用含浸剤。
- 前記アミノシラン系化合物を、2種以上含む、請求項1に記載のコンクリート用含浸剤。
- 前記溶媒が、水である、請求項1または2に記載のコンクリート用含浸剤。
- 前記アミノシラン系化合物を、0.1質量%以上含む、請求項1〜3のいずれか一項に記載のコンクリート用含浸剤。