JP6159505B2 - Flat copper particles - Google Patents

Flat copper particles Download PDF

Info

Publication number
JP6159505B2
JP6159505B2 JP2010292693A JP2010292693A JP6159505B2 JP 6159505 B2 JP6159505 B2 JP 6159505B2 JP 2010292693 A JP2010292693 A JP 2010292693A JP 2010292693 A JP2010292693 A JP 2010292693A JP 6159505 B2 JP6159505 B2 JP 6159505B2
Authority
JP
Japan
Prior art keywords
particles
copper particles
copper
flat copper
flat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2010292693A
Other languages
Japanese (ja)
Other versions
JP2012140661A (en
Inventor
良憲 清水
良憲 清水
Original Assignee
三井金属鉱業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三井金属鉱業株式会社 filed Critical 三井金属鉱業株式会社
Priority to JP2010292693A priority Critical patent/JP6159505B2/en
Publication of JP2012140661A publication Critical patent/JP2012140661A/en
Application granted granted Critical
Publication of JP6159505B2 publication Critical patent/JP6159505B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、扁平な形状をした銅粒子に関する。本発明の扁平銅粒子は、例えばプリント配線板の回路形成や、セラミックコンデンサの外部電極の電気的導通確保のために用いられる銅ペーストの原料として特に好適に用いられる。   The present invention relates to a copper particle having a flat shape. The flat copper particles of the present invention are particularly preferably used as a raw material for a copper paste used, for example, for circuit formation of a printed wiring board and ensuring electrical continuity of external electrodes of a ceramic capacitor.
従来、電子部品等の電極や回路を形成する方法として、導電性材料である銅粉をペーストに分散させた導電性ペーストを基板に印刷した後、該ペーストを焼結又は硬化させて回路を形成する方法が知られている。   Conventionally, as a method of forming electrodes and circuits for electronic components, etc., a conductive paste in which copper powder as a conductive material is dispersed in a paste is printed on a substrate, and then the paste is sintered or cured to form a circuit. How to do is known.
例えば、セラミックコンデンサの外部電極の導通に導電性ペーストを用いる場合は、外部電極に導電性ペーストを塗布し、次いで加熱することで脱バインダーを行い、その後に銅粒子を焼結させる。この場合、外観保持、脱バインダー効率及び導電性向上のために、銅粒子の形状は、球状よりも扁平であることが好ましいとされている。扁平状の粒子は比表面積が大きく、粒子どうしの接触面積が大きくなるので、電気抵抗を減少させ、導体形状の精度を上げるのに有効だからである。   For example, when using a conductive paste for conduction of the external electrode of the ceramic capacitor, the conductive paste is applied to the external electrode, and then the binder is removed by heating, after which the copper particles are sintered. In this case, the shape of the copper particles is preferably flat rather than spherical in order to maintain the appearance, improve the binder removal efficiency, and improve the conductivity. This is because flat particles have a large specific surface area and a large contact area between the particles, which is effective in reducing electrical resistance and increasing the accuracy of the conductor shape.
従来、扁平状の銅粒子は、例えば球形の銅粒子をボールミル等で機械的に変形させて製造していた(例えば特許文献1参照)。この方法では、使用するビーズの大きさよって粒子の扁平化に限界がある。また、製造に長時間を有し、また歩留りも下がるので、製造経費を抑えることが容易でなかった。そこで、このような機械的な方法に代えて、化学的に扁平状の銅粒子を製造する方法も提案されている(例えば特許文献2参照)。   Conventionally, flat copper particles have been manufactured by mechanically deforming, for example, spherical copper particles with a ball mill or the like (see, for example, Patent Document 1). In this method, there is a limit to flattening the particles depending on the size of the beads used. Moreover, since it takes a long time to manufacture and the yield decreases, it is not easy to suppress the manufacturing cost. Therefore, instead of such a mechanical method, a method for producing chemically flat copper particles has also been proposed (see, for example, Patent Document 2).
扁平状の銅粒子の技術とは別に、銅粒子の表面にSiO2の膜を形成する技術も知られている(特許文献3参照)。この銅粒子は、導電ペーストの導電フイラーに用いるものであり、5重量%以下のSiを含有し、そのSiの実質上すべてがSiO2系ゲルコーティング膜として銅粒子表面に被着しているものである。同文献によれば、この銅粒子は耐酸化性に優れたものであるとされている。 In addition to the technique of flat copper particles, a technique of forming a SiO 2 film on the surface of copper particles is also known (see Patent Document 3). This copper particle is used for a conductive filler of a conductive paste, contains 5% by weight or less of Si, and substantially all of the Si is deposited on the surface of the copper particle as a SiO 2 -based gel coating film. It is. According to this document, the copper particles are said to be excellent in oxidation resistance.
Siを含む銅粒子に関し、本出願人は先に、粒子内部にSiを0.1〜10atm%含有する導電性ペースト用銅粉を提案した(特許文献4参照)。Siは銅粉の耐酸化性を高める目的で添加される。この銅粉は金属銅及び金属ケイ素を溶融させて溶湯とし、これを高圧ガスアトマイズすることで得られる。   Regarding the copper particles containing Si, the present applicant has previously proposed copper powder for conductive paste containing 0.1 to 10 atm% of Si inside the particles (see Patent Document 4). Si is added for the purpose of increasing the oxidation resistance of the copper powder. This copper powder is obtained by melting metal copper and metal silicon to form a molten metal, and subjecting this to high pressure gas atomization.
特開2003−119501号公報JP 2003-119501 A 特開2005−314755号公報JP 2005-314755 A 特開2003−16832号公報JP 2003-16832 A 特開2010−13726号公報JP 2010-13726 A
特許文献2に記載の化学的な方法によれば、特許文献1に記載の技術よりも高い歩留りで、粒径の小さな扁平状の粒子を製造することができる。しかし、反応時にリン等の添加剤を加えることに起因して、この添加剤に由来するリン等の元素が粒子内に残存する。リン等の添加は、銅の結晶性の向上に寄与するという利点をもたらすが、その反面、銅粒子の熱収縮温度を低下させることがある。   According to the chemical method described in Patent Document 2, flat particles having a small particle diameter can be produced with a higher yield than the technique described in Patent Document 1. However, due to the addition of an additive such as phosphorus during the reaction, elements such as phosphorus derived from this additive remain in the particles. Addition of phosphorus or the like brings about an advantage that it contributes to the improvement of the crystallinity of copper, but on the other hand, it may lower the heat shrink temperature of the copper particles.
特許文献3に記載の銅粒子は、その表面がSiO2でコーティングされていることで、酸化されにくい状態になっており、粒子それ単独では耐熱収縮性を有する。しかし、ペーストとして使用した場合には、耐熱収縮性が極端に低下する。この理由は、ペーストの焼結時に、SiO2コーティングが、ペーストに含まれるガラスフリットに引き寄せられてしまい、粒子の表面から離脱してしまうからである。 The copper particles described in Patent Document 3 are not easily oxidized because the surfaces thereof are coated with SiO 2 , and the particles themselves have heat shrinkage resistance. However, when used as a paste, the heat shrinkage is extremely reduced. This is because, during sintering of the paste, the SiO 2 coating is attracted to the glass frit contained in the paste and detached from the surface of the particles.
特許文献4に記載の銅粉は、Siを含有しているものの、Siは母材であるCu中に固溶した状態になっている。つまり、Siは四価の酸化物の状態ではなく、ゼロ価の状態になっている。このことに起因して、この銅粉は、耐酸化性は高いが、耐熱収縮性については一層の改善が望ましい。   Although the copper powder described in Patent Document 4 contains Si, Si is in a state of being dissolved in Cu as a base material. That is, Si is not in a tetravalent oxide state but in a zero-valent state. Due to this, the copper powder has high oxidation resistance, but further improvement in heat shrinkability is desirable.
したがって本発明の課題は、前述した従来技術の銅粒子よりも各種の特性が一層向上した扁平銅粒子を提供することにある。   Accordingly, an object of the present invention is to provide flat copper particles having various characteristics further improved as compared with the copper particles of the prior art described above.
本発明は、1mol/Lの水酸化ナトリウム水溶液を用い、70℃以上で60分間煮沸して溶出する、粒子最表面部分に存在するSiが粒子全体に対して重量基準で100〜2000ppmであり、かつ該Siの少なくとも一部が四価の状態で存在している扁平銅粒子であって、
1mol/Lの水酸化ナトリウム水溶液を用い、70℃以上で60分間煮沸した後の前記銅粒子を酸によってすべて溶解させ、得られた溶液について元素分析を行い測定されたSiの量が、粒子全体に対して重量基準で20〜300ppmであり、
粒径(μm)と厚み(μm)との積で表されるA値が0.0125以上0.05未満であり、焼結開始温度が400〜500℃であるか、
粒径(μm)と厚み(μm)との積で表されるA値が0.05以上0.3未満であり、焼結開始温度が600〜800℃であるか、又は
粒径(μm)と厚み(μm)との積で表されるA値が0.3以上8以下であり、焼結開始温度が700〜800℃である扁平銅粒子を提供することで前記の課題を解決したものである。
In the present invention, a 1 mol / L sodium hydroxide aqueous solution is used and boiled at 70 ° C. or higher for 60 minutes to elute, and Si present on the outermost surface of the particle is 100 to 2000 ppm by weight based on the entire particle. And the flat copper particle in which at least a part of the Si exists in a tetravalent state,
Using a 1 mol / L sodium hydroxide aqueous solution, all the copper particles after boiling for 60 minutes at 70 ° C. or more were dissolved with an acid, and the amount of Si measured by performing elemental analysis on the resulting solution was determined as the whole particles. 20 to 300 ppm on a weight basis,
A value represented by the product of the particle size (μm) and the thickness (μm) is 0.0125 or more and less than 0.05, and the sintering start temperature is 400 to 500 ° C.,
The A value represented by the product of the particle size (μm) and the thickness (μm) is 0.05 or more and less than 0.3, and the sintering start temperature is 600 to 800 ° C. or the particle size (μm) A value expressed by the product of the thickness and the thickness (μm) is 0.3 or more and 8 or less, and the above problem is solved by providing flat copper particles having a sintering start temperature of 700 to 800 ° C. It is.
また本発明は、前記の扁平銅粒子の好適な製造方法として、
水溶性銅化合物を含む水溶液に還元剤を添加して銅の還元を行う還元工程を有
還元の前又は還元中に、水溶性ケイ酸塩を添加することを特徴とする扁平銅粒子の製造方法を提供するものである。
In addition, the present invention provides a suitable method for producing the flat copper particles,
By adding a reducing agent to an aqueous solution containing a water-soluble copper compound have a reduction step for reducing the copper,
The present invention provides a method for producing flat copper particles, characterized by adding a water-soluble silicate before or during the reduction.
本発明の扁平銅粒子によれば、電気伝導性を損なうことなく、小粒径でありながら耐熱収縮性を高めることができる。   According to the flat copper particles of the present invention, heat shrinkage can be improved while maintaining a small particle size without impairing electrical conductivity.
図1は、実施例1で得られた扁平銅粒子の走査型電子顕微鏡像である。1 is a scanning electron microscope image of the flat copper particles obtained in Example 1. FIG. 図2は、実施例2で得られた扁平銅粒子の走査型電子顕微鏡像である。FIG. 2 is a scanning electron microscope image of the flat copper particles obtained in Example 2. 図3は、実施例3で得られた扁平銅粒子の走査型電子顕微鏡像である。FIG. 3 is a scanning electron microscope image of the flat copper particles obtained in Example 3. 図4は、実施例4で得られた扁平銅粒子の走査型電子顕微鏡像である。4 is a scanning electron microscope image of the flat copper particles obtained in Example 4. FIG. 図5は、実施例5で得られた扁平銅粒子の走査型電子顕微鏡像である。FIG. 5 is a scanning electron microscope image of the flat copper particles obtained in Example 5. 図6は、実施例6で得られた扁平銅粒子の走査型電子顕微鏡像である。FIG. 6 is a scanning electron microscope image of the flat copper particles obtained in Example 6. 図7は、実施例7で得られた扁平銅粒子の走査型電子顕微鏡像である。FIG. 7 is a scanning electron microscope image of the flat copper particles obtained in Example 7. 図8は、比較例1で得られた銅粒子の走査型電子顕微鏡像である。FIG. 8 is a scanning electron microscope image of the copper particles obtained in Comparative Example 1. 図9は、比較例2で得られた扁平銅粒子の走査型電子顕微鏡像である。FIG. 9 is a scanning electron microscope image of the flat copper particles obtained in Comparative Example 2. 図10(a)及び(b)は、比較例3並びに実施例2、4及び7で得られた銅粒子の熱機械分析結果を示すグラフである。FIGS. 10A and 10B are graphs showing the results of thermomechanical analysis of the copper particles obtained in Comparative Example 3 and Examples 2, 4 and 7. FIG.
以下本発明を、その好ましい実施形態に基づき説明する。本発明の銅粒子は、その形状が扁平であることによって特徴付けられる。具体的には、対向する略平坦な2つの面を有し、該面の大きさ(横断長さ)が厚みに比べて大きくなっている板状の形状をしている。後述する製造方法から明らかなように、本発明においては、好ましくは化学的な製造方法を採用することで扁平な形状の銅粒子を得ている。   Hereinafter, the present invention will be described based on preferred embodiments thereof. The copper particles of the present invention are characterized by their flat shape. Specifically, it has a plate-like shape having two substantially flat surfaces facing each other, and the size (transverse length) of the surfaces is larger than the thickness. As apparent from the manufacturing method described later, in the present invention, flat copper particles are preferably obtained by adopting a chemical manufacturing method.
本発明の扁平銅粒子は、耐熱収縮性が高いことが特徴の一つである。後述するように、本発明の扁平銅粒子の耐熱収縮性は、該扁平銅粒子の表面に微量のSiを存在させることで発現する。本発明の扁平銅粒子の耐熱収縮性は、その粒径が小さい場合に特に顕著である。すなわち、銅粒子は一般に、その粒径が小さくなるに連れて耐熱収縮性が低くなる傾向にあるところ、同じ粒径で比較した場合、本発明の扁平銅粒子は、従来の銅粒子よりも耐熱収縮性が高いものである。この観点から、本発明の扁平銅粒子は、その平均粒径が好ましくは0.5〜5μm、更に好ましくは0.6〜2μmである場合に、その特徴が顕著なものとなる。この平均粒径は、扁平銅粒子を走査型電子顕微鏡(SEM)で観察し、画像解析して算出された板面の平均粒径のことである。この画像解析による平均粒径は、SEMを用い5000倍〜20000倍に拡大して直接観察して得られるSEM像に基づき、個々の銅粒子(測定サンプル数は10個以上)の最大横断長を実測し、測定サンプル数で平均することで求められる。   One feature of the flat copper particles of the present invention is that they have high heat shrinkage resistance. As will be described later, the heat shrinkability of the flat copper particles of the present invention is manifested by the presence of a small amount of Si on the surface of the flat copper particles. The heat-shrinkage resistance of the flat copper particles of the present invention is particularly remarkable when the particle size is small. In other words, copper particles generally tend to have lower thermal shrinkage as their particle size becomes smaller. When compared with the same particle size, the flat copper particles of the present invention are more heat resistant than conventional copper particles. High shrinkage. From this viewpoint, the flat copper particles of the present invention have remarkable features when the average particle diameter is preferably 0.5 to 5 μm, more preferably 0.6 to 2 μm. This average particle diameter is the average particle diameter of the plate surface calculated by observing flat copper particles with a scanning electron microscope (SEM) and analyzing the image. The average particle size obtained by this image analysis is based on the SEM image obtained by direct observation using a SEM with a magnification of 5000 to 20000 times, and the maximum transverse length of each copper particle (the number of measurement samples is 10 or more). It is obtained by actually measuring and averaging by the number of measurement samples.
本発明の扁平銅粒子における板面の好適な平均粒径が前記の範囲であるのに対して、該粒子の厚み、すなわち2つの対向する板面間の距離は、板面の平均粒径よりも小さくなっている。具体的には、好ましくは0.025〜1.66μm、更に好ましくは0.03〜0.1μmになっている。したがって、粒径/厚みで定義されるアスペクト比は、好ましくは2〜200、更に好ましくは6〜66になっている。扁平銅粒子の厚みは、SEMによる直接観察で測定される実測値を平均して(測定サンプル数10個以上)求められる。   Whereas the preferred average particle size of the plate surface in the flat copper particles of the present invention is within the above range, the thickness of the particle, that is, the distance between two opposing plate surfaces is more than the average particle size of the plate surface. Is also getting smaller. Specifically, it is preferably 0.025 to 1.66 μm, more preferably 0.03 to 0.1 μm. Therefore, the aspect ratio defined by the particle size / thickness is preferably 2 to 200, more preferably 6 to 66. The thickness of the flat copper particles is obtained by averaging measured values measured by direct observation with an SEM (number of measurement samples: 10 or more).
扁平銅粒子は一般に、その粒径が大きいほど耐熱収縮性が高くなり、また厚みが厚いほど耐熱収縮性が高くなる。そこで本発明の扁平銅粒子における耐熱収縮性は、その粒径(μm)と厚み(μm)との積で表される値(以下、この値を「A値」という。)によって評価することができる。この値が大きいほど耐熱収縮性が高いと言える。本発明においては、扁平銅粒子の平均粒径及び厚みが上述の範囲内であることを条件として、(イ)A値が0.0125以上0.05未満の範囲内である場合、焼結開始温度が400〜500℃、特に420〜495℃であることが好ましい。また、(ロ)A値が0.05以上0.3未満の範囲内である場合、焼結開始温度が600〜800℃、特に650〜795℃であることが好ましい。更に、(ハ)A値が0.3以上8以下の範囲内である場合、焼結開始温度が700〜800℃、特に720〜795℃であることが好ましい。このような高い耐熱収縮性は、扁平銅粒子の表面に、後述する範囲の量のSiを存在させることで初めて実現される。   In general, the flat copper particles have a higher heat shrinkage resistance as the particle size is larger, and the heat shrinkage property is higher as the thickness is larger. Therefore, the heat shrinkage resistance of the flat copper particles of the present invention can be evaluated by a value represented by the product of the particle size (μm) and the thickness (μm) (hereinafter, this value is referred to as “A value”). it can. It can be said that heat resistance shrinkage is so high that this value is large. In the present invention, on the condition that the average particle diameter and thickness of the flat copper particles are within the above range, (a) when the A value is within the range of 0.0125 or more and less than 0.05, the sintering starts. The temperature is preferably 400 to 500 ° C, particularly 420 to 495 ° C. Further, (b) when the A value is in the range of 0.05 or more and less than 0.3, the sintering start temperature is preferably 600 to 800 ° C, particularly preferably 650 to 795 ° C. Furthermore, (c) when the A value is in the range of 0.3 to 8, the sintering start temperature is preferably 700 to 800 ° C, particularly preferably 720 to 795 ° C. Such a high heat shrinkage resistance is realized for the first time by allowing Si in an amount to be described later to be present on the surface of the flat copper particles.
本発明の扁平銅粒子が前記の(イ)の条件を満たす場合、該粒子の平均粒径は、上述の範囲内であることを条件として、0.5〜0.8μm、特に0.6〜0.78μmであることが好ましく、該粒子の厚みは、上述の範囲内であることを条件として、0.020〜0.062μm、特に0.025〜0.060μmであることが好ましい。本発明の扁平銅粒子が前記の(ロ)の条件を満たす場合には、該粒子の平均粒径は、0.8〜1.2μm、特に1〜1.1μmであることが好ましく、該粒子の厚みは、0.062〜0.25μm、特に0.10〜0.24μmであることが好ましい。前記の(ハ)の条件を満たす場合には、平均粒径は、1.2〜5μm、特に1.25〜4μmであることが好ましく、厚みは、0.25〜1.6μm、特に0.3〜1.3μmであることが好ましい。   When the flat copper particles of the present invention satisfy the condition (a), the average particle size of the particles is 0.5 to 0.8 μm, particularly 0.6 to 0.6, provided that the average particle size is within the above range. The thickness of the particles is preferably 0.78 μm, and the thickness of the particles is preferably 0.020 to 0.062 μm, particularly preferably 0.025 to 0.060 μm, provided that the thickness is within the above range. When the flat copper particles of the present invention satisfy the condition (b), the average particle size of the particles is preferably 0.8 to 1.2 μm, particularly preferably 1 to 1.1 μm. The thickness of is preferably 0.062 to 0.25 μm, particularly preferably 0.10 to 0.24 μm. In the case where the condition (c) is satisfied, the average particle size is preferably 1.2 to 5 μm, particularly preferably 1.25 to 4 μm, and the thickness is preferably 0.25 to 1.6 μm, particularly preferably 0.00. It is preferable that it is 3-1.3 micrometers.
前記の焼結開始温度は、熱分析装置を用いた熱機械分析(TMA)によって測定することができる。具体的には、SEIKO Instrument Inc.製のSEIKO EXSTAR 6000を用いる。試料は、測定対象となる扁平銅粒子0.5gを金型に計りとり、プレス機によって1ton/cm2の圧力で加圧してペレットにしたものを用いる。この試料を熱分析装置にセットし、測定前の試料長を測定する(装置が自動測定する)。試料は49mNの圧力で上側から押さえつけられている。雰囲気1%H2−N2(150mL/min)、昇温速度10℃/minの条件で温度を上昇させていき、試料の長さが0.2%収縮したときの温度を読み取り、そのときの温度を焼結開始温度とする。焼結開始温度は、その値が大きいほど、銅粒子の耐熱収縮性が高いことを意味する。 The sintering start temperature can be measured by thermomechanical analysis (TMA) using a thermal analyzer. Specifically, SEIKO EXSTAR 6000 manufactured by SEIKO Instrument Inc. is used. As the sample, 0.5 g of flat copper particles to be measured is measured in a mold and pressed into a pellet by pressing with a press at a pressure of 1 ton / cm 2 . This sample is set in a thermal analyzer, and the sample length before measurement is measured (the device automatically measures). The sample was pressed from above with a pressure of 49 mN. The temperature was raised under the conditions of an atmosphere of 1% H 2 —N 2 (150 mL / min) and a heating rate of 10 ° C./min, and the temperature when the sample contracted 0.2% was read. Is the sintering start temperature. The larger the value of the sintering start temperature, the higher the heat shrinkage resistance of the copper particles.
本発明の扁平銅粒子の板面の輪郭(扁平銅粒子を平面視した場合の板面の形状)に特に制限はなく、例えば円形、楕円形、長円形、多角形、不定形等であり得る。扁平銅粒子の充填密度を高める観点から、該粒子の板面の形状は、円形、楕円形、長円形、多角形等であることが好ましい。   There is no particular limitation on the contour of the plate surface of the flat copper particles of the present invention (the shape of the plate surface when the flat copper particles are viewed in plan), and may be, for example, a circle, an ellipse, an oval, a polygon, an irregular shape, or the like. . From the viewpoint of increasing the packing density of the flat copper particles, the shape of the plate surface of the particles is preferably a circle, an ellipse, an oval, a polygon or the like.
先に述べたとおり、本発明の扁平銅粒子は、粒子最表面部分にSiが存在している。粒子最表面部分とは、銅粒子自体の最も表面の部位のことである。したがって、銅粒子の表面に更に何らかの物質の被覆層が形成されている場合、該被覆層の表面の部位は、前記の「粒子最表面部分」には該当しない。本発明の扁平銅粒子の粒子最表面部分に存在しているSiは、その価数が四価になっている。尤も、後述するように、扁平銅粒子の粒子最表面部分に存在するSiの量は微量なので、扁平銅粒子の表面において四価のSiがどのような状態で存在しているのかは同定することが容易ではないが、本発明者らは、Siはその酸化物の状態で存在しているのではないかと推測している。本発明者らは、本発明の扁平銅粒子に含まれるSiが四価のものであることを、次の方法で確認している。まず本発明の扁平銅粒子を得る合成方法において、銅源になる銅化合物を加えずに反応を行い、Siの生成物を得た。得られたSi生成物のXRD測定結果から、この生成物がSiOであることが確認された。次に、銅源を加えた実施例1の合成方法で扁平銅粒子を得た。得られた扁平銅粒子をXRD測定してもSi生成量が微量であるために検出されなかった。
As described above, the flat copper particles of the present invention have Si present at the outermost surface portion of the particles. The particle outermost surface portion is a portion of the outermost surface of the copper particle itself. Therefore, when a coating layer of some substance is further formed on the surface of the copper particles, the surface portion of the coating layer does not correspond to the “particle outermost surface portion”. Si present in the outermost surface portion of the flat copper particles of the present invention has a valence of four. However, as will be described later, since the amount of Si present on the outermost surface portion of the flat copper particles is very small, it is necessary to identify the state in which tetravalent Si is present on the surface of the flat copper particles. Although it is not easy, the present inventors speculate that Si exists in the state of its oxide. The present inventors have confirmed by the following method that Si contained in the flat copper particles of the present invention is tetravalent. First, in the synthesis method for obtaining flat copper particles according to the present invention, a reaction was performed without adding a copper compound serving as a copper source to obtain a Si product. From the XRD measurement result of the obtained Si product, it was confirmed that this product was SiO 2 . Next, flat copper particles were obtained by the synthesis method of Example 1 in which a copper source was added. Even if the obtained flat copper particles were measured by XRD, they were not detected because the amount of Si produced was very small.
なお、本発明の扁平銅粒子の粒子最表面部分に存在するSiは、四価のみであることが好ましいが、微量であれば、粒子最表面部分に四価以外の価数のSiが存在していることは妨げられない。   Si present in the outermost surface portion of the flat copper particles of the present invention is preferably tetravalent only, but if the amount is small, Si having a valence other than tetravalent exists in the outermost surface portion of the particle. It is not hindered.
本発明においては、扁平銅粒子の粒子最表面部分に存在するSiの量を100〜2000ppmという微量に設定している。このような微量のSiが粒子最表面部分に存在していることで、本発明の扁平銅粒子は、その電気伝導性を損なうことなく、耐熱収縮性が高められたものとなる。特に、小粒径でありながら耐熱収縮性が高められたものとなる。粒子最表面部分に特定量のSiが存在している本発明の扁平銅粒子の耐熱収縮性が高くなる理由は、銅粒子の粒子最表面部分に存在しているSiを含む化合物が、該粒子の加熱時に、該粒子の収縮を妨げるためではないかと、本発明者らは考えている。また、後述するとおり、本発明の扁平銅粒子は化学的な方法によって製造されるものなので、銅の結晶子径が大きくなり、そのことに起因しても耐熱収縮性が高くなるではないかと、本発明者らは考えている。しかも、銅粒子の粒子最表面部分に存在するSiの量は上述のとおり微量であり、そのことに起因して該粒子の表面には銅が露出していると考えられるので、該粒子の電気導電性が損なわれないと、本発明者らは考えている。なおppmは、重量基準の百万分率のことである。
In the present invention, the amount of Si present in the outermost surface portion of the flat copper particles is set to a very small amount of 100 to 2000 ppm. The presence of such a small amount of Si on the outermost surface part of the particles makes the flat copper particles of the present invention improved in heat shrinkage without impairing their electrical conductivity. In particular, the heat shrinkage resistance is improved while having a small particle size. The reason why the flattened copper particles of the present invention in which a specific amount of Si is present in the outermost surface part of the particles is high in heat shrinkage is that the compound containing Si present in the outermost surface part of the copper particles is the particles The present inventors consider that it may prevent the shrinkage of the particles during heating. Further, as will be described later, since the flat copper particles of the present invention are produced by a chemical method, the crystallite diameter of copper is increased, and heat shrinkage may be increased due to that, The present inventors are thinking. In addition, the amount of Si present on the outermost surface portion of the copper particles is very small as described above, and it is considered that copper is exposed on the surface of the particles. The present inventors consider that the conductivity is not impaired. Ppm means parts per million by weight.
扁平銅粒子の粒子最表面部分に存在するSiの量は、該粒子を強アルカリ水溶液、例えば1mol/Lの水酸化ナトリウム水溶液を用い、70℃以上で60分間煮沸して、Siを液中に溶解させ、その液を元素分析(例えばICPによる分析)することで求めることができる。   The amount of Si present in the outermost surface portion of the flat copper particles is determined by boiling the particles with a strong alkaline aqueous solution, for example, a 1 mol / L sodium hydroxide aqueous solution at 70 ° C. or more for 60 minutes, so that Si is contained in the liquid. It can be obtained by dissolving and performing elemental analysis (for example, analysis by ICP) of the liquid.
本発明の扁平銅粒子の粒子最表面部分に存在している元素であるSiは、導電性ペーストに通常含まれている成分であるガラスフリットを構成する元素でもある。したがって、ガラスフリットを含む導電性ペーストに、本発明の扁平銅粒子を添加してペーストを得る場合には、該ペーストの焼結時の高温によってガラスフリットにSiが吸収される。その結果、不純物の少ない焼結膜を形成することが可能になる。   Si, which is an element present on the outermost surface portion of the flat copper particles of the present invention, is also an element that constitutes a glass frit, which is a component that is usually contained in a conductive paste. Therefore, when the flat copper particles of the present invention are added to a conductive paste containing glass frit to obtain a paste, Si is absorbed by the glass frit due to the high temperature during sintering of the paste. As a result, a sintered film with few impurities can be formed.
本発明の扁平銅粒子は、該粒子の粒子最表面部分にSiが存在していることに加えて、粒子の内部にもSiを含んでいることが好ましい。粒子の内部に存在しているSiは、導電性ペーストの焼結時に、該ペーストに含まれるガラスフリットに引き寄せられることがないので、焼結中も銅粒子内に存在した状態が保たれる。その結果、本発明の扁平銅粒子は、粒子の状態でも、及びペーストに調製された状態でも、耐熱収縮性の高いものとなる。この観点から、粒子の内部に存在するSiの量は、粒子の重量に対して20〜300ppm、特に80〜250ppmであることが好ましい。 The flat copper particles of the present invention preferably contain Si in the inside of the particles in addition to the presence of Si in the outermost surface portion of the particles. Since the Si present inside the particles is not attracted to the glass frit contained in the paste during sintering of the conductive paste, the state of being present in the copper particles is maintained even during the sintering. As a result, the flat copper particles of the present invention have high heat shrinkage resistance both in the particle state and in the state prepared in a paste. From this viewpoint, the amount of Si present inside the particles is preferably 20 to 300 ppm, particularly preferably 80 to 250 ppm, based on the weight of the particles.
粒子の内部に存在するSiの量は、次の方法で測定することができる。まず、先に述べた方法で、銅粒子の粒子最表面部分に存在しているSiを除去してその量を測定する。次に、粒子最表面部分に存在するSiが除去された後の銅粒子を、酸によってすべて溶解させる。この溶液について、例えばICPを用いて元素分析を行い、Siの量を測定する。このSiの量を、粒子の内部に存在するSiの量とする。   The amount of Si present inside the particles can be measured by the following method. First, Si existing on the outermost surface portion of the copper particles is removed by the method described above and the amount thereof is measured. Next, all the copper particles from which Si present on the outermost surface portion of the particles has been removed are dissolved by an acid. This solution is subjected to elemental analysis using, for example, ICP to measure the amount of Si. This amount of Si is defined as the amount of Si present inside the particles.
本発明の扁平銅粒子は、Si以外の元素(ただし、酸素及び水素を除く)を含んでいないことが好ましい。例えばリンを含んでいないことが好ましい。先に述べたとおり、リンは、銅の結晶子径の向上に寄与するものの、耐熱収縮性にはマイナスに作用する傾向があるからである。   The flat copper particles of the present invention preferably do not contain any element other than Si (excluding oxygen and hydrogen). For example, it is preferable that phosphorus is not included. As described above, phosphorus contributes to an improvement in the crystallite diameter of copper, but tends to negatively affect the heat shrinkage resistance.
耐酸化性を向上させる観点から、本発明の扁平銅粒子は、その表面が有機化合物によって処理されていてもよい。例えば、飽和脂肪酸、不飽和脂肪酸、窒素含有有機化合物、硫黄含有有機化合物又はシランカップリング剤等で扁平銅粒子の表面を処理することで、該粒子の耐酸化性が一層向上する。これら各種の有機化合物の詳細については、例えば本出願人の先の出願に係る特開2005−314755号公報に記載されている。   From the viewpoint of improving oxidation resistance, the surface of the flat copper particles of the present invention may be treated with an organic compound. For example, by treating the surface of the flat copper particles with a saturated fatty acid, an unsaturated fatty acid, a nitrogen-containing organic compound, a sulfur-containing organic compound, or a silane coupling agent, the oxidation resistance of the particles is further improved. Details of these various organic compounds are described in, for example, Japanese Patent Application Laid-Open No. 2005-314755 related to the earlier application of the present applicant.
次に、本発明の扁平銅粒子の好適な製造方法について説明する。本製造方法では、水溶性銅化合物を含む水溶液に還元剤を添加して銅の還元を行うという化学的方法で扁平銅粒子を得る。先に述べた特許文献1に記載されているような機械的な方法は、本製造方法では採用していない。本製造方法では、銅の還元の前又は還元中に、水溶性ケイ素化合物を反応系に添加することを特徴としている。銅の還元は1段階で行ってもよく、あるいは2段階又はそれ以上で行ってもよい。以下の説明は、2段階の還元によって、目的とする銅粒子を得る方法についてのものである。   Next, the suitable manufacturing method of the flat copper particle of this invention is demonstrated. In this production method, flat copper particles are obtained by a chemical method in which a reducing agent is added to an aqueous solution containing a water-soluble copper compound to reduce copper. The mechanical method described in Patent Document 1 described above is not adopted in this manufacturing method. This production method is characterized in that a water-soluble silicon compound is added to the reaction system before or during the reduction of copper. Copper reduction may be performed in one stage, or may be performed in two stages or more. The following description relates to a method for obtaining target copper particles by two-stage reduction.
本製造方法においては、まず水溶性銅化合物を含む水溶液(以下「銅含有水溶液」とも言う。)を調製する。水溶性銅化合物としては、例えば硫酸銅、硝酸銅、酢酸銅又はこれらの水和物等を用いることができる。これらの銅化合物のうち、硫酸銅五水和物及び硝酸銅は、水溶性が高く、水溶液中での銅濃度を高くすることができ、また粒度の均一性の高い扁平銅粒子が得られやすいので好適に用いられる。   In this production method, first, an aqueous solution containing a water-soluble copper compound (hereinafter also referred to as “copper-containing aqueous solution”) is prepared. As the water-soluble copper compound, for example, copper sulfate, copper nitrate, copper acetate, or a hydrate thereof can be used. Among these copper compounds, copper sulfate pentahydrate and copper nitrate are highly water-soluble, can increase the copper concentration in the aqueous solution, and can easily obtain flat copper particles with high particle size uniformity. Therefore, it is preferably used.
銅含有水溶液は、水100重量部に対して銅化合物を好ましくは10重量部〜50重量部、更に好ましくは20重量部〜40重量部含む。この範囲の割合で銅化合物が含まれていることで、粒径の均一性の高い扁平銅粒子が得られやすくなる。銅含有液は例えば、水を攪拌した状態にしておき、これに銅化合物を添加して攪拌することで得られる。銅含有水溶液の調製の際の液温は、均一な粒径の扁平銅粒子を得る観点から、好ましくは35℃〜90℃、更に好ましくは45℃〜80℃である。   The copper-containing aqueous solution preferably contains 10 to 50 parts by weight, more preferably 20 to 40 parts by weight of the copper compound with respect to 100 parts by weight of water. By containing the copper compound in a proportion within this range, it becomes easy to obtain flat copper particles having a highly uniform particle size. The copper-containing liquid can be obtained, for example, by stirring water after adding a copper compound thereto. The liquid temperature during the preparation of the copper-containing aqueous solution is preferably 35 ° C. to 90 ° C., more preferably 45 ° C. to 80 ° C., from the viewpoint of obtaining flat copper particles having a uniform particle size.
このようにして得られた銅含有水溶液に塩基性化合物を添加して酸化第二銅(CuO)を生成させる。このために用いられる塩基性化合物としては、例えば水酸化ナトリウムや水酸化カリウム等のアルカリ金属の水酸化物及びアンモニアが挙げられる。生成した酸化第二銅は微小な固体状粒子の状態で液中に懸濁している。   A basic compound is added to the copper-containing aqueous solution thus obtained to produce cupric oxide (CuO). Examples of the basic compound used for this purpose include alkali metal hydroxides such as sodium hydroxide and potassium hydroxide, and ammonia. The produced cupric oxide is suspended in the liquid in the form of fine solid particles.
銅含有水溶液への塩基性化合物の添加方法としては例えば、銅含有水溶液を攪拌した状態にしておき、これに塩基性化合物の水溶液を添加して攪拌する方法が挙げられる。このときの混合液の液温は好ましくは35℃〜90℃、更に好ましくは45℃〜80℃とすることができる。液温がこの範囲内にあると、一次粒子の凝集が少ない粒径の均一性の高い扁平銅粒子が得られやすいので好ましい。   Examples of the method for adding the basic compound to the copper-containing aqueous solution include a method in which the copper-containing aqueous solution is kept in a stirred state, and an aqueous solution of the basic compound is added thereto and stirred. The liquid temperature of the mixed liquid at this time is preferably 35 ° C to 90 ° C, more preferably 45 ° C to 80 ° C. When the liquid temperature is within this range, it is preferable because flat copper particles having a high particle size with little primary particle aggregation are easily obtained.
塩基性化合物の銅含有水溶液への添加量は、銅化合物1モルに対する塩基性化合物の量が、好ましくは1.05モル〜3モル、更に好ましくは1.1モル〜2モルとなるような量とする。塩基性化合物の添加量をこの範囲内にすることで、粒径の均一性の高い扁平銅粒子が得られやすいので好ましい。   The amount of the basic compound added to the copper-containing aqueous solution is such that the amount of the basic compound with respect to 1 mol of the copper compound is preferably 1.05 mol to 3 mol, more preferably 1.1 mol to 2 mol. And By making the addition amount of the basic compound within this range, it is preferable because flat copper particles having a high uniformity in particle diameter can be easily obtained.
銅含有水溶液への塩基性化合物の添加によって酸化第二銅が生成した後も液の攪拌を継続させて熟成を行うことが好ましい。熟成は10分〜60分、特に20分〜40分行うことが好ましい。熟成によって酸化第二銅が十分に生成し、それによって粒径の均一性の高い扁平銅粒子が得られやすいので好ましい。   After cupric oxide is formed by adding a basic compound to the copper-containing aqueous solution, it is preferable to continue aging by continuing the stirring of the solution. The aging is preferably performed for 10 minutes to 60 minutes, particularly 20 minutes to 40 minutes. It is preferable because cupric oxide is sufficiently produced by aging, and flat copper particles having high uniformity in particle size are thereby easily obtained.
このようにして酸化第二銅が生成したら、次に第1の還元工程を行う。本還元工程においては、液を攪拌しながら還元剤を添加することで、液中に含まれている酸化第二銅を酸化第一銅(Cu2O)に還元する。したがって、本還元工程において用いられる還元剤は、酸化第二銅を酸化第一銅に還元する作用を有するものである。この還元剤としては、例えばヒドラジン系還元剤や水素化ホウ素ナトリウム等を用いることができる。還元剤は、単独で又は2種以上を組み合わせて用いることができる。ヒドラジン系還元剤としては、抱水ヒドラジン、硫酸ヒドラジン、無水ヒドラジン等を用いることができる。 When cupric oxide is produced in this way, the first reduction step is performed next. In this reduction step, cupric oxide contained in the liquid is reduced to cuprous oxide (Cu 2 O) by adding a reducing agent while stirring the liquid. Therefore, the reducing agent used in this reduction step has an action of reducing cupric oxide to cuprous oxide. As this reducing agent, for example, a hydrazine-based reducing agent or sodium borohydride can be used. A reducing agent can be used individually or in combination of 2 or more types. As the hydrazine reducing agent, hydrazine hydrate, hydrazine sulfate, anhydrous hydrazine and the like can be used.
本還元工程においては、液中に含まれる銅1モルに対して還元剤を好ましくは0.1モル〜3モル、更に好ましくは0.3モル〜1.5モル添加する。還元剤の添加量がこの範囲内であると、酸化第二銅の酸化第一銅への還元反応が十分に行われるので好ましい。また、分散状態が良好な酸化第一銅が得られるので、その後の形状制御に有利になるので好ましい。   In this reduction step, the reducing agent is preferably added in an amount of 0.1 mol to 3 mol, more preferably 0.3 mol to 1.5 mol, per 1 mol of copper contained in the liquid. It is preferable that the amount of the reducing agent added is within this range because the reduction reaction of cupric oxide to cuprous oxide is sufficiently performed. Moreover, since cuprous oxide with a favorable dispersion state is obtained, it is preferable because it is advantageous for subsequent shape control.
本還元工程によって酸化第二銅が酸化第一銅へ還元した後も、液の攪拌を継続させて熟成を行うことが好ましい。熟成は10分〜60分、特に20分〜40分行うことが好ましい。熟成によって酸化第一銅が十分に生成し、反応中間体が減るので、その後の反応制御が有利になるため好ましい。   Even after cupric oxide is reduced to cuprous oxide by this reduction step, it is preferable to continue aging by continuing the stirring of the liquid. The aging is preferably performed for 10 minutes to 60 minutes, particularly 20 minutes to 40 minutes. Since cuprous oxide is sufficiently produced by aging and reaction intermediates are reduced, the subsequent reaction control is advantageous, which is preferable.
第1の還元工程が完了したら、引き続き第2の還元工程を行う。本還元工程においては、液を攪拌しながら還元剤を添加することで、液中に含まれている酸化第一銅を銅に還元する。したがって、本還元工程において用いられる還元剤は、酸化第一銅を銅に還元する作用を有するものである。この還元剤としては、例えばヒドラジン系還元剤や水素化ホウ素ナトリウムを用いることができる。ヒドラジン系還元剤としては、先に述べたものと同様のものを用いることができる。   When the first reduction process is completed, the second reduction process is continued. In this reduction process, cuprous oxide contained in the liquid is reduced to copper by adding a reducing agent while stirring the liquid. Therefore, the reducing agent used in this reduction step has an action of reducing cuprous oxide to copper. As this reducing agent, for example, a hydrazine-based reducing agent or sodium borohydride can be used. As the hydrazine-based reducing agent, the same ones as described above can be used.
第2の還元工程においては、液中に含まれる銅1モルに対して還元剤を好ましくは1.2モル〜4モル、更に好ましくは2モル〜3モル添加する。還元剤の使用量をこの範囲内に設定することで、目的とする扁平銅粒子を首尾良く得ることができる。   In the second reduction step, the reducing agent is preferably added in an amount of 1.2 mol to 4 mol, more preferably 2 mol to 3 mol, with respect to 1 mol of copper contained in the liquid. By setting the amount of the reducing agent used within this range, the intended flat copper particles can be successfully obtained.
第2の還元工程においては、前記の還元剤の添加と同時、又は添加の前後に水溶性ケイ素化合物を液中に添加する。なお、「還元剤の添加の前」とは、第2の還元工程における還元剤の添加の前だけではなく、酸化第一銅の生成後であって、かつ第1の還元工程における還元剤の添加の前又は添加と同時も包含する。したがって水溶性ケイ素化合物は、酸化第一銅を第2の還元工程において銅に還元するときに少なくとも存在していればよい。つまり、第2の還元工程において酸化第一銅を銅に還元するときには、水溶性ケイ素化合物の存在下に当該還元を行う。水溶性ケイ素化合物は、扁平な形状の銅粒子を得るために用いられる。詳細には、水溶性ケイ素化合物は液中でイオン化してケイ酸イオンとなり、該ケイ酸イオンが、酸化第一銅の銅への還元時に生成した銅の核粒子における(111)結晶面に特異吸着し、該結晶面における銅の析出・成長を抑制することが本発明者の検討の結果判明した。この析出・成長の抑制に起因して銅の析出・成長は一つの面方向に沿って優先的に進行する。その結果、得られる銅粒子は扁平の形状になる。また、水溶性ケイ素化合物の添加によって、目的とする扁平銅粒子の表面にSiを存在させることができる。   In the second reduction step, the water-soluble silicon compound is added to the liquid simultaneously with or before the addition of the reducing agent. “Before the addition of the reducing agent” means not only before the addition of the reducing agent in the second reduction step, but also after the formation of cuprous oxide and the reduction agent in the first reduction step. Includes before or simultaneously with addition. Accordingly, the water-soluble silicon compound only needs to be present at least when cuprous oxide is reduced to copper in the second reduction step. That is, when reducing cuprous oxide to copper in the second reduction step, the reduction is performed in the presence of a water-soluble silicon compound. The water-soluble silicon compound is used to obtain flat copper particles. Specifically, the water-soluble silicon compound is ionized in the liquid to form a silicate ion, and the silicate ion is specific to the (111) crystal plane in the copper core particles generated during the reduction of cuprous oxide to copper. As a result of the inventor's investigation, it has been found that it adsorbs and suppresses the precipitation and growth of copper on the crystal plane. Due to the suppression of the precipitation / growth, the precipitation / growth of copper proceeds preferentially along one plane direction. As a result, the obtained copper particles have a flat shape. Moreover, Si can be made to exist on the surface of the target flat copper particle by addition of a water-soluble silicon compound.
前記の水溶性ケイ素化合物としては、例えばケイ酸ナトリウム、ケイ酸カリウム、ケイ酸マグネシウム、メタケイ酸ナトリウム等のケイ酸塩等が挙げられる。これらのケイ酸塩は、銅の析出・成長の抑制効果が高い点から好ましく用いられる。   Examples of the water-soluble silicon compound include silicates such as sodium silicate, potassium silicate, magnesium silicate, and sodium metasilicate. These silicates are preferably used because they have a high effect of suppressing the precipitation and growth of copper.
水溶性ケイ素化合物の添加量は、Si原子に換算して、液中に含まれる銅1モルに対して1.2×10-4モル〜3.0×10-2モル、特に3.0×10-4モル〜1.5×10-2モルとすることが、銅の(111)結晶面に水溶性ケイ素化合物を必要十分な量だけ特異吸着させることができ、首尾良く扁平銅粒子を得ることができる点、及び該粒子の表面に所望の量のSiを存在させることができる点から好ましい。水溶性ケイ素化合物の添加量が過度に多いと、銅の核粒子の全域に水溶性ケイ素化合物が存在してしまい、特異吸着が起こりにくくなる。 The amount of the water-soluble silicon compound added is 1.2 × 10 −4 mol to 3.0 × 10 −2 mol, particularly 3.0 ×, in terms of Si atoms, with respect to 1 mol of copper contained in the liquid. 10 −4 mol to 1.5 × 10 −2 mol can specifically adsorb a water-soluble silicon compound in a necessary and sufficient amount on the (111) crystal plane of copper, and successfully obtain flat copper particles. This is preferable because it can be present and a desired amount of Si can be present on the surface of the particle. If the amount of the water-soluble silicon compound added is excessively large, the water-soluble silicon compound will be present in the entire area of the copper core particles, making it difficult for specific adsorption to occur.
水溶性ケイ素化合物の存在下における銅の析出・成長においては、液のpHを8〜14、特に8.5〜10に維持することが好ましい。液のpHをこの範囲内に維持することで、液のゲル化を効果的に防止でき、水溶性ケイ素化合物を特定の結晶面に効率的に吸着させることができる。液のpHの調整のためには、例えば適量の希硫酸、希硝酸、希酢酸等を液に添加すればよい。   In the deposition and growth of copper in the presence of a water-soluble silicon compound, it is preferable to maintain the pH of the solution at 8 to 14, particularly 8.5 to 10. By maintaining the pH of the liquid within this range, gelation of the liquid can be effectively prevented, and the water-soluble silicon compound can be efficiently adsorbed on a specific crystal plane. In order to adjust the pH of the liquid, for example, an appropriate amount of dilute sulfuric acid, dilute nitric acid, dilute acetic acid or the like may be added to the liquid.
本発明者らの検討結果、上述の製造方法を採用することで、水溶性ケイ素化合物に由来するSiは、目的とする扁平銅粒子の表面に存在し、かつ粒子の内部にも取り込まれることが判明した。これによって、本発明の扁平銅粒子は、粒子最表面部分のみならず、内部にもSiを含むものとなる。   As a result of the study by the present inventors, by employing the above-described production method, Si derived from the water-soluble silicon compound is present on the surface of the target flat copper particles and can be taken into the particles. found. As a result, the flat copper particles of the present invention contain Si not only in the outermost surface part of the particles but also in the inside.
本還元工程によって酸化第一銅が銅へ還元した後も、液の攪拌を継続させて熟成を行うことが好ましい。熟成は20分〜120分、特に40分〜90分行うことが好ましい。熟成によって還元が十分に進行し、扁平粒子が十分に成長するため好ましい。   Even after cuprous oxide is reduced to copper by this reduction step, it is preferable to continue aging by agitating the liquid. Aging is preferably performed for 20 minutes to 120 minutes, particularly 40 minutes to 90 minutes. Reduction is sufficiently progressed by aging, and flat particles grow sufficiently, which is preferable.
生成した扁平銅粒子は、ヌッチェ等を用いた濾過によって液から分離される。次いで純水での洗浄を1回又は複数回行う。その後、必要に応じ、脂肪酸等の有機化合物を含むメタノール溶液等で洗浄することで表面処理を行う。   The produced flat copper particles are separated from the liquid by filtration using Nutsche or the like. Next, cleaning with pure water is performed once or a plurality of times. Then, if necessary, surface treatment is performed by washing with a methanol solution containing an organic compound such as a fatty acid.
以上の方法においては、(a)第2の還元工程における還元剤の添加と同時又はその後に、(b)第1の還元工程における還元剤の添加の前若しくは添加と同時に、又は(c)第1の還元工程の後であって、かつ第2の還元工程における還元剤の添加の前に、水溶性ケイ素化合物を添加したが、これに代えて、塩基性化合物を添加して第二酸化銅を生成させるのと同時に水溶性ケイ素化合物を添加することもできる。また、これらの添加時期のうちの2つ以上の時期に水溶性ケイ素化合物を添加してもよい。   In the above method, (a) at the same time as or after the addition of the reducing agent in the second reduction step, (b) before or at the same time as the addition of the reducing agent in the first reduction step, or (c) the first The water-soluble silicon compound was added after the reduction step 1 and before the addition of the reducing agent in the second reduction step, but instead, a basic compound was added to add the copper dioxide. A water-soluble silicon compound can be added simultaneously with the formation. Further, the water-soluble silicon compound may be added at two or more of these addition times.
また、前記の方法は、2段階の還元によって銅粒子を得る方法であったが、これに代えて、1段階の還元によってCu2+イオンから直接銅粒子を得てもよい。 Moreover, although the said method was a method of obtaining a copper particle by a two-step reduction, it may replace with this and may obtain a copper particle directly from Cu <2+> ion by a one-step reduction.
また、前記の方法によれば、先に述べたとおり、還元によって生成した銅の核粒子の表面に水溶性ケイ素化合物が特異吸着しているので、該核粒子どうしの凝集が、該水溶性ケイ素化合物によって妨げられている。その結果、従来、銅粒子の湿式還元法による製造において用いられてきた有機化合物からなる分散剤を使用しなくても、分散性の高い銅粒子を得ることができるという利点が、本製造方法にはある。有機化合物からなる分散剤の不存在下に湿式還元を行うことで、得られる銅粒子中に炭素分が含有されなくなるという利点がある。炭素分は、導電性ペーストの焼結時に、クラックや剥離等の不都合が生じる原因となる場合がある。   Further, according to the above method, as described above, since the water-soluble silicon compound is specifically adsorbed on the surface of the copper core particles produced by reduction, the aggregation of the core particles is caused by the water-soluble silicon compound. Blocked by compounds. As a result, the present manufacturing method has an advantage that copper particles having high dispersibility can be obtained without using a dispersant composed of an organic compound that has been conventionally used in the production of copper particles by a wet reduction method. There is. By performing wet reduction in the absence of a dispersant composed of an organic compound, there is an advantage that no carbon content is contained in the obtained copper particles. The carbon content may cause inconveniences such as cracks and peeling during sintering of the conductive paste.
以上の方法によって目的とする扁平銅粒子が得られる。このようにして得られた扁平銅粒子は例えば導電性ペーストの原料として好適に用いられる。この導電性ペーストは、本発明の扁平銅粒子を含む金属粒子と、有機ビヒクルと、ガラスフリットとを含有するものである。この有機ビヒクルは、樹脂成分と溶剤とを含む。樹脂成分としては、例えば、アクリル樹脂、エポキシ樹脂、エチルセルロース、カルボキシエチルセルロース等が挙げられる。溶剤としては、ターピネオール及びジヒドロターピネオール等のテルペン系溶剤や、エチルカルビトール及びブチルカルビトール等のエーテル系溶剤が挙げられる。ガラスフリットとしては、ホウケイ酸ガラス、ホウケイ酸バリウムガラス、ホウケイ酸亜鉛ガラス等が挙げられる。導電性ペーストにおける金属粉の割合は36〜97.5重量%とすることが好ましい。ガラスフリットの割合は1.5〜14重量%とすることが好ましい。有機ビヒクルの割合は1〜50重量%とすることが好ましい。この導電性ペーストにおける金属粒子としては、本発明の扁平銅粒子のみを用いてもよく、あるいは該扁平銅粒子と球形等の他の形状の銅粒子とを組み合わせて用いてもよい。本発明の扁平銅粒子と球他の形状の銅粒子とを組み合わせて用いることで、ペーストの粘度調整を精密に行うことが容易になる。   The target flat copper particles are obtained by the above method. The flat copper particles thus obtained are suitably used as a raw material for conductive paste, for example. This conductive paste contains metal particles including the flat copper particles of the present invention, an organic vehicle, and glass frit. This organic vehicle includes a resin component and a solvent. Examples of the resin component include acrylic resin, epoxy resin, ethyl cellulose, carboxyethyl cellulose, and the like. Examples of the solvent include terpene solvents such as terpineol and dihydroterpineol, and ether solvents such as ethyl carbitol and butyl carbitol. Examples of the glass frit include borosilicate glass, borosilicate barium glass, and borosilicate zinc glass. The proportion of the metal powder in the conductive paste is preferably 36 to 97.5% by weight. The glass frit ratio is preferably 1.5 to 14% by weight. The proportion of the organic vehicle is preferably 1 to 50% by weight. As the metal particles in the conductive paste, only the flat copper particles of the present invention may be used, or the flat copper particles and copper particles having other shapes such as a spherical shape may be used in combination. By using the flat copper particles of the present invention in combination with spheres or other shapes of copper particles, it becomes easy to precisely adjust the viscosity of the paste.
このようにして得られた導電性ペーストは、例えば、プリント配線板の回路形成、セラミックコンデンサの外部電極等の電気的導通確保、EMI対策のために好適に使用される。   The conductive paste thus obtained is preferably used for, for example, circuit formation of a printed wiring board, ensuring electrical continuity of an external electrode of a ceramic capacitor, and measures against EMI.
以下、実施例により本発明を更に詳細に説明する。しかしながら本発明の範囲は、かかる実施例に制限されない。   Hereinafter, the present invention will be described in more detail with reference to examples. However, the scope of the present invention is not limited to such examples.
〔実施例1〕
50℃の純水2Lに、硫酸銅3モルを添加して攪拌を行い、銅含有水溶液を得た。次に、この水溶液を攪拌した状態で、該水溶液にアンモニア水(アンモニアに換算して、銅1モルに対して1.77モル)を添加して液中に酸化第二銅を生成させた。引き続き30分攪拌した後、ヒドラジンを、銅1モルに対して0.53モル添加した。またアンモニア水(アンモニアに換算して、銅1モルに対して0.81モル)を添加した。これによって第1の還元反応を行い、酸化第二銅を酸化第一銅に還元させた。引き続き30分攪拌した後、液を攪拌した状態でヒドラジンを、銅1モルに対して2.29モル一括添加した。この一括添加と同時に、ケイ酸ナトリウムを、銅1モルに対して0.008モル一括添加して第2の還元反応を行い、酸化第一銅を銅に還元させた。引き続き1時間攪拌を行って反応を終了させた。反応終了後、得られたスラリーを、ヌッチェを用いて濾過し、次いで純水及びメタノールで洗浄し、更に乾燥して目的とする扁平銅粒子を得た。この銅粒子のSEM像を図1に示す。同図から明らかなように、得られた銅粒子は板状をしていることが確認された。
[Example 1]
3 mol of copper sulfate was added to 2 L of pure water at 50 ° C. and stirred to obtain a copper-containing aqueous solution. Next, with this aqueous solution being stirred, aqueous ammonia (1.77 mol per 1 mol of copper in terms of ammonia) was added to the aqueous solution to produce cupric oxide in the solution. Subsequently, after stirring for 30 minutes, 0.53 mol of hydrazine was added to 1 mol of copper. Aqueous ammonia (0.81 mol per mol of copper in terms of ammonia) was added. Thus, a first reduction reaction was performed to reduce cupric oxide to cuprous oxide. Subsequently, after stirring for 30 minutes, 2.29 mol of hydrazine was added all at once to 1 mol of copper while the solution was stirred. Simultaneously with this batch addition, 0.008 mol of sodium silicate was added all at once with respect to 1 mol of copper, and a second reduction reaction was performed to reduce cuprous oxide to copper. Subsequently, stirring was performed for 1 hour to complete the reaction. After completion of the reaction, the resulting slurry was filtered using a Nutsche, then washed with pure water and methanol, and further dried to obtain the desired flat copper particles. The SEM image of this copper particle is shown in FIG. As is clear from the figure, it was confirmed that the obtained copper particles were plate-shaped.
〔実施例2ないし7及び比較例1〕
以下の表1に示す条件で製造を行う以外は実施例1と同様にして銅粒子を得た。得られた銅粒子のSEM像を、図2(実施例2)、図3(実施例3)、図4(実施例4)、図5(実施例5)、図6(実施例6)、図7(実施例7)、図8(比較例1)に示す。これらの図から明らかなように、各実施例で得られた銅粒子は板状をしていることが確認された。比較例1で得られた銅粒子は球状のものであった。
[Examples 2 to 7 and Comparative Example 1]
Copper particles were obtained in the same manner as in Example 1 except that the production was performed under the conditions shown in Table 1 below. SEM images of the obtained copper particles are shown in Fig. 2 (Example 2), Fig. 3 (Example 3), Fig. 4 (Example 4), Fig. 5 (Example 5), Fig. 6 (Example 6), This is shown in FIG. 7 (Example 7) and FIG. 8 (Comparative Example 1). As is clear from these figures, it was confirmed that the copper particles obtained in each example had a plate shape. The copper particles obtained in Comparative Example 1 were spherical.
〔比較例2〕
本比較例では、機械的な処理によって扁平銅粒子を製造した。すなわち、比較例で得られた球状銅粒子を用い、これを遊星ボールミルで25分間粉砕して扁平銅粒子を得た。メディアとして、直径0.05mmのジルコニアビーズを用いた。溶媒にメタノールを用いて25分間粉砕を行った。得られた銅粒子のSEM像を図9に示す。
[Comparative Example 2]
In this comparative example, flat copper particles were produced by mechanical treatment. That is, the spherical copper particles obtained in the comparative example were used and pulverized with a planetary ball mill for 25 minutes to obtain flat copper particles. As media, zirconia beads having a diameter of 0.05 mm were used. Milling was performed for 25 minutes using methanol as a solvent. An SEM image of the obtained copper particles is shown in FIG.
〔評価〕
実施例及び比較例で得られた銅粒子について、粒子最表面部分に存在するSiの量及び、粒子内部に含まれるSiの量、平均粒径、厚み、アスペクト比、A値及び焼結開始温度を、上述の方法で測定した。また、体積抵抗値を以下の方法で測定した。なお、粒子表面に存在するSiの量及び、粒子内部に含まれるSiの量はいずれもICPを用いて測定した。これらの結果を以下の表2に示す。
[Evaluation]
For the copper particles obtained in the examples and comparative examples, the amount of Si present in the outermost surface portion of the particles, the amount of Si contained in the particles, average particle diameter, thickness, aspect ratio, A value, and sintering start temperature Was measured by the method described above. Moreover, the volume resistance value was measured by the following method. The amount of Si present on the particle surface and the amount of Si contained inside the particle were both measured using ICP. These results are shown in Table 2 below.
〔体積抵抗値〕
圧粉抵抗測定システム(三菱化学PD−41)と抵抗率測定器(三菱化学MCP−T600)を用いて圧粉抵抗値を測定した。試料15gをプローブシリンダへ投入し、プローブユニットをPD−41へセットした。油圧ジャッキによって1000f/kgの圧力を印加したときの抵抗値を、MCP−T600を用いて測定した。測定した抵抗値と試料厚みから、体積抵抗値を算出した。
(Volume resistance value)
The dust resistance value was measured using a dust resistance measurement system (Mitsubishi Chemical PD-41) and a resistivity meter (Mitsubishi Chemical MCP-T600). A sample 15g was put into the probe cylinder, and the probe unit was set in PD-41. The resistance value when a pressure of 1000 f / kg was applied by a hydraulic jack was measured using MCP-T600. The volume resistance value was calculated from the measured resistance value and sample thickness.
表2及び図1〜図7に示す結果から明らかなように、各実施例で得られた銅粒子は板状の微粒のものであることが判る。また表2に示す結果から明らかなように、焼結開始温度が高く、耐熱収縮性が高いものであることが判る。これに対して、還元時に水溶性ケイ素化合物を用いなかった比較例1の銅粒子は扁平なものとならなかった。また、従来の機械的な方法で扁平化を行って得られた比較例2の銅粒子は、実施例の銅粒子に比べて焼結開始温度が低く、耐熱収縮性が低いものであることが判る。なお、表には示していないが、各実施例で得られた銅粒子に含まれているSiの価数は四価であった。   As is apparent from the results shown in Table 2 and FIGS. 1 to 7, it can be seen that the copper particles obtained in each Example are of a plate-like fine particle. Further, as apparent from the results shown in Table 2, it can be seen that the sintering start temperature is high and the heat shrinkage resistance is high. On the other hand, the copper particles of Comparative Example 1 that did not use the water-soluble silicon compound during the reduction did not become flat. Further, the copper particles of Comparative Example 2 obtained by flattening by a conventional mechanical method have a lower sintering start temperature and lower heat shrinkage resistance than the copper particles of Examples. I understand. Although not shown in the table, the valence of Si contained in the copper particles obtained in each example was tetravalent.
〔比較例3〕
特許文献3の実施例1に記載の方法に従い粒状の銅粒子(D50=4.0μm)を製造した。Siの含有量は5000ppmであった。この銅粒子について、熱機械分析を行い熱収縮の程度を測定した。測定は、銅粒子をアルカリ煮沸する前後において行った。アルカリ煮沸は、銅粒子の表面に存在するSi分を除去する目的で行った。アルカリ煮沸は、アルカリとして水酸化ナトリウム水溶液を用い、70℃以上で60分間行った。その結果を、図10(a)及び(b)に示す。同図には、同様にして測定された実施例2、4及び7で得られた扁平銅粒子の結果も併せて示されている。同図に示す結果から明らかなとおり、各実施例の扁平銅粒子に比べ、比較例3の銅粒子は、粒子表面のSi分の除去によって、熱収縮の程度が極端に大きくなることが判る。
[Comparative Example 3]
According to the method described in Example 1 of Patent Document 3, granular copper particles (D 50 = 4.0 μm) were produced. The Si content was 5000 ppm. The copper particles were subjected to thermomechanical analysis to measure the degree of thermal shrinkage. The measurement was performed before and after the copper particles were boiled with alkali. The alkali boiling was performed for the purpose of removing Si content existing on the surface of the copper particles. The alkali boiling was performed at 70 ° C. or more for 60 minutes using an aqueous sodium hydroxide solution as an alkali. The results are shown in FIGS. 10 (a) and 10 (b). The figure also shows the results of the flat copper particles obtained in Examples 2, 4 and 7 measured in the same manner. As is clear from the results shown in the figure, it can be seen that the degree of thermal shrinkage of the copper particles of Comparative Example 3 is extremely increased by removing the Si content on the particle surface as compared with the flat copper particles of each Example.

Claims (6)

  1. 1mol/Lの水酸化ナトリウム水溶液を用い、70℃以上で60分間煮沸して溶出する、粒子最表面部分に存在するSiが粒子全体に対して重量基準で100〜2000ppmであり、かつ該Siの少なくとも一部が四価の状態で存在している扁平銅粒子であって、
    1mol/Lの水酸化ナトリウム水溶液を用い、70℃以上で60分間煮沸した後の前記銅粒子を酸によってすべて溶解させ、得られた溶液について元素分析を行い測定されたSiの量が、粒子全体に対して重量基準で20〜300ppmであり、
    粒径(μm)と厚み(μm)との積で表されるA値が0.0125以上0.05未満であり、焼結開始温度が400〜500℃であるか、
    粒径(μm)と厚み(μm)との積で表されるA値が0.05以上0.3未満であり、焼結開始温度が600〜800℃であるか、又は
    粒径(μm)と厚み(μm)との積で表されるA値が0.3以上8以下であり、焼結開始温度が700〜800℃である扁平銅粒子。
    Using a 1 mol / L sodium hydroxide aqueous solution, boiling and eluting at 70 ° C. or more for 60 minutes, the Si present on the outermost surface of the particle is 100 to 2000 ppm on a weight basis with respect to the entire particle, and the Si Flat copper particles at least partially present in a tetravalent state,
    Using a 1 mol / L sodium hydroxide aqueous solution, all the copper particles after boiling for 60 minutes at 70 ° C. or more were dissolved with an acid, and the amount of Si measured by performing elemental analysis on the resulting solution was determined as the whole particles. 20 to 300 ppm on a weight basis,
    A value represented by the product of the particle size (μm) and the thickness (μm) is 0.0125 or more and less than 0.05, and the sintering start temperature is 400 to 500 ° C.,
    The A value represented by the product of the particle size (μm) and the thickness (μm) is 0.05 or more and less than 0.3, and the sintering start temperature is 600 to 800 ° C. or the particle size (μm) The flat copper particle whose A value represented by the product of (A) and thickness (micrometer) is 0.3-8, and whose sintering start temperature is 700-800 degreeC.
  2. 平均粒径が0.5〜5μmであり、アスペクト比(粒径/厚み)が2〜200である請求項1記載の扁平銅粒子。   2. The flat copper particles according to claim 1, wherein the average particle diameter is 0.5 to 5 μm and the aspect ratio (particle diameter / thickness) is 2 to 200. 3.
  3. 請求項1に記載の扁平銅粒子の製造方法であって、
    水溶性銅化合物を含む水溶液に還元剤を添加して銅の還元を行う還元工程を有し、
    還元の前又は還元中に、水溶性ケイ酸塩を添加することを特徴とする扁平銅粒子の製造方法。
    It is a manufacturing method of the flat copper particles according to claim 1,
    A reduction step of reducing copper by adding a reducing agent to an aqueous solution containing a water-soluble copper compound;
    A method for producing flat copper particles, comprising adding a water-soluble silicate before or during the reduction.
  4. 水溶性銅化合物を含む水溶液に塩基性化合物を添加して酸化第二銅を生成させ、次いで
    生成した酸化第二銅を第1の還元工程において酸化第一銅に還元させ、
    酸化第一銅を第2の還元工程において水溶性ケイ酸塩の存在下に銅に還元する請求項記載の扁平銅粒子の製造方法。
    Adding a basic compound to an aqueous solution containing a water-soluble copper compound to produce cupric oxide, and then reducing the produced cupric oxide to cuprous oxide in the first reduction step;
    The method for producing flat copper particles according to claim 3 , wherein cuprous oxide is reduced to copper in the presence of water-soluble silicate in the second reduction step.
  5. 有機化合物からなる分散剤の不存在下に還元を行う請求項又は記載の扁平銅粒子の製造方法。 The method for producing flat copper particles according to claim 3 or 4 , wherein the reduction is performed in the absence of a dispersant composed of an organic compound.
  6. 請求項1又は2に記載の扁平銅粒子を含むことを特徴とする導電性ペースト。
    Conductive paste comprising a flat copper particles according to claim 1 or 2.
JP2010292693A 2010-12-28 2010-12-28 Flat copper particles Active JP6159505B2 (en)