JP6119936B1 - ポリエステル樹脂組成物、これを含む光反射体用部品および光反射体 - Google Patents
ポリエステル樹脂組成物、これを含む光反射体用部品および光反射体 Download PDFInfo
- Publication number
- JP6119936B1 JP6119936B1 JP2016563860A JP2016563860A JP6119936B1 JP 6119936 B1 JP6119936 B1 JP 6119936B1 JP 2016563860 A JP2016563860 A JP 2016563860A JP 2016563860 A JP2016563860 A JP 2016563860A JP 6119936 B1 JP6119936 B1 JP 6119936B1
- Authority
- JP
- Japan
- Prior art keywords
- polyester resin
- resin composition
- mass
- organic acid
- acid salt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
一方、ランプ部材としての形状や仕様によっては、製品が高温となる場合があり、高い耐熱性をも有する樹脂が要求されることも多い。
[1] 50〜100質量%のポリブチレンテレフタレート樹脂と、0〜50質量%のポリエチレンテレフタレート樹脂とを含有するポリエステル樹脂Aを含むポリエステル樹脂組成物であって、前記ポリエステル樹脂組成物は、アルカリ金属の有機酸塩およびアルカリ土類金属の有機酸塩のいずれか一方または両方である金属有機酸塩Bと、前記ポリエステル樹脂A100質量部に対し、0.05〜3質量部の多官能グリシジル基含有スチレン系ポリマーC、1〜20質量部の平均粒子径0.05〜3μmである無機フィラーDとを含み、前記ポリエステル樹脂組成物は、アルカリ金属原子およびアルカリ土類金属原子のいずれか一方または両方を、前記ポリエステル樹脂A100質量部に対し、0.000005〜0.05質量部含み、かつ、前記ポリエステル樹脂組成物は、ポリブチレンテレフタレートの線状オリゴマーの含有量、または前記ポリブチレンテレフタレートの線状オリゴマーおよびポリエチレンテレフタレートの線状オリゴマーの含有量が1000mg/kg以下である、ポリエステル樹脂組成物。
[2] 上記ポリエステル樹脂組成物は、上記アルカリ金属原子および上記アルカリ土類金属原子のいずれか一方または両方を、上記ポリエステル樹脂A100質量部に対し、0.0005〜0.05質量部含む、[1]に記載のポリエステル樹脂組成物。
[3] 上記ポリエステル樹脂組成物は、チタン原子の含有量が50mg/kg以下である、[1]または[2]に記載のポリエステル樹脂組成物。
[4] 上記金属有機酸塩Bの金属種は、リチウム、ナトリウム、カリウム、カルシウム、マグネシウムからなる群より選ばれる1種または2種以上である、[1]〜[3]のいずれかに記載のポリエステル樹脂組成物。
[5] 上記金属有機酸塩Bは、酢酸リチウム、酢酸ナトリウム、酢酸カリウム、酢酸カルシウム、酢酸マグネシウム、安息香酸リチウム、安息香酸ナトリウムおよび安息香酸カリウムからなる群より選ばれる1種または2種以上である、[1]〜[4]のいずれかに記載のポリエステル樹脂組成物。
[6] 前記無機フィラーDは、炭酸カルシウム、シリカ、カオリン、硫酸バリウムおよび二酸化チタンからなる群より選ばれる1種または2種以上である、[1]〜[5]のいずれかに記載のポリエステル樹脂組成物。
[7] [1]〜[6]のいずれかに記載のポリエステル樹脂組成物を含む、光反射体用部品。
[8] [7]に記載の光反射体用部品の表面の少なくとも一部に光反射金属層が形成されている、光反射体。
[ポリエステル樹脂組成物]
本発明は、50〜100質量%(50質量%以上100質量%以下、本明細書において数値範囲を「〜」を用いて表わす場合、その範囲は上限および下限の数値を含むものとする)のポリブチレンテレフタレート樹脂と、0〜50質量%のポリエチレンテレフタレート樹脂とを含有するポリエステル樹脂Aを含むポリエステル樹脂組成物である。ポリエステル樹脂組成物は、アルカリ金属の有機酸塩およびアルカリ土類金属の有機酸塩のいずれか一方または両方である金属有機酸塩Bと、ポリエステル樹脂A100質量部に対し、0.05〜3質量部の多官能グリシジル基含有スチレン系ポリマーC、1〜20質量部の平均粒子径0.05〜3μmである無機フィラーDとを含む。さらにポリエステル樹脂組成物は、アルカリ金属原子およびアルカリ土類金属原子のいずれか一方または両方を、ポリエステル樹脂A100質量部に対し、0.000005〜0.05質量部含む。さらに、ポリエステル樹脂組成物は、ポリブチレンテレフタレートの線状オリゴマーの含有量、またはポリブチレンテレフタレートの線状オリゴマーおよびポリエチレンテレフタレートの線状オリゴマーの含有量が1000mg/kg以下である。
本発明においてポリエステル樹脂Aは、50〜100質量%のポリブチレンテレフタレート樹脂と、0〜50質量%のポリエチレンテレフタレート樹脂とを含有する。ポリエステル樹脂Aは、ポリブチレンテレフタレート樹脂およびポリエチレンテレフタレート樹脂以外の第3の成分を含むことを除外するものではないが、この2成分で構成されることが好ましい。ポリエステル樹脂組成物中のポリエステル樹脂Aは、ポリエステル樹脂Aが主成分である限り特に限定されないが、90質量%以上であることが好ましく、92質量%以上であることがより好ましい。
ポリブチレンテレフタレート樹脂は、テレフタル酸またはそのエステル形成性誘導体を主たる成分とするジカルボン酸と、1、4−ブタンジオールまたはそのエステル形成性誘導体を主たる成分とするジオールとを重縮合反応させるなどの一般的な重合方法によって得ることができる重合体である。ポリブチレンテレフタレート樹脂は、ブチレンテレフタレートの繰返し単位が80モル%以上であることが好ましく、90モル%以上であることがより好ましく、95モル%以上であることがさらに好ましく、100モル%であることが最も好ましい。
上記式(I)において、ηr=η/η0であり、ηはポリブチレンテレフタレート樹脂溶液の落下秒数であり、η0は混合溶媒のみの落下秒数であり、Cはポリブチレンテレフタレート樹脂溶液の濃度(g/dl)である。
ポリエチレンテレフタレート樹脂は、テレフタル酸またはそのエステル形成性誘導体を主たる成分とするジカルボン酸と、エチレングリコールまたはそのエステル形成性誘導体を主たる成分とするジオールとを重縮合反応させるなどの一般的な重合方法によって得ることができる重合体である。ポリエチレンテレフタレート樹脂は、エチレンテレフタレートの繰返し単位が80モル%以上であることが好ましく、90モル%以上であることがより好ましく、95モル%以上であることがさらに好ましく、100モル%であることが特に好ましい。
本発明を構成するポリブチレンテレフタレート樹脂は、たとえば1、4−ブタンジオールと、テレフタル酸またはテレフタル酸ジアルキルとのチタン触媒を使用したエステル化反応またはエステル交換反応により得ることができる。このとき、成形時のシリンダー内での滞留による分解抑制の観点から、本発明のポリエステル樹脂組成物は、チタン原子の含有量が50mg/kg以下であることが好ましい。すなわち、本発明ではポリエステル樹脂組成物に含まれるチタン触媒の含有量を、チタン原子の含有量により規定している。チタン原子の含有量は、より好ましくは45mg/kg以下であり、さらに好ましくは40mg/kg以下であり、特に好ましくは35mg/kg以下である。チタン原子の含有量の下限は、5mg/kgであることが好ましく、より好ましくは8mg/kgであり、さらに好ましくは15mg/kgである。チタン原子の含有量が50mg/kgを超えると、金型汚れの抑制効果が発現しにくくなる。
本発明において、連続成形の際の金型汚れを抑制することができるのは、以下の理由によるものと考えられる。
本発明に係るポリエステル樹脂組成物は、アルカリ金属の有機酸塩およびアルカリ土類金属の有機酸塩のいずれか一方または両方である金属有機酸塩Bを含む。その含有量は、アルカリ金属原子およびアルカリ土類金属原子のいずれか一方または両方の含有量を基準として特定され、具体的には、アルカリ金属原子およびアルカリ土類金属原子のいずれか一方または両方を、上記ポリエステル樹脂A100質量部に対し、0.000005〜0.05質量部含むものとなる。すなわち本発明では、ポリエステル樹脂組成物に含まれる金属有機酸塩Bの含有量を、アルカリ金属原子およびアルカリ土類金属原子のいずれか一方または両方の含有量を特定することにより把握するものとしている。
金属有機酸塩Bを、ポリエステル樹脂Aを構成するポリブチレンテレフタレート樹脂の重合初期(エステル化反応後またはエステル交換反応後)、およびポリブチレンテレフタレート樹脂の重合後期(重縮合工程(減圧工程)中または重合終了後)のタイミングで添加する場合、その原料であるテレフタル酸と金属有機酸塩B中のアルカリ金属またはアルカリ土類金属とが塩を形成し、金属有機酸塩Bの作用が失われることにより、金型汚れを抑制する効果が低下する恐れがある。さらに、形成した塩が析出してブツ(seeds)となることにより、良好な外観(特に平滑性を示す鏡面外観)が得られず、この析出した塩などの異物が材料破壊の起点となって機械特性も低下する恐れがある(金属有機酸塩Bを重合終了後に添加する場合には、樹脂の粘度が高いため均一分散が困難であり、金属有機酸塩B自体がブツとなることもある)。
一方、あらかじめ作製した金属有機酸塩Bのマスターペレットをポリエステル樹脂組成物の混練時もしくは成形時に添加する場合、金属有機酸塩Bの存在下でポリエステル樹脂Aが溶融状態である時間を短くすることが可能となり、上記問題が解決されるだけでなく、ポリエステル樹脂Aの分解が低減されるため、色調の悪化(黄色味の増大)が抑制され、かつ耐フォギング性を維持することもできる。
したがって、金属有機酸塩Bは、ポリブチレンテレフタレート樹脂の重合時に添加するよりも、マスターペレットとしてポリエステル樹脂組成物の混練時もしくは成形時に添加することが好ましい。
本発明に係るポリエステル樹脂組成物は、ポリエステル樹脂A100質量部に対し、0.05〜3質量部の多官能グリシジル基含有スチレン系ポリマーCを含む。多官能グリシジル基含有スチレン系ポリマーCの含有量をこのような範囲にすることにより、後述する離型剤Eから発生する遊離有機酸などのガス成分、環状オリゴマー、線状オリゴマー、ならびにポリブチレンテレフタレートおよびポリエチレンテレフタレートのモノマーなどを効率的に捕捉することができ、低フォギング性をはじめとする優れた低ガス性を実現することができる。金型汚れの抑制にも寄与する。
本発明に係るポリエステル樹脂組成物は、ポリエステル樹脂A100質量部に対し、1〜20質量部の平均粒子径0.05〜3μmである無機フィラーDを含む。無機フィラーDをこのような範囲にすることにより、耐熱性及び剛性がより向上し、さらに収縮率を小さく制御することができる。特に収縮率が大きいと、射出成形時に金型へのだきつきによる離型不良が生じたり、成形品が大型である場合や形状が複雑な場合などには、成形品に歪みが生じたりすることがあるため、無機フィラーDにより収縮率を小さく制御することは非常に重要である。
無機フィラーDの含有量が1質量部未満の場合、耐熱性及び剛性の向上効果が小さい。20質量部を超えると、フィラーの浮き出しにより、ランプ部材として用いるために必要な表面平滑性が損なわれる。
耐熱性及び剛性の向上、表面平滑性の観点から、無機フィラーDの含有量は2質量部以上が好ましく、さらに収縮率制御の観点から、無機フィラーDの含有量は3質量部以上がより好ましい。
表面処理としては、アミノシランカップリング剤、エポキシシランカップリング剤、チタネート系カップリング剤、アルミネート系カップリング剤等の表面処理剤による処理、シリカによる処理、脂肪酸による処理、SiO2−Al2O3による処理、リン化合物などの酸性化合物による中和処理等が挙げられ、これらの処理を組み合わせても良い。フォギング性の観点から、シリカによる処理、エポキシシランカップリング剤による処理、アルキルシランカップリング剤による処理が好ましい。
(離型剤E)
本発明のポリエステル樹脂組成物は、離型性をより向上させるために、離型剤Eを含有することができる。離型剤Eは、金型汚れを抑制する観点から、脂肪酸エステル化合物であることが好ましい。この脂肪酸エステル化合物には、カルボン酸が部分的に、モノグリコールまたはポリグリコールによりエステル化されている化合物、および部分的に金属塩を形成している化合物を含むことができる。離型剤Eが脂肪酸エステル化合物であることにより、金属有機酸塩Bおよび多官能グリシジル基含有スチレン系ポリマーCの作用によって、離型剤Eに基づく遊離脂肪酸の生成が抑制される傾向にあり、金型汚れを抑制することができ、かつフォギング性を改善することができる。離型剤Eの含有量は、ポリエステル樹脂A100質量部に対し、0.05〜3質量部であることが好ましい。離型剤Eの含有量が0.05質量部未満であると十分な離型効果が得られず、離型不良または離型ジワなどが発生する恐れがある。離型剤Eはそれ自体がガス化し、またはブリードアウトすることによって、金型汚れを引き起こす。さらに、たとえばこの離型剤Eを含むポリエステル樹脂組成物を自動車用ランプに適用したとき、100℃〜200℃の範囲の温度環境下でヘッドライトのカバーまたはミラーなどに付着し、曇りを発生(フォギング)させたりする。これらの問題は、離型剤Eの含有量が3質量部を超えると顕著となる。
本発明に係るポリエステル樹脂組成物を製造する方法は、上述した各成分、および必要に応じて添加する安定剤などの添加剤を混合し、溶融混練することにより製造することができる。溶融混練の方法は、公知の方法を用いることが可能であり、たとえば、単軸押出機、二軸押出機、加圧ニーダーまたはバンバリーミキサーなどを使用して溶融混練することができる。なかでも二軸押出機を使用することが好ましい。一般的な溶融混練の条件としては、二軸押出機を使用する場合、シリンダー温度を250〜280℃とし、混練時間を2〜15分とすることができる。
本発明に係る光反射体用部品は、上記ポリエステル樹脂組成物を含む。光反射体用部品は、射出成形法、押出成形法、ブロー成形法などの公知の方法でポリエステル樹脂組成物を成形することにより得ることができ、汎用性の観点から射出成形法を用いて得ることが好ましい。光反射体用部品は、たとえば光反射金属層を備えることにより、後述する光反射体となる。
本発明に係る光反射体は、上記光反射体用部品の表面の少なくとも一部に、光反射金属層が形成されている。たとえば、光反射体は、上記光反射体用部品の表面の少なくとも一部に、光反射金属層としての金属薄膜(たとえば、アルミニウム箔)を直接形成することにより得ることができる。特に、光反射体は、上記光反射体用部品の表面の少なくとも一部に、金属薄膜を蒸着することにより得ることが好ましい。蒸着方法は特に制限されず、公知の方法を用いることができる。
ポリエチレンテレフタレート樹脂bの場合: {(iii)×1000000/2}/{(i)×192/4}=末端水酸基濃度(eq/ton)。
カラム: Shim−pack XR−ODS 2.2μm(3×100mm)
移動相: A 0.2%酢酸水、B アセトニトリル
グラジエント: 0min(10%B)、25min(100%B)、27min(100%B)、27.01min(10%B)、32min(10%B)
流速: 1.1ml/min
カラム温度: 50℃
注入量: 5μl
検出波長: UV258nm。
B: ほとんど汚れが認められない
C: ゲート部反対側の凹部付近の中心に汚れがぼんやりと認められる
D: ゲート部反対側の凹部付近の中心の汚れがはっきりとした輪郭で黒く目立つ。
射出成形機(商品名:「EC100N」、東芝機械株式会社製)を準備し、♯14000番のやすりで磨かれた鏡面を有する金型を用い、100mm×100mm×2mmのポリエステル樹脂組成物からなる平板成形品を射出成形することにより得た。この平板成形品は、金型から転写された鏡面を片面に有する。成形時のシリンダー温度は260℃で、金型温度は60℃、サイクルタイムは40秒であった。表面にフィラー浮きが起こりやすい低速の射出速度で実施した。成形品の鏡面を、フィラーの浮きによる不良(白化、表面の荒れ)がないか目視により評価した。
◎:白化、表面の荒れが全く無い。
○:白化、表面の荒れが目視の角度によりわずかに認められるが、実用上問題ない程度である。
×:白化、表面の荒れが目立つ。
射出成形機(商品名:「EC100N」、東芝機械株式会社製)を用い、シリンダー温度260℃、金型温度60℃の条件で、ISO−3167の多目的試験片を成形した。この多目的試験片に対し、ISO−75に準拠し、0.45MPaで荷重したときの熱変形温度を測定した。
射出成形機(商品名:「EC100N」、東芝機械株式会社製)を用い、シリンダー温度260℃、金型温度60℃の条件で、100mm×100mm×2mmのポリエステル樹脂組成物からなる平板成形品を射出成形することにより得た。成形後24時間経過後に成形品の流動方向と、流動方向に対して直角方向の成形品の幅をノギスでそれぞれ測定し、下記式により、成形収縮率(流動方向、直角方向の成形収縮率の平均値)を算出した。
成形収縮率: [{100−(成形品の流動方向の幅)}/100+{100−(成形品の直角方向の幅)}/100]/2
ポリエステル樹脂Aは、以下のポリブチレンテレフタレート樹脂aのいずれかからなり、または以下のポリブチレンテレフタレート樹脂aのいずれかとポリエチレンテレフタレート樹脂bとからなる。
a−1: IV=0.83dl/g、末端水酸基=95eq/ton、酸価=9eq/ton、チタン原子含有量=80mg/kg(IV=0.78dl/gの溶融重合樹脂を使用、210℃でIV=0.83dl/gに到達するまで固相重合した)。ただし、金属有機酸塩Bとして酢酸カリウム10mg/kgを上記溶融重合樹脂の溶融重合時(エステル化反応後)に添加
a−2: IV=0.83dl/g、末端水酸基=95eq/ton、酸価=9eq/ton、チタン原子含有量=30mg/kg(IV=0.78dl/gの溶融重合樹脂を使用、210℃でIV=0.83dl/gに到達するまで固相重合した)。ただし、金属有機酸塩Bとして酢酸カリウム10mg/kgを上記溶融重合樹脂の溶融重合時(エステル化反応後)に添加
a−3: IV=0.83dl/g、末端水酸基=90eq/ton、酸価=6eq/ton、チタン原子含有量=30mg/kg(IV=0.73dl/gの溶融重合樹脂を使用、210℃でIV=0.83dl/gに到達するまで固相重合した)。ただし、金属有機酸塩Bとして酢酸カリウム10mg/kgを上記溶融重合樹脂の溶融重合時(エステル化反応後)に添加
a−4: IV=0.83dl/g、末端水酸基=95eq/ton、酸価=9eq/ton、チタン原子含有量=30mg/kg(IV=0.78dl/gの溶融重合樹脂を使用、210℃でIV=0.83dl/gに到達するまで固相重合した)。ただし、金属有機酸塩Bとして酢酸カリウム20mg/kgを上記溶融重合樹脂の溶融重合時(エステル化反応後)に添加
a−5: IV=0.83dl/g、末端水酸基=95eq/ton、酸価=9eq/ton、チタン原子含有量=30mg/kg(IV=0.78dl/gの溶融重合樹脂を使用、210℃でIV=0.83dl/gに到達するまで固相重合した)。ただし、金属有機酸塩Bとして酢酸マグネシウム10mg/kgを上記溶融重合樹脂の溶融重合時(エステル化反応後)に添加
a−6: IV=0.83dl/g(溶融重合により得た樹脂)、末端水酸基=100eq/ton、酸価=10eq/ton、チタン原子含有量=80mg/kg(線状オリゴマーの含有量を低減するための特段の処理をしなかった)。ただし、金属有機酸塩Bとして酢酸カリウム10mg/kgを上記樹脂の溶融重合時(エステル化反応後)に添加
a−7: IV=0.83dl/g(溶融重合により得た樹脂)、末端水酸基=100eq/ton、酸価=10eq/ton、チタン原子含有量=30mg/kg(線状オリゴマーの含有量を低減するための特段の処理をしなかった)。ただし、金属有機酸塩Bとして酢酸カリウム10mg/kgを上記樹脂の溶融重合時(エステル化反応後)に添加
a−8: IV=0.83dl/g(溶融重合により得た樹脂)、末端水酸基=100eq/ton、酸価=10eq/ton、チタン原子含有量=80mg/kg(線状オリゴマーの含有量を低減するための特段の処理をしなかった)。ただし、金属有機酸塩Bとして酢酸カリウム90mg/kgを上記樹脂の溶融重合時(エステル化反応後)に添加
a−9: IV=0.83dl/g、末端水酸基=95eq/ton、酸価=9eq/ton、チタン原子含有量=30mg/kg(IV=0.78dl/gの溶融重合樹脂を使用、210℃でIV=0.83dl/gに到達するまで固相重合した)。ただし、金属有機酸塩B不添加
a−10: IV=0.83dl/g、末端水酸基=95eq/ton、酸価=9eq/ton、チタン原子含有量=80mg/kg(IV=0.78dl/gの溶融重合樹脂を使用、210℃でIV=0.83dl/gに到達するまで固相重合した)。ただし、溶融混練時に金属有機酸塩Bをマスターペレットにより添加
a−11: IV=0.83dl/g、末端水酸基=95eq/ton、酸価=9eq/ton、チタン原子含有量=30mg/kg(IV=0.78dl/gの溶融重合樹脂を使用、210℃でIV=0.83dl/gに到達するまで固相重合した)。ただし、溶融混練時に金属有機酸塩Bをマスターペレットにより添加
a−12: IV=0.83dl/g、末端水酸基=90eq/ton、酸価=6eq/ton、チタン原子含有量=30mg/kg(IV=0.73dl/gの溶融重合樹脂を使用、210℃でIV=0.83dl/gに到達するまで固相重合した)。ただし、溶融混練時に金属有機酸塩Bをマスターペレットにより添加
a−13: IV=0.83dl/g(溶融重合により得た樹脂)、末端水酸基=100eq/ton、酸価=10eq/ton、チタン原子含有量=80mg/kg(線状オリゴマーの含有量を低減するための特段の処理をしなかった)。ただし、溶融混練時に金属有機酸塩Bをマスターペレットにより添加
a−14: IV=0.83dl/g(溶融重合により得た樹脂)、末端水酸基=100eq/ton、酸価=10eq/ton、チタン原子含有量=30mg/kg(線状オリゴマーの含有量を低減するための特段の処理をしなかった)。ただし、溶融混練時に金属有機酸塩Bをマスターペレットにより添加。
B−1: 酢酸カリウム(和光純薬工業株式会社製)
B−2: 酢酸マグネシウム(和光純薬工業株式会社製)
B−3: 酢酸カリウム(和光純薬工業株式会社製)のマスターペレット
B−4: 酢酸マグネシウム(和光純薬工業株式会社製)のマスターペレット。
C−1: スチレン/グリシジルアクリレート共重合体[商品名:「ARUFON UG−4050」、東亜合成株式会社製(Mw:8500、エポキシ価0.67meq/g、屈折率1.55)]
C−2: スチレン/グリシジルアクリレート共重合体[商品名:「ARUFON UG−4070」、東亜合成株式会社製(Mw:9700、エポキシ価1.4meq/g、屈折率1.57)]。
下記平均粒子径は、レーザー回折法により測定した値(体積累積粒度分布の50%径)を示す。
D−1: 軽質炭酸カルシウム[商品名:「RK−92BR3F」、白石工業株式会社製(シリカ/エポキシシランカップリング剤処理、平均粒子径0.15μm)]
D−2: 軽質炭酸カルシウム[商品名:「RK−82BR1F」、白石工業株式会社製(シリカ/アルキルシランカップリング剤処理、平均粒子径0.15μm)]
D−3: 軽質炭酸カルシウム[商品名:「RK−87BR2F」、白石工業株式会社製(シリカ処理、平均粒子径0.15μm)]
D−4: 溶融シリカ[商品名:「MC3000」、キンセイマテック株式会社製(平均粒子径1.2μm)]
D−5: 含水カオリン[商品名:「ASP−200」、BASF社製(平均粒子径0.4μm)]
D−6: 沈降性硫酸バリウム[商品名:「B−54」、堺化学工業株式会社製(平均粒子径0.7μm)]
D−7: 二酸化チタン[商品名:「PF−739」、石原産業株式会社製(平均粒子径0.6μm)]
D−8: 炭酸カルシウム[商品名:「SCP E−#45」、林化成株式会社製(平均粒子径20.0μm)]
D−9: 硫酸バリウム[商品名:「BMH−100」、堺化学工業株式会社社製(平均粒子径11.6μm)]。
E−1: トリグリセリンベヘン酸フルエステル(商品名:「ポエムTR−FB」、理研ビタミン株式会社製)
E−2: ペンタエリスリトールステアリン酸フルエステルおよびペンタエリスリトールパルミチン酸フルエステルの混合物(商品名:「リケスターEW−440A」、理研ビタミン株式会社製)。
表1〜6に示す組み合わせで配合した配合成分を、シリンダー温度260℃に設定した同方向二軸押出機で混練を行い、得られたストランドを水冷し、ペレット化した。得られた各ペレットを130℃で4時間乾燥し、各実施例および各比較例に対応するポリエステル樹脂組成物を得た。これらのポリエステル樹脂組成物を対象にして、上述の各評価試験(4)〜(11)を行なった。
Claims (8)
- 50〜100質量%のポリブチレンテレフタレート樹脂と、0〜50質量%のポリエチレンテレフタレート樹脂とを含有するポリエステル樹脂Aを含むポリエステル樹脂組成物であって、
前記ポリエステル樹脂組成物は、アルカリ金属の有機酸塩およびアルカリ土類金属の有機酸塩のいずれか一方または両方である金属有機酸塩Bと、前記ポリエステル樹脂A100質量部に対し、0.05〜3質量部の多官能グリシジル基含有スチレン系ポリマーC、1〜20質量部の平均粒子径0.05〜3μmである無機フィラーDとを含み、
前記ポリエステル樹脂組成物は、アルカリ金属原子およびアルカリ土類金属原子のいずれか一方または両方を、前記ポリエステル樹脂A100質量部に対し、0.000005〜0.05質量部含み、かつ、
前記ポリエステル樹脂組成物は、ポリブチレンテレフタレートの線状オリゴマーの含有量、または前記ポリブチレンテレフタレートの線状オリゴマーおよびポリエチレンテレフタレートの線状オリゴマーの含有量が1000mg/kg以下である、ポリエステル樹脂組成物。 - 前記ポリエステル樹脂組成物は、前記アルカリ金属原子および前記アルカリ土類金属原子のいずれか一方または両方を、前記ポリエステル樹脂A100質量部に対し、0.0005〜0.05質量部含む、請求項1に記載のポリエステル樹脂組成物。
- 前記ポリエステル樹脂組成物は、チタン原子の含有量が50mg/kg以下である、請求項1または2に記載のポリエステル樹脂組成物。
- 前記金属有機酸塩Bの金属種は、リチウム、ナトリウム、カリウム、カルシウム、マグネシウムからなる群より選ばれる1種または2種以上である、請求項1〜3のいずれかに記載のポリエステル樹脂組成物。
- 前記金属有機酸塩Bは、酢酸リチウム、酢酸ナトリウム、酢酸カリウム、酢酸カルシウム、酢酸マグネシウム、安息香酸リチウム、安息香酸ナトリウムおよび安息香酸カリウムからなる群より選ばれる1種または2種以上である、請求項1〜4のいずれかに記載のポリエステル樹脂組成物。
- 前記無機フィラーDは、炭酸カルシウム、シリカ、カオリン、硫酸バリウムおよび二酸化チタンからなる群より選ばれる1種または2種以上である、請求項1〜5のいずれかに記載のポリエステル樹脂組成物。
- 請求項1〜6のいずれかに記載のポリエステル樹脂組成物を含む、光反射体用部品。
- 請求項7に記載の光反射体用部品の表面の少なくとも一部に光反射金属層が形成されている、光反射体。