JP6071762B2 - ポリ塩化ビニル系樹脂フィルムおよびポリ塩化ビニル系粘着テープ - Google Patents
ポリ塩化ビニル系樹脂フィルムおよびポリ塩化ビニル系粘着テープ Download PDFInfo
- Publication number
- JP6071762B2 JP6071762B2 JP2013117632A JP2013117632A JP6071762B2 JP 6071762 B2 JP6071762 B2 JP 6071762B2 JP 2013117632 A JP2013117632 A JP 2013117632A JP 2013117632 A JP2013117632 A JP 2013117632A JP 6071762 B2 JP6071762 B2 JP 6071762B2
- Authority
- JP
- Japan
- Prior art keywords
- polyvinyl chloride
- adhesive tape
- release agent
- pressure
- sensitive adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明のポリ塩化ビニル系樹脂フィルムは、ポリ塩化ビニルを主成分とするフィルムの少なくとも一方の表面に、長鎖アルキル系離型剤とエチレン−酢酸ビニル共重合体の混合物を主成分として含む離型剤層を設けたものである。図1に、本発明のポリ塩化ビニル系樹脂フィルムの一例の概略断面図を示す。図1においては、本発明のポリ塩化ビニル系樹脂フィルム10は、ポリ塩化ビニルを主成分とするフィルム1と離型剤層2との積層構造からなる。また、本発明のポリ塩化ビニル系樹脂フィルムは、本発明の効果を損なわない範囲で、任意の適切な他の層を有していても良い。
ポリ塩化ビニルを主成分とするフィルムは、ポリ塩化ビニルを、好ましくは50重量%〜100重量%含み、より好ましくは60重量%〜100重量%含み、さらに好ましくは70重量%〜100重量%含み、特に好ましくは80重量%〜100重量%含み、最も好ましくは90重量%〜100重量%含む。上記フィルム中のポリ塩化ビニルの含有割合を上記範囲内に調整することにより、成膜性が良く且つ柔軟で破断し難いフィルムとなり得る。
離型剤層は、長鎖アルキル系離型剤とエチレン−酢酸ビニル共重合体の混合物を主成分として含む。
本発明のポリ塩化ビニル系粘着テープは、本発明のポリ塩化ビニル系樹脂フィルムの離型剤層が設けられていない側の表面上に粘着剤層が設けられたものである。図2に、本発明のポリ塩化ビニル系粘着テープの一例の概略断面図を示す。図2においては、本発明のポリ塩化ビニル系粘着テープ100は、離型剤層2とポリ塩化ビニルを主成分とするフィルム1と粘着剤層3との積層構造からなる。離型剤層2とポリ塩化ビニルを主成分とするフィルム1との積層体は、ポリ塩化ビニル系樹脂フィルム10である。また、本発明のポリ塩化ビニル系粘着テープは、本発明の効果を損なわない範囲で、任意の適切な他の層を有していても良い。
本発明のポリ塩化ビニル系樹脂フィルムおよび本発明のポリ塩化ビニル系粘着テープは、任意の適切な用途に用い得る。好ましい用途としては、例えば、金属板の表面保護が挙げられ、具体的には、好ましくは、ステンレス板、アルミ板、塗装鋼板から選ばれる少なくとも1種の被着体の表面保護に用いられる。特に好ましくは、これらの金属板を加工する際に用いられる。
測定対象の粘着テープを5.0cm×5.0cmの大きさに切り取り、粘着剤層の無い面側に水を10ml設置した後、23.0℃、湿度50%の環境下、接触角測定装置(「CA−X」、協和界面科学社製)を用いて1種の粘着テープ試料につき任意10箇所で接触角を測定し、その平均値を接触角とした。
測定対象の粘着テープを、23.0℃、湿度50%の環境下、1時間放置した後、その粘着テープの一部を20mm幅×100mm長さに切断し、そのテープの粘着剤層を、100mm×100mmに切断した同一の粘着テープの背面側(粘着剤層と反対側)に流れ方向が一致するように線圧78.5N/cm、速度0.3m/分で貼り合せた後、23.0℃、湿度50%の環境下で30分間放置し、剥離角度180°、引張速度0.3m/分で粘着テープを剥離し、その時の剥離力を測定した。
測定対象の粘着テープを230mm幅3インチボール紙芯に50m巻きつけて、40.0℃、相対湿度92%の環境下で3日間保存して、ロール状粘着テープを得た。
ロール状粘着テープのボール紙芯に、3インチボール紙芯を宙づりするための金属棒を通して宙づりにした。この状態で、粘着テープを1m/秒で1mずつ巻き戻しを行うことで1つのロール状粘着テープで50回巻き戻しと巻き戻し停止を繰り返して、下記の判断基準に基づき、巻き戻し性の評価を行った。
×:巻き戻し時に粘着テープの粘着剤層が隣接する粘着テープの背面(粘着剤層と反対側の表面)に粘着するなどして、粘着テープの破れや千切れ、粘着剤層の粘着剤脱落など、粘着テープに破損が起きた。
△:巻き戻し時に粘着テープの粘着剤層が隣接する粘着テープの背面(粘着剤層と反対側の表面)に粘着するなどして、延伸されるなどの粘着テープの変形が起き、巻き戻し作業が困難となった。もしくは、巻き戻し時に粘着テープの粘着剤層が隣接する粘着テープの背面(粘着剤層と反対側の表面)に貼りつくことはないが、巻き戻し中に巻きずれが生じた。
○:上記の問題がなく、ロールから粘着テープを巻き戻すことができた。
測定対象の粘着テープを、35℃、湿度80%の環境下で24時間加熱後、SUS304片面#8研磨板に貼付け、35℃、湿度80%の環境下に24時間投入し、30分以上放置後、手で剥がした。SUSのテープ剥離面を目視で観察して、下記の判断基準に基づき、被着体汚染性を確認した。
○:SUS板表面の汚れ曇り(SUS表面が白くなる)なし。
×:SUS板表面の汚れ曇りあり。
測定対象の粘着テープを23℃、湿度50%の環境下で1時間放置した後、粘着テープを長さ150mm×幅10mmにカットした。そのサンプルを、チャック間50mm、引張速度300mm/分で200%引っ張った際、チャック間にあった粘着テープの背面側(粘着剤層と反対の表面側)の離型剤層のひび割れを目視で確認した。
○:ひび割れなし。
×:ひび割れあり。
評価項目≪ロール状粘着テープの巻き戻し試験≫、≪被着体汚染性≫、≪離型剤層のテープへの追従性≫について、すべてが○であったものを合格品、ひとつでも×があったものを不合格品とした。
重合度P=1050のポリ塩化ビニル100重量部に対してDOP可塑剤(フタル酸ビス(2−エチルヘキシル)、ジェイプラス製)27重量部を含んだ軟質ポリ塩化ビニルフィルムをカレンダー法によって製造した。この軟質ポリ塩化ビニルフィルムの厚みは70μmであり、JIS−K−7127に従って測定される弾性率(MD)が250MPa、JIS−K−7127に従って測定される最大伸び(MD)が400%であった。また、製造直後の表面粗さ(算術平均表面粗さRa)は0.1μmであった。
長鎖アルキル系離型剤(ピーロイル1010、直鎖アルキル基の鎖長=炭素数18、一方社油脂製、オクタデシルイソシアナートとポリビニルアルコールの付加物)20重量部、エチレン−酢酸ビニル共重合体(EVA)(エバフレックスEV−150、三井デュポン社製)100重量部を、溶液状態で混合して、混合溶液(1A)を得た。混合溶液(1A)中の長鎖アルキル系離型剤とエチレン−酢酸ビニル共重合体の混合比は、重量比で、長鎖アルキル系離型剤:エチレン−酢酸ビニル共重合体(EVA)=1:5であった。
製造例1で製造した軟質ポリ塩化ビニルフィルムの片方の面に、上記混合溶液(1A)を塗布して、厚さ1.0μm、算術平均表面粗さRa=0.5μmの離型剤層を形成させた。
このようにして、ポリ塩化ビニル系樹脂フィルム(1B)を得た。
続いて、ブチルアクリレート(BA)/アクリロニトリル(AN)/アクリル酸(AA)/ヒドロキシエチルアクリレート=92/5/2/0.3(重量比)から構成されるアクリル共重合ポリマー100重量部、メラミン系架橋剤(ブタノール変性メラミンホルムアルデヒド樹脂、「スーパーベッカミンJ−820−60N」、日本ポリウレタン製)1重量部、エポキシ系架橋剤(1,3−ビス(N,N−ジグリシジルアミノメチル)ジクロルヘキサン「テトラッドC」、三菱瓦斯化学製)0.5重量部からなる粘着剤をトルエン溶液とした粘着剤溶液を、ポリ塩化ビニル系樹脂フィルム(1B)の離型剤層と反対側の面に塗布した後、130℃×90秒で乾燥し、厚み10μmの粘着剤層をポリ塩化ビニル系樹脂フィルム(1B)の離型剤層と反対側の面に形成した。
このようにして、ポリ塩化ビニル系粘着テープ(1C)を得た。
結果を表1に示した。
長鎖アルキル系離型剤(ピーロイル1010、直鎖アルキル基の鎖長=炭素数18、一方社油脂製)1.0重量部、エチレン−酢酸ビニル共重合体(EVA)(エバフレックスEV−150、三井デュポン社製)100重量部を、溶液状態で混合して、混合溶液(2A)を得た。混合溶液(2A)中の長鎖アルキル系離型剤とエチレン−酢酸ビニル共重合体の混合比は、重量比で、長鎖アルキル系離型剤:エチレン−酢酸ビニル共重合体(EVA)=1:100であった。
製造例1で製造した軟質ポリ塩化ビニルフィルムの片方の面に、上記混合溶液(2A)を塗布して、厚さ1.0μm、算術平均表面粗さRa=0.5μmの離型剤層を形成させた。
このようにして、ポリ塩化ビニル系樹脂フィルム(2B)を得た。
続いて、ブチルアクリレート(BA)/アクリロニトリル(AN)/アクリル酸(AA)/ヒドロキシエチルアクリレート=92/5/2/0.3(重量比)から構成されるアクリル共重合ポリマー100重量部、メラミン系架橋剤(ブタノール変性メラミンホルムアルデヒド樹脂、「スーパーベッカミンJ−820−60N」、日本ポリウレタン製)1重量部、エポキシ系架橋剤(1,3−ビス(N,N−ジグリシジルアミノメチル)ジクロルヘキサン「テトラッドC」、三菱瓦斯化学製)0.5重量部からなる粘着剤をトルエン溶液とした粘着剤溶液を、ポリ塩化ビニル系樹脂フィルム(2B)の離型剤層と反対側の面に塗布した後、130℃×90秒で乾燥し、厚み10μmの粘着剤層をポリ塩化ビニル系樹脂フィルム(2B)の離型剤層と反対側の面に形成した。
このようにして、ポリ塩化ビニル系粘着テープ(2C)を得た。
結果を表1に示した。
ブチルアクリレート(BA)/アクリロニトリル(AN)/アクリル酸(AA)/ヒドロキシエチルアクリレート=92/5/2/0.3(重量比)から構成されるアクリル共重合ポリマー100重量部、メラミン系架橋剤(ブタノール変性メラミンホルムアルデヒド樹脂、「スーパーベッカミンJ−820−60N」、日本ポリウレタン製)1重量部、エポキシ系架橋剤(1,3−ビス(N,N−ジグリシジルアミノメチル)ジクロルヘキサン「テトラッドC」、三菱瓦斯化学製)0.5重量部からなる粘着剤をトルエン溶液とした粘着剤溶液を、製造例1で製造した軟質ポリ塩化ビニルフィルムの片方の面に塗布した後、130℃×90秒で乾燥し、厚み10μmの粘着剤層を軟質ポリ塩化ビニルフィルムの片方の面に形成した。
このようにして、離型剤層を有さないポリ塩化ビニル系粘着テープ(C1C)を得た。
結果を表1に示した。
長鎖アルキル系離型剤(ピーロイル1010、直鎖アルキル基の鎖長=炭素数18、一方社油脂製)100重量部を、溶液状態にして、希釈溶液(3A)を得た。
製造例1で製造した軟質ポリ塩化ビニルフィルムの片方の面に、上記希釈溶液(C2A)を塗布して、厚さ1.0μm、算術平均表面粗さRa=0.5μmの離型剤層を形成させた。
このようにして、ポリ塩化ビニル系樹脂フィルム(C2B)を得た。
続いて、ブチルアクリレート(BA)/アクリロニトリル(AN)/アクリル酸(AA)/ヒドロキシエチルアクリレート=92/5/2/0.3(重量比)から構成されるアクリル共重合ポリマー100重量部、メラミン系架橋剤(ブタノール変性メラミンホルムアルデヒド樹脂、「スーパーベッカミンJ−820−60N」、日本ポリウレタン製)1重量部、エポキシ系架橋剤(1,3−ビス(N,N−ジグリシジルアミノメチル)ジクロルヘキサン「テトラッドC」、三菱瓦斯化学製)0.5重量部からなる粘着剤をトルエン溶液とした粘着剤溶液を、ポリ塩化ビニル系樹脂フィルム(C2B)の離型剤層と反対側の面に塗布した後、130℃×90秒で乾燥し、厚み10μmの粘着剤層をポリ塩化ビニル系樹脂フィルム(C2B)の離型剤層と反対側の面に形成した。
このようにして、ポリ塩化ビニル系粘着テープ(C3C)を得た。
結果を表1に示した。
2 離型剤層
3 粘着剤層
10 ポリ塩化ビニル系樹脂フィルム
100 ポリ塩化ビニル系粘着テープ
Claims (9)
- ポリ塩化ビニルを主成分とするフィルムの少なくとも一方の表面に、長鎖アルキル系離型剤とエチレン−酢酸ビニル共重合体の混合物を主成分として含む離型剤層を設けた、該離型剤層の表面に対する水の接触角が90.0°〜130.0°である、ポリ塩化ビニル系樹脂フィルム。
- 前記離型剤層の厚みが0.01μm〜10.0μmである、請求項1に記載のポリ塩化ビニル系樹脂フィルム。
- 前記離型剤層に含まれる長鎖アルキル系離型剤が炭素数12以上の直鎖アルキル基を含む、請求項1または2に記載のポリ塩化ビニル系樹脂フィルム。
- 前記ポリ塩化ビニルが軟質ポリ塩化ビニルである、請求項1から3までのいずれかに記載のポリ塩化ビニル系樹脂フィルム。
- 請求項1から4までのいずれかに記載のポリ塩化ビニル系樹脂フィルムの離型剤層が設けられていない側の表面上に粘着剤層が設けられた、ポリ塩化ビニル系粘着テープ。
- 前記粘着剤層が、(メタ)アクリル系ポリマーまたはゴム系粘着剤を含む、請求項5に記載のポリ塩化ビニル系粘着テープ。
- 前記ポリ塩化ビニル系粘着テープの粘着剤層を前記ポリ塩化ビニル系粘着テープの離型剤層に貼り合せて引張速度0.3m/分で剥離した場合の粘着力が0.1N/20mm〜3.0N/20mmである、請求項5または6に記載のポリ塩化ビニル系粘着テープ。
- ステンレス板、アルミ板、塗装鋼板から選ばれる少なくとも1種の被着体の表面保護に用いられる、請求項5から7までのいずれかに記載のポリ塩化ビニル系粘着テープ。
- 金属板加工に用いられる、請求項5から8までのいずれかに記載のポリ塩化ビニル系粘着テープ。