JP5854675B2 - 樹脂成形体及び自動車内装部品 - Google Patents
樹脂成形体及び自動車内装部品 Download PDFInfo
- Publication number
- JP5854675B2 JP5854675B2 JP2011158578A JP2011158578A JP5854675B2 JP 5854675 B2 JP5854675 B2 JP 5854675B2 JP 2011158578 A JP2011158578 A JP 2011158578A JP 2011158578 A JP2011158578 A JP 2011158578A JP 5854675 B2 JP5854675 B2 JP 5854675B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- polybutylene terephthalate
- terephthalate resin
- polyamide
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(測定方法)
前記ポリブチレンテレフタレート樹脂組成物から構成される100mm×40mm×2mmの試験片2枚の試験片を、65℃の条件で2時間処理したときに、発生するアルデヒドガス排出量、ホルムアルデヒドガス排出量を測定する。
本発明の樹脂成形体は、ポリブチレンテレフタレート樹脂と、ポリアミド樹脂とを含むポリブチレンテレフタレート樹脂組成物(以下、単に「樹脂組成物」という場合がある。)から構成される。
本発明の樹脂成形体は上述の樹脂組成物を、一般的な成形方法で成形してなる。成形方法としては、例えば、射出成形法、押出成形法が挙げられる。以下、本発明の樹脂成形体の製造方法について、押出成形機を用いる場合を例に説明する。
本発明の樹脂成形体は、アセトアルデヒドの含有量、ホルムアルデヒドの含有量が非常に少ない。下記の方法で測定したアセトアルデヒドの排出量が0.20μg以下であり、ホルムアルデヒドの含有量が0.10μg以下である。
(測定方法)
ポリブチレンテレフタレート樹脂組成物から構成される100mm×40mm×2mmの試験片2枚を、65℃の条件で2時間処理したときに、発生するアセトアルデヒドガス排出量、ホルムアルデヒドガス排出量を測定する。より具体的には実施例に記載の通りである。
実施例、及び比較例で、ポリブチレンテレフタレート樹脂組成物の材料として、以下の成分を使用した。
(ポリブチレンテレフタレート樹脂)
テレフタル酸と1,4−ブタンジオールとの重縮合体、固有粘度(IV)が0.69、ウィンテックポリマー社製「ジュラネックス 300FP」
(ポリアミド樹脂)
ポリアミド6 宇部興産株式会社製 UBEナイロン 1015B
(ヒンダードフェノール系酸化防止剤)
テトラキス[メチレン−3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)プロピオネート]メタン
表1に示す成分を表1に示す割合(単位は質量%)で混合したものを原料とし、この原料を二軸押出機(JSW製、TEX−30)に投入した。下記の条件にて、上記原料を溶融混練してポリブチレンテレフタレート樹脂組成物を製造した。溶融混練されたポリブチレンテレフタレート樹脂組成物を、孔径4mmの円形の吐出孔を備える二軸押出機の先端のダイからストランド状に吐出し、ポリブチレンテレフタレート樹脂組成物のストランドが冷却された後に、ストランドを3mm長に切断して、ポリブチレンテレフタレート樹脂組成物のペレットを得た。
(溶融混練条件)
シリンダー温度:260℃
スクリュー回転数:130rpm
押出量:12kg/hr
ポリブチレンテレフタレート樹脂組成物のペレットを140℃の恒温機内で3時間保持し、ペレットを乾燥した。乾燥させたペレットを用いて、射出成形機(JSW製、J75EP)により、100mm×40mm×2mmの試験片を成形した。
(射出成形条件)
シリンダー温度:250℃
金型温度:60℃
射出速度:16.7mm/秒
実施例及び比較例の樹脂成形体から発生するアセトアルデヒドガスの量、ホルムアルデヒドガスの量を、以下の方法で測定されるアセトアルデヒドガス排出量、ホルムアルデヒドガス排出量で評価した。
(i)射出成形によって作製した試験片2枚を容積10Lのテドラーバッグに封入し、バッグに含まれる空気を真空ポンプにて除去した後、テドラーバッグに純窒素ガス4Lを充填し、テドラーバッグのコックを閉じた。テドラーバッグをオーブンの中に入れ、コックの先にサンプリング用テフロン(登録商標)チューブを取り付けてオーブンの外まで延ばし、この状態で65℃、2時間加熱処理を行った。この加熱処理で試料ガスを作製した。
(ii)上記(ii)で作製した試料ガスを、65℃の加熱状態で、2,4−ジニトロフェニルヒドラジン(2,4−Dinitrophenylhydrazine(略称:DNPH))カートリッジに3L採取した。採取後のカートリッジはアセトニトリルで溶出処理を行い、得られた溶出液を高速液体クロマトグラフ(HPLC;Waters製、型式:Ultra Performance Liquid Chromatography Aquiy)を用いて、溶出した成分のホルムアルデヒド排出量、アセトアルデヒド排出量を測定した。排出量算出は、アルデヒド・ケトンーDNPH標準混合試料ERA―028を標準溶液として、サンプルのピーク面積から、2枚の成形片から発生したホルムアルデヒドガス量、アセトアルデヒドガス量を算出した。導出結果を表1に示した。
Claims (3)
- エチレングリコール由来の繰り返し単位が0モル%以上1モル%以下のポリブチレンテレフタレート樹脂と、ポリアミド樹脂とを含むポリブチレンテレフタレート樹脂組成物から構成され、
前記ポリアミド樹脂が、ポリアミド6であり、0.5質量%以上5質量%未満の範囲で含有されており、
前記樹脂組成物は、さらにヒンダードフェノール系酸化防止剤を含み、
下記の方法で測定したアセトアルデヒドガス排出量が0.20μg以下であり、ホルムアルデヒドガス排出量が0.10μg以下である樹脂成形体。
(測定方法)
前記ポリブチレンテレフタレート樹脂組成物から構成される100mm×40mm×2mmの試験片2枚を、65℃という条件で2時間処理したときに、発生するアルデヒドガス排出量、ホルムアルデヒドガス排出量を測定する。 - 前記ヒンダードフェノール系酸化防止剤の含有量が、0.01質量%以上3質量%以下である請求項1に記載の樹脂成形体。
- 請求項1又は2に記載の樹脂成形体から構成される自動車内装部品。