JP5775271B2 - Paper containing recycled pulp - Google Patents

Paper containing recycled pulp Download PDF

Info

Publication number
JP5775271B2
JP5775271B2 JP2010156990A JP2010156990A JP5775271B2 JP 5775271 B2 JP5775271 B2 JP 5775271B2 JP 2010156990 A JP2010156990 A JP 2010156990A JP 2010156990 A JP2010156990 A JP 2010156990A JP 5775271 B2 JP5775271 B2 JP 5775271B2
Authority
JP
Japan
Prior art keywords
paper
pulp
recycled pulp
layer
postcard
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2010156990A
Other languages
Japanese (ja)
Other versions
JP2011094280A (en
Inventor
柳内 晃一
晃一 柳内
知弘 干潟
知弘 干潟
清高 植松
清高 植松
篤志 畑田
篤志 畑田
Original Assignee
日本製紙株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to JP2009162794 priority Critical
Priority to JP2009162794 priority
Priority to JP2009224637 priority
Priority to JP2009224637 priority
Application filed by 日本製紙株式会社 filed Critical 日本製紙株式会社
Priority to JP2010156990A priority patent/JP5775271B2/en
Publication of JP2011094280A publication Critical patent/JP2011094280A/en
Application granted granted Critical
Publication of JP5775271B2 publication Critical patent/JP5775271B2/en
Application status is Active legal-status Critical
Anticipated expiration legal-status Critical

Description

本発明は、再生パルプを含有する紙に関し、特にはがき用紙に好適な紙に関する。 The present invention relates to a paper containing recycled pulp, more particularly suitable for paper postcard paper.

一般に紙は、大きくは紙と板紙とに分類される。 Generally the paper is roughly classified into paper and paperboard. 前者の紙の用途には様々なものがあるが、「官製はがき」(あるいは「郵政はがき」)、「私製はがき」と呼ばれる郵便はがきもその一つである。 Although the former paper applications there are a variety of things, "postcard" (or "postal postcard"), postcard, which is called "I made postcard" is one of them. 郵便はがきは、通常、原料パルプからはがき用紙を製造し所定のサイズに裁断したものであり、官製の場合、表面に郵便番号記載枠や切手と同じ効力を持つ額面が記載された料額印面が印刷される。 Postcards usually manufactured postcard paper from pulp is obtained by cutting into a predetermined size, when the government-, postal code, wherein frame and stamps describes par with the same potency as the postal stamp face on the surface It is printed. お年玉付き年賀はがきや夏のお便りはがきなどでは、さらに下端に組番号や抽選番号が印刷される。 Such as in the lottery with New Year's postcards and summer of letter postcard, set number or lottery numbers are printed on the further lower end. これらの印刷は、通常オフセット印刷方式にて行われる。 These printing is performed in the normal offset printing method.

このようなはがき用紙として、例えば特許文献1(特許第3755483号公報)には、化学パルプや脱墨パルプ等を混合し填料として炭酸カルシウムを使用することなどが記載されている。 Such postcard paper, for example, Patent Document 1 (Japanese Patent No. 3755483), etc. The use of calcium carbonate is described as a mixture of chemical pulp and deinked pulp filler. 特許文献2(特開2004−1000049号公報)には、多層構造の支持体の一方の面にインクジェット記録に適するようインク受理層を設けることが記載されている。 Patent Document 2 (JP 2004-1000049) describes providing an ink-receiving layer to be suitable for ink jet recording on one surface of the support of the multi-layer structure. 特許文献3(特開2003−291515号公報)、特許文献4(特開2002−127592号公報)、特許文献5(特開平10−297148号公報)、および特許文献6(特許第4031277号公報)には、2層以上の多層構造の支持体としてインク吸収性に優れることが記載されている。 Patent Document 3 (JP 2003-291515 JP), Patent Document 4 (JP 2002-127592 JP), Patent Document 5 (JP-A-10-297148), and Patent Document 6 (Japanese Patent No. 4031277) in is described to be excellent in ink absorbency as a support for a multilayer structure of two or more layers.

近年、紙の製造においては、リサイクルや省資源など環境意識の高まりに伴って、原料パルプとして古紙の利用が推進されている。 In recent years, in the production of paper, along with the growing environmental awareness, such as recycling and resource conservation, the use of waste paper has been promoted as a raw material pulp. はがき用紙や封書用紙においても、古紙の活用に対する要望は非常に高い。 In the postcard paper and envelope paper, demand for the use of waste paper is very high. 例えば、特許文献7(特開2005−35224号公報)には、原料パルプとして古紙から得られる再生パルプを含有するはがきの輸送システムが記載されている。 For example, Patent Document 7 (JP-2005-35224), postcard transportation systems containing is recycled pulp obtained from waste paper as raw material pulp is described.

一方、郵便局では、郵便物に差出人によって記載された郵便番号や住所氏名等をOCRで読み取り、これらの宛先情報をバーコードとして印字し、自動区分機による機械処理により選別・搬送区分することが行われている。 On the other hand, the post office, that reads the postal code and address name and the like that are described by the sender on the postal matter with OCR, and printing these destination information as a bar code, sorting and transport segment by mechanical treatment with automatic sorter It has been made. なお、このバーコードは、赤外線または紫外線励起の蛍光ステルスインクを用いて、目には見えない不可視情報として印字されている。 Note that this bar code, using fluorescent stealth ink infrared or ultraviolet excitation, and is printed as an invisible information invisible. 例えば、特許文献8(特開平11−076950号公報)には、郵便物の仕分け用バーコード印字システムが記載されている。 For example, Patent Document 8 (JP-A-11-076950), it describes a sorting bar code printing system of the mail.
また、特許文献9には、古紙パルプを用紙中に40質量%以上含有し、3層以上の多層抄き合わせにより抄造される再生葉書用紙が記載されている。 In Patent Document 9, a waste paper pulp containing 40 wt% or more on paper, reproduction postcard sheet being papermaking is described by three or more layers paper making alignment.

特許第3755483号 Patent No. 3755483 特開2004−100049号公報 JP 2004-100049 JP 特開2003−291515号公報 JP 2003-291515 JP 特開2002−127592号公報 JP 2002-127592 JP 特開平10−297148号公報 JP 10-297148 discloses 特許第4031277号 Patent No. 4031277 特開2005−035224号公報 JP 2005-035224 JP 特開平11−076950号公報 JP 11-076950 discloses 特開2010−047894号公報 JP 2010-047894 JP

上記のように、郵便物は、差出人が記載した宛先情報を光学的に読み取りステルスバーコード化することで、効率良く搬送されるシステムとなっている。 As mentioned above, postal matter, by optically reading Stealth barcodes the destination information sender is described, which is a system that is efficiently transported. しかし、紙の製造においてパルプ類には、塵やピッチ、古紙由来のインキ粕やトナー粕等の夾雑物が混入しやすく、これらのチリやダート(夾雑物による黒点や異物)により宛先情報の読み取り精度が低下して、正確にバーコード化されない問題がある。 However, the pulps in the manufacture of paper, read the dust and pitch, contaminants easily mixed ink dregs or toner lees etc. from waste paper, the destination information by these dust and dirt (black spots and foreign substances by contaminants) accuracy is lowered, there is a problem that not correctly barcoded. また、古紙に含まれる蛍光染料などの蛍光物質は、バーコードの印字部と地色部とのコントラストを低下させて、自動区分機でのバーコードの読み取りに支障を及ぼし、正確に搬送されない問題がある。 The fluorescent substance such as a fluorescent dye contained in the used paper, reduce the contrast between the printing portion and the ground color portion of the bar code, have a difficulty in reading the bar code in an automatic sorter, not conveyed correctly problems there is. そして、古紙を原料とする再生パルプを多量に配合する場合、差出人が記載した宛先情報やステルスバーコードの読み取り精度は、さらに悪化してしまう。 Then, when the large amount of recycled pulp to make paper as a raw material, accuracy of reading the address information and stealth barcode sender is described, resulting in worse. また、再生パルプを高配合すると、白色性など製品の外観が損なわれる問題がある。 Further, when high loading recycled pulp, there is a problem that the appearance of the products such as white may be impaired.

このように、古紙利用の推進と郵便搬送システムの効率化とは反比例の関係にあり、宛先情報やバーコードの読み取り精度を悪化させることなく、再生パルプを増配することが望まれている。 Thus, the propulsion and efficiency postal transport system paper recycling is inversely proportional, without deteriorating the reading accuracy of the address information and bar codes, it is desirable to dividend recycled pulp. そこで、本発明は、再生パルプを高配合しながら、白色性に優れ、蛍光強度が低く、チリやダートの少ないはがき用紙に適した紙を提供することを目的とする。 The present invention, while high loading recycled pulp, excellent whiteness, fluorescence intensity is low, and an object thereof is to provide a paper which is suitable for small postcard paper of dust and dirt.

本発明者らは、再生パルプの中でも白色度の高いパルプを用いることで、上記課題を解決し、本発明に到達した。 The present inventors have found that by using a pulp of high brightness among regenerated pulp, to solve the above problems, and have reached the present invention. 詳しくは、パルプを主原料とした3層以上の多層構造で、表層と裏層との間に形成された少なくとも1つの内層に再生パルプを含有する紙であって、全パルプ固形分に対し再生パルプを20質量%以上含有し、かつ、再生パルプの全固形分に対し白色度が60%以上である再生パルプを50質量%以上含有することにより、課題を達成できることを見出した。 Specifically, the pulp in three or more layers structure in which a main raw material, a paper which contains at least one inner layer in recycled pulp formed between the surface layer and the backing layer, reproducing the total pulp solids the pulp contains more than 20 wt%, and, by containing recycled pulp whiteness is 60% or more than 50 wt% relative to the total solids content of the recycled pulp, was found to be able to achieve problem.

本発明によれば、再生パルプを高配合することができ、環境に配慮した紙とすることができる。 According to the present invention, the recycled pulp can be high loading, it can be a paper environmentally friendly. また、再生パルプを高配合しても、白色性に優れ、蛍光強度が低く、チリやダートが少なく郵便搬送システムに適したはがき用紙を提供することが出来る。 Further, the recycled pulp also high loading, good whiteness, fluorescence intensity is low, it is possible to provide a postcard paper for dust and dirt is small postal delivery system.

本発明における紙は、板紙を含まない。 Paper in the present invention will not include paperboard. 以下、はがき用紙の場合を例として本発明を詳細に説明する。 Hereinafter, the case of postcard paper of the present invention in detail by way of example.

(はがき用紙の構造) (Structure of postcard paper)
本発明のはがき用紙は、パルプを主原料とした3層以上の多層構造からなり、抄き合わせあるいは多層抄きで製造される。 Postcard paper of the invention comprises the pulp from the main raw material and a three-layer or more multilayer structure, is manufactured in the paper making paper making alignment or multilayer. 例えば、3層の場合は「表層」「中層」「裏層」、4層の場合は「表層」「表下層」「裏下層」「裏層」、5層の場合は「表層」「表下層」「中層」「裏下層」「裏層」からそれぞれ構成される。 For example, in the case of a three-layer "surface layer", "middle", "lining", "surface", "Tables underlayer" "lower back", "back layer" in the case of four layers, in the case of five-layer "surface layer", "Table lower each consisting of "," middle "," lower back "," back layer ". 積層数はこれらに限定されるものではない。 The number of layers is not limited thereto. 表層はステルスバーコードの印刷面を含む。 Surface layer comprises a printing surface of the Stealth barcodes. なお、本発明でいう表層と裏層との間に形成された内層とは、「表下層」、「中層」、「裏下層」等を意味する。 Incidentally, an inner layer formed between the surface layer and the backing layer in the present invention, "front lower", "middle", means "lower back", and the like.

本発明のはがき用紙は、少なくとも1層の内層、すなわち、例えば3層の場合は「中層」に、4層の場合は「表下層」および/又は「裏下層」に、5層の場合は「表下層」「中層」「裏下層」のいずれか1層以上に、パルプとして古紙を原料とする再生パルプを含有する。 Postcard paper of the invention, the inner layer of at least one layer, i.e., for example, in the case of three layers "middle", in the case of four layers in "Table underlayer" and / or "lower back", in the case of five layers " Table underlayer "" middle "any one or more layers of" lower back "to contain recycled pulp to the paper as a raw material as pulp. 本発明ではこのように内層に再生パルプを含有することにより、再生パルプを高配合したはがき用紙でありながら白色性が高く、また、再生パルプに含まれるチリやダート、蛍光物質の影響を低く抑えることが可能となる。 By the present invention containing an inner layer in recycled pulp thus, a recycled pulp, yet whiteness high a postcard sheet that has high loading, also suppress dust and dirt contained in the reproduction pulp, the effect of the fluorescent substance low it becomes possible. 本発明において、再生パルプの含有割合は環境面から多いほど望ましく、全パルプ固形分に対し20質量%以上であり、40質量%以上がより好ましく、60質量%以上がさらに好ましい。 In the present invention, the content of recycled pulp is preferably the larger the environmental, is 20 wt% or more based on the total pulp solids, more preferably at least 40 wt%, more preferably at least 60 wt%.

(パルプ原料) (Pulp)
本発明においては、再生パルプとして白色度が60%以上であるものを使用し、全再生パルプの固形分に対して50質量%以上の割合で含有することで、チリやダート、蛍光強度など再生パルプを高配合した場合の問題を解消できるとともに、優れた白色性を得ることができる。 In the present invention, to use a whiteness is 60% or more recycled pulp, by a proportion of more than 50 wt% based on the solids content of the total reproduction pulp, dust or dirt, such as fluorescent intensity Play it is possible to solve the problem in the case of high loading pulp, it is possible to obtain an excellent whiteness. 再生パルプの白色度は65%以上であることがより好ましく、70%以上であることがさらに好ましい。 Whiteness of recycled pulp is more preferably 65% ​​or more, more preferably 70% or more.

このような白色度を有する再生パルプとして、本発明では脱墨古紙パルプ(DIP)を用いることが好ましい。 As regenerated pulp having such whiteness, it is preferable to use deinked waste paper pulp (DIP) in the present invention. DIPは一般に、古紙の離解処理、クリーナーやスクリーンによる除塵処理、フローテーターによる脱墨(インキ分離)処理、漂白処理、ニーダーやディスパーザーによる分散処理、DNTウォッシャー等による洗浄・脱水処理の各工程を経て製造される。 DIP is generally maceration processing of waste paper, dust treatment with cleaners or screens, deinking (ink separation) process by flotation, bleaching, distributed processing by a kneader or a disperser, the steps of washing and dewatering process by DNT washer etc. It is produced through. 洗浄は必要に応じて各工程の中でも行われる。 Washing is also performed in each step as required. DIPの白色度は、漂白処理や洗浄処理により調整することができる。 DIP whiteness can be adjusted by bleaching or cleaning process. なお、本発明におけるパルプおよびはがき用紙の白色度は、JIS P 8148に準じて測定したものである。 Note that brightness of the pulp and postcard paper of the present invention are those measured according to JIS P 8148.

また、本発明において、再生パルプに含有される灰分は、チリやダートを低減する観点から、再生パルプ中の20質量%未満が好ましく、さらに10質量%未満が好ましい。 Further, in the present invention, the ash contained in the recycled pulp, from the viewpoint of reducing the dust and dirt, is preferably less than 20 wt% in recycled pulp, more preferably less than 10 wt%. このように再生パルプ中の灰分が少ないことにより、多層構造における内部結合強度も良好となる。 By thus ash in recycled pulp is small, also becomes good internal bond strength in a multi-layer structure. 再生パルプ中の灰分は、除塵処理、脱墨処理、脱水機による洗浄などにより調整することができる。 Ash in recycled pulp may be adjusted dust removing treatment, deinking process, such as by washing with dehydrator. また、これらの処理を十分に行うことで、再生パルプに含有される微細繊維量は少なくなり、長さが0.1mm以下の微細繊維の含有割合として10質量%未満、さらには5質量%未満となる。 By performing these processes sufficiently, reproduction fines content contained in the pulp is reduced less than 10 mass% content ratio of 0.1mm or less fine fibers length, even less than 5 wt% to become. なお、再生パルプ中の灰分は、JIS P 8251に規定される525℃燃焼法に準じて測定したものである。 Incidentally, the ash in the recycled pulp is obtained by measurement in accordance with 525 ° C. combustion method specified in JIS P 8251. 微細繊維量は、JIS P 8226に規定される光学的自動分析法による繊維長測定方法に準じて測定したものであり、具体的には、Kajaanisy社製パルプ分析装置「FiberLab」にて測定したときの長さ平均算出時の繊維長分布における0.1mm以下の頻度をいう。 Fines amount is one measured according to fiber length measurement method by optical automatic analysis method specified in JIS P 8226, specifically, when measured at Kajaanisy manufactured pulp analyzer "FiberLab" It refers to less frequently 0.1mm of the fiber length distribution during long averaging.

本発明において、4層以上で複数の内層に再生パルプを配合する場合は、各内層に配合する再生パルプは同一でも異なっていても良い。 In the present invention, when formulating the recycled pulp to a plurality of inner four layers or more, recycled pulp to be blended in the inner layer may be the same or different. 各層に用いられる再生パルプの白色度が異なっている場合は、例えば5層以上のとき、表下層や裏下層に用いられる再生パルプの白色度が、中層に用いられる再生パルプの白色度よりも高いことが好ましい。 If the whiteness of recycled pulp used in each layer are different, for example, when five or more layers, the whiteness of recycled pulp used in Table lower and lower back is higher than the whiteness of recycled pulp used in the middle layer it is preferable. ひいては、はがき用紙を各層に分割したとき、表下層や裏下層の紙の白色度が、中層の紙の白色度よりも高いことが好ましい。 Therefore, when dividing the postcard paper layers, whiteness table lower and lower back of the paper is preferably higher than the whiteness of the middle layer of paper.

さらに必要に応じて、内層には、機械パルプ(MP)、広葉樹クラフトパルプ(LKP)、針葉樹クラフトパルプ(NKP)など、抄紙原料として一般的に使用されているものの1種類または2種類以上と再生パルプとを混合して使用することができる。 If necessary regeneration, the inner layer, mechanical pulp (MP), hardwood kraft pulp (LKP), such as softwood kraft pulp (NKP), and one or more kinds of what is generally used as a paper stock it can be used by mixing the pulp. 機械パルプとしては、砕木パルプ(GP)、リファイナー砕木パルプ(RGP)、サーモメカニカルパルプ(TMP)、ケミサーモメカニカルパルプ(CTMP)、ケミグランドパルプ(CGP)、セミケミカルパルプ(SCP)などが挙げられる。 The mechanical pulp, groundwood pulp (GP), refiner groundwood pulp (RGP), thermomechanical pulp (TMP), chemi-thermo-mechanical pulp (CTMP), and the like chemi-ground pulp (CGP), semi-chemical pulp (SCP) . 環境の観点からは、再生パルプの使用量が多いことが望ましい。 From the viewpoint of environment, it is desirable that the amount of the recycled pulp is large. 再生パルプと他のパルプを混合して使用する場合、内層各層における両者の比率は任意に設定することができ特に限定されないが、再生パルプ:他のパルプ=50:50〜100:0が好適である。 When using a mixture of recycled pulp and other pulps, is not particularly limited can be the ratio of the two is set arbitrarily in the inner layers, recycled pulp: other pulp = 50: 50 to 100: 0 is preferred is there.

再生パルプの原料となる古紙としては、上質紙、中質紙、下級紙、新聞紙、チラシ、雑誌などの選別古紙やこれらが混合している無選別古紙や、コピー紙や感熱紙、ノーカーボン紙などを含むオフィス古紙などを好適に使用することができる。 The waste paper as a raw material for recycled pulp, fine paper, medium quality paper, inferior paper, newsprint, flyers, sorting waste paper and or unsorted waste paper to which they are mixed, such as magazines, copy paper and thermal paper, carbonless paper the office waste paper including the like can be suitably used.

一方、表層や裏層には、再生パルプを配合してもよいが、製品の白色性や蛍光強度、チリやダート等の観点から、針葉樹クラフトパルプ、広葉樹クラフトパルプなどの化学パルプを用いることが好ましい。 On the other hand, the surface layer and the backing layer may contain a recycled pulp but whiteness and fluorescence intensity of the product, from the viewpoint of dust and dirt, softwood kraft pulp, the use of chemical pulps such as hardwood kraft pulp preferable. 特に、表層は、紙の外観を決定づけるとともに、ステルスバーコードが印刷される面側でもあるため、化学パルプ100質量%が好ましい。 In particular, the surface layer, as well as determines the appearance of the paper, since that is also the side where stealth bar code is printed, chemical pulp 100% by mass.

本発明によれば、外観の白色性に優れたはがき用紙を得ることができる。 According to the present invention, it is possible to obtain an excellent postcard paper whiteness appearance. 再生パルプを利用したはがき用紙として、紙の表面および裏面の白色度としては74%程度が望ましいが、本発明によれば76%以上の白色度のものも得ることができる。 As postcard paper of recycled pulp, as the front and back surfaces of the whiteness of paper may be but about 74% is desired, also be obtained as 76% or more of whiteness according to the present invention.

(蛍光失活処理) (Fluorescence deactivation processing)
本発明においては、蛍光強度低下の観点から、再生パルプに蛍光失活処理を施すことが望ましい。 In the present invention, from the viewpoint of fluorescence intensity reduction, it is desirable to perform the fluorescence deactivation process recycled pulp. 蛍光失活処理としては、再生パルプスラリーへの蛍光失活剤の添加、多価金属処理、酵素処理、過酸化物処理、オゾン処理、マスキング処理、脱墨後のパルプの二酸化塩素等による処理等が挙げられる。 The fluorescent deactivation treatment, the addition of a fluorescent quencher of the recycled pulp slurry, the polyvalent metal treatment, enzyme treatment, the peroxide treatment, ozone treatment, masking, treatment by chlorine dioxide or the like pulp after deinking and the like.

本発明では、蛍光失活剤が添加された再生パルプを使用することが望ましい。 In the present invention, it is desirable to use recycled pulp fluorescent deactivating agent is added. 蛍光失活剤としては、ジクロルイソシアヌール酸塩やN−ビニルホルムアミド系重合体、あるいは芳香族カルボン酸・アミン縮合物等が挙げられるが、これに限定されるものではない。 The fluorescent quenchers, dichlorprop isocyanuric acid salt or N- vinylformamide polymer, or is an aromatic carboxylic acid amine condensates and the like, but is not limited thereto.

蛍光失活剤の添加量は、再生パルプの固形分あたり固形分質量で0.01〜2%が好ましく、0.03〜1.5%であることが更に好ましい。 The addition amount of the fluorescent deactivating agent is preferably 0.01% to 2% on a solids by weight per solid content of the recycled pulp, more preferably from 0.03 to 1.5%. 蛍光失活剤の添加量が多くても蛍光除去効果は頭打ちであり、また、多すぎるとパルプの白色度が低下する傾向がある一方で、蛍光失活剤が少なすぎると、効果が不十分である。 Fluorescent removal effect even much amount of fluorescent deactivating agent is peaked, and if too much while brightness of the pulp tends to decrease, the fluorescence quencher is too small, the effect is insufficient it is. 特に、例えば5層の場合など、表下層及び/又は裏下層に含有される再生パルプに添加することが好ましい。 In particular, for example, when a five-layer, it is preferably added to recycled pulp to be contained in Tables lower layer and / or lower back. 表層あるいは裏層に近い内層に存在する蛍光染料を失活させることで、再生パルプ由来の蛍光染料の悪影響をより効率良く抑えることができると考えられる。 By deactivating the fluorescent dye present in the inner layer close to the surface layer or backing layer, it is believed to be able to suppress more efficiently the deleterious effects of fluorescent dye from recycled pulp.

蛍光失活剤を再生パルプに添加するには、再生パルプの製造後が好ましい。 In adding a fluorescent quencher the recycled pulp after the production of recycled pulp is preferable. 本発明では蛍光失活剤のマスキング作用が発揮されることで、蛍光強度が低下すると推測される。 In the present invention, by masking the action of the fluorescent quenching agent is exhibited, the fluorescence intensity is presumed to decrease. 再生パルプの製造前あるいは製造中に添加すると、その処理工程で水と一緒に流出したり、攪拌などによりパルプ繊維に十分に密着しないと考えられる。 The addition before production of recycled pulp or during production, or flows out with water at the processing step, it would not sufficiently adhere to the pulp fibers by such agitation.

(抄紙方法) (Papermaking method)
本発明のはがき用紙の製造方法は特に限定されるものでなく、各層の紙料をそれぞれ調製し、例えば長網型湿式抄紙機により各層を抄き合わせて多層構造とすることによって得ることができる。 Method of manufacturing postcard paper of the invention is not limited in particular, the stock of each layer were prepared, respectively, can be obtained by a multilayer structure combined paper making each layer by, for example, Fourdrinier type wet paper machine . また、多層ヘッドボックスから各層の紙料をそれぞれ噴射して多層抄きしてもよい。 It is also possible to paper making multilayer with each injection the stock of each layer of a multilayer headbox. 抄紙機としては上記の他、ツインワイヤー型抄紙機、円網抄紙機、短網抄紙機等が挙げられる。 The paper machine in addition to the above, a twin wire paper machine, cylinder paper machine, a short net paper machine or the like.

本発明では、多層構造の内部結合強度を高めるために、澱粉その他の接着剤を各層間に塗布することや、紙力増強剤の配合を行ってもよい。 In the present invention, in order to increase the internal bond strength of the multilayer structure, and applying a starch other adhesives between the layers may be performed formulation of paper strength agent. 但し、リサイクル時の離解性の観点から、内部結合強度は高すぎないことが望ましい。 However, from the viewpoint of defibration properties during recycling, it is desirable internal bond strength not too high. 本発明においては、JAPAN TAPPI No. In the present invention, JAPAN TAPPI No. 18−1に沿った測定値として、500KPa未満が好ましく、450KPa以下がより好ましく、さらに好ましくは400KPa以下である。 As measurements along 18-1, preferably less than 500 KPa, more preferably at most 450 kPa, more preferably not more than 400 kPa. あるいは、JAPAN TAPPI No. Alternatively, JAPAN TAPPI No. 18−2に沿った測定値として、1650KPa未満が好ましく、より好ましくは1600KPa以下である。 As measurements along 18-2, preferably less than 1650 kPa, more preferably not more than 1600 kPa. このような範囲の内部結合強度を有する多層構造の紙を得る方法としては、例えば、澱粉や接着剤を塗布する層間としない層間とを設ける、紙力増強剤を配合する層としない層を設けることなどが挙げられるが、これに限定されるものではない。 As a method for obtaining a sheet of a multilayer structure having an internal bond strength of this range, for example, provided with an interlayer without an interlayer of applying starch or adhesive, a layer which is not a layer blended paper strength agent it like, but not limited thereto.

また、はがき用紙サイズに裁断する際の紙粉発生や、印刷時または自動区分機処理時の紙剥けを防止するために、紙が有する内部結合強度として、JAPAN TAPPI No. Furthermore, paper dust generation and the time of cutting the postcard paper size, in order to prevent picking paper in printing or during automatic sorter process, as internal bond strength of paper has, JAPAN TAPPI No. 18−1に沿った測定値において300KPa以上、JAPAN TAPPI No. 300KPa above the measurements along 18-1, JAPAN TAPPI No. 18−2に沿った測定値において1300KPa以上であってもよい。 It may be more 1300KPa in measurements along 18-2.

(坪量) (Basis weight)
はがき用紙の坪量としては180〜200g/m であることが望ましい。 It is desirable as the basis weight of the postcard paper is 180-200 g / m 2. 抄き合わせにおける各層の坪量範囲は、本発明の効果を損なわない範囲で調整が可能であるが、表層および裏層の坪量は、各々20〜60g/m であることが好ましく、25〜50g/m であることが更に好ましい。 The basis weight range of each layer in alignment paper making is susceptible adjusted within a range not to impair the effects of the present invention, the basis weight of the surface layer and the back layer is preferably each 20 to 60 g / m 2, 25 further preferably to 50 g / m 2. 表層、裏層の坪量が低すぎると、再生パルプ由来の蛍光強度が高くなる懸念があり、一方、表層および裏層の坪量が高すぎる場合、蛍光強度やダートの点では良好だが、表層、裏層に用いられる化学パルプの量が多くなり、コスト的にも環境的にも望ましくない。 Surface layer, the basis weight of the backing layer is too low, there is a concern that the fluorescence intensity derived from the recycled pulp is increased, whereas, if the basis weight of the surface layer and the back layer is too high, but good in terms of fluorescence intensity or dirt, the surface layer , the more the amount of chemical pulp to be used in the backing layer, undesirable environmentally in cost.

内層の坪量は、60〜160g/m 程度が好ましい。 The basis weight of the inner layer is about 60 to 160 / m 2 is preferred. また4層以上(内層が2層以上)の抄き合わせで用紙を製造する場合は、各層の坪量は30〜80g/m であることが更に好ましい。 When manufacturing a paper in The paper making alignment of four or more layers (or inner two layers), the basis weight of each layer is more preferably 30 to 80 g / m 2. 内層の坪量が低すぎると、再生パルプの配合率を高く出来ず、一方内層の坪量が高すぎると、表層、裏層の坪量が低くなるため、再生パルプ由来の蛍光強度が高くなり、宛先情報バーコードの読取適性等に問題が生じるおそれがある。 If the basis weight of the inner layer is too low, it can not increase the blending ratio of recycled pulp, whereas when the basis weight of the inner layer is too high, the surface layer, because the basis weight of the backing layer is low, the fluorescence intensity derived from the recycled pulp is high , there is a possibility that problems in reading aptitude of the destination information bar code may occur.

(填料) (Filler)
また、本発明のはがき用紙には、填料を含有しても良い。 Further, the postcard paper of the invention may contain a filler. 特に、不透明度を高めるため、表層および/又は裏層は填料を含有することが好ましい。 In particular, to increase the opacity, surface and / or back layer preferably contains a filler. 填料の種類は特に制限されないが、例えば、重質炭酸カルシウムや軽質炭酸カルシウムなどの炭酸カルシウム、炭酸カルシウム−シリカ複合物、酸化チタン、クレー、シリカ、タルク、カオリン、焼成カオリン、デラミカオリン、炭酸マグネシウム、炭酸バリウム、酸化亜鉛、酸化珪素、非晶質シリカ、水酸化アルミニウム、水酸化カルシウム、水酸化マグネシウム、水酸化亜鉛、酸化チタン、ベントナイトなどの無機填料;尿素−ホルマリン樹脂、ポリスチレン樹脂、メラミン樹脂、フェノール樹脂、微小中空粒子等の有機填料;を単独または適宜2種類以上を組み合わせて使用することができる。 The type of filler is not particularly limited, for example, calcium carbonate such as heavy calcium and precipitated calcium carbonate, calcium carbonate - silica composite, titanium oxide, clay, silica, talc, kaolin, calcined kaolin, delaminated kaolin, magnesium carbonate , barium carbonate, zinc oxide, silicon oxide, amorphous silica, aluminum hydroxide, calcium hydroxide, magnesium hydroxide, zinc hydroxide, inorganic fillers such as titanium oxide, bentonite; urea - formalin resin, polystyrene resin, a melamine resin , phenolic resins, organic fillers such as fine hollow particles; a may be used singly or in combinations of appropriate two or more. また、製紙スラッジや脱墨フロス等を原料とした再生填料も使用することができる。 The reproduction filler in which the paper sludge or deinked froth like as a raw material can also be used. 酸性抄紙の場合は、前記填料から、酸溶解性のものを除いた填料が使用され、その単独または適宜2種類以上を組み合わせて使用される。 For acidic papermaking, from the filler, filler, excluding those acid-soluble are used, are used in combination thereof alone or optionally two or more.

本発明では中でも、リサイクル可能でかつ紙の不透明度や白色度を比較的低コストで向上させることができるため、炭酸カルシウムを使用して紙面pHが6.0〜9.5となるように中性抄紙することが好ましい。 Above all in the present invention, it is possible to improve recyclable and relatively inexpensive opacity and whiteness of the paper, medium as paper pH of 6.0 to 9.5 using calcium carbonate it is preferable that the sex paper. 填料の含有量は、少なすぎると不透明度に劣り、多すぎるとオフセット印刷時や断裁時に紙粉が発生しやすいことなどから、対パルプ絶乾質量あたり1〜10質量%が好ましい。 The content of filler is too small poor opacity, is too large or the like to the paper dust at the time or cutting offset printing tends to occur, 1-10 wt% per pulp absolute dry mass is preferred. なお、ここでいう填料の含有量とは、再生パルプに由来するもの、および抄紙の際に添加されたものなどいずれも含む。 Here, the content of filler to say, those derived from recycled pulp, and any such include those added during the papermaking.

(製紙用薬品) (Paper chemicals)
また、本発明では必要に応じて各種の製紙用薬品を添加することができる。 Further, it is possible to add chemicals for various paper as needed in the present invention. 具体的には、ポリアクリルアミド系高分子、ポリビニルアルコール系高分子、カチオン性澱粉、各種変性澱粉、尿素・ホルマリン樹脂、メラミン・ホルマリン樹脂などの内添紙力増強剤;ロジン系サイズ剤、AKD系サイズ剤、ASA系サイズ剤、石油系サイズ剤、中性ロジンサイズ剤などの内添サイズ剤;などを挙げることができる。 Specifically, polyacrylamide polymers, polyvinyl alcohol polymers, cationic starch, various modified starches, internal paper strength agent such as urea-formalin resin, melamine-formalin resin; rosin sizing agent, AKD-based sizing agents, ASA-based sizing agents, petroleum sizing agent, internal sizing agents, such as neutral rosin sizing agent; and the like. また、歩留剤、濾水性向上剤、凝結剤、硫酸バンド、ベントナイト、シリカ、染料、消泡剤、紫外線防止剤、退色防止剤、ピッチコントロール剤、スライムコントロール剤などを用いることができる。 Further, it FuTomezai, drainage aids, coagulant, aluminum sulfate, bentonite, silica, dyes, antifoaming agents, anti-UV agents, anti-fading agents, pitch control agents, be used as the slime control agent.

(表面処理) (surface treatment)
また、本発明のはがき用紙には、必要に応じて、表面および/又は裏面に表面処理剤を塗布することができる。 Further, the postcard paper of the invention may be applied if necessary, the surface treatment agent surface and / or on the back. 表面処理剤の種類や組成は、特に限定はないが、表面強度の向上を目的とした水溶性高分子物質としては、生澱粉、酸化澱粉、エステル化澱粉、カチオン化澱粉、酵素変性澱粉、アルデヒド化澱粉、ヒドロキシエチル化澱粉、ヒドロキシプロピル化澱粉などの澱粉;カルボキシメチルセルロース、ヒドロキシエチルセルロース、メチルセルロースなどのセルロース誘導体;ポリビニルアルコール、カルボキシル変性ポリビニルアルコールなどの変性アルコール;スチレンブタジエン共重合体、ポリ酢酸ビニル、塩化ビニル−酢酸ビニル共重合体、ポリ塩化ビニル、ポリ塩化ビニリデン、ポリアクリル酸エステル、ポリアクリルアミドなどを単独または併用する。 The type and composition of the surface treatment agent is not particularly limited, as the water-soluble polymer for the purpose of improving surface strength, raw starch, oxidized starch, esterified starch, cationized starch, enzyme-modified starches, aldehyde starch, hydroxyethyl starch, starch, such as hydroxypropylated starch; carboxymethyl cellulose, hydroxyethyl cellulose, cellulose derivatives such as methyl cellulose; polyvinyl alcohol, denatured alcohol such as carboxyl modified polyvinyl alcohol; styrene-butadiene copolymer, polyvinyl acetate, vinyl chloride - vinyl acetate copolymer, polyvinyl chloride, polyvinylidene chloride, polyacrylic acid esters, etc., alone or in combination polyacrylamide. また、本発明では筆記適性あるいはプリンターでの印字適性のため、ステキヒトサイズ度が250〜600秒であることが好ましく、吸水抵抗性を高めるために、前記の水溶性高分子物質の他に、スチレンアクリル酸、スチレンマレイン酸、オレフィン系化合物など表面サイズ剤を併用塗布してもよい。 Moreover, since the printing suitability in writing aptitude or printer in the present invention, it is preferable that Stöckigt sizing degree of 250 to 600 seconds, in order to increase the water resistance, in addition to the water-soluble polymeric substance, styrene acrylate, styrene-maleic acid may be a combination coating surface sizing agent such as olefinic compounds. 表面処理剤の塗布量は特に制限されず、通常、両面当たり0.5〜5g/m 程度である。 The coating amount of the surface treatment agent is not particularly limited, usually, a double-sided per 0.5 to 5 g / m 2 approximately. また、水溶性高分子物質と表面サイズ剤からなる表面処理剤を塗布する場合、水溶性高分子物質と表面サイズ剤との混合比率は公用の範囲で行えばよい。 In addition, when applying the surface treating agent comprising a water-soluble polymer and surface sizing agent, mixing ratio of the water-soluble polymer and surface sizing agent may be performed in a range of public.

前述した表面処理剤を塗布する場合、塗工装置は一般に使用されるものを用いることができ、例えば、2ロールサイズプレス、ゲートロールコーター、ロッドメタリングサイズプレス、ブレードコーター、バーブレードコーター、エアナイフコーター、カーテンコーター、スプレーコーターなどをオンマシンまたはオフマシンで用いることができる。 When applying a surface treatment agent foregoing, the coating apparatus can be used as is commonly used, for example, a 2-roll size press, gate roll coater, rod metering size press, a blade coater, a bar blade coater, air knife coater, a curtain coater, a spray coater can be used on-machine or off-machine. さらに、本発明においては紙表面にカレンダー処理を施すこともできる。 Further, in the present invention may be subjected to a calender treatment to the paper surface. カレンダー装置の種類と処理条件は特に限定はなく、金属ロールから成る通常のカレンダーやソフトニップカレンダー、高温ソフトニップカレンダーなどの公用の装置を適宜選定し、品質目標値に応じて、これらの装置の制御可能な範囲内で条件を設定すればよい。 Type and process conditions of calendering device is not particularly limited, and usual calendar or soft nip calender comprising a metal roll, appropriately selected and commonly used devices such as a hot soft nip calender, in accordance with the quality target value, of these devices it may be set condition in controllable range.

また、本発明のはがき用紙には、必要に応じて、印刷適性を高めるために表面および/又は裏面に顔料を含有する塗工層を設けることもできる。 Further, the postcard paper of the invention, if desired, can be provided a coating layer containing a pigment on the surface and / or back surface to enhance printability. また、インクジェットプリンター適性を向上する方法として、吸油性填料や内添サイズ剤の内添や、染料定着剤としてカチオン性樹脂等を塗布することなどが挙げられる。 Further, as a method of improving the ink-jet printer suitability, or internal addition of oil-absorbing fillers and internal sizing agents, and applying a cationic resin such as a dye fixing agent.

(他の用途) (Other uses)
本発明の紙は、はがき用紙以外にも、印刷用紙、情報用紙、新聞用紙、包装用紙等に使用することができる。 The paper of this invention, in addition to postcard paper, printing paper, information paper, can be used newsprint, packaging paper or the like. 坪量等の諸物性や製造方法などは、各用途に応じて適宜設定すればよい。 Etc. Physical properties and production method of the basis weight, etc., may be appropriately set according to each application.

以下、実施例に基づいて本発明を更に詳細に説明する。 Hereinafter, the present invention will be described more specifically with reference to Examples. なお、本発明はこれらの実施例に制限されるものではない。 The present invention is not limited to these examples. 実施例及び比較例において部及び%は固形分質量部及び固形分質量%を表す。 Parts and percentages in the examples and comparative examples represent solid weight parts and wt-% solids. なお、以下の実施例は5層の抄き合わせであり、各層を順に「表層」「表下層」「中層」「裏下層」「裏層」で記載した。 The following examples are alignment paper making five layers, described in turn the layers' surface, "" Tables lower "," middle "," lower back "," back layer ".

[再生パルプの製造] Production of recycled pulp]
(DIP−A) (DIP-A)
高濃度パルパーに、新聞古紙:雑誌古紙:ケント古紙:チラシ古紙=65:16:11:8の割合で古紙を投入した。 A high concentration pulper, newspaper paper: magazine paper: Kent paper: Flyers paper = 65: 16: 11: waste paper was charged with 8 ratio. ここに薬品を加えてパルプ濃度が15質量%となるように調整し、離解処理を行った。 Here the addition of chemicals was adjusted to a pulp concentration of 15 wt% was subjected to maceration processing. 使用薬品は、それぞれ対古紙質量に対する割合で苛性ソーダ2.0%、高級アルコール系脱墨剤0.2%を加えた。 Using chemicals, 2.0% sodium hydroxide at a rate for each pair paper mass, it was added 0.2% higher alcohol deinking agent. 続いて、粗選スクリーン、フローテーター、精選スクリーン、ディスパーザーを経てDIP(脱墨再生パルプ)を製造した。 Then, to produce a DIP (deinked recycled pulp) through roughing screen, flotation, selective screen, the disperser. このDIPにさらにホルムアミジンスルフィン酸(FAS)を添加し、ディスパーザーで分散処理を行った後、水で希釈し、高速ワイヤーベルト式脱水機(DNTウォッシャー)で洗浄することで、DIP−Aを得た。 Further added formamidine sulfinic acid in the DIP (FAS), after dispersion treatment with a disperser, diluted with water, followed by washing with a high speed wire belt dehydrator (DNT washer), the DIP-A Obtained. DIP−Aの白色度は70%、灰分は3%、0.1mm以下の微細繊維量は1.4%であった。 The whiteness of the DIP-A 70%, ash content of 3% or less of the fine fiber content 0.1mm was 1.4%.

(DIP−B) (DIP-B)
ホルムアミジンスルフィン酸(FAS)添加以降の工程を行わない以外は、DIP−Aと同様にしてDIP−Bを得た。 Except that not performed formamidine sulfinic acid (FAS) after addition step, to obtain a DIP-B in the same manner as DIP-A. DIP−Bの白色度は55%、灰分は12%、0.1mm以下の微細繊維量は10%であった。 The whiteness of the DIP-B 55%, ash content 12%, less fines amount 0.1mm was 10%.

[実施例1] [Example 1]
(表層及び裏層) (Surface layer and the back layer)
カナディアンスタンダードフリーネス(CSF)400mlに叩解したLBKP100部に対して、填料として炭酸カルシウムを2部、内添サイズ剤を0.4部、歩留まり剤を0.1部、硫酸バンドを2部添加してスラリーを調製した。 Against LBKP100 parts beaten to Canadian Standard Freeness (CSF) 400 ml, 2 parts of calcium carbonate as a filler, 0.4 parts of an internal sizing agent, 0.1 parts of retention aid, is added 2 parts of aluminum sulfate the slurry was prepared.
(表下層、裏下層) (Table lower, lower back)
CSF400mlのLBKP50部と、白色度70%の再生パルプ(以下DIP−Aとする。)50部とを混合し、内添サイズ剤を0.75部、硫酸バンドを2.5部添加してスラリーを調製した。 And LBKP50 parts of CSF400ml, whiteness 70% recycled pulp (hereinafter referred to as DIP-A.) And 50 parts were mixed, 0.75 parts of the internal sizing agent, the slurry was added 2.5 parts of aluminum sulfate It was prepared.
(中層) (Middle)
白色度70%の再生パルプ(DIP−A)を100部に対し内添サイズ剤として0.75部、硫酸バンドを2.5部添加してスラリーを調製した。 0.75 parts of 70% whiteness reproduction pulp (DIP-A) as an internal sizing agent to 100 parts to prepare a slurry by adding 2.5 parts of aluminum sulfate.
(抄き合わせ) (Paper making alignment)
上記3種類の紙料スラリーを、表層=28g/m 、表下層・中層・裏下層=各44g/m 、裏層=30g/m となるように長網抄紙機で抄紙し、湿紙の状態で抄き合わせて乾燥し、坪量190g/m となるように原紙を抄造した。 The above three kinds of stock slurry, and paper making the surface layer = 28 g / m 2, Table lower-middle-lower back = each 44 g / m 2, the back layer = 30 g / m 2 and composed as Fourdrinier paper machine, wet dried combined paper making in the form of paper, and papermaking base paper so that the basis weight of 190 g / m 2. 抄き合わせに際し、裏層と裏下層との間を除く各層間には、顆粒澱粉の2.3%水溶液を塗布量1g/m となるようにスプレー塗布した。 Upon registration paper making, the respective layers except between the backing layer and the lower back, and spray coated to a 2.3% aqueous solution of granular starch coating weight 1 g / m 2. この原紙に2ロールサイズプレスでポリビニルアルコールを両面で1.8g/m 塗布し、ベック平滑度が30秒となるようにカレンダー処理を行って、はがき用紙を得た。 Polyvinyl alcohol 2-roll size press in the base paper 1.8 g / m 2 was coated on both sides, by performing a calender treatment so as Bekk smoothness of 30 seconds, to obtain a postcard paper.

[実施例2] [Example 2]
実施例1の表下層、裏下層のパルプスラリーにおいて、LBKP50部と再生パルプ(DIP−A)50部とに代えて、それぞれ再生パルプ(DIP−A)100部を使用した以外は、実施例1と同様にしてはがき用紙を得た。 Table underlayer of Example 1, the lower back of the pulp slurry, except that in place of the LBKP50 parts of recycled pulp (DIP-A) 50 parts, were used, respectively regenerated pulp (DIP-A) 100 parts Example 1 to obtain a postcard paper in the same manner as.
[実施例3] [Example 3]
実施例1において、表下層、裏下層のそれぞれのパルプスラリー調製時に、蛍光失活剤として芳香族カルボン酸・アミン縮合物(里田加工FQ−50)を、LBKPおよび再生パルプ(DIP−A)とを合わせた対パルプ当たり0.05%添加(DIP−Aに対し0.1%添加に相当)した以外は、実施例1と同様にしてはがき用紙を得た。 In Example 1, Table lower, when each of the pulp slurry preparation of the backing layer, an aromatic carboxylic acid amine condensates as a fluorescent deactivating agent (Satoda processing FQ-50), and LBKP and recycled pulp (DIP-A) except for adding 0.05% per pulp the combined (corresponding to the addition of 0.1% relative to DIP-a) was obtained the postcard paper in the same manner as in example 1.

[実施例4] [Example 4]
実施例1の中層のパルプスラリーにおいて、再生パルプ(DIP−A)100部に代えて、白色度55%の再生パルプ(DIP−B)100部を使用した以外は、実施例1と同様にしてはがき用紙を得た。 In pulp slurry intermediate of Example 1, recycled pulp (DIP-A) in place of 100 parts, except for using whiteness 55% recycled pulp (DIP-B) 100 parts, the same procedure as in Example 1 to obtain a postcard paper.

[比較例1] [Comparative Example 1]
CSF400mlのLBKP60部と、再生パルプ(DIP−A)40部とを混合し、填料として炭酸カルシウムを5部、内添サイズ剤を1.4部、硫酸バンドを2部添加して紙料スラリーを調製した。 And LBKP60 ​​parts CSF400ml, was mixed with recycled pulp (DIP-A) 40 parts, 5 parts of calcium carbonate as a filler, 1.4 parts of the internal sizing agent, the stock slurry was added 2 parts of aluminum sulfate It was prepared. この紙料スラリーを、長網抄紙機で坪量190g/m となるように抄紙し、サイズプレスでポリビニルアルコールを1.8g/m 塗布し、ベック平滑度が30秒となるようにカレンダー処理を行って、はがき用紙を得た。 The stock slurry was paper so that the basis weight of 190 g / m 2 in Fourdrinier, polyvinyl alcohol 1.8 g / m 2 was applied in the size press, calender as Bekk smoothness of 30 seconds processing is performed to obtain a postcard paper.

[比較例2] [Comparative Example 2]
再生パルプ(DIP−A)40部に代えて、白色度55%の再生パルプ(DIP−B)40部を使用した以外は、比較例1と同様にしてはがき用紙を得た。 Recycled pulp in place of (DIP-A) 40 parts, except for using whiteness 55% recycled pulp (DIP-B) 40 parts, to obtain a postcard paper in the same manner as in Comparative Example 1.

[比較例3] [Comparative Example 3]
実施例2の表下層、中層、裏下層のパルプスラリーにおいて、再生パルプ(DIP−A)100部に代えて、再生パルプ(DIP−B)100部をそれぞれ使用した以外は、実施例2と同様にしてはがき用紙を得た。 Table underlayer of Example 2, the middle layer, in lower back pulp slurry, instead of the 100 parts of recycled pulp (DIP-A), except for using recycled pulp (DIP-B) 100 parts, respectively, similarly to Example 2 to obtain a postcard paper to.

[評価方法] [Evaluation method]
各実施例および比較例で得られたはがき用紙の評価を、以下に示す方法により行った。 The evaluation of the postcard paper obtained in Examples and Comparative Examples were performed by the following methods. 評価結果を表1にまとめて示す。 The evaluation results are shown in Table 1.

<白色度> <Whiteness>
パルプおよびはがき用紙について、JIS P 8148に準じて測定した。 For pulp and paper postcard, it was measured in accordance with JIS P 8148.
<蛍光強度> <Fluorescence intensity>
JIS P 8148に準じて、紫外線領域を含む光を照射した時の白色度(X)と紫外線を含まない光を照射した時の白色度(Y)をそれぞれ測定し、両者の差(X−Y)により蛍光強度を求めた。 In accordance with JIS P 8148, the whiteness when irradiated with light containing ultraviolet region (X) and whiteness when irradiated with light containing no ultraviolet (Y) was measured, respectively, both the difference (X-Y It was determined the fluorescence intensity by). 値が小さいほど蛍光強度が小さいことを示す。 The smaller the value, the fluorescence intensity is low.
<チリ・ダート> <Chile Dart>
目視で評価を行い次の基準で示した。 Evaluated visually shown by the following criteria.
◎ チリ・ダートが目立たない ○ チリ・ダートがほとんど目立たない △ チリ・ダートがやや目立つ × チリ・ダートが多い<DIP微細繊維量> ◎ Chile Dirt is not noticeable ○ Chile Dirt is hardly noticeable △ Chile is somewhat conspicuous × often Chile Dart Dart <DIP fine fiber content>
Kajaanisy社製パルプ分析装置「FiberLab」を用いて、長さ平均算出時の繊維長分布における0.1mm以下の頻度を測定した。 Kajaanisy manufactured pulp analyzer using "FiberLab" was measured less frequently 0.1mm in the fiber length distribution of the time lengths averaging.
<内部結合強度> <Internal bond strength>
JAPAN TAPPI No. JAPAN TAPPI No. 18−1およびNo. 18-1 and No. 18−2に沿って測定した。 It was measured along the 18-2. 前者はZ軸方向引張り、後者はインターナルボンドを表す。 The former tensile Z-axis direction, the latter represents the Internal Bond.
<自動区分機処理試験> <Automatic sorting machine processing test>
自動区分機による処理試験の結果を下記に示す。 The results of processing test by an automatic sorting machine below.
○ 良好 △ やや不良 × 不良 ○ good △ slightly bad × bad

表1中の*印の白色度60%以上は、再生パルプに対する白色度60%以上の再生パルプの割合である。 Table 1 in asterisk whiteness 60% is the percentage of whiteness of 60% or more of recycled pulp against recycled pulp.

表1より、実施例1〜4のはがき用紙は白色性に優れ、蛍光強度が低く、チリやダートも問題ないレベルであり、自動区分機処理の結果が良好であった。 From Table 1, postcard paper of Example 1-4 is excellent in whiteness, fluorescence intensity is low, dust or dirt is also no problem, the result of an automatic sorting machine process was good. 中でも、蛍光失活剤を添加した実施例3は、蛍光強度がより低下した。 Among them, Example 3 with the addition of fluorescent quencher, the fluorescence intensity was reduced more. 一方、単層抄きで白色度の高い再生パルプを用いた比較例1では、蛍光強度が高く再生パルプ由来の蛍光染料の影響が強く、チリやダートも増加した。 On the other hand, in Comparative Example 1 using high brightness recycled pulp in a single layer paper making, strong influence of fluorescent dye from high recycled pulp fluorescence intensity, also increased dust and dirt. さらに、単層抄きで白色度の低い再生パルプを用いた比較例2では、白色性に劣り、蛍光強度が高く、チリやダートも増加した。 In Comparative Example 2 using a low whiteness recycled pulp in a single layer paper making, poor whiteness, fluorescence intensity is high, and also increased dust and dirt. また、多層構造であるものの白色度の低い再生パルプを用いた比較例3では、チリやダートが増加した。 In Comparative Example 3 using a white low degree of recycled pulp of those a multi-layer structure, dust or dirt is increased.

本発明の紙は、古紙を活用した環境に優しい郵便はがきとして使用することができる。 The paper of this invention can be used as a friendly postcards environment utilizing waste paper.

Claims (5)

  1. パルプを主原料とした3層以上の多層構造を有し、表層と裏層との間に形成された内層のうちの少なくとも1つの層が再生パルプを含有する層である紙であって、 表層及び裏層が共に再生パルプを含有せず、表層と裏層の坪量は各々20〜60g/m であり、全パルプ固形分に対し再生パルプを20質量%以上含有し、 さらに、該再生パルプを含有する層のうちの少なくとも1つの層は、その固形分あたり固形分質量で0.01〜2%の蛍光失活剤を含有し、かつ、前記再生パルプの全固形分のうち白色度が60%以上である再生パルプを50質量%以上含有するはがき用紙。 It has three or more layers structure in which the pulp as the main raw material, at least one layer of the inner layer which is formed between the surface layer and the backing layer is a paper as a layer containing a recycled pulp, the surface layer and back layer contains no recycled pulp together, the basis weight of the surface layer and the back layer are each 20 to 60 g / m 2, relative to the total pulp solids containing recycled pulp least 20 mass%, furthermore, the reproduction at least one of the layers containing the pulp contains a fluorescent quencher of 0.01% to 2% in the solid content per solid content, and the whiteness of the total solid content of the recycled pulp postcard paper but containing recycled pulp is 60% or more than 50 wt%.
  2. 前記はがき用紙の坪量が180〜200g/m であり、前記内層を合計した坪量が60〜160g/m である請求項1に記載のはがき用紙。 Wherein a postcard basis weight of 180-200 g / m 2 paper, postcard paper of claim 1 having a basis weight which is the sum of the inner layer is 60 to 160 / m 2.
  3. 3〜5層の多層構造である請求項1又は2に記載のはがき用紙。 Postcard paper of claim 1 or 2 which is a multilayer structure of 3 to 5 layers.
  4. JAPAN TAPPI No. JAPAN TAPPI No. 18−1で規定される内部結合強度が500KPa未満である請求項1〜3のいずれか1項に記載のはがき用紙。 Postcard paper according to any one of claims 1 to 3 internal bond strength defined by 18-1 is less than 500 KPa.
  5. JAPAN TAPPI No. JAPAN TAPPI No. 18−1で規定される内部結合強度が300KPa以上である請求項1〜4のいずれか1項に記載のはがき用紙。 Postcard paper according to any one of claims 1 to 4 internal bond strength defined by 18-1 is equal to or greater than 300 KPa.
JP2010156990A 2009-07-09 2010-07-09 Paper containing recycled pulp Active JP5775271B2 (en)