JP5720992B2 - Method of manufacturing a thermal transfer sheet and the information recording medium using the same - Google Patents

Method of manufacturing a thermal transfer sheet and the information recording medium using the same

Info

Publication number
JP5720992B2
JP5720992B2 JP2011053313A JP2011053313A JP5720992B2 JP 5720992 B2 JP5720992 B2 JP 5720992B2 JP 2011053313 A JP2011053313 A JP 2011053313A JP 2011053313 A JP2011053313 A JP 2011053313A JP 5720992 B2 JP5720992 B2 JP 5720992B2
Authority
JP
Grant status
Grant
Patent type
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2011053313A
Other languages
Japanese (ja)
Other versions
JP2012187818A (en )
Inventor
東 峰 子 伊
東 峰 子 伊
Original Assignee
大日本印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Grant date

Description

本発明は、熱転写シートに関し、より詳細には、文字情報と画像情報とが同一面上に記録された、IDカードやキャッシュカード等の情報記録体を製造する際に好適に使用される文字情報記録用の熱転写シートに関する。 The present invention relates to a thermal transfer sheet, and more particularly, character information and the character information and image information recorded on the same surface, it is suitably used in manufacturing the information recording medium such as ID card or cash card on the thermal transfer sheet for recording.

身分証明書等のIDカードや銀行等のキャッシュカードにおいて、個別認識できるように、その一方の面に、人物の顔写真等の画像情報とその人物の住所や名前等の文字情報とが記録されたものが使用されている。 In cash card such as an ID card or bank identification certificate, etc., individual recognition as possible to, on one surface thereof, the image information of the face photograph, etc. of the person and the character information of the address and the name, etc. of the person is recorded is being used ones were. このようなIDカードや銀行等のキャッシュカード等の情報記録体は、プラスチック等のカードの一方の面に画像情報と文字情報とを記録することにより製造されている。 Such ID card or bank information recording medium such as a cash card or the like is manufactured by recording the image information and character information on one surface of the card, such as plastics. このような情報記録体は、画像情報の鮮明性や文字情報を印字する際の簡便性を考慮して、熱転写シートを用いて製造されている。 Such information recording medium, in consideration of the convenience at the time of printing the clearness and character information of the image information are made using the thermal transfer sheet. 例えば、基材上にイエロー、マゼンタおよびシアン等の色材層を設けた熱転写シートを用いて、カード上にカラーの人物画像を記録し、次いで、ブラックの色材層を設けた熱転写シートを用いて、基材上の人物画像を形成した以外の部分に文字等を記録することにより製造されている。 For example, yellow on a substrate, using a thermal transfer sheet provided with a colorant layer of the magenta and cyan or the like, records the human image of the color on the card, then, using a thermal transfer sheet provided with a colorant layer of black Te are manufactured by recording characters or the like on a portion other than the formation of the human image on the substrate. 熱転写シートを用いて得られる画像は、中間色の再現性や階調性に優れ、フルカラー写真画像に匹敵する高品質な画像を形成できるため、特に身分証明書等のIDカードや銀行等のキャッシュカードのような、記録画像により個別認識を必要とするような情報記録体においては、熱転写シートを用いて製造することが一般的となっている。 Image obtained using the thermal transfer sheet is excellent in reproducibility and gradation of intermediate colors, it is possible to form a high-quality image comparable to full color photographic images, in particular identification etc. ID card or bank like cash cards such as, in the information recording medium that requires a separate recognition by the recording image, be produced using a thermal transfer sheet has become common.

近年、プリンタの高速化に伴い、より低いエネルギーで画像の濃淡を表現でき、かつ優れた画像耐久性を実現できる、いわゆるポストキレート方式による熱転写方法が提案されている。 In recent years, with the speeding up of the printer, it can represent the contrast of the image at a lower energy, and can realize excellent image durability, thermal transfer method according to a so-called post-chelate system has been proposed. ポストキレート方式とは、受像層中に特定の金属イオン化合物を含有させた被記録体と、その特定金属イオンとキレート錯体を形成し得る染料を色材層とした熱転写シートとを用いて、熱転写後に、それらを反応させてキレート錯体を形成させることにより画像を形成する方法である(例えば、特開平4−89292号公報や特開平4−292989号公報等)。 The post chelate method using a recording material which contains a specific metal ion compound in the image-receiving layer, was the thermal transfer sheet of dye capable of forming the specific metal ion chelate complex color material layer, a thermal transfer later, they were reacted is a method of forming an image by forming a chelate complex (e.g., JP-a-4-89292 Publication and Japanese Patent 4-292989 Patent Publication). このポストキレート方式により形成された画像は、染料の褪色や滲みが生じにくく耐光性にも優れることから、上記したようなカード類等の情報記録体にも適用され始めている。 This post chelate type image formed by is the fact that excellent in discoloration or bleeding occurs hardly lightfastness of dyes, began to be applied to the information recording medium such as a card, such as described above.

ポストキレート方式を用いて画像情報を情報記録体に形成する場合、色材を熱転写シートから情報記録体の受像層へ移行させる際の熱エネルギーだけでは、受像層中の金属イオン化合物と色材との反応が不十分な場合があり、良好な色調が得られない場合がある。 When forming the information recording medium image information by using a post-chelate type, only the thermal energy at the time of shifting the colorant from a thermal transfer sheet to the information recording medium of the image receiving layer includes a metal ion compounds of the image receiving layer and the colorant of may reaction is insufficient, there may not satisfactory color tone is obtained. 特にプリンタの高速化により、熱転写時のエネルギーだけではキレート反応を十分に進めることができないという問題がある。 Particularly Faster printer, only the energy at the time of thermal transfer is a problem that can not be advanced sufficiently chelating reaction. この問題を解決するために、例えば特開2003−58847号公報には、画像情報と文字情報とを記録した後に、画像情報が記録された部分に透明保護転写箔を転写して、転写時の熱エネルギーにより、画像情報が記録された部分を再加熱してキレート反応を完全ならしめることが行われている。 To solve this problem, for example, JP 2003-58847 discloses, after recording the image information and character information, and transferring the transparent protective transfer foil in a portion where the image information is recorded, at the time of transfer by thermal energy, that makes it completely chelating reaction being carried out by reheating the portion where image information is recorded.

特開平4−89292号公報 JP 4-89292 discloses 特開平4−292989号公報 JP-4-292989 discloses 特開2003−58847号公報 JP 2003-58847 JP

しかしながら、プリンタの更なる高速化が希求されており、キレート反応を完全ならしめるための再加熱工程が高速化の障害となっていた。 However, higher speed of the printer has been desired, reheating step for makes it complete chelation reaction had become an obstacle to high speed. また、上記の特開2003−58847号公報に開示されている方法においては、図12に示すように、イエロー、マゼンタおよびシアンの各色材層を面順次の設けた熱転写シートを用いて、先ず画像情報部分を形成し、次いで、図13に示すような、ブラック色材層と透明保護転写箔とが面準位に設けられた熱転写シートを用いて、文字情報を画像形成部分以外の部分に形成した後に、画像形成部分に透明保護転写箔を転写することが行われていた。 Further, in the method disclosed in JP 2003-58847 publication described above, as shown in FIG. 12, with yellow, a thermal transfer sheet provided for each color material layers of magenta and cyan frame sequential, first image forming a information part, then, as shown in FIG. 13, black color material layer and the transparent protective transfer foil by using a thermal transfer sheet provided on a surface level, forming character information in a portion other than the image forming portion after, transferring the transparent protective transfer foil to the image forming portion has been performed. そのため、転写工程が複雑となりプリンタ装置自体を小型化することが困難であった。 Therefore, it is difficult to miniaturize the printer apparatus itself becomes complicated transfer process.

本発明者らは、先の出願(特願2010−140252号)において、ポストキレート熱転写方式により基材上に画像を形成し、次いで基材上の画像形成部分以外の部分に文字情報を熱転写により記録する際に、同時に画像形成部分を再加熱することにより、画像情報の画質を維持しつつプリンタ装置を高速化および小型化できる情報記録体の製造方法を提案している。 The present inventors have found that in the previous application (Japanese Patent Application No. 2010-140252), an image is formed on the substrate by the post-chelate thermal transfer method, followed by thermal transfer of character information in a portion other than the image forming portion on the substrate when recording, proposed by reheating the image forming portion, a method of manufacturing an information recording medium capable of high speed and compact printer device while maintaining the image quality of the image information at the same time. しかしながら、上記の再加熱は、文字情報記録用熱転写シートを用いて、画像情報がすでに記録された被記録体に熱転写する際のサーマルヘッド等の熱エネルギーにより行われるため、画像形成部分の受容層から色材が文字情報記録用熱転写シートに逆転写されてしまい、被記録体に形成した画像の発光効率が低下する場合がある。 However, the above reheating, using the character information recording thermal transfer sheet, the image information is already effected by thermal energy such as a thermal head at the time of thermal transfer to the recorded the recording medium, the receiving layer of the image forming portion colorant will be reverse transcribed into text information recording thermal transfer sheet from the sometimes luminous efficiency of the image formed on the recording medium is lowered.

今般、上記したようなポストキレート方式により被記録体上に画像を形成し、次いで基材上の画像形成部分以外の部分に文字情報を熱転写により記録したような情報記録体を製造する場合に、文字情報記録用の熱転写シートの、被記録体の画像形成部分に相当する部分にバリア層を設けておくことにより、上記のような文字情報記録時の熱転写による再加熱を行っても、画像形成部分の受容層から色材が文字情報記録用熱転写シートに逆転写されず、結果として、画像情報部分の優れた画質と、プリンタ装置の高速化および小型化とを両立させることができる、との知見を得た。 If now, the image formed on the recording medium by the post chelate method as described above, and then to produce the information recording medium, such as recording the character information by the thermal transfer to the portion other than the image forming portion on the substrate, the thermal transfer sheet of the character information recording, by providing a barrier layer in a portion corresponding to the image forming portion of the recording medium, even if the reheating by the character information recorded at the time of thermal transfer as described above, the image forming portion of the colorant from the receiving layer without being reverse-transcribed into text information recording thermal transfer sheet, as a result, good picture quality of the image information portion, it is possible to achieve both high-speed and miniaturization of the printer, and the findings were obtained. 本発明はかかる知見によるものである。 The present invention has been made based on such finding.

したがって、本発明の目的は、ポストキレート方式により被記録体上に画像を形成し、次いで基材上の画像形成部分以外の部分に文字情報を熱転写により記録したような情報記録体を製造する場合において、上記のような文字情報記録時の熱転写による再加熱を行っても、画像形成部分の受容層から色材が文字情報記録用熱転写シートに逆転写されないため、画像情報部分の優れた画質と、プリンタ装置の高速化および小型化とを両立させることができる文字情報記録用熱転写シートを提供することである。 Accordingly, an object of the present invention, when an image is formed on the recording medium by the post chelate system, then producing the information recording medium as recorded by thermal transfer of character information in a portion other than the image forming portion on the substrate in, even if the reheating by the character information recorded at the time of thermal transfer as described above, since the color material from the receiving layer of the image forming portions is not reverse transcribed into text information recording thermal transfer sheet, and excellent image quality of the image information portion is to provide a character information recording thermal transfer sheet capable of satisfying both high speed and miniaturization of the printer device.

また、本発明の別の目的は、上記の文字情報記録用熱転写シートを用いた情報記録体の製造方法を提供することである。 Another object of the present invention is to provide a method of manufacturing an information recording medium using the above-mentioned character information recording thermal transfer sheet.

本発明による文字情報記録用熱転写シートは、ポストキレート方式により画像形成された被記録体の同一面上に文字情報を記録するために用いられる熱転写シートであって、 Character information recording thermal transfer sheet according to the present invention is a thermal transfer sheet used for recording character information onto the same surface of the recording medium on which an image is formed by the post chelate system,
基材と、前記基材上の一部に設けられた色材層と、前記基材上の前記色材層が設けられていない部分に設けられたバリア層と、を少なくとも備え、 Comprising a substrate, a color material layer provided on a part of the substrate, a barrier layer in which the colorant layer is provided in a portion not provided on the substrate, at least,
前記バリア層が、前記被記録体上の画像情報が印画された部分と対応するように、パターニングされてなる、ことを特徴とするものである。 Said barrier layer is such that said image information on the recording medium correspond with the printing portion, formed by patterning, it is characterized in.

また、本発明の態様においては、前記バリア層がアクリル系樹脂からなることが好ましい。 In the embodiment of the present invention, it is preferable that the barrier layer is made of acrylic resin.

また、本発明の態様においては、前記基材がポリエチレンテレフタレートフィルムからなることが好ましい。 In the embodiment of the present invention, it is preferable that the substrate is made of polyethylene terephthalate film.

また、本発明の態様においては、前記基材上の、前記色材層および前記バリア層が設けられていない部分に、シアン染料層、マゼンタ染料層およびイエロー染料層が面順位に設けられていることが好ましい。 In the embodiment of the present invention, on the substrate, the portion where the color material layer and the barrier layer is not provided, the cyan dye layer, a magenta dye layer and a yellow dye layer is provided on a surface Position it is preferable.

また、本発明の別の態様による情報記録体の製造方法は、上記文字情報記録用熱転写シートを用いて、文字情報および画像情報が同一面上に記録された情報記録体を製造する方法であって、 The manufacturing method of another embodiment according to the information recording medium of the present invention, there in a way that by using the character information recording thermal transfer sheet, character information and image information to produce the recorded information recording medium on the same plane Te,
画像情報記録用熱転写シート中の色材とキレート錯体を形成し得る金属イオン含有化合物を含んでなる受像層を備えた被記録体を準備し、 Prepare the recording medium having an image receiving layer comprising a metal ion-containing compound capable of forming a coloring material and chelate complexes of the image information being recorded thermal transfer sheet,
前記色材を含んでなる色材層を備えた画像情報記録用熱転写シートを用いて、色材を前記被記録体の受像層側に熱転写して画像情報を印画し、 Using the image information recording thermal transfer sheet provided with a colorant layer comprising the coloring material, the image information and printing by thermally transferring the colorant to the image-receiving layer side of the recording member,
前記受像層上の画像情報形成部以外の部分に、前記文字情報記録用熱転写シートを用いて、色材を前記被記録体の受像層側に熱転写して文字情報を印画する際に、前記被記録体に印画された前記画像情報形成部の加熱を行う、 A portion other than the image information forming unit on the image-receiving layer, using the character information recording thermal transfer sheet, when printing the character information to transfer the colorant to the image-receiving layer side of the recording material, the object to be for heating of the printed on the recording medium the image information forming unit,
ことを含んでなることを特徴とするものである。 It is characterized in that it comprises a.

また、本発明の態様においては、前記画像情報形成部の加熱が、前記文字情報記録用熱転写シートから色材を熱転写する際のサーマルヘッドからの熱エネルギーにより行われることが好ましい。 In the embodiment of the present invention, heating of the image information forming unit is preferably performed by thermal energy from a thermal head at the time of thermal transfer of colorant from the character information recording thermal transfer sheet.

また、本発明の態様においては、前記文字情報記録用熱転写シートから色材を熱転写する際に、前記バリア層が設けられた部分に、サーマルヘッドからの熱エネルギーを付与して、前記被記録体に印画された前記画像情報形成部の加熱を行うことが好ましい。 In the embodiment of the present invention, when the thermal transfer of colorant from the character information recording thermal transfer sheet, the portion where the barrier layer is provided, by applying the thermal energy from the thermal head, the recording material it is preferable to perform the heating of the image information forming unit that is printed on.

また、本発明の別の態様においては、上記の製造方法により得られた情報記録体も提供される。 Further, in another aspect of the present invention, the information recording medium obtained by the manufacturing method described above is also provided.

本発明による文字情報記録用熱転写シートには、被記録体の画像形成部分に相当する部分にバリア層が設けられているため、ポストキレート方式により被記録体上に画像を形成し、次いで基材上の画像形成部分以外の部分に文字情報を熱転写により記録したような情報記録体を製造する場合において、上記のような文字情報記録時の熱転写による再加熱を行っても、画像形成部分の受容層から色材が文字情報記録用熱転写シートに逆転写されず、結果として、画像情報部分の優れた画質と、プリンタ装置の高速化および小型化とを両立させることができる。 The character information recording thermal transfer sheet according to the present invention, since the barrier layer is provided in a portion corresponding to the image forming portion of the recording medium, the image formed on the recording medium by the post chelate type, then the substrate in case of manufacturing the information recording medium, such as recording the character information by the thermal transfer to the portion other than the image forming portion of the upper, even if the reheating by the character information recorded at the time of thermal transfer as described above, reception of the image forming portion coloring material is not reverse transcribed into text information recording thermal transfer sheet from the layer, as a result, good picture quality of the image information portion, it is possible to achieve both high-speed and miniaturization of the printer device.

本発明による文字情報記録用熱転写シートの一実施形態を示した斜視概略図である。 It is a perspective schematic view showing an embodiment of a character information recording thermal transfer sheet according to the present invention. 図1の文字情報記録用熱転写シートのA−A'断面を示した断面概略図である。 It is a cross-sectional schematic view showing the A-A 'cross section of the character information recording thermal transfer sheet of FIG. 被記録体の一実施形態を示した断面概略図である。 It is a cross-sectional schematic view showing an embodiment of the recording medium. 被記録体の別の実施形態を示した断面概略図である。 It is a cross-sectional schematic view showing another embodiment of the recording medium. 画像情報記録用熱転写シートの一実施形態を示した断面概略図である。 It is a cross-sectional schematic view showing an embodiment of an image information recording thermal transfer sheet. 画像情報記録用熱転写シートの別の実施形態を示した斜視概略図である。 It is a perspective schematic view showing another embodiment of an information recording thermal transfer sheet. 本発明による情報記録体の製造方法に用いられる製造装置の一実施形態を示した概略構成図である。 It is a schematic diagram showing an embodiment of a production apparatus used in the method of manufacturing the information recording medium according to the present invention. 文字情報記録用と画像情報記録用を兼ね備える熱転写シートの一実施形態を示した斜視概略図である。 It is a perspective schematic view showing an embodiment of a thermal transfer sheet having both text information recording and image information recording. 透明保護層転写箔シートの一実施形態を示した断面概略図である。 It is a cross-sectional schematic view showing an embodiment of a transparent protective layer transfer foil sheet. 光学変化素子転写箔シートの一実施形態を示した断面概略図である。 It is a cross-sectional schematic view showing an embodiment of an optical variable device transfer foil sheet. 本発明による情報記録体の一実施形態を示した断面概略図である。 It is a cross-sectional schematic view showing an embodiment of an information recording medium according to the present invention. 従来の情報記録体の製造に用いられていた画像情報記録用熱転写シートを示した断面概略図である。 It is a cross-sectional schematic view showing an image information recording thermal transfer sheet which has been used in the manufacture of conventional information recording medium. 従来の情報記録体の製造に用いられていた文字情報記録用熱転写シートを示した断面概略図である。 It is a cross-sectional schematic view showing the character information recording thermal transfer sheet which has been used in the manufacture of conventional information recording medium.

<文字情報記録用熱転写シート> <Character information recording thermal transfer sheet>
本発明による熱転写シートは、ポストキレート方式により画像形成された被記録体の同一面上に文字情報を記録するために用いられる熱転写シートであって、図1に示すように、基材24と、基材24上の一部に設けられた色材層22と、基材24上の色材層22が設けられていない部分に設けられたバリア層23と、を少なくとも備えた層構成を有しており、バリア層23が、被記録体上の画像情報が印画された部分と対応するようにパターニングされているものである。 The thermal transfer sheet according to the present invention is a thermal transfer sheet used for recording character information on the same surface of the recording medium on which an image is formed by the post chelate system, as shown in FIG. 1, a substrate 24, It includes a colorant layer 22 provided on a part of the substrate 24, a barrier layer 23 that the colorant layer 22 on the substrate 24 is provided in a portion not provided, at least comprising a layer structure of and it is a barrier layer 23, in which image information on the recording medium is patterned to correspond with printed portions. ポストキレート方式により画像形成された被記録体の同一面上に、上記のようなバリア層を設けた熱転写シートを用いて文字情報を記録する場合、プリンタのサーマルヘッドからの熱エネルギーにより、熱転写シートの熱溶融ブラック色材層中の色材が、被記録体へ熱転写されて、画像形成部分以外の部分の所望の位置に文字情報を記録することができる。 On the same surface of the recording medium on which an image is formed by the post chelate method, when recording the text information using the thermal transfer sheet such provided a barrier layer as described above, the thermal energy from the printer of a thermal head, a thermal transfer sheet color material thermally fusible black coloring material layer is, is thermally transferred to the recording medium, it can record character information at a desired position in the portion other than the image forming portion. また、熱転写シートのバリア層が設けられた部分にサーマルヘッドからの熱エネルギーを付与することにより、バリア層を介して、被記録体の画像情報が記録された部分(すなわち、被記録体の受像層のうち、熱転写シートのバリア層が設けられている範囲に対応した範囲)に熱が伝達され、被記録体の受像層中の色材(イエロー染料、マゼンタ染料およびシアン染料)と金属イオン含有化合物とがキレート反応が促進されて、所望の発色及び階調を有する画像情報が形成される。 Further, by applying thermal energy from the thermal head portion of the barrier layer of the thermal transfer sheet is provided, through a barrier layer, partial image information of the recording medium has been recorded (i.e., an image receiving of a recording medium of the layers, the heat is transmitted to the range) that corresponds to the range where the barrier layer of the thermal transfer sheet is provided, the metal ion-containing coloring material receiving layer in the recording medium (yellow dye, magenta dye and cyan dye) and compounds is promoted chelating reaction, image information having a desired color and gradation is formed.

上記のようなバリア層が文字情報記録用熱転写シートに設けられていない場合、熱転写の際に、被記録体の画像情報が記録された部分は直接、熱転写シートの基材と接することとなるため、画像情報が記録された部分により効率的に熱エネルギーを付与することができるが、この熱によって画像形成部分の受容層から色材(イエロー染料、マゼンタ染料およびシアン染料)が文字情報記録用熱転写シートに逆転写されてしまい、被記録体に形成した画像の発光効率が低下することがある。 When the barrier layer as described above is not provided in the character information recording thermal transfer sheet, upon thermal transfer, direct a portion where image information is recorded in the recording medium, since that would contact with the substrate of the thermal transfer sheet by partial image information has been recorded but can be efficiently applying thermal energy, the colorant from the receiving layer of the image forming portion by the heat (yellow dye, magenta dye and cyan dye) the character information recorded thermal transfer will be reverse transcribed to the sheet, the light emission efficiency of the image formed on the recording medium may be decreased. 本発明においては、熱転写シートにバリア層を設けることにより、画像形成部分の受容層から色材の逆転写を防止している。 In the present invention, by providing a barrier layer in the thermal transfer sheet, thereby preventing the reverse transcription of the colorant from the receiving layer of the image forming portion. 以下、文字情報記録用熱転写シートを構成する各層について説明する。 The following describes each of the layers constituting the character information recording thermal transfer sheet.

図2は、図1のA−A'断面を示した概略断面図である。 Figure 2 is a schematic sectional view showing an A-A 'section in FIG. 基材24上には、色材層22とバリア層23とが設けられている。 On the substrate 24, the color material layer 22 and the barrier layer 23 is provided. 基材としては、従来公知の熱転写シートに用いられている基材フィルムを用いることができ、例えば、ポリエチレンテレフタレートフィルム、1,4−ポリシクロヘキシレンジメチレンテレフタレートフィルム、ポリエチレンナフタレートフィルム、ポリフェニレンサルフィドフィルム、ポリスチレンフィルム、ポリプロピレンフィルム、ポリサルホンフィルム、アラミドフィルム、ポリカーボネートフィルム、ポリビニルアルコールフィルム、セロハン、酢酸セルロース等のセルロース誘導体、ポリエチレンフィルム、ポリ塩化ビニルフィルム、ナイロンフィルム、ポリイミドフィルム、アイオノマーフィルム等の樹脂フィルム等を用いることができる。 The substrate is used in the conventional thermal transfer sheet can be used the base film is, for example, polyethylene terephthalate film, 1,4-polycyclohexylenedimethylene terephthalate film, polyethylene naphthalate film, polyphenylene sulfide film, polystyrene film, polypropylene film, polysulfone film, aramid film, polycarbonate film, polyvinyl alcohol film, cellophane, cellulose derivatives such as cellulose acetate, polyethylene film, polyvinyl chloride film, nylon film, polyimide film, resin film such as ionomer film or the like can be used. これら樹脂フィルムの中でも耐熱性やコストの観点からポリエチレンテレフタレートフィルムが好適に使用できる。 Polyethylene terephthalate film in view of heat resistance and cost Among these resin films are preferably used. ポリエチレンテレフタレートは、染料を吸着し易い特性があるが、本発明の熱転写シートは、後記するようなバリア層を備えるため、熱転写時に被記録体の画像情報が記録されている受容層から色材の逆転写を防止することができる。 Polyethylene terephthalate, it is easy properties to adsorb a dye, a thermal transfer sheet of the present invention, since with a barrier layer as described below, the colorant from the receiving layer on which an image information of the recording medium at the time of thermal transfer is recorded it is possible to prevent the reverse transcription.

印刷速度を向上させ、また再加熱時の熱量を増大させる観点から、基材の厚みは2〜10μm、好ましくは2〜6μm、より好ましくは2〜4μmである。 To improve the printing speed, and from the viewpoint of increasing the amount of heat at the time of re-heating, the thickness of the substrate is 2 to 10 [mu] m, preferably 2-6 [mu] m, more preferably 2-4 [mu] m. 基材は薄い方が好ましいが、2μm未満では張力により、熱転写シートが変形し易くなる。 The substrate is preferably thin, but the tension is less than 2 [mu] m, the thermal transfer sheet is liable to deform. 隣接する層との接着性を向上させるため、基材表面には、表面処理を施してもよい。 To improve the adhesion between adjacent layers, the substrate surface may be subjected to surface treatment. 上記表面処理としては、コロナ放電処理、火炎処理、オゾン処理、紫外線処理、放射線処理、粗面化処理、化学薬品処理、プラズマ処理、グラフト化処理等、公知の樹脂表面改質技術を適用することができる。 As the surface treatment, corona discharge treatment, flame treatment, ozone treatment, ultraviolet treatment, radiation treatment, roughening treatment, chemical treatment, plasma treatment, grafting treatment, and other, applying a known surface modifying treatments can.

また、必要に応じ、その一方の面又は両面にプライマー層(図示せず)を設けてもよい。 Further, if necessary, (not shown) the primer layer on the surface or both surfaces of its one may be provided. プライマー層は、例えば基材フィルムの溶融押出しの成膜時に、未延伸フィルムにプライマー液を塗布し、その後に延伸処理して行なうことができる。 The primer layer, for example, during the formation of the melt extrusion of the substrate film, a primer solution is applied to the unstretched film can be carried out followed by stretching treatment. また、プライマー液としては、例えば、ポリエステル系樹脂、ポリアクリル酸エステル系樹脂、ポリ酢酸ビニル系樹脂、ポリウレタン系樹脂、スチレンアクリレート系樹脂、ポリアクリルアミド系樹脂、ポリアミド系樹脂、ポリエーテル系樹脂、ポリスチレン系樹脂、ポリエチレン系樹脂、ポリプロピレン系樹脂、ポリ塩化ビニル樹脂やポリビニルアルコール樹脂、ポリ塩化ビニリデン樹脂等のビニル系樹脂、ポリビニルアセトアセタールやポリビニルブチラール等のポリビニルアセタール系樹脂、セルロース系樹脂等からなる塗工液を使用することができる。 As the primer liquid, for example, polyester resins, polyacrylate resins, polyvinyl acetate resins, polyurethane resins, styrene acrylate resins, polyacrylamide resins, polyamide resins, polyether resins, polystyrene system resin, polyethylene resin, polypropylene resin, polyvinyl chloride resin, polyvinyl alcohol resin, vinyl-based resins such as polyvinylidene chloride resins, polyvinyl acetal resins such as polyvinyl acetoacetal and polyvinyl butyral, a coating made of a cellulose resin or the like it is possible to use a coating liquid.

色材層22は、基材24上に顔料等で着色した熱溶融性インキを塗工することにより形成することができる。 Colorant layer 22 can be formed by coating a hot-melt ink colored with pigments or the like on the base material 24. 熱溶融性インキとしては、従来公知の熱転写シートに用いられているものを制限なく使用することができる。 The hot-melt ink, can be used without limitation those used in conventional thermal transfer sheet. 例えば、グラビア印刷法、スクリーン印刷法、グラビア版を用いたリバースロールコーティング印刷法等の公知の手段により、基材の一方の面に公知のブラックインキを塗布し、乾燥することにより色材層を形成することができる。 For example, gravure printing, screen printing, by means known in the reverse roll coating printing method using a gravure plate, coated with known black ink on one side of the substrate, the color material layer by drying it can be formed. このようにして形成される色材層の厚みは、0.1〜5.0μm程度、好ましくは0.2〜3.0μmである。 The thickness of the thus color material layer formed is about 0.1 to 5.0 [mu] m, preferably 0.2 to 3.0 [mu] m.

基材24上に色材層22を直接設けてもよいが、基材24と色材層22との間に剥離層25を設けてもよい。 While on the substrate 24 may be provided a color material layer 22 directly, a separation layer may be provided 25 between the substrate 24 and the color material layer 22. 剥離層を設けることにより、熱転写時に溶融したブラックインキ溶融を基材から剥離し易くするとともに、被記録体に文字情報を記録した後も、文字記録部分に滑り性を与えて、耐擦過性を向上させることができる。 By providing the release layer, thereby easily separating the black ink melted melted during thermal transfer from the substrate, even after recording the character information on the recording medium, giving slipperiness to the character recording part, the scratch resistance it is possible to improve. 剥離層としては、融点もしくは軟化点が、50〜150℃、特に60〜120℃の範囲にある熱可塑性樹脂や2種以上熱可塑性樹脂を混合して上記の温度範囲になるものを好適に使用できる。 As the release layer, the melting point or softening point, 50 to 150 ° C., preferably used those comprising a temperature range of the particularly mixing a thermoplastic resin and two or more thermoplastic resins in the range of 60 to 120 ° C. it can. 例えば、アクリル樹脂、シリコーン樹脂、フッ素樹脂、シリコーンまたはフッ素で変性した各種の樹脂やワックスを主成分とした従来公知のものを使用することができる。 For example, it is possible to use acrylic resins, silicone resins, fluorocarbon resins, those with a silicone or fluorine-modified various known conventional resin or wax as a main component of. また、熱可塑性樹脂の他に、必要に応じて、パルミチン酸、ステアリン酸、マルガリン酸およびベヘン酸等の高級脂肪酸;パルミチルアルコール、ステアリルアルコール、ベヘニルアルコール、マルガニルアルコール、ミリシルアルコールおよびエイコサノール等の高級アルコール;バルミチン酸セチル、バルミチン酸ミリシル、ステアリン酸セチルおよびステアリン酸ミリシル等の高級脂肪酸エステル;アセトアミド、プロピオン酸アミド、パルミチン酸アミド、ステアリン酸アミドおよびアミドワックス等のアミド類;ならびにステアリルアミン、ベヘニルアミンおよびパルチミルアミン等の高級アミン類などを添加してもよい。 In addition to the thermoplastic resin, if necessary, palmitic acid, stearic acid, higher fatty acids such as margaric acid and behenic acid; palmityl alcohol, stearyl alcohol, behenyl alcohol, Marga alkenyl alcohols, such as myricyl alcohol and eicosanol higher alcohol; palmitic acid cetyl, palmitic acid myricyl, higher fatty acid esters such as myricyl stearate, cetyl and stearic acid; acetamide, amides propionic acid, palmitic acid amide, such as stearic acid amide and amide wax; and stearylamine, behenyl and higher amines such as amines and Paruchimiruamin may be added. これら添加成分は、1種単独で用いてもよいし、2種以上を併用してもよい。 These additional ingredients may be used either alone, or in combination of two or more. また、剥離性を調節するため界面活性剤を含んでいてもよく、好適な界面活性剤として、ポリオキシエチレン鎖含有化合物が挙げられる。 Also, it may contain a surfactant to adjust the releasability, suitable surfactants, polyoxyethylene chain-containing compounds. さらに、無機あるいは有機の微粒子(金属粉、シリカゲルなど)や、オイル類(アマニ油鉱油など)を添加することもできる。 Further, inorganic or organic fine particles (metal powder, silica gel etc.) or may be added to oils (such as linseed oil mineral oil). 熱伝導性の観点から、剥離層の厚みは、0.05〜2.0μm、好ましくは0.1〜1.0μmとするのが好ましい。 From the viewpoint of thermal conductivity, thickness of the release layer, 0.05 to 2.0, preferably preferably set to 0.1 to 1.0 [mu] m.

色材層22上には、接着層26を設けて、色材層と被記録体との接着性を向上させてもよい。 On the colorant layer 22 is provided with a adhesive layer 26 may be improved adhesion to the colorant layer and the recording medium. この接着層は、サーマルヘッド、レーザー等の加熱により、軟化して接着性を発揮する熱可塑性エラストマーを主体とし、得られる熱転写シートをロール状に巻き取った時にブロッキングを防止するために、ワックス類、高級脂肪酸のアミド、エステル及び塩、フッ素樹脂や無機物質の粉末のようにブロッキング防止剤を添加することができる。 The adhesive layer is a thermal head, the heat such as a laser, soften mainly of thermoplastic elastomer which exhibits adhesion, a thermal transfer sheet obtained in order to prevent blocking when wound into a roll, waxes , amides of higher fatty acids, can be added esters and salts, anti-blocking agent as a powder of a fluororesin and an inorganic material. 熱可塑性エラストマーとして、例えば、エチレン−酢酸ビニル共重合体(EVA)、エチレン−アクリル酸エステル共重合体(EEA)、ポリエステル樹脂、ポリエチレン、ポリスチレン、ポリプロピレン、ポリブデン、石油樹脂、塩化ビニル樹脂、塩化ビニル−酢酸ビニル共重合体、ポリビニルアルコール、塩化ビニリデン樹脂、メタクリル樹脂、ポリアミド、ポリカーボネート、ポリビニルフォルマール、ポリビニルブチラール、アセチルセルロース、ニトロセルロース、ポリ酢酸ビニル、ポリイソブチレン、エチルセルロースまたはポリアセタールなどが挙げられる。 As the thermoplastic elastomer, such as ethylene - vinyl acetate copolymer (EVA), ethylene - acrylic acid ester copolymer (EEA), polyester resin, polyethylene, polystyrene, polypropylene, polybutene, petroleum resin, vinyl chloride resin, a vinyl chloride - vinyl acetate copolymer, polyvinyl alcohol, vinylidene chloride resin, methacrylic resin, polyamide, polycarbonate, polyvinyl formal, polyvinyl butyral, acetyl cellulose, nitrocellulose, polyvinyl acetate, polyisobutylene, such as ethyl cellulose or polyacetals and the like. また、添加されるワックス類としては、例えば、マイクロクリスタリンワックス、カルナバワックス、パラフィンワックス等がある。 As the wax to be added, for example, microcrystalline wax, carnauba wax, and paraffin wax. 更に、フィッシャートロプシュワックス、各種低分子量ポリエチレン、木ロウ、ミツロウ、鯨ロウ、イボタロウ、羊毛ロウ、セラックワックス、キャンデリラワックス、ペトロラクタム、ポリエステルワックス、一部変性ワックス、脂肪酸エステル、脂肪酸アミド等、種々のワックスが挙げられる。 Additionally, Fischer-Tropsch wax, various low molecular weight polyethylene, Japan wax, beeswax, spermaceti, insect wax, wool wax, shellac wax, candelilla wax, petrolatum, polyester wax, partially modified wax, fatty acid esters, fatty acid amides, various include the wax.

接着層は、熱可塑性エラストマーと添加剤とを適当な溶剤に溶解または分散させた塗工液を、従来公知のホットメルトコート、ホットラッカーコート、グラビアダイレクトコート、グラビアリバースコート、ナイフコート、エアコート、ロールコート等の方法により形成することができる。 Adhesive layer, a thermoplastic elastomer and coating liquid dissolved or dispersed an additive in an appropriate solvent, conventional hot melt coating, hot lacquer coating, gravure direct coating, gravure reverse coating, knife coating, air coating, it can be formed by a method such as roll coating. 接着層の厚みは、0.05〜2.0μm程度、好ましくは0.1〜1.0μmである。 The thickness of the adhesive layer is about 0.05 to 2.0, preferably 0.1 to 1.0 [mu] m.

また、基材24の色材層22を設けた側とは反対の側の面には、背面層27を設けてもよい。 Further, the side provided with the color material layer 22 of the substrate 24 on the opposite side of the can be provided with a back layer 27. 背面層は、熱転写時の熱で熱転写シートが変形しないように耐熱性を向上させるとともに、また熱転写時のサーマルヘッドの走行性を改善してスティッキング等を抑制する機能を有する。 Back layer has a with heat transfer sheet during thermal transfer improves the heat resistance so as not to deform, also function of suppressing sticking such as to improve the running properties of the thermal transfer at the thermal head. 背面層は、バインダー樹脂に滑性剤、界面活性剤、無機粒子、有機粒子、顔料等を添加したものを塗布、乾燥することにより形成できる。 Back layer, lubricity agent in the binder resin, a surfactant, inorganic particles, organic particles, coating the material obtained by adding pigment or the like can be formed by drying. 耐熱層に使用されるバインダー樹脂としては、従来公知のものを使用でき、例えば、エチルセルロース、ヒドロキシエチルセルロース、ヒドロキシプロピルセルロース、メチルセルロース、酢酸セルロース、酢酪酸セルロース、硝化綿などのセルロース系樹脂、ポリビニルアルコール、ポリ酢酸ビニル、ポリビニルブチラール、ポリビニルアセタール、ポリビニルピロリドン、アクリル樹脂、ポリアクリルアミド、アクリロニトリル−スチレン共重合体などのビニル系樹脂、ポリエステル樹脂、ポリウレタン樹脂、シリコーン変性またはフッ素変性ウレタン樹脂等が挙げられる。 The binder resin used in the heat resistant layer, conventional ones can be used. Known, for example, ethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, methyl cellulose, cellulose acetate, cellulose acetate butyrate, cellulose resins such as nitrocellulose, polyvinyl alcohol, polyvinyl acetate, polyvinyl butyral, polyvinyl acetal, polyvinyl pyrrolidone, acrylic resin, polyacrylamide, acrylonitrile - vinyl resins such as styrene copolymers, polyester resins, polyurethane resins, and silicone-modified or fluorine-modified urethane resins. また、滑性剤としては、従来公知のものを使用することができ、例えば、ポリオレフィンおよびエチレン性不飽和カルボン酸またはそのエステル無水物から誘導されたポリマーを含むワックス等を好適に使用することができる。 As the slip agent, it can be conventionally used known ones, for example, be suitably used wax comprising a polymer derived from a polyolefin and an ethylenically unsaturated carboxylic acid or its ester anhydrides it can. このような背面層を設けることにより、文字情報記録用熱転写シートをロール状にした場合の基材の裏面と色材層との接触面積を小さくして、基材裏面へ色材が移行するのを低減することもできる。 By providing such a back layer, to reduce the contact area between the rear surface and the coloring material layer of the substrate when the character information recording thermal transfer sheet into a roll, the coloring material to migrate into the substrate back surface It can also be reduced. 背面層の厚みは、熱伝導性の観点から、0.05〜2.0μm程度、好ましくは0.2〜2.0μmである。 The thickness of the back layer, from the viewpoint of thermal conductivity, about 0.05 to 2.0, preferably 0.2 to 2.0 [mu] m.

基材24上の色材層22が設けられていない部分に設けるバリア層23は、熱転写時の熱エネルギーによって、被記録体の画像情報が記録された部分の受容層から色材が、文字情報記録用熱転写シート側に逆転写されないようにするためのものである。 Barrier layer 23 provided on the portion where the color material layer 22 on the substrate 24 is not provided, the thermal energy of the thermal transfer, the coloring material from the receiving layer of the portion where the image information on the recording medium is recorded, the character information it is intended for preventing reverse transcribed to the recording thermal transfer sheet side. このバリア層23は、基材24上の色材層22がない部分に設けられるとともに、熱転写の際に被記録体上の画像情報が印画された部分(図1の符合23の部分)と、文字情報記録用熱転写シートのバリア層のある部分(図2の符合23の部分)とが対応するように、パターニングされて設けられている。 The barrier layer 23 is provided in an portion no color material layer 22 on the substrate 24, a portion where image information on the recording medium is printed when the thermal transfer (partial tally 23 in FIG. 1), character information recording thermal transfer sheet barrier with a layer portion such that the (part of the sign 23 in FIG. 2) corresponding, are provided by patterning.

バリア層は、色材との親和性が低い化学構造を有し、かつ色材の透過速度が低い樹脂、すなわち、疎水性、吸水性および透湿性が低い樹脂を適当な溶剤に溶解させた塗工液を基材上に塗布、乾燥させることにより形成することができる。 Barrier layer has a low affinity chemical structure of the colorant, and the permeation rate of the colorant is less resin, i.e., hydrophobic, water absorption and moisture permeability by dissolving a low resin in a suitable solvent coating coating a coating solution on a substrate can be formed by drying. このような樹脂としては、アクリル系、塩化ビニル、塩化ビニリデン、アクリロニトリルおよび酢酸ビニルなどのビニル重合体もしくは共重合体、ポリビニルホルマール、ポリビニルアセタール、ポリビニルベンザールなどのアセタール類、ニトロセルロース、ジアセチルセルロース、トリアセチルセルロース、セルロースアセテートプロピオネート、セルロースアセテートブチレート樹脂などのセルロース誘導体、スチレン系樹脂などが挙げられる。 Such resins, acrylic resins, vinyl chloride, vinylidene chloride, vinyl polymer or copolymer of acrylonitrile and vinyl acetate, polyvinyl formal, polyvinyl acetal, acetals such as polyvinyl benzal, nitrocellulose, diacetyl cellulose, triacetyl cellulose, cellulose acetate propionate, cellulose derivatives such as cellulose acetate butyrate resins, and styrene-based resins. これらのなかでもアクリル系、ポリビニルアルキルアセタール系、アセチルセルロース系、スチレン系樹脂を好適に使用することができる。 Acrylic Among these, polyvinyl alkyl acetal may be preferably used acetylcellulose, a styrene resin.

バリア層には、シリカ等の微粒子が含まれていてもよい。 The barrier layer may contain fine particles such as silica. 文字情報記録用熱転写シートをロール状にして保管する場合のように、バリア層23と背面層27とが接しながら保管される場合に、バリア層中に上記のような微粒子が含まれることにより、背面層とのブロッキングを防止することができる。 Character information recording heat transfer sheet as in the case of storage in a roll form, when the barrier layer 23 and the back layer 27 are stored while contacting, by containing the fine particles as described above in the barrier layer, it is possible to prevent blocking with the backside layer.

バリア層は、図1に示すようにパターニングして設けられているため、文字情報記録用熱転写シート20の表面に段差を生じる場合がある。 Barrier layer, because it is provided by patterning as shown in FIG. 1, there is a case where the surface of the character information recording thermal transfer sheet 20 caused a step. そのため、バリア層は、図2に示すように、色材層22の設けられた部分の総厚みと同じ厚みになるように形成されることが好ましい。 Therefore, the barrier layer, as shown in FIG. 2, is preferably formed so as to have the same thickness as the total thickness of the provided portion of the colorant layer 22. 色材層22の設けられた部分の総厚みと同じ厚みになるようにバリア層を形成することにより、文字情報記録用熱転写シートをロール状に巻回した状態で供給する場合であっても、熱転写シートの膜厚差による巻き跡がでにくくなる。 By forming a barrier layer so as to have the same thickness as the total thickness of the provided portion of the colorant layer 22, also character information recording thermal transfer sheet in a case of supplying in a state wound into a roll, hardly out winding marks due to the film thickness difference of the thermal transfer sheet. したがって、バリア層の厚みは、色材層の設けられている部分の各層(接着層、離型層、色材層等)の厚みにもよるが、0.2〜7.0μm程度、好ましくは1.0〜5.0μmである。 Therefore, the thickness of the barrier layer, each layer of the portion provided with the color material layer (adhesive layer, a release layer, a color material layer, etc.) depending on the thickness of about 0.2~7.0Myuemu, preferably it is 1.0~5.0μm.

文字情報記録用熱転写シートは、上記した各層以外にも、従来公知の熱転写シートと同様に、離型層や下引き層等のその他の層が設けられていてもよい。 Character information recording thermal transfer sheet, in addition each layer described above, similarly to the conventional thermal transfer sheet, other layers may be provided, such as a release layer or undercoat layer.

<情報記録体の製造方法> <Method of manufacturing an information recording medium>
次に、上記した文字情報記録用熱転写シートを用いた情報記録体の製造方法を、図面を参照しながら説明する。 Next, a method of manufacturing an information recording medium using the character information recording thermal transfer sheet as described above will be described with reference to the drawings. 本発明による情報記録体の製造方法は、文字情報および画像情報が同一面上に記録された情報記録体を製造する方法であって、 Method of manufacturing an information recording medium according to the present invention is a method of character information and image information to produce the recorded information recording medium on the same surface,
(1)画像情報記録用熱転写シート中の色材とキレート錯体を形成し得る金属イオン含有化合物を含んでなる受像層を備えた被記録体を準備する工程、 (1) providing a recording material having an image receiving layer comprising a metal ion-containing compound capable of forming a coloring material and chelate complexes of the image information being recorded thermal transfer sheet,
(2)前記色材を含んでなる色材層を備えた画像情報記録用熱転写シートを用いて、色材を前記被記録体の受像層側に熱転写して画像情報を印画する工程、 (2) using image information recording thermal transfer sheet provided with a colorant layer comprising the coloring material, the step of printing the image information by thermally transferring the colorant to the image-receiving layer side of the recording member,
(3)前記受像層上の画像情報形成部以外の部分に、前記文字情報記録用熱転写シートを用いて、色材を前記被記録体の受像層側に熱転写して文字情報を印画する際に、前記被記録体に印画された前記画像情報形成部の加熱を行う工程、 (3) in a portion other than the image information forming unit on the image-receiving layer, using the character information recording thermal transfer sheet, when printing the character information to transfer the colorant to the image-receiving layer side of the recording member , the step of performing the heating of the said image information forming unit which is printed on the recording medium,
を含むものである。 It is intended to include. 以下、本発明による情報記録体の製造方法を、図面を参照しながら各工程順に説明する。 Hereinafter, a method of manufacturing an information recording medium according to the present invention will be described with reference to the drawings in the order of steps.

本発明による情報記録体の製造方法においては、受像層を一方の面に備えた被記録体に文字情報および画像情報を印画することにより、文字情報および画像情報が同一面上に記録された情報記録体が製造される。 Information In the method of manufacturing an information recording medium according to the present invention, by printing the character information and image information on the recording medium having an image receiving layer on one surface, character information and image information is recorded on the same plane recording material is produced. 本発明においては、身分証明書等のIDカードや銀行等のキャッシュカードのような情報記録体を製造することを目的とするものであり、従って、被記録体として、ICチップを供えたIDカード基材に文字情報や画像情報等を印画することを一例に、被記録体について、まず説明する。 In the present invention, which aims to produce the information recording medium, such as a cash card such as an ID card or bank identification, etc., therefore, as the recording medium, ID card includes an IC chip one example to print the character information, image information, etc. to a substrate, for the recording medium will be described first.

図3は、ICカード基材2と受像層3とを備えた被記録体1の断面図を示したものである。 Figure 3 shows a cross-sectional view of the recording medium 1 provided with the IC card base 2 and the image receiving layer 3. ICカード基材2は、第1のシート部材4と第2のシート部材5との間に所定の厚みの電子部品8とを備えており、電子部品8は、アンテナ体8a、ICチップ8b等からなり、この電子部品8のICモジュールはインレット7に備えられている。 IC card substrate 2 comprises a first sheet member 4 comprises an electronic component 8 having a predetermined thickness between the second sheet member 5, the electronic component 8, the antenna 8a, IC chip 8b, etc. consists, IC module of the electronic component 8 is provided in the inlet 7. 第1のシート部材4と第2のシート部材5との間にインレット7を配置し、接着剤6を介在して、各部材を積層した積層構造である。 A first sheet member 4 to the inlet 7 is disposed between the second sheet member 5, interposed an adhesive 6, a laminated structure obtained by laminating the members. また、被記録体は、図4に示すように、電子部品8を接着剤6中に備えた構造としてもよい。 Further, the recording medium, as shown in FIG. 4 may be an electronic component 8 as a structure having in the adhesive 6.

被記録体1は、ICカード基材2の第2シート部材5側に受像層3が設けられている。 The recording medium 1, the image-receiving layer 3 is provided on the second sheet member 5 of the IC card substrate 2. 受像層3は、熱転写記録方式で昇華もしくは熱拡散性染料画像を受容して、被記録体1に文字情報および画像情報を印画するためのものである。 Receiving layer 3 is to receive a sublimable or heat diffusible dye image thermal transfer recording method is used for printing the character information and image information on the recording medium 1. 受像層を形成するための材料としては、昇華性染料または熱溶融性インキ等の熱移行性の色材を受容し易い従来公知の樹脂材料を使用することができる。 As a material for forming the image-receiving layer, it is possible to use thermal migration of conventionally known resin material easily receive the color material such as sublimable dyes, or hot-melt ink. 例えば、ポリプロピレン等のポリオレフィン系樹脂、ポリ塩化ビニルもしくはポリ塩化ビニリデン等のハロゲン化樹脂、ポリ酢酸ビニル、塩化ビニル−酢酸ビニル系共重合体、エチレン−酢酸ビニル共重合体もしくはポリアクリル酸エステル等のビニル系樹脂、ポリエチレンテレフタレートもしくはポリブチレンテレフタレート等のポリエステル樹脂、ポリスチレン系樹脂、ポリアミド系樹脂、エチレンもしくはプロピレン等のオレフィンと他のビニルポリマーとの共重合体系樹脂、アイオノマーもしくはセルロースジアスターゼ等のセルロース系樹脂、ポリカーボネート等が挙げられ、特に、塩化ビニル系樹脂、アクリル−スチレン系樹脂またはポリエステル樹脂が好ましい。 For example, polyolefin resins such as polypropylene, halogenated resins such as polyvinyl chloride or polyvinylidene chloride, polyvinyl acetate, vinyl chloride - vinyl acetate copolymer, ethylene - vinyl copolymer or the like polyacrylic ester acetate vinyl resins, polyethylene terephthalate or polybutylene terephthalate polyester resin, polystyrene resin, polyamide resin, copolymer-based resins of olefins and other vinyl polymers such as ethylene or propylene, a cellulose resin such as ionomer or cellulose diastase , polycarbonate and the like, in particular, vinyl chloride resin, acryl - styrene resin or a polyester resin.

本発明においては、受像層3は、後記する色材である色素化合物と反応してキレートを形成し得る金属イオン含有化合物を含有している。 In the present invention, the image receiving layer 3 contains a metal ion-containing compound capable of forming a chelate by reacting with the dye compound is a coloring material to be described later. すなわち、本発明においては、色材である色素化合物を受像層へ熱転写した後、受像層中の金属イオン含有化合物と色素化合物とを反応させてキレート錯体を形成する、いわゆるポストキレート方式により、画像情報および/または文字情報を被記録体に転写して画像形成するものである。 That is, in the present invention, after the dye compound was thermal transfer to the image-receiving layer is a coloring material and a metal ion-containing compound and a dye compound of the image receiving layer is reacted to form a chelate complex, the so-called post-chelate type, image information and / or character information is transferred to the recording medium in which an image is formed. ポストキレート方式を採用することにより、被記録体へ転写された画像や文字の耐光性を向上させることができる。 By adopting the post chelate method, it is possible to improve the light resistance of images and characters that have been transferred to the recording medium.

受像層中に含有させる金属イオン含有化合物としては、従来公知のものを使用することができ、第I、第VIII族に属する2価および多価の金属の無機または有機の塩および金属錯体を好適に使用することができる。 The metal ion-containing compound contained in the image-receiving layer, conventionally known ones can be used, the first I, 2 and multivalent metals of inorganic or organic salts and metal complexes belonging to group VIII preferably it can be used for. 例えば、Ni 2+ 、Cu 、Co 2+ 、Cr 2+およびZn 2+を含有する、下記一般式: For example, Ni 2+, Cu +, Co 2+, containing Cr 2+ and Zn 2+, the following general formula:
[M(Q1)k(Q2)m (Q3)n]p p(L [M (Q1) k (Q2 ) m (Q3) n] p + p (L -)
(式中、Mは金属イオンを表し、Q1、Q2、Q3は各々Mで表される金属イオンと配位結合可能な配位化合物を表わし、Lは錯体を形成しうる対アニオンを表し、kは1、2または3の整数を表し、mは1、2または0を表し、nは1または0を表すが、これらは前記一般式で表される錯体が4座配位か、6座配位かによって決定されるか、あるいはQ1、Q2、Q3の配位子の数によって決定され、pは1、2または3を表す。)で表される錯体が好ましく用いられる。 (Wherein, M represents a metal ion, Q1, Q2, Q3 represents each M can coordinately bound to metal ion represented by coordination compounds, L is a counter anion capable of forming a complex, k represents an integer of 1, 2 or 3, m represents 1, 2 or 0, n each represents 1 or 0, which are either complex tetradentate represented by the general formula, 6 tetradentate or is determined by either position, or is determined by the Q1, Q2, Q3 of the number of ligands, p is the complex represented by the representative.) 1, 2 or 3 are preferably used. これらの中でも、金属と配位結合する少なくとも一個のアミノ基を有する配位化合物が好ましく、具体的にはエチレンジアミンおよびその誘導体、グリシンアミドおよびその誘導体、ピコリンアミドおよびその誘導体が挙げられる。 Among these, preferred coordination compounds having at least one amino group metal coordinate bonds, specifically ethylene diamine and its derivatives, glycine amide and derivatives thereof, picolinic amides and derivatives thereof. また、錯体を形成しうる対アニオンLとしては、Cr、SO 、ClO 等の無機化合物アニオンやベンゼンスルホン酸誘導体、アルキルスルホン酸誘導対等の有機化合物アニオンが挙げられるが、特に好ましくはテトラフェニルホウ素アニオンおよびその誘導体、ならびにアルキルベンゼンスルホン酸アニオンおよびその誘導体である。 As the counter anion L capable of forming a complex, Cr, SO 4, the inorganic compound anions and benzenesulfonic acid derivatives of ClO 4, etc., and organic compound anions of alkylsulfonic acids derived equal the like, particularly preferably tetraphenyl boron anion and its derivatives, as well as alkyl benzene sulfonic acid anion and its derivatives. このような金属イオン含有化合物としては、米国特許第4,987,049号明細書に例示されたものを挙げることができる。 Such metal ion containing compounds may include those exemplified in U.S. Patent No. 4,987,049.

金属イオン含有化合物の樹脂中への添加量は0.5〜20g/m が好ましく、1〜15g/m がより好ましい。 The addition amount of the resin of the metal ion-containing compound is preferably 0.5~20g / m 2, 1~15g / m 2 is more preferable.

受像層には、離型剤が添加されていてもよい。 The image-receiving layer, the release agent may be added. 離型剤としては、用いるバインダーと相溶性のあるものが好ましく、具体的には変性シリコーンオイル、変性シリコーンポリマーが代表的であり、例えばアミノ変性シリコーンオイル、エポキシ変性シリコーンオイル、ポリエステル変性シリコーンオイル、アクリル変性シリコーン樹脂、ウレタン変性シリコーン樹脂等が挙げられる。 The release agent is preferably one with a binder compatible with use, specifically modified silicone oils, the modified silicone polymer is typically, for example, amino-modified silicone oil, epoxy-modified silicone oil, a polyester-modified silicone oil, acrylic-modified silicone resin, urethane-modified silicone resins. このなかでもポリエステル変性シリコーンオイルはインクシートとの融着を防止するが、受像層の2次加工性を妨げないという点で特に優れている。 Polyester-modified silicone oil Among this is to prevent fusion with the ink sheet, is particularly excellent in that it does not interfere with the secondary processing of the image-receiving layer. その他の離型剤として、シリカ等の微粒子や硬化型シリコーン化合物等を使用することもできる。 Other release agents, silica fine particles and curable silicone compounds such like can also be used.

上記した各成分を溶媒に分散あるいは溶解させた受像層用塗工液を調製し、受像層用塗工液をICカード基材の一方のシート部材上に塗布し、乾燥することよって受像層を形成することができる。 The above-described components to prepare the image-receiving layer coating liquid dispersed or dissolved in a solvent, the image-receiving layer coating solution was coated onto one of the sheet member of the IC card substrate, an image receiving layer I by drying it can be formed. 受像層の厚みは、一般的に1〜50μm、好ましくは2〜10μm程度である。 The thickness of the image receiving layer is generally 1 to 50 [mu] m, preferably about 2 to 10 [mu] m.

受像層には、画像情報や文字情報を印画する前に、予め、罫線等のフォーマット印刷がされていてもよい。 The image-receiving layer, prior to printing the image information and character information, in advance, may be the format printed ruled lines or the like. フォーマット印刷は、オフセット印刷、グラビア印刷、シルク印刷、スクリーン印刷、凹版印刷、凸版印刷、インクジェット方式、昇華転写方式、電子写真方式、熱溶融方式等のいずれの方式によって形成することができる。 Format printing, offset printing, gravure printing, silk printing, screen printing, intaglio printing, letterpress printing, ink jet method, a sublimation transfer method, electrophotographic method, can be formed by any method such as thermal fusion type.

ICカード基材2は、図3および4に示したように、第1のシート部材4と第2のシート部材5との間に所定の厚みの電子部品8とを備えており、電子部品8は、アンテナ体8a、ICチップ8b等からなり、この電子部品8のICモジュールはインレット7または接着層6に備えられている。 IC card substrate 2, as shown in Figures 3 and 4, a first sheet member 4 comprises an electronic component 8 having a predetermined thickness between the second sheet member 5, the electronic component 8 an antenna body 8a, made IC chip 8b, etc., IC module of the electronic component 8 is provided in the inlet 7 or an adhesive layer 6. ICカード基材2は、第1のシート部材4と第2のシート部材5との間にインレット7を配置し、接着剤6を介在して、各部材を積層した積層構造を有する。 IC card substrate 2 has a laminated structure an inlet 7 arranged, which adhesive 6 interposed, by laminating the member between the first sheet member 4 and the second sheet member 5. ICカード基材に用いられるシート部材としては、例えば、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンテレフタレート/イソフタレート共重合体等のポリエステル樹脂、ポリエチレン、ポリプロピレン、ポリメチルペンテン等のポリオレフィン樹脂、ポリフッ化ビニル、ポリフッ化ビニリデン、ポリ4フッ化エチレン、エチレン−4フッ化エチレン共重合体、等のポリフッ化エチレン系樹脂、ナイロン6、ナイロン6.6等のポリアミド、ポリ塩化ビニル、塩化ビニル/酢酸ビニル共重合体、エチレン/酢酸ビニル共重合体、エチレン/ビニルアルコール共重合体、ポリビニルアルコール、ビニロン等のビニル重合体、生分解性脂肪族ポリエステル、生分解性ポリカーボネート、生分解性ポリ乳酸、生分解性 The sheet member used in IC card substrate, for example, polyethylene terephthalate, polybutylene terephthalate, polyethylene terephthalate / isophthalate copolymer, polyester resin, polyethylene, polypropylene, polymethylpentene or the like of polyolefin resins, polyvinyl fluoride, polyvinylidene fluoride, polytetrafluoroethylene, ethylene-tetrafluoroethylene copolymer, polyfluoroethylene resin etc., nylon 6, polyamide such as nylon 6.6, polyvinyl chloride, vinyl chloride / vinyl acetate copolymerization coalescing, ethylene / vinyl acetate copolymer, ethylene / vinyl alcohol copolymer, polyvinyl alcohol, vinyl polymers vinylon, biodegradable aliphatic polyesters, biodegradable polycarbonates, biodegradable polylactic acid, biodegradable リビニルアルコール、生分解性セルロースアセテート、生分解性ポリカプロラクトン等の生分解性樹脂、三酢酸セルロース、セロファン等のセルロース系樹脂、ポリメタアクリル酸メチル、ポリメタアクリル酸エチル、ポリアクリル酸エチル、ポリアクリル酸ブチル、等のアクリル系樹脂、ポリスチレン、ポリカーボネート、ポリアリレート、ポリイミド等の合成樹脂シート、または上質紙、薄葉紙、グラシン紙、硫酸紙等の紙、金属箔等の単層体あるいはこれら2層以上の積層体が挙げられる。 Polyvinyl alcohol, biodegradable cellulose acetate, biodegradable polycaprolactone of biodegradable resin, cellulose triacetate, cellulose resins cellophane, polymethyl methacrylate, poly ethyl methacrylate, polyethyl acrylate, polybutyl acrylate, acrylic resins and the like, polystyrene, polycarbonate, polyarylate, synthetic resin sheet such as polyimide or fine paper, thin paper, glassine paper, paper such as parchment paper, single-layer body or the two metal foils such as laminate can be given more layers.

シート部材の厚みは30〜300μm、好ましくは50〜200μmである。 The thickness of the sheet member is 30 to 300 [mu] m, preferably 50 to 200 [mu] m. 50μm以下であるとシート部材1,2を互いに貼り合わせる際に熱収縮等を起こす場合がある。 Which may cause thermal shrinkage or the like when bonding together sheet members 1, 2 If it is 50μm or less. なお、熱収縮率を低減させるシート部材のアニール処理を行ってもよい。 It is also annealed sheet member to reduce the thermal shrinkage.

電子部品8は、一般的に、電子カードの利用者の情報を電気的に記憶するICチップ8bおよびICチップ8bに接続されたコイル状のアンテナ体8aとから構成される。 Electronic components 8 are generally composed of an electronic card IC chip 8b and IC chip 8b to connected coiled antenna body 8a electrically stores information of a user of. また、電子部品8を含むインレット7または接着剤6中には、ICチップは点圧強度が弱いためにICチップ近傍に補強板9を備えていてもよい。 Further, during the inlet 7 or adhesive 6 including electronic components 8, the IC chip may be provided with a reinforcing plate 9 to the IC chip near to a weak point pressure strength. インレットを含む電子部品の全厚さは100〜600μmが好ましく、より好ましくは150〜500μm、特に好ましくは、150〜450μmである。 The total thickness of an electronic component comprising an inlet is preferably 100~600Myuemu, more preferably 150 to 500, particularly preferably from 150~450Myuemu.

また、本発明においては、図3に示した被記録体のように、受像層3と第2シート部材2との間にクッション層10が設けられていてもよい。 In the present invention, as the recording medium shown in FIG. 3, the cushion layer 10 may be provided between the image receiving layer 3 and the second sheet member 2. クッション層を設けると、熱転写の際の表面の凹凸の影響を緩和することができ画像や文字を再現性良く転写記録することができる。 The provision of the cushion layer can be reproducibly transferred records can be images, text to mitigate the effects of unevenness of the surface during thermal transfer.

クッション層を形成する材料としては、ポリオレフィンが好ましい。 As a material for forming the cushion layer, polyolefin is preferable. 例えばポリエチレン、ポリプロピレン、エチレン−酢酸ビニル共重合体、エチレン−アクリル酸エチル共重合体、スチレン−ブタジエン−スチレンブロック共重合体、スチレン−イソプレン−スチレンブロック共重合体、スチレン−エチレン−ブタジエン−スチレンブロック共重合体、スチレン−水素添加イソプレン−スチレンブロック共重合体、ポリブタジエン、光硬化型樹脂層のような柔軟性を有し、熱伝導性の低いものが適する。 Such as polyethylene, polypropylene, ethylene - vinyl acetate copolymer, ethylene - ethyl acrylate copolymer, styrene - butadiene - styrene block copolymer, styrene - isoprene - styrene block copolymer, styrene - ethylene - butadiene - styrene block copolymer, styrene - hydrogenated isoprene - styrene block copolymer, polybutadiene, have a flexibility such as a light-curing resin layer, having a low thermal conductivity is suitable. 具体的には、特願平2001−16934等のクッション層を使用することができる。 Specifically, it is possible to use a cushion layer such as Japanese Patent Application No. 2001-16934.

第1のシート部材と第2のシート部材との間に所定の電子部品と設けた積層構造を形成する方式としては、熱貼合法、接着剤貼合法、接着剤塗布法及び射出成形法が挙げられる。 As a method of forming a laminated structure in which a predetermined electronic component between the first sheet member and the second sheet member, heat lamination method, an adhesive lamination method, the adhesive coating and injection molding can be mentioned It is. また、各部材を貼り合わせる際には、シート基材の表面平滑性や、第1のシート部材と第2のシート部材との間に設ける電子部品の密着性を向上させるために、上下プレス方式、ラミネート方式等により加熱及び加圧を行うことが好ましい。 Further, when bonding the respective members, the surface smoothness of the sheet base material or, in order to improve the adhesion of the electronic component provided between the first sheet member and the second sheet member, vertical press method , it is preferable to perform heating and pressing the lamination method or the like.

本発明においては、上記した被記録体の受像層に、画像情報記録用熱転写シートを用いて、画像情報を印画する。 In the present invention, the image receiving layer of the recording medium as described above, using the image information recording thermal transfer sheet, and printing the image information. 上記したような被記録体と画像情報記録用熱転写シートとを、被記録体の受像層と画像情報記録用熱転写シートの色材層とが対抗するように重ね合わせて、画像情報記録用熱転写シート側から、サーマルヘッド等の加熱手段により加熱して、色材層中の色材を、被記録体の受像層へ熱転写することにより、画像情報を被記録体へ画像情報を印画する。 And the recording medium and the image information recording thermal transfer sheet as described above, are superimposed so that the image-receiving layer and the image information recording thermal transfer sheet color material layer of the recording medium is to counter, the image information recording thermal transfer sheet from the side, is heated by a heating means such as a thermal head, the color material of the color material layer, by thermal transfer to the image receiving layer of the recording medium to print the image information of image information to the recording medium.

画像情報記録用熱転写シート10は、図5に示すように、基材11の一方の面に設けた色材層12を備えたものである。 Image information recording thermal transfer sheet 10, as shown in FIG. 5, but provided with a colorant layer 12 provided on one surface of the substrate 11. 基材11の前記色材層12を設けた面とは反対側の面に耐熱滑性層13を設けてもよい。 It may be provided with a surface opposite to the heat-resistant lubricating layer 13 and the surface provided with the color material layer 12 of the substrate 11. 色材層12は、従来公知の熱転写シートと同様に、イエロー染料層、マゼンタ染料層、シアン染料層とから構成されていてよいが、本発明においては、図6に示すように、シアン染料層(C)、マゼンタ染料層(M)およびイエロー染料層(Y)が面順位に設けられた画像情報記録用熱転写シートを用い、シアン、マゼンタ、およびイエローの順で、各染料を被記録体の受像層へ熱転写して画像情報の印画を行うことが好ましい。 Color material layer 12, as in the conventional thermal transfer sheet, the yellow dye layer, a magenta dye layer, may be composed of a cyan dye layer, in the present invention, as shown in FIG. 6, the cyan dye layer (C), magenta dye layer (M) and the yellow dye layer (Y) is using the image information recording thermal transfer sheet provided on the surface order, cyan, magenta, and in the order of yellow, each dye of the recording medium and thermal transfer to the image receiving layer is preferably performed the printing of the image information. 後記するように、画像情報記録用熱転写シートに使用される昇華性染料として、いわゆるポストキレート色素を用いる場合、ポストキレート色素は、上記の被記録体の受像層中のメタルソースと反応して発色する。 As described later, as a sublimable dye used in the image information recording thermal transfer sheet, when using a so-called post-chelate dye, post chelate dye is reacted with the metal source of the image-receiving layer of the above recording body color to. そのため、必ずしも画像情報記録用熱転写シート上に設けた色材層の色(シアン、マゼンタ、イエロー)と、被記録体へ画像情報を熱転写した後の色(すなわち、受像層で色素染料がメタルソースと反応した後の色)とが同じように発色せず、むしろ全く異なる色となる場合がある。 Therefore, always image information color recording color material layer provided on the thermal transfer sheet (cyan, magenta, yellow) and color after thermal transfer of the image information to the recording medium (i.e., the metal source is a dye dye image-receiving layer reacted without color to color) and the same as after a, it may become completely different colors rather. 熱転写時の熱量が不十分で、色素とメタルソースとの反応が不完全な場合、未反応のポストキレート色素の色が、被転写体の受像層に形成された画像部分に残存するため、画像の色濁りが生じやすくなる。 Heat during thermal transfer is insufficient, when the reaction between the dye and the metal source is incomplete, since the color of the post chelate dye unreacted, remaining in the formed image portion in the image receiving layer of the transfer member, the image is likely to occur is the color turbidity. 特に、メタルソースと反応する前のポストキレートシアン染料やポストキレートマゼンタ染料の濃度は、ポストキレートイエロー染料の濃度と比べて高くなる傾向があるため、ポストキレート反応が不完全であると、被記録体の受像層に熱転写した際に、イエロー染料からなる色成分にシアンやマゼンタ染料が混入して、印画部分に色濁りが生ずる場合がある。 In particular, the concentration of the post-chelate cyan dye and post chelate magenta dye prior to reacting with the metal source, because it tends to be higher than the concentration of the post chelate yellow dye, the post chelating reaction was incomplete, a recording upon thermal transfer image-receiving layer of the body, which may be mixed into the color component consisting of yellow dye is cyan and magenta dye, color turbidity occurs on printing portion. 本発明においては、染料層において染料濃度が高くなる順に、画像情報記録用熱転写シート上に、シアン染料層(C)、マゼンタ染料層(M)およびイエロー染料層(Y)を面順位に設けて、画像形成の際に、シアン、マゼンタ、イエローの順で熱転写を行うことにより、熱転写時に、染料濃度の高い染料ほどより多くの熱エネルギーを付与することができる。 In the present invention, the order in which the dye concentration increases in the dye layer, the image information recording thermal transfer sheet, a cyan dye layer (C), magenta dye layer (M) and the yellow dye layer (Y) provided on the surface Position at the time of image formation, cyan, magenta, by performing thermal transfer in the order of yellow, when the thermal transfer, it is possible to impart more heat energy than the higher the dye concentration dye. その結果、染料濃度の高いシアンやマゼンタ染料が受像層中でのメタルソースとより完全に反応し、所望の染料の発色が得られるため、形成画像の色濁りが生じにくくなる。 As a result, a high cyan and magenta dyes of the dye concentration is more completely react with metal sources in the image-receiving layer, because the color of the desired dye is obtained, color turbidity of the formed image is less likely to occur. 特に、上記のような順で各染料層を設けることにより、シアン染料が熱転写された印画部分のマゼンタ濁りが解消する。 In particular, by providing the respective dye layers in the order as described above, the cyan dye is eliminated magenta turbidity thermally transferred printed portion.

上記したようなポストキレート色素としては、従来公知のものを使用することができ、このようなキレート形成可能な昇華性色素としては、例えば特開昭59−78893号、同59−109349号、特願平2−213303号、同2−214719号、同2−203742号に記載されている、少なくとも2座のキレートを形成することができるシアン色素、マゼンタ色素およびイエロー色素を挙げることができる。 The post-chelate dye as described above, can be conventionally used known ones, as such chelating possible sublimable dyes, for example, JP-A Nos. 59-78893, the 59-109349 JP, JP Gantaira 2-213303 Patent, the 2-214719 Patent, are described in Nos. 2-203742, cyan dye capable of forming a chelate of at least bidentate, it may be mentioned magenta dye and yellow dye. キレートの形成可能な好ましい昇華性色素は、下記一般式で表わすことができる。 Capable of forming a preferred sublimable dye chelates can be represented by the following general formula.
X1−N=N−X2−G X1-N = N-X2-G
(式中、X1は、少なくとも一つの環が5〜7個の原子から構成される芳香族の炭素環、または複素環を完成するのに必要な原子の集まりを表わし、アゾ結合に結合する炭素原子の隣接位の少なくとも一つが、窒素原子またはキレート化基で置換された炭素原子であり、X2は、少なくとも一つの環が5〜7個の原子から構成される芳香族複素環または、芳香族炭素環を表わし、Gはキレート化基を表わす。) (Wherein, X1 represents a group of atoms necessary to complete at least one ring is aromatic comprised 5-7 atoms carbocyclic or heterocyclic ring, carbon bonded to the azo bond at least one adjacent position of atoms is a carbon atom substituted with a nitrogen atom or a chelating group, X2 is at least one ring is five to seven aromatic heterocyclic ring composed of atoms or aromatic represents a carbocyclic ring, G represents a chelating group.)

上記したようなポストキレート昇華性色素の使用量は、通常、基材1m 当たり0.1〜20g、好ましくは0.2〜5gである。 The amount of post-chelate sublimable dyes such as described above, usually, the substrate 1 m 2 per 0.1 to 20 g, preferably 0.2-5 g.

色材層を構成するバインダーとしては、特に制限がなく従来から公知のものを使用することができる。 The binder constituting the color material layer may be a known especially from conventional no limit. さらに前記インク層には、従来から公知の各種添加剤を適宜に添加することができる。 Further, the ink layer can be added appropriately to various known additives conventionally.

画像情報記録用熱転写シートは、インク層を形成する前記各種の成分を溶媒に分散ないし溶解させた塗工液を調製し、これを基材表面に塗工し、乾燥することにより作製することができる。 Image information recording thermal transfer sheet, that the various components forming the ink layer a coating solution prepared by dispersing or dissolving in a solvent, which was coated on the substrate surface is prepared by drying it can. 色材層の厚さは、通常0.2〜10μmであり、好ましくは、0.3〜3μmである。 The thickness of the color material layer is usually 0.2 to 10 [mu] m, preferably from 0.3 to 3 m.

次に、本発明による文字情報記録用熱転写シートと上記画像情報記録用熱転写シートとを用いた情報録体の製造方法の一例を、図面を参照しながら説明する。 Next, an example of a method of manufacturing the information recording body using the character information recording thermal transfer sheet and the image recording and thermal transfer sheet according to the present invention will be described with reference to the drawings.

図7は、本発明による方法の一実施形態を実施するための情報記録体製造装置の概略構成図を示したものである。 Figure 7 is a diagram showing a schematic configuration of an information recording medium manufacturing apparatus for implementing an embodiment of the method according to the invention. 情報記録体製造装置30は、上方位置にカード基材供給部40及び情報記録部50が配置され、下方位置に、透明保護層付与部及び/又は光学変化素子層付与部60、並びに樹脂層形成用塗工液付与部及び/又は活性放射線照射部70が配置されている。 Information recording medium manufacturing apparatus 30, the card substrate supply section 40 and information recording section 50 is disposed in the upper position, the lower position, the transparent protective layer providing unit and / or optical variable device layer providing unit 60, and a resin layer formed use coating liquid application unit and / or the active radiation irradiation section 70 is disposed. 本実施形態においては、一例として、カード状の情報記録体を製造する方法を説明するが、情報記録体としてシート状のものを製造できることは言うまでもない。 In the present embodiment, as an example, is described a method of manufacturing a card-like information recording medium, it is needless to say capable of producing a sheet-like as the information recording medium.

カード基材供給部40には、カード使用者の個人情報を書き込むために予め枚葉状にカットされた複数枚のカード基材1が、顔写真等の画像情報を記録する面(即ち受像層を設けた面)を上に向けてストックされている。 The card substrate supply section 40, a plurality of card substrate 1 was cut in advance sheet form for writing personal information of the card user, the surface (i.e., the image-receiving layer for recording image information, such as face photograph provided the surface) to facing upward are stocked. 本実施形態においては、受像層を備えたカード基材1が1枚ずつ、カード基材供給部40から所定のタイミングで自動供給される。 In the present embodiment, the card base member 1 having an image-receiving layer is one by one, is automatically fed at a predetermined timing from the card substrate supply section 40.

情報記録部50は、図6に示したようなイエロー染料層、マゼンタ染料層およびシアン染料層が面順次に設けられた画像情報記録用熱転写シート10が配置され、その位置に対応してサーマルヘッド51が配置された画像情報記録部52と、図1に示したような熱溶融ブラック色材層とバリア層とがパターニングされて設けられた文字情報記録用熱転写シート20が配置され、その位置に対応してサーマルヘッド53が配置された文字情報記録部54とから構成されている。 Information recording unit 50, yellow dye layer as shown in FIG. 6, the image information recording thermal transfer sheet 10 magenta dye layer and the cyan dye layer are provided sequentially faces are arranged, the thermal head in correspondence with the position 51 an image information recording unit 52 is disposed, the character information recorded thermal transfer sheet 20 and the hot-melt black colorant layer and the barrier layer as is provided by patterning shown in Figure 1 is disposed in that position the thermal head 53 correspondingly is composed of arranged character information recording unit 54. なお、図8に示すような画像情報記録用熱転写シートと文字情報記録用熱転写シートとを兼ねる熱転写シートを用いてもよく、この場合、情報記録部のサーマルヘッドを1つにすることができるため、より装置の簡素化が図られることは言うまでもない。 Incidentally, may be used a thermal transfer sheet which also serves as an image information recording thermal transfer sheet and the character information recorded thermal transfer sheet as shown in FIG. 8, in this case, it is possible to one of a thermal head of the information recording portion , more simplified equipment can of course be achieved.

カード基材供給部40から供給されたカード基材1は、先ず画像情報記録部52において、カード基材1が移動している間に、その受像層の所定領域にカード使用者の顔写真等の諧調を有する画像情報が、画像情報記録用熱転写シートによりイエロー、マゼンタ、シアンの順に記録される。 Card substrate 1 which is supplied from the card substrate supply section 40, first, in the image information recording unit 52, while the card substrate 1 is moving, the card user's face photograph or the like in a predetermined area of ​​the image-receiving layer image information with the gradation is recorded by the image information recording thermal transfer sheet yellow, magenta, in the order of cyan.

受像層への画像情報の熱転写に続いて、カード基材1の所定領域に、カード使用者の氏名やカード発行日等の文字情報が、文字情報記録用熱転写シート20により記録される。 Following transfer of the image information to the image-receiving layer, in a predetermined area of ​​the card substrate 1, character information such as card user name and card issue date is recorded by the character information recording thermal transfer sheet 20. その際、受像層の画像情報が記録されている領域にもサーマルヘッドからの熱エネルギーが付与され、画像情報が記録された受像層中の色材(イエロー染料、マゼンタ染料およびシアン染料)と金属イオン含有化合物とがキレート反応が促進されて、所望の発色及び階調を有する画像情報が形成される。 At that time, even in a region where the image information of the image-receiving layer is recorded is thermal energy applied from the thermal head, the coloring material of the image-receiving layer in which image information is recorded (yellow dye, magenta dye and cyan dye) and a metal ion-containing compound and the chelating reaction is promoted, the image information having a desired color and gradation is formed. 従って、ポストキレート方式により画像情報を形成した情報記録体の製造方法において、本発明では、従来の方法のように画像情報を形成した後にヒートスタンプやホットローラ等による再加熱の工程を必要としない。 Accordingly, in the method of manufacturing an information recording medium formed with the image information by the post chelate method, the present invention does not require a reheating step by heat stamping or hot roller or the like after the formation of the image information as in the conventional method . その結果、優れた発色性と耐光性とを備える画像を被記録体上に形成できるとともに、製造工程を簡略化できるため、製造装置を小型化することができる。 As a result, an image and a good color developing properties and light fastness can be formed on the recording medium, it is possible to simplify the manufacturing process, it is possible to reduce the size of the manufacturing apparatus. また、カード基材に文字情報を記録すると同時に画像情報部分の加熱を行うため、連続して情報記録体を製造する場合の各工程を高速化することができる。 Also, in order to perform heating at the same time the image information portion when recording the text information to the card substrate, it is possible to speed up the process in the case of producing the information recording medium in succession.

免許証やIDカード等の文字情報および画像情報が同一面上に記録された情報記録体においては、人物の顔等が画像情報として記録されることが多いが、一般的に、画像部分は情報記録体の全面積に対して比較的小さい割合である。 In the information recording medium in which character information and image information is recorded on the same surface, such as a driver's license or ID card, is often face or the like of the person is recorded as image information, in general, image portion information it is a relatively small percentage of the total area of ​​the recording medium. そのため、通常は、画像部分の周辺まで文字情報が書き込まれている場合が多い。 Therefore, usually, when the character information to the periphery of the image portion is written in many cases. このよう情報記録体を製造する場合、文字情報を被記録体に熱転写する際に、文字情報記録用熱転写シート用のサーマルヘッドで、先に形成された画像部分の再加熱を行い、ポストキレート染料の発色性を向上させる場合がある。 When producing such information recording medium, when the thermal transfer of character information to the recording medium, a thermal head of the character information for recording thermal transfer sheet, and re-heating of the image portion previously formed, post chelate dye which may improve the color developability. 被転写体への文字情報の記録と同時に、先に形成された画像部分の再加熱行う場合、画像の発色性を向上させるために再加熱を充分にすると、熱溶融ブラック色材により記録した文字情報が影響を受けることがあり、例えば、情報記録体の画像部分の周辺の文字潰れが生じる場合がある。 Simultaneously with the recording of the character information to the transfer receiving material, in the case of reheating image portion previously formed, when sufficient reheating in order to improve the coloring property of images, characters were recorded by hot-melt black colorant information may be affected, for example, may collapse characters around the image of the information recording medium may occur. 特に、再加熱した画像部分の周縁部は熱が伝わりやすくなるため文字記録部分が受ける影響も顕著である。 In particular, the peripheral portion of the reheated image portions influence received character recording part for easily heat is conducted also is remarkable. そのため、文字潰れが生じないような熱量で熱溶融ブラック色材の転写を行う必要があり、同じサーマルヘッド等の加熱手段を用いて先に形成した画像部分を再加熱する場合に、再加熱の熱量が不足することがある。 Therefore, it is necessary to perform the transfer of the hot-melt black coloring material by heat, such as character collapse does not occur, in the case of reheating the image portion previously formed by using a heating means such as the same thermal head, the reheating there is that amount of heat is insufficient.

本発明においては、同じ加熱手段(すなわち、文字情報を記録する際の画像情報記録用熱転写シートへのサーマルヘッド等の熱源)を用いて、文字潰れの解消と再加熱時の熱量増加を行うために、以下のような方法が好ましく適用できる。 In the present invention, the same heating means (i.e., a heat source such as a thermal head to the image information recording thermal transfer sheet for recording character information) is used for performing the heat increase during eliminated and reheating character collapse to, the following method can be preferably applied. 例えば、文字情報を熱転写する際の印画速度を高速化するとともに、熱転写時の熱エネルギーの付与を、高温化かつ短時間化することができる。 For example, with the speed of the printing speed in thermal transfer character information, the application of thermal energy during heat transfer, can be high temperature and shorter time. 例えば、従来の情報記録体を製造する際の印画速度は6.8mm/s程度であったが、これを15〜30mm/s、より好ましくは20mm/s程度とし、熱転写時の熱エネルギーの付与時間を、従来7.5ms/lであったのを、0.5〜5ms/l、より好ましくは1〜3ms/lとする。 For example, the printing speed when manufacturing the conventional information recording medium has been of the order of 6.8 mm / s, which 15 to 30 mm / s, more preferably about 20 mm / s, application of thermal energy during heat transfer time, the was a conventional 7.5ms / l, 0.5~5ms / l, more preferably from 1~3ms / l. なお、「ms/l」とは、1ライン印画(加熱)するのに要する時間(秒数)を意味する。 It is to be noted that the "ms / l" means one line printing (heating) to the time required for the number of seconds. 印画速度を高速化は、熱転写シートの巻き取り装置の速度を上げることにより行われるが、巻き取り装置のモーターは、精度が高くかつ高出力で小型のものを使用することが好ましい。 Faster printing speed is carried out by raising the speed of the winding device of the thermal transfer sheet, the motor of the winding apparatus, it is preferable to use a small one is high and a high output accuracy.

さらに本発明においては、文字潰れの解消と再加熱時の熱量増加を行うために、印画速度や再加熱時の熱量を増加させることの他、画像情報が形成された部分へ供給する熱量を補うため、画像情報形成時にサーマルヘッド周囲の環境温湿度を高めたり、基材の裏面から熱を加える装置を備え付けて、ポストキレート反応を促進させる方法が好ましく用いられる。 Further, in the present invention, in order to perform the heat increase during eliminated and reheating character collapse, other increasing the amount of heat at the time of printing speed and reheated to compensate for the amount of heat supplied to the partial image information is formed Therefore, to enhance the environmental temperature and humidity of the ambient thermal head at the time of image information formed by equipped with a device for applying heat from the back of the substrate, a method of promoting the post chelating reaction is preferably used.

また、熱溶融ブラック色材層とバリア層とを備えた文字情報記録用熱転写シートを用いて、被記録体にブラック色材を熱転写するとともに、被記録体の画像部分をバリア層を介して再加熱する手段として、ヘッド面積の小さなユニットを2つ組み合わせたサーマルヘッドを用いてもよい。 Further, by using the character information recording thermal transfer sheet and a hot-melt black colorant layer and the barrier layer, as well as thermal transfer of black colorant in the recording medium, through the barrier layer an image portion of the recording Regeneration as means for heating, a small unit of the head area may be used two combined thermal head. 2つのユニットからなるサーマルヘッドを用いることにより、画像情報が形成された部分を、文字情報の熱転写時に再加熱する際、文字情報記録用のヘッド(すなわち熱溶融ブラック色材層を熱転写するためのユニット)とは別に、画像情報部分側のヘッドの電圧を上げて熱量を増やすことができ、それによりポストキレート反応をより効率よく促進することができる。 By using a thermal head composed of two units, a portion where image information is formed, when re-heated during thermal transfer of character information, character information recording heads (i.e., to transfer the hot-melt black coloring material layer the unit) separately, by raising the voltage of the image information portion of the head you can increase the amount of heat, thereby promoting more efficient post-chelation reaction.

受像層に画像および文字情報が記録されたカード基材1は、次いで、透明保護層付与部及び/又は光学変化素子層付与部60に移動する。 Receiving layer card substrate 1 on which an image and character information are recorded, the then moves to the transparent protective layer providing unit and / or optical variable device layer providing unit 60. 透明保護層付与部及び/又は光学変化素子層付与部には、保護層転写箔シート61および/または光学変化素子転写箔シート62が配置され、その位置に対応してヒートローラー63が配置されている。 The transparent protective layer providing unit and / or optical variable device layer providing unit, the protective layer transfer foil sheets 61 and / or optical variable device transfer foil sheet 62 is disposed, it is disposed a heat roller 63 in correspondence with the position there.

透明保護層転写箔シート61は、図9に示すように、支持体611その支持体611の一方の面に設けられた透明保護転写層612とから構成され、透明保護転写層612は、支持体611側から順に、離型層613、透明保護層614および接着層615が積層した構造を有する。 Transparent protective layer transfer foil sheet 61, as shown in FIG. 9, it is configured from a support 611 that supports 611 one provided on the surface transparent protective transfer layer 612 of the transparent protective transfer layer 612, the support from 611 to downstream in the mentioned order, with a release layer 613, the transparent protective layer 614 and the adhesive layer 615 has a laminated structure. この透明保護層転写箔シート61は、サーマルヘッド、ヒートローラー、ホットスタンプ等の加熱手段により、透明保護層転写層612が支持体611から剥離して被記録体である基材カード1に転写されるものである。 The transparent protective layer transfer foil sheet 61, a thermal head, heat roller, a heating means such as hot stamp, a transparent protective layer transfer layer 612 is transferred to the substrate card 1 is the recording medium is peeled from the support 611 is shall. また、光学変化素子転写箔シート62は、図10に示すように、支持体621とその支持体621の一方の面に設けられた光学変化素子転写層622とから構成され、光学変化素子転写層622は、支持体621側から順に、離型層623、光学変化素子層624および接着層625が積層した構造を有する。 The optical variable device transfer foil sheet 62, as shown in FIG. 10, is composed of the support 621 and the support 621 one provided on a surface optical variable device transfer layer 622 Prefecture of optical variable device transfer layer 622, in order from the support 621 side, and a release layer 623, an optical variable device layer 624 and the adhesive layer 625 has a laminated structure. この光学変化素子転写箔シート62は、サーマルヘッド、ヒートローラー、ホットスタンプ等の加熱手段により、光学変化素子転写層622が支持体621から剥離して被記録体である基材カード1に転写されるものである。 The optical variable device transfer foil sheet 62, a thermal head, heat roller, a heating means such as hot stamp, is transferred to a substrate card 1 optical variable device transfer layer 622 is the recording medium is peeled from the support 621 is shall.

透明保護層付与部及び/又は光学変化素子層付与部60に移動したカード基材1は、この工程において、適宜、透明保護転写層および/または光学変化素子転写層が転写される。 Transparent protective layer providing unit and / or the card substrate 1 having moved to the optical variable device layer imparting unit 60, in this process, as appropriate, transparent protective transfer layer and / or an optical variable device transfer layer is transferred. 例えば、カード基材1上の画像情報を記録した部分にのみ透明保護転写層61を設けたり、カード基材1上の任意の位置に光学変化素子転写層62を設けたりすることができる。 For example, it is possible or provided only or a transparent protective transfer layer 61 to the recording portion of the image information on the card substrate 1, an optical variable device transfer layer 62 to an arbitrary position on the card substrate 1. カード基材1の画像情報記録部分に透明保護転写層61を設ける際には、上記したように、サーマルヘッド、ヒートロール、ホットスタンプ等の加熱手段を利用して透明保護転写層がカード基材1に熱転写されるため、画像情報部分の再加熱を兼ねることになる。 In providing a transparent protective transfer layer 61 to the image information recording portion of the card substrate 1, as described above, a thermal head, a heat roll, a transparent protective transfer layer card substrate by using a heating means such as hot stamp to be thermally transferred to 1, also serves as the reheating of the image information portion. その結果、受像層中の色材と金属イオン含有化合物とのキレート反応がさらに促進することになり、より優れた発色と階調を有する画像情報をカード基材上に形成することができる。 As a result, the chelating reaction between the colorant and the metal ion-containing compound of the image receiving layer is further accelerated, it is possible to form an image information having a better color and gradation on the card substrate. また、光学変化素子転写層をカード基材上に転写することにより、情報記録体の偽変造を抑制することができる。 Furthermore, by transferring the optical variable device transfer layer on a card substrate, it is possible to suppress the forgery of information recording medium.

上記した透明保護層転写箔シートや光学変化素子転写箔シートは、従来公知のものを使用することができる。 The above-mentioned transparent protective layer transfer foil sheet or an optical variable device transfer foil sheets may be conventionally used known ones. 例えば、透明保護層としては、被記録体に記録された画像情報を保護するために、耐久性や透明性に優れた樹脂であれば、従来公知の何れの樹脂も使用でき、例えば、アクリル樹脂、セルロース系樹脂、ポリビニルアセタール樹脂、ポリエステル樹脂、ポリアミド樹脂、エポキシ樹脂等が挙げられる。 For example, the transparent protective layer to protect the image information recorded on the recording medium, if a resin having excellent durability and transparency, can be used any conventionally known resin such as acrylic resin , cellulose resins, polyvinyl acetal resins, polyester resins, polyamide resins, epoxy resins, and the like. 透明保護層は、例えば、適当な溶剤又は分散液に、上記の樹脂を溶解又は分散させた保護層塗工液を、支持体又は離型層の表面に、厚みが0.5〜5g/m (乾燥基準)程度となるように塗布し、乾燥させることにより形成することができる。 Transparent protective layer, for example, in a suitable solvent or dispersion, a protective layer coating liquid obtained by dissolving or dispersing the above resin, the surface of the support or the release layer, the thickness is 0.5 to 5 g / m 2 was applied to a (dry basis) degree, it can be formed by drying. 透明樹脂層の厚みは0.3〜50μmが好ましく、より好ましくは0.3〜30μm、特に好ましくは0.3〜20μmである。 The thickness of the transparent resin layer is preferably 0.3~50Myuemu, more preferably 0.3~30Myuemu, particularly preferably ordinarily from 0.3 to 20 m.

光学変化素子層としては、従来公知の光学変化素子を用いることができ、例えば、キネグラムのような回折格子の2次元のCG画像であって線画像構成の画像が移動、回転、膨張、縮小等事由に動き、変化する点に特徴があるもの、ピクセルグラムのような画像がポジとネガに変化する点に特徴があるもの、OSD(Optical Security Device)のような色が金色から緑色に変化する点に特徴があるもの、LEAD(Long Economical Anticopy Device)のような画像が変化して見える点に特徴を有するもの、ストライプ型OVD(Optical VariableDevice)、金属箔、および日本印刷学会誌(1998年)第35巻第6号第482〜496頁に記載されているような The optical variable device layer, may be used any of conventionally known optical variable device, e.g., a two-dimensional CG image by the image of the line image configuration the movement of a diffraction grating as a kinegram, rotation, expansion, contraction, etc. motion grounds, which is characterized in that changes, which images, such as pixel grams is characterized in that changes to the positive and negative, like color OSD (Optical Security Device) changes to green from gold characterized in point, LEAD (Long Economical Anticopy Device) which image has a feature that appears to change as a stripe type OVD (Optical VariableDevice), metal foils, and Nippon printing Journal (1998) as described in Vol. 35 No. 6, pp. 482-496 材、特殊な印刷法、特殊なインキ等により形成されたもの、を用いることができる。 Wood, special printing method, those formed by a special ink or the like, can be used. また、ホログラム等も好適に使用できる。 Also, holograms can be preferably used.

また、上記の透明保護層転写箔シートや光学変化素子転写箔シートの支持体としては、ポリエチレンテレフタレート、ポリブチレンテレフタレート等のポリエステル樹脂、ポリエチレン、ポリプロピレン、ポリメチルペンテン等のポリオレフィン樹脂、ポリフッ化ビニル、ポリフッ化ビニリデン、ポリ4フッ化エチレン、エチレン−4フッ化エチレン共重合体、等のポリフッ化エチレン系樹脂、ナイロン6、ナイロン6.6等のポリアミド樹脂、ポリ塩化ビニル、塩化ビニル/酢酸ビニル共重合体、エチレン/酢酸ビニル共重合体、エチレン/ビニルアルコール共重合体、ポリビニルアルコール、ビニロン等のビニル重合体、三酢酸セルロース、セロファン等のセルロース系樹脂、ポリメタアクリル酸メチル、ポリメタアクリル酸エチル、ポ Further, as the support of the transparent protective layer transfer foil sheet or an optical variable device transfer foil sheet, polyethylene terephthalate, polybutylene terephthalate polyester resin, polyethylene, polypropylene, polymethylpentene or the like of polyolefin resins, polyvinyl fluoride, polyvinylidene fluoride, polytetrafluoroethylene, ethylene-tetrafluoroethylene copolymer, polyfluoroethylene resin etc., nylon 6, nylon 6.6 and the like of the polyamide resins, polyvinyl chloride, vinyl chloride / vinyl acetate copolymer polymer, ethylene / vinyl acetate copolymer, ethylene / vinyl alcohol copolymer, polyvinyl alcohol, vinyl polymers such as vinylon, cellulose triacetate, cellulose resins cellophane, polymethyl methacrylate, polymethacrylic acid ethyl, port アクリル酸エチル、ポリアクリル酸ブチル、等のアクリル系樹脂、ポリスチレン、ポリカーボネート、ポリアリレート、ポリイミド等の合成樹脂シート、又は上質紙、薄葉紙、グラシン紙、硫酸紙等の紙、金属箔等の単層体またはこれら2層以上の積層体が挙げられる。 Ethyl acrylate, polybutyl acrylate, acrylic resins and the like, polystyrene, polycarbonate, polyarylate, synthetic resin sheet such as polyimide, or high-quality paper, thin paper, glassine paper, paper such as parchment paper, a single layer such as a metal foil body or these two or more layers of the laminate and the like. 支持体の厚みは10〜200μm、好ましくは15〜80μmである。 The thickness of the support is 10 to 200 [mu] m, preferably 15~80Myuemu.

透明保護層転写箔シートや光学変化素子転写箔シートの離型層としては、高ガラス転移温度を有するアクリル樹脂、ポリビニルアセタール樹脂、ボリビニルブチラール樹脂などの樹脂、ワックス類、シリコンオイル類、フッ素化合物、水溶性を有するポリビニルピロリドン樹脂、ポリビニルアルコール樹脂、Si変性ポリビニルアルコール、メチルセルロース樹脂、ヒドロキシセルロース樹脂、シリコン樹脂、パラフィンワックス、アクリル変性シリコーン、ポリエチレンワックス、エチレン酢酸ビニルなどの樹脂、ポリジメチルシロキサンやその変性物、フッ素化オレフィン、パーフルオロ燐酸エステル系化合物等のフッ素系化合物が挙げられる。 The transparent protective layer transfer foil sheet or release layer of the optical variable device transfer foil sheet, an acrylic resin having a high glass transition temperature, polyvinyl acetal resin, resins such as Helsingborg vinyl butyral resins, waxes, silicone oils, fluorine compounds , polyvinyl pyrrolidone resin having a water-soluble, polyvinyl alcohol resins, Si-modified polyvinyl alcohol, methyl cellulose resin, hydroxypropyl cellulose resin, silicone resin, paraffin wax, acryl-modified silicone, polyethylene waxes, resins such as ethylene vinyl acetate, polydimethylsiloxane or its modified products, fluorinated olefin, fluorine-based compounds such as perfluoro-phosphate ester-based compound.

透明保護層転写箔シートや光学変化素子転写箔シートの接着層としては、熱貼着性樹脂としてエチレン酢酸ビニル樹脂、エチンエチルアクリレート樹脂、エチレンアクリル酸樹脂、アイオノマー樹脂、ポリブタジエン樹脂、アクリル樹脂、ポリスチレン樹脂、ポリエステル樹脂、オレフィン樹脂、ウレタン樹脂、粘着付与剤などが挙げられ、それらの共重合体や混合物でもよい。 The transparent protective layer transfer foil sheet or an adhesive layer of an optical variable device transfer foil sheets, thermal lamination ethylene-vinyl acetate resin as a wear resistant resin, ethyne ethyl acrylate resin, ethylene acrylic acid resins, ionomer resins, polybutadiene resins, acrylic resins, polystyrene resins, polyester resins, olefin resins, urethane resins, include such as tackifiers, or a copolymer thereof or a mixture thereof. 具体的には、ハイテックS−6254、S−6254B、S−3129等(東邦化学工業(株)製)、ジュリマーAT−210、AT−510、AT−613等(日本純薬(株)製)、プラスサイズL−201、SR−102、SR−103、J−4等(互応化学工業(株)製)の市販のものを使用することができる。 Specifically, the high-tech S-6254, S-6254B, etc. S-3129 (manufactured by Toho Chemical Industry Co., Ltd.), JURYMER AT-210, AT-510, AT-613, etc. (Japan Pure Chemical Co., Ltd.) can be used commercially available ones plus size L-201, SR-102, SR-103, J-4, etc. (GOO CHEMICAL Co., Ltd.). 接着層の厚みは0.1〜1.0μm程度である。 The thickness of the adhesive layer is about 0.1 to 1.0 [mu] m.

また、透明保護層転写箔シートや光学変化素子転写箔シートは、支持体、離型層、透明保護層または光学変化素子層、ならびに接着層の各層の接着性を向上させるため、各層の間に中間層としてプライマー層や保護層が設けられていてもよい。 The transparent protective layer transfer foil sheet or an optical variable device transfer foil sheet comprises a support, a release layer, a transparent protective layer or an optical variable device layer, and to improve adhesion of the layers of the adhesive layer, between the layers primer layer and a protective layer may be provided as an intermediate layer.

透明保護転写層61および/または光学変化素子転写層62が転写されたカード基材1は、続いて、活性放射線硬化層付与部及び/又は活性放射線照射部70に移動する。 Transparent protective transfer layer 61 and / or the card substrate 1 in which the optical variable device transfer layer 62 is transferred, subsequently, moved to the active radiation curable layer providing unit and / or the active radiation irradiation section 70. 本工程において、画像/文字情報が記録され、透明保護転写層等が転写されたカード基材1の表面に活性放射線硬化液が塗布され、活性放射線により露光が行なわれ、活性放射線硬化層が形成される。 In this step, the image / character information is recorded, the active radiation curable liquid is applied to the transferred transparent protective transfer layer such as a card substrate 1 of the surface, exposed by actinic radiation is carried out, the active radiation-cured layer is formed It is. 活性放射線硬化層は、カード基材上に記録された文字/画像情報や光学変化素子層等を保護し、情報記録体の耐久性を向上させるために設ける任意の層である。 Active radiation-cured layer is an optional layer provided in order to protect the recorded text / image information and optical variable device layer or the like on a card substrate, thereby improving the durability of the information recording medium.

活性放射線硬化層は、紫外線や電子線等の活性放射線の照射により硬化する樹脂であれば従来公知のものを使用することができ、例えばエポキシ変性アクリレート樹脂、ウレタン変性アクリレート樹脂、アクリル変性ポリエステル等に光重合開始剤、光増感剤を添加した電離放射線硬化性樹脂を使用できる。 Active radiation-cured layer may be used Any known resin that is cured by irradiation with actinic radiation of the ultraviolet or electron beam or the like, for example, epoxy-modified acrylate resins, urethane-modified acrylate resins and acryl-modified polyester photopolymerization initiator, the added ionizing radiation curable resin photosensitizers can be used. 電離放射線硬化樹脂は、これらの樹脂を主成分とする共重合樹脂、または、混合体(アロイを含む)であっても良い。 Ionizing radiation curing resin, a copolymer resin composed mainly of these resins, or may be a mixture (including an alloy).

<情報記録体> <Information recording medium>
上記のようにして得られた情報記録体90は、図11に示すように、カード基材1の受像層3中に画像情報81および文字情報82が記録され、画像情報81が記録された部分には、透明保護転写層61が設けられ、また、カード基材表面の任意の位置に光学変化素子転写層62が設けられている。 Information recording medium 90 obtained as described above, as shown in FIG. 11, image information 81 and the character information 82 is recorded in the image receiving layer 3 of the card substrate 1, part image data 81 is recorded the protective transfer layer 61 is provided a transparent, also the optical variable device transfer layer 62 is provided at an arbitrary position of the card substrate surface. さらに、これら文字情報82、透明保護転写層61、および光学変化素子転写層62を覆うように、活性放射線硬化層71が設けられている。 In addition, these character information 82, the transparent protective transfer layer 61, and to cover the optical variable device transfer layer 62, an active radiation-cured layer 71 is provided. また、カード基材1の受像層3を設けていない側の面には、任意の層として、筆記層や帯電防止層(図示せず)を設けてもよい。 Further, on the side of the surface not provided with the image-receiving layer 3 of the card substrate 1, as an optional layer may be provided a writing layer and an antistatic layer (not shown).

次に、実施例を挙げて、本発明をさらに詳細に説明するが、本発明は、これら実施例に限定されるものではない。 Next, Examples will be described the present invention in more detail, the present invention is not limited to these examples. なお、特に断りのない限り、「部」は質量基準である。 Unless otherwise specified, "parts" are by weight.

実施例1 Example 1
<文字情報記録用熱転写シートの準備> <Preparation of character information recording thermal transfer sheet>
基材として、厚さ4.5μmの易接着処理済みポリエチレンテレフタレートフィルム(ルミラー、東レ株式会社製)を用いた。 As the substrate, with thickness 4.5μm easy-adhesion treated polyethylene terephthalate film (Lumirror, manufactured by Toray Industries, Inc.). 基材の一方の面に、下記の組成の背面層用塗工液をグラビアコーターを用いて塗工し、80℃で1分間乾燥させ、厚さ1.6μmの背面層を形成した。 On one surface of the substrate, the back layer coating solution having the following composition was applied by using a gravure coater, and dried for 1 minute at 80 ° C., to form a back layer having a thickness of 1.6 [mu] m. また、基材の他方の面(易接着処理面)に、図1に示した符合23の部分(Bk)に相当するパターンとなるように、下記の組成の剥離層用塗布液をグラビアコーターにより塗布量が0.3g/m (固形分)となるように塗布、乾燥して剥離層を形成した。 Further, the other surface of the base material (easy-adhesion treated face), so that the pattern corresponding to the portion (Bk) tally 23 shown in FIG. 1, by a gravure coater peeling layer coating solution having the following composition applied so as the coating amount is 0.3 g / m 2 (solid content) and dried to form a release layer.

<背面層用塗工液> <Back layer coating solution>
ポリビニルブチラール樹脂 (エスレックBX−1、積水化学工業株式会社製) 2.0部 リン酸エステル系界面活性剤 (プライサーフA208N、第一工業製薬株式会社製) 1.3部 タルク(ミクロエースP−3、日本タルク工業株式会社製) 0.3部 ポリイソシアネート (バーノックD750−45、大日本インキ化学工業株式会社製) 9.2部 メチルエチルケトン 43.6部 トルエン 43.6部 Polyvinyl butyral resin (S-LEC BX-1, manufactured by Sekisui Chemical Co., Ltd.) 2.0 parts Phosphate ester surfactant (PLYSURF A208N, manufactured by Dai-ichi Kogyo Seiyaku Co., Ltd.) 1.3 parts Talc (MICRO ACE P- 3, Nippon talc Kogyo Co., Ltd.) 0.3 parts of polyisocyanate (BARNOCK D750-45, manufactured by Dainippon Ink and Chemicals, Inc.) 9.2 parts 43.6 parts Methyl ethyl ketone 43.6 parts toluene

<剥離層用インキ> <Ink for the release layer>
塩素化ポリプロピレン 20.0部 溶剤(トルエン/酢酸エチル(質量比1:1)) 80.0部 Chlorinated polypropylene 20.0 parts solvent (toluene / ethyl acetate (mass ratio 1: 1)) 80.0 parts

続いて、剥離層の表面に、下記の組成の熱溶融性ブラックインキ層をグラビアコーターにより塗布量が1.5g/m となるように塗布、乾燥して、熱溶融性ブラックインキ層を形成した。 Subsequently, the surface of the release layer, applying a hot-melt black ink layer having the following composition as weight applied by a gravure coater is 1.5 g / m 2, and dried, the heat-fusible black ink layer formed did.
<熱溶融性インキ層用塗布液> <Hot-melt ink layer coating solution>
カーボンブラック(ダイヤブラック、三菱化学株式会社製) 10.0部 エチレン−酢酸ビニル共重合体(EVAFLEX200W、三井ポリケミカル株式会社製) 10.0部 カルナバワックス 15.0部 パラフィンワックス 60.0部 Carbon black (Diablack, manufactured by Mitsubishi Chemical Corporation) 10.0 parts of ethylene - vinyl acetate copolymer (EVAFLEX200W, Mitsui Poly Chemical Co., Ltd.) 10.0 parts carnauba wax 15.0 parts Paraffin wax 60.0 parts

更に、熱溶融性インキ層の上に、下記組成の感熱接着層用塗布液をグラビアコート法により塗布量が0.2g/m (固形分換算)となるように塗布、乾燥して、接着層を形成した。 Furthermore, on the heat-fusible ink layer, coated heat-sensitive adhesive layer coating solution having the following composition as weight applied by a gravure coating method is 0.2 g / m 2 (solid basis), and dried, the adhesive to form a layer.
<感熱接着層用塗布液> <Heat-sensitive adhesive layer coating liquid>
エチレン−酢酸ビニル共重合樹脂(EVAFLEX#420、三井ポリケミカル株式会社製) 10.0部 溶剤(トルエン) 90.0部 Ethylene - vinyl acetate copolymer resin (EVAFLEX # 420, manufactured by Mitsui Poly Chemical Co., Ltd.) 10.0 parts Solvent (toluene) 90.0 parts

次に、基材上の、剥離層、熱溶融性ブラックインキ層および接着層を設けていない部分(図1の符合23の部分に相当)に、下記の組成のバリア層用塗布液をグラビアコーターにより塗布量が2.0g/m (固形分換算)となるように塗布、乾燥してバリア層を形成することにより、文字情報記録用熱転写シートを作製した。 Next, on the substrate, a release layer, the heat-fusible black ink layer and a portion not provided with the adhesive layer (corresponding to the portion of the sign 23 in FIG. 1), a gravure coater a barrier layer coating solution having the following composition coated amount coated to a 2.0 g / m 2 (solid basis), by drying to form a barrier layer, to prepare a character information recording thermal transfer sheet by.
<バリア層用インキ> <Barrier layer for ink>
ポリスチレン樹脂(デンカスチロールQP−3、電気化学工業株式会社製) 10.0部 シリカ(ニップシールE200A、日本シリカ工業株式会社製) 0.5部 溶剤(メチルエチルケトン/トルエン(質量比1:1)) 90.0部 Polystyrene resin (Denka styrol QP-3, produced by Denki Kagaku Kogyo Kabushiki Kaisha) 10.0 parts Silica (Nipsil E200A, Nippon Silica Kogyo Co., Ltd.) 0.5 parts Solvent (methyl ethyl ketone / toluene (weight ratio 1: 1)) 90 2.0 parts

<画像情報記録用熱転写シートの準備> <Image information preparation of the recording thermal transfer sheet>
基材として、厚さ4.5μmの易接着処理済みポリエチレンテレフタレートフィルム(ルミラー、東レ株式会社製)を用いた。 As the substrate, with thickness 4.5μm easy-adhesion treated polyethylene terephthalate film (Lumirror, manufactured by Toray Industries, Inc.). 基材の一方の面に、文字情報記録用熱転写シートの作製に用いたものと同様の背面層用塗工液をグラビアコーターを用いて塗工し、80℃で1分間乾燥させ、厚さ1.6μmの背面層を形成した。 On one side of a substrate, a character information recording thermal transfer sheet similar back layer coating solution as that used in the production of coated using a gravure coater, and dried for 1 minute at 80 ° C., thickness 1 to form a back layer of .6Myuemu. また、基材の他方の面(易接着処理面)に、下記の組成の染料層用塗工液を厚さ2.0μmの各染料層となるように、イエロー染料層(Y)、シアン染料層(C)、マゼンタ染料層(M)の順に面順次に繰り返し、グラビアコーターを用いて塗布、乾燥することにより、画像情報記録用熱転写シートを作製した。 Further, the other surface of the base material (easy-adhesion treated face), so that each dye layer having a thickness of 2.0μm the dye layer coating solution having the following composition, a yellow dye layer (Y), cyan dye layer (C), the order on the surface sequentially repeated for the magenta dye layer (M), applied with a gravure coater, followed by drying, to produce an image information recording thermal transfer sheet.

<染料層用塗工液> <For the dye layer coating solution>
イエロー染料層用塗工液(Y) Yellow dye layer coating solution (Y)
分散染料(ホロンブリリアントイエローS−6GL) 5.5部 ポリビニルアセタール樹脂(エスレックスKS−5、積水化学株式会社製) 4.5部 リン酸エステル系界面活性剤(プライサーフA208N、第一工業製薬株式会社製) 0.1部 ポリエチレンワックス 0.1部 トルエン 44.9部 メチルエチルケトン 44.9部 Disperse dyes (holon Brilliant Yellow S-6GL) 5.5 parts Polyvinyl acetal resin (LEC KS-5, manufactured by Sekisui Chemical Co., Ltd.) 4.5 parts Phosphate ester surfactant (PLYSURF A208N, manufactured by Dai 44.9 parts Methyl ethyl ketone 44.9 parts Ltd.) 0.1 parts polyethylene wax 0.1 parts toluene

マゼンタ染料層用塗工液(M) Magenta dye layer coating liquid (M)
MS−RED−G MS-RED-G
(ディスパーレッド60、三井東圧化学株式会社製) 1.5部 マクロレックスレッドバイオレットR (Disperse Red 60, manufactured by Mitsui Toatsu Chemicals, Inc.) 1.5 parts macro Rex Red Violet R
(ディスパースバイオレット26 バイエル株式会社製) 2.0部 ポリビニルアセタール樹脂(エスレックスKS−5、積水化学株式会社製) 4.6部 リン酸エステル系界面活性剤(プライサーフA208N、第一工業製薬株式会社製) 0.1部 ポリエチレンワックス 0.1部 トルエン 45.8部 メチルエチルケトン 45.8部 (Disperse Violet 26, Bayer Co., Ltd.) 2.0 parts Polyvinyl acetal resin (LEC KS-5, manufactured by Sekisui Chemical Co., Ltd.) 4.6 parts Phosphate ester surfactant (PLYSURF A208N, manufactured by Dai 45.8 parts Methyl ethyl ketone 45.8 parts Ltd.) 0.1 parts polyethylene wax 0.1 parts toluene

シアン染料層用塗工液(C) Cyan dye layer coating solution (C)
分散染料(カヤセットブルー714) 4.5部 ポリビニルアセタール樹脂(エスレックスKS−5、積水化学株式会社製) 4.5部 リン酸エステル系界面活性剤(プライサーフA208N、第一工業製薬株式会社製) 0.1部 ポリエチレンワックス 0.1部 トルエン 45.4部 メチルエチルケトン 45.4部 Disperse dyes (Kayaset Blue 714) 4.5 parts Polyvinyl acetal resin (LEC KS-5, manufactured by Sekisui Chemical Co., Ltd.) 4.5 parts Phosphate ester surfactant (PLYSURF A208N, Dai-ichi Kogyo Seiyaku Co., Ltd. Ltd.) 0.1 parts 0.1 parts of polyethylene wax toluene 45.4 parts Methyl ethyl ketone 45.4 parts

<ICカードへの画像情報および文字情報の記録> <Recording of image information and character information to the IC card>
ICカードとして、特開2005−174220の実施例(塗液L、接着剤S2使用)のICカードを用いた。 As IC card, using the IC card of the embodiment of JP 2005-174220 (coating liquid L, adhesives S2 used). また、カードプリンタとして、カード表面に2ユニットで印画及び印字を行い、次いで、カード表面に表面保護箔を熱転写する機能を有するIDカード用プリンタ(CX120、日本ビクター株式会社製)を用いた。 Further, as the card printer performs printing and printing with 2 units on the card surface, then using the printer ID card having the function of heat transfer surface protective foil on the card surface (CX120, JVC Co., Ltd.).
上記のようにして得られた画像情報記録用熱転写シートを用いて、下記の印画条件1でICカード上に印画し、続いて、上記のようにして得られた文字情報記録用熱転写シートを用いて、下記の印画条件2で印字した。 Using the image information recording thermal transfer sheet obtained as described above was printed on an IC card printing condition 1 below, followed by using the character information recording thermal transfer sheets obtained in the above Te, it was printed in the print conditions 2 below.

印画条件1(画像情報記録) Printing condition 1 (image information recording)
サーマルヘッド抵抗値:4000(Ω) Thermal head resistance value: 4000 (Ω)
サーマルヘッド電圧値:18(V) Thermal head voltage: 18 (V)
印圧:2.2kg/inch Printing pressure: 2.2kg / inch
印画速度:2.5msec/line Print speed: 2.5msec / line
Duty:75% Duty: 75%
サーマルヘッド解像度:400dpi The thermal head resolution: 400dpi
印画パターン:255階調目 ベタ画像 Print pattern: 255-th gray-scale solid image

印画条件2(文字情報記録) Printing condition 2 (character information recorded)
サーマルヘッド抵抗値:4000(Ω) Thermal head resistance value: 4000 (Ω)
サーマルヘッド電圧値:19(V) Thermal head voltage: 19 (V)
印圧:2.2kg/inch Printing pressure: 2.2kg / inch
印画速度:1.4msec/line Print speed: 1.4msec / line
Duty:熱溶融ブラック色材層部分:60%、バリア層(色材層が無い)部分:40% Duty: hot-melt black colorant layer portion: 60%, (no color material layer) barrier layer portion: 40%
サーマルヘッド解像度:400dpi The thermal head resolution: 400dpi

比較例1 Comparative Example 1
実施例1で使用した文字情報記録用熱転写シートにおいて、バリア層を設けなかった以外は、実施例1と同様にして文字情報記録用熱転写シートを作製し、実施例1と同様にして、ICカードへの画像情報および文字情報の記録を行った。 In the character information recording thermal transfer sheet used in Example 1, except that was not provided a barrier layer, to prepare a character information recording thermal transfer sheet in the same manner as in Example 1, in the same manner as in Example 1, IC card the recording of the image information and character information to went.

評価結果 Evaluation results
印画済みの文字情報記録用熱転写シートの表面に、画像情報が逆転写されているかどうかを目視にて確認した。 The printing already character information recording thermal transfer sheet surface, it was confirmed whether the image information is reverse transcribed visually. その結果、実施例1の文字情報記録用熱転写シートでは、バリア層が設けられているため、画像情報の逆転写は観察されなかった。 As a result, the character information recording thermal transfer sheet of Example 1, since the barrier layer is provided, the reverse transcription of the image information was observed. 一方、比較例1の文字情報記録用熱転写シートでは、その表面の一部に画像情報が逆転写されていることが確認できた。 On the other hand, in the character information recorded thermal transfer sheet of Comparative Example 1, image information can be confirmed to be reverse transcribed in a part of its surface.

1 被記録体(ICカード) 1 the recording medium (IC card)
2 カード基材 3 受像層 10 画像情報記録用熱転写シート 11 基材 12 色材層(YMC) 2 card substrate 3-receiving layer 10 image information recording thermal transfer sheet 11 substrate 12 color material layer (YMC)
13 耐熱滑性層 20 文字情報記録用熱転写シート 21 基材 22 熱溶融ブラック色材層 23 バリア層 30 情報記録体製造装置 40 カード基材供給部 50 情報記録部 60 透明保護層付与部及び/又は光学変化素子層付与部 61 透明保護層転写箔シート 62 光学変化素子転写箔シート 70 樹脂層形成用塗工液付与部及び/又は活性放射線照射部 71 活性放射線硬化層 81 画像情報 82 文字情報 90 情報記録体 13 heat-resistant lubricating layer 20 character information recording thermal transfer sheet 21 substrate 22 thermally fusible black colorant layer 23 barrier layer 30 information recording medium manufacturing apparatus 40 the card substrate supply section 50 the information recording section 60 transparent protective layer providing unit and / or optical variable device layer imparting unit 61 the transparent protective layer transfer foil sheet 62 optical variable device transfer foil sheet 70 resin layer forming coating liquid application unit and / or the active radiation irradiation unit 71 active radiation curable layer 81 image information 82 character information 90 information recording body

Claims (8)

  1. ポストキレート方式により画像形成された被記録体の同一面上に文字情報を記録するために用いられる文字情報記録用熱転写シートであって、 A character information on the same surface of the recording medium on which an image is formed character information recording thermal transfer sheet used for recording by the post chelate system,
    基材と、前記基材上の一部に設けられた色材層と、前記基材上の前記色材層が設けられていない部分に剥離しないように設けられたバリア層と、を少なくとも備え、 Comprising a substrate, a color material layer provided on a part of the substrate, and a barrier layer provided so as not to peel the portion of colorant layer is not provided on the substrate at least ,
    前記バリア層が、前記被記録体上の画像情報が印画された部分と対応し、前記画像情報が文字情報記録用熱転写シートへ逆転写されないようにパターニングされてなることを特徴とする、 文字情報記録用熱転写シート。 The barrier layer, the image information on the recording medium corresponds with printed portions, wherein the image information is formed by patterning so as not to be reverse transcribed to text information recording thermal transfer sheet, character information record for the thermal transfer sheet.
  2. 前記バリア層がスチレン系樹脂からなる、請求項1に記載の文字情報記録用熱転写シート。 The barrier layer is made of a styrene resin, character information recorded thermal transfer sheet according to claim 1.
  3. 前記基材がポリエチレンテレフタレートフィルムからなる、 請求項1または2に記載の文字情報記録用熱転写シート。 It said substrate made of polyethylene terephthalate film, character information recorded thermal transfer sheet according to claim 1 or 2.
  4. 請求項1〜3のいずれか一項に記載の文字情報記録用熱転写シートと、前記文字情報記録用熱転写シートの基材上の一部にシアン染料層、マゼンタ染料層およびイエロー染料層が面順位に設けられている画像情報記録用熱転写シートと、を備えてなり、前記基材上の前記色材層および前記バリア層が設けられていない部分に、前記シアン染料層、前記マゼンタ染料層および前記イエロー染料層が設けられていることを特徴とする、熱転写シート。 And character information recording thermal transfer sheet according to claim 1, wherein the character information cyan dye layer on a part of the recording thermal transfer sheet of the base material, the magenta dye layer and a yellow dye layer surface Position be provided with an image information recording thermal transfer sheet is provided in, on the partial color material layer and said barrier layer is not provided on the substrate, wherein the cyan dye layer, the magenta dye layer and the wherein the yellow dye layer is provided, the thermal transfer sheet.
  5. 字情報および画像情報が同一面上に記録された情報記録体を製造する方法であって、 Character information and image information is a method of manufacturing a recorded information recording medium on the same surface,
    画像情報記録用熱転写シート中の色材とキレート錯体を形成し得る金属イオン含有化合物を含んでなる受像層を備えた被記録体を準備し、 Prepare the recording medium having an image receiving layer comprising a metal ion-containing compound capable of forming a coloring material and chelate complexes of the image information being recorded thermal transfer sheet,
    像情報記録用熱転写シートを用いて、色材を前記被記録体の受像層側に熱転写して画像情報を印画し、 Using images information recording thermal transfer sheet, the image information and printing by thermally transferring the colorant to the image-receiving layer side of the recording member,
    前記受像層上の画像情報形成部以外の部分に、請求項1〜3のいずれか一項に記載の文字情報記録用熱転写シートを用いて、色材を前記被記録体の受像層側に熱転写して文字情報を印画する際に、前記被記録体に印画された前記画像情報形成部の加熱を行う、ことを含んでなることを特徴とする、方法。 A portion other than the image information forming unit on the image-receiving layer, using the character information recording thermal transfer sheet according to any one of claims 1 to 3, the coloring material-receiving layer side of the recording member when printing the character information by the thermal transfer, the performing heating of the image information forming unit which is printed on the recording medium, characterized in that it comprises the method.
  6. 文字情報および画像情報が同一面上に記録された情報記録体を製造する方法であって、 Character information and image information is a method of manufacturing a recorded information recording medium on the same surface,
    画像情報記録用熱転写シート中の色材とキレート錯体を形成し得る金属イオン含有化合物を含んでなる受像層を備えた被記録体を準備し、 Prepare the recording medium having an image receiving layer comprising a metal ion-containing compound capable of forming a coloring material and chelate complexes of the image information being recorded thermal transfer sheet,
    請求項4に記載の熱転写シートの画像情報記録用熱転写シートを用いて、色材を前記被記録体の受像層側に熱転写して画像情報を印画し、 Using the image information recording thermal transfer sheet of the thermal transfer sheet according to claim 4, the image information and printing by thermally transferring the colorant to the image-receiving layer side of the recording member,
    前記受像層上の画像情報形成部以外の部分に、請求項4に記載の熱転写シートの文字情報記録用熱転写シートを用いて、色材を前記被記録体の受像層側に熱転写して文字情報を印画する際に、前記被記録体に印画された前記画像情報形成部の加熱を行う、ことを含んでなることを特徴とする、方法。 A portion other than the image information forming unit on the image-receiving layer, using the character information recording thermal transfer sheet of the thermal transfer sheet according to claim 4, character information by thermally transferring the colorant to the image-receiving layer side of the recording member the when printing, the performing heating of the image information forming unit which is printed on the recording medium, characterized in that it comprises the method.
  7. 前記画像情報形成部の加熱が、前記文字情報記録用熱転写シートから色材を熱転写する際のサーマルヘッドからの熱エネルギーにより行われる、 請求項5または6に記載の方法。 The heating of the image information forming section, the place from the character information recording thermal transfer sheet by the thermal energy from the thermal head at the time of thermal transfer of colorant, a method according to claim 5 or 6.
  8. 前記文字情報記録用熱転写シートから色材を熱転写する際に、前記バリア層が設けられた部分に、サーマルヘッドからの熱エネルギーを付与して、前記被記録体に印画された前記画像情報形成部の加熱を行う、 請求項7に記載の方法。 When thermally transferring colorant from said character information recording thermal transfer sheet, the portion where the barrier layer is provided, by applying the thermal energy from the thermal head, wherein the image information forming unit which is printed on the recording medium performing a heating method according to claim 7.
JP2011053313A 2011-03-10 2011-03-10 Method of manufacturing a thermal transfer sheet and the information recording medium using the same Active JP5720992B2 (en)