JP5698607B2 - ポリエチレン系樹脂積層発泡シートの製造方法 - Google Patents
ポリエチレン系樹脂積層発泡シートの製造方法 Download PDFInfo
- Publication number
- JP5698607B2 JP5698607B2 JP2011123898A JP2011123898A JP5698607B2 JP 5698607 B2 JP5698607 B2 JP 5698607B2 JP 2011123898 A JP2011123898 A JP 2011123898A JP 2011123898 A JP2011123898 A JP 2011123898A JP 5698607 B2 JP5698607 B2 JP 5698607B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- forming
- surface layer
- polyethylene
- core layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
すなわち、ブタンのような脂肪族炭化水素を発泡剤として使用して厚物のポリオレフィン系樹脂発泡シートを製造する場合には、発泡体の発泡後の収縮を抑制しつつも、長期間の養生を必要とせず、かつ機械的強度に優れた発泡体を得る技術は確立されていなかったのが現状である。
本発明は、上記問題点を解決して、押出発泡後の発泡シートの収縮を抑制しながらも、長時間の養生が不要であると共に、圧縮強度等の機械的強度に優れ、更に繰り返し圧縮に対する耐性の大きい厚手のポリエチレン系樹脂積層発泡シートの製造方法を提供することを目的とする。
すなわち、本発明は、以下の(1)から(4)に記載する発明を要旨とする。
(1)ポリエチレン系樹脂とブタンとを混練してなる発泡芯層形成用溶融樹脂と、ポリエチレン系樹脂を基材樹脂とする表面層形成用溶融樹脂とを環状ダイから共押出することにより、発泡芯層の両面に表面層が積層された筒状積層発泡体を形成し、該筒状積層発泡体を押出方向に切開くことにより、発泡芯層の両面に表面層が積層された、積層発泡シート全体の見掛け密度18〜90kg/m3、かつ厚み2mm以上30mm未満の積層発泡シートを製造する方法であって、表面層形成用溶融樹脂には、脂肪酸エステル、脂肪族アミン、及び脂肪酸アミドから選択された1種又は2種以上からなる収縮防止剤が、表面層形成用溶融樹脂のポリエチレン系樹脂100質量部に対して0.7質量部以上の配合割合で配合されており、発泡芯層形成用溶融樹脂には、脂肪酸エステル、脂肪族アミン、及び脂肪酸アミドから選択された1種又は2種以上からなる収縮防止剤が、発泡芯層形成用溶融樹脂のポリエチレン系樹脂100質量部に対して0.7質量部未満の配合割合で配合されている、または脂肪酸エステル、脂肪族アミン、及び脂肪酸アミドから選択された1種又は2種以上からなる収縮防止剤が配合されておらず、積層発泡シート全体の厚みt[mm]に対する片面当たりの表面層の坪量m[g/m2]の比m/tをそれぞれ3〜15とすることを特徴とするポリエチレン系樹脂積層発泡シートの製造方法。
(2)前記発泡芯層形成用溶融樹脂への収縮防止剤の配合割合が、発泡芯層形成用溶融樹脂のポリエチレン系樹脂100質量部に対して0.5質量部以下(ただし、0を含む。)であることを特徴とする前記(1)に記載のポリエチレン系樹脂積層発泡シートの製造方法。
(3)前記表面層形成用溶融樹脂に、炭素数2〜7の脂肪族炭化水素、炭素数4〜7の脂環式炭化水素、炭素数1〜4の脂肪族アルコール、および炭素数2〜8の脂肪族エーテルから選択される1種又は2種以上の有機化合物が配合されていることを特徴とする前記(1)または(2)のいずれかに記載のポリエチレン系樹脂積層発泡シートの製造方法。
(4)前記発泡芯層のポリエチレン系樹脂が低密度ポリエチレンであることを特徴とする前記(1)〜(3)のいずれかに記載のポリエチレン系樹脂積層発泡シートの製造方法。
積層発泡シート1は、発泡芯層形成用溶融樹脂9の両面に、表面層形成用溶融樹脂5を積層して共押出し、発泡芯層形成用溶融樹脂を発泡させることにより製造される。
第1の押出機11の投入口に、表面層を形成するためのポリエチレン系樹脂2と、必要量の収縮防止剤3を供給し、それらを溶融混練した後、必要に応じて有機化合物4を押出機途中から添加し、さらに溶融混練して表面層形成用溶融樹脂5を調整する。第2の押出機12の投入口に、発泡芯層を形成するためのポリエチレン系樹脂6、必要に応じて収縮防止剤7を供給し、それらを溶融混練した後に発泡剤8を押出機途中から添加し、さらに溶融混練して発泡芯層形成用溶融樹脂9を調整する。押出機の下流に備えられた共押出環状ダイ13内で、発泡温度に調整された発泡芯層形成用溶融樹脂9の両面(外面および内面)に表面層形成用溶融樹脂5を積層し、共押出環状ダイ13の先端に設けられた環状のダイリップから該ダイ内よりも低圧下(通常は大気圧下)に共押出して発泡芯層形成用溶融樹脂9を発泡させて、発泡芯層の両面に表面層が積層された筒状積層発泡体を形成し、該積層発泡体を押出方向に切り開くことにより、ポリエチレン系樹脂積層発泡シート1が製造される。
脂肪酸エステルとしては、炭素数8〜30の脂肪酸と水酸基を3〜7個有する多価アルコールとのエステルが好ましい。炭素数8以上の脂肪酸としては、ラウリン酸、オレイン酸、ステアリン酸、ベヘン酸、リグノセリン酸、セロチン酸、ヘプタコ酸、モンタン酸、メリシン酸、ラクセル酸などが挙げられる。水酸基を3〜7個有する多価アルコールとしては、グリセリン、ジグリセリン、トリグリセリン、エリトリットアラビット、キシリマアット、マンニット、ソルビット、ソルビタンなどが挙げられる。
これらのエステル化合物の中でも、これらの完全エステル化物よりは部分エステル化物、特にモノエステル化物がより顕著な収縮防止効果が得られるため好ましく、ステアリン酸モノグリセライド、ベヘン酸モノグリセライド、又はステアリン酸モノグリセライドとベヘン酸モノグリセライドの混合物が更に好ましい。
また、脂肪族アミンとしては、ドデシルアミン、テトラデシルアミン、ヘキサデシルアミン、オクタデシルアミン、エイコシルアミン、ドコシルアミン、N−メチルオクタデシルアミン、N−エチルオクタデシルアミン、ヘキサデシルプロピレンジアミン、オクタデシルプロピレンジアミンなどが挙げられる。
また、脂肪酸アミドとしては、ラウリン酸アミド、ミリスチン酸アミド、パルミチン酸アミド、ステアリン酸アミド、N−メチルステアリン酸アミド、N−エチルステアリン酸アミド、N,N−ジメチルステアリン酸アミド、N,N−ジエチルステアリン酸アミド、ジラウリン酸アミド、ジステアリン酸アミド、トリラウリン酸アミド、トリステアリン酸アミドなどが挙げられる。
発泡後の収縮を防止するためには、両表面付近にのみ収縮防止剤が多く存在して、発泡シート全体からの急激な発泡剤の放散を防げばよいことを見出した。積層発泡シートが冷却した後は、両表面付近には収縮防止剤が多く存在するが、積層発泡シート内部の収縮防止剤の濃度が相対的に少ないので、発泡シート全体に収縮防止剤が高濃度で存在する場合と比べると、積層発泡シートから発泡剤が速く放散していくこととなる。これにより上記効果が得られるものと推察される。
一方、発泡芯層形成用溶融樹脂への収縮防止剤の配合割合(A2)は、発泡剤と空気とのガス置換速度を速めて積層発泡シートの養生時間を短縮するために、表面層形成用溶融樹脂への収縮防止剤の配合割合(A1)よりも低い濃度であり、発泡芯層形成用溶融樹脂のポリエチレン系樹脂100質量部に対して0.7質量部未満(ただし、0を含む。)である。
本発明において、上記発泡芯層および表面層に用いられるポリエチレン系樹脂には、本発明の目的及び効果を阻害しない範囲で、ポリスチレン等のスチレン系樹脂、エチレンプロピレンゴム等のゴム、スチレン−ブタジエン−スチレンブロック共重合体等のエラストマー等のポリエチレン系樹脂以外の重合体を添加することができる。その場合、前記ポリエチレン系樹脂以外の重合体の添加量は40質量%以下、更に20質量%以下、特に10質量%以下とすることが好ましい。
発泡芯層と表面層にそれぞれ用いられる好ましいポリエチレン系樹脂については後述する。
前述の通り、オゾン層破壊や地球温暖化などの環境問題の顕在化によりこれらフロン系の発泡剤は利用が難しくなっている実情から脂肪族炭化水素を用いるようになっているが、本発明においては、ポリオレフィン系樹脂を押出発泡させやすいことから、発泡剤として脂肪族炭化水素の中でもブタンが使用される。ブタンとしては、ノルマルブタン、イソブタン、又はノルマルブタンとイソブタンの混合物が挙げられる。これらの中でも、発泡時に発泡シートから放散しにくいことから、イソブタン又はイソブタンを30モル%以上含むノルマルブタンとイソブタンとの混合物が好ましい。
表面層形成用溶融樹脂に特定の有機化合物が配合され、該溶融樹脂が可塑化されることにより、該溶融樹脂の樹脂温度を発泡芯層の発泡を阻害しない温度まで低下させる冷却調整が可能となると共に発泡芯層に追従する伸長性を付与することができる。このような手段は、特に発泡芯層を高発泡倍率とする場合に効果的であり、表面層に亀裂や裂け等を発生させることなく、表面層を発泡芯層上に積層することが可能となり、さらに発泡芯層の連続気泡率の低い積層発泡シートを製造することが可能になる。また、特定の有機化合物は、押出後表面層から放散していくため、積層発泡シートの機械的強度に影響を与えにくい。
有機化合物としては、炭素数3〜6の脂肪族炭化水素、炭素数4〜7の脂環式炭化水素、炭素数1〜4の脂肪族アルコール、および炭素数2〜8の脂肪族エーテルから選択される1種又は2種以上を使用することができ、特に炭素数3〜6の脂肪族炭化水素が好ましく用いられる。上記炭化水素の使用は、表面層形成用溶融樹脂を効率よく可塑化させるという点から好ましい。上記炭化水素としては、例えば、プロパン、ノルマルブタン、イソブタン、ノルマルペンタン、イソペンタン、シクロペンタン、イソヘキサン、シクロヘキサン、シクロヘプタンなどが挙げられこれらの中でも、ブタンを使用することが好ましい。
発泡芯層形成用溶融樹脂には、前記ポリエチレン系樹脂と、発泡剤としてブタンとが含まれ、更に必要により気泡調整剤、収縮防止剤等が配合される。
発泡芯層形成用溶融樹脂の基材樹脂であるポリエチレン系樹脂としては、190℃におけるメルトフローレイト(MFR)が0.05〜10g/10分、更に0.1〜8.0g/10分、190℃における溶融張力(MT)が3〜30cN、更に3.5〜25cNのポリエチレン系樹脂であることが、目的とする見掛け密度のポリオレフィン系樹脂発泡層を得る上で好ましい。更に該基材樹脂が、密度0.900〜0.935g/cm3のポリエチレン系樹脂を主成分とするものであることが好ましい。尚、メルトフローレート(MFR)は、JIS K7210(1999)A法に準拠して、試験温度190℃、荷重21.18Nで測定される値である。
ここで、上記Tmaxとは、上記テンション荷重曲線において、検出されたピーク(山)値の合計値を検出された個数で除した値であり、上記Tminとは、上記テンション荷重曲線において、検出されたディップ(谷)値の合計値を検出された個数で除した値である。尚、当然のことながら上記測定において溶融樹脂をオリフィスから紐状に押出す際には該紐状物に、できるだけ気泡が入らないようにする。
発泡芯層形成用溶融樹脂における発泡剤の配合量は、目的とする見掛け密度に応じて調整する。即ち、見掛け密度18〜90kg/m3の発泡芯層を得るためには、ブタンの添加量はポリオレフィン系樹脂100質量部当たり3〜35質量部とすることが好ましい。
一方、本発明の積層発泡シートの製造方法で得られる積層発泡シート全体の厚みが厚い場合、シート端部小口(筒状発泡体を切り開いた際の切断面)からも発泡剤が放散しやすくなるため、この小口からの発泡剤の放散を防ぐために発泡芯層にもごく少量の収縮防止剤が配合されることが好ましい。かかる観点から、収縮防止剤の配合量の下限は、該溶融樹脂のポリエチレン系樹脂100質量部に対して0.1質量部であることが好ましく、より好ましくは0.2質量部である。
本発明において、表面層を形成する基材樹脂のポリエチレン系樹脂としては、発泡芯層の基材樹脂と同様のものを使用することができる。発泡芯層との接着性の観点からは、発泡芯層のポリエチレン系樹脂と同種のものを使用することが好ましい。
表面層形成用溶融樹脂への脂肪酸エステル、脂肪族アミン、及び脂肪酸アミドから選択された1種又は2種以上からなる前記収縮防止剤の配合量は、前述の通り、該溶融樹脂のポリエチレン系樹脂100質量部に対して0.7質量部以上であり、該収縮防止剤の配合量が前記範囲未満では収縮防止効果が不充分となる。一方、配合量が多すぎても収縮防止効果が頭打ちとなる。かかる観点から収縮防止剤の配合量は、該溶融樹脂のポリエチレンン系樹脂100質量部に対して0.8〜2.5質量部が好ましく、より好ましくは0.9〜1.5質量部である。
また、表面層の坪量が特定量以上、例えば60g/m2以上となるように共押出することにより、前記有機化合物が発泡剤として作用し、表面層が発泡した積層発泡シートを得ることもできる。また、表面層が発泡した積層発泡シートを得るためには、表面層形成用溶融樹脂には気泡調整剤が配合されることが好ましい。表面層の坪量が小さい場合や、気泡調整剤が配合されていない場合には、表面層が発泡しないことがあり、その場合には、前記有機化合物は、上記可塑剤として作用する。
有機化合物としては、前述の通り、炭素数3〜6の脂肪族炭化水素の使用が好ましく、表面層形成用溶融樹脂を効率よく可塑化させることができることからブタンの使用が特に好ましい。
一方、有機物化合物の添加量が前記20質量部以下であると、有機物化合物が表面層を形成する溶融樹脂と充分に混練されるためダイリップからの有機化合物の噴き出しを防止でき、その結果、積層発泡シートの表面層に穴が開くのを抑制して、所望の収縮防止効果を得ることが可能になる。
すなわち、有機物化合物の配合量を上記範囲とすることで、共押出時の表面層形成用溶融樹脂の溶融粘度低下効果と伸張性向上効果を確保できる。かかる観点から、前記有機化合物の配合量は、ポリオレフィン系樹脂100質量部に対して3〜20質量部であることがより好ましく、さらに好ましくは5〜15質量部である。
図1を用いて、本発明の「ポリエチレン系樹脂積層発泡シートの製造方法」を例示するが、本発明は、図1の例示に限定されるものではない。
表面層形成用溶融樹脂5と発泡芯層形成用溶融樹脂9を、各押出機11、12内においてそれぞれ適正温度に調整してから、合流ダイ13内にて積層して該ダイ13から共押出すことにより、発泡芯層の両面に表面層が積層された積層発泡シートが形成される。
上記溶融樹脂9の押出機12内における適正温度とは、上記溶融樹脂9が発泡芯層を形成するのに最適な粘弾性を示す温度のことである。また上記溶融樹脂5の押出機11内における適正温度は、上記溶融樹脂5が表面層を形成するのに良好な伸長性を示し且つ発泡芯層の形成を阻害しない温度のことである。具体的には、上記溶融樹脂9、5の該適正温度は、それぞれ各層のエチレン系樹脂の[結晶化温度+5℃]以上で[結晶化温度+30℃]以下であり、かつ上記溶融樹脂9、5の該適正温度の関係から、表面層形成用溶融樹脂5の温度が[発泡芯層形成用溶融樹脂の温度−30℃]以上で[発泡層形成用溶融樹脂の温度+30℃]以下であることが、発泡芯層の連続気泡率の低下や得られる積層発泡シートの収縮を抑える観点から好ましく、さらに好ましくは表面層形成用溶融樹脂5の温度が[発泡芯層形成用溶融樹脂の温度−15℃]以上で[発泡芯層形成用溶融樹脂の温度+15℃]以下である。
なお、本明細書において結晶化温度は、JIS K7122(1987)に準拠して測定される値であり、加熱速度10℃/minにて常温から200℃まで加熱して溶融させたサンプルを冷却速度10℃/minにて40℃まで温度を降下させる際に得られるDSC曲線の結晶化熱量ピークの頂点温度を結晶化温度(℃)とする。
すなわち、表面層で発泡剤の散逸を防止し、収縮せず、且つ発泡剤と空気とのガス置換が早い積層発泡シートを得るためには、表面層のガス透過速度をコントロールすることとなるが、その場合、表面層に加えられる収縮防止材の配合量とともに、表面層の樹脂量をコントロールすることが重要である。そのためには、積層発泡シートを製造する際に、押出直後の積層発泡シート全体の厚みt[mm]に対する片面当たりの表面層の坪量m[g/m2]の比m/tを上記範囲内としておけばよい。
前記比率m/tが上記範囲の上限を超えると、当初の目的である養生期間の短縮化が達成できないおそれがある。一方で、前記比率m/tが上記範囲の下限未満になると、収縮防止効果を発揮できず、積層発泡シートが収縮し、かえって所望の密度まで回復するまで長い養生期間をとる必要が出る場合もある。かかる観点から、該比m/tは4〜12とすることが好ましく、より好ましくは4〜10である。
片面あたりの表面層の坪量は、表面層形成用溶融樹脂のポリエチレン系樹脂の吐出量、積層発泡シートの幅、及び積層発泡シート製造時の引取速度から下記式により求めることができる。
片面あたりの表面層の坪量(W1)[g/m2]=
吐出量[g/hr]/(シート幅[m]×引取速度[m/hr])
(1)原材料
(イ)ポリエチレン系樹脂
低密度ポリエチレン(以下、LDPEと記載することがある)
日本ユニカー(株)製、商品名:NUC8321、(密度922g/L、MFR=2.4g/10分)
(ロ)収縮防止剤
ステアリン酸モノグリセライド(表1〜4中、GMSと記載する)
(ハ)気泡調整剤
タルク(松村産業(株)製、ハイフィラー#12)
(イ)押出直後の積層発泡シート全体の厚み
押出直後の積層発泡シートの全体の厚みの測定は、前記の測定法を採用し、押出直後の積層発泡シートの厚みを測定した。
押出直後の積層発泡シート全体の見掛け密度の測定は、以下のようにして行った。押出直後の積層発泡シートからシートの幅方向全体に亘って押出方向に10cmの長さに切り出したサンプルの質量を測定し、該サンプル質量を、前記方法により求めたシートの厚みと、シート幅と、サンプル長さ(具体的には10cm)とから求めたサンプルの体積で割り算し、単位を[g/cm3]に換算することにより、積層発泡シート全体の見掛け密度を求めた。
また、表面層が発泡している場合には、押出直後の表面層の見掛け密度の測定は、以下のようにして行った。押出直後の積層発泡シートからシートの幅方向全体に亘って押出方向に10cmの長さのサンプルを切り出し、さらにサンプルから発泡芯層が含まれないように両表面層を切り分け、該表面層の質量を測定し、水没法により求めた表面層の体積で割り算し、単位を[g/cm3]に換算することにより求めた。
積層発泡シートをその押出後直ちに、温度50℃、相対湿度50%の雰囲気下で保管し、押出から1日経過後に、前記測定方法と同様にして積層発泡シート全体の見掛け密度を求めた。
(ニ)表面層の坪量
表面層の坪量の測定は前記の測定法を採用した。
必要養生日数とは、積層発泡シートを押出直後から50℃、相対湿度50%の雰囲気下で養生した際に、積層発泡シートの比容変化率が±20%以内で、且つ発泡剤(ブタン)残量が1質量%以下となるのに要した日数である。
比容変化率は、発泡直後の積層発泡シートの比容Vaに対する、50℃、相対湿度50%の雰囲気下で任意の期間養生した後の積層発泡体の比容Vbの比である。なお、積層発泡体の比容とは、積層発泡体の見掛け密度の逆数である。
比容変化率[%]=100−(任意の期間養生後の比容Vb[cm3/kg]÷発泡直後の比容Va[cm3/kg])×100
発泡剤残量は以下の方法により求めた。積層発泡シートの発泡層の中心部から、約1g程度の試験片切り出した。この試験片を密閉容器内で既知量のシクロペンタンをトルエンに加えた45mlの溶媒中に常温で24時間浸漬して、試験片中に残存する発泡剤(ブタン)を溶媒中に抽出した。溶媒中に抽出されたブタン量をガスクロマトグラフ(内部標準法)により定量し、予め測定しておいた試験片の質量から、発泡芯層中に残存する発泡剤(ブタン)量を求めた。
養生完了後、上記と同様な方法にて、積層発泡シート全体の見掛け密度および厚みを求めた。
発泡芯層形成用押出機として内径90mmの単軸の第一押出機と内径120mmの単軸の第二押出機を直列に連結した押出機を用いた。表面層形成用押出機として内径115mmの単軸の第三押出機を用いた。該第二押出機の出口に共押出用ダイが取付けられ、該共押出用ダイに第三押出機連結させた共押出装置を用いた。
ポリエチレン系樹脂として低密度ポリエチレン及び収縮防止剤、気泡調整剤を表1に示す配合にて第一押出機に投入し、溶融混練後、同押出機内に発泡剤のブタンとして表1に示す量のイソブタン:ノルマルブタン=30:70(モル比)の混合ブタン(表中SBと記す。)を注入し再び混練した後第二押出機にて目標の樹脂温度まで冷却し、発泡芯層形成用溶融樹脂とした。なお、収縮防止剤、気泡調整剤、ブタンの配合量(質量部)は、発泡芯層形成用溶融樹脂のポリエチレン系樹脂100質量部に対する値である。
同様に、ポリエチレン系樹脂として低密度ポリエチレン及び収縮防止剤、気泡調整剤を表1に示す配合にて第三押出機に供給し、溶融混練後、有機化合物として表1に示す量のイソブタン:ノルマルブタン=30:70(モル比)の混合ブタンを注入し再び混練した後目標の樹脂温度まで冷却し、表面層形成用溶融樹脂とした。なお、収縮防止剤、気泡調整剤、有機化合物の配合量(質量部)は、表面層形成用溶融樹脂のポリエチレン系樹脂100質量部に対する値である。
得られた積層発泡シートの評価結果を表2に示す。なお、実施例7で得られた積層発泡シートの表面層は発泡しており、その密度は61kg/m3であった。また、実施例7以外の実施例、比較例で得られた積層発泡シートの表面層は発泡していなかった。
比較例1および比較例2として、発泡芯層形成用押出機として内径90mmの単軸の第一押出機と内径120mmの単軸の第二押出機を直列に連結した押出機を単独で用いた以外は実施例1と同様にして従来通りの単層の発泡シートを得た。比較例1では収縮防止剤をポリエチレン系樹脂100質量部に対して1.2質量部加え、比較例3では収縮防止剤を全く加えなかった。得られた単層の発泡シートの評価結果を表2に示す。その結果、比較例1の発泡シートは押出後に収縮は生じなかったが、発泡シートからのブタンの放散が遅くガス置換に時間を要し、必要養生日数は4日であった。一方、収縮防止材を加えなかった比較例2の発泡シートは、押出後に著しく収縮してしまった。
2 ポリエチレン系樹脂
3 収縮防止剤
4 有機化合物
5 表面層形成用溶融樹脂
6 ポリエチレン系樹脂
7 収縮防止剤
8 発泡剤
9 発泡芯層形成用溶融樹脂
11 表面層形成用押出機
12 発泡芯層形成用押出機
13 共押出環状ダイ
Claims (4)
- ポリエチレン系樹脂とブタンとを混練してなる発泡芯層形成用溶融樹脂と、ポリエチレン系樹脂を基材樹脂とする表面層形成用溶融樹脂とを環状ダイから共押出することにより、発泡芯層の両面に表面層が積層された筒状積層発泡体を形成し、該筒状積層発泡体を押出方向に切開くことにより、発泡芯層の両面に表面層が積層された、積層発泡シート全体の見掛け密度18〜90kg/m3、かつ厚み2mm以上30mm未満の積層発泡シートを製造する方法であって、
表面層形成用溶融樹脂には、脂肪酸エステル、脂肪族アミン、及び脂肪酸アミドから選択された1種又は2種以上からなる収縮防止剤が、表面層形成用溶融樹脂のポリエチレン系樹脂100質量部に対して0.7質量部以上の配合割合で配合されており、
発泡芯層形成用溶融樹脂には、脂肪酸エステル、脂肪族アミン、及び脂肪酸アミドから選択された1種又は2種以上からなる収縮防止剤が、発泡芯層形成用溶融樹脂のポリエチレン系樹脂100質量部に対して0.7質量部未満の配合割合で配合されている、または脂肪酸エステル、脂肪族アミン、及び脂肪酸アミドから選択された1種又は2種以上からなる収縮防止剤が配合されておらず、
積層発泡シート全体の厚みt[mm]に対する片面当たりの表面層の坪量m[g/m2]の比m/tをそれぞれ3〜15とすることを特徴とするポリエチレン系樹脂積層発泡シートの製造方法。 - 前記発泡芯層形成用溶融樹脂への収縮防止剤の配合割合が、発泡芯層形成用溶融樹脂のポリエチレン系樹脂100質量部に対して0.5質量部以下(ただし、0を含む。)であることを特徴とする請求項1に記載のポリエチレン系樹脂積層発泡シートの製造方法。
- 前記表面層形成用溶融樹脂に、炭素数3〜6の脂肪族炭化水素、炭素数4〜7の脂環式炭化水素、炭素数1〜4の脂肪族アルコール、および炭素数2〜8の脂肪族エーテルから選択される1種又は2種以上の有機化合物が配合されていることを特徴とする請求項1又は2に記載のポリエチレン系樹脂積層発泡シートの製造方法。
- 前記発泡芯層のポリエチレン系樹脂が、低密度ポリエチレンであることを特徴とする請求項1〜3のいずれかに記載のポリエチレン系樹脂積層発泡シートの製造方法。