JP5413772B2 - Co-based metallic glass alloy, magnetic core, electromagnetic transducer and watch - Google Patents

Description

  The present invention relates to a Co-based metallic glass alloy, a magnetic core, an electromagnetic transducer, and a timepiece.

When a mixture containing a specific metal material as a main component and a material containing an element satisfying a predetermined condition is cooled very rapidly from a molten state, an alloy in a random amorphous state before crystals are formed. May be formed. Among such alloys, an amorphous alloy that behaves like a glass in a predetermined temperature range is called “metallic glass”.
Such a metallic glass has, as an index indicating its characteristics, a crystallization start temperature Tx which is a temperature at which crystallization starts, a phase transition temperature which is a glass transition temperature Tg which causes a glass transition, and the entire alloy when heated. Has a liquidus temperature Tl which is a temperature at which becomes a complete liquid state. The difference Tx−Tg between these temperatures is generally defined as the supercooled liquid temperature range ΔTx, and Tg / Tl is defined as the converted vitrification temperature. These ΔTx and Tg / Tl are indicators showing the easiness of forming a metal glass (glass forming ability), and a metal glass having a wider supercooled liquid temperature range ΔTx and a higher converted vitrification temperature Tg / Tl is more stable. Can exist.

In recent years, attention has been paid to excellent mechanical properties such as high strength and low Young's modulus of metal glass and excellent magnetic properties such as high magnetic permeability and soft magnetic properties. For example, motors, generators, antennas, voltage It is applied in various fields as a magnetic core of an electromagnetic converter such as a conversion transformer.
For example, Patent Document 1 discloses a magnetic core made of a metallic glass alloy containing Fe as a main component, and Patent Document 2 discloses a metallic glass alloy containing Co as a main component.

However, the metallic glass alloy mainly composed of Fe of Patent Document 1 has a supercooled liquid temperature range ΔTx as high as 20K or higher, but the frequency range where the relative permeability is as high as about 10,000 is 100 KHz. The magnetic core of an electronically controlled mechanical timepiece used at about 10 Hz cannot exhibit sufficient magnetic properties.
Further, the metallic glass alloy containing Co as a main component in Patent Document 1 has a supercooled liquid temperature range ΔTx as high as 20K or higher and soft magnetic properties, but has a high relative permeability of 20,000 or higher. The frequency region is 1 KHz, and the magnetic core of an electronically controlled mechanical timepiece cannot exhibit sufficient magnetic characteristics as in Patent Document 1.

Japanese Patent No. 3532390 Japanese Patent No. 3877893

  Therefore, the present invention has been made paying attention to the unsolved problems of the above-described conventional example, and is stably present as a metallic glass having a wide supercooled liquid temperature range ΔTx and a large converted vitrification temperature Tg / Tl. Co-based metallic glass alloys that can exhibit excellent magnetic properties at low frequencies, high-performance magnetic cores composed of such Co-based metallic glass alloys, and high-performance electromagnetic conversions comprising this magnetic core To provide a machine and a clock.

In order to achieve the above object, the Co-based metallic glass alloy of the present invention has an Fe content of 2 atomic% to 6 atomic%, an Ni content of 0 atomic% to 4 atomic%, The content is 15 atomic% or more and 20 atomic% or less, the Si content is 8 atomic% or more and 13 atomic% or less, the Nb content is 0 atomic% or more and 3 atomic% or less, and the Mo content is 0.00. A Co-based metallic glass alloy , characterized in that it is 1 atomic% or more and 1 atomic% or less, the Cr content is 0 atomic% or more and 2 atomic% or less, and the balance is Co. Is the supercooled liquid temperature range Δ defined by Tx−Tg, where Tx [K] is the crystallization start temperature, Tg [K] is the glass transition temperature, and Tl [K] is the liquidus temperature of the alloy. Tx is 30K or more, and the conversion vitrification temperature Tg / Tl is 0.58 Thus, the maximum permeability at a measurement frequency of 10 Hz is 80,000 or more.

According to the present invention, the supercooled liquid temperature range ΔTx is wide and can stably exist as a metal glass having a large converted vitrification temperature Tg / Tl, and can exhibit excellent magnetic properties at a low frequency.
Further, according to the present invention, the Co-based metallic glass alloy exhibits a sufficient glass forming ability. Therefore, the metallic glass can be easily obtained by using a special cooling means without cooling at a large cooling rate.
Further, according to the present invention, for example, the Co-based metallic glass alloy of the present invention is particularly suitably used as a magnetic core material for motors and generators used in a low frequency band. That is, in such a magnetic core, the density of magnetic flux passing through the inside of the magnetic core increases as the relative permeability increases, and the performance of the motor or generator can be improved. Therefore, it is possible to obtain a magnetic core exhibiting high performance in a low frequency band.

In the Co-based metallic glass alloy of the present invention, the combined content of Co and Fe is preferably 68 atomic% or more and 71 atomic% or less.
According to this invention, it is possible to increase the relative permeability of the Co-based metallic glass alloy, and to obtain a magnetic core having excellent magnetic properties, for example.
In the Co-based metallic glass alloy of the present invention, the Si content is preferably 10 atomic% or more and 11 atomic% or less.
According to the present invention, the glass forming ability of the Co-based metallic glass alloy can be enhanced by widening the supercooled liquid temperature range ΔTx and increasing the conversion vitrification temperature Tg / Tl.

In the Co-based metallic glass alloy of the present invention, the Mo content is preferably 0.2 atomic% or more and 0.35 atomic% or less.
According to the present invention, the supercooled liquid temperature range ΔTx can be widened, the converted vitrification temperature Tg / Tl can be increased, and the glass forming ability of the Co-based metal glass alloy can be increased, and the relative permeability can be further increased. it can.

The magnetic core of the present invention is preferably composed of the above Co-based metallic glass alloy.
According to the present invention, the density of magnetic flux passing through the inside in the low frequency band is increased, and a high-performance magnetic core can be obtained.
In addition, the magnetic core of the present invention is preferably composed of a molded body formed by molding a powder composed of the Co-based metallic glass alloy, or a sintered body formed by sintering the molded body.

According to the present invention, since the Co-based metallic glass alloy particles are insulated by the resin material, eddy current loss can be reduced. For this reason, a lower-loss magnetic core can be obtained.
In the magnetic core of the present invention, the sintering is preferably performed by discharge plasma sintering.

According to the present invention, in discharge plasma sintering, pulsed electric energy is introduced into the gap between particles of a Co-based metallic glass alloy, and high energy generated by high-temperature plasma generated by spark discharge is used for sintering of particles. Can do. For this reason, especially the surface vicinity of particle | grains is selectively sintered, and each particle | grain can maintain the characteristic of a metallic glass alloy reliably.
In the magnetic core of the present invention, it is preferable that the magnetic core is formed by casting a melt of the Co-based metallic glass alloy.

According to the present invention, a magnetic core having a target shape can be obtained with high dimensional accuracy.
Moreover, the electromagnetic converter of this invention has the magnetic core of this invention, and the coil wound around the outer periphery of this magnetic core, It is characterized by the above-mentioned.
According to the present invention, the density of magnetic flux passing through the inside in a low frequency band is increased, and high performance as an electromagnetic transducer is exhibited.

In the electromagnetic transducer according to the present invention, it is preferable that the cross-sectional shape of the winding portion of the magnetic core in contact with the coil is a circular shape.
According to the present invention, a gap is hardly generated between the outer periphery of the winding portion and the coil wound around the winding portion, and when a voltage is applied to the coil, a larger magnetic flux density is produced with respect to the magnetic core. be able to.

Moreover, it is preferable that the electromagnetic converter of this invention has a passive film containing the element in the said Co group metal glass alloy in the surface which contacts the said coil of the said magnetic core.
According to the present invention, it is possible to easily form the insulating layer for insulating the magnetic core from the coil.
Furthermore, the timepiece of the present invention preferably includes the electromagnetic converter of the present invention. According to the present invention, a high-performance timepiece can be obtained.

It is a figure which shows the relationship between the content rate which combined Co and Fe, and maximum magnetic permeability. It is a figure which shows the relationship between the content rate which combined Co and Fe, and magnetic flux density. It is a figure which shows the relationship between the content rate of Si, and conversion vitrification temperature. It is a figure which shows the relationship between the content rate of Si, and liquidus temperature. It is a figure which shows the relationship between the content rate of Si, and the maximum magnetic permeability. It is a figure which shows the relationship between the content rate of Si, and magnetic flux density. It is a figure which shows the relationship between the content rate of Mo, and conversion vitrification temperature. It is a figure which shows the relationship between the content rate of Mo, and liquidus temperature. It is a figure which shows the relationship between the content rate of Mo, a magnetic flux density, and coercive force. It is a schematic diagram (perspective view) showing the first embodiment of the magnetic core of the present invention. It is a mimetic diagram (longitudinal sectional view) showing a 1st embodiment of an electromagnetic transducer of the present invention. FIG. 2 is a schematic diagram (longitudinal sectional view) showing a configuration of an injection molding apparatus used for manufacturing the magnetic core shown in FIG. 1. It is a schematic diagram (perspective view) showing a second embodiment of the magnetic core of the present invention. FIG. 5 is a schematic diagram (longitudinal sectional view) showing a configuration of an injection molding apparatus used for manufacturing the magnetic core shown in FIG. 4. FIG. 2 is a plan view schematically showing the first embodiment of the timepiece of the invention. It is a top view which shows typically 2nd Embodiment of the timepiece of this invention.

The Co-based metallic glass alloy, magnetic core, electromagnetic transducer and timepiece of the present invention will be described below with reference to the drawings.
[Co-based metallic glass alloy]
First, the Co-based metallic glass alloy of the present invention will be described.
The Co-based metallic glass alloy of the present invention is mainly composed of Co (cobalt), Fe (iron), Ni (nickel), B (boron), Si (silicon), Nb (niobium), Mo (molybdenum) and Cr. (Chromium) is included. The Fe content is 2 atomic% to 6 atomic%, the Ni content is 0 atomic% to 4 atomic%, the B content is 15 atomic% to 20 atomic%, Si content The ratio is 8 atomic% to 13 atomic%, the Nb content is 0 atomic% to 3 atomic%, the Mo content is 0.1 atomic% to 1 atomic%, and the balance is Co. Yes.

Such a Co-based metallic glass alloy has a wide supercooled liquid temperature range ΔTx, a high conversion vitrification temperature Tg / Tl, and is stable. Further, this Co-based metallic glass alloy is excellent in magnetic properties and exhibits high magnetic permeability at a low frequency. For this reason, for example, a magnetic core made of such a Co-based metallic glass alloy has high performance and high reliability.
Here, the supercooled liquid temperature range ΔTx is an index defined by the difference Tx−Tg between the crystallization start temperature Tx, which is the temperature at which the metal glass alloy begins to crystallize, and the glass transition temperature Tg, which is the temperature at which glass transition occurs. It is. This index is an index indicating the easiness of forming a metal glass (glass forming ability), and a metal glass having a wider supercooled liquid temperature range ΔTx can exist stably.

The conversion vitrification temperature Tg / Tl is defined by a value obtained by dividing the glass transition temperature Tg by the liquidus temperature Tl that is the temperature at which the entire alloy becomes a complete liquid state when heated. It is an index indicating ease (glass forming ability), and a metal glass having a higher converted vitrification temperature Tg / Tl can be stably present.
Hereinafter, the content of each constituent element constituting the Co-based metallic glass alloy of the present invention will be sequentially described with reference to FIGS.

Co is a main component of the Co-based metallic glass alloy of the present invention, and mainly has properties such as exhibiting excellent mechanical properties along with excellent soft magnetic properties (soft magnetism) of the Co-based metallic glass alloys. It is an ingredient. In addition, in this invention, a main component means the thing with the highest content rate in each component which comprises Co group metal glass alloy.
Fe is a component having properties such as mainly affecting the saturation magnetic flux density of the Co-based metallic glass alloy and increasing the relative permeability.

  By setting the Fe content to 2 atomic% or more and 6 atomic% or less, a sufficient supercooled liquid temperature range ΔTx can be secured while increasing the saturation magnetic flux density of the Co-based metallic glass alloy. When the Fe content is lower than the lower limit (2 atomic% or more), the saturation magnetic flux density of the Co-based metallic glass alloy is greatly reduced, for example, the magnetic properties of the magnetic core made of the Co-based metallic glass alloy are degraded. On the other hand, when the Fe content exceeds the upper limit (6 atomic% or less), the saturation magnetic flux density of the Co-based metallic glass alloy is improved, but the coercive force is increased, and as a result, the relative permeability is decreased. . For this reason, there is a possibility that the magnetic properties of the magnetic core may be reduced as described above.

Here, when the content ratio of Co and Fe is set to Co: Fe = 94.2: 5.8, it is well known that the magnetostriction is zero and the iron loss is improved. Co and Fe are contained in the content ratio (Co: Fe = 94.2: 5.8).
FIG. 1 and FIG. 2 show the characteristics of the maximum magnetic permeability μm and the magnetic flux density Bm with respect to the change in the content ratio of Co and Fe with the content ratio. As is apparent from FIGS. 1 and 2, when the Co and Fe contents are set to 68 atomic% or more and 71 atomic%, the maximum magnetic permeability μm and the magnetic flux density Bm show the maximum values. Thereby, the relative magnetic permeability of the Co-based metallic glass alloy can be increased, and for example, a magnetic core having excellent magnetic properties can be obtained.

The Ni content is preferably 4 atomic% or less as described above. Since Ni is a component having properties such as mainly affecting the magnetostriction of the Co-based metallic glass alloy, the relative permeability of the Co-based metallic glass alloy is increased by including Ni in a content within the above range. be able to. Thereby, for example, a magnetic core having excellent magnetic characteristics can be obtained.
Since B is an element having an atomic size different from that of Co as a main component, it is a component mainly having properties such as affecting the glass forming ability, that is, the supercooled liquid temperature range ΔTx. A sufficient supercooled liquid temperature range ΔTx can be ensured by setting the B content to 15 atomic% or more and 20 atomic% or less. When the B content is lower than the lower limit (15 atomic%), the supercooled liquid temperature range ΔTx becomes extremely narrow, and the glass-forming ability of the Co-based metallic glass alloy is significantly reduced. On the other hand, when the B content exceeds the upper limit (20 atomic%), the relative magnetic permeability is significantly reduced.

Si is a component having properties such as mainly affecting the viscosity of the supercooled liquid when the Co-based metallic glass alloy of the present invention is in the supercooled liquid state.
3 and 4 show the characteristics of the liquidus temperature Tl and the converted vitrification temperature Tg / Tl with respect to the change in the Si content. 3 and 4, it can be seen that when the Si content changes in the range of 8 to 13 atomic%, the liquidus temperature Tl decreases and the converted vitrification temperature Tg / Tl increases.

  As a result, the Si content is 8 atomic% or more and 13 atomic% or less, thereby optimizing the viscosity of the supercooled liquid of the Co-based metallic glass alloy and improving the formability of the supercooled liquid. The sufficient supercooled liquid temperature range ΔTx and the converted vitrification temperature Tg / Tl can be increased. When the Si content is below the lower limit (8 atomic%), the glass-forming ability of the Co-based metallic glass alloy decreases (the supercooled liquid temperature range ΔTx becomes narrower and the converted vitrification temperature Tg / Tl becomes smaller). . On the other hand, when the Si content exceeds the upper limit (13 atomic%), the supercooled liquid temperature range ΔTx is remarkably narrowed, the converted vitrification temperature Tg / Tl is also reduced, and the glass of the Co-based metal glass alloy Formability is significantly reduced.

  Here, as shown in FIG. 5 and FIG. 6, when the Si content is in the range of 8 atomic% to 13 atomic%, the Si content is 8 atomic% or more and 11 atomic% or less. Maximum magnetic permeability μm and magnetic flux density Bm are maximum values. Thereby, when the Si content is 8 atomic% or more and 11 atomic% or less, the relative magnetic permeability can be increased while enhancing the glass forming ability of the Co-based metallic glass alloy. For example, a magnetic core having excellent magnetic properties can be obtained. Can be obtained.

  Nb is a component having properties such as mainly affecting the magnetostriction of the Co-based metallic glass alloy and affecting the magnetic properties of the Co-based metallic glass alloy. By setting the Nb content to 3 atomic% or less as described above, it is possible to secure a sufficient supercooled liquid temperature range ΔTx while increasing the relative permeability of the Co-based metallic glass alloy. When the Nb content exceeds the upper limit (3 atomic%), the relative permeability of the Co-based metallic glass alloy decreases, and for example, the magnetic properties of a magnetic core made of a Co-based metallic glass alloy decrease.

  Cr is a component mainly having properties such as increasing the specific resistance of the Co-based metallic glass alloy and capable of forming a passive film on the Co-based metallic glass alloy. By setting the Cr content to 2 atomic% or less as described above, it is possible to increase the relative magnetic permeability of the Co-based metallic glass alloy and to obtain a Co-based metallic glass alloy having excellent weather resistance and chemical resistance. As a result, for example, a high-performance and highly reliable magnetic core can be obtained.

A sufficient supercooled liquid temperature range ΔTx can be secured by setting the Mo content to 0.1 atomic% or more and 1 atomic% or less. When the Mo content falls below the lower limit (0.1 atomic%), the supercooled liquid temperature range ΔTx becomes extremely narrow, and the glass-forming ability of the Co-based metallic glass alloy is significantly reduced.
FIGS. 7 to 9 show changes in conversion vitrification temperature Tg / Tl, liquidus temperature Tl, magnetic flux density Bm, and coercive force corresponding to changes in the Mo content.

Here, as shown in FIG. 8, the liquidus temperature Tl is the lowest when the Mo content is 0.3 atomic%, but the Mo containing 0.3 atomic% is composed of B and Si. It plays the role of returning the alloy composition shifted from the eutectic point to the original eutectic point.
7 and 8 that the liquidus temperature Tl decreases and the converted vitrification temperature Tg / Tl increases when the Mo content changes in the range of 0.2 to 0.35 atomic%. . Further, it can be seen from FIG. 9 that when the Mo content is changed in the range of 0.2 to 0.35 atomic%, the magnetic flux density Bm is secured to 500 mT, and the holding force is a minimum value of 1.7 A / m. .

Thereby, conversion vitrification temperature Tg / Tl becomes large, ensuring sufficient subcooling liquid temperature range (DELTA) Tx by making Mo content into 0.2 atomic% or more and 0.35 atomic% or less. The glass forming ability can be increased and the coercive force can be decreased to increase the relative permeability. For example, a magnetic core having excellent magnetic properties can be obtained.
Here, the metallic glass alloy can be obtained by cooling the raw material in a molten state. By cooling, the atomic arrangement of the raw material in a molten state can be fixed, and an alloy having a random atomic arrangement can be obtained. If the supercooled liquid temperature range ΔTx is wide and the converted vitrification temperature Tg / Tl is large, a metal glass alloy can be obtained reliably even when a sufficient cooling rate cannot be ensured.

  From this viewpoint, it is more preferable that the Co-based metallic glass alloy of the present invention has a supercooled liquid temperature range ΔTx of 30 K or higher and a converted vitrification temperature Tg / Tl of 0.58 or higher. When the supercooled liquid temperature range ΔTx and the converted vitrification temperature Tg / Tl are within such ranges, the Co-based metallic glass alloy exhibits sufficient glass forming ability. Therefore, the metallic glass can be easily obtained by using a special cooling means without cooling at a large cooling rate.

Further, when obtaining a bulk metallic glass alloy having a large heat capacity, it can be vitrified reliably even if the internal cooling rate is not sufficiently high. For this reason, a metallic glass alloy having a desired shape can be obtained without being restricted by the shape.
Further, as described above, the Co-based metallic glass alloy of the present invention exhibits soft magnetic properties and high relative magnetic permeability.

By the way, it is known that the relative permeability of a magnetic material changes depending on the measurement frequency.
The Co-based metallic glass alloy of the present invention preferably has a maximum relative magnetic permeability of 80,000 or more at a measurement frequency of 10 Hz. When the maximum relative permeability at a relatively low frequency of about 10 Hz is within the above range, for example, the Co-based metallic glass alloy of the present invention is particularly suitable as a magnetic core material for motors and generators used in a low frequency band. Used. That is, in such a magnetic core, the density of magnetic flux passing through the inside of the magnetic core increases as the relative permeability increases, and the performance of the motor or generator can be improved. Therefore, it is possible to obtain a magnetic core exhibiting high performance in a low frequency band.

  By the way, generally used metal materials are composed of crystalline metals. In this crystalline metal, there are crystal grain boundaries inside, and dislocations within the crystal grains (displacement at the atomic level) occur. Such crystal grain boundaries and intra-grain dislocations promote the progress of cracks generated in the crystal metal, leading to a decrease in the mechanical strength of the metal material. In addition, when crystal grain boundaries near the surface or dislocations within the crystal grains come into contact with the outside air, the metal material may be corroded starting from the contact portion.

  In addition, when a molding is obtained by filling a crystalline metal melt into a mold, the temperature of the melt decreases and crystallization occurs. At the time of this crystallization, atoms in the melt move to a more stable position, so that the resulting molded product is displaced from the mold. That is, there is a problem that transferability at the time of molding is poor.

  On the other hand, as described above, the metallic glass alloy has a random internal arrangement of atoms, so that there is no crystal grain boundary or intra-grain dislocation. For this reason, in the metal glass alloy, it is possible to reliably prevent the deterioration of the mechanical strength and the progress of corrosion, which are problems with the crystalline metal. Therefore, the metallic glass alloy can exhibit excellent mechanical properties and excellent weather resistance and chemical resistance.

  In addition, since no movement of atoms accompanying crystallization occurs during molding, a molded body faithfully reproducing the molding die can be obtained. That is, the metallic glass alloy is excellent in transferability. By taking advantage of such advantages, it is possible to obtain a more complex and fine molded body, or a molded body to which fine characters and patterns are transferred with the metal glass alloy.

[Magnetic core and electromagnetic converter]
<First Embodiment>
Next, a first embodiment of the magnetic core and electromagnetic transducer of the present invention will be described.
FIG. 10 is a schematic diagram (perspective view) showing the first embodiment of the magnetic core of the present invention.
A magnetic core 1 shown in FIG. 10 includes a cylindrical winding part 40 (circular cross-sectional shape is circular), two coil frames 41, 41 provided at both ends of the winding part 40, and each coil frame 41, Connection portions 42 and 42 are provided on the opposite side of the winding portion 40 of 41. The surfaces of the two coil frames 41, 41 facing the winding part 40 are formed with tapered surfaces 41 a, 41 a that are close to each other from the outer peripheral side toward the inner peripheral side. Thus, the magnetic core 1 in which the surfaces facing the winding portions 40 of the two coil frames 41, 41 are tapered surfaces 41a, 41a has good moldability by injection molding.

Moreover, the coil | winding part 40, each coil frame 41 and 41, and each connection part 42 and 42 which are shown in FIG. 10 are integrally formed.
The magnetic core 1 is composed of the aforementioned Co-based metallic glass alloy of the present invention. As described above, the Co-based metallic glass alloy of the present invention has a wide supercooled liquid temperature range ΔTx, a large converted vitrification temperature Tg / Tl, and can exist stably, and has a low frequency. It shows a high magnetic permeability. Therefore, the magnetic core 1 made of such a Co-based metallic glass alloy has a high magnetic flux density that penetrates the inside in a low frequency band, and exhibits high performance as a magnetic core and an electromagnetic transducer to be described later.

Such a magnetic core 1 is used in such a manner that a conducting wire (coil) is wound around the winding portion 40, and is applied to a magnetic core of various electromagnetic converters such as a motor, a generator, an antenna, and a voltage conversion transformer. The
Among these, for example, when the magnetic core 1 is applied to the magnetic core of a motor, the power consumption of the motor can be reduced by improving the magnetic characteristics of the magnetic core. As a result, the battery life of a watch equipped with this motor can be extended.

  In addition, for example, when the magnetic core 1 is applied to the magnetic core of an antenna, the magnetic characteristics of the magnetic core are improved, so that the reception sensitivity of the antenna is improved, power consumption is reduced, and the antenna is downsized while maintaining the reception sensitivity. It becomes possible to plan. As a result, for example, the battery life of a timepiece equipped with this antenna can be extended and the timepiece can be downsized.

FIG. 11 is a schematic diagram (longitudinal sectional view) showing the first embodiment of the electromagnetic transducer of the present invention.
The electromagnetic transducer 2 shown in FIG. 11 has a magnetic core 1 and a conductive wire (coil) 43 wound around the winding portion 40 of the magnetic core 1 over a plurality of layers. And the outer diameter of the wound conducting wire 43 is substantially equal to the outer diameter of each coil frame 41.
As described above, since the winding portion 40 has a cylindrical shape (the cross-sectional shape is circular), the conductive wire 43 is wound around the winding portion 40 so as to draw an arc. In such a configuration, since the outer periphery of the winding portion 40 that contacts the conducting wire 43 is a curved surface, the conducting wire 43 is prevented from being bent compared to a conventional magnetic core having a prismatic winding portion. can do.

Further, since the surfaces of the two coil frames 41, 41 facing the winding portion 40 are formed as tapered surfaces 41a, 41a that are close to each other from the outer peripheral side toward the inner peripheral side, the conductive wire 43 overlaps with a plurality of layers. It becomes easy. For this reason, disconnection of the conducting wire 43 due to contact between the conducting wire 43 and the winding portion 40 can be reliably prevented.
Moreover, the conducting wire 43 has an insulating coating on the surface. Since the winding portion 40 of the present embodiment has a cylindrical shape as described above, it is possible to reliably prevent damage to the insulating coating. Thereby, insulation between the conducting wires 43 can be more reliably ensured.

  In the present embodiment, the conductive wire 43 and the magnetic core 1 are insulated from each other by the insulating film provided in the conductive wire 43, but this insulation method is not particularly limited. For example, an insulating layer is formed on the outer periphery of the winding portion 40. You may make it do. This insulating layer is composed of, for example, an insulating tape, various insulating layers made of an organic insulating material or an inorganic insulating material, and an insulating layer (passive film) containing an element in a Co-based metal glass alloy. Can do.

Of these, the insulating layer is preferably composed of a passive film. This passive film can be formed by leaving the magnetic core 1 in the air or by oxidation treatment. Therefore, the insulating layer can be easily formed without winding the insulating tape or forming a separate insulating layer.
Further, since the winding portion 40 has a cylindrical shape, there is an advantage that a gap is hardly generated between the conductive wire 43 wound around the winding portion 40 and the outer peripheral surface of the winding portion 40. Thereby, for example, when a voltage is applied to the conducting wire 43, a larger magnetic flux density can be provided to the magnetic core 1.

By the way, for example, when a voltage is applied to both ends of the conducting wire 43, a magnetic field is generated in the winding portion 40 of the magnetic core 1 along with the current flowing through the conducting wire 43. This magnetic field passes through the coil frame 41 from the winding part 40 and reaches the connection part 42.
In the magnetic core 1 shown in FIG. 10, as described above, the winding portion 40, the coil frames 41 and 41, and the connection portions 42 and 42 are integrally formed, so that a magnetic field passes between these portions. It becomes easy to do. For this reason, the magnetic flux density in the connection part 42 becomes high, and the performance of the magnetic core 1 can be improved more.

  Further, as shown in FIG. 10, the end portions of the connection portions 42, 42 on the side opposite to the winding portion 40 are comb-shaped. Thereby, for example, by connecting the comb teeth portions of other members (not shown) to the respective comb teeth portions, it is difficult to generate a gap between each of the connection portions 42 and 42 and the other members. Become. Thereby, it is possible to prevent a demagnetizing field from being generated in the gap, and to prevent the magnetic characteristics of the magnetic core 1 from deteriorating. As a result, the magnetic core 1 can be used as, for example, a higher performance motor magnetic core.

Such a magnetic core 1 can be manufactured using, for example, an injection molding apparatus (casting apparatus) 100 as shown in FIG. In the following description, the upper side in FIG. 3 is referred to as “upper” and the lower side is referred to as “lower”.
An injection molding apparatus 100 shown in FIG. 12 includes an apparatus main body 101, a cylindrical sleeve 102 provided in the apparatus main body 101, an induction coil 103 wound around the outer periphery of the sleeve 102, and the inside of the sleeve 102 in the vertical direction. A movable piston 104 and a mold 110 disposed on the upper part of the apparatus main body 101 are provided. A cavity 111 is provided in the mold 110, and the inside of the sleeve 102 and the cavity 111 communicate with each other via a flow path (gate) 112. Moreover, the injection molding apparatus 100 has a decompression means (not shown), and can decompress the inside of the sleeve 102, the cavity 111, and the flow path 112.

  The sleeve 102 of the injection molding apparatus 100 has a function of storing a raw material and a molten metal (melt) obtained by melting the raw material. Such a sleeve 102 is made of a high heat resistant material such as quartz glass or ceramics. The induction coil 103 functions as a heating means that generates an eddy current in the raw material by applying a high-frequency voltage and causes the raw material to self-heat. Such heating means can be replaced by other heating means such as arc heating and gas heating.

  The molding die 110 obtains a molded body corresponding to the shape of the cavity 111 by solidifying the molten metal filled in the cavity 111 in the cavity 111. As described above, when obtaining a metallic glass alloy, it is necessary to rapidly cool the molten metal. Therefore, the mold 110 has cooling means (not shown) for cooling the molten metal injected into the cavity 111. doing. Examples of such cooling means include a heat exchanger using a refrigerant. From this point of view, the mold 110 is preferably made of a material having excellent heat resistance and excellent thermal conductivity. Thereby, the molten metal injected into the cavity 111 can be rapidly cooled.

Next, a method for manufacturing a magnetic core using the injection molding apparatus 100 shown in FIG. 12 will be described.
[1] First, the constituent element material for obtaining the Co-based metallic glass alloy of the present invention is weighed according to the content of each constituent element described above to obtain a raw material.
[2] Next, this raw material is placed on the piston 104 in the sleeve 102 of the injection molding apparatus 100. Then, the inside of the sleeve 102, the cavity 111, and the flow path 112 are decompressed by the decompression means. Subsequently, a high frequency voltage is applied to the induction coil 103 to heat the raw material in the sleeve 102 to a predetermined temperature. Thereby, a raw material is melt | dissolved and a molten metal (melt) is obtained.
[3] Next, the mold 110 is cooled. Subsequently, the piston 104 is moved upward. As a result, the molten metal on the piston 104 is injected into the cavity 111 through the flow path 112. The molten metal injected into the cavity 111 is rapidly cooled by contacting the inner wall of the cavity 111. Thereby, each atom which existed randomly in the molten metal is solidified in a state where the random arrangement is preserved. As a result, the molten metal becomes a metallic glass alloy in which atoms are randomly arranged. Then, the shape of the cavity 111 can be faithfully reproduced, and a magnetic core having a desired shape can be obtained with high dimensional accuracy.
[4] Next, the mold 110 is opened and the magnetic core is taken out.

As described above, the magnetic core 1 shown in FIG. 1 can be manufactured.
The magnetic core 1 obtained by such a method is substantially composed entirely of a metallic glass alloy. For this reason, the ratio (space factor) which a metal glass alloy accounts in the magnetic core 1 becomes very high, and the magnetic flux density of the magnetic core 1 improves in connection with it. As a result, a higher performance magnetic core 1 can be obtained.

  After that, it is preferable to subject the obtained winding portion 40 of the magnetic core 1 to an oxidation treatment. As a result, the above-described insulating layer made of an oxide of a Co-based metallic glass alloy is formed on the surface of the winding portion 40. If the insulating layer is formed by such a method, it is possible to omit the trouble of covering the surface of the winding portion with an insulating material such as an insulating tape as in the prior art, thereby simplifying the manufacturing process and reducing the cost. Can be planned.

Second Embodiment
Next, a second embodiment of the magnetic core and electromagnetic transducer of the present invention will be described.
FIG. 13 is a schematic view (perspective view) showing a second embodiment of the magnetic core of the present invention.
Hereinafter, although the second embodiment will be described, the description will focus on the differences from the first embodiment shown in FIG. 10, and the description of the same matters will be omitted.
The magnetic core and electromagnetic transducer of the present embodiment are the same as those of the first embodiment except that the constituent material of the magnetic core and the manufacturing method are different.
The magnetic core 1a shown in FIG. 13 is composed of the aforementioned Co-based metallic glass alloy powder of the present invention and a resin material that insulates the particles in the powder.

  In such a magnetic core 1a, the particles of the Co-based metallic glass alloy are insulated by the resin material, so that the eddy current loss can be reduced. For this reason, a lower-loss magnetic core can be obtained. Further, as described above, the Co-based metallic glass alloy of the present invention can exhibit excellent magnetic properties at a low frequency, so that a magnetic core exhibiting high performance at a low frequency range can be obtained.

The magnetic core 1a can be manufactured using, for example, an injection molding apparatus 200 as shown in FIG. In the following description, the upper side in FIG. 14 is referred to as “upper” and the lower side is referred to as “lower”.
An injection molding apparatus 200 shown in FIG. 14 includes a molding die 201, a cavity 202 provided in the molding die 201, a nozzle 203 that injects molten metal into the cavity 202, and a flow that connects the nozzle 203 and the cavity 202. And a road (gate) 204.

Next, a method for manufacturing the magnetic core 1a using the injection molding apparatus 200 shown in FIG. 14 will be described.
[1] First, the constituent element material for obtaining the Co-based metallic glass alloy of the present invention is weighed according to the content of each constituent element described above to obtain a raw material.
[2] Next, this raw material is heated and melted to obtain a molten metal (melt).
[3] Next, the obtained molten metal is pulverized and rapidly cooled and solidified to obtain a powder composed of a Co-based metallic glass alloy. As a method for powderizing and cooling, various atomizing methods such as a water atomizing method, a gas atomizing method, and a high-speed rotating water atomizing method can be used. According to the atomizing method, extremely fine powder can be produced efficiently. In addition, since the particles in the powder produced by the atomizing method have a spherical shape close to a true sphere, the particles are excellent in dispersibility and fluidity. For example, a composition containing such powder is used as a mold. When filling, there is an advantage that the filling property is increased.

[4] Next, the obtained powder and the resin material are kneaded to obtain a kneaded product. By this kneading, the powder and the resin material are uniformly dispersed in the kneaded product. Examples of the resin material include polyolefins such as polyethylene, polypropylene, and ethylene-vinyl acetate copolymer, acrylic resins such as polymethyl methacrylate and polybutyl methacrylate, styrene resins such as polystyrene, polyvinyl chloride, polyvinylidene chloride, Various resins such as polyesters such as polyamide, polyethylene terephthalate, polybutylene terephthalate, polyethers, polyvinyl alcohol, or copolymers thereof, various waxes, paraffins, higher fatty acids (eg stearic acid), higher alcohols, higher fatty acid esters Higher fatty acid amides, etc., and one or more of these can be used in combination.

A plasticizer may be added to the kneaded product. Examples of the plasticizer include phthalic acid esters (eg, DOP, DEP, DBP), adipic acid esters, trimellitic acid esters, sebacic acid esters, and the like, and one or more of these are mixed. Can be used.
Furthermore, in addition to the powder, the resin material, and the plasticizer, various additives such as an antioxidant, a degreasing accelerator, and a surfactant can be added to the kneaded material as necessary. The kneaded product may be pelletized (small lumps) as necessary.

[5] Next, the obtained kneaded material or pellets thereof are injected into the cavity 202 from the nozzle 203 of the injection molding apparatus 200 shown in FIG. Thereby, the kneaded material is filled in the cavity 202, and a molded body having a magnetic core shape is obtained.
[6] Next, the obtained molded body is subjected to heat treatment. Thereby, a molded object hardens | cures and the magnetic core 1a comprised with the powder and resin material of Co group metal glass alloy is obtained.

  Examples of such heat treatment include discharge plasma sintering, sintering in a firing furnace, and sintering by microwave or millimeter wave irradiation. Among them, heat treatment by discharge plasma sintering is preferable. In the discharge plasma sintering, pulsed electric energy is introduced into the gap between the particles of the Co-based metallic glass alloy, and high energy by the high temperature plasma generated by the spark discharge can be used for the sintering of the particles. For this reason, especially the surface vicinity of particle | grains can be selectively sintered and each particle | grain can maintain the characteristic of a metallic glass alloy reliably.

[clock]
The electromagnetic transducer as described above can be incorporated in a watch, for example. Hereinafter, the timepiece of the present invention provided with the electromagnetic transducer of the present invention will be described.
<< First Embodiment >>
FIG. 15 is a plan view schematically showing the first embodiment of the timepiece of the invention, and shows a timepiece 500 using an electronically controlled mechanical timepiece as an example.
This watch 500 includes an barrel wheel 501, a second wheel 506, a third wheel 507, a second hand wheel 508, a forty-fourth wheel (intermediate wheel) 509, a fourth wheel 510, a fifth wheel 511, a sixth wheel 512, and It has mechanical parts such as gears of the rotor 513.

  The barrel complete 501 has a mainspring, barrel barrel gear, barrel barrel true, and barrel barrel lid (all not shown). Then, the rotational energy of the mainspring is transmitted from the barrel complete 501 to the second wheel & pinion 506, then accelerated, and transmitted to the third wheel & pinion 507. Subsequently, the data is transmitted from the third wheel & pinion 507 to the forty-second wheel & pinion 509 via a second hand wheel 508 that drives a second hand (not shown) of the timepiece 500. Thereafter, the speed is further transmitted from the forty-fourth wheel 509 to the fourth wheel 510, the fifth wheel 511, the sixth wheel 512, and the rotor 513 while further increasing the speed.

The timepiece 500 includes a generator 520 including a rotor 513, a stator 521, a first coil block 522, a second coil block 523, and a joint 524.
The stator 521 forms part of the magnetic circuit of the generator 520, and has an arrangement hole 521a in which the rotor magnet is arranged, so that the magnetic flux of the rotor 513 is linked.

  The first coil block 522 and the second coil block 523 are formed by winding coils (conductive wires) around the magnetic cores 522a and 523a, respectively. The magnetic cores of the present invention are used as the magnetic cores 522a and 523a, and the electromagnetic transducers of the present invention are used as the first coil block 522 and the second coil block 523. Thereby, the magnetic characteristics of the first coil block 522 and the second coil block 523 are improved, and the power generation performance of the generator 520 can be significantly increased.

  In addition, the stator 521 and the joint 524 can be made of the Co-based metallic glass alloy of the present invention. Thereby, the power generation performance of the generator 520 is further improved. As a result, the rotational energy of the mainspring can be used efficiently, the driving time of the timepiece accompanying one winding of the mainspring can be extended, and the higher-performance timepiece 500 can be obtained.

In such a generator 520, when the mainspring in the barrel complete 501 is wound up, torque output when the mainspring is unwound is transmitted from the barrel complete to the rotor 513 via the wheel train of the sixth wheel 512, and the rotor 513. , An alternating voltage is induced in each of the coil blocks 522 and 523.
The AC output from the generator 520 is boosted and rectified through a rectifier circuit configured by boost rectification, full-wave rectification, half-wave rectification, transistor rectification, and the like, and is charged into a smoothing capacitor. A control circuit (not shown) that controls the rotation of the generator 20 with the electric power from the capacitor is operated. The control circuit has an integrated circuit (IC) including an oscillation circuit, a frequency dividing circuit, a rotation detection circuit, a rotation speed comparison circuit, an electromagnetic brake control means, and the like. The oscillation circuit has a crystal resonator.

The mainspring in the barrel complete 501 is wound up by rotating the square hole wheel 504 shown in FIG.
The method of rotating the square hole wheel 504 is performed via the kite wheel 531, the round hole wheel 532, and the square hole intermediate wheel 533 by operating a winding stem 530 connected to a crown (not shown). The rotation direction of the square hole wheel 504 is regulated by the kohaze 504a. Similarly, the minute hand and the hour hand are adjusted by operating the winding stem 530 through the pinion wheel 534, the small iron wheel 535, the minute intermediate wheel 536, and the minute wheel 537. The drive system is stopped by bringing the control lever 538 into contact with the fifth wheel & pinion 511. Since these mechanisms are the same as those of a general mechanical timepiece automatic winding or manual winding mechanism, further detailed description is omitted.

<< Second Embodiment >>
Next, FIG. 16 is a plan view schematically showing a second embodiment of the timepiece of the invention, which is a radio-controlled timepiece having a function of receiving a standard radio wave on which time information is superimposed and correcting a display time. An example of a watch 600 is shown. In the following description, the front side of the sheet in FIG. 16 is referred to as “up” and the back side of the sheet is referred to as “down”. FIG. 16 is drawn with the case for storing the movement of the watch omitted.

  The movement of the timepiece 600 includes a main plate 681, two stepping motors 682 for driving a pointer (not shown) composed of a second hand, a minute hand, and an hour hand, and an illustration for transmitting the rotational motion of these stepping motors 682 to the pointer. Circuit block 685 including a train wheel not to be connected, a battery (drive source) 683, a CPU (control means) 684 for controlling the operation of the timepiece 600, and a radio wave receiving antenna for receiving standard radio waves (the electromagnetic converter of the present invention) 690. A winding stem 686 is provided in the 3 o'clock direction of the timepiece 600 to manually adjust the position of the pointer.

  The stepping motor 682 includes a stepping motor 682A for the second hand and a stepping motor 682B for the minute hand and hour hand. The stepping motor 682A is disposed in the approximately 600 o'clock direction of the timepiece 600, and the stepping motor 682B is disposed in the approximately 5 o'clock direction of the timepiece 600. These stepping motors 682A and 682B are connected to the pointer in the center of the movement through independent wheel trains, so that the second hand, the minute hand, and the hour hand can be driven independently.

The battery 683 is a primary battery or a secondary battery. Such a battery 683 is arranged in a direction from approximately 1 o'clock to approximately 2 o'clock of the timepiece 600, and is electrically connected by a battery retainer 6831 having a spring property and is held by the main plate 681.
The circuit block 685 includes a quartz oscillator 6851 for timing which oscillates a reference clock, the above-described CPU 684, a bandpass filter crystal oscillator (not shown) that selectively allows a standard radio wave signal to pass through, and a radio wave receiver. And a receiving IC (receiving circuit) 687 for processing the standard radio wave received by the antenna 690. Such a circuit block 685 is sandwiched between the circuit holder and the ground plane 681 and is fixed to the ground plane 681 using a fixing means such as a screw.

  The time-measurement crystal resonator 6851 is arranged in the approximately 3 o'clock direction of the timepiece 600. For example, in Japan, two crystal resonators for bandpass filters are provided: a crystal resonator for filtering a standard radio wave of 60 kHz and a crystal resonator for filtering a standard radio wave of 40 kHz. In addition, for example, in Europe and the United States, a crystal unit for 60 kHz and a crystal unit for 77.5 kHz may be used.

The CPU 684 is arranged in the direction from about 9 o'clock to about 11 o'clock of the timepiece 600, a frequency dividing circuit that divides the frequency from the crystal resonator 6851 and generates a reference clock, and counts the reference clock to determine the time. A timing circuit for timing, a control circuit for controlling the operation of the stepping motors 682A and 682B based on a signal from the timing circuit, and the like are provided.
The reception IC 687 includes a demodulation circuit that demodulates a standard radio wave received by the radio wave reception antenna 690, an amplification circuit that amplifies a reception signal, and the like.

  The radio wave receiving antenna 690 is disposed in the movement and is disposed in the approximately 9 o'clock direction of the timepiece 600 and occupies a space from approximately 7 o'clock to approximately 12 o'clock. Here, the radio wave receiving antenna 690 is disposed at a position away from the battery 683 in the movement. Thereby, when the radio wave receiving antenna 690 receives the standard radio wave, the influence of the metal outer can of the battery 683 on the reception of the standard radio wave can be minimized. In addition, since the radio wave receiving antenna 690 and the receiving IC 687 are arranged close to each other in the movement, when the received signal flows from the radio wave receiving antenna 690 to the receiving IC 687, signal deterioration and noise are mixed. As a result, the reception IC 687 can perform signal reception satisfactorily. Note that the CPU 684 and the stepping motor 682A are preferably arranged on the inner side (center side) of the radio wave receiving antenna 690 as long as they do not interfere with the radio wave receiving antenna 690.

In this embodiment, the electromagnetic exchange of the present invention is used as the radio wave receiving antenna 690. Thereby, the reception sensitivity of the radio wave receiving antenna 690 in the standard radio wave reception can be greatly increased. As a result, power consumption required for radio wave reception by the radio wave receiving antenna 690 can be reduced, and the life of the battery 683 can be extended.
As described above, the Co-based metallic glass alloy, the magnetic core, the electromagnetic exchange, and the timepiece of the present invention have been described based on the preferred embodiments, but the present invention is not limited thereto. For example, in the above-described embodiment, the case where the magnetic core and the electromagnetic exchange according to the present invention are used in a timepiece has been described as a representative. Moreover, each part of the magnetic core of this invention, an electromagnetic switch, and a timepiece can be substituted with the thing of the arbitrary structures which can exhibit the same function. In addition, each part of the magnetic core, the electromagnetic exchange, and the timepiece of the present invention may be a combination of a plurality of configurations described in the above embodiments.

Next, specific examples of the present invention will be described.
1. Manufacture and evaluation of magnetic core of Co-based metallic glass alloy Fe content is 2 atomic% or more and 6 atomic% or less, Ni content is 4 atomic% or less, B content is 15 atomic% or more and 20 atomic% or less The Si content is 8 atomic% or more and 13 atomic% or less, the Nb content is 3 atomic% or less, the Mo content is 0.1 atomic% or more and 1 atomic% or less, and the Cr content is 2 atoms. % Of the magnetic core 1 shown in FIG. 10 made of a Co-based metallic glass alloy having a composition of (Co _0.6594 Fe _0.0406 Si _0.11 B _0.17 Nb _0.02 ) _99.7 Mo _0.3 so that the balance is in the composition range of Co. The magnetic core 1 of the embodiment) was molded using the injection molding apparatus 100 of FIG.

Differential scanning calorimetry was performed on the magnetic core 1 of the present embodiment using a differential scanning calorimeter (DSC method). Then, from the measurement results, the crystallization start temperature Tx and the glass transition temperature Tg were estimated, and a difference ΔTx (= Tx−Tg) between these temperatures was calculated. Moreover, conversion vitrification temperature Tg / Tl was computed from liquidus temperature Tl and glass transition temperature Tg.
Next, the maximum relative magnetic permeability at a measurement frequency of 10 Hz was measured for the magnetic core 1 of the present embodiment. Further, the magnetic core 1 of the present embodiment was cut so as to be orthogonal to the longitudinal direction, and the cut surface was observed with a scanning electron microscope. Then, the ratio of the area occupied by the Co-based metallic glass alloy on the cut surface was calculated as a space factor.

In the magnetic core 1 of the present embodiment, the supercooled liquid temperature range ΔTx was as wide as 42 K, the converted vitrification temperature Tg / Tl was as large as 0.602, and the glass forming ability was high. In addition, the magnetic core 1 of the present embodiment has a high relative permeability at a low frequency of 10 Hz, and a high space factor of 85%.
2. Manufacture and evaluation of timepiece Using the magnetic core 1 of this embodiment, the electromagnetic transducer 2 shown in FIG. 11 was manufactured. At this time, an insulating layer (passive film) containing an element in the Co-based metallic glass alloy was formed on the outer periphery of the winding portion 40 of the magnetic core 1. Further, the electromagnetic converter 2 is manufactured as the first coil block 522 and the second coil block 523 of the generator 520 of FIG. 15 to produce the electronically controlled mechanical timepiece 500 of FIG. 15 (hereinafter referred to as the timepiece 500 of the present embodiment). did.

  Then, the mainspring of the timepiece 500 of this embodiment was wound up to the end, and then the time until the hands of the timepiece 500 stopped was measured. As a result, the driving time of the conventional timepiece (a timepiece not using the magnetic core 1 of the present embodiment) was about 48 hours, but the timepiece 500 of the present embodiment realized a driving time of 84 hours. The winding part 40 of the magnetic core 1 constituting the electromagnetic transducer 2 of the present embodiment has a cylindrical shape (circular cross-sectional shape), and an insulating layer (passive film) is not provided on the outer periphery of the winding part 40 instead of an insulating tape. ) Is formed, the winding efficiency of the conducting wire 43 is improved. As a result, the power generation efficiency of the power generator 520 including the electromagnetic converter 2 (the first coil block 522 and the second coil block 523) as a constituent member is improved, so that the performance of the driving time of the timepiece 500 of the present embodiment can be improved. It became clear.

DESCRIPTION OF SYMBOLS 1 ... Magnetic core, 2 ... Electromagnetic converter, 40 ... Winding part, 41 ... Coil frame, 42 ... Connection part 43 ... Conducting wire (coil), 100 ... Injection molding apparatus, 101 ... Main body, 102 ... Sleeve, 103 DESCRIPTION OF SYMBOLS ... Induction coil, 104 ... Piston, 110 ... Mold, 111 ... Cavity, 112 ... Channel (gate), 200 ... Injection molding device, 201 ... Mold, 202 ... Cavity, 203 ... Nozzle, 204 ... Channel (gate) ), 500 ... Clock, 501 ... Barrel wheel, 504 ... Square hole car, 504a ... Kohaze, 506 ... Second car, 507 ... Third car, 508 ... Second hand wheel, 509 ... Forty-four car (intermediate car) 510 ... Fourth wheel, 511 ... Fifth wheel, 512 ... Sixth wheel, 513 ... Rotor, 520 ... Generator, 521 ... Stator, 521a ... Arrangement hole, 522 ... First coil block, 522a, 523a ... Magnetic core, 52 3 ... 2nd coil block, 524 ... joint, 530 ... winding stem, 531 ... kite wheel, 532 ... round hole wheel, 533 ... square hole intermediate wheel, 534 ... pinwheel, 535 ... small iron wheel, 536 ... back of the sun Intermediate wheel, 537 ... Sunlight vehicle, 538 ... Control lever, 600 ... Clock, 681 ... Ground plate, 682, 682A, 682B ... Stepping motor, 683 ... Battery (drive source), 683 ... Battery holder, 684 ... CPU (control) Means), 685 ... circuit block, 685 ... crystal resonator, 686 ... winding stem, 687 ... receiving IC, 690 ... radio wave receiving antenna

Claims (12)

Fe content is 2 atomic% or more and 6 atomic% or less,
Ni content is 0 atomic% or more and 4 atomic% or less,
B content is 15 atomic% or more and 20 atomic% or less,
Si content is 8 atomic% or more and 13 atomic% or less,
Nb content of 0 atomic% or more and 3 atomic% or less,
Mo content is 0.1 atomic% or more and 1 atomic% or less,
Cr content of 0 atomic% or more and 2 atomic% or less,
A Co-based metallic glass alloy characterized in that the balance is Co ,
When the crystallization start temperature of the Co-based metallic glass alloy is Tx [K], the glass transition temperature is Tg [K], and the liquidus temperature of the alloy is Tl [K], it is defined by Tx−Tg. Co-based metal characterized in that the supercooled liquid temperature range ΔTx is 30K or more, the converted vitrification temperature Tg / Tl is 0.58 or more, and the maximum permeability at a measurement frequency of 10 Hz is 80,000 or more. Glass alloy.   The Co-based metallic glass alloy according to claim 1, wherein the combined content of Co and Fe is 68 atomic% or more and 71 atomic% or less.   The Co-based metallic glass alloy according to claim 1 or 2, wherein the Si content is 10 atomic% or more and 11 atomic% or less.   The Co-based metallic glass alloy according to any one of claims 1 to 3, wherein the Mo content is 0.2 atomic% or more and 0.35 atomic% or less. A magnetic core comprising the Co-based metallic glass alloy according to any one of claims 1 to 4. The magnetic core according to claim 5, wherein the magnetic core is formed of a molded body formed by molding a powder composed of the Co-based metallic glass alloy, or a sintered body formed by sintering the molded body. The magnetic core according to claim 6, wherein the sintering is performed by spark plasma sintering. 6. The magnetic core according to claim 5, wherein a melt of the Co-based metallic glass alloy is cast and formed . An electromagnetic converter comprising: the magnetic core according to claim 5; and a coil wound around an outer periphery of the magnetic core. The electromagnetic transducer according to claim 9, wherein a cross-sectional shape of a winding portion of the magnetic core in contact with the coil is a circular shape. The electromagnetic transducer according to claim 9, wherein a passive film is formed on a surface of the magnetic core that contacts the coil . A timepiece comprising the electromagnetic converter according to any one of claims 9 to 11.