JP5342883B2 - 複層軸受 - Google Patents
複層軸受 Download PDFInfo
- Publication number
- JP5342883B2 JP5342883B2 JP2009001888A JP2009001888A JP5342883B2 JP 5342883 B2 JP5342883 B2 JP 5342883B2 JP 2009001888 A JP2009001888 A JP 2009001888A JP 2009001888 A JP2009001888 A JP 2009001888A JP 5342883 B2 JP5342883 B2 JP 5342883B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- resin
- bearing
- fluororesin
- bearing according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(1)PTFE樹脂:三井・デュポンフロロケミカル社製;テフロン(登録商標)7J
(2)PPS樹脂:東ソー社製;B160(融点288℃)
(3)PEEK樹脂:ビクトレックス・エムシー社製;PEEK450P(融点334℃)
(4)ポリイミド樹脂:宇部興産社製;UIP−R(融点400℃)
(5)PAN系炭素繊維:東レ社製;トレカMLD30(繊維長30μm 、繊維径7μm)
(6)ピッチ系炭素繊維 1:大阪ガス社製;ザイラスGM−100J(繊維長100μm、繊維径12μm)
(7)ピッチ系炭素繊維 2:呉羽化学社製;クレカミルドM101S(繊維長130μm、繊維径14.5μm)
(8)二硫化モリブデン:ダウコーニング社製;モリコートZパウダー
(9)四酸化三鉛:鉛市化学工業社製;鉛丹1号
(10)硫酸カルシウム:大日精化工業社製;硫酸カルシウム
両面に銅メッキの付けられたSPCC鋼板(日新製鋼社製;カッパータイト)の片方の表面に青銅粉末(#100メッシュパス、#200メッシュオン)を散布し、加熱・加圧することにより鋼板上に均一な層厚の多孔質性層(焼結金属層)を形成した。この多孔質層の上に、表1に示す配合割合で調整したPTFE樹脂組成物のディスパージョンを塗布し、乾燥炉中で溶媒を蒸発させ、加熱・加圧により固形成分を多孔質層に含浸被覆した。このようにして得られた複層軸受の板材を幅25mm×長さ50mm×厚さ1mmの形状に加工し、複層軸受試験片を得た。得られた複層軸受試験片を以下に示す往復動試験に供し、摩擦係数および摩耗量を測定した。結果を摩耗量を図3に、摩擦係数を図4に、それぞれ示す。
得られた複層軸受試験片6を図2に示す往復動試験機を用いて、摩擦摩耗試験を実施した。図2に示すように往復動試験機5は、複層軸受試験片6を固定する固定治具7と、相手材8を保持し、針状ころ10を介して固定台11上を往復動する相手材ホルダー9と、カップリング12を介して往復動を相手材ホルダー9に付与する油圧サーボ機構13と、摩擦力を検出するロードセル14とを備える。得られた複層軸受試験片6を固定治具7に取り付け、荷重15を印加して表2に示す面圧条件で相手材8に押し付け、相手材8を往復動させたときの両者の摺動面に生じる摩擦係数をロードセル14により測定する。摩擦摩耗試験終了後に試験片を取り出し、摩耗量を測定する。摩擦摩耗試験は表2に示す低面圧条件である往復動試験Aおよび高面圧条件である往復動試験Bの2種類について実施する。
2 金属基材
3 多孔質層
4 樹脂組成物
5 往復動試験機
6 複層軸受試験片
7 固定治具
8 相手材
9 相手材ホルダー
10 針状ころ
11 固定台
12 カップリング
13 油圧サーボ機構
14 ロードセル
15 荷重
Claims (16)
- 金属基材と、該金属基材の一方の表面に形成された多孔質層と、該多孔質層に含浸被覆された樹脂組成物とからなる複層軸受であって、
前記樹脂組成物は、フッ素樹脂に、前記フッ素樹脂の融点の−50℃〜+20℃の範囲の融点を有する熱可塑性樹脂と、炭素繊維と、二硫化モリブデンとを少なくとも配合してなり、前記炭素繊維および前記二硫化モリブデン以外の無機充填材を含まないフッ素樹脂組成物であることを特徴とする複層軸受。 - 前記フッ素樹脂は、ポリテトラフルオロエチレン樹脂であることを特徴とする請求項1記載の複層軸受。
- 前記熱可塑性樹脂は、ポリフェニレンサルファイド樹脂、ポリエーテルエーテルケトン樹脂、テトラフルオロエチレン−パーフルオロアルキルビニルエーテル共重合樹脂から選ばれる少なくとも一つであることを特徴とする請求項1または請求項2記載の複層軸受。
- 前記炭素繊維は、平均繊維長が100μm以下であることを特徴とする請求項1ないし請求項3のいずれか一項記載の複層軸受。
- 前記炭素繊維は、PAN系炭素繊維であることを特徴とする請求項4記載の複層軸受。
- 前記フッ素樹脂組成物は、前記フッ素樹脂100重量部に対して、前記熱可塑性樹脂を0.5〜13重量部、前記炭素繊維を2〜20重量部、前記二硫化モリブデンを4〜35重量部、少なくとも配合することを特徴とする請求項1ないし請求項5のいずれか一項記載の複層軸受。
- 前記フッ素樹脂組成物は、実質的に前記フッ素樹脂、前記熱可塑性樹脂、前記炭素繊維、前記二硫化モリブデンの4成分からなることを特徴とする請求項1ないし請求項6のいずれか一項記載の複層軸受。
- 前記多孔質層は、非鉄金属の焼結層または溶射層であることを特徴とする請求項1ないし請求項7のいずれか一項記載の複層軸受。
- 前記金属基材は鋼板であり、前記多孔質層の非鉄金属は前記鋼板より軟質の金属であることを特徴とする請求項1ないし請求項8のいずれか一項記載の複層軸受。
- 前記非鉄金属は、銅または銅を主成分とする銅合金であることを特徴とする請求項8または請求項9記載の複層軸受。
- 前記鋼板には、前記非鉄金属と同等の金属がメッキされていることを特徴とする請求項9または請求項10記載の複層軸受。
- 前記金属基材の他方の表面には防錆用メッキが付けられていることを特徴とする請求項1ないし請求項11のいずれか一項記載の複層軸受。
- 前記防錆用メッキは、錫メッキであることを特徴とする請求項12記載の複層軸受。
- 前記複層軸受は、相手材との摺動条件が油脂類を使用しない無潤滑で使用されるドライ軸受であることを特徴とする請求項1ないし請求項13のいずれか一項記載の複層軸受。
- 前記複層軸受は、面圧が10MPaをこえる条件下で使用されることを特徴とする請求項1ないし請求項14のいずれか一項記載の複層軸受。
- 前記熱可塑性樹脂は、前記フッ素樹脂、前記炭素繊維、および前記二硫化モリブデンを三次元網目構造的に保持していることを特徴とする請求項1ないし請求項15のいずれか一項記載の複層軸受。