JP5295775B2 - ガラス組成 - Google Patents
ガラス組成 Download PDFInfo
- Publication number
- JP5295775B2 JP5295775B2 JP2008537845A JP2008537845A JP5295775B2 JP 5295775 B2 JP5295775 B2 JP 5295775B2 JP 2008537845 A JP2008537845 A JP 2008537845A JP 2008537845 A JP2008537845 A JP 2008537845A JP 5295775 B2 JP5295775 B2 JP 5295775B2
- Authority
- JP
- Japan
- Prior art keywords
- amount
- weight percent
- glass
- percent
- feo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
Claims (29)
- 高耐熱性のガラス繊維を形成するためのガラスの組成であって、
69.93から81.59質量パーセントまでの範囲の量のSiO2と、
0.00から0.37質量パーセントまでの範囲の量のAl2O3と、
0.00から3.97質量パーセントまでの範囲の量のNa2Oと、
0.00から2.57質量パーセントまでの範囲の量のK2Oと、
3.31から10.00質量パーセントまでの範囲の量のCaOと、
0.00から5.00質量パーセントまでの範囲の量のMgOと、
5.28から11.94質量パーセントまでの範囲の量のFe2O3+FeOと、
0.00から1.84質量パーセントまでの範囲の量のTiO2と、
0.00から4.24質量パーセントまでの範囲の量のB2O3と、
0.00から6.01質量パーセントまでの範囲の量のLi2Oと、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
76.78質量パーセントの量のSiO2と、
0.00質量パーセントの量のAl2O3と、
2.26質量パーセントの量のNa2Oと、
2.26質量パーセントの量のK2Oと、
3.79質量パーセントの量のCaOと、
1.82質量パーセントの量のMgOと、
11.60質量パーセントの量のFe2O3+FeOと、
1.48質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
70.50質量パーセントの量のSiO2と、
0.00質量パーセントの量のAl2O3と、
3.30質量パーセントの量のNa2Oと、
1.80質量パーセントの量のK2Oと、
10.00質量パーセントの量のCaOと、
5.00質量パーセントの量のMgOと、
8.30質量パーセントの量のFe2O3+FeOと、
1.10質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
72.38質量パーセントの量のSiO2と、
0.00質量パーセントの量のAl2O3と、
2.41質量パーセントの量のNa2Oと、
0.95質量パーセントの量のK2Oと、
8.31質量パーセントの量のCaOと、
4.08質量パーセントの量のMgOと、
10.27質量パーセントの量のFe2O3+FeOと、
1.60質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
77.78質量パーセントの量のSiO2と、
0.00質量パーセントの量のAl2O3と、
2.57質量パーセントの量のNa2Oと、
2.57質量パーセントの量のK2Oと、
3.78質量パーセントの量のCaOと、
3.98質量パーセントの量のMgOと、
8.60質量パーセントの量のFe2O3+FeOと、
0.71質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
73.83質量パーセントの量のSiO2と、
0.00質量パーセントの量のAl2O3と、
2.31質量パーセントの量のNa2Oと、
1.81質量パーセントの量のK2Oと、
8.42質量パーセントの量のCaOと、
3.99質量パーセントの量のMgOと、
8.54質量パーセントの量のFe2O3+FeOと、
1.10質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
77.63質量パーセントの量のSiO2と、
0.00質量パーセントの量のAl2O3と、
1.97質量パーセントの量のNa2Oと、
0.67質量パーセントの量のK2Oと、
6.77質量パーセントの量のCaOと、
3.31質量パーセントの量のMgOと、
8.36質量パーセントの量のFe2O3+FeOと、
1.29質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
80.49質量パーセントの量のSiO2と、
0.00質量パーセントの量のAl2O3と、
2.03質量パーセントの量のNa2Oと、
0.01質量パーセントの量のK2Oと、
6.55質量パーセントの量のCaOと、
4.27質量パーセントの量のMgOと、
5.28質量パーセントの量のFe2O3+FeOと、
1.37質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
73.54質量パーセントの量のSiO2と、
0.00質量パーセントの量のAl2O3と、
2.45質量パーセントの量のNa2Oと、
0.97質量パーセントの量のK2Oと、
8.44質量パーセントの量のCaOと、
4.15質量パーセントの量のMgOと、
10.43質量パーセントの量のFe2O3+FeOと、
0.00質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
77.20質量パーセントの量のSiO2と、
0.00質量パーセントの量のAl2O3と、
2.55質量パーセントの量のNa2Oと、
2.55質量パーセントの量のK2Oと、
3.75質量パーセントの量のCaOと、
3.95質量パーセントの量のMgOと、
9.96質量パーセントの量のFe2O3+FeOと、
0.00質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
81.59質量パーセントの量のSiO2と、
0.00質量パーセントの量のAl2O3と、
2.06質量パーセントの量のNa2Oと、
0.01質量パーセントの量のK2Oと、
6.64質量パーセントの量のCaOと、
4.33質量パーセントの量のMgOと、
5.35質量パーセントの量のFe2O3+FeOと、
0.00質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
77.63質量パーセントの量のSiO2と、
0.67質量パーセントの量のNa2Oと、
1.97質量パーセントの量のK2Oと、
6.77質量パーセントの量のCaOと、
3.31質量パーセントの量のMgOと、
8.35質量パーセントの量のFe2O3+FeOと、
1.29質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
75.63質量パーセントの量のSiO2と、
0.67質量パーセントの量のNa2Oと、
1.97質量パーセントの量のK2Oと、
6.77質量パーセントの量のCaOと、
3.31質量パーセントの量のMgOと、
10.36質量パーセントの量のFe2O3+FeOと、
1.29質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
78.61質量パーセントの量のSiO2と、
3.97質量パーセントの量のNa2Oと、
0.67質量パーセントの量のK2Oと、
6.40質量パーセントの量のCaOと、
10.35質量パーセントの量のFe2O3+FeOと、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
72.26質量パーセントの量のSiO2と、
2.36質量パーセントの量のNa2Oと、
1.04質量パーセントの量のK2Oと、
8.34質量パーセントの量のCaOと、
4.09質量パーセントの量のMgOと、
10.31質量パーセントの量のFe2O3+FeOと、
1.60質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
79.33質量パーセントの量のSiO2と、
1.03質量パーセントの量のNa2Oと、
5.43質量パーセントの量のCaOと、
3.91質量パーセントの量のMgOと、
8.78質量パーセントの量のFe2O3+FeOと、
1.52質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
76.34質量パーセントの量のSiO2と、
7.14質量パーセントの量のCaOと、
3.99質量パーセントの量のMgOと、
8.95質量パーセントの量のFe2O3+FeOと、
0.57質量パーセントの量のTiO2と、
3.01質量パーセントの量のB2O3と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
69.93質量パーセントの量のSiO2と、
2.92質量パーセントの量のNa2Oと、
0.96質量パーセントの量のK2Oと、
8.40質量パーセントの量のCaOと、
11.94質量パーセントの量のFe2O3+FeOと、
1.84質量パーセントの量のTiO2と、
4.01質量パーセントの量のB2O3と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
78.44質量パーセントの量のSiO2と、
2.91質量パーセントの量のNa2Oと、
6.63質量パーセントの量のCaOと、
3.09質量パーセントの量のMgOと、
8.94質量パーセントの量のFe2O3+FeOと、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
78.62質量パーセントの量のSiO2と、
0.83質量パーセントの量のK2Oと、
8.60質量パーセントの量のCaOと、
2.05質量パーセントの量のMgOと、
8.78質量パーセントの量のFe2O3+FeOと、
1.13質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
72.38質量パーセントの量のSiO2と、
2.55質量パーセントの量のNa2Oと、
8.31質量パーセントの量のCaOと、
4.08質量パーセントの量のMgOと、
10.33質量パーセントの量のFe2O3+FeOと、
2.41質量パーセントの量のB2O3と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
78.34質量パーセントの量のSiO2と、
2.59質量パーセントの量のNa2Oと、
4.02質量パーセントの量のCaOと、
0.81質量パーセントの量のMgOと、
10.18質量パーセントの量のFe2O3+FeOと、
4.24質量パーセントの量のB2O3と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
78.34質量パーセントの量のSiO2と、
2.03質量パーセントの量のNa2Oと、
6.55質量パーセントの量のCaOと、
3.27質量パーセントの量のMgOと、
8.53質量パーセントの量のFe2O3+FeOと、
1.01質量パーセントの量のB2O3と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
72.51質量パーセントの量のSiO2と、
2.41質量パーセントの量のNa2Oと、
8.31質量パーセントの量のCaOと、
4.08質量パーセントの量のMgOと、
10.27質量パーセントの量のFe2O3+FeOと、
1.59質量パーセントの量のTiO2と、
0.83質量パーセントの量のLi2Oと、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
72.51質量パーセントの量のSiO2と、
2.41質量パーセントの量のNa2Oと、
0.82質量パーセントの量のK2Oと、
8.31質量パーセントの量のCaOと、
4.08質量パーセントの量のMgOと、
10.27質量パーセントの量のFe2O3+FeOと、
1.59質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
73.10質量パーセントの量のSiO2と、
1.36質量パーセントの量のNa2Oと、
8.14質量パーセントの量のCaOと、
3.99質量パーセントの量のMgOと、
10.04質量パーセントの量のFe2O3+FeOと、
1.56質量パーセントの量のTiO2と、
1.81質量パーセントの量のLi2Oと、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
72.78質量パーセントの量のSiO2と、
2.26質量パーセントの量のNa2Oと、
1.26質量パーセントの量のK2Oと、
3.79質量パーセントの量のCaOと、
2.81質量パーセントの量のMgOと、
9.60質量パーセントの量のFe2O3+FeOと、
1.48質量パーセントの量のTiO2と、
6.01質量パーセントの量のLi2Oと、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
77.23質量パーセントの量のSiO2と、
0.37質量パーセントの量のAl2O3と、
1.92質量パーセントの量のNa2Oと、
0.67質量パーセントの量のK2Oと、
6.22質量パーセントの量のCaOと、
4.04質量パーセントの量のMgOと、
8.28質量パーセントの量のFe2O3+FeOと、
1.27質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。 - 請求項1に記載のガラスの組成において、
75.36質量パーセントの量のSiO2と、
0.15質量パーセントの量のAl2O3と、
3.97質量パーセントの量のNa2Oと、
0.67質量パーセントの量のK2Oと、
6.22質量パーセントの量のCaOと、
4.06質量パーセントの量のMgOと、
8.30質量パーセントの量のFe2O3+FeOと、
1.27質量パーセントの量のTiO2と、
を具えることを特徴とするガラスの組成。