JP5083796B2 - Anti-counterfeit sheet-like material - Google Patents

Anti-counterfeit sheet-like material Download PDF

Info

Publication number
JP5083796B2
JP5083796B2 JP2006206762A JP2006206762A JP5083796B2 JP 5083796 B2 JP5083796 B2 JP 5083796B2 JP 2006206762 A JP2006206762 A JP 2006206762A JP 2006206762 A JP2006206762 A JP 2006206762A JP 5083796 B2 JP5083796 B2 JP 5083796B2
Authority
JP
Grant status
Grant
Patent type
Prior art keywords
example
organic solvent
anti
soluble
sheet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2006206762A
Other languages
Japanese (ja)
Other versions
JP2008031594A (en )
Inventor
寛規 三浦
孝之 西村
Original Assignee
特種東海製紙株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Grant date

Description

本発明は偽造防止用シート状物に関する。 The present invention relates to anti-counterfeit sheet. 詳しくは有機溶剤を用いて改竄を試みても、その痕跡を可視光下で容易に視認することのできる偽造防止用シート状物に関する。 Even more information, attempts to tamper with an organic solvent, to the anti-counterfeit sheet which can easily visually recognize the traces under visible light.

紙幣、商品券、パスポート、株券、小切手等は不正に偽造されないように各種の偽造防止対策が施されている。 Bill, gift certificates, passports, stock certificates, checks and the like are illegally forged so as not to a variety of anti-counterfeiting measures are applied. 例えば、自然光や通常の照明下で、特殊な機器を用いずに容易に視認できる偽造防止手段を施すことが考えられている。 For example, it has been proposed to lower the illumination of natural light and typically subjected to forgery prevention means can be easily visually recognized without using special equipment. この考えに基づき、改竄された痕跡が容易に視認できる偽造防止用紙や偽造防止印刷物、およびこれらに使用する材料の提案が以下に示すように各種なされている。 Based on this idea, anti-falsification paper and anti-counterfeit printed matter falsified traces readily visible, and suggestions of the materials used in these have been made various as shown below.

例えば、特許文献1や特許文献2では、マンガンのフェロサイトアナイドを用紙中に含ませ、金額欄に記載された文字をインク消しを用いて消そうとすると褐色に変色する証券用紙の提案がある。 For example, Patent Document 1 and Patent Document 2, a ferro-site Ana Id manganese contained in the paper, the characters written in amount fields suggestions security papers discolored brown when you put out using the ink off is there.

特許文献3には、酸化剤により変色する物質とタンニン質と浸透剤を用紙に加工し、インク消しで改竄すると消滅することのない色が出る改竄防止用紙の提案がある。 Patent Document 3, by processing the material with tannin quality and penetrants discolored by oxidation agent to the paper, there is proposed a tamperproof paper color never disappears and tampering exits with ink off.

特許文献4には、水溶性のピレンスルホン酸金属塩系の反応性蛍光染料を用紙中に含有させ、インク消しや弱アルカリで改竄を試みると蛍光色を呈する安全紙の提案がある。 Patent Document 4, a reactive fluorescent dye soluble pyrene sulfonic acid metal salt-based is contained in the paper, there is proposed a safety paper exhibiting fluorescent colors attempt to tamper with the ink off or weak alkali.

特許文献5には、ロイコ染料とフェノール性物質、バインダーを主成分とする発色層を用紙表面に設け、有機溶剤で改竄を試みた場合有機溶剤の浸透でロイコ染料とフェノール性物質が溶出し、両者が化学反応し発色する改竄防止用紙の提案がある。 Patent Document 5, a leuco dye and a phenolic material, provided with a color developing layer mainly composed of a binder to the paper surface, leuco dye and a phenolic substance is eluted by penetration of the organic solvent when trying to tamper with an organic solvent, both are suggestions tamperproof paper to be chemically reacted color. さらには、特許文献6〜9には、ロイコ染料と顕色剤を組み合わせることにより、有機溶剤に反応して発色する改竄防止技術を設けたラベルやシールの提案がされている。 Furthermore, Patent Document 6 to 9, by combining the leuco dye and a developer, it has been proposed labels and seals provided with tamperproof technique of color in response to organic solvents.

また、本出願人は先に特許文献10において、水不溶性でかつ有機溶剤可溶性の蛍光染料粒子を用紙中に含ませ、有機溶剤で改竄を試みると染料が溶出浸透し蛍光色を呈する偽造防止用紙の提案を行った。 Further, in Patent Document 10 to present applicant previously fluorescent dye particles of water-insoluble and organic solvent-soluble contained in the paper, anti-falsification paper which dye attempt to tamper with an organic solvent exhibits a dissolution permeated fluorescent color proposal was carried out. しかしながら、この用紙に有機溶剤を滴下すると有機溶剤の浸透が悪いため、改竄の痕跡が明確に判断できない場合があった。 However, this order penetration of the organic solvent is poor when dropping the organic solvent to the paper, there is a case where traces of tampering can not be clearly determined. また、印刷適性が低いため用途が限られていた。 In addition, applications due to the low printability has been limited.

特許第78774号 Patent No. 78774 特許第77962号 Patent No. 77962 特許第136286号 Patent No. 136286 特許第1414483号 Patent No. 1414483 特開昭63−182496号 JP-A-63-182496 特開平07−271302号 Japanese Unexamined Patent Publication No. 07-271302 特開平10−250228号 Japanese Unexamined Patent Publication No. 10-250228 特開平10−268772号 Japanese Unexamined Patent Publication No. 10-268772 特開2003−29637号 Japanese Unexamined Patent Publication No. 2003-29637 特開2000−129596号 Japanese Unexamined Patent Publication No. 2000-129596

印刷物の表面に印刷された内容を改竄する目的で、各種の有機溶剤を使用して印刷インキを除去しようとした際に、容易に改竄の痕跡を視認できる偽造防止手段があると便利である。 In order to tamper with the contents printed on the surface of the printed material, while attempting to remove the printing ink using various organic solvents, it is useful to have a means of preventing forgery, which readily visible traces of tampering. 本発明は、このような手段として有用な偽造防止用シート状物を提供することを課題とする。 The present invention aims to provide a useful anti-counterfeit sheet as such means. 具体的には、溶解度パラメーターの異なる複数の種類の有機溶剤を滴下した場合であっても滴下部分が発色し、可視光下で容易に改竄の痕跡を確認することができる偽造防止用シート状物を提供することである。 Specifically, the solubility different types of drip portion even when the dropped organic solvent having parameters colored, the anti-counterfeit sheet which can be confirmed traces of easily tampered under visible light it is to provide a. また、シート状物における有機溶剤の浸透や拡散を向上させることにより、発色がより鮮明になるような手段を提供することである。 Also, by improving the penetration and diffusion of the organic solvent in the sheet-like material is to provide means such as color becomes clearer.

すなわち本発明の請求項1に係る発明は、水不溶性でかつ有機溶剤可溶性の染料および/または顔料を1種類以上含有し、1種類以上の有機溶剤の滴下による改竄の痕跡を可視光下で視認できるようにしたことを特徴とする偽造防止用シート状物である。 That invention according to claim 1 of the present invention, the water-insoluble and organic solvent-soluble dyes and / or pigments containing 1 or more, visible traces of tampering by dropwise addition of one or more organic solvents under visible light it was possible manner is the anti-counterfeit sheet according to claim.

すなわち本発明の請求項2に係る発明は、水不溶性でかつ有機溶剤可溶性の染料および/または顔料を1種類以上含む塗工層が少なくともシート状物の片面に存在し、1種類以上の有機溶剤の滴下による改竄の痕跡を可視光下で視認できるようにしたことを特徴とする偽造防止用シート状物である。 Invention, a coating layer comprising a water-insoluble and organic solvent-soluble dyes and / or pigments one or more is present in at least one side of the sheet-like material, one or more organic solvents i.e. according to claim 2 of the present invention traces of tampering by dropping a anti-counterfeit sheet, characterized in that to be able to visually recognize under visible light.

すなわち本発明の請求項3に係る発明は、填料およびバインダーを含む塗工層が存在することを特徴とする請求項1または2に記載の偽造防止用シート状物である。 That invention according to claim 3 of the present invention is the anti-counterfeit sheet according to claim 1 or 2, characterized by the presence of coating layer containing a filler and a binder.

すなわち本発明の請求項4に係る発明は、溶解度パラメーターの異なる2種類以上の有機溶剤をそれぞれ滴下したときに、いずれの場合でも滴下の痕跡を可視光下で視認できることを特徴とする請求項1〜3のいずれか1項に記載の偽造防止用シート状物である。 That invention according to claim 4 of the present invention, claims, characterized in that the solubility parameter of two or more kinds of organic solvent when dropped respectively, traces of dropping any case visible under visible light 1 it is anti-counterfeit sheet according to any one of to 3.

すなわち本発明の請求項5に係る発明は、シート状物が木材パルプを主原料としたものであることを特徴とした、請求項1〜4のいずれか1項に記載の偽造防止用シート状物である。 That invention according to claim 5 of the present invention, sheet-like material is characterized by a constitution that the wood pulp as the main raw material, the anti-counterfeit sheet according to any one of claims 1 to 4 thing is.

すなわち本発明の請求項6に係る発明は、水不溶性でかつ有機溶剤可溶性の染料がアゾ系染料、アミノケトン系染料、クマリン系染料であることを特徴とする請求項1〜5のいずれか1項に記載の偽造防止用シート状物である。 That invention according to claim 6 of the present invention, any one of the preceding claims dye water-insoluble and organic solvent-soluble is characterized in that it is a azo dyes, aminoketone dyes, coumarin dyes it is anti-counterfeit sheet according to.

すなわち本発明の請求項7に係る発明は、水不溶性でかつ有機溶剤可溶性の顔料がアゾ系顔料、フタロシアニン系顔料であることを特徴とする請求項1〜5のいずれか1項に記載の偽造防止用シート状物である。 That invention according to claim 7 of the present invention, forgery according to any one of claims 1 to 5, wherein the pigment of the water-insoluble and organic solvent-soluble azo pigments, phthalocyanine pigments it is the prevention sheet-like material.

本発明による偽造防止用シート状物によれば、水不溶性でかつ有機溶剤可溶性の染料および/または顔料を1種類以上含む塗工層が設けられ、さらには填料およびバインダーを含む塗工層が存在することによって、印刷物の表面に印刷された内容を改竄する目的で、各種の有機溶剤を使用して印刷インキを除去しようとした際に、容易に改竄の痕跡を視認できるので、紙幣、商品券、パスポート、株券、小切手等の偽造防止手段として好ましく使用することができる。 According to the anti-counterfeit sheet according to the invention, a coating layer comprising a water-insoluble and organic solvent-soluble dyes and / or pigments one or more is provided, furthermore there is a coating layer comprising a filler and a binder by, for the purpose of tampering with contents printed on the surface of the printed material, while attempting to remove the printing ink using a variety of organic solvents, since readily visible traces of tampering, bills, gift certificates , it can be preferably used passports, stock certificates, as means of preventing forgery such as checks.

本発明で使用する染料および/または顔料は水不溶性でかつ有機溶剤可溶性であることが必要である。 Dyes and / or pigments used in the present invention should be water insoluble and organic solvent-soluble. 水溶性であるとシート状物製造中等において、該染願料粒子が水中に溶解してしまい本発明の目的を達成できなくなるからである。 The sheet material producing moderate to be water-soluble, because 該染 Ganryo particles can not be achieve the object of the present invention will be dissolved in the water. また、偽造防止用紙は油溶性のインキを使用した印刷を施したり、住所、氏名、金額などの可変情報を油溶性のインキを使用したボールペンで記載したりすることが一般的であり、これらの情報を改竄するためには有機溶剤が用いられることが必要となる。 Further, anti-falsification paper or by printing using an ink of oil-soluble, address, name, is common or to described ballpoint pen variable information using the ink of an oil-soluble, such as amounts, of to falsify information it is necessary that the organic solvent is used. そのため、本発明で用いる染料および/または顔料が有機溶剤に可溶でないと、有機溶剤を用いて改竄を試みた際に改竄の痕跡を視認できなくなるからである。 Therefore, dyes and / or pigments used in the present invention is the non-soluble in organic solvents, because not visible traces of tampering when attempting tampering with an organic solvent.

本発明で使用する染料および/または顔料は、有機溶剤を用いて改竄を試みた際に改竄の痕跡が通常の光原のもとで発色するものであって、有色となり、目視により容易に確認できるものが好ましい。 Dyes and / or pigments used in the present invention, which traces of tampering when attempting tampering with an organic solvent is colored under normal HikariHara, it becomes colored, easily visually recognized possible is preferable.

本発明で使用する染料粒子は水不溶性でかつ有機溶剤可溶性であればどのようなものでも使用できる。 Dye particles to be used in the present invention can be used of any type as long as and organic solvent-soluble water-insoluble. 例えば、アゾ系、アミノケトン系、クマリン系、オキサゾール系、ピラリゾン系といった各種染料が挙げられるが、これらに限定されるものではない。 For example, azo, aminoketone, coumarin, oxazole, including but various dyes such pyrazoline-based, but is not limited thereto. この種の染料としては染料メーカーから販売されているが、実例を商品名で挙げると「Oil Red 5B」(オリエント化学工業(株)製造)、「Yellowfluor 10GN」(ランクセス(株)製造)、「Kayaset Flavine FN」(日本化薬(株)製造)、「Leucopher EF 2N」(クラリアント(株)製造)、「TBO」(住友精化(株)製造)、「Kayaset Red SF−R」(日本化薬(株)製造)、「VALIFAST BLUE 1605」(オリエント化学工業(株)製造)、「Oil Green BG」(オリエント化学工業(株)製造)、「VALIFAST RED 2303」(オリエント化学工業(株)製造)、「Oil Blue BOS」(オリエント化学工業(株)製造)、「 But as this type of dye has been sold from the dye maker, Taking the example under the trade name "Oil Red 5B" (Orient Chemical Industries Co., Ltd. production), "Yellowfluor 10GN" (Lanxess Co., Ltd. production), " Kayaset Flavine FN "(manufactured by Nippon Kayaku Co., Ltd. production)," Leucopher EF 2N "(Clariant Co., Ltd. production)," TBO "(manufactured by Sumitomo Seika Chemicals Co., Ltd. production)," Kayaset Red SF-R "(Japan of medicine Co., Ltd. manufacturing), "VALIFAST BLUE 1605" (manufactured by Orient Chemical Industries Co., Ltd. production), "Oil Green BG" (manufactured by Orient Chemical Industries Co., Ltd. production), "VALIFAST RED 2303" (manufactured by Orient Chemical Industries Co., Ltd. production ), "Oil Blue BOS" (Orient Chemical Industries Co., Ltd. production), " PILON RED GEH Special」(保土ヶ谷化学工業(株)製造)、「MACROLEX VIOLET 3R」(ランクセス(株)製造)、「MACROLEX Red 5B FG」(ランクセス(株)製造)、「MACROLEX Green 5B」(ランクセス(株)製造)、「Kayafect Blue T」(日本化薬(株)製造)、「Kayaset Blue 814」(日本化薬(株)製造)、「SPILON BLUE 2BNH」(保土ヶ谷化学工業(株)製造)、「SPIRON GREEN 3GNH Special」(保土ヶ谷化学工業(株)製造)等であるが、これらに限定されるものではない。 PILON RED GEH Special "(Hodogaya Chemical Industry Co., Ltd. production)," MACROLEX VIOLET 3R "(Lanxess Co., Ltd. production)," MACROLEX Red 5B FG "(Lanxess Co., Ltd. production)," MACROLEX Green 5B "(Lanxess ( Co., Ltd.) production), "Kayafect Blue T" (manufactured by Nippon Kayaku Co., Ltd. production), "Kayaset Blue 814" (manufactured by Nippon Kayaku Co., Ltd. production), "SPILON BLUE 2BNH" (Hodogaya chemical industry Co., Ltd. production), a "SPIRON GREEN 3GNH Special" (Hodogaya chemical Co., Ltd. manufacture), but is not limited thereto. これらの中でも特に、アゾ系染料、アミノケトン系染料、クマリン系染料を用いると、可視光下での発色が有色で鮮やかとなるので好ましい。 Among these, azo dyes, aminoketone dyes, the use of coumarin dyes, since color under visible light becomes bright in color preferred.

本発明で用いられる顔料としては、アゾ系、フタロシアニン系・アントラキノン系・ペルリン系・ピランスロン系、キナクリドン系・ジオキサジン系・イソインドリノン系、チオインジゴ系、キノフタロン系・金属系・ピグメント系・カーボン系・酸化硫黄系・亜酸化銅系、硫酸塩系、炭酸塩系、ケイ酸塩系、クロム酸塩系、アルミン酸塩系、フェロシアン系等の有機顔料または無機顔料が挙げられるが、これらに限定されるものではない。 The pigment used in the present invention, azo, phthalocyanine, anthraquinone, Perurin system, pyranthrone, quinacridone, dioxazine, isoindolinone, thioindigo, quinophthalone-metallic Pigment-based, carbon-based, sulfur oxide-based, cuprous oxide-based, sulfate-based, carbonate-based, silicate-based, chromate-based, aluminate-based, but include organic pigments or inorganic pigments ferrocyanide system such as, limited to not intended to be. 実例を商品名で挙げると、「TB−200 Red GY」、「TB−500 Orange R」、「TB−520BLUE 2B」、「TB−510 Green B」、「セイカファーストカーミン1476T−7」、「A120 レッド」、「430 ブリリアントボルドー 10B」、「モノアゾレーキ10G」、「セイカファーストレッド 116」、「セイカファーストエロー 1983−10G」(いずれも大日精化工業(株)製造)等があるが、これらに限定されるものではない。 To illustrate the trade name "TB-200 Red GY", "TB-500 Orange R", "TB-520BLUE 2B", "TB-510 Green B", "Seika Fast Carmine 1476T-7", "A120 Red "," 430 Brilliant Bordeaux 10B "," monoazo lake 10G "," Seika Fast Red 116 ", but there is a" Seika Fast Yellow 1983-10G "(Dainichiseika Color & Chemicals Mfg. both Co., Ltd. production), etc., limited to not intended to be. 特に、アゾ系顔料、フタロシアニン系顔料を用いると、可視光下での発色が有色で鮮やかとなるので好ましい。 In particular, azo pigments, the use of phthalocyanine pigments, the color under visible light becomes bright in color preferred.

本発明で用いる染料および/または顔料は、粒子状のものを用いる。 Dyes and / or pigments used in the present invention, used as the particulate. 粒子の大きさは、通常200μm以下であるが、本発明では塗料中に分散して使用する目的から粒子径は50μm以下のものを使用するのが好ましい。 The particle size, but is usually 200μm or less, the particle diameter of the objective in the present invention to be used by dispersing in the coating are preferably used those 50μm or less.

本発明に用いる染料および/または顔料は、必要に応じて2種類以上の染料および/または顔料を混合して用いることが好ましい。 Dyes and / or pigments used in the present invention, it is preferable to use a mixture of two or more dyes and / or pigments as necessary. 特に、溶解度パラメーターが異なる2種類以上の有機溶剤に溶解可能となるように異なる染料および/または顔料を選択して混合使用すると、様々な有機溶剤を用いた改竄にも任意に対応できるので特に好ましい。 In particular, when the solubility parameter of two or more different soluble in an organic solvent and so as to select a different dyes and / or pigments mixed use, particularly preferable because arbitrarily can cope with tampering with various organic solvents .

改竄に用いられる有機溶剤としてはメタノール、エタノール、アニリン、イソプロピルアルコール、アセトン、メチルエチルケトン、クロロホルム、クレゾール、アセトニトリル、ベンゼン、シクロヘキサン、酢酸エチル、トルエン、オクタン等の各種有機溶剤やこれらの混合物、石油中間留分であるナフサなどが考えられる。 Methanol as the organic solvent used in the alteration, ethanol, aniline, isopropyl alcohol, acetone, methyl ethyl ketone, chloroform, cresol, acetonitrile, benzene, cyclohexane, ethyl acetate, toluene, various organic solvents and mixtures thereof octane, petroleum middle distillate such as naphtha is a minute is considered. これらの有機溶剤は溶解度パラメーターの違いから、溶出させることのできる染料や顔料の種類が異なる。 These organic solvents due to the difference in solubility parameter, the type of dye or pigment capable of eluting is different. そのため、前述のように2種類以上の水不溶性でかつ有機溶剤可溶性の染料および/または顔料を混合してシート状物に含ませることにより、溶解性の異なる複数の有機溶剤に対して発色性を示すため、染料や顔料を単独で使用した場合に比べて、より高度な改竄防止効果が得られる。 Therefore, by including the sheet by mixing a dye and / or pigment of two or more water-insoluble and organic solvent-soluble as described above, the coloring property against solubility of different organic solvents to illustrate, compared to the case of using a dye or pigment alone, a more sophisticated anticounterfeiting effect.

溶解度パラメーターとはsp値とも呼ばれている値で、ポリマーと溶媒との溶解性を決める一つの因子である。 A value is the solubility parameter which is also referred to as sp value, which is one of the factors determining the solubility of the polymer and solvent. 一般に、極性をもつポリマーは極性溶媒に溶けやすく、非極性溶媒には溶けにくい傾向がある。 In general, polymers with polarity soluble in a polar solvent, the non-polar solvent is less likely to melt. 一方非極性のポリマーは逆の傾向になる。 While the non-polar polymer is reversed trend. この親和性の強さを判断する因子が溶解度パラメーターでありδで示される。 Factors determining the affinity strength is represented by and δ is the solubility parameter. ある液体のモル蒸発熱をΔH、モル体積をVとしたときにδ=(ΔH/V) 1/2で定義される。 [Delta] H the molar evaporative heat of a liquid is defined by δ = (ΔH / V) 1/2 when a molar volume was V. 代表的な溶剤の溶解度パラメーターの値を表1に示した。 The value of the solubility parameter of typical solvents shown in Table 1.
(表1)各種溶剤の溶解度パラメーターsp値:溶解度パラメーター値 (Table 1) various solvents solubility parameter sp value: Solubility parameter value

本発明で基材として用いられるシート状物としては、紙、フィルム、不織布、合成紙等が挙げられる。 The sheet-like material used as the substrate in the present invention, paper, film, nonwoven fabric, synthetic paper. 紙としては、製紙用として一般的に用いられている木材パルプ、例えば針葉樹晒クラフトパルプ(NBKP)、広葉樹晒クラフトパルプ(LBKP)、針葉樹晒サルファイトパルプ(NBSP)、サーモメカニカルパルプ(TMP)等の単独もしくは混合物を主体にして、これに必要に応じて麻、竹、藁、ケナフ等の非木材パルプやカチオン化パルプ、マーセル化パルプ等の変性パルプ、ミクロフィブリル化パルプ、レーヨン、ビニロン、ナイロン、アクリル、ポリエステル等の再生繊維、半合成繊維、合成繊維を適宜混合して用いることができる。 The paper, wood pulp, which is generally used as papermaking, for example, softwood bleached kraft pulp (NBKP), hardwood bleached kraft pulp (LBKP), needle bleached sulfite pulp (NBSP), thermomechanical pulp (TMP) etc. and a single or a mixture mainly, to which optionally hemp, bamboo, straw, non-wood pulp and cationized pulp such as kenaf, modified pulp such as mercerized pulps, microfibrillated pulp, rayon, vinylon, nylon , they may be mixed as appropriate acrylic, regenerated fibers such as polyester, semisynthetic fibers, synthetic fibers. フィルムとしては、ポリエステル系樹脂、ポリエチレンテレフタレート系樹脂、ジアセテート系樹脂、トリアテセート系樹脂、アクリル系樹脂、ポリカーボネート系樹脂、ポリ塩化ビニル系樹脂、ポリイミド系樹脂、セロハン、セルロイド等の材料が挙げられる。 The film, polyester resin, polyethylene terephthalate resin, diacetate resin, Toriateseto resins, acrylic resins, polycarbonate resins, polyvinyl chloride resins, polyimide resins, cellophane, and materials such as celluloid. 不織布としてはレーヨン、ビニロン、ナイロン、アクリル、ポリエステル、綿、パルプ、麻、羊毛、ガラス繊維等の材料を使用して乾式、湿式、直接式で製造したものが挙げられる。 The nonwoven rayon, vinylon, nylon, acrylic, polyester, cotton, pulp, hemp, wool, dry using a material such as glass fibers, wet, include those produced by direct expression. 合成紙としては、例えばポリプロピレン、ポリスチレン、ポリエチレン、エチレンープロピレン共重合体、エチレンー酢酸ビニル共重合、ポリ塩化ビニル、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリアミド等を原材料とし、延伸法により製造した物が挙げられるが、いずれも上記したものに限定されるものではない。 The synthetic paper, such as polypropylene, polystyrene, polyethylene, ethylene-propylene copolymer, ethylene-vinyl acetate copolymer, polyvinyl chloride, polyethylene terephthalate, polybutylene terephthalate, and polyamide as raw material, include those produced by stretching It is but none are not limited to those described above.

本発明において、シート状物に染料および/または顔料を含ませる方法としては、通常使用される一般的な方法が使用できる。 In the present invention, as a method to include dyes and / or pigments sheet, the general methods that are normally used can be used. 例えば紙、不織布であれば原料中に分散することが考えられ、フィルムであれば原料への練り込み等の対応が可能である。 Such as paper, it is believed that dispersed in the raw material if nonwoven, it is possible to correspond the kneading or the like into the raw material if the film. この他シート状物の表面への塗工を行うことも可能である。 It is also possible to perform coating on the surface of the other sheet.

本発明において、染料および/または顔料をシート状物に塗工する場合、カオリン、炭酸カルシウム、酸化チタン、クレー、タルク、水酸化アルミニウム、酸化亜鉛、ケイ酸アルミニウム、ケイ酸カルシウム、合成非晶質シリカ、ゼオライト等の無機系填料やスチレン系あるいはアクリル系プラスチックピグメント、ポリエチレン等の一般的に塗工用として使用される填料成分を適用することが好ましい。 In the present invention, when applying the dye and / or pigment in a sheet-like material, kaolin, calcium carbonate, titanium oxide, clay, talc, aluminum hydroxide, zinc oxide, aluminum silicate, calcium silicate, synthetic amorphous silica, inorganic filler and a styrene-based or acrylic-based plastic pigments such as zeolite, it is preferable to apply the general filler component which is used as a coating such as polyethylene. これらを全く含まないと塗工層中への有機溶剤の浸透が遅く、染料が溶出する現象の妨げとなり、さらにはブリスター、ブロッキングの原因となる場合もあるので好ましくない。 If does not contain these quite slow permeation of the organic solvent into the coating layer, it hampers phenomena dye is eluted, so more blisters, sometimes cause blocking undesirable.

本発明における染料および/または顔料を含む塗工層には、当該染料および/または顔料を0.05〜3.0質量%配合することが好ましい。 The coating layer containing a dye and / or pigment in the present invention, it is preferable to blend the dyes and / or pigments 0.05 to 3.0 wt%. 3.0質量%より多く配合すると製造機械を汚したり、裏写りを引き起こしたりするので好ましくない。 And 3.0% by weight to more blended or soil the production machine, so or cause the show-through is undesirable. 0.05質量%未満だと発色が弱くなるため十分な効果が得られないため好ましくない。 Undesirably sufficient effect can not be obtained for a less than 0.05 mass% coloring is weak.

本発明において染料および/または顔料を含む塗工層には、バインダーを全填料に対して10〜80質量部配合することが好ましい。 The coating layer containing a dye and / or pigments in the present invention, it is preferable to blend 10 to 80 parts by weight of binder relative to the total filler. 10質量部未満であるとバインダー量が不足するので塗料としての強度が弱くなり好ましくない。 Strength becomes weak undesirably as paint since the binder amount is less than 10 parts by mass is insufficient. また80質量部を超えると塗料としての強度は十分であるが、ブロッキングや塗工層表面のべたつき等の現象が著しくなるので好ましくない。 Strength as a coating exceeds 80 parts by mass Further is sufficient, undesirable phenomena stickiness such blocking and coating layer surface becomes significant. バインダーとしては、例えば合成高分子ラテックスとしてアクリル系、スチレン系、スチレン−アクリル系、スチレン−ブタジエン系などの各種共重合体を用いることができる。 As the binder, for example, acrylic as synthetic polymer latices, styrene, a styrene - acrylic, styrene - it is possible to use various copolymers such as butadiene. 更に、ポリビニルアルコール、カルボキシメチルセルロース等の合成バインダー、酸化デンプン、エーテル化デンプン、エステル化デンプン、酵素変性デンプン等のデンプン、変性デンプン、デンプン誘導体、カゼイン等の天然系バインダーも使用することができる。 Furthermore, polyvinyl alcohol, synthetic binders such as carboxymethyl cellulose, oxidized starch, etherified starch, esterified starch, starch such as enzyme-modified starches, modified starches, starch derivatives, can also be used natural binder such as casein. また、必要に応じて、分散剤、保水剤、消泡剤、耐水化剤、防かび剤、抗菌剤等の各種助剤も適宜配合することができる。 If necessary, dispersants, water retention agents, antifoaming agents, waterproofing agents, antifungal agents, various aids such as antimicrobial agents can also be appropriately blended.

本発明において、偽造防止用シート状物表面に填料およびバインダーを含む塗工層を設けることにより、例えば、染料および/または顔料を含んでいる塗工層を隠蔽することができるといったような種々の効果が得られるので好ましい。 In the present invention, by providing a coating layer comprising a filler and a binder on the anti-counterfeit sheet surface, for example, various such as can be concealed a coating layer containing dyes and / or pigments the preferred because the effect can be obtained.

また、填料およびバインダーを含む塗工層を設けることにより、染料および/または顔料を含む層への溶剤の浸透を向上させることができ、かつ溶出した染料および/または顔料のシート状物表面への拡散、定着も向上することができる。 Further, by providing the coating layer containing a filler and a binder, to dyes and / or pigments can improve the penetration of the solvent into the layer containing, and eluted dyes and / or pigments sheet surface of diffusion, fixing can be improved. その結果、発色が鮮明となり、目視での視認がより容易となる。 As a result, color development becomes clear, the visibility of the visual becomes easier. さらには、この塗工層を設けることで、シート状物の印刷適性を向上させることも可能となるので好ましい。 Further, by providing the coating layer is preferable because it is possible to improve the printability of the sheet.

填料およびバインダーを含む塗工層に用いる填料としては、カオリン、軽質炭酸カルシウム、重質炭酸カルシウム、タルク、酸化チタン、シリカ、クレー、プラスチックピグメント、コロイダルシリカ、アルミナ、水酸化アルミニウム、硫酸カルシウム、硫酸バリウム、酸化亜鉛、サチンホワイト、ケイ酸アルミニウム、ケイ酸マグネシウム、ケイ酸カルシウム、炭酸マグネシウム、ゼオライト等の紙塗工用として一般的に用いられる填料が適用できる。 The filler used in the coating layer comprising a filler and a binder, kaolin, light calcium carbonate, heavy calcium carbonate, talc, titanium oxide, silica, clay, plastic pigment, colloidal silica, alumina, aluminum hydroxide, calcium sulfate, barium, zinc oxide, satin white, aluminum silicate, magnesium silicate, calcium silicate, magnesium carbonate, commonly filler used for the paper coating of zeolite applied.

填料およびバインダーを含む塗工層には、バインダーを填料に対して5〜25質量部配合すると好ましい。 The coating layer comprising a filler and binder, preferably a binder from 5 to 25 parts by weight is blended with respect to the filler. バインダーとしては、アクリル系、スチレン系、スチレン−アクリル系、スチレン−ブタジエン系、尿素、無水マレイン酸、エチレン−酢酸ビニル共重合体、メラミン、メタクリレート系などの各種合成高分子、ポリビニルアルコール、カルボキシメチルセルロース、カルボキシエチルセルロース、アクリル酸エステル等の合成バインダー、または酸化デンプン、エーテル化デンプン、エステル化デンプン、酵素変性デンプン等のデンプン、変性デンプン、デンプン誘導体、カゼイン、大豆タンパク、ゼラチン等の天然系バインダーを使用することができる。 As the binder, acrylic, styrene, styrene - acrylic, styrene - butadiene, urea, maleic anhydride, ethylene - vinyl acetate copolymer, melamine, and various synthetic polymers such as methacrylate, polyvinyl alcohol, carboxymethyl cellulose the use carboxyethyl cellulose, synthetic binders or oxidized starch, such as acrylic acid esters, etherified starch, esterified starch, starch such as enzyme-modified starches, modified starches, starch derivatives, casein, soy protein, natural-based binder such as gelatin can do. また、必要に応じて、分散剤、保水剤、消泡剤、耐水化剤、防かび剤、抗菌剤等の各種助剤も適宜配合することができる。 If necessary, dispersants, water retention agents, antifoaming agents, waterproofing agents, antifungal agents, various aids such as antimicrobial agents can also be appropriately blended.

本発明において、染料および/または顔料を含む塗工層を設ける際にはエアナイフコーター、ブレードコーター、ダイコーター、ロールコーター、グラビアコーター、バーコーター、ゲートロールコーター等の一般的な塗工機が使用できる。 In the present invention, the coating layer air knife coater in providing a blade coater, die coater, roll coater, gravure coater, a bar coater, a general coating machine such as a gate roll coater is used that contains the dye and / or pigments it can.

本発明において、染料および/または顔料を含む塗工層を設ける際に印刷機を使用し塗工層が文字を形成するようにしても良い。 In the present invention, coating layers using a printing machine in providing a coating layer containing a dye and / or pigments may be formed characters. これにより有機溶剤で改竄を試みると文字を浮き上がらせることができ、偽造防止効果を一層向上させることができるので好ましい。 Thus it can clarify the character attempts to tamper with an organic solvent, since the anti-counterfeit effect can be further improved preferably.

以下に実施例を述べるが、文中の「質量部」、「g/m 」は固形分換算の数値を意味する。 As will be described by the following examples, "parts by weight" of the sentence, "g / m 2" means a numerical value on solid basis.
[実施例1] [Example 1]
カオリン70質量部、炭酸カルシウム30質量部、バインダーとしてデンプン5質量部、SBRラテックス(商品名「スマーテックスSN−322」日本エイアンドエル(株)製造)15質量部を主体とする水性塗料(濃度35質量%)を常法に従い調製した(これを塗料Aとする)。 70 parts by weight of kaolin, 30 parts by weight of calcium carbonate, starch 5 parts by weight as a binder, SBR latex (trade name "smart tex SN-322" Nippon A & L Inc. preparation) aqueous coating mainly composed of 15 parts by weight (concentration of 35 mass %) was prepared according to a conventional method (referred to as coating a). これに平均粒径が4μmの水不溶性でかつ有機溶剤可溶性のアンスラキノン系染料粒子(商品名「MACROLEX Red Violet R」ランクセス(株)製造)を塗料固形分に対し1質量部、平均粒径が3μmの水不溶性でかつ有機溶剤可溶性のピラリゾン系染料粒子(商品名「Kayaset Flavine FN」日本化薬(株)製造)を塗料固形分に対し5質量部添加した(これを塗料Bとする)。 1 part by weight with respect to the average particle size anthraquinone dye particles of water-insoluble and organic solvent-soluble 4 [mu] m (trade name "MACROLEX Red Violet R" Lanxess Corporation manufacturing) the paint solids to an average particle size of 3μm water insoluble and organic solvent-soluble pyrazoline dyes particles (trade name "Kayaset Flavine FN" by Nippon Kayaku Co. manufacturing) was added 5 parts by weight based on solid content (referred to as coating B). この塗料Bを針葉樹晒クラフトパルプ(NBKP)40質量部、広葉樹晒クラフトパルプ(LBKP)60質量部を400mlC. Softwood bleached kraft pulp (NBKP) 40 parts by mass of the paint B, hardwood bleached kraft pulp (LBKP) 400mlC 60 parts by mass. S. S. F. F. に叩解し、白土、紙力増強剤、サイズ剤を加えたスラリーを長網抄紙機で坪量60g/m に抄造した原紙片面にエアナイフコーターを用いて10g/m 塗工した。 Was beaten in, clay, paper strength agent was 10 g / m 2 coated with an air knife coater slurry plus sizing a base paper one surface that the papermaking basis weight 60 g / m 2 in Fourdrinier paper machine. さらにこの塗工層上に塗料Aを15g/m 塗工し、坪量が85g/m の偽造防止用シート状物を得た。 Furthermore paint A was 15 g / m 2 coated on the coating layer, basis weight was obtained anti-counterfeit sheet of 85 g / m 2.

[実施例2] [Example 2]
針葉樹晒クラフトパルプ(NBKP)40質量部、広葉樹晒クラフトパルプ(LBKP)60質量部を400mlC. Softwood bleached kraft pulp (NBKP) 40 parts by weight, hardwood bleached kraft pulp (LBKP) 400mlC 60 parts by mass. S. S. F. F. に叩解し、これに紙力増強剤0.4質量部、サイズ剤0.3質量部、硫酸バンドを適量添加しパルプスラリーを調整した。 Was beaten in, Kamiryoku enhancer 0.4 parts by weight of a sizing agent 0.3 part by mass, to prepare a pulp slurry was added an appropriate amount of aluminum sulfate. これに平均粒径が4μmのアンスラキノン系染料粒子(商品名「MACROLEX Red Violet R」ランクセス(株)製造)を1.0質量部、平均粒径が3μmの水不溶性でかつ有機溶剤可溶性のピラリゾン系染料粒子(商品名「Kayaset Flavine FN」日本化薬(株)製造)を3.0質量部混合した後、常法に従い長網抄紙機で95g/m の偽造防止用シート状物を得た。 Average particle size 4μm anthraquinone dye particles (trade name "MACROLEX Red Violet R" Lanxess Corporation production) 1.0 parts by weight to an average particle size and the organic solvent-soluble and 3μm water insoluble pyrazoline after system dye particles (trade name "Kayaset Flavine FN" by Nippon Kayaku Co. manufacturing) were mixed 3.0 parts by weight, to give the anti-counterfeit sheet of 95 g / m 2 by a conventional method Fourdrinier It was.

[実施例3] [Example 3]
実施例2と同様の方法で針葉樹晒クラフトパルプ(NBKP)40質量部、広葉樹晒クラフトパルプ(LBKP)60質量部を400mlC. Softwood bleached kraft pulp (NBKP) 40 mass parts in the same manner as in Example 2, hardwood bleached kraft pulp (LBKP) 400mlC 60 parts by mass. S. S. F. F. に叩解し、これに紙力増強剤0.4質量部、サイズ剤0.3質量部、硫酸バンドを適量添加しパルプスラリーを調整した。 Was beaten in, Kamiryoku enhancer 0.4 parts by weight of a sizing agent 0.3 part by mass, to prepare a pulp slurry was added an appropriate amount of aluminum sulfate. これに平均粒径が3μmのピグメント系顔料粒子(商品名「Sumikaprint Red BF」住化カラー(株)製造)を3.0質量部、平均粒径4μmのピグメント系顔料粒子(商品名「Sumikaprint Yellow 2RN」住化カラー(株)製造)を5.0質量部混合した後、常法に従い長網抄紙機で95g/m の偽造防止用シート状物を得た。 Average particle size 3μm pigment-based pigment particles (trade name "Sumikaprint Red BF" by Sumika Color Co. preparation) 3.0 parts by weight of a mean particle size 4μm pigment-based pigment particles (trade name "Sumikaprint Yellow 2RN "manufactured by Sumika color Co. production) were mixed 5.0 part by weight of the anti-counterfeit sheet of 95 g / m 2 by a conventional method Fourdrinier.

[実施例4] [Example 4]
カオリン70質量部、炭酸カルシウム30質量部、バインダーとしてデンプン5質量部、SBRラテックス(商品名「スマーテックスSN−322」)15質量部を主体とする水性塗料(濃度35質量%)を常法に従い調製し、塗料Aとした。 70 parts by weight of kaolin, 30 parts by weight of calcium carbonate, starch 5 parts by weight as a binder, SBR latex (trade name "smart tex SN-322") water-based paint made mainly of 15 parts by mass (concentration 35 mass%) according to a conventional method prepared, and the paint a. これに平均粒径が4μmの水不溶性でかつ有機溶剤可溶性のアゾ系染料粒子(商品名「SPILON RED GEH Special」)を塗料固形分に対し1質量部、平均粒径が4μmの水不溶性でかつ有機溶剤可溶性のアゾ系染料粒子(商品名「SPILON BLUE 2BNH」)を塗料固形分に対し5質量部添加し、塗料Bとした。 1 part by weight relative to solid content of the average particle size of 4μm water insoluble and organic solvent-soluble azo dye particles (trade name "Spilon RED GEH Special") to an average particle size and with 4μm water insoluble organic solvent-soluble azo dye particles (trade name "SPILON BLUE 2BNH") were added 5 parts by weight based on coating solids, was paint B. この塗料Bを針葉樹晒クラフトパルプ(NBKP)40質量部、広葉樹晒クラフトパルプ(LBKP)60質量部に白土、紙力増強剤、サイズ剤を加えたスラリーを長網抄紙機で坪量60g/m に抄造した原紙片面にエアナイフコーターを用いて10g/m 塗工した。 Softwood bleached kraft pulp (NBKP) 40 parts by mass of the paint B, leaf bleached kraft pulp (LBKP) clay to 60 parts by weight, basis weight of 60 g / m paper strength agent, a slurry was added sizing agent in Fourdrinier and 10 g / m 2 coated with an air knife coater on a base paper one surface that the papermaking 2. さらにこの塗工層上に塗料Aを15g/m 塗工し、坪量が85g/m の偽造防止用シート状物を得た。 Furthermore paint A was 15 g / m 2 coated on the coating layer, basis weight was obtained anti-counterfeit sheet of 85 g / m 2.

[実施例5] [Example 5]
カオリン70質量部、炭酸カルシウム30質量部、バインダーとしてデンプン5質量部、SBRラテックス(商品名「スマーテックスSN−322」)15質量部を主体とする水性塗料(濃度35質量%)を常法に従い調製し、塗料Aとした。 70 parts by weight of kaolin, 30 parts by weight of calcium carbonate, starch 5 parts by weight as a binder, SBR latex (trade name "smart tex SN-322") water-based paint made mainly of 15 parts by mass (concentration 35 mass%) according to a conventional method prepared, and the paint a. これに平均粒径が3μmの水不溶性でかつ有機溶剤可溶性のアゾ系顔料粒子(商品名「モノアゾレーキ10G」)を塗料固形分に対し1質量部、平均粒径が4μmの水不溶性でかつ有機溶剤可溶性のアゾ系染料粒子(商品名「シアニンブルーHS−3」大日精化(株)製造)を塗料固形分に対し5質量部添加し、塗料Bとした。 Average particle size 3μm water insoluble and organic solvent-soluble azo pigment particles thereto (trade name "monoazo laked 10G") to 1 part by weight relative to paint solids, a water-insoluble average particle size of 4μm and organic solvents soluble azo dye particles (trade name "cyanine Blue HS-3" manufactured by Dainichi Seika Co. preparation) was added 5 parts by weight based on coating solids, was paint B. この塗料Bを針葉樹晒クラフトパルプ(NBKP)40質量部、広葉樹晒クラフトパルプ(LBKP)60質量部に白土、紙力増強剤、サイズ剤を加えたスラリーを長網抄紙機で坪量60g/m に抄造した原紙片面にエアナイフコーターを用いて10g/m 塗工した。 Softwood bleached kraft pulp (NBKP) 40 parts by mass of the paint B, leaf bleached kraft pulp (LBKP) clay to 60 parts by weight, basis weight of 60 g / m paper strength agent, a slurry was added sizing agent in Fourdrinier and 10 g / m 2 coated with an air knife coater on a base paper one surface that the papermaking 2. さらにこの塗工層上に塗料Aを15g/m 塗工し、坪量が85g/m の偽造防止用シート状物を得た。 Furthermore paint A was 15 g / m 2 coated on the coating layer, basis weight was obtained anti-counterfeit sheet of 85 g / m 2.

[実施例6] [Example 6]
ポリプロピレン製の合成紙(ユポFPG#110,(株)ユポ・コーポレーション社製)を用意し、これにバーコーターを用いて、実施例4で使用した塗料Bを10g/m 塗工した。 Polypropylene synthetic paper (Yupo FPG # 110, (Ltd.) Yupo Corporation Co., Ltd.) was prepared, to which by means of a bar coater, and 10 g / m 2 coated with the coating material B used in Example 4. さらにこの塗工層上に実施例4で使用した塗料Aを15g/m 塗工し、偽造防止用シート状物を得た。 The coating paint A used in Example 4 on the layer 15 g / m 2 was applied to obtain the anti-counterfeit sheet further.

[実施例7] [Example 7]
表面に親水化処理を施したポリエチレンテレフタレート製フィルムシート(厚さ110μm)を用意し、これにバーコーターにて実施例5で使用した塗料Bを固形分質量で10g/m 塗工した。 Providing a polyethylene terephthalate film sheet (thickness 110 [mu] m) which surface is subjected to hydrophilization treatment, this was 10 g / m 2 coated with solid mass paint B used in Example 5 at a bar coater. さらにこの塗工層上に実施例5で使用した塗料Aを15g/m 塗工して偽造防止用シート状物を得た。 To give an additional anti-counterfeit sheet paint A used in Example 5 in the coating layer was 2 coated 15 g / m.

[実施例8] [Example 8]
坪量50g/m のポリエステル不織布を用意し、これにロールコーターにて実施例5で使用した塗料Bを固形分質量で10g/m 塗工した。 Providing a polyester nonwoven fabric of basis weight 50 g / m 2, and 10 g / m 2 coated with solid mass paint B used in Example 5 by a roll coater to this. さらにこの塗工層上に実施例5で使用した塗料Aを15g/m 塗工して偽造防止用シート状物を得た。 To give an additional anti-counterfeit sheet paint A used in Example 5 in the coating layer was 2 coated 15 g / m.

[比較例1] [Comparative Example 1]
実施例1と同様の方法で針葉樹晒クラフトパルプ(NBKP)40質量部、広葉樹晒クラフトパルプ(LBKP)60質量部を400mlC. Softwood bleached kraft pulp (NBKP) 40 mass parts in the same manner as in Example 1, hardwood bleached kraft pulp (LBKP) 400mlC 60 parts by mass. S. S. F. F. に叩解し、これに紙力増強剤0.4質量部、サイズ剤0.3質量部、硫酸バンドを適量添加しパルプスラリーを調整した。 Was beaten in, Kamiryoku enhancer 0.4 parts by weight of a sizing agent 0.3 part by mass, to prepare a pulp slurry was added an appropriate amount of aluminum sulfate. これにフタロシアニン系のカチオン性直接染料(商品名「Turquoise K−GL liq」クラリアント(株)製造)(水溶性で有機溶剤に不溶性)を内添し、常法に従い長網抄紙機にて95g/m のシート状物を抄造した。 Cationic direct dyes of phthalocyanine thereto (trade name "Turquoise K-GL liq" Clariant Corp. manufacturing) were internally added (insoluble in an organic solvent in water-soluble), 95 g at ordinary manner Fourdrinier / the sheet material of m 2 and papermaking.

[比較例2] [Comparative Example 2]
ポリプロピレン樹脂を主成分として二軸延伸フィルム成形された、合成紙(ユポFPG#200,王子油化合成紙製)上に塗料Aにフタロシアニン系のカチオン性直接染料(商品名「Turquoise K−GL liq」クラリアント(株)製造)を混合した塗料(塗料Cとする)を15g/m 塗工しシート状物を得た。 Polypropylene resin is biaxially stretched film molding as the main component, a synthetic paper (Yupo FPG # 200, Oji-Yuka Synthetic Paper) cationic phthalocyanine direct dye (trade name Coating A on "Turquoise K-GL liq "Clariant Co., Ltd. paint mixed preparation) (a paint C) to give a 15 g / m 2 coated with sheet.

[比較例3] [Comparative Example 3]
表面に親水化処理を施したポリエチレンテレフタレート製フィルムシート(厚さ110μm)を用意し、これにバーコーターにて比較例2と同じ塗料Cを15g/m 塗工してシート状物を得た。 Providing a hydrophilic treatment of the polyethylene terephthalate film sheet which has been subjected (thickness 110 [mu] m) on the surface to obtain a sheet-like material thereto was 2 coated 15 g / m the same coating C as in Comparative Example 2 by a bar coater .

[比較例4] [Comparative Example 4]
坪量50g/m のポリエステル不織布を用意し、これにロールコーターにて比較例2と同じ塗料Cを15g/m 塗工してシート状物を得た。 Providing a polyester nonwoven fabric of basis weight 50 g / m 2, to obtain a sheet-like material thereto was 2 coated 15 g / m the same coating C as in Comparative Example 2 by a roll coater.

実施例および比較例で得られたシート状物の表面に代表的な有機溶剤として酢酸エチル、トルエン、メチルエチルケトン、イソプロピルアルコール、ベンゼンを滴下し、有機溶剤が蒸発した後に滴下した個所を可視光下で目視観察した。 Ethyl acetate as a typical organic solvent to the surface of the sheet obtained in Examples and Comparative Examples, toluene, methyl ethyl ketone, isopropyl alcohol, was added dropwise benzene, the point was dropped after the organic solvent was evaporated under visible light It was visually observed. なお、参考のため水を滴下した場合についても目視観察した。 Incidentally, it was also visually observed for the case where water was added dropwise for reference. 以上の観察結果を表2、表3に示す。 Shown in Table 2, Table 3 or more observations. 発色は、著しい発色を◎、通常の発色を○、変化しないものを×と評価し、○以上を合格とした。 Color development, significant color development ◎, ○ a normal color, was evaluated as × those that do not change, was passed more than ○. なお、評価に用いる可視光は自然光下、白熱電球による照明下どちらでも同一の結果が得られることを確認した。 The visible light used for evaluation was confirmed that under natural light, the same result either under illumination by incandescent light bulbs can be obtained.

(表2) (Table 2)
(表3) (Table 3)

実施例1の塗工面、および実施例2、実施例3の用紙表面は染料または顔料粒子が均一に分散されているため、使用している染料または顔料の色相に淡く着色されているように見える。 Coated surface, and Example 2, the surface of the paper of Example 3 of Example 1 since the dye or pigment particles are uniformly dispersed, appears to be pale colored hue of dye or pigment being used . しかし、拡大鏡を使用して観察すると粒子の状態で分布していることがわかる。 However, it can be seen that distributed in the particle state of when observed using a magnifying glass.

これら実施例で得られた偽造防止用シート状物の表面に各種有機溶剤を滴下すると、含まれている染料または顔料が溶出して、毛細管現象で周囲に拡散する。 Added dropwise and various organic solvents on the surface of the obtained anti-counterfeit sheet in these examples, dyes or pigments are included eluted, diffusing around a capillary phenomenon. 溶剤が揮発した後に滴下部位を観察すると、例えば酢酸エチルの滴下においては実施例1、実施例4、実施例6で黄に赤の斑点が確認され、実施例2、実施例3では赤の円が、実施例5、実施例7、実施例8で青の斑点が確認された。 When the solvent is observed dripping site after volatilized, for example, embodiments in dropwise ethyl acetate 1, Example 4, Yellow Red spots were identified in Example 6, Example 2, Example 3, the red circle but example 5, example 7, speckled blue was confirmed in example 8. トルエンの滴下では、実施例1、実施例2、実施例4、実施例6で黄に赤の斑点が、実施例3で赤の円が、実施例5、実施例7、実施例8で青の円が確認された。 The dropwise addition of toluene, Example 1, Example 2, Example 4, red spots on the yellow in Example 6, the red circle in Example 3, blue in Example 5, Example 7, Example 8 circle of has been confirmed. メチルエチルケトンの滴下では、実施例1、実施例4、実施例6で黄に赤の斑点が、実施例2で黄に赤の円が、実施例3で赤の円が、実施例5、実施例7、実施例8で赤に青の斑点が確認された。 The methyl ethyl ketone dropwise, Example 1, Example 4, red spots on the yellow in Example 6, a circle of red yellow in Example 2, the red circle in Example 3, Example 5, Example 7, spots of blue has been confirmed in the red in example 8. イソプロピルアルコールの滴下では、実施例1、実施例2、実施例4、実施例6で黄の円が、実施例3で赤に黄の斑点が、実施例5、実施例7、実施例8で赤の斑点が確認された。 The dropwise addition of isopropyl alcohol, Example 1, Example 2, Example 4, a circle of yellow in Example 6, spots yellow to red in Example 3, Example 5, Example 7, Example 8 red spots has been confirmed. ベンゼンの滴下では、実施例1、実施例2、実施例4、実施例6で黄の円が、実施例3で赤と黄の斑点が、実施例5、「実施例7、実施例8で赤に青の斑点が確認された。また、いずれの実施例においても、水の滴下においては何らの変化も確認されなかった。また、比較例1〜4は、テストで使用した全ての有機溶剤、及び水の滴下に対して何らの変化も確認されなかった。 The dropwise addition of benzene, Example 1, Example 2, Example 4, a circle of yellow in Example 6, spots red and yellow in Example 3, Example 5, "Example 7, Example 8 red spots blue was confirmed. Further, in all examples, the dropping of the water was also confirmed no change. in Comparative example 1-4, all of the organic solvent used in the test , and it was also confirmed no change against dripping water.

本発明の偽造防止用シート状物は、下記に示すような効果を有する。 Anti-counterfeit sheet of this invention has the effect shown below.
(1)パスポート、トラベラーズチェック、小切手、手形、身分証明書では油溶性インキを使用して氏名、金額などの可変情報を記載する事が多く、また、パスポート、身分証明書などは写真を保護するシートが貼られていることが多い。 (1) passport, traveler's checks, checks, bills, full name in the identification using an oil-soluble ink, it is a number that describes the variable information such as the amount of money, also, passport, such as the identification is to protect the photo it is often the sheet is affixed. 本発明によれば、溶剤を用いて油溶性インキを使用した可変情報の改竄や、写真の貼り替えを試みた際の痕跡が、特別な器具を使用することなく可視光下で目視にて視認できることが可能となることから、本発明の偽造防止用シート状物はこのような偽造防止用途に好適に使用することができる。 According to the present invention, visual alteration or variable information using the oil-soluble ink, traces when attempting to stick re pictures are visually under visible light without the use of special instruments with a solvent since it is possible to be able to, anti-counterfeit sheet of this invention can be suitably used for such anti-counterfeiting applications.
(2)また、溶剤、ラベル剥がしを使用して不正を行い、再添付した痕跡を容易に視認することができるという特徴を活かして、ブランド品の証明、電子機器の封印(クレジットカードリーダーなど内部仕様の不正な書き換えを防ぐ目的)といったブランドプロテクトラベル用途にも好適に使用できる。 (2) In addition, make solvent, unauthorized using the peel off label, internal taking advantage of the feature that the re-attach the traces can be easily visible, proof of brand-name products, such as sealing of electronic devices (credit card reader an illegal rewriting of the specification can also be suitably used in brand protection label applications such purposes) to prevent.
(3)本発明で使用する染料および/または顔料は、改竄に使用されると目される溶剤に応じて適宜選択することができる。 (3) dyes and / or pigments used in the present invention can be appropriately selected depending on the solvent to be eye when used to tampering. また、溶解度パラメーターの異なる2種類以上の染料および/または顔料を同時に使用することで、幅広い溶剤に対応することができ、その溶解性の違いから、改竄の痕跡が円状、斑点状など一定でないため、より高い偽造防止効果が得られる。 Moreover, the use of two or more dyes having different solubility parameter and / or pigments simultaneously, it is possible for a wide range of solvents, from the difference of the solubility, not constant traces of tampering circular, spotty etc. Therefore, a higher forgery prevention effect can be obtained.

:本発明の偽造防止用シート状物について一例を示した断面図である。 : It is a cross-sectional view showing an example for anti-counterfeit sheet of this invention. 基材中に水不溶性でかつ有機溶剤可溶性の染料および/または顔料を含有する。 Containing a dye and / or pigment water-insoluble and organic solvent-soluble in the substrate. :本発明の偽造防止用シート状物を示した一例を示した断面図である。 : It is a cross-sectional view showing an example showing the anti-counterfeit sheet of this invention. 基材上に顔料を含む塗工層を設けている。 It is provided a coating layer comprising a pigment on a substrate. :本発明の偽造防止用シート状物を示した一例を示した断面図である。 : It is a cross-sectional view showing an example showing the anti-counterfeit sheet of this invention. 図1のシート状物上に顔料を含む塗工層を設けている。 It is provided a coating layer containing a pigment on a sheet-like material of Figure 1.

符号の説明 DESCRIPTION OF SYMBOLS

1. 1. 基材2. The base material 2. 染料または顔料粒子3. Dye or pigment particles 3. 顔料塗工基材 Pigment coated substrate

Claims (5)

  1. 水不溶性でかつ有機溶剤可溶性の通常の光源下で発色する染料および/または顔料(但し 、粉状物質との混合物の造粒物を除く)を1種類以上含む塗工層が少なくともシート状物の片面に存在し、 Dyes and / or pigments which color under normal light source of the water insoluble and organic solvent-soluble (but granules excluding the mixture of the powdery material) of the coating layer is at least sheet-like material comprising one or more It exists on one side,
    前記塗工層上に填料およびバインダーを含む塗工層が存在しており、 Wherein and coating layer is present containing filler and binder in the coating layer,
    1種類以上の有機溶剤の滴下による改竄の痕跡を可視光下で視認できるようにしたことを特徴とする偽造防止用シート状物。 Anti-counterfeit sheet material one or more traces of tampering by dropwise addition of an organic solvent, characterized in that to be able to visually recognize under visible light.
  2. 溶解度パラメーターの異なる2種類以上の有機溶剤をそれぞれ滴下したときに、いずれの場合でも滴下の痕跡を可視光下で視認できることを特徴とする請求項1記載の偽造防止用シート状物。 Two or more organic solvents having different solubility parameter and when dropped respectively, the anti-counterfeit sheet according to claim 1, wherein traces of dropping any case, characterized in that the visible under visible light.
  3. シート状物が木材パルプを主原料としたものであることを特徴とした、請求項1又は2記載の偽造防止用シート状物。 Sheet is characterized by a constitution that the wood pulp as the main raw material, according to claim 1 or 2 anti-counterfeit sheet according.
  4. 水不溶性でかつ有機溶剤可溶性の通常の光源下で発色する染料(但し、粉状物質との混合 物の造粒物を除く)がアゾ系染料、アミノケトン系染料、クマリン系染料であることを特徴とする請求項1〜3のいずれか1項に記載の偽造防止用シート状物。 Wherein water-insoluble and dyes coloring under normal light source of an organic solvent-soluble (except for granulation of a mixture of the powdery material) is azo dyes, aminoketone dyes, that the coumarin-based dye anti-counterfeit sheet according to any one of claims 1 to 3.
  5. 水不溶性でかつ有機溶剤可溶性の通常の光源下で発色する顔料(但し、粉状物質との混合 物の造粒物を除く)がアゾ系顔料、フタロシアニン系顔料であることを特徴とする請求項1〜3のいずれか1項に記載の偽造防止用シート状物。 Claims pigment that develops color under normal light source of the water insoluble and organic solvent-soluble (except for granulation of a mixture of the powdery material) is characterized in that an azo-based pigments, phthalocyanine pigments anti-counterfeit sheet according to any one of 1 to 3.
JP2006206762A 2006-07-28 2006-07-28 Anti-counterfeit sheet-like material Active JP5083796B2 (en)