JP5040070B2 - Charge transport material, laminate and organic electroluminescent device - Google Patents
Charge transport material, laminate and organic electroluminescent device Download PDFInfo
- Publication number
- JP5040070B2 JP5040070B2 JP2005149918A JP2005149918A JP5040070B2 JP 5040070 B2 JP5040070 B2 JP 5040070B2 JP 2005149918 A JP2005149918 A JP 2005149918A JP 2005149918 A JP2005149918 A JP 2005149918A JP 5040070 B2 JP5040070 B2 JP 5040070B2
- Authority
- JP
- Japan
- Prior art keywords
- group
- charge transport
- transport material
- ring
- organic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、電荷輸送材料並びにそれを用いた積層体及び有機電界発光素子に関する。 The present invention relates to a charge transport material, a laminate using the same, and an organic electroluminescent device.
近年、薄膜型の電界発光素子(以下適宜、「EL素子」という)としては、電荷輸送材料などに無機材料を使用したものに代わり、有機材料を用いた有機EL素子の開発が行われるようになっている。また、有機EL素子の発光効率を上げる試みとして、蛍光(一重項励起子による発光)ではなく燐光(三重項励起子による発光)を用いることが検討されている。燐光を用いると、蛍光を用いたEL素子と比べて、3倍程度に発光効率が向上すると考えられており、例えば、ユーロピウム錯体、白金錯体等を使用することが報告されている。 In recent years, as thin-film electroluminescent elements (hereinafter referred to as “EL elements” as appropriate), organic EL elements using organic materials have been developed in place of those using inorganic materials as charge transport materials and the like. It has become. In addition, as an attempt to increase the light emission efficiency of the organic EL element, use of phosphorescence (light emission by triplet excitons) instead of fluorescence (light emission by singlet excitons) has been studied. When phosphorescence is used, it is considered that the luminous efficiency is improved about three times as compared with an EL element using fluorescence. For example, it has been reported that a europium complex, a platinum complex, or the like is used.
これまでに開発された燐光分子を用いた有機EL素子の多くは、発光層のホスト材料として、カルバゾリル基を含む材料を用いている。そのような技術の例を挙げれば、例えば、非特許文献1が挙げられる。非特許文献1では、発光層のホスト材料として、以下の構造式で表わされるビフェニル誘導体(H−1)を用いている。
ビフェニル誘導体(H−1)は、連結基を介して一分子中に2つのカルバゾール環を有し、かつN原子同士が共役しているため、正孔輸送能と電子輸送能とがともに優れている。このため、ビフェニル誘導体(H−1)は、耐熱性、非晶質性には課題を有するものの、ホスト材料として優れて理想的な材料と考えられていた。 Since the biphenyl derivative (H-1) has two carbazole rings in one molecule through a linking group and N atoms are conjugated, both hole transport ability and electron transport ability are excellent. Yes. For this reason, although the biphenyl derivative (H-1) has problems in heat resistance and amorphousness, it is considered to be an excellent and ideal material as a host material.
しかしながら、ビフェニル誘導体(H−1)をホスト材料に用いた有機EL素子をはじめ、従来の有機EL素子は、フラットパネル・ディスプレイ等の表示素子に応用するためには駆動寿命を向上する必要があり、いまだ実用の域に達していない。
そこで、これまで、駆動寿命を向上させるための技術の研究がなされてきた。例えば、特許文献1では、有機EL素子を構成するいずれかの層において、その層を構成する電荷輸送材料中の不純物であるハロゲン化合物の含有量を低減させることにより、有機EL素子の駆動寿命を向上させると共に、駆動電圧を低下させることが記載されている。
However, conventional organic EL elements including organic EL elements using biphenyl derivatives (H-1) as host materials need to have a longer driving life in order to be applied to display elements such as flat panel displays. It has not yet reached the practical level.
So far, research has been conducted on techniques for improving the drive life. For example, in Patent Document 1, in any layer constituting an organic EL element, the drive life of the organic EL element is increased by reducing the content of a halogen compound that is an impurity in the charge transport material constituting the layer. It is described that the drive voltage is lowered while improving.
有機EL素子では、その使用に伴って、駆動に要する電圧が上昇する。有機EL素子を実用化するには、駆動寿命を向上させる他、この駆動電圧上昇を抑制する必要がある。しかし、特許文献1などの従来の技術では、駆動電圧上昇を抑制することができなかった。
本発明は上記の課題に鑑みて創案されたもので、有機EL素子の駆動寿命を向上させるとともに、駆動電圧上昇を抑制することができる電荷輸送材料、並びに、それを用いた積層体及び有機電界発光素子を提供することを目的とする。
In the organic EL element, the voltage required for driving increases with use. In order to put the organic EL element into practical use, it is necessary to improve the driving life and suppress the increase in driving voltage. However, the conventional technology such as Patent Document 1 cannot suppress the drive voltage rise.
The present invention was devised in view of the above problems, and improves the driving life of an organic EL element and suppresses an increase in driving voltage, as well as a laminate and an organic electric field using the same. An object is to provide a light-emitting element.
本発明の発明者らは、上記課題を解決するべく、電荷輸送材料中に使用される化合物及び混入している副成分に関して鋭意検討した結果、電荷輸送材料に含まれる特定の基の濃度を所定値以下とすることにより、駆動寿命が長く、且つ、駆動電圧上昇を抑制することができる有機電界発光素子を得られることを見出し、本発明を完成させた。 In order to solve the above-mentioned problems, the inventors of the present invention have intensively studied the compounds used in the charge transport material and the subcomponents mixed therein, and as a result, determined the concentration of a specific group contained in the charge transport material. It was found that an organic electroluminescent element having a long driving life and capable of suppressing an increase in driving voltage can be obtained by setting it to a value not more than the value, and the present invention has been completed.
即ち、本発明の要旨は、酸化電位が+0.8V以上である、以下に記載するいずれかの構造からなるピリジン系化合物を含む有機電界発光素子用電荷輸送材料であって、
また、本発明の別の要旨は、酸化電位が+0.8V以上である、以下に記載するいずれかの構造からなるピリジン系化合物を含む有機電界発光素子用電荷輸送材料であって、
このとき、前記式(1)で表される基が、前記ピリジン系化合物の原料もしくは中間体または前記ピリジン系化合物を置換する基であることが好ましい(請求項3)。
さらに、前記式(1)で表わされる基が、メチル基またはメチレン基であることが好ましい(請求項4)。
At this time, it is preferable that the group represented by the formula (1) is a group that substitutes the raw material or intermediate of the pyridine compound or the pyridine compound (Claim 3).
Furthermore, it is preferable that the group represented by the formula (1) is a methyl group or a methylene group .
また、本発明の別の要旨は、上記の有機電界発光素子用電荷輸送材料のみから形成された層を少なくとも有することを特徴とする、有機電界発光素子用積層体に存する(請求項5)。
さらに、本発明の更に別の要旨は、上記の有機電界発光素子用電荷輸送材料と、ドーパントとから形成された有機発光層を少なくとも有することを特徴とする、有機電界発光素子用積層体に存する(請求項6)。
Another gist of the present invention resides in a laminate for an organic electroluminescence device , characterized in that it has at least a layer formed only from the charge transport material for an organic electroluminescence device .
Furthermore, still another subject matter of the present invention resides in a laminate for an organic electroluminescent device , characterized by having at least an organic light emitting layer formed from the charge transport material for an organic electroluminescent device described above and a dopant. (Claim 6).
また、本発明の更に別の要旨は、基板上に、陽極と、陰極と、該陽極及び該陰極の間に設けられた有機発光層とを有し、更に、上記の有機電界発光素子用電荷輸送材料のみから形成された層を少なくとも1層有することを特徴とする、有機電界発光素子に存する(請求項7)。
さらに、本発明の更に別の要旨は、基板上に、陽極と、陰極と、該陽極及び該陰極との間に設けられ、上記の有機電界発光素子用電荷輸送材料及びドーパントから形成された有機発光層とを有することを特徴とする、有機電界発光素子に存する(請求項8)。
Still another subject matter of the present invention, on a substrate, an anode, comprises a cathode, and an organic light emitting layer provided between the anode and the cathode, further, the organic electroluminescence device for charge An organic electroluminescent element having at least one layer formed of only a transport material (Claim 7).
Still another subject matter of the present invention is an organic material formed on a substrate between an anode, a cathode, the anode and the cathode, and formed from the charge transport material for an organic electroluminescent element and a dopant. An organic electroluminescent device comprising a light emitting layer (claim 8).
ここで、式(1)で表わされる基が少ないことが好ましい理由について説明する。
本発明の発明者らが推察するところ、有機EL素子の駆動電圧が上昇する要因は、有機EL素子を構成する化合物が、使用に伴い、本来の分子構造から変化するためと考えられる。また、この分子構造の変化は、有機EL素子の電荷輸送材料等の有機化合物が、電気的酸化や還元を受ける際の、酸化状態や還元状態の安定性に関係すると考えられる。
Here, the reason why it is preferable that the number of groups represented by the formula (1) is small will be described.
As the inventors of the present invention infer, the reason why the driving voltage of the organic EL element increases is that the compound constituting the organic EL element changes from its original molecular structure with use. In addition, this change in molecular structure is considered to be related to the stability of the oxidation state or reduction state when an organic compound such as a charge transport material of the organic EL element undergoes electrical oxidation or reduction.
上記のような酸化状態や還元状態の安定性の低下は、本来耐久性に優れている電荷輸送材料中に、酸化状態や還元状態の安定性に劣る副成分が混在することにより誘起されると考えられる。 The decrease in stability of the oxidized state or reduced state as described above is induced by the presence of a minor component inferior in stability of the oxidized state or reduced state in the charge transport material that is inherently excellent in durability. Conceivable.
上記の見解に基づき検討した結果、前記の式(1)で表わされる基を有する化合物を有する場合に、駆動電圧上昇及び駆動寿命に課題が生じることが分かった。この課題は、式(1)で表わされる基を有する化合物を、主成分として大量に有する場合はもちろん、副成分として少量有する場合であっても生じる。 As a result of examination based on the above view, it has been found that when a compound having a group represented by the above formula (1) is included, a problem occurs in driving voltage increase and driving life. This problem arises not only when the compound having the group represented by the formula (1) is contained in a large amount as a main component but also when it is contained in a small amount as an accessory component.
例えば、一般に入手可能なカルバゾールには、比較的高い濃度でメチル置換カルバゾールが混入している。具体例を挙げると、市販のカルバゾールは、通常、純度95〜98%であり、その中に、置換位置の異なる少なくとも2種類のメチル置換カルバゾール{下記式(2)}を0.1〜1.0重量%程度含有している。
よって、市販のカルバゾールを用いて合成されたカルバゾール系化合物には、完全に除去することが困難な不純物として、式(2)のメチル置換カルバゾールに起因するメチル置換体が含まれている。したがって、このようにして合成されたカルバゾール系化合物を電荷輸送材料として有機EL素子を製造した場合、この不純物であるメチル置換体が、駆動電圧上昇及び駆動寿命の課題の原因となっていた。 Therefore, a carbazole compound synthesized using a commercially available carbazole contains a methyl-substituted product derived from the methyl-substituted carbazole of formula (2) as an impurity that is difficult to remove completely. Therefore, when an organic EL device is produced using the carbazole compound synthesized as described above as a charge transport material, the methyl substitution product, which is an impurity, causes problems of an increase in driving voltage and driving life.
以上のように、式(1)で表わされる基は、駆動電圧上昇及び駆動寿命の課題の原因となっている。したがって、これを少なくする、あるいは無くすことにより、分子構造の変化を生じない安定な電荷輸送材料を得ることができる。これにより、駆動寿命が長く、且つ、駆動電圧上昇を抑制できる有機電界発光素子が得られるようになるのである。 As described above, the group represented by the formula (1) causes the problem of the drive voltage rise and the drive life. Therefore, by reducing or eliminating this, a stable charge transport material that does not cause a change in molecular structure can be obtained. As a result, an organic electroluminescent element having a long driving life and capable of suppressing an increase in driving voltage can be obtained.
本発明の電荷輸送材料や積層体を用いることにより、駆動寿命が向上し、且つ、駆動電圧上昇を抑制することが可能な、有機電界発光素子を得ることができる。 By using the charge transport material or the laminate of the present invention, an organic electroluminescence device capable of improving the driving life and suppressing an increase in driving voltage can be obtained.
以下、本発明について説明するが、本発明は以下の説明に限定されるものではなく、その要旨を逸脱しない範囲において任意に変形して実施することができる。
[I.電荷輸送材料]
本発明の電荷輸送材料は、酸化電位が+0.8V以上の1種又は2種以上の化合物よりなり、且つ、本発明の電荷輸送材料中の下記式(1)で表わされる基(以下適宜、CH基という)の存在割合が、0〜70ppmである。ただし、本明細書において「ppm」は、重量を基準とした割合を表わす。また、本発明の電荷輸送材料に含まれる化合物は有機化合物であるが、有機EL素子の材料として使用する場合には、適宜、任意の無機化合物と混合して用いることもできる。また、CH基の炭素原子は、少なくとも1つの、アリール基、ヘテロアリール基またはカルボニル基と直接結合するか、或いは、少なくとも1つの、アリール基またはヘテロアリール基と直接結合する。特に、CH基の炭素原子が少なくとも1つのアリール基またはヘテロアリール基と直接結合している場合にCH基は駆動電圧上昇や駆動寿命低下をより招きやすいため、少なくとも1つのアリール基またはヘテロアリール基と直接結合する炭素原子を有するCH基の存在割合を上記のように小さくすることがより好ましい。さらに、式(1)における炭素原子は、芳香環を構成する炭素原子ではない。なお、以下適宜、CH基の炭素原子がアリール基、ヘテロアリール基又はカルボニル基に直接結合することを、それぞれ、CH基がアリール基、ヘテロアリール基又はカルボニル基に直接結合するという。
[I. Charge transport material]
The charge transport material of the present invention comprises one or two or more compounds having an oxidation potential of +0.8 V or more, and a group represented by the following formula (1) in the charge transport material of the present invention (hereinafter, The existing ratio of CH group is 0 to 70 ppm. In this specification, “ppm” represents a ratio based on weight. In addition, the compound contained in the charge transport material of the present invention is an organic compound, but when used as a material for an organic EL device, it can be appropriately mixed with any inorganic compound. The carbon atom of the CH group is directly bonded to at least one aryl group, heteroaryl group or carbonyl group, or directly bonded to at least one aryl group or heteroaryl group. In particular, when the carbon atom of the CH group is directly bonded to at least one aryl group or heteroaryl group, the CH group is more likely to cause an increase in driving voltage or a decrease in driving life, so at least one aryl group or heteroaryl group It is more preferable to reduce the abundance ratio of the CH group having a carbon atom directly bonded to as described above. Furthermore, the carbon atom in Formula (1) is not a carbon atom which comprises an aromatic ring. In addition, hereinafter, when the carbon atom of the CH group is directly bonded to the aryl group, heteroaryl group or carbonyl group, the CH group is directly bonded to the aryl group, heteroaryl group or carbonyl group, respectively.
<1.電荷輸送材料に用いることができる化合物>
電荷輸送材料とは、与えられた電荷(即ち、電子や正孔)を移動させることができる材料であり、上記の条件を満たしていれば他に制限はなく、任意の材料を用いることができる。また、電荷輸送材料は、1種の化合物を単独で用いてもよく、2種以上の化合物を任意の組み合わせ及び比率で併用してもよい。
<1. Compound that can be used for charge transport material>
The charge transport material is a material that can move a given charge (that is, electrons and holes), and any material can be used as long as the above conditions are satisfied. . In addition, as the charge transport material, one type of compound may be used alone, or two or more types of compounds may be used in any combination and ratio.
ただし、電荷輸送材料は、通常、以下の機能を有するものが好ましい。
(i)注入機能:電界印加時に陽極又は正孔注入層より正孔を注入することができる機能、及び/又は、陰極又は電子注入層より電子を注入することができる機能。
(ii)輸送機能:注入した電荷を電界の力で移動させる機能。
(iii)発光機能:電子と正孔との再結合の場を提供し、これを発光につなげる機能。
(iv)阻止機能:電荷をバランスよく移動、再結合させるため、移動調整する機能。
なお、正孔の注入されやすさと電子の注入されやすさには違いがあってよく、正孔と電子の移動度で表される輸送性能に大小があってもよいが、どちらか一方の電荷を移動することが好ましい。
However, the charge transporting material usually preferably has the following functions.
(I) Injection function: a function capable of injecting holes from the anode or the hole injection layer when an electric field is applied, and / or a function capable of injecting electrons from the cathode or the electron injection layer.
(Ii) Transport function: A function to move the injected charge by the force of an electric field.
(Iii) Light-emitting function: A function that provides a field for recombination of electrons and holes and connects this to light emission.
(Iv) Blocking function: A function to adjust the movement in order to move and recombine charges in a balanced manner.
Note that there is a difference between the ease of hole injection and the ease of electron injection, and the transport performance represented by the mobility of holes and electrons may be large or small. It is preferable to move.
上記の観点から、電荷輸送材料として用いる化合物は、特に、下記式(3)で表される有機化合物が好ましい。
以下、上記式(3)で表わされる化合物について詳細に説明する。
式(3)において、nは、通常1以上、好ましくは2以上、また、通常10以下、好ましくは6以下の整数を表わす。この範囲を超えると各種精製によってCH基の存在割合を十分に低下させることが困難になるために好ましくなく、この範囲を下回ると電荷注入・輸送性が著しく低下することがあるために好ましくない。
Hereinafter, the compound represented by the above formula (3) will be described in detail.
In the formula (3), n represents an integer of usually 1 or more, preferably 2 or more, and usually 10 or less, preferably 6 or less. Exceeding this range is not preferable because it is difficult to sufficiently reduce the proportion of CH groups present by various purifications. Beyond this range, charge injection / transport properties may be significantly reduced, which is not preferable.
また、式(3)において、nが1の場合、Zは、水素原子又は任意の置換基である。ここで、Zが置換基である場合の具体例は、アミノ基類、アルコキシカルボニルアミノ基、アリールオキシカルボニルアミノ基、ヘテロ環オキシカルボニルアミノ基、スルホニルアミノ基、アルコキシ基、アリールオキシ基、ヘテロ環オキシ基、アシル基、アルコキシカルボニル基、アリールオキシカルボニル基、ヘテロ環オキシカルボニル基、アシルオキシ基、スルファモイル基類、カルバモイル基類、アルキルチオ基、アリールチオ基、ヘテロ環チオ基、スルホニル基類、スルフェニル基類、ウレイド基、リン酸アミド基、ヒドロキシル基、メルカプト基、シアノ基、スルホ基、カルボキシル基、ニトロ基、ヒドロキサム酸基、スルフィノ基、ヒドラジノ基、シリル基類、ボリル基類、ホスフィノ基、アリール基、ヘテロアリール基、下記式(4)で表わされる基、下記式(5)で表わされる基などが挙げられる。 In formula (3), when n is 1, Z is a hydrogen atom or an arbitrary substituent. Here, specific examples when Z is a substituent include amino groups, alkoxycarbonylamino groups, aryloxycarbonylamino groups, heterocyclic oxycarbonylamino groups, sulfonylamino groups, alkoxy groups, aryloxy groups, and heterocyclic rings. Oxy group, acyl group, alkoxycarbonyl group, aryloxycarbonyl group, heterocyclic oxycarbonyl group, acyloxy group, sulfamoyl group, carbamoyl group, alkylthio group, arylthio group, heterocyclic thio group, sulfonyl group, sulfenyl group Ureido group, phosphoric acid amide group, hydroxyl group, mercapto group, cyano group, sulfo group, carboxyl group, nitro group, hydroxamic acid group, sulfino group, hydrazino group, silyl group, boryl group, phosphino group, aryl Group, heteroaryl group, below Group represented by formula (4), and a group represented by the following formula (5).
ただし、式(4)において、Raは任意の置換基を表わす。また、Raの炭素数は、通常1以上、また、通常10以下、好ましくは6以下である。さらに、Raの具体例を挙げると、アルキル基、アラルキル基、アリール基などが挙げられる。
また、式(4)及び式(5)において、Rb,Rc,Rdはそれぞれ独立に、水素原子又は任意の置換基を表わす。また、Rb,Rc,Rdが任意の置換基である場合には、その炭素数及び具体例としては、それぞれ独立に、Raと同様の炭素数及び具体例が挙げられる。
However, in Formula (4), R a represents an arbitrary substituent. The carbon number of Ra is usually 1 or more, and usually 10 or less, preferably 6 or less. Furthermore, specific examples of Ra include an alkyl group, an aralkyl group, and an aryl group.
In the formulas (4) and (5), R b , R c and R d each independently represent a hydrogen atom or an arbitrary substituent. In addition, when R b , R c , and R d are arbitrary substituents, the carbon number and specific examples thereof include the same carbon numbers and specific examples as those of R a .
Zがアミノ基類である場合、アミノ基類にはアミノ基にアルキル基やアリール基等の炭化水素基が置換したものも含む。その炭素数は、通常0以上、また、通常36以下、好ましくは20以下、より好ましくは12以下である。その具体例としては、アミノ基、メチルアミノ基、ジメチルアミノ基、エチルアミノ基、ジエチルアミノ基、フェニルアミノ基、ジフェニルアミノ基、ジベンジルアミノ基、チエニルアミノ基、ジチエニルアミノ基、ピリジルアミノ基、ジピリジルアミノ基等が挙げられる。 When Z is an amino group, the amino group includes an amino group substituted with a hydrocarbon group such as an alkyl group or an aryl group. The carbon number is usually 0 or more, and usually 36 or less, preferably 20 or less, more preferably 12 or less. Specific examples thereof include amino group, methylamino group, dimethylamino group, ethylamino group, diethylamino group, phenylamino group, diphenylamino group, dibenzylamino group, thienylamino group, dithienylamino group, pyridylamino group, A pyridylamino group etc. are mentioned.
Zがアルコキシカルボニルアミノ基である場合、その炭素数は、通常2以上、また、通常20以下、好ましくは16以下、より好ましくは12以下である。その具体例としては、メトキシカルボニルアミノ基等が挙げられる。 When Z is an alkoxycarbonylamino group, the carbon number is usually 2 or more, and usually 20 or less, preferably 16 or less, more preferably 12 or less. Specific examples thereof include a methoxycarbonylamino group.
Zがアリールオキシカルボニルアミノ基である場合、その炭素数は、通常7以上、また、通常20以下、好ましくは16以下、より好ましくは12以下である。その具体例としては、フェノキシカルボニル基等が挙げられる。 When Z is an aryloxycarbonylamino group, the carbon number is usually 7 or more, and usually 20 or less, preferably 16 or less, more preferably 12 or less. Specific examples thereof include a phenoxycarbonyl group.
Zがヘテロ環オキシカルボニルアミノ基である場合、その炭素数は、通常2以上、好ましくは5以上、また、通常21以下、好ましくは15以下、より好ましくは11以下である。その具体例としては、チエニルオキシカルボニルアミノ基等が挙げられる。 When Z is a heterocyclic oxycarbonylamino group, the carbon number thereof is usually 2 or more, preferably 5 or more, and usually 21 or less, preferably 15 or less, more preferably 11 or less. Specific examples thereof include a thienyloxycarbonylamino group.
Zがスルホニルアミノ基である場合、その炭素数は、通常1以上、また、通常20以下、好ましくは16以下、より好ましくは12以下である。その具体例としては、メタンスルホニルアミノ基、ベンゼンスルホニルアミノ基、チオフェンスルホニルアミノ基等が挙げられる。 When Z is a sulfonylamino group, the carbon number is usually 1 or more, and usually 20 or less, preferably 16 or less, more preferably 12 or less. Specific examples thereof include a methanesulfonylamino group, a benzenesulfonylamino group, and a thiophenesulfonylamino group.
Zがアルコキシ基である場合、その炭素数は、通常1以上、また、通常20以下、好ましくは12以下、より好ましくは8以下である。その具体例としては、メトキシ基、エトキシ基、イソプロポキシ基、n−ブトキシ基、t−ブトキシ基等が挙げられる。 When Z is an alkoxy group, the carbon number is usually 1 or more, and usually 20 or less, preferably 12 or less, more preferably 8 or less. Specific examples thereof include methoxy group, ethoxy group, isopropoxy group, n-butoxy group, t-butoxy group and the like.
Zがアリールオキシ基である場合、その炭素数は、通常6以上、また、通常10以下、好ましくは8以下、より好ましくは炭素数6である。その具体例としては、フェノキシ基等が挙げられる。 When Z is an aryloxy group, the carbon number is usually 6 or more, and usually 10 or less, preferably 8 or less, more preferably 6 carbon atoms. Specific examples thereof include a phenoxy group.
Zがヘテロ環オキシ基である場合、その炭素数は、通常1以上、好ましくは2以上、より好ましくは4以上、また、通常10以下、好ましくは8以下、より好ましくは5以下である。その具体例としては、チエニルオキシ基、ピリジルオキシ基等が挙げられる。 When Z is a heterocyclic oxy group, the number of carbon atoms is usually 1 or more, preferably 2 or more, more preferably 4 or more, and usually 10 or less, preferably 8 or less, more preferably 5 or less. Specific examples thereof include a thienyloxy group and a pyridyloxy group.
Zがアシル基である場合、その炭素数は、通常1以上、また、通常20以下、好ましくは16以下、より好ましくは12以下である。その具体例としては、アセチル基、ベンゾイル基、ホルミル基、ピバロイル基、テノイル基、ニコチノイル基等が挙げられる。 When Z is an acyl group, the carbon number is usually 1 or more, and usually 20 or less, preferably 16 or less, more preferably 12 or less. Specific examples thereof include acetyl group, benzoyl group, formyl group, pivaloyl group, thenoyl group, nicotinoyl group and the like.
Zがアルコキシカルボニル基である場合、その炭素数は、通常2以上、また、通常20以下、好ましくは16以下、より好ましくは12以下である。その具体例としては、メトキシカルボニル基、エトキシカルボニル基等が挙げられる。 When Z is an alkoxycarbonyl group, the carbon number is usually 2 or more, and usually 20 or less, preferably 16 or less, more preferably 12 or less. Specific examples thereof include a methoxycarbonyl group and an ethoxycarbonyl group.
Zがアリールオキシカルボニル基である場合、その炭素数は、通常7以上、また、通常20以下、好ましくは16以下、より好ましくは7である。その具体例としては、フェノキシカルボニル基などが挙げられる。 When Z is an aryloxycarbonyl group, the carbon number is usually 7 or more, and usually 20 or less, preferably 16 or less, more preferably 7. Specific examples thereof include a phenoxycarbonyl group.
Zがヘテロ環オキシカルボニル基である場合、その炭素数は、通常2以上、好ましくは5以上、また、通常20以下、好ましくは12以下、より好ましくは6以下である。その具体例としては、チエニルオキシカルボニル基、ピリジルオキシカルボニル基等が挙げられる。 When Z is a heterocyclic oxycarbonyl group, its carbon number is usually 2 or more, preferably 5 or more, and usually 20 or less, preferably 12 or less, more preferably 6 or less. Specific examples thereof include a thienyloxycarbonyl group and a pyridyloxycarbonyl group.
Zがアシルオキシ基である場合、その炭素数は、通常2以上、また、通常20以下、好ましくは16以下、より好ましくは12以下である。その具体例は、アセトキシ基、エチルカルボニルオキシ基、ベンゾイルオキシ基、ピバロイルオキシ基、テノイルオキシ基、ニコチノイルオキシ基等が挙げられる。 When Z is an acyloxy group, the carbon number is usually 2 or more, and usually 20 or less, preferably 16 or less, more preferably 12 or less. Specific examples thereof include an acetoxy group, ethylcarbonyloxy group, benzoyloxy group, pivaloyloxy group, thenoyloxy group, nicotinoyloxy group and the like.
Zがスルファモイル基類である場合、スルファモイル基類にはスルファモイル基にアルキル基やアリール基等の炭化水素基が置換したものも含む。その炭素数は、通常0以上、また、通常20以下、好ましくは12以下である。その具体例は、スルファモイル基、メチルスルファモイル基、ジメチルスルファモイル基、フェニルスルファモイル基、チエニルスルファモイル基等が挙げられる。 When Z is a sulfamoyl group, the sulfamoyl group includes a sulfamoyl group substituted with a hydrocarbon group such as an alkyl group or an aryl group. The carbon number is usually 0 or more, and usually 20 or less, preferably 12 or less. Specific examples thereof include a sulfamoyl group, a methylsulfamoyl group, a dimethylsulfamoyl group, a phenylsulfamoyl group, and a thienylsulfamoyl group.
Zがカルバモイル基類である場合、カルバモイル基類にはカルバモイル基にアルキル基やアリール基等の炭化水素基が置換したものも含む。その炭素数は、通常1以上、また、通常20以下、好ましくは16以下、より好ましくは12以下である。その具体例は、カルバモイル基、メチルカルバモイル基、ジエチルカルバモイル基、フェニルカルバモイル基等が挙げられる。 When Z is a carbamoyl group, the carbamoyl group includes a carbamoyl group substituted with a hydrocarbon group such as an alkyl group or an aryl group. The carbon number is usually 1 or more, and usually 20 or less, preferably 16 or less, more preferably 12 or less. Specific examples thereof include a carbamoyl group, a methylcarbamoyl group, a diethylcarbamoyl group, and a phenylcarbamoyl group.
Zがアルキルチオ基である場合、その炭素数は、通常1以上、また、通常20以下、好ましくは16以下、より好ましくは12以下である。その具体例は、メチルチオ基、エチルチオ基、n−ブチルチオ基等が挙げられる。 When Z is an alkylthio group, the carbon number is usually 1 or more, and usually 20 or less, preferably 16 or less, more preferably 12 or less. Specific examples thereof include a methylthio group, an ethylthio group, and an n-butylthio group.
Zがアリールチオ基である場合、その炭素数は、通常6以上、また、通常26以下、好ましくは20以下、より好ましくは12以下である。その具体例は、フェニルチオ等が挙げられる。 When Z is an arylthio group, the carbon number is usually 6 or more, and usually 26 or less, preferably 20 or less, more preferably 12 or less. Specific examples thereof include phenylthio.
Zがヘテロ環チオ基である場合、その炭素数は、通常1以上、好ましくは2以上、より好ましくは5以上、また、通常25以下、好ましくは19以下、より好ましくは11以下である。その具体例は、チエニルチオ基、ピリジルチオ基等が挙げられる。 When Z is a heterocyclic thio group, the carbon number thereof is usually 1 or more, preferably 2 or more, more preferably 5 or more, and usually 25 or less, preferably 19 or less, more preferably 11 or less. Specific examples thereof include a thienylthio group and a pyridylthio group.
Zがスルホニル基類である場合、スルホニル基類にはスルホニル基にアルキル基やアリール基等の炭化水素基が置換したものも含む。その炭素数は、通常1以上、また、通常20以下、好ましくは16以下、より好ましくは12以下である。その具体例としては、トシル基、メシル基などが挙げられる。 When Z is a sulfonyl group, the sulfonyl group includes a sulfonyl group substituted with a hydrocarbon group such as an alkyl group or an aryl group. The carbon number is usually 1 or more, and usually 20 or less, preferably 16 or less, more preferably 12 or less. Specific examples thereof include a tosyl group and a mesyl group.
Zがスルフェニル基類である場合、スルフェニル基類にはスルフェニル基にアルキル基やアリール基等の炭化水素基が置換したものも含む。その炭素数は、通常1以上、また、通常20以下、好ましくは16以下、より好ましくは12以下である。その具体例としては、メチルスルフィニル基、フェニルスルフィニル基等が挙げられる。 When Z is a sulfenyl group, the sulfenyl group includes a sulfenyl group substituted with a hydrocarbon group such as an alkyl group or an aryl group. The carbon number is usually 1 or more, and usually 20 or less, preferably 16 or less, more preferably 12 or less. Specific examples thereof include a methylsulfinyl group and a phenylsulfinyl group.
Zがウレイド基類である場合、ウレイド基類にはウレイド基にアルキル基やアリール基等の炭化水素基が置換したものも含む。その炭素数は、通常1以上、また、通常20以下、好ましくは16以下、より好ましくは12以下である。その具体例としては、ウレイド基、メチルウレイド基、フェニルウレイド基等が挙げられる。 When Z is a ureido group, the ureido group includes a ureido group substituted with a hydrocarbon group such as an alkyl group or an aryl group. The carbon number is usually 1 or more, and usually 20 or less, preferably 16 or less, more preferably 12 or less. Specific examples thereof include a ureido group, a methylureido group, and a phenylureido group.
Zがリン酸アミド基類である場合、リン酸アミド基類にはリン酸アミド基にアルキル基やアリール基等の炭化水素基が置換したものも含む。その炭素数は、通常1以上、また、通常20以下、好ましくは16以下、より好ましくは12以下である。その具体例としては、ジエチルリン酸アミド基、フェニルリン酸アミド基等が挙げられる。 When Z is a phosphoric acid amide group, the phosphoric acid amide group includes those in which a hydrocarbon group such as an alkyl group or an aryl group is substituted on the phosphoric acid amide group. The carbon number is usually 1 or more, and usually 20 or less, preferably 16 or less, more preferably 12 or less. Specific examples thereof include a diethylphosphoric acid amide group and a phenylphosphoric acid amide group.
Zがシリル基類である場合、シリル基類にはシリル基にアルキル基やアリール基等の炭化水素基が置換したものも含む。その炭素数は、通常1以上、また、通常10以下、好ましくは6以下である。その具体例としては、トリメチルシリル基、トリフェニルシリル基等が挙げられる。 When Z is a silyl group, the silyl group includes a silyl group substituted with a hydrocarbon group such as an alkyl group or an aryl group. The carbon number is usually 1 or more, and usually 10 or less, preferably 6 or less. Specific examples thereof include a trimethylsilyl group and a triphenylsilyl group.
Zがボリル基類である場合、ボリル基類にはボリル基にアルキル基やアリール基等の炭化水素基が置換したものも含む。その炭素数は、通常1以上、また、通常10以下、好ましくは6以下である。その具体例としては、ジメシチルボリル基等が挙げられる。 When Z is a boryl group, the boryl group includes a boryl group substituted with a hydrocarbon group such as an alkyl group or an aryl group. The carbon number is usually 1 or more, and usually 10 or less, preferably 6 or less. Specific examples thereof include a dimesitylboryl group.
Zがホスフィノ基類である場合、ホスフィノ基類にはホスフィノ基にアルキル基やアリール基等の炭化水素基が置換したものも含む。その炭素数は、通常1以上、また、通常10以下、好ましくは6以下である。その具体例としては、ジフェニルホスフィノ基等が挙げられる。 When Z is a phosphino group, the phosphino group includes a phosphino group substituted with a hydrocarbon group such as an alkyl group or an aryl group. The carbon number is usually 1 or more, and usually 10 or less, preferably 6 or less. Specific examples thereof include a diphenylphosphino group.
Zがアリール基である場合、その炭素数は、通常6以上、また、通常20以下、好ましくは14以下である。その具体例としては、ベンゼン環、ナフタレン環、アントラセン環、フェナントレン環、ペリレン環、テトラセン環、ピレン環、ベンズピレン環、クリセン環、トリフェニレン環、フルオランテン環等由来の6員環の単環或いは2〜5縮合環由来の基などが挙げられる。 When Z is an aryl group, the carbon number is usually 6 or more, and usually 20 or less, preferably 14 or less. Specific examples thereof include a benzene ring, naphthalene ring, anthracene ring, phenanthrene ring, perylene ring, tetracene ring, pyrene ring, benzpyrene ring, chrysene ring, triphenylene ring, fluoranthene ring, etc. And a group derived from a 5-fused ring.
Zがヘテロアリール基である場合、そのヘテロ原子としては、窒素原子、酸素原子、硫黄原子等が挙げられる。また、このとき、Zの炭素数は、通常1以上、好ましくは3以上、また、通常19以下、好ましくは13以下である。その具体例を挙げると、フラン環、ベンゾフラン環、チオフェン環、ベンゾチオフェン環、ピロール環、ピラゾール環、オキサゾール環、イミダゾール環、オキサジアゾール環、インドール環、カルバゾール環、ピロロイミダゾール環、ピロロピラゾール環、ピロロピロール環、チエノピロール環、チエノチオフェン環、フロピロール環、フロフラン環、チエノフラン環、ベンゾイソオキサゾール環、ベンゾイソチアゾール環、ベンゾイミダゾール環、ピリジン環、ピラジン環、ピリダジン環、ピリミジン環、トリアジン環、キノリン環、イソキノリン環、シノリン環、キノキサリン環、ベンゾイミダゾール環、ペリミジン環、キナゾリン環、キナゾリノン環、アズレン環等の5員環又は6員環の単環或いは2〜4縮合環由来の基が挙げられる。 When Z is a heteroaryl group, examples of the hetero atom include a nitrogen atom, an oxygen atom, and a sulfur atom. At this time, the carbon number of Z is usually 1 or more, preferably 3 or more, and usually 19 or less, preferably 13 or less. Specific examples are furan ring, benzofuran ring, thiophene ring, benzothiophene ring, pyrrole ring, pyrazole ring, oxazole ring, imidazole ring, oxadiazole ring, indole ring, carbazole ring, pyrroloimidazole ring, pyrrolopyrazole ring. , Pyrrolopyrrole ring, thienopyrrole ring, thienothiophene ring, furopyrrole ring, furofuran ring, thienofuran ring, benzisoxazole ring, benzisothiazole ring, benzimidazole ring, pyridine ring, pyrazine ring, pyridazine ring, pyrimidine ring, triazine ring, Examples include groups derived from 5-membered or 6-membered monocycles such as quinoline ring, isoquinoline ring, sinoline ring, quinoxaline ring, benzimidazole ring, perimidine ring, quinazoline ring, quinazolinone ring, and azulene ring, or from 2 to 4 condensed rings. Is .
一方、nが2以上の場合、Zは直接結合又はn価の連結基を表わす。
Zがn価の連結基である場合、その具体例としては、下記式で表わされる基が挙げられる。
また、Zがアルキニル基である場合、その炭素数は、通常2以上、また、通常8以下、好ましくは4以下である。その具体例としてはエチニル基、プロパルギル基等が挙げられる。
On the other hand, when n is 2 or more, Z represents a direct bond or an n-valent linking group.
When Z is an n-valent linking group, specific examples thereof include groups represented by the following formulae.
When Z is an alkynyl group, the carbon number is usually 2 or more, and usually 8 or less, preferably 4 or less. Specific examples thereof include ethynyl group and propargyl group.
これらの中でも、Zは、電気的酸化還元耐久性を向上させる観点、及び、耐熱性を向上させる観点から、アリール基またはヘテロアリール基であることが好ましい。
なお、Zは、さらに置換基を有していても良く、他の基と縮合していてもよい。また、Zが有する置換基が2個以上ある場合には、それらは同一でもよく、異なっていてもよい。さらに、可能な場合には連結して環を形成してもよい。
Among these, Z is preferably an aryl group or a heteroaryl group from the viewpoint of improving electrical redox durability and from the viewpoint of improving heat resistance.
Z may further have a substituent and may be condensed with other groups. Moreover, when there are two or more substituents of Z, they may be the same or different. Further, if possible, they may be linked to form a ring.
Zが有する置換基は任意であるが、例えば、アリール基、アシル基、アルコキシ基、アリールオキシ基、アルキルチオ基、アリールチオ基、アルコキシカルボニル基、アリールオキシカルボニル基、アリールアミノ基、アルキルアミノ基、ヘテロアリール基などが挙げられる。この中でも、アリール基、ヘテロアリール基が好ましく、アリール基がより好ましい。なお、ここで例示した置換基の具体例としては、Zが置換基である場合について具体例として例示したものと同様のものが挙げられる。 Although the substituent which Z has is arbitrary, for example, aryl group, acyl group, alkoxy group, aryloxy group, alkylthio group, arylthio group, alkoxycarbonyl group, aryloxycarbonyl group, arylamino group, alkylamino group, hetero An aryl group etc. are mentioned. Among these, an aryl group and a heteroaryl group are preferable, and an aryl group is more preferable. In addition, specific examples of the substituents exemplified here include those similar to those exemplified as specific examples in the case where Z is a substituent.
また、Zの分子量は任意であるが、Zが置換基又は連結基である場合、通常1000以下、好ましくは500以下である。Zの分子量をこの範囲とすることにより、蒸着法を用いた成膜の際、電荷輸送材料の気化温度が極度に高温となることを防止できる。また、湿式法を用いた成膜の際、電荷輸送材料の溶媒に対する溶解性を損なうことを防止できる。これにより、本発明の電荷輸送材料を用いて良好な特性の有機EL素子を得ることができる。 Moreover, although the molecular weight of Z is arbitrary, when Z is a substituent or a coupling group, it is usually 1000 or less, preferably 500 or less. By setting the molecular weight of Z within this range, it is possible to prevent the vaporization temperature of the charge transport material from becoming extremely high during film formation using the vapor deposition method. In addition, it is possible to prevent the charge transport material from being damaged in a solvent during film formation using a wet method. Thereby, the organic EL element of a favorable characteristic can be obtained using the charge transport material of this invention.
式(3)において、Aは、任意のアリール基又はヘテロアリール基を表す。
Aがアリール基である場合、その炭素数は、通常6以上、また、通常30以下、好ましくは20以下である。その具体例としては、ベンゼン環、ナフタレン環、アントラセン環、フェナントレン環、ペリレン環、テトラセン環、ピレン環、ベンズピレン環、クリセン環、トリフェニレン環、フルオランテン環等の6員環の単環或いは2〜5縮合環由来の基などが挙げられる。
In formula (3), A represents an arbitrary aryl group or heteroaryl group.
When A is an aryl group, the carbon number is usually 6 or more, and usually 30 or less, preferably 20 or less. Specific examples thereof include a benzene ring, naphthalene ring, anthracene ring, phenanthrene ring, perylene ring, tetracene ring, pyrene ring, benzpyrene ring, chrysene ring, triphenylene ring, fluoranthene ring and the like, or 2 to 5 Examples include a group derived from a condensed ring.
また、Aがヘテロアリール基である場合、その炭素数は、通常1以上、好ましくは3以上、また、通常29以下、好ましくは19以下である。その具体例としては、フラン環、ベンゾフラン環、チオフェン環、ベンゾチオフェン環、ピロール環、ピラゾール環、オキサゾール環、イミダゾール環、オキサジアゾール環、インドール環、カルバゾール環、ピロロイミダゾール環、ピロロピラゾール環、ピロロピロール環、チエノピロール環、チエノチオフェン環、フロピロール環、フロフラン環、チエノフラン環、ベンゾイソオキサゾール環、ベンゾイソチアゾール環、ベンゾイミダゾール環、ピリジン環、ピラジン環、ピリダジン環、ピリミジン環、トリアジン環、キノリン環、イソキノリン環、シノリン環、キノキサリン環、ベンゾイミダゾール環、ペリミジン環、キナゾリン環、キナゾリノン環、アズレン環、テトラゾール環、イミダゾピリジン環等の5員環又は6員環の単環或いは2〜4縮合環由来の基などが挙げられる。 When A is a heteroaryl group, the carbon number is usually 1 or more, preferably 3 or more, and usually 29 or less, preferably 19 or less. Specific examples thereof include furan ring, benzofuran ring, thiophene ring, benzothiophene ring, pyrrole ring, pyrazole ring, oxazole ring, imidazole ring, oxadiazole ring, indole ring, carbazole ring, pyrroloimidazole ring, pyrrolopyrazole ring, Pyrrolopyrrole ring, thienopyrrole ring, thienothiophene ring, furopyrrole ring, furofuran ring, thienofuran ring, benzisoxazole ring, benzisothiazole ring, benzimidazole ring, pyridine ring, pyrazine ring, pyridazine ring, pyrimidine ring, triazine ring, quinoline Ring, isoquinoline ring, sinoline ring, quinoxaline ring, benzimidazole ring, perimidine ring, quinazoline ring, quinazolinone ring, azulene ring, tetrazole ring, imidazopyridine ring, etc. It is like groups derived from 2-4 fused rings.
例示したものの中でも、Aとしては、電気的酸化還元耐久性の点、及び、広いHOMO−LUMOのバンドギャップの点から、ベンゼン環、ナフタレン環、ピリジン環、ピリミジン環、ピラジン環、トリアジン環、キノリン環、イソキノリン環、チアゾール環、オキサゾール環、イミダゾール環、インドール環、ベンゾイミダゾール環、イミダゾピリジン環、カルバゾール環由来の基が好ましい。 Among those exemplified, A represents benzene ring, naphthalene ring, pyridine ring, pyrimidine ring, pyrazine ring, triazine ring, quinoline from the viewpoint of electrical redox durability and wide band gap of HOMO-LUMO. A group derived from a ring, isoquinoline ring, thiazole ring, oxazole ring, imidazole ring, indole ring, benzimidazole ring, imidazopyridine ring or carbazole ring is preferred.
この中でも、ベンゼン環、ナフタレン環、ピリジン環、トリアジン環、オキサゾール環、チアゾール環、イミダゾール環、キノリン環、イソキノリン環、ベンゾイミダゾール環、イミダゾピリジン環、カルバゾール環由来の基がより好ましい。また、ベンゼン環、ピリジン環、キノリン環、イソキノリン環、ベンゾイミダゾール環、イミダゾピリジン環、カルバゾール環由来の基がより好ましい。 Among these, groups derived from a benzene ring, naphthalene ring, pyridine ring, triazine ring, oxazole ring, thiazole ring, imidazole ring, quinoline ring, isoquinoline ring, benzimidazole ring, imidazopyridine ring, and carbazole ring are more preferable. Further, a group derived from a benzene ring, a pyridine ring, a quinoline ring, an isoquinoline ring, a benzimidazole ring, an imidazopyridine ring, or a carbazole ring is more preferable.
さらに、Aは、ピリジン環又はカルバゾール環由来の基が、特に好ましい。
ピリジン環由来の基の中でも、ピリジン環の2,4,6−位に置換基を有するものは、電気的酸化還元安定性に優れるため、好ましい。また、このピリジン環に結合する置換基は任意であるが、アリール基又はヘテロアリール基であることが好ましい。
また、カルバゾール環由来の基の中でも、アルキル基、アミノ基、アルコキシ基等の電子供与性基を置換基として有さないものが、電気的還元耐久性を低下させないため、好ましい。
Furthermore, A is particularly preferably a group derived from a pyridine ring or a carbazole ring.
Among groups derived from a pyridine ring, those having a substituent at the 2,4,6-position of the pyridine ring are preferable because of excellent electrical redox stability. The substituent bonded to the pyridine ring is arbitrary, but is preferably an aryl group or a heteroaryl group.
Among groups derived from a carbazole ring, those having no electron-donating group such as an alkyl group, amino group, and alkoxy group as a substituent are preferable because they do not lower the electrical reduction durability.
さらに、式(3)において、Aは置換基を有していてもよい。Aが有していてもよい置換基は任意であるが、その具体例としては、Zが有し得る置換基として前述したものと同様のものが挙げられる。 Furthermore, in Formula (3), A may have a substituent. The substituent that A may have is arbitrary, and specific examples thereof include those similar to those described above as the substituent that Z may have.
また、Aの分子量は、その置換基も含めて、通常1000以下、好ましくは500以下である。Aの分子量をこの範囲とすることにより、蒸着法を用いた成膜の際、電荷輸送材料の気化温度が極度に高温となることを防止できる。また、湿式法を用いた成膜の際、電荷輸送材料の溶媒に対する溶解性を損なうことを防止できる。これにより、本発明の電荷輸送材料を用いて良好な特性の有機EL素子を得ることができる。 Moreover, the molecular weight of A is 1000 or less normally including the substituent, Preferably it is 500 or less. By setting the molecular weight of A within this range, the vaporization temperature of the charge transport material can be prevented from becoming extremely high during film formation using the vapor deposition method. In addition, it is possible to prevent the charge transport material from being damaged in a solvent during film formation using a wet method. Thereby, the organic EL element of a favorable characteristic can be obtained using the charge transport material of this invention.
以下、A,Zについて、それぞれ具体例を例示する。
まず、A、及び、n=1の場合のZの具体例としては、以下の基R−1〜R−88が挙げられる。ただし、以下の具体例において、L1及びL2はそれぞれ独立に、水素原子又は任意の置換基を表わす。また、ここで例示した基は、L1及びL2以外にも置換基を有していてもよい。なお、Phはフェニル基を表わす。
Hereinafter, specific examples of A and Z are illustrated.
First, specific examples of Z in the case of A and n = 1 include the following groups R-1 to R-88. However, in the following specific examples, L 1 and L 2 each independently represent a hydrogen atom or an arbitrary substituent. Moreover, the group illustrated here may have a substituent other than L 1 and L 2 . Ph represents a phenyl group.
また、nが2以上の場合のZの具体例としては、以下の結合及び基が挙げられる。なお、Z−1で表わしたものは直接結合を表わし、Z−2〜Z−184で表わしたものは基を表わす。
また、式(3)で表わされる化合物の具体例としては、以下のようなものが挙げられる。
カルバゾール系化合物(トリアリールアミン系化合物を含む)としては、特開昭63−235946号公報、特開平2−285357号公報、特開平2−261889号公報、特開平3−230584号公報、特開平3−232856号公報、特開平5−263073号公報、特開平6−312979号公報、特開平7−053950号公報、特開平8−003547号公報、特開平9−157643号公報、特開平9−268283号公報、特開平9−165573号公報、特開平9−249876号公報、特開平9−310066号公報、特開平10−041069号公報、特開平10−168447号公報、欧州特許第847228号明細書、特開平10−208880号公報、特開平10−226785号公報、特開平10−312073号公報、特開平10−316658号公報、特開平10−330361号公報、特開平11−144866号公報、特開平11−144867号公報、特開平11−144873号公報、特開平11−149987号公報、特開平11−167990号公報、特開平11−233260号公報、特開平11−241062号公報、WO−00/70655号公報、米国特許第6562982号明細書、特開2003−040844号公報、特開2001−313179号公報、特開2001−257076号公報、特願2003−202925号明細書、特願2003−204940号明細書、特願2003−299512号明細書等に電荷輸送材料として記載の化合物などが挙げられる。
Specific examples of the compound represented by formula (3) include the following.
Examples of carbazole compounds (including triarylamine compounds) include JP-A-63-235946, JP-A-2-285357, JP-A-2-261889, JP-A-3-230584, and JP-A-3230584. JP-A-3-232856, JP-A-5-263073, JP-A-6-312979, JP-A-7-053950, JP-A-8-003547, JP-A-9-157743, JP-A-9- No. 268283, JP-A-9-165573, JP-A-9-249876, JP-A-9-310066, JP-A-10-041069, JP-A-10-168447, European Patent No. 847228 , JP-A-10-208880, JP-A-10-226785, JP-A-10-312 73, JP-A-10-316658, JP-A-10-330361, JP-A-11-144866, JP-A-11-144867, JP-A-11-144873, JP-A-11-149987 Gazette, JP-A-11-167990, JP-A-11-233260, JP-A-11-241662, WO-00 / 70655, U.S. Pat. No. 6,562,982, JP-A-2003-040844, JP-A-2001-313179, JP-A-2001-257076, Japanese Patent Application No. 2003-202925, Japanese Patent Application No. 2003-204940, Japanese Patent Application No. 2003-299512, etc. Compound etc. are mentioned.
また、フェニルアントラセン誘導体としては、特開2000−344691号公報等に電荷輸送材料として記載の化合物などが挙げられる。
さらに、縮環アリーレンのスターバースト型化合物としては、特開2001−192651号公報、特開2002−324677号公報等に電荷輸送材料として記載の化合物などが挙げられる。
Examples of the phenylanthracene derivative include compounds described as charge transport materials in JP-A No. 2000-344691.
Furthermore, examples of the starburst type compound of condensed ring arylene include compounds described as charge transport materials in JP-A No. 2001-192651, JP-A No. 2002-324677, and the like.
また、縮環型イミダゾール系化合物としては、「Appl. Phys. Lett., 78巻, 1622項、2001」、特開2001−335776号公報、特開2002−338579号公報、特開2002−319491号公報、特開2002−367785号公報、特開2002−367786号公報等に電荷輸送材料として記載の化合物などが挙げられる。 Examples of the condensed ring imidazole compound include “Appl. Phys. Lett., 78, 1622, 2001”, JP-A No. 2001-335776, JP-A No. 2002-338579, and JP-A No. 2002-319491. JP-A 2002-367785, JP-A 2002-367786, and the like include compounds described as charge transport materials.
さらに、アゼピン系化合物としては、特開2002−235075号公報等に電荷輸送材料として記載の化合物などが挙げられる。
また、縮環型トリアゾール系化合物としては、特開2002−356489号公報等に電荷輸送材料として記載の化合物などが挙げられる。
さらに、プロペラ型アリーレン系化合物としては、特開2003−027048号公報等に電荷輸送材料として記載の化合物などが挙げられる。
Furthermore, examples of the azepine-based compound include compounds described as charge transport materials in JP-A No. 2002-2335075 and the like.
In addition, examples of the condensed triazole-based compound include compounds described as charge transporting materials in JP-A No. 2002-356489 and the like.
Further, examples of the propeller-type arylene compound include compounds described in JP-A-2003-027048 as charge transport materials.
また、モノトリアリールアミン型化合物としては、特開2002−175883号公報、特開2002−249765号公報、特開2002−324676号公報等に電荷輸送材料として記載の化合物などが挙げられる。
さらに、アリールベンジジン系化合物としては、特開2002−329577号公報等に電荷輸送材料として記載の化合物などが挙げられる。
Examples of the monotriarylamine type compounds include compounds described as charge transport materials in JP-A No. 2002-17583, JP-A No. 2002-249765, JP-A No. 2002-324676, and the like.
Furthermore, examples of the arylbenzidine compounds include compounds described as charge transport materials in JP-A No. 2002-329577 and the like.
また、トリアリール硼素化合物としては、特開2003−031367号公報、特開2003−031368号公報等に電荷輸送材料として記載の化合物などが挙げられる。
さらに、インドール系化合物としては、特開2002−305084号公報、特開2003−008866号公報、特開2002−015871号公報等に電荷輸送材料として記載の化合物などが挙げられる。
Examples of the triaryl boron compound include compounds described as charge transport materials in JP-A Nos. 2003-031367 and 2003-031368.
Further, examples of the indole compounds include compounds described in JP 2002-305084 A, JP 2003-008866 A, JP 2002-015871 A, and the like as charge transport materials.
また、インドリジン系化合物としては、特開2000−311787号公報等に電荷輸送材料として記載の化合物などが挙げられる。
さらに、ピレン系化合物としては、特開2001−118682号公報等に電荷輸送材料として記載の化合物などが挙げられる。
また、ジベンゾオキサゾール(又はジベンゾチアゾール)系化合物としては、特開2002−231453号公報等に電荷輸送材料として記載の化合物などが挙げられる。
Examples of indolizine compounds include compounds described as charge transport materials in JP-A No. 2000-311787.
Furthermore, examples of the pyrene compound include compounds described as charge transport materials in JP-A No. 2001-118682 and the like.
Examples of the dibenzoxazole (or dibenzothiazole) compound include compounds described as charge transport materials in JP-A No. 2002-231453.
さらに、ビピリジル系化合物としては、特開2003−123983号公報等に電荷輸送材料として記載の化合物などが挙げられる。
また、ピリジン系化合物としては、特願2003−347307号明細書、特願2003−374430号明細書等に電荷輸送材料として記載の化合物などが挙げられる。
Further, examples of the bipyridyl compounds include compounds described as charge transport materials in JP-A No. 2003-123983 and the like.
Examples of the pyridine compound include compounds described as charge transport materials in Japanese Patent Application Nos. 2003-347307 and 2003-374430.
これらの中でも、有機EL素子としての優れた発光特性の点から、カルバゾール系化合物(トリアリールアミン系化合物を含む)、縮環アリーレンのスターバースト型化合物、縮環型イミダゾール系化合物、プロペラ型アリーレン系化合物、モノトリアリールアミン型化合物、インドール系化合物、インドリジン系化合物、ビピリジル系化合物、ピリジン系化合物等が好ましい。
更に、有機EL素子としての駆動寿命の点から、カルバゾール系化合物及びピリジン系化合物がより好ましい。
電荷輸送材料として、とりわけ好ましい化合物の具体例を以下に示す。
Of these, carbazole compounds (including triarylamine compounds), condensed arylene starburst compounds, condensed imidazole compounds, propeller arylene compounds from the viewpoint of excellent light emitting characteristics as organic EL devices. Compounds, monotriarylamine type compounds, indole compounds, indolizine compounds, bipyridyl compounds, pyridine compounds and the like are preferable.
Furthermore, a carbazole compound and a pyridine compound are more preferable from the viewpoint of driving life as an organic EL element.
Specific examples of particularly preferable compounds as the charge transport material are shown below.
また、電荷輸送材料として用いる化合物は、そのバンドギャップが、通常3.0V以上、好ましくは3.2V以上、より好ましくは3.5V以上のものが望ましい。燐光発光性色素、とりわけ緑〜青色発光性色素は、バンドギャップが大きく、この燐光発光性色素を用いて有機EL素子を作製する場合には、燐光発光性色素をとりまく電荷輸送材料は、通常、この燐光発光色素のバンドギャップ以上のバンドギャップを有していることが、有機EL素子としての発光効率や寿命の点で好ましいのためである。なお、バンドギャップはサイクリックボルタンメトリーにより測定することができる。 The compound used as the charge transport material preferably has a band gap of usually 3.0 V or higher, preferably 3.2 V or higher, more preferably 3.5 V or higher. Phosphorescent dyes, especially green to blue light-emitting dyes, have a large band gap. When an organic EL device is produced using this phosphorescent dye, the charge transporting material surrounding the phosphorescent dye is usually This is because having a band gap equal to or larger than the band gap of the phosphorescent dye is preferable in terms of luminous efficiency and lifetime as an organic EL element. The band gap can be measured by cyclic voltammetry.
さらに、電荷輸送材料として用いる化合物は、そのガラス転移点が、通常70℃以上、好ましくは100℃以上、より好ましくは130℃以上、さらに好ましくは150℃以上であることが望ましい。ガラス転移点が低すぎると、有機EL素子としての耐熱性が低下する虞があるほか、駆動寿命が短くなる可能性があるためである。 Furthermore, it is desirable that the compound used as the charge transport material has a glass transition point of usually 70 ° C. or higher, preferably 100 ° C. or higher, more preferably 130 ° C. or higher, and further preferably 150 ° C. or higher. This is because if the glass transition point is too low, the heat resistance of the organic EL element may be lowered and the driving life may be shortened.
また、電荷輸送材料として用いる化合物は、その気化温度が、常圧条件下で、通常300℃以上、好ましくは350℃以上、より好ましくは400℃以上、また、通常700℃以下、好ましくは600℃以下、さらに好ましくは550℃以下である。本発明の電荷輸送材料を蒸着法により成膜する場合や昇華法を用いて精製する場合に、高温による劣化を招く虞があるためである。 The compound used as the charge transport material has a vaporization temperature of usually 300 ° C. or higher, preferably 350 ° C. or higher, more preferably 400 ° C. or higher, and usually 700 ° C. or lower, preferably 600 ° C., under normal pressure conditions. Hereinafter, it is more preferably 550 ° C. or lower. This is because the charge transport material of the present invention may be deteriorated due to high temperature when it is formed by vapor deposition or purified by sublimation.
さらに、本発明の電荷輸送材料に用いる化合物の分子量は、通常4000以下、好ましくは3000以下、より好ましくは2000以下、また、通常300以上、好ましくは400以上、より好ましくは500以上である。分子量が大きすぎると昇華性が低下し、例えば蒸着による薄膜形成が困難になる傾向がある。また、その合成の過程において、有機EL素子としての駆動寿命を損ない得る、除去が困難な不純物(即ち、CH基を有する化合物)が生成しがちであるため、後述するように有機EL素子を構成する層に使用する電荷輸送材料として適さなくなる虞がある。一方、分子量が小さすぎると、例えば、昇華温度が低くなりすぎるため蒸着による薄膜形成が困難になったり、融点やガラス転移点が低下して耐熱性が低下したり、あるいは、容易に結晶化が起こって成膜性(アモルファス性)が低下したりする虞がある。 Furthermore, the molecular weight of the compound used for the charge transport material of the present invention is usually 4000 or less, preferably 3000 or less, more preferably 2000 or less, and usually 300 or more, preferably 400 or more, more preferably 500 or more. If the molecular weight is too large, the sublimation property is lowered, and for example, it tends to be difficult to form a thin film by evaporation. In addition, in the process of synthesis, impurities that can impair the driving life of the organic EL element and that are difficult to remove (that is, compounds having a CH group) tend to be generated. There is a possibility that it is not suitable as a charge transporting material used for the layer to be applied. On the other hand, if the molecular weight is too small, for example, the sublimation temperature becomes too low, making it difficult to form a thin film by vapor deposition, the melting point and the glass transition point are lowered, the heat resistance is lowered, or crystallization is easy. It may happen that the film formability (amorphous property) may deteriorate.
<2.酸化電位>
本発明の電荷輸送材料の酸化電位は通常+0.8V以上であり、好ましくは+1.0V以上、より好ましくは+1.2V以上である。従来、前述のように、本発明の電荷輸送材料を有機EL素子に用いた場合に、CH基の酸化によりC−H結合解裂が生じ、それにより、有機EL素子の駆動電圧上昇及び駆動寿命低下が発生するという課題があった。これに対し、本発明の電荷輸送材料を用いれば、この駆動電圧上昇及び駆動寿命低下の発生を抑制することができるが、酸化電位が+0.8V未満であると、分子内の他の部位が主として酸化を受け、CH基が酸化される確率が低下するため、CH基に由来する駆動電圧上昇や駆動寿命低下が発生する確率が著しく低下する。このため、酸化電位が+0.8V以上の電荷輸送材料において本発明を適用することが望まれるのである。
<2. Oxidation potential>
The oxidation potential of the charge transport material of the present invention is usually +0.8 V or higher, preferably +1.0 V or higher, more preferably +1.2 V or higher. Conventionally, as described above, when the charge transport material of the present invention is used in an organic EL device, C—H bond cleavage occurs due to oxidation of the CH group, thereby increasing the driving voltage and driving life of the organic EL device. There was a problem that a decrease occurred. On the other hand, if the charge transport material of the present invention is used, the increase in drive voltage and the decrease in drive life can be suppressed, but if the oxidation potential is less than +0.8 V, other sites in the molecule Since the probability that the CH group is oxidized mainly decreases and the CH group is oxidized, the probability that the drive voltage rise and the drive life decrease derived from the CH group will be remarkably lowered. For this reason, it is desired to apply the present invention to a charge transport material having an oxidation potential of +0.8 V or more.
また、本発明における酸化電位は、以下に述べるような電気化学測定(サイクリックボルタンメトリー)によって測定することができる。なお、測定に用いられる支持電解質、溶媒および電極については、以下に示す例示物に限定されるわけではなく、同程度の測定が可能なものであれば任意のものを用いることができる。 The oxidation potential in the present invention can be measured by electrochemical measurement (cyclic voltammetry) as described below. Note that the supporting electrolyte, the solvent, and the electrode used for the measurement are not limited to the examples shown below, and any one can be used as long as the same level of measurement is possible.
支持電解質として、例えば過塩素酸テトラブチルアンモニウムやヘキサフルオロリン酸テトラブチルアンモニウム等を0.1mol/L程度含有させた有機溶媒に、測定対象材料(本発明の電荷輸送材料)を0.1〜2mM程度溶解させる。こうして得られた溶液を、作用電極として例えばグラッシーカーボン電極を用い、対電極として例えば白金電極を用い、掃引速度100mV/secにて電解酸化(又は還元)する。電解酸化(又は還元)時の電位を、例えばフェロセン等の基準物質の酸化還元電位と比較することにより、測定対象材料の酸化電位を得る。こうして得られた酸化電位を、更に飽和甘コウ電極(SCE)を基準電極として換算した値が、本発明における酸化電位である。
なお、用いられる有機溶媒としてはアセトニトリル、塩化メチレン、およびテトラヒドロフランなど、本発明の電荷輸送材料を良く溶解させ、且つ、それ自身が電解酸化(又は還元)されにくい、したがって、電位窓を広くとることができるものが用いられる。
As a supporting electrolyte, for example, an organic solvent containing about 0.1 mol / L of tetrabutylammonium perchlorate, tetrabutylammonium hexafluorophosphate, and the like, a measurement target material (charge transport material of the present invention) is 0.1 to 0.1 mol / L. Dissolve about 2 mM. The solution thus obtained is electrolytically oxidized (or reduced) at a sweep rate of 100 mV / sec using, for example, a glassy carbon electrode as the working electrode and using, for example, a platinum electrode as the counter electrode. By comparing the potential during electrolytic oxidation (or reduction) with the oxidation-reduction potential of a reference substance such as ferrocene, the oxidation potential of the material to be measured is obtained. A value obtained by further converting the oxidation potential thus obtained using a saturated sweet potato electrode (SCE) as a reference electrode is the oxidation potential in the present invention.
As the organic solvent to be used, the charge transport material of the present invention such as acetonitrile, methylene chloride, and tetrahydrofuran is well dissolved, and itself is not easily oxidized (or reduced). Therefore, a wide potential window is required. What can be used is used.
<3.CH基>
本発明の電荷輸送材料は、CH基の存在割合が、重量比(即ち、「CH重量」/「電荷輸送材料の総重量」)で、通常0〜70ppmの範囲である。即ち、上記存在割合は、通常70ppm以下であり、50ppm以下が好ましく、30ppm以下がより好ましい。とりわけ、本発明の電荷輸送材料を、大きい酸化電位(具体的には、酸化電位が+1.5V以上)を有する正孔阻止材料に用いる場合には、上記存在割合は10ppm以下であるのが特に好ましい。
<3. CH group>
In the charge transporting material of the present invention, the CH group is present in a weight ratio (ie, “CH weight” / “total weight of charge transporting material”) and is usually in the range of 0 to 70 ppm. That is, the abundance ratio is usually 70 ppm or less, preferably 50 ppm or less, and more preferably 30 ppm or less. In particular, when the charge transport material of the present invention is used for a hole blocking material having a large oxidation potential (specifically, an oxidation potential of +1.5 V or more), the abundance ratio is particularly 10 ppm or less. preferable.
前述のように、有機化合物中において、CH基は、電気的酸化を受けた場合にC−H結合解裂を起こし、分解劣化しやすい部位であることを本発明者らは見出した。したがって、こうした劣化中心となりうる部位を70ppm以下に抑えることにより、電荷輸送材料のC−H結合解裂を抑制し、それを用いた有機EL素子の駆動電圧上昇及び駆動寿命低下を抑制することが可能となる。なお、CH基の存在割合が70ppmを越えると、有機EL素子の駆動電圧上昇が、定電圧制御型デバイスとしては不適となるレベルにまで増大する上、定電流制御型デバイスとした場合の有機EL素子の輝度低下速度も、実用可能な範囲から逸脱してしまう虞がある。 As described above, the present inventors have found that in an organic compound, a CH group is a site that undergoes C—H bond cleavage when subjected to electrical oxidation and is prone to degradation. Therefore, by suppressing the portion that can be a degradation center to 70 ppm or less, it is possible to suppress the C—H bond cleavage of the charge transport material and to suppress the drive voltage increase and the drive life decrease of the organic EL element using the charge transport material. It becomes possible. If the CH group content exceeds 70 ppm, the driving voltage rise of the organic EL element increases to a level that is inappropriate for a constant voltage control type device, and the organic EL in the case of a constant current control type device. There is also a possibility that the luminance reduction speed of the element may deviate from the practical range.
ただし、CH基は、芳香環の骨格に含まれない部分であり、したがって、CH基の炭素原子は芳香環を構成する炭素原子ではない。
また、CH基は、少なくとも1つのアリール基またはヘテロアリール基と単結合によって直接結合している基である。このように、アリール基またはヘテロアリール基と直接結合している場合に、CH基は分解劣化しやすい部位となる。したがって、アリール基またはヘテロアリール基と直接結合しているCH基は、存在割合を上記範囲のように小さくすることが望ましい。
さらに、CH基は、少なくとも1つのカルボニル基と単結合によって直接結合している場合にも、上記のように分解劣化しやすい部位となることがある。したがって、カルボニル基と直接結合しているCH基も、存在割合を上記範囲のように小さくすることが望ましい。
However, the CH group is a portion not included in the skeleton of the aromatic ring, and therefore the carbon atom of the CH group is not a carbon atom constituting the aromatic ring.
The CH group is a group directly bonded to at least one aryl group or heteroaryl group by a single bond. Thus, when directly bonded to the aryl group or heteroaryl group, the CH group becomes a site that is easily decomposed and degraded. Therefore, it is desirable that the CH group directly bonded to the aryl group or heteroaryl group has a small abundance ratio within the above range.
Furthermore, even when the CH group is directly bonded to at least one carbonyl group by a single bond, it may become a site that is easily decomposed and degraded as described above. Therefore, it is desirable that the CH group directly bonded to the carbonyl group has a small abundance ratio within the above range.
よって、CH基は、少なくとも1つの、アリール基、ヘテロアリール基またはカルボニル基と直接結合するか、或いは、少なくとも1つの、アリール基またはヘテロアリール基と直接結合する基であり、このようなCH基が少ないことにより、有機EL素子の駆動電圧上昇及び駆動寿命低下を抑制することが可能となる。ただし、CH基がアリール基またはヘテロアリール基と直接結合している場合に、このCH基は特に分解劣化しやすい部位となることから、少なくとも1つのアリール基またはヘテロアリール基と直接結合するCH基の存在割合を上記のように小さくすることがより好ましい。
ここで、CH基が直接結合するアリール基及びヘテロアリール基に制限はなく、任意のアリール基及びヘテロアリール基が当てはまるが、詳しくは、式(3)におけるAと同様である。
Therefore, the CH group is a group directly bonded to at least one aryl group, heteroaryl group or carbonyl group, or a group directly bonded to at least one aryl group or heteroaryl group. When there is little, it becomes possible to suppress the drive voltage rise and drive life fall of an organic EL element. However, when a CH group is directly bonded to an aryl group or a heteroaryl group, this CH group is particularly susceptible to degradation and degradation, so a CH group that is directly bonded to at least one aryl group or heteroaryl group It is more preferable to reduce the presence ratio of as described above.
Here, there is no limitation on the aryl group and heteroaryl group to which the CH group is directly bonded, and any aryl group and heteroaryl group can be applied, but the details are the same as A in Formula (3).
さらに、CH基が有する3本の結合手の内の少なくとも1本にアリール基、ヘテロアリール基またはカルボニル基が直接結合した際、残りの結合手に直接結合する基は任意である。即ち、CH基がアリール基、ヘテロアリール基またはカルボニル基と1本の結合手で結合した場合には、残りの2本の結合手に任意の基が直接結合することができ、アリール基、ヘテロアリール基またはカルボニル基が2つの結合手で結合した場合には、残りの1本の結合手に任意の基が直接結合することができる。また、残りの結合手には、水素原子が直接結合していても良い。さらに、アリール基、ヘテロアリール基またはカルボニル基がCH基に3つ直接結合している場合も含まれることは言うまでもない。 Furthermore, when an aryl group, heteroaryl group, or carbonyl group is directly bonded to at least one of the three bonds of the CH group, any group that is directly bonded to the remaining bonds is arbitrary. That is, when a CH group is bonded to an aryl group, a heteroaryl group or a carbonyl group with one bond, any group can be directly bonded to the remaining two bonds. When an aryl group or a carbonyl group is bonded with two bonds, an arbitrary group can be directly bonded to the remaining one bond. In addition, hydrogen atoms may be directly bonded to the remaining bonds. Furthermore, it goes without saying that the case where three aryl groups, heteroaryl groups or carbonyl groups are directly bonded to the CH group is also included.
CH基の残りの結合手に直接結合する、アリール基、ヘテロアリール基及びカルボニル基以外の基の具体例としては、アルケニル基、アルキニル基、アルキルアミノ基、アリールアミノ基、ヘテロアリールアミノ基、アシルアミノ基、アルコキシ基、アリールオキシ基、ヘテロアリールオキシ基、アシル基、アルコキシカルボニル基、アリールオキシカルボニル基、アルキルカルボニルオキシ基、カルボキシル基、シアノ基、水酸基、メルカプト基、アルキルチオ基、アリールチオ基、スルホニル基類、シリル基類、ボリル基類、ホスフィノ基類などが挙げられる。なお、これらは置換基を有していてもよい。 Specific examples of groups other than aryl group, heteroaryl group and carbonyl group which are directly bonded to the remaining bond of CH group include alkenyl group, alkynyl group, alkylamino group, arylamino group, heteroarylamino group, acylamino group Group, alkoxy group, aryloxy group, heteroaryloxy group, acyl group, alkoxycarbonyl group, aryloxycarbonyl group, alkylcarbonyloxy group, carboxyl group, cyano group, hydroxyl group, mercapto group, alkylthio group, arylthio group, sulfonyl group , Silyl groups, boryl groups, phosphino groups and the like. These may have a substituent.
また、CH基の残りの結合手に直接結合する基がアルケニル基である場合、その炭素数は通常2以上9以下である。その具体例としては、ビニル基、アリル基、1−ブテニル基等が挙げられる。
さらに、CH基の残りの結合手に直接結合する基がアルキニル基である場合、その炭素数は通常2以上9以下である。その具体例としては、エチニル基、プロパルギル基等が挙げられる。
In addition, when the group directly bonded to the remaining bond of the CH group is an alkenyl group, the carbon number is usually 2 or more and 9 or less. Specific examples thereof include a vinyl group, an allyl group, and a 1-butenyl group.
Furthermore, when the group directly bonded to the remaining bond of the CH group is an alkynyl group, the carbon number is usually 2 or more and 9 or less. Specific examples thereof include an ethynyl group and a propargyl group.
また、CH基の残りの結合手に直接結合する基がアルキルアミノ基である場合、その炭素数は通常1以上8以下である。その具体例としては、メチルアミノ基、ジメチルアミノ基、ジエチルアミノ基、ジベンジルアミノ基等が挙げられる。
さらに、CH基の残りの結合手に直接結合する基がアリールアミノ基である場合、その炭素数は通常6以上14以下である。その具体例としては、フェニルアミノ基、ジフェニルアミノ基、ジトリルアミノ基等が挙げられる。
When the group directly bonded to the remaining bond of the CH group is an alkylamino group, the carbon number is usually 1 or more and 8 or less. Specific examples thereof include a methylamino group, a dimethylamino group, a diethylamino group, and a dibenzylamino group.
Furthermore, when the group directly bonded to the remaining bond of the CH group is an arylamino group, the carbon number is usually 6 or more and 14 or less. Specific examples thereof include a phenylamino group, a diphenylamino group, and a ditolylamino group.
また、CH基の残りの結合手に直接結合する基が5又は6員環のヘテロアリール環を有するヘテロアリールアミノ基である場合、その炭素数は通常6以上14以下である。その具体例としては、ピリジルアミノ基、チエニルアミノ基、ジチエニルアミノ基等が挙げられる。
さらに、CH基の残りの結合手に直接結合する基がアシルアミノ基である場合、その炭素数は通常2以上10以下である。その具体例としては、アセチルアミノ基、ベンゾイルアミノ基等が挙げられる。
When the group directly bonded to the remaining bond of the CH group is a heteroarylamino group having a 5- or 6-membered heteroaryl ring, the carbon number is usually 6 or more and 14 or less. Specific examples thereof include a pyridylamino group, a thienylamino group, a dithienylamino group, and the like.
Furthermore, when the group directly bonded to the remaining bond of the CH group is an acylamino group, the carbon number is usually 2 or more and 10 or less. Specific examples thereof include an acetylamino group and a benzoylamino group.
また、CH基の残りの結合手に直接結合する基がアルコキシ基である場合、その炭素数は通常1以上8以下である。その具体例は、メトキシ基、エトキシ基、ブトキシ基等が挙げられる。
さらに、CH基の残りの結合手に直接結合する基がアリールオキシ基である場合、その炭素数は通常6以上12以下である。その具体例としては、フェニルオキシ基、1−ナフチルオキシ基、2−ナフチルオキシ基等が挙げられる。
When the group directly bonded to the remaining bond of the CH group is an alkoxy group, the carbon number is usually 1 or more and 8 or less. Specific examples thereof include a methoxy group, an ethoxy group, and a butoxy group.
Furthermore, when the group directly bonded to the remaining bond of the CH group is an aryloxy group, the carbon number is usually 6 or more and 12 or less. Specific examples thereof include a phenyloxy group, a 1-naphthyloxy group, and a 2-naphthyloxy group.
また、CH基の残りの結合手に直接結合する基が5又は6員環のヘテロアリール環を有するヘテロアリールオキシ基である場合、その炭素数は通常6以上14以下である。その具体例としては、ピリジルオキシ基、チエニルオキシ基等が挙げられる。
さらに、CH基の残りの結合手に直接結合する基がアシル基である場合、その炭素数は通常2以上10以下である。その具体例としては、ホルミル基、アセチル基等が挙げられる。
When the group directly bonded to the remaining bond of the CH group is a heteroaryloxy group having a 5- or 6-membered heteroaryl ring, the carbon number is usually 6 or more and 14 or less. Specific examples thereof include a pyridyloxy group and a thienyloxy group.
Furthermore, when the group directly bonded to the remaining bond of the CH group is an acyl group, the carbon number is usually 2 or more and 10 or less. Specific examples thereof include formyl group and acetyl group.
また、CH基の残りの結合手に直接結合する基がアルコキシカルボニル基である場合、その炭素数は通常2以上10以下である。その具体例としては、メトキシカルボニル基、エトキシカルボニル基等が挙げられる。
さらに、CH基の残りの結合手に直接結合する基がアリールオキシカルボニル基である場合、その炭素数は通常7以上13以下である。その具体例としては、フェノキシカルボニル基等が挙げられる。
When the group directly bonded to the remaining bond of the CH group is an alkoxycarbonyl group, the carbon number is usually 2 or more and 10 or less. Specific examples thereof include a methoxycarbonyl group and an ethoxycarbonyl group.
Furthermore, when the group directly bonded to the remaining bond of the CH group is an aryloxycarbonyl group, the carbon number is usually 7 or more and 13 or less. Specific examples thereof include a phenoxycarbonyl group.
また、CH基の残りの結合手に直接結合する基がアルキルカルボニルオキシ基である場合、その炭素数は通常2以上10以下である。その具体例としては、アセトキシ基等が挙げられる。
さらに、CH基の残りの結合手に直接結合する基がアルキルチオ基である場合、その炭素数は通常1以上8以下である。その具体例としては、メチルチオ基、エチルチオ基等が挙げられる。
When the group directly bonded to the remaining bond of the CH group is an alkylcarbonyloxy group, the carbon number is usually 2 or more and 10 or less. Specific examples thereof include an acetoxy group.
Furthermore, when the group directly bonded to the remaining bond of the CH group is an alkylthio group, the carbon number is usually 1 or more and 8 or less. Specific examples thereof include a methylthio group and an ethylthio group.
また、CH基の残りの結合手に直接結合する基がアリールチオ基である場合、その炭素数は通常6以上12以下である。その具体例としてはフェニルチオ基、1−ナフチルチオ基等が挙げられる。
さらに、CH基の残りの結合手に直接結合する基がスルホニル基類である場合、スルホニル基類にはスルホニル基にアルキル基やアリール基等の炭化水素基が置換したものも含む。その炭素数は通常1以上10以下である。その具体例としては、トシル基、メシル基などが挙げられる。
When the group directly bonded to the remaining bond of the CH group is an arylthio group, the carbon number is usually 6 or more and 12 or less. Specific examples thereof include a phenylthio group and a 1-naphthylthio group.
Furthermore, when the group directly bonded to the remaining bond of the CH group is a sulfonyl group, the sulfonyl group includes a sulfonyl group in which a hydrocarbon group such as an alkyl group or an aryl group is substituted. The carbon number is usually 1 or more and 10 or less. Specific examples thereof include a tosyl group and a mesyl group.
また、CH基の残りの結合手に直接結合する基がシリル基類である場合、シリル基類にはシリル基にアルキル基やアリール基等の炭化水素基が置換したものも含む。その炭素数は、通常3以上30以下である。その具体例としては、トリメチルシリル基、トリフェニルシリル基等が挙げられる。
さらに、CH基の残りの結合手に直接結合する基がボリル基類である場合、ボリル基類にはボリル基にアルキル基やアリール基等の炭化水素基が置換したものも含む。その炭素数は通常8以上28以下である。その具体例としては、ジメシチルボリル基等が挙げられる。
Further, when the group directly bonded to the remaining bond of the CH group is a silyl group, the silyl group includes those in which a hydrocarbon group such as an alkyl group or an aryl group is substituted on the silyl group. The carbon number is usually 3 or more and 30 or less. Specific examples thereof include a trimethylsilyl group and a triphenylsilyl group.
Further, when the group directly bonded to the remaining bond of the CH group is a boryl group, the boryl group includes a boryl group substituted with a hydrocarbon group such as an alkyl group or an aryl group. The carbon number is usually 8 or more and 28 or less. Specific examples thereof include a dimesitylboryl group.
また、CH基の残りの結合手に直接結合する基がホスフィノ基類である場合、ホスフィノ基類にはホスフィノ基にアルキル基やアリール基等の炭化水素基が置換したものも含む。その炭素数は通常8以上28以下である。その具体例としては、ジフェニルホスフィノ基等が挙げられる。
ただし、好ましくないCH基の順序としては、置換基を3つ有する3級炭素型CH基が最も素子寿命低下及び駆動電圧上昇を助長するために最も好ましくなく、次には置換基を2つ有する2級炭素型が好ましくなく、その次には置換基を1つ有する1級炭素型が好ましくない。
When the group directly bonded to the remaining bond of the CH group is a phosphino group, the phosphino group includes a phosphino group substituted with a hydrocarbon group such as an alkyl group or an aryl group. The carbon number is usually 8 or more and 28 or less. Specific examples thereof include a diphenylphosphino group.
However, as an unfavorable order of the CH group, a tertiary carbon type CH group having three substituents is most unfavorable in order to promote the decrease in device lifetime and increase in driving voltage, and then has two substituents. The secondary carbon type is not preferred, followed by the primary carbon type having one substituent.
また、本発明の電荷輸送材料は、アリール基と直接結合しているCH基、又は、ヘテロアリール基と直接結合しているCH基と、カルボニル基と直接結合しているCH基とが、一分子内に両方とも存在する化合物を含有しないことが好ましい。 In the charge transport material of the present invention, a CH group directly bonded to an aryl group or a CH group directly bonded to a heteroaryl group and a CH group directly bonded to a carbonyl group are combined. It is preferred not to contain compounds that are both present in the molecule.
<4.CH基の存在割合の算出>
ここで、電荷輸送材料中におけるCH基の存在割合を算出する方法を説明する。
CH基の存在割合を算出する第1の算出方法としては、次のような方法がある。即ち、後述する分析方法を用いて、電荷輸送材料中に存在する化合物の分子構造が同定できた場合、高速液体クロマトグラフ、ガスクロマトグラフ等を用い、電荷輸送材料中で、CH基を有する化合物が存在する割合(重量比;以下、PMと表記する)を導出し、CH基を有する化合物中で、CH基が占める割合(重量比;以下、RCHと表記する)を求める。これにより、電荷輸送材料全体に占めるCH基の割合(重量比;以下、PCHと表記する)を得ることができる。
<4. Calculation of CH Group Abundance>
Here, a method for calculating the abundance ratio of CH groups in the charge transport material will be described.
As a first calculation method for calculating the abundance ratio of the CH group, there is the following method. That is, when the molecular structure of the compound present in the charge transport material can be identified using the analysis method described later, a compound having a CH group is identified in the charge transport material using a high performance liquid chromatograph, a gas chromatograph or the like. percentage present (weight ratio; hereinafter, referred to as P M) derives, in compounds having a CH group, the proportion of the CH group (weight ratio; hereinafter, referred to as R CH) Request. Thereby, the ratio (weight ratio; hereinafter referred to as P CH ) of the CH groups in the entire charge transport material can be obtained.
即ち、CH基を有する単一または複数の化合物の総重量をWMとし、CH基を有さない単一または複数の化合物の総重量をWAとすると、下記式(6)が成立する。
PM=WM/(WA+WM) ・・・式(6)
ここで、CH基のモル重量(=13.019)をMCHとし、CH基を有する単一または複数の化合物の分子量の平均値をMMとすると、下記式(7)が成立する。
RCH=MCH/MM ・・・式(7)
That is, the total weight of a single or more compounds having a CH group as W M, when the total weight of a single compound or compounds having no CH group and W A, the following equation (6) is established.
P M = W M / (W A + W M ) (6)
Here, when the molar weight of the CH group (= 13.019) is M CH and the average molecular weight of the single or plural compounds having the CH group is M M , the following formula (7) is established.
R CH = M CH / M M (7)
したがって、PCHは下記式(8)により算出される。
PCH=RCH×PM ・・・式(8)
これを用いて、例えば、高速液体クロマトグラフのUV吸収ピーク面積からPMを算出し、それとCH基を有する化合物の分子量とから、PCHを得ることができる。また、ここでのUV吸収ピーク面積の測定には波長254nmのUV光を使用することができる。
Therefore, P CH is calculated by the following formula (8).
P CH = R CH × P M (8)
Using this, for example, P M can be calculated from the UV absorption peak area of a high performance liquid chromatograph, and P CH can be obtained from the molecular weight of the compound having a CH group. Further, UV light having a wavelength of 254 nm can be used for measurement of the UV absorption peak area here.
なお、第1の算出方法によりCH基の存在割合を算出する場合、電荷輸送材料中に存在する化合物の分子構造を同定する分析方法としては、後述する分析方法の中でも特に、質量分析(高速液体クロマトグラフと組合せた、所謂LC−MSを含む)、各種NMR測定、元素分析、高速液体クロマトグラフ、薄層クロマトグラフ等を利用した標品との比較に基づく不純物の同定などを用いることが好ましい。 In addition, when calculating the abundance ratio of the CH group by the first calculation method, an analysis method for identifying the molecular structure of the compound present in the charge transport material is a mass analysis (high-speed liquid), among the analysis methods described later. (Including so-called LC-MS in combination with a chromatograph), various NMR measurements, elemental analysis, high performance liquid chromatographs, identification of impurities based on comparison with standard samples using thin layer chromatographs, etc. are preferably used. .
また、CH基の存在割合を算出する第2の算出方法としては、次のような方法がある。即ち、後述する分析方法を用いることにより、電荷輸送材料全体を構成する元素比率や置換基構成、分子部分構造などを明らかにし、次いで、1H−NMRスペクトル(2次元NMRスペクトルを含む)から、CH基の存在割合を上記スペクトルの積分比から導き出す。 In addition, as a second calculation method for calculating the abundance ratio of the CH group, there is the following method. That is, by using the analysis method described later, the ratio of elements constituting the entire charge transport material, the structure of substituents, the molecular partial structure, etc. are clarified, and then from the 1 H-NMR spectrum (including the two-dimensional NMR spectrum), The proportion of CH groups present is derived from the integral ratio of the spectrum.
なお、第2の算出方法によりCH基の存在割合を算出する場合、電荷輸送材料中に存在する化合物の分子構造を同定する分析方法としては、後述する分析方法の中でも特に、元素分析、質量分析、NMRスペクトル、原子吸光分析、蛍光X線分析(ファンダメンタルパラメーター法を含む)、ICP(=誘導結合プラズマ)発光分析、X線光電子分光法などを用いることが好ましい。 In addition, when calculating the abundance ratio of the CH group by the second calculation method, as an analysis method for identifying the molecular structure of the compound present in the charge transporting material, elemental analysis, mass spectrometry, among the analysis methods described later, are mentioned. , NMR spectrum, atomic absorption analysis, fluorescent X-ray analysis (including fundamental parameter method), ICP (= inductively coupled plasma) emission analysis, X-ray photoelectron spectroscopy, etc. are preferably used.
電荷輸送材料中に存在する化合物の分子構造を同定する分析方法としては、公知の分析方法を任意に用いることができる。分析方法の例としては、ガスクロマトグラフ(GC)、高速液体クロマトグラフ(HPLC)、高速アミノ酸分析計(AAA)、キャピラリー電気泳動測定(CE)、サイズ排除クロマトグラフ(SEC)、ゲル浸透クロマトグラフ(GPC)、交差分別クロマトグラフ(CFC)質量分析(MS、LC−MS,GC−MS,MS/MS)、核磁気共鳴装置{NMR(1H−NMR,13C−NMR)}、フーリエ変換赤外分光光度計(FT−IR)、紫外可視近赤外分光光度計(UV.VIS,NIR)、電子スピン共鳴装置(ESR)、透過型電子顕微鏡(TEM−EDX)、電子線マイクロアナライザー(EPMA)、金属元素分析{イオンクロマトグラフ、誘導結合プラズマ−発光分光(ICP−AES)、原子吸光分析(AAS)、蛍光X線分析装置(XRF)}、非金属元素分析、微量成分分析(ICP−MS,GF−AAS,GD−MS)等が挙げられる。 As an analysis method for identifying the molecular structure of the compound present in the charge transport material, a known analysis method can be arbitrarily used. Examples of analysis methods include gas chromatograph (GC), high performance liquid chromatograph (HPLC), high speed amino acid analyzer (AAA), capillary electrophoresis measurement (CE), size exclusion chromatograph (SEC), gel permeation chromatograph ( GPC), cross-fractionation chromatograph (CFC) mass spectrometry (MS, LC-MS, GC-MS, MS / MS), nuclear magnetic resonance apparatus {NMR ( 1 H-NMR, 13 C-NMR)}, Fourier transform red External spectrophotometer (FT-IR), UV-visible near-infrared spectrophotometer (UV.VIS, NIR), electron spin resonance apparatus (ESR), transmission electron microscope (TEM-EDX), electron beam microanalyzer (EPMA) ), Metal element analysis {ion chromatograph, inductively coupled plasma-emission spectroscopy (ICP-AES), atomic absorption analysis (AAS), Fluorescent X-ray analyzer (XRF)}, non-metallic element analysis, trace component analysis (ICP-MS, GF-AAS, GD-MS) and the like.
さらに具体的に分析方法の一例を挙げて説明する。
有機化合物を構成材料とする電荷輸送材料は有機溶剤に可溶であるため、まずHPLCを用いて構成成分を検出する。次にHPLCにて検出された成分についてLC−MSによる分子量測定を行なう。一方、HPLCにより得られた成分を分取HPLCにより各成分分取を実施し、分取された各成分を1H−NMRにて構造確認を実施することにより推定構造が得られる。より確実にするために13C−NMRを測定するとなおよい。HPLCの代わりにGPCを用いて各分子量ごとに分取し、同様に1H−NMRを用いて構造確認する方法でもよい。さらにFT−IR、元素分析等を実施することにより、構成元素、構成置換基がより明確に推定可能となる。
More specifically, an example of the analysis method will be described.
Since the charge transport material containing an organic compound as a constituent material is soluble in an organic solvent, the constituent components are first detected using HPLC. Next, the molecular weight of the components detected by HPLC is measured by LC-MS. On the other hand, a component obtained by HPLC is subjected to preparative HPLC, and a presumed structure is obtained by confirming the structure of each fractionated component by 1 H-NMR. It is even better to measure 13 C-NMR for more certainty. Alternatively, GPC may be used for each molecular weight instead of HPLC, and the structure may be confirmed using 1 H-NMR. Furthermore, by performing FT-IR, elemental analysis, etc., the constituent elements and constituent substituents can be estimated more clearly.
以上の分析結果より、電荷輸送材料構成成分の構造を推定することができる。特にNMRでCH基存在の有無はほぼ明確に確認できるため、完全な構造一致が困難な場合でも、CH基を有するか否かは判断でき得る。
またCH基の含有量は、上記構造決定に用いたHPLC等により、CH基を有する構成材料の電荷輸送材料に対する成分比を求め、例えば第1の算出方法により算出することにより得ることができる。
From the above analysis results, the structure of the charge transport material component can be estimated. In particular, the presence or absence of a CH group can be almost clearly confirmed by NMR, and therefore it can be determined whether or not it has a CH group even when complete structural matching is difficult.
The content of the CH group can be obtained by calculating the component ratio of the constituent material having a CH group to the charge transporting material by HPLC or the like used for the structure determination, and calculating by the first calculation method, for example.
<5.CH基の排除>
次に、電荷輸送材料中のCH基を排除して、本発明の電荷輸送材料を製造する方法を説明する。
本発明の電荷輸送材料の製造方法に制限はなく、任意の方法を用いることができるが、例えば、
(a)CH基を含まない原料のみを使用して電荷輸送材料を製造する方法
(b)原料、中間体、最終合成物の何れかの段階で、各種精製方法を用いて、CH基を有する化合物(不純物)を、排除する方法
などが挙げられる。
<5. Exclusion of CH group>
Next, a method for producing the charge transport material of the present invention by eliminating CH groups in the charge transport material will be described.
There is no limitation on the method for producing the charge transport material of the present invention, and any method can be used.
(A) Method for producing charge transport material using only raw material not containing CH group (b) Having a CH group using various purification methods at any stage of raw material, intermediate and final synthesized product For example, a method of eliminating the compound (impurities) may be used.
上記の方法(b)における精製方法としては、公知の方法を任意に用いることができるが、例えば、「分離精製技術ハンドブック」(1993年、(財)日本化学会編)、「化学変換法による微量成分および難精製物質の高度分離」(1988年、(株)アイ ピー シー発光)、あるいは「実験化学講座(第4版)1」(1990年、(財)日本化学会編)の「分離と精製」の項に記載の方法などを用いることができる。 As the purification method in the above method (b), known methods can be arbitrarily used. For example, “Separation and Purification Technology Handbook” (1993, edited by The Chemical Society of Japan), “by chemical conversion method” “Separation of trace components and difficult-to-purify substances” (1988, IC Luminescence Co., Ltd.) or “Experimental Chemistry Course (4th Edition) 1” (1990, The Chemical Society of Japan) And the method described in the section of “Purification” can be used.
具体例としては、抽出(懸濁洗浄、煮沸洗浄、超音波洗浄、酸塩基洗浄を含む)、吸着、吸蔵、融解、晶析(溶媒からの再結晶、再沈殿を含む)、蒸留(常圧蒸留、減圧蒸留)、蒸発、昇華(常圧昇華、減圧昇華)、イオン交換、透析、濾過、限外濾過、逆浸透、圧浸透、帯域溶解、電気泳動、遠心分離、浮上分離、沈降分離、磁気分離、各種クロマトグラフィー(形状分類:カラム、ペーパー、薄層、キャピラリー等。移動相分類:ガス、液体、ミセル、超臨界流体等。分離機構:吸着、分配、イオン交換、分子ふるい、キレート、ゲル濾過、排除、アフィニティー等。)などが挙げられる。 Specific examples include extraction (including suspension washing, boiling washing, ultrasonic washing, and acid-base washing), adsorption, occlusion, melting, crystallization (including recrystallization from solvent, reprecipitation), distillation (atmospheric pressure) Distillation, vacuum distillation), evaporation, sublimation (atmospheric pressure sublimation, vacuum sublimation), ion exchange, dialysis, filtration, ultrafiltration, reverse osmosis, pressure osmosis, zone lysis, electrophoresis, centrifugation, flotation separation, sedimentation separation, Magnetic separation, various chromatography (shape classification: column, paper, thin layer, capillary, etc. Mobile phase classification: gas, liquid, micelle, supercritical fluid, etc. Separation mechanism: adsorption, distribution, ion exchange, molecular sieve, chelate, Gel filtration, exclusion, affinity, etc.).
<6.電荷輸送材料の用途>
本発明の電荷輸送材料は任意の用途に用いることができるが、有機EL素子に用いて好適である。例えば、有機EL素子の正孔輸送層、発光層、正孔阻止層、電子輸送層、正孔注入層の材料として好ましく用いることができる。
<6. Applications of charge transport materials>
The charge transport material of the present invention can be used for any application, but is suitable for use in an organic EL device. For example, it can be preferably used as a material for a hole transport layer, a light emitting layer, a hole blocking layer, an electron transport layer, and a hole injection layer of an organic EL device.
中でも、本発明の電荷輸送材料を正孔輸送層の材料(正孔輸送材料)として用いる場合には、本発明の電荷輸送材料は、正孔の注入がされやすく、また、正孔の輸送能が大きいものが好ましい。
上記観点から、本発明の電荷輸送材料を正孔輸送材料として用いる場合、本発明の電荷輸送材料の酸化電位は、+1.4V以下が好ましく、+1.35V以下がより好ましく、+1.3V以下が特に好ましい。
In particular, when the charge transport material of the present invention is used as a material for the hole transport layer (hole transport material), the charge transport material of the present invention is easy to inject holes and has a hole transport capability. A large one is preferable.
From the above viewpoint, when the charge transport material of the present invention is used as a hole transport material, the oxidation potential of the charge transport material of the present invention is preferably +1.4 V or less, more preferably +1.35 V or less, and +1.3 V or less. Particularly preferred.
さらに、本発明の電荷輸送材料を正孔輸送材料として用いる場合、本発明の電荷輸送材料の正孔移動度は、1×10-5cm2/V・sec以上が好ましく、5×10-5cm2/V・sec以上がより好ましく、1×10-4cm2/V・sec以上が特に好ましい。なお、正孔移動度は、ガラス基盤/ITO膜/本発明の電荷輸送材料の膜(2〜10μm)/アルミニウム膜をこの順に積層し、TOF移動度測定法により測定することができる。 Further, when the charge transport material of the present invention is used as a hole transport material, the hole mobility of the charge transport material of the present invention is preferably 1 × 10 −5 cm 2 / V · sec or more, and preferably 5 × 10 −5. cm 2 / V · sec or more is more preferable, and 1 × 10 −4 cm 2 / V · sec or more is particularly preferable. The hole mobility can be measured by TOF mobility measurement method by laminating glass substrate / ITO film / charge transport material film of the present invention (2 to 10 μm) / aluminum film in this order.
また、本発明の電荷輸送材料を正孔阻止層の材料(正孔阻止材料)として用いる場合には、本発明の電荷輸送材料は、電子の注入がされやすく、また、電子の輸送性能が正孔の輸送性能に比べて大きく、さらに、正孔注入機能が低いものが好ましい。
上記観点から、本発明の電荷輸送材料を正孔阻止材料として用いる場合、本発明の電荷輸送材料の酸化電位は、+1.5V以上が好ましく、+1.6V以上がより好ましく、+1.7V以上が特に好ましい。
In addition, when the charge transport material of the present invention is used as a hole blocking layer material (hole blocking material), the charge transport material of the present invention is easy to inject electrons and has a positive electron transport performance. Those having a large hole transporting performance and a low hole injection function are preferable.
From the above viewpoint, when the charge transport material of the present invention is used as a hole blocking material, the oxidation potential of the charge transport material of the present invention is preferably +1.5 V or more, more preferably +1.6 V or more, and +1.7 V or more. Particularly preferred.
さらに、本発明の電荷輸送材料を正孔阻止材料として用いる場合、本発明の電荷輸送材料の電子移動度は、1×10-5cm2/V・sec以上が好ましく、5×10-5cm2/V・sec以上がより好ましく、1×10-4cm2/V・sec以上が特に好ましい。なお、電子移動度は、上記のTOF移動度測定法により測定することができる。
また、本発明の電荷輸送材料を正孔阻止材料として用いる場合、本発明の電荷輸送材料の正孔移動度は、1×10-5cm2/V・sec以下が好ましく、1×10-7cm2/V・sec以下がより好ましく、1×10-9cm2/V・sec以下が特に好ましい。
Furthermore, when the charge transport material of the present invention is used as a hole blocking material, the electron mobility of the charge transport material of the present invention is preferably 1 × 10 −5 cm 2 / V · sec or more, preferably 5 × 10 −5 cm. 2 / V · sec or more is more preferable, and 1 × 10 −4 cm 2 / V · sec or more is particularly preferable. The electron mobility can be measured by the above TOF mobility measurement method.
When the charge transport material of the present invention is used as a hole blocking material, the hole mobility of the charge transport material of the present invention is preferably 1 × 10 −5 cm 2 / V · sec or less, preferably 1 × 10 −7. cm 2 / V · sec or less is more preferable, and 1 × 10 −9 cm 2 / V · sec or less is particularly preferable.
[II.有機電界発光素子]
以下、本発明の有機EL素子について、図面を参照しながら説明する。
図1は本発明に用いられる一般的な有機EL素子の構造例を模式的に示す断面図であり、1は基板、2は陽極、4は正孔輸送層、5は発光層(有機発光層)、6は正孔阻止層、8は陰極を各々表わす。さらに、本発明の一実施形態であるこの有機EL素子においては、正孔輸送層4、正孔阻止層6、並びに、後述する電子輸送層7及び正孔注入層3のうち少なくともいずれかが、本発明の電荷輸送材料のみにより形成され、且つ/又は、発光層5が、本発明の電荷輸送材料とドーパントとから形成されることが望ましい。
以下、詳細に説明する。
[II. Organic electroluminescent device]
Hereinafter, the organic EL element of the present invention will be described with reference to the drawings.
FIG. 1 is a cross-sectional view schematically showing a structural example of a general organic EL element used in the present invention. 1 is a substrate, 2 is an anode, 4 is a hole transport layer, and 5 is a light emitting layer (organic light emitting layer). ), 6 represents a hole blocking layer, and 8 represents a cathode. Furthermore, in this organic EL device that is an embodiment of the present invention, at least one of the hole transport layer 4, the hole blocking layer 6, and the electron transport layer 7 and the hole injection layer 3 described later is: It is desirable that the light-emitting layer 5 is formed only of the charge transport material of the present invention and / or the light emitting layer 5 is formed of the charge transport material of the present invention and a dopant.
Details will be described below.
<1.基板>
基板1は有機EL素子の支持体となるものである。その材質や形状は任意であるが、例えば、石英やガラスの板、金属板や金属箔、プラスチックフィルムやシートなどが用いられる。特にガラス板や、ポリエステル、ポリメタクリレート、ポリカーボネート、ポリスルホンなどの透明な合成樹脂の板が好ましい。合成樹脂基板を使用する場合にはガスバリア性に留意する必要がある。基板1のガスバリア性が小さすぎると、基板1を通過した外気により有機EL素子が劣化することがあるので好ましくない。このため、合成樹脂基板の少なくとも片面に緻密なシリコン酸化膜等を設けてガスバリア性を確保する方法も好ましい方法の一つである。
<1. Substrate>
The substrate 1 serves as a support for the organic EL element. Although the material and shape are arbitrary, for example, a quartz or glass plate, a metal plate or a metal foil, a plastic film or a sheet is used. In particular, a glass plate or a transparent synthetic resin plate such as polyester, polymethacrylate, polycarbonate, or polysulfone is preferable. When using a synthetic resin substrate, it is necessary to pay attention to gas barrier properties. If the gas barrier property of the substrate 1 is too small, the organic EL element may be deteriorated by the outside air that has passed through the substrate 1, which is not preferable. For this reason, a method of providing a gas barrier property by providing a dense silicon oxide film or the like on at least one surface of the synthetic resin substrate is also a preferable method.
<2.陽極>
基板1上には陽極2が設けられる。陽極2は正孔輸送層4への正孔注入の役割を果たすものである。この陽極の材質は任意であるが、通常、アルミニウム、金、銀、ニッケル、パラジウム、白金等の金属、インジウム及び/またはスズの酸化物などの金属酸化物、ヨウ化銅などのハロゲン化金属、カーボンブラック、あるいは、ポリ(3−メチルチオフェン)、ポリピロール、ポリアニリン等の導電性高分子などにより構成される。
<2. Anode>
An anode 2 is provided on the substrate 1. The anode 2 plays a role of hole injection into the hole transport layer 4. The material of this anode is arbitrary, but usually metal such as aluminum, gold, silver, nickel, palladium, platinum, metal oxide such as indium and / or tin oxide, metal halide such as copper iodide, It is composed of carbon black or a conductive polymer such as poly (3-methylthiophene), polypyrrole, or polyaniline.
陽極2の形成は通常、スパッタリング法、真空蒸着法などにより行われることが多い。また、銀などの金属微粒子、ヨウ化銅などの微粒子、カーボンブラック、導電性の金属酸化物微粒子、導電性高分子微粉末などの粉末材料を用いて陽極2を形成する場合には、適当なバインダー樹脂溶液に粉末材料を分散し、基板1上に塗布することにより陽極2を形成することもできる。
さらに、導電性高分子を用いて陽極2を形成する場合は、電解重合により直接基板1上に薄膜を形成したり、基板1上に導電性高分子を塗布して陽極2を形成することもできる(Appl.Phys.Lett.,60巻,2711頁,1992年)。
In general, the anode 2 is often formed by sputtering, vacuum deposition, or the like. Further, when the anode 2 is formed using a powder material such as fine metal particles such as silver, fine particles such as copper iodide, carbon black, conductive metal oxide fine particles, and conductive polymer fine powder, it is suitable. The anode 2 can also be formed by dispersing a powder material in a binder resin solution and applying it onto the substrate 1.
Further, when the anode 2 is formed using a conductive polymer, a thin film may be directly formed on the substrate 1 by electrolytic polymerization, or the anode 2 may be formed by applying a conductive polymer on the substrate 1. (Appl. Phys. Lett., 60, 2711, 1992).
また、陽極2は、異なる物質で積層して形成することも可能である。
陽極2の厚みは任意であるが、通常、必要とする透明性により設定することが望ましい。透明性が必要とされる場合は、可視光の透過率を、通常60%以上、好ましくは80%以上とすることが望ましい。この場合、陽極2の厚みは、通常5nm以上、好ましくは10nm以上、また、通常1000nm以下、好ましくは500nm以下程度である。不透明でよい場合、陽極2は基板1と同一でもよい。また、さらには上記の陽極2の上に異なる導電材料を積層することも可能である。
The anode 2 can be formed by stacking different materials.
Although the thickness of the anode 2 is arbitrary, it is usually desirable to set it according to the required transparency. When transparency is required, the visible light transmittance is usually 60% or more, preferably 80% or more. In this case, the thickness of the anode 2 is usually 5 nm or more, preferably 10 nm or more, and usually 1000 nm or less, preferably about 500 nm or less. If it can be opaque, the anode 2 may be the same as the substrate 1. Furthermore, it is also possible to laminate different conductive materials on the anode 2 described above.
<3.正孔輸送層>
陽極2上(又は、後述する正孔注入層3上)には、正孔輸送層4が設けられている。この正孔輸送層4は、正孔を効率よく発光層5に注入するために、陽極2と発光層5との間に設けられる。よって、正孔輸送層4の材料(以下適宜「正孔輸送材料」という)に要求される条件としては、陽極2からの正孔注入効率が高く、かつ、注入された正孔を効率よく輸送することができる材料であることが必要である。そのためには、イオン化ポテンシャルが小さく、可視光の光に対して透明性が高く、しかも正孔移動度が大きく、さらに安定性に優れ、トラップとなる不純物が製造時や使用時に発生しにくいことが要求される。また、発光層5に接するために発光層5からの発光を消光したり、発光層5との間でエキサイプレックスを形成して効率を低下させないことが求められる。
<3. Hole transport layer>
On the anode 2 (or on the hole injection layer 3 described later), a hole transport layer 4 is provided. The hole transport layer 4 is provided between the anode 2 and the light emitting layer 5 in order to inject holes into the light emitting layer 5 efficiently. Therefore, the conditions required for the material of the hole transport layer 4 (hereinafter referred to as “hole transport material” as appropriate) are high in the hole injection efficiency from the anode 2 and efficiently transport the injected holes. It must be a material that can be made. For this purpose, the ionization potential is small, the transparency to visible light is high, the hole mobility is high, the stability is high, and impurities that become traps are less likely to be generated during manufacturing and use. Required. Further, in order to contact the light emitting layer 5, it is required not to quench the light emitted from the light emitting layer 5 or to form an exciplex with the light emitting layer 5 to reduce the efficiency.
上記の一般的要求以外に、車載表示用等への応用を考えた場合、有機EL素子にはさらに耐熱性が要求される。したがって、正孔輸送層4の材料としては、ガラス転移温度Tgとして85℃以上の値を有する材料が望ましい。また、これは、正孔注入層3、発光層5、正孔阻止層6、電子輸送層7、などの正孔輸送層4以外の層の材料についても同様である。 In addition to the above general requirements, when considering application to in-vehicle display or the like, the organic EL element is further required to have heat resistance. Therefore, as the material of the hole transport layer 4, a material having a glass transition temperature Tg of 85 ° C. or more is desirable. The same applies to materials of layers other than the hole transport layer 4 such as the hole injection layer 3, the light emitting layer 5, the hole blocking layer 6, and the electron transport layer 7.
前述のように、正孔輸送層4の材料である正孔輸送材料として、本発明の電荷輸送材料を用いることができる。この際、正孔輸送材料として本発明の電荷輸送材料に無機材料からなる電荷輸送材料を混合して用いても良いが、通常は、本発明の電荷輸送材料のみを用い、正孔輸送層4を、本発明の電荷輸送材料のみからなる層として形成することが望ましい。これにより、有機EL素子の駆動寿命を向上させるとともに、駆動電圧上昇を抑制することができる。また、この場合、正孔輸送材料として用いることができる化合物の具体例としては、下記式で表されるものなどが挙げられる。 As described above, the charge transport material of the present invention can be used as the hole transport material that is the material of the hole transport layer 4. At this time, the charge transport material of the present invention may be mixed with the charge transport material of the present invention as the hole transport material, but usually, only the charge transport material of the present invention is used and the hole transport layer 4 is used. Is preferably formed as a layer made of only the charge transport material of the present invention. As a result, the drive life of the organic EL element can be improved and an increase in drive voltage can be suppressed. In this case, specific examples of the compound that can be used as the hole transport material include those represented by the following formula.
また、正孔輸送材料として本発明の電荷輸送材料以外の材料を用いる場合、このような正孔輸送材料としては、例えば、4,4′−ビス[N−(1−ナフチル)−N−フェニルアミノ]ビフェニルで代表される2個以上の3級アミンを含み2個以上の縮合芳香族環が窒素原子に置換した芳香族ジアミン(特開平5−234681号公報)、4,4′,4″−トリス(1−ナフチルフェニルアミノ)トリフェニルアミン等のスターバースト構造を有する芳香族アミン化合物(J.Lumin.,72巻−74巻、985頁、1997年)、トリフェニルアミンの四量体から成る芳香族アミン化合物(Chem.Commun.,2175頁、1996年)、2,2′,7,7′−テトラキス−(ジフェニルアミノ)−9,9′−スピロビフルオレン等のスピロ化合物(Synth.Metals,91巻、209頁、1997年)等が挙げられる。 When a material other than the charge transport material of the present invention is used as the hole transport material, examples of such a hole transport material include 4,4′-bis [N- (1-naphthyl) -N-phenyl. Aromatic diamines containing two or more tertiary amines typified by amino] biphenyl and having two or more condensed aromatic rings substituted with nitrogen atoms (Japanese Patent Laid-Open No. 5-234681), 4,4 ′, 4 ″ -An aromatic amine compound having a starburst structure such as tris (1-naphthylphenylamino) triphenylamine (J. Lumin., 72-74, 985, 1997), from a tetramer of triphenylamine Aromatic amine compound (Chem. Commun., 2175, 1996), 2,2 ', 7,7'-tetrakis- (diphenylamino) -9,9'-spirobifluor Spiro compounds such as emissions (Synth.Metals, 91 vol, 209 pp., 1997), and the like.
また、上記の化合物のほか、正孔輸送層4の材料として、ポリビニルカルバゾール、ポリビニルトリフェニルアミン(特開平7−53953号公報)、テトラフェニルベンジジンを含有するポリアリーレンエーテルサルホン(Polym.Adv.Tech.,7巻、33頁、1996年)等の高分子材料を用いることも可能である。
なお、これら正孔輸送材料として用いられる化合物は、1種を単独で用いてもよく、2種以上を任意の組み合わせ及び比率で併用してもよい。
In addition to the above-mentioned compounds, polyarylene ether sulfone (Polym. Adv.) Containing polyvinyl carbazole, polyvinyl triphenylamine (Japanese Patent Laid-Open No. 7-53953), and tetraphenylbenzidine as materials for the hole transport layer 4 can be used. Tech., Vol. 7, p. 33, 1996) can also be used.
In addition, the compound used as these hole transport materials may be used individually by 1 type, and may use 2 or more types together by arbitrary combinations and ratios.
正孔輸送層4の形成方法は任意であるが、通常は、塗布法又は真空蒸着法により形成することができる。
塗布法の場合は、正孔輸送材料と、必要により正孔のトラップにならないバインダー樹脂や塗布性改良剤などの添加剤とを混合し、溶媒又は分散媒に溶解又は分散して塗布液を調製する。その後、調製した塗布液をスピンコート法などの方法により陽極2上に塗布し、溶媒又は分散媒を乾燥、除去して正孔輸送層4を形成する。
Although the formation method of the positive hole transport layer 4 is arbitrary, Usually, it can form by the apply | coating method or a vacuum evaporation method.
In the case of the coating method, a hole transport material and, if necessary, a binder resin that does not trap holes and an additive such as a coating property improver are mixed, and dissolved or dispersed in a solvent or dispersion medium to prepare a coating solution. To do. Thereafter, the prepared coating liquid is applied onto the anode 2 by a method such as spin coating, and the solvent or dispersion medium is dried and removed to form the hole transport layer 4.
溶媒及び分散媒は、正孔輸送材料等の種類に応じて、任意のものを用いればよい。
また、バインダー樹脂は任意であるが、例えば、ポリカーボネート、ポリアリレート、ポリエステル等を用いることが出来る。ただし、バインダー樹脂がCH基を有していると、そこから前述した分解劣化が生じる虞があるため、塗布法に用いるバインダー樹脂としては、CH基の含有割合が小さいか、又はCH基を有さないバインダー樹脂を用いることが好ましい。このようなバインダー樹脂の具体例としては、ポリアセチレン、ポリフェニレンエーテル、ポリフェニレンスルフィド、下記化合物(P−1),(P−3)などが挙げられる。なお、下記式においてmはそれぞれ独立に正の数を表わす。
Moreover, although binder resin is arbitrary, for example, polycarbonate, polyarylate, polyester, etc. can be used. However, if the binder resin has a CH group, the above-described degradation and degradation may occur. Therefore, the binder resin used in the coating method has a small CH group content or a CH group. It is preferable to use a binder resin that does not. Specific examples of such a binder resin include polyacetylene, polyphenylene ether, polyphenylene sulfide, and the following compounds (P-1) and (P-3). In the following formula, m independently represents a positive number.
さらに、バインダー樹脂は、その使用量が多いと正孔移動度を低下させる虞があるので、使用量は少ない方が望ましく、通常、50重量%以下が好ましい。
なお、バインダー樹脂や添加剤の酸化電位が+0.8V以上である場合、正孔輸送層4に含まれるCH基の存在割合を70ppm以下とすることができるのであれば、正孔輸送材料、バインダー樹脂、添加剤などをまとめて、本発明の電荷輸送材料とみなすこともできる。これにより、バインダー樹脂や添加剤などの正孔輸送材料以外の材料を用いた場合でも、正孔輸送層4を、本発明の電荷輸送材料のみからなる層として形成することが可能となる。
Further, since the binder resin may reduce hole mobility when the amount used is large, it is desirable that the amount used is small, and usually 50% by weight or less is preferable.
When the oxidation potential of the binder resin or additive is +0.8 V or higher, the hole transport material, the binder can be used as long as the CH group content in the hole transport layer 4 can be 70 ppm or less. Resins, additives and the like can be collectively regarded as the charge transport material of the present invention. Accordingly, even when a material other than the hole transport material such as a binder resin or an additive is used, the hole transport layer 4 can be formed as a layer made of only the charge transport material of the present invention.
一方、真空蒸着法の場合には、陽極2上に正孔輸送材料を蒸着させて、正孔輸送層4を形成する。具体的操作の一例を挙げると、正孔輸送材料を真空容器内に設置されたルツボに入れ、真空容器内を適当な真空ポンプで10-4Pa程度にまで排気した後、ルツボを加熱して、正孔輸送材料を蒸発させ、ルツボと向き合って置かれた、陽極2が形成された基板1上に正孔輸送層4を形成させる。
また、正孔輸送層4の膜厚は任意であるが、通常5nm以上、好ましくは10nm以上、また、通常300nm以下、好ましくは100nm以下である。このように薄い層を一様に形成するためには、一般に、真空蒸着法がよく用いられる。
On the other hand, in the case of the vacuum deposition method, a hole transport material is deposited on the anode 2 to form the hole transport layer 4. As an example of a specific operation, the hole transport material is put in a crucible installed in a vacuum vessel, the inside of the vacuum vessel is evacuated to about 10 −4 Pa with an appropriate vacuum pump, and then the crucible is heated. Then, the hole transport material is evaporated, and the hole transport layer 4 is formed on the substrate 1 on which the anode 2 is formed, which is placed facing the crucible.
The thickness of the hole transport layer 4 is arbitrary, but is usually 5 nm or more, preferably 10 nm or more, and usually 300 nm or less, preferably 100 nm or less. In order to form such a thin layer uniformly, generally, a vacuum evaporation method is often used.
<4.発光層>
正孔輸送層4の上には発光層5が設けられている。発光層5は、発光材料を含有し、電界を与えられた電極間において、陽極2から注入されて正孔輸送層4を移動する正孔と、陰極8から注入されて正孔阻止層6を移動する電子との再結合により励起されて、強い発光を示す。
なお発光層5は、本発明の性能を損なわない範囲で、発光材料以外の材料を含んでいてもよい。
<4. Light emitting layer>
A light emitting layer 5 is provided on the hole transport layer 4. The light-emitting layer 5 contains a light-emitting material, and between the electrodes to which an electric field is applied, holes that are injected from the anode 2 and move through the hole transport layer 4 and holes that are injected from the cathode 8 to form the hole blocking layer 6. Excited by recombination with moving electrons, emits intense light.
In addition, the light emitting layer 5 may contain materials other than a light emitting material in the range which does not impair the performance of this invention.
発光層5に用いられる発光材料は任意である。ただし、一般に、発光材料は、安定な薄膜形状を有し、固体状態で高い発光(蛍光または燐光)量子収率を示し、正孔及び/又は電子を効率よく輸送することができる化合物であることが望ましい。さらに電気化学的かつ化学的に安定であり、トラップとなる不純物が製造時や使用時に発生しにくい化合物であることが要求される。 The light emitting material used for the light emitting layer 5 is arbitrary. However, in general, a luminescent material is a compound that has a stable thin film shape, exhibits high emission (fluorescence or phosphorescence) quantum yield in a solid state, and can efficiently transport holes and / or electrons. Is desirable. Further, it is required to be a compound that is electrochemically and chemically stable and does not easily generate impurities as traps during production or use.
このような条件を満たし、蛍光を発する有機発光層を形成する材料としては、例えば、8−ヒドロキシキノリンのアルミニウム錯体などの金属錯体(特開昭59−194393号公報)、10−ヒドロキシベンゾ[h]キノリンの金属錯体(特開平6−322362号公報)、ビススチリルベンゼン誘導体(特開平1−245087号公報、同2−222484号公報)、ビススチリルアリーレン誘導体(特開平2−247278号公報)、(2−ヒドロキシフェニル)ベンゾチアゾールの金属錯体(特開平8−315983号公報)、シロール誘導体、等が挙げられる。これらの発光層材料は、通常は真空蒸着法により正孔輸送層上に積層される。また、前述の正孔輸送層材料のうち、発光性を有する芳香族アミン系化合物も発光層材料として用いることが出来る。 As a material that satisfies such conditions and forms an organic light emitting layer that emits fluorescence, for example, a metal complex such as an aluminum complex of 8-hydroxyquinoline (Japanese Patent Laid-Open No. 59-194393), 10-hydroxybenzo [h ] Metal complexes of quinoline (JP-A-6-322362), bisstyrylbenzene derivatives (JP-A-1-245087, JP-A-2-222484), bisstyrylarylene derivatives (JP-A-2-247278), Examples include (2-hydroxyphenyl) benzothiazole metal complexes (JP-A-8-315983), silole derivatives, and the like. These light emitting layer materials are usually laminated on the hole transport layer by a vacuum deposition method. Of the hole transport layer materials described above, an aromatic amine compound having a light emitting property can also be used as the light emitting layer material.
また、発光材料は、ドーパントとホスト材料とから形成されることがある。この場合、ホスト材料には本発明の電荷輸送材料を用い、発光層5を、前述のように、本発明の電荷輸送材料及びドーパントから形成された層とすることが望ましい。さらに、発光層5は、本発明の電荷輸送材料及びドーパントのみで形成された層とすることがより望ましい。これにより、有機EL素子の駆動寿命を向上させるとともに、駆動電圧上昇を抑制することができる。また、ドーパントもCH基を有していない方が好ましい。 The light emitting material may be formed of a dopant and a host material. In this case, the charge transport material of the present invention is used as the host material, and the light-emitting layer 5 is preferably a layer formed from the charge transport material of the present invention and the dopant as described above. Furthermore, the light emitting layer 5 is more preferably a layer formed only of the charge transport material and the dopant of the present invention. As a result, the drive life of the organic EL element can be improved and an increase in drive voltage can be suppressed. Further, it is preferable that the dopant also has no CH group.
また、このような場合、燐光発光を示す発光層は、ドーパントとして燐光性ドーパントを含んで形成される。燐光性ドーパントに制限はなく任意のものを用いることができるが、例えば、周期表7ないし11族から選ばれる金属を含む有機金属錯体が挙げられ、該金属錯体のT1(最低励起三重項準位)より高いT1を有する電荷輸送性有機化合物をホスト材料として使用することが好ましい。 In such a case, the light-emitting layer that exhibits phosphorescence is formed including a phosphorescent dopant as a dopant. The phosphorescent dopant is not limited, and any one can be used. For example, an organometallic complex containing a metal selected from Groups 7 to 11 of the periodic table can be used, and T1 (lowest excited triplet level) of the metal complex can be mentioned. It is preferred to use a charge transporting organic compound having a higher T1 as the host material.
周期表7ないし11族から選ばれる金属を含む燐光性有機金属錯体における金属として好ましくは、ルテニウム、ロジウム、パラジウム、銀、レニウム、オスミウム、イリジウム、白金、金等が挙げられる。これらの有機金属錯体として、好ましくは下記式(9)または式(10)で表される化合物が挙げられる。 Preferred examples of the metal in the phosphorescent organometallic complex containing a metal selected from Groups 7 to 11 of the periodic table include ruthenium, rhodium, palladium, silver, rhenium, osmium, iridium, platinum, and gold. As these organometallic complexes, compounds represented by the following formula (9) or formula (10) are preferable.
ML(q-j)L′j ・・・式(9)
{式(9)中、Mは金属を表わし、qは上記金属の価数を表わす。また、L及びL′は二座配位子を表わす。さらに、jは0、1又は2を表わす。}
ぞれ独立に置換基を表わす。ただし、Tが窒素の場合は、R94及びR95は無い。}
ML (qj) L ′ j Expression (9)
{In Formula (9), M represents a metal, and q represents the valence of the metal. L and L ′ represent bidentate ligands. Furthermore, j represents 0, 1 or 2. }
以下、まず、式(9)で表わされる化合物について説明する。
式(9)中、Mは任意の金属を表わし、好ましいものの具体例としては、周期表7ないし11族から選ばれる金属として前述した金属が挙げられる。
また、式(9)中の二座配位子L及びL′は、それぞれ、以下の部分構造を有する配位子を示す。
In formula (9), M represents an arbitrary metal, and specific examples of preferable ones include the metals described above as the metal selected from Groups 7 to 11 of the periodic table.
Moreover, the bidentate ligands L and L ′ in the formula (9) each represent a ligand having the following partial structure.
上記L,L′の部分構造において、環A1″及び環A1′は、それぞれ独立に、芳香族炭化水素基又は芳香族複素環基を表わし、これらは置換基を有していてもよい。また、環A2及び環A2′は、それぞれ独立に、含窒素芳香族複素環基を表わし、これらは置換基を有していてもよい。さらに、R′、R″およびR″′は、それぞれ独立に、ハロゲン原子、アルキル基、アルケニル基、アルコキシカルボニル基、メトキシ基、アルコキシ基、アリールオキシ基、ジアルキルアミノ基、ジアリールアミノ基、カルバゾリル基、アシル基、ハロアルキル基又はシアノ基を表す。 In the partial structures of L and L ′, the ring A1 ″ and the ring A1 ′ each independently represent an aromatic hydrocarbon group or an aromatic heterocyclic group, and these may have a substituent. , Ring A2 and ring A2 ′ each independently represent a nitrogen-containing aromatic heterocyclic group, which may have a substituent. R ′, R ″ and R ″ ′ are each independently Represents a halogen atom, an alkyl group, an alkenyl group, an alkoxycarbonyl group, a methoxy group, an alkoxy group, an aryloxy group, a dialkylamino group, a diarylamino group, a carbazolyl group, an acyl group, a haloalkyl group or a cyano group.
式(9)で表される化合物として、さらに好ましくは、下記式(9a)、(9b)、(9c)で表される化合物が挙げられる。
上記式(9a)、(9b)、(9c)において、環A1″および環A1′としては、好ましくは、例えばフェニル基、ビフェニル基、ナフチル基、アントリル基、チエニル基、フリル基、ベンゾチエニル基、ベンゾフリル基、ピリジル基、キノリル基、イソキノリル基、カルバゾリル基等が挙げられる。 In the above formulas (9a), (9b) and (9c), the ring A1 ″ and the ring A1 ′ are preferably, for example, phenyl group, biphenyl group, naphthyl group, anthryl group, thienyl group, furyl group, benzothienyl group. Benzofuryl group, pyridyl group, quinolyl group, isoquinolyl group, carbazolyl group and the like.
また、環A2、環A2′としては、好ましくは、例えばピリジル基、ピリミジル基、ピラジル基、トリアジル基、ベンゾチアゾール基、ベンゾオキサゾール基、ベンゾイミダゾール基、キノリル基、イソキノリル基、キノキサリル基、フェナントリジル基等が挙げられる。 The ring A2 and ring A2 ′ are preferably, for example, pyridyl group, pyrimidyl group, pyrazyl group, triazyl group, benzothiazole group, benzoxazole group, benzimidazole group, quinolyl group, isoquinolyl group, quinoxalyl group, phenane. A tridyl group etc. are mentioned.
更に、式(9a)、(9b)、(9c)で表される化合物が有していてもよい置換基としては、フッ素原子等のハロゲン原子;メチル基、エチル基等のアルキル基;ビニル基等のアルケニル基;メトキシカルボニル基、エトキシカルボニル基等のアルコキシカルボニル基;メトキシ基、エトキシ基等のアルコキシ基;フェノキシ基、ベンジルオキシ基などのアリールオキシ基;ジメチルアミノ基、ジエチルアミノ基等のジアルキルアミノ基;ジフェニルアミノ基等のジアリールアミノ基;カルバゾリル基;アセチル基等のアシル基;トリフルオロメチル基等のハロアルキル基;シアノ基等が挙げられる。 Furthermore, the substituents that the compounds represented by the formulas (9a), (9b), and (9c) may have include halogen atoms such as fluorine atoms; alkyl groups such as methyl groups and ethyl groups; vinyl groups Alkenyl groups such as methoxycarbonyl group and ethoxycarbonyl group; alkoxy groups such as methoxy group and ethoxy group; aryloxy groups such as phenoxy group and benzyloxy group; dialkylamino groups such as dimethylamino group and diethylamino group A diarylamino group such as a diphenylamino group; a carbazolyl group; an acyl group such as an acetyl group; a haloalkyl group such as a trifluoromethyl group; a cyano group;
また、置換基がアルキル基である場合は、その炭素数は通常1以上6以下である。さらに、置換基がアルケニル基である場合は、その炭素数は通常2以上6以下である。また、置換基がアルコキシカルボニル基である場合は、その炭素数は通常2以上6以下である。さらに、置換基がアルコキシ基である場合は、その炭素数は通常1以上6以下である。また、置換基がアリールオキシ基である場合は、その炭素数は通常6以上14以下である。さらに、置換基がジアルキルアミノ基である場合は、その炭素数は通常2以上24以下である。また、置換基がジアリールアミノ基である場合は、その炭素数は通常12以上28以下である。さらに、置換基がアシル基である場合は、その炭素数は通常1以上14以下である。また、置換基がハロアルキル基である場合は、その炭素数は通常1以上12以下である。 Moreover, when a substituent is an alkyl group, the carbon number is 1 or more and 6 or less normally. Furthermore, when the substituent is an alkenyl group, the carbon number is usually 2 or more and 6 or less. When the substituent is an alkoxycarbonyl group, the carbon number is usually 2 or more and 6 or less. Further, when the substituent is an alkoxy group, the carbon number is usually 1 or more and 6 or less. Moreover, when a substituent is an aryloxy group, the carbon number is 6 or more and 14 or less normally. Furthermore, when the substituent is a dialkylamino group, the carbon number is usually 2 or more and 24 or less. Further, when the substituent is a diarylamino group, the carbon number is usually 12 or more and 28 or less. Furthermore, when the substituent is an acyl group, the carbon number is usually 1 or more and 14 or less. Moreover, when a substituent is a haloalkyl group, the carbon number is 1 or more and 12 or less normally.
なお、これら置換基は互いに連結して環を形成しても良い。具体例としては、環A1″が有する置換基と環A2が有する置換基とが結合するか、または、環A1′が有する置換基と環A2′が有する置換基とが結合するかして、一つの縮合環を形成してもよい。このような縮合環としては、7,8−ベンゾキノリン基等が挙げられる。
中でも、環A1″、環A1′、環A2及び環A2′の置換基として、より好ましくはアルキル基、アルコキシ基、芳香族炭化水素基、シアノ基、ハロゲン原子、ハロアルキル基、ジアリールアミノ基、カルバゾリル基が挙げられる。
These substituents may be connected to each other to form a ring. As a specific example, a substituent of the ring A1 ″ and a substituent of the ring A2 are bonded, or a substituent of the ring A1 ′ and a substituent of the ring A2 ′ are bonded, One condensed ring may be formed, such as a 7,8-benzoquinoline group.
Among them, as a substituent for ring A1 ″, ring A1 ′, ring A2 and ring A2 ′, an alkyl group, alkoxy group, aromatic hydrocarbon group, cyano group, halogen atom, haloalkyl group, diarylamino group, carbazolyl are more preferable. Groups.
また、式(9a)、(9b)、(9c)におけるM4,M5として好ましくは、ルテニウム、ロジウム、パラジウム、銀、レニウム、オスミウム、イリジウム、白金または金が挙げられる。
上記式(9)、(9a)、(9b)又は(9c)で示される有機金属錯体の具体例を以下に示す。ただし、ドーパントは下記の化合物に限定されるものではない。
Further, M 4 and M 5 in the formulas (9a), (9b), and (9c) are preferably ruthenium, rhodium, palladium, silver, rhenium, osmium, iridium, platinum, or gold.
Specific examples of the organometallic complex represented by the above formula (9), (9a), (9b) or (9c) are shown below. However, the dopant is not limited to the following compounds.
さらに、上記式(9)、(9a)、(9b)、(9c)で表される有機金属錯体の中でも、特に、配位子L及び/又はL′として2−アリールピリジン系配位子、即ち、2−アリールピリジン、これに任意の置換基が結合したもの、及び、これに任意の基が縮合してなるものを有する化合物が好ましい。 Furthermore, among the organometallic complexes represented by the above formulas (9), (9a), (9b), and (9c), in particular, as the ligand L and / or L ′, a 2-arylpyridine-based ligand, That is, a compound having 2-arylpyridine, a compound in which an arbitrary substituent is bonded thereto, and a compound in which an arbitrary group is condensed to this is preferable.
次に、式(10)で表わされる化合物について説明する。
式(10)中、M7は金属を表わし、具体例としては、周期表7ないし11族から選ばれる金属として前述した金属が挙げられる。中でも好ましくは、ルテニウム、ロジウム、パラジウム、銀、レニウム、オスミウム、イリジウム、白金または金が挙げられ、特に好ましくは、白金、パラジウム等の2価の金属が挙げられる。
Next, the compound represented by formula (10) will be described.
In the formula (10), M 7 represents a metal, and specific examples thereof include the metals described above as the metal selected from Groups 7 to 11 of the periodic table. Among these, ruthenium, rhodium, palladium, silver, rhenium, osmium, iridium, platinum or gold is preferable, and divalent metals such as platinum and palladium are particularly preferable.
また、式(10)において、R92及びR93は、それぞれ独立に、水素原子、ハロゲン原子、アルキル基、アラルキル基、アルケニル基、シアノ基、アミノ基、アシル基、アルコキシカルボニル基、カルボキシル基、アルコキシ基、アルキルアミノ基、アラルキルアミノ基、ハロアルキル基、水酸基、アリールオキシ基、芳香族炭化水素基または芳香族複素環基を表わす。 In the formula (10), R 92 and R 93 each independently represent a hydrogen atom, a halogen atom, an alkyl group, an aralkyl group, an alkenyl group, a cyano group, an amino group, an acyl group, an alkoxycarbonyl group, a carboxyl group, Represents an alkoxy group, an alkylamino group, an aralkylamino group, a haloalkyl group, a hydroxyl group, an aryloxy group, an aromatic hydrocarbon group or an aromatic heterocyclic group;
さらに、Tが炭素の場合、R94及びR95は、それぞれ独立に、R92及びR93と同様の例示物で表わされる置換基を表わす。また、Tが窒素の場合はR94及びR95は無い。
また、R92〜R95はさらに置換基を有していてもよい。さらに有していてもよい置換基に制限はなく、任意の基を置換基とすることができる。
さらに、R92〜R95は互いに連結して環を形成してもよい。
Further, when T is carbon, R 94 and R 95 each independently represent a substituent represented by the same examples as R 92 and R 93 . Further, when T is nitrogen, there is no R 94 or R 95 .
R 92 to R 95 may further have a substituent. Furthermore, there is no restriction | limiting in the substituent which you may have and arbitrary groups can be used as a substituent.
Further, R 92 to R 95 may be connected to each other to form a ring.
式(10)で表わされる有機金属錯体の具体例(T−1,T−10〜T−15)を以下に示す。ただし、ドーパントは、下記の例示物に限定されるものではない。また、Meはメチル基を表わし、Etはエチル基を表わす。 Specific examples (T-1, T-10 to T-15) of the organometallic complex represented by the formula (10) are shown below. However, the dopant is not limited to the following examples. Me represents a methyl group, and Et represents an ethyl group.
また、前述したように、感光層に使用されるホスト材料としては、本発明の電荷輸送材料を用いることが好ましい。 As described above, the charge transport material of the present invention is preferably used as the host material used in the photosensitive layer.
さらに、ホスト材料としては、適宜、本発明の電荷輸送材料以外の材料を用いてもよい。本発明の電荷輸送材料以外のホスト材料としては、燐光性ドーパントに対するホスト材料として、例えば、トリス(8−ヒドロキシキノリン)アルミニウム(米国特許第63030238号明細書)、2,2′,2″−(1,3,5−ベンゼントリル)トリス[1−フェニル−1H−ベンズイミダゾール](Appl.Phys.Lett.,78巻,1622項,2001)、ポリビニルカルバゾール(特開2001−257076号公報)等が挙げられる。 Furthermore, as the host material, a material other than the charge transport material of the present invention may be used as appropriate. As a host material other than the charge transport material of the present invention, as a host material for a phosphorescent dopant, for example, tris (8-hydroxyquinoline) aluminum (US Pat. No. 6,030,238), 2,2 ′, 2 ″-( 1,3,5-benzenetolyl) tris [1-phenyl-1H-benzimidazole] (Appl. Phys. Lett., 78, 1622, 2001), polyvinyl carbazole (JP 2001-257076 A) and the like. Can be mentioned.
なお、発光材料は、1種を単独で用いてもよく、2種以上を任意の組み合わせ及び比率で併用してもよい。したがって、発光材料としてドーパント及びホスト材料を用いる場合には、ドーパント及びホスト材料は、それぞれ独立に、1種を単独で用いてもよく、2種以上を任意の組み合わせ及び比率で併用してもよい。 In addition, a luminescent material may be used individually by 1 type, and may use 2 or more types together by arbitrary combinations and a ratio. Therefore, when a dopant and a host material are used as the light emitting material, the dopant and the host material may be used independently, or two or more may be used in any combination and ratio. .
また、本発明の有機EL素子における発光層は、ホスト材料及びドーパント以外の添加物を含有していてもよい。例えば、燐光発光を示す発光層において、任意の蛍光色素を含有していてもよい。
さらに、発光層中にドーパントとして含有される有機金属錯体の量は、通常0.1重量%以上、好ましくは1重量%以上、また、通常30重量%以下、好ましくは10重量%以下が望ましい。下限値を下回ると有機EL素子の発光効率向上に寄与できない場合があり、上限値を上回ると有機金属錯体同士が2量体を形成する等の理由で濃度消光が生じ、発光効率の低下に至る可能性がある。
Moreover, the light emitting layer in the organic EL element of this invention may contain additives other than a host material and a dopant. For example, the light emitting layer that emits phosphorescence may contain any fluorescent dye.
Furthermore, the amount of the organometallic complex contained as a dopant in the light emitting layer is usually 0.1% by weight or more, preferably 1% by weight or more, and usually 30% by weight or less, preferably 10% by weight or less. If the lower limit is not reached, it may not be possible to contribute to the improvement of the light emission efficiency of the organic EL device. there is a possibility.
また、燐光発光を示す発光層における燐光性ドーパントの量は、蛍光(1重項)を用いた有機EL素子において、発光層に含有されるドーパント(蛍光色素)の量より、若干多い方が好ましい傾向がある。また、燐光性ドーパントと共に蛍光色素が発光層中に含有される場合、蛍光色素の量は、0.05重量%以上が好ましく、0.1重量%以上がより好ましい。また10重量%以下が好ましく、3重量%以下がより好ましい。 In addition, the amount of the phosphorescent dopant in the light emitting layer exhibiting phosphorescence is preferably slightly larger than the amount of the dopant (fluorescent dye) contained in the light emitting layer in the organic EL element using fluorescence (singlet). Tend. Moreover, when a fluorescent pigment | dye is contained in a light emitting layer with a phosphorescent dopant, 0.05 weight% or more is preferable and 0.1 weight% or more is more preferable. Moreover, 10 weight% or less is preferable and 3 weight% or less is more preferable.
発光層5の形成方法は任意であり、例えば、正孔輸送層4と同様の方法で形成することができる。
塗布法により発光層5を形成する場合は、ホスト材料及びドーパントなどの発光材料と、さらに必要に応じて、電子のトラップや発光の消光剤とならないバインダー樹脂と、レベリング剤等の塗布性改良剤などの添加剤とを混合し、溶媒又は分散媒に溶解又は分散した塗布液を調整する。その後、調製した塗布液をスピンコート法などの方法により正孔輸送層4上に塗布し、溶媒又は分散媒を乾燥、除去して発光層5を形成する。
The formation method of the light emitting layer 5 is arbitrary, For example, it can form by the method similar to the hole transport layer 4.
When the light-emitting layer 5 is formed by a coating method, a light-emitting material such as a host material and a dopant, a binder resin that does not become an electron trap or a light-extinguishing quencher, and a coating agent for improving the coating properties such as a leveling agent. Etc. are mixed to prepare a coating solution dissolved or dispersed in a solvent or dispersion medium. Thereafter, the prepared coating solution is applied onto the hole transport layer 4 by a method such as spin coating, and the solvent or dispersion medium is dried and removed to form the light emitting layer 5.
溶媒及び分散媒は、正孔輸送層4と同様、発光材料等の種類に応じて、任意のものを用いればよい。
また、バインダー樹脂の種類や使用量、添加剤などについても、正孔輸送層4の場合と同様である。さらに、発光材料としてドーパント及びホスト材料を用い、更に、バインダー樹脂や添加剤を用いる場合、バインダー樹脂や添加剤の酸化電位が+0.8V以上であるときには、ドーパントを除き発光層5に含まれるCH基の存在割合を70ppm以下とすることができるのであれば、ホスト材料、バインダー樹脂、添加剤などをまとめて、本発明の電荷輸送材料とみなすこともできる。これにより、バインダー樹脂や添加剤などのホスト材料以外の材料を用いた場合でも、発光層5を、本発明の電荷輸送材料及びドーパントからなる層として形成することが可能となる。
Any solvent and dispersion medium may be used in the same manner as the hole transport layer 4 depending on the type of the light emitting material and the like.
In addition, the type and amount of binder resin used, and additives are the same as in the case of the hole transport layer 4. Further, when a dopant and a host material are used as the light emitting material, and further a binder resin or additive is used, when the oxidation potential of the binder resin or additive is +0.8 V or more, the CH contained in the light emitting layer 5 except for the dopant is included. If the group content can be 70 ppm or less, the host material, the binder resin, the additive, and the like can be collectively regarded as the charge transport material of the present invention. Accordingly, even when a material other than the host material such as a binder resin or an additive is used, the light emitting layer 5 can be formed as a layer made of the charge transport material and the dopant of the present invention.
一方、真空蒸着法の場合には、正孔輸送層4上に発光材料を蒸着させて、発光層5を形成する。具体的操作の一例として、発光材料としてホスト材料とドーパントとを用いた場合について説明すると、ホスト材料を真空容器内に設置されたるつぼに入れ、また、ドーパントを別のるつぼに入れて、真空容器内を適当な真空ポンプで1.0×10-4Torr程度にまで排気する。その後、各々のるつぼを同時に加熱してホスト材料及びドーパントを蒸発させて、るつぼと向かい合って置かれた基板1の正孔輸送層4上に発光層5を形成する。また、他の操作の例として、発光材料としてホスト材料とドーパントとを予め所定比で混合したものを用意し、その発光材料を同一のるつぼを用いて蒸発させてもよい。 On the other hand, in the case of the vacuum vapor deposition method, a light emitting material is deposited on the hole transport layer 4 to form the light emitting layer 5. As an example of a specific operation, the case where a host material and a dopant are used as a light emitting material will be described. The host material is put in a crucible installed in a vacuum vessel, and the dopant is put in another crucible, The inside is evacuated to about 1.0 × 10 −4 Torr with a suitable vacuum pump. Thereafter, each crucible is heated at the same time to evaporate the host material and the dopant, thereby forming a light emitting layer 5 on the hole transport layer 4 of the substrate 1 placed facing the crucible. As another example of the operation, a light emitting material prepared by mixing a host material and a dopant in a predetermined ratio in advance may be prepared, and the light emitting material may be evaporated using the same crucible.
ところで、ドーパントを発光層5にドープした場合、通常は発光層5の膜厚方向において均一にドープされるが、膜厚方向において濃度分布があっても構わない。例えば、正孔輸送層4との界面近傍にのみドーパントをドープしたり、逆に、正孔阻止層6界面近傍にのみドーパントをドープしてもよい。
さらに、発光層5の膜厚は任意であるが、通常3nm以上、好ましくは5nm以上、より好ましくは10nm以上、さらに好ましくは20nm以上、また、通常200nm以下、好ましくは100nm以下である。また、発光層5も正孔輸送層4と同様、通常は真空蒸着法により形成される。
By the way, when the dopant is doped into the light emitting layer 5, it is normally doped uniformly in the film thickness direction of the light emitting layer 5, but there may be a concentration distribution in the film thickness direction. For example, the dopant may be doped only in the vicinity of the interface with the hole transport layer 4, or conversely, the dopant may be doped only in the vicinity of the interface of the hole blocking layer 6.
Furthermore, although the film thickness of the light emitting layer 5 is arbitrary, it is usually 3 nm or more, preferably 5 nm or more, more preferably 10 nm or more, further preferably 20 nm or more, and usually 200 nm or less, preferably 100 nm or less. Similarly to the hole transport layer 4, the light emitting layer 5 is usually formed by a vacuum deposition method.
<5.正孔阻止層>
発光層5の上には、正孔阻止層6が設けられている。この正孔阻止層6は、正孔輸送層4から移動してくる正孔が陰極8に到達するのを阻止し、陰極8から注入された電子を効率よく発光層5の方向に輸送するために設けられる。よって、正孔阻止層6の材料(以下適宜「正孔阻止材料」という)に要求される条件としては、電子移動度が高く正孔移動度が低いことが必要である。これにより、正孔阻止層6は正孔と電子とを発光層5内に閉じ込めて、有機EL素子の発光効率を向上させることができるようになる。
<5. Hole blocking layer>
A hole blocking layer 6 is provided on the light emitting layer 5. The hole blocking layer 6 prevents holes moving from the hole transport layer 4 from reaching the cathode 8 and efficiently transports electrons injected from the cathode 8 toward the light emitting layer 5. Is provided. Therefore, as a condition required for the material of the hole blocking layer 6 (hereinafter referred to as “hole blocking material” as appropriate), it is necessary that the electron mobility is high and the hole mobility is low. Accordingly, the hole blocking layer 6 can confine holes and electrons in the light emitting layer 5 and improve the light emission efficiency of the organic EL element.
上記の観点から、正孔阻止材料のイオン化ポテンシャルは、発光層5の発光材料のイオン化ポテンシャル(発光層5がホスト材料とドーパントとを含んでいる場合には、ドーパントのイオン化ポテンシャル)よりも通常0.1eV以上、好ましくは0.5eV以上大きいことが好ましい。さらに、この場合、ドーパントのイオン化ポテンシャルは、ホスト材料のイオン化ポテンシャルよりも、通常0.1eV以上、好ましくは0.3eV以上小さいことがより好ましい。 From the above viewpoint, the ionization potential of the hole blocking material is usually 0 than the ionization potential of the light emitting material of the light emitting layer 5 (or the ionization potential of the dopant when the light emitting layer 5 includes a host material and a dopant). 0.1 eV or more, preferably 0.5 eV or more. Furthermore, in this case, the ionization potential of the dopant is usually 0.1 eV or more, more preferably 0.3 eV or more smaller than the ionization potential of the host material.
イオン化ポテンシャルは、物質のHOMO(最高被占分子軌道)レベルにある電子を真空準位に放出するのに必要なエネルギーで定義される。イオン化ポテンシャルは光電子分光法で直接定義されるが、電気化学的に測定した酸化電位を基準電極に対して補正しても求められる。後者の方法の場合、例えば飽和甘コウ電極(SCE)を基準電極として用いたとき、下記式(11)で定義される(“Molecular Semiconductors”,Springer−Verlag,1985年、98頁)。
イオン化ポテンシャル=酸化電位(vs.SCE)+4.3eV ・・・式(11)
The ionization potential is defined as the energy required to emit electrons at the HOMO (highest occupied molecular orbital) level of a substance to the vacuum level. The ionization potential is directly defined by photoelectron spectroscopy, but can also be obtained by correcting the electrochemically measured oxidation potential with respect to the reference electrode. In the case of the latter method, for example, when a saturated sweet potato electrode (SCE) is used as a reference electrode, it is defined by the following formula (11) (“Molecular Semiconductors”, Springer-Verlag, 1985, page 98).
Ionization potential = oxidation potential (vs. SCE) +4.3 eV (11)
さらに、正孔阻止材料の電子親和力(EA)は、発光層5の電子親和力(発光層5がホスト材料とドーパントとを含んでいる場合には、ホスト材料の電子親和力)と比較して同等以上であることが好ましい。電子親和力も、イオン化ポテンシャルと同様に、真空準位を基準として、真空準位にある電子が物質のLUMO(最低空分子軌道)レベルに落ちて安定化するエネルギーで定義される。電子親和力は、前述のイオン化ポテンシャルから光学的バンドギャップを差し引いて求められるが、電気化学的な還元電位から下記式(12)を用いても求められる。
電子親和力=還元電位(vs.SCE)+4.3eV ・・・式(12)
Furthermore, the electron affinity (EA) of the hole blocking material is equal to or greater than the electron affinity of the light emitting layer 5 (in the case where the light emitting layer 5 contains a host material and a dopant, the electron affinity of the host material). It is preferable that Similarly to the ionization potential, the electron affinity is also defined by the energy at which the electrons at the vacuum level fall to the LUMO (lowest empty molecular orbital) level of the substance and stabilize with respect to the vacuum level. The electron affinity can be obtained by subtracting the optical band gap from the above-mentioned ionization potential, but can also be obtained from the electrochemical reduction potential using the following formula (12).
Electron affinity = reduction potential (vs. SCE) +4.3 eV (12)
したがって、正孔阻止材料の酸化電位及び還元電位は、下記式(13),(14)のように表わすこともできる。
(正孔阻止材料の酸化電位)−(発光材料の酸化電位)≧0.1V ・・・式(13)
(正孔阻止材料の還元電位)≧(発光材料の還元電位) ・・・式(14)
Therefore, the oxidation potential and reduction potential of the hole blocking material can also be expressed as in the following formulas (13) and (14).
(Oxidation potential of hole blocking material) − (oxidation potential of light emitting material) ≧ 0.1 V (13)
(Reduction potential of hole blocking material) ≧ (Reduction potential of light emitting material) Formula (14)
さらに、後述の電子輸送層7を有する有機EL素子においては、正孔阻止材料の電子親和力は、電子輸送層7の材料(以下適宜「電子輸送材料」という)の電子親和力と比較して、下記式(15)で表わすように、同等以下であることが好ましい。
(電子輸送材料の還元電位)≧(正孔阻止材料の還元電位)≧(発光材料の還元電位)
・・・式(15)
Furthermore, in the organic EL device having the electron transport layer 7 described later, the electron affinity of the hole blocking material is as follows compared to the electron affinity of the material of the electron transport layer 7 (hereinafter referred to as “electron transport material” as appropriate). As represented by Formula (15), it is preferable that they are equal or less.
(Reduction potential of electron transport material) ≧ (Reduction potential of hole blocking material) ≧ (Reduction potential of light emitting material)
... Formula (15)
前述のように、正孔阻止層7の材料である正孔阻止材料として、本発明の電荷輸送材料を用いることができる。この際、正孔阻止材料として本発明の電荷輸送材料に無機材料からなる電荷輸送材料を混合して用いても良いが、通常は、本発明の電荷輸送材料のみを用い、正孔阻止層7を、本発明の電荷輸送材料のみからなる層として形成することが望ましい。これにより、有機EL素子の駆動寿命を向上させるとともに、駆動電圧上昇を抑制することができる。また、この場合、正孔阻止材料として用いることができる化合物の具体例としては、電荷輸送材料として好ましい化合物の具体例として例示したものと同様のものが挙げられる。 As described above, the charge transport material of the present invention can be used as the hole blocking material that is the material of the hole blocking layer 7. At this time, as the hole blocking material, the charge transporting material of the present invention may be mixed with the charge transporting material made of an inorganic material. However, normally, only the charge transporting material of the present invention is used and the hole blocking layer 7 is used. Is preferably formed as a layer made of only the charge transport material of the present invention. As a result, the drive life of the organic EL element can be improved and an increase in drive voltage can be suppressed. Further, in this case, specific examples of the compound that can be used as the hole blocking material include the same compounds as those exemplified as specific examples of the preferable compound as the charge transport material.
また、本発明の電荷輸送材料以外に正孔阻止材料として用いることができるものとしては、例えば、下記式(16)で表わされる混合配位子錯体が挙げられる。
さらに、L3は、以下に示す式(17a)、(17b)、(17c)のいずれかで表され
る配位子を表わす。
In addition to the charge transport material of the present invention, examples of materials that can be used as a hole blocking material include mixed ligand complexes represented by the following formula (16).
Furthermore, L 3 represents a ligand represented by any of the following formulas (17a), (17b), and (17c).
前記式(16)において、R16〜R21はそれぞれ独立して水素原子又は任意の置換基を表わす。ただし、好ましくは、水素原子;塩素、臭素等のハロゲン原子;メチル基、エチル基等のアルキル基;ベンジル基等のアラルキル基;ビニル基等のアルケニル基;シアノ基;アミノ基;アシル基;メトキシ基、エトキシ基等のアルコキシ基;メトキシカルボニル基、エトキシカルボニル基等のアルコキシカルボニル基;カルボキシル基;フェノキシ基、ベンジルオキシ基などのアリールオキシ基;ジエチルアミノ基、ジイソプロピルアミノ基等のジアルキルアミノ基;ジベンジルアミノ基、ジフェネチルアミノ基などのジアラルキルアミノ基;トリフルオロメチル基等のα−ハロアルキル基;水酸基;置換基を有していても良い、フェニル基、ナフチル基等の芳香族炭化水素基;置換基を有していても良い、チエニル基、ピリジル基等の芳香族複素環基を表わす。 In the formula (16), R 16 to R 21 each independently represents a hydrogen atom or an arbitrary substituent. However, preferably, a hydrogen atom; a halogen atom such as chlorine or bromine; an alkyl group such as a methyl group or an ethyl group; an aralkyl group such as a benzyl group; an alkenyl group such as a vinyl group; a cyano group; an amino group; Group, alkoxy group such as ethoxy group; alkoxycarbonyl group such as methoxycarbonyl group and ethoxycarbonyl group; carboxyl group; aryloxy group such as phenoxy group and benzyloxy group; dialkylamino group such as diethylamino group and diisopropylamino group; Diaralkylamino groups such as benzylamino group and diphenethylamino group; α-haloalkyl groups such as trifluoromethyl group; hydroxyl groups; optionally substituted aromatic hydrocarbon groups such as phenyl group and naphthyl group A fragrance such as thienyl group and pyridyl group which may have a substituent It represents a heterocyclic group.
なお、R16〜R21がアルキル基の場合、その炭素数は通常1以上6以下である。さらに、R16〜R21がアラルキル基の場合、その炭素数は通常7以上12以下である。また、R16〜R21がアルケニル基である場合は、その炭素数は通常2以上6以下である。さらに、R16〜R21がアシル基の場合、その炭素数は通常1以上14以下である。また、R16〜R21がアルコキシ基である場合は、その炭素数は通常1以上6以下である。さらに、R16〜R21がアルコキシカルボニル基である場合は、その炭素数は通常2以上6以下である。また、R16〜R21ががアリールオキシ基の場合、その炭素数は通常6以上14以下である。さらに、R16〜R21がジアルキルアミノ基の場合、その炭素数は通常2以上16以下である。また、R16〜R21がジアラルキルアミノ基の場合、その炭素数は通常14以上24以下である。さらに、R16〜R21がα−ハロアルキル基の場合、その炭素数は通常1以上8以下である。また、R16〜R21が芳香族炭化水素基の場合、その炭素数は通常6以上18以下である。さらに、R16〜R21が芳香族複素環基の場合、その炭素数は通常2以上17以下である。 In addition, when R < 16 > -R < 21 > is an alkyl group, the carbon number is 1 or more and 6 or less normally. Furthermore, when R 16 to R 21 are an aralkyl group, the carbon number is usually 7 or more and 12 or less. Moreover, when R < 16 > -R < 21 > is an alkenyl group, the carbon number is 2 or more and 6 or less normally. Further, when R 16 to R 21 are acyl groups, the carbon number is usually 1 or more and 14 or less. Moreover, when R < 16 > -R < 21 > is an alkoxy group, the carbon number is 1 or more and 6 or less normally. Further, when R 16 to R 21 are alkoxycarbonyl groups, the carbon number is usually 2 or more and 6 or less. Further, when R 16 to R 21 is an aryl group, and the number of carbon atoms is usually 6 to 14. Furthermore, when R 16 to R 21 are dialkylamino groups, the carbon number is usually 2 or more and 16 or less. Further, when R 16 to R 21 is a di-aralkylamino groups, the carbon number is usually 14 or more 24 or less. Furthermore, when R 16 to R 21 are α-haloalkyl groups, the carbon number is usually 1 or more and 8 or less. Further, when R 16 to R 21 is an aromatic hydrocarbon group, the carbon number is usually 6 to 18. Furthermore, when R 16 to R 21 are aromatic heterocyclic groups, the carbon number is usually 2 or more and 17 or less.
また、R16〜R21が芳香族炭化水素基又は芳香族複素環基である場合、その芳香族炭化水素基及び芳香族複素環基が有しうる置換基としては、上記の式(9a)、(9b)、(9c)で表される化合物が有していてもよい置換基として例示したものと同様の置換基が挙げられる。即ち、フッ素原子等のハロゲン原子;メチル基、エチル基等のアルキル基;ビニル基等のアルケニル基;メトキシカルボニル基、エトキシカルボニル基等のアルコキシカルボニル基;メトキシ基、エトキシ基等のアルコキシ基;フェノキシ基、ベンジルオキシ基などのアリールオキシ基;ジメチルアミノ基、ジエチルアミノ基等のジアルキルアミノ基;ジフェニルアミノ基等のジアリールアミノ基;カルバゾリル基;アセチル基等のアシル基;トリフルオロメチル基等のハロアルキル基;シアノ基等が挙げられる。 Moreover, when R < 16 > -R < 21 > is an aromatic hydrocarbon group or an aromatic heterocyclic group, as a substituent which the aromatic hydrocarbon group and aromatic heterocyclic group may have, said formula (9a) , (9b), and the substituents similar to those exemplified as the substituents that the compound represented by (9c) may have. A halogen atom such as a fluorine atom; an alkyl group such as a methyl group or an ethyl group; an alkenyl group such as a vinyl group; an alkoxycarbonyl group such as a methoxycarbonyl group or an ethoxycarbonyl group; an alkoxy group such as a methoxy group or an ethoxy group; Group, aryloxy group such as benzyloxy group; dialkylamino group such as dimethylamino group and diethylamino group; diarylamino group such as diphenylamino group; carbazolyl group; acyl group such as acetyl group; haloalkyl group such as trifluoromethyl group A cyano group and the like.
また、R16〜R21が芳香族炭化水素基又は芳香族複素環基である場合に、その芳香族炭化水素基及び芳香族複素環基が有しうる置換基の炭素数も、上記の式(9a)、(9b)、(9c)で表される化合物が有する置換基の説明において述べた置換基の炭素数と、ジアルキルアミノ基及びハロアルキル基を除いて同様である。即ち、置換基がアルキル基である場合は、その炭素数は通常1以上6以下である。さらに、置換基がアルケニル基である場合は、その炭素数は通常2以上6以下である。また、置換基がアルコキシカルボニル基である場合は、その炭素数は通常2以上6以下である。さらに、置換基がアルコキシ基である場合は、その炭素数は通常1以上6以下である。また、置換基がアリールオキシ基である場合は、その炭素数は通常6以上14以下である。さらに、置換基がジアルキルアミノ基である場合は、その炭素数は通常2以上16以下である。また、置換基がジアリールアミノ基である場合は、その炭素数は通常12以上28以下である。さらに、置換基がアシル基である場合は、その炭素数は通常1以上14以下である。また、置換基がハロアルキル基である場合は、その炭素数は通常1以上8以下である。 In addition, when R 16 to R 21 are an aromatic hydrocarbon group or an aromatic heterocyclic group, the carbon number of the substituent that the aromatic hydrocarbon group and the aromatic heterocyclic group may have is also the above formula. The same applies to the number of carbon atoms of the substituent described in the description of the substituent of the compound represented by (9a), (9b), or (9c), except for the dialkylamino group and the haloalkyl group. That is, when the substituent is an alkyl group, the carbon number is usually 1 or more and 6 or less. Furthermore, when the substituent is an alkenyl group, the carbon number is usually 2 or more and 6 or less. When the substituent is an alkoxycarbonyl group, the carbon number is usually 2 or more and 6 or less. Further, when the substituent is an alkoxy group, the carbon number is usually 1 or more and 6 or less. Moreover, when a substituent is an aryloxy group, the carbon number is 6 or more and 14 or less normally. Furthermore, when the substituent is a dialkylamino group, the carbon number is usually 2 or more and 16 or less. Further, when the substituent is a diarylamino group, the carbon number is usually 12 or more and 28 or less. Furthermore, when the substituent is an acyl group, the carbon number is usually 1 or more and 14 or less. Moreover, when a substituent is a haloalkyl group, the carbon number is 1 or more and 8 or less normally.
ただし、R16〜R21としてより好ましくは、水素原子、アルキル基、ハロゲン原子、シアノ基等が挙げられる。また特に、R19としては、シアノ基がさらに好ましい。
また、上記式(17a),(17b),(17c)中、Ar11〜Ar15として、具体的には、フェニル基、ビフェニル基、ナフチル基等の芳香族炭化水素基、又は、チエニル基、ピリジル基等の芳香族複素環基を表わす。なお、これらAr11〜Ar15はさらに置換基を有していてもよい。その置換基は、R16〜R21が芳香族炭化水素基又は芳香族複素環基である場合、その芳香族炭化水素基及び芳香族複素環基が有しうる置換基として示したものと同様のものが挙げられる。
However, R 16 to R 21 are more preferably a hydrogen atom, an alkyl group, a halogen atom, a cyano group, or the like. In particular, R 19 is more preferably a cyano group.
Further, in the above formula (17a), (17b), (17c), as Ar 11 to Ar 15, specifically, a phenyl group, a biphenyl group, an aromatic hydrocarbon group such as a naphthyl group, or a thienyl group, Represents an aromatic heterocyclic group such as a pyridyl group; In addition, these Ar < 11 > -Ar < 15 > may have a substituent further. When R 16 to R 21 are an aromatic hydrocarbon group or an aromatic heterocyclic group, the substituent is the same as that shown as the substituent that the aromatic hydrocarbon group and the aromatic heterocyclic group may have. Can be mentioned.
上記式(16)で表わされる化合物の好ましい具体例(HB−1〜HB−20)を以下に示す。ただし、正孔阻止材料となりうる化合物は、下記の化合物に限定されるものではない。
さらに、正孔阻止材料としては、上記式(16)で表わされる混合配位子錯体の他に、以下の式(18)で示される1,2,4−トリアゾール環残基を、少なくとも1個有する化合物を用いることができる。
上記式(18)で表わされる1,2,4−トリアゾール環残基を、少なくとも1個有する化合物の具体例を以下に示す。ただし、1,2,4−トリアゾール環残基を少なくとも1個有する化合物は、下記の例示物に限定されるものではない。なお、t−Buはt−ブチル基を表わす。 Specific examples of the compound having at least one 1,2,4-triazole ring residue represented by the above formula (18) are shown below. However, the compound having at least one 1,2,4-triazole ring residue is not limited to the following examples. T-Bu represents a t-butyl group.
また、更に別の正孔阻止材料として、下記式(19)で示されるフェナントロリン環を少なくとも1個有する化合物が挙げられる。
上記式(19)で表わされるフェナントロリン環を少なくとも1個有する化合物の具体例を以下に示す。ただし、フェナントロリン環を少なくとも1個有する化合物は、下記の例示物に限定されるものではない。 Specific examples of the compound having at least one phenanthroline ring represented by the above formula (19) are shown below. However, the compound having at least one phenanthroline ring is not limited to the following examples.
なお、正孔阻止材料は、1種の化合物を単独で用いてもよく、2種以上を任意の組み合わせ及び比率で併用してもよい。
正孔阻止層6の形成方法は任意であるが、通常は、正孔輸送層4と同様、塗布法又は真空蒸着法により形成することができる。
塗布法により正孔阻止層6を形成する場合は、正孔輸送材料に代えて正孔阻止材料を用いるほかは、正孔輸送層4の形成と同様にして層形成を行なうことができる。また、バインダー樹脂や添加剤として適当なものを用いることで、正孔阻止層6を、本発明の電荷輸送材料のみからなる層として形成することが可能となることも同様である。
As the hole blocking material, one type of compound may be used alone, or two or more types may be used in any combination and ratio.
Although the formation method of the hole-blocking layer 6 is arbitrary, it can usually be formed by a coating method or a vacuum evaporation method as in the case of the hole-transporting layer 4.
When the hole blocking layer 6 is formed by a coating method, the layer formation can be performed in the same manner as the hole transporting layer 4 except that a hole blocking material is used instead of the hole transporting material. Similarly, the hole blocking layer 6 can be formed as a layer made of only the charge transport material of the present invention by using an appropriate binder resin or additive.
一方、真空蒸着法により正孔阻止層6を形成する場合も、正孔輸送材料に代えて正孔阻止材料を用い、陽極2上に代えて発光層5上に蒸着を行なう他は、正孔輸送層4の形成と同様にして層形成を行なうことができる。
また、正孔阻止層6の膜厚は任意であるが、通常0.3nm以上、好ましくは0.5nm以上、また、通常100nm以下、好ましくは50nm以下である。さらに、正孔阻止層6も正孔輸送層4と同様、通常は真空蒸着法で形成される。
On the other hand, when the hole blocking layer 6 is formed by the vacuum evaporation method, the hole blocking material is used instead of the hole transporting material, and the evaporation is performed on the light emitting layer 5 instead of the anode 2. Layer formation can be performed in the same manner as the formation of the transport layer 4.
The thickness of the hole blocking layer 6 is arbitrary, but is usually 0.3 nm or more, preferably 0.5 nm or more, and usually 100 nm or less, preferably 50 nm or less. Further, the hole blocking layer 6 is usually formed by a vacuum deposition method, similarly to the hole transport layer 4.
<6.陰極>
正孔阻止層6上(又は、後述する電子輸送層7上)には、陰極8が設けられる。陰極8は、正孔阻止層6を介して発光層5に電子を注入する役割を果たすものである。
この陰極8の材質は任意であるが、通常、陽極2に使用される材料を用いることが可能である。ただし、効率よく電子注入を行なうには、仕事関数の低い金属が好ましい。この観点から、通常は、スズ、マグネシウム、インジウム、カルシウム、アルミニウム、銀等の適当な金属、又はそれらの合金が用いられる。合金の具体例としては、マグネシウム−銀合金、マグネシウム−インジウム合金、アルミニウム−リチウム合金等の低仕事関数合金が挙げられる。
<6. Cathode>
A cathode 8 is provided on the hole blocking layer 6 (or on an electron transport layer 7 described later). The cathode 8 serves to inject electrons into the light emitting layer 5 through the hole blocking layer 6.
The material of the cathode 8 is arbitrary, but the material used for the anode 2 can be usually used. However, a metal having a low work function is preferable for efficient electron injection. From this viewpoint, usually, a suitable metal such as tin, magnesium, indium, calcium, aluminum, silver, or an alloy thereof is used. Specific examples of the alloy include low work function alloys such as a magnesium-silver alloy, a magnesium-indium alloy, and an aluminum-lithium alloy.
さらに、陰極8と正孔阻止層6(又は、後述する電子輸送層7上)との界面にLiF、MgF2、Li2O等の極薄絶縁膜(0.1nm〜5nm)を挿入することも、有機EL素子の効率を向上させる有効な方法である(Appl.Phys.Lett.,70巻,152頁,1997年;特開平10−74586号公報;IEEETrans.Electron.Devices,44巻,1245頁,1997年)。 Furthermore, an ultrathin insulating film (0.1 nm to 5 nm) such as LiF, MgF 2 , Li 2 O or the like is inserted at the interface between the cathode 8 and the hole blocking layer 6 (or on the electron transport layer 7 described later). Is also an effective method for improving the efficiency of the organic EL device (Appl. Phys. Lett., 70, 152, 1997; Japanese Patent Laid-Open No. 10-74586; IEEE Trans. Electron. Devices, 44, 1245). Page, 1997).
陰極8の形成は、陽極2と同様、通常、スパッタリング法、真空蒸着法などにより行われることが多い。さらに、粉末材料や導電性高分子を用いて陰極8を形成する場合には、陽極2と同様、塗布により形成することもできる。
また、陽極2と同様に、陰極8を異なる物質で積層して形成することも可能である。
The cathode 8 is often formed by a sputtering method, a vacuum vapor deposition method, or the like in the same manner as the anode 2. Further, when the cathode 8 is formed using a powder material or a conductive polymer, it can be formed by coating as in the case of the anode 2.
Similarly to the anode 2, the cathode 8 can be formed by stacking different materials.
陰極8の膜厚は通常、陽極2と同様である。低仕事関数金属から成る陰極を保護する目的で、この上にさらに、仕事関数が高く大気に対して安定な金属層を積層することは素子の安定性を増大させる。この目的のために、アルミニウム、銀、銅、ニッケル、クロム、金、白金等の金属が使われる。 The film thickness of the cathode 8 is usually the same as that of the anode 2. For the purpose of protecting the cathode made of a low work function metal, further laminating a metal layer having a high work function and stable to the atmosphere increases the stability of the device. For this purpose, metals such as aluminum, silver, copper, nickel, chromium, gold, platinum are used.
<7.電子輸送層>
有機EL素子の発光効率をさらに向上させることを目的として、正孔阻止層6と陰極8との間には、図2のように、電子輸送層7を設けることがある。電子輸送層7は、電界を与えられた電極2,8間において、陰極8から注入された電子を効率よく正孔阻止層6の方向に輸送し、陰極8から発光層5に電子を効率よく注入して、発光層5内における正孔と電子との再結合を容易にするために設けられるものである。よって、電子輸送層7の電子輸送材料としては、陰極8からの電子注入効率が高く、かつ、高い電子移動度を有し、さらに、注入された電子を効率よく輸送することができる材料であることが必要である。
<7. Electron transport layer>
For the purpose of further improving the light emission efficiency of the organic EL element, an electron transport layer 7 may be provided between the hole blocking layer 6 and the cathode 8 as shown in FIG. The electron transport layer 7 efficiently transports electrons injected from the cathode 8 between the electrodes 2 and 8 to which an electric field is applied in the direction of the hole blocking layer 6, and efficiently transports electrons from the cathode 8 to the light emitting layer 5. It is provided to facilitate recombination of holes and electrons in the light emitting layer 5 by being injected. Therefore, the electron transport material of the electron transport layer 7 is a material that has high electron injection efficiency from the cathode 8, has high electron mobility, and can efficiently transport injected electrons. It is necessary.
前述のように、電子輸送層7の材料である電子輸送材料として、本発明の電荷輸送材料を用いることができる。この際、電子輸送材料として本発明の電荷輸送材料に無機材料からなる電荷輸送材料を混合して用いても良いが、通常は、本発明の電荷輸送材料のみを用い、電子輸送層7を、本発明の電荷輸送材料のみからなる層として形成することが望ましい。これにより、有機EL素子の駆動寿命を向上させるとともに、駆動電圧上昇を抑制することができる。また、この場合、電子輸送材料として用いることができる化合物の具体例としては、電荷輸送材料や正孔阻止材料として好ましい化合物の具体例として例示したものと同様のものなどが挙げられる。 As described above, the charge transport material of the present invention can be used as the electron transport material that is the material of the electron transport layer 7. At this time, as the electron transport material, the charge transport material of the present invention may be used by mixing a charge transport material composed of an inorganic material, but usually, only the charge transport material of the present invention is used, and the electron transport layer 7 is It is desirable to form it as a layer consisting only of the charge transport material of the present invention. As a result, the drive life of the organic EL element can be improved and an increase in drive voltage can be suppressed. In this case, specific examples of the compound that can be used as the electron transport material include the same compounds as those exemplified as specific examples of the compound preferable as the charge transport material and the hole blocking material.
また、電子輸送材料として本発明の電荷輸送材料以外の材料を用いる場合、上記の条件を満たす材料としては、8−ヒドロキシキノリンのアルミニウム錯体などの金属錯体(特開昭59−194393号公報)、10−ヒドロキシベンゾ[h]キノリンの金属錯体、オキサジアゾール誘導体、ジスチリルビフェニル誘導体、シロール誘導体、3−又は5−ヒドロキシフラボン金属錯体、ベンズオキサゾール金属錯体、ベンゾチアゾール金属錯体、トリスベンズイミダゾリルベンゼン(米国特許第5645948号明細書)、キノキサリン化合物(特開平6−207169号公報)、フェナントロリン誘導体(特開平5−331459号公報)、2−t−ブチル−9,10−N,N′−ジシアノアントラキノンジイミン、n型水素化非晶質炭化シリコン、n型硫化亜鉛、n型セレン化亜鉛などが挙げられる。 When a material other than the charge transport material of the present invention is used as the electron transport material, examples of the material satisfying the above conditions include metal complexes such as an aluminum complex of 8-hydroxyquinoline (Japanese Patent Laid-Open No. 59-194393), 10-hydroxybenzo [h] quinoline metal complex, oxadiazole derivative, distyrylbiphenyl derivative, silole derivative, 3- or 5-hydroxyflavone metal complex, benzoxazole metal complex, benzothiazole metal complex, trisbenzimidazolylbenzene ( US Pat. No. 5,645,948), quinoxaline compound (JP-A-6-207169), phenanthroline derivative (JP-A-5-331459), 2-t-butyl-9,10-N, N′-dicyanoanthraquinone Diimine, n-type hydrogenated amorphous carbonization Recon, n-type zinc sulfide, etc. n-type zinc selenide.
また、正孔阻止層6にフェナントロリン誘導体や金属錯体やアルカリ金属をドープしたり、オキサジアゾール誘導体、キノキサリン化合物、フェナントロリン誘導体等の電子輸送性が高く分子量の小さい有機物をドープする等して、正孔阻止層6の電子輸送能を高めることにより、電子輸送層7を形成することもできる。 In addition, the hole blocking layer 6 may be doped with a phenanthroline derivative, a metal complex, or an alkali metal, or doped with an organic substance having a high electron transporting property such as an oxadiazole derivative, a quinoxaline compound, or a phenanthroline derivative. The electron transport layer 7 can also be formed by increasing the electron transport capability of the hole blocking layer 6.
電子輸送層7の形成方法は任意であるが、通常は、正孔輸送層4と同様、塗布法又は真空蒸着法により形成することができる。
塗布法により電子輸送層7を形成する場合は、正孔輸送材料に代えて電子輸送材料を用いるほかは、正孔輸送層4の形成と同様にして層形成を行なうことができる。また、バインダー樹脂や添加剤として適当なものを用いることで、電子輸送層7を、本発明の電荷輸送材料のみからなる層として形成することが可能となることも同様である。
Although the formation method of the electron carrying layer 7 is arbitrary, it can form normally by the apply | coating method or a vacuum evaporation method similarly to the positive hole transport layer 4. FIG.
When the electron transport layer 7 is formed by a coating method, the layer can be formed in the same manner as the hole transport layer 4 except that an electron transport material is used instead of the hole transport material. Similarly, by using an appropriate binder resin or additive, the electron transport layer 7 can be formed as a layer made of only the charge transport material of the present invention.
一方、真空蒸着法により電子輸送層7を形成する場合も、正孔輸送材料に代えて電子輸送材料を用い、陽極2上に代えて正孔阻止層6上に蒸着を行なう他は、正孔輸送層4の形成と同様にして層形成を行なうことができる。
また、電子輸送層7の膜厚は任意であるが、通常5nm以上、好ましくは10nm以上、また、通常200nm以下、好ましくは100nm以下である。さらに、電子輸送層7も正孔輸送層4と同様、通常は真空蒸着法で形成される。
On the other hand, when the electron transport layer 7 is formed by a vacuum deposition method, the hole transport material is replaced with an electron transport material, and the hole transport layer 7 is replaced with a hole blocking layer 6 instead of the anode 2. Layer formation can be performed in the same manner as the formation of the transport layer 4.
The thickness of the electron transport layer 7 is arbitrary, but is usually 5 nm or more, preferably 10 nm or more, and usually 200 nm or less, preferably 100 nm or less. Further, the electron transport layer 7 is usually formed by a vacuum deposition method, similarly to the hole transport layer 4.
<8.正孔注入層>
正孔注入の効率をさらに向上させ、かつ、有機層全体の陽極2への付着力を改善させる目的で、正孔輸送層4と陽極2との間には、図3のように、正孔注入層3を設けることがある。正孔注入層3は、使用初期の有機EL素子の駆動電圧を低下させると共に、有機EL素子を定電流で連続駆動した時の電圧上昇を抑制するために設けられるものである。よって、正孔注入層3に用いられる材料(以下適宜「正孔注入材料」という)には、陽極2とのコンタクトがよく均一な薄膜が形成でき、熱的に安定、即ち、融点及びガラス転移温度が高いことが要求される。通常要求される具体的な融点及びガラス転移温度は、融点が300℃以上、ガラス転移温度が100℃以上である。さらに、正孔注入材料には、イオン化ポテンシャルが低く陽極2からの正孔注入が容易なこと、及び、正孔移動度が大きいことも要求される。
<8. Hole injection layer>
For the purpose of further improving the efficiency of hole injection and improving the adhesion of the entire organic layer to the anode 2, there is a hole between the hole transport layer 4 and the anode 2 as shown in FIG. An injection layer 3 may be provided. The hole injection layer 3 is provided to reduce the drive voltage of the organic EL element in the initial stage of use and to suppress a voltage increase when the organic EL element is continuously driven with a constant current. Therefore, the material used for the hole injection layer 3 (hereinafter referred to as “hole injection material” as appropriate) can form a uniform thin film with good contact with the anode 2 and is thermally stable, that is, melting point and glass transition. High temperature is required. The specific melting point and glass transition temperature normally required are a melting point of 300 ° C. or higher and a glass transition temperature of 100 ° C. or higher. Further, the hole injection material is required to have a low ionization potential, facilitate hole injection from the anode 2, and have high hole mobility.
前述のように、正孔注入層3の材料である正孔注入材料として、本発明の電荷輸送材料を用いることができる。この際、正孔注入材料として本発明の電荷輸送材料に無機材料からなる電荷輸送材料を混合して用いても良いが、通常は、本発明の電荷輸送材料のみを用い、正孔注入層3を、本発明の電荷輸送材料のみからなる層として形成することが望ましい。これにより、有機EL素子の駆動寿命を向上させるとともに、駆動電圧上昇を抑制することができる。 As described above, the charge transport material of the present invention can be used as the hole injection material that is the material of the hole injection layer 3. At this time, the charge transport material of the present invention may be mixed with the charge transport material of the present invention as the hole injection material, but usually, only the charge transport material of the present invention is used and the hole injection layer 3 is used. Is preferably formed as a layer made of only the charge transport material of the present invention. As a result, the drive life of the organic EL element can be improved and an increase in drive voltage can be suppressed.
また、正孔注入材料として本発明の電荷輸送材料以外の材料を用いる場合、上記の条件を満たす材料としては、銅フタロシアニン等のフタロシアニン化合物(特開昭63−295695号公報)、ポリアニリン(Appl.Phys.Lett.,64巻、1245頁,1994年)、ポリチオフェン(Optical Materials,9巻、125頁、1998年)等の有機化合物や、スパッタ・カーボン膜(Synth.Met.,91巻、73頁、1997年)や、バナジウム酸化物、ルテニウム酸化物、モリブデン酸化物等の金属酸化物(J.Phys.D,29巻、2750頁、1996年)などが挙げられる。
また、芳香族ジアミン含有ポリエーテルにDDQ(2,3-dicyano-5,6-dichloro-p-benzoquinone)等の電子受容性基をドーピングする等して正孔注入を容易にすることもできる。
When a material other than the charge transport material of the present invention is used as the hole injection material, examples of the material satisfying the above conditions include phthalocyanine compounds such as copper phthalocyanine (Japanese Patent Laid-Open No. 63-295695), polyaniline (Appl. Phys., Lett., 64, 1245, 1994), organic compounds such as polythiophene (Optical Materials, 9, 125, 1998), and sputtered carbon films (Synth. Met., 91, 73). 1997) and metal oxides such as vanadium oxide, ruthenium oxide, and molybdenum oxide (J. Phys. D, 29, 2750, 1996).
Moreover, hole injection can be facilitated by doping an electron-accepting group such as DDQ (2,3-dicyano-5,6-dichloro-p-benzoquinone) into an aromatic diamine-containing polyether.
正孔注入層3の形成方法は任意であるが、通常は、正孔輸送層4と同様、塗布法又は真空蒸着法により形成することができる。また、正孔注入層3の場合、正孔注入材料が無機物の場合には、スパッタ法や電子ビーム蒸着法、プラズマCVD法が用いられる。
塗布法により正孔注入層3を形成する場合は、正孔輸送材料に代えて正孔注入材料を用いるほかは、正孔輸送層4の形成と同様にして層形成を行なうことができる。また、バインダー樹脂や添加剤として適当なものを用いることで、正孔注入層3を、本発明の電荷輸送材料のみからなる層として形成することが可能となることも同様である。
Although the formation method of the hole injection layer 3 is arbitrary, it can usually be formed by a coating method or a vacuum evaporation method as in the case of the hole transport layer 4. In the case of the hole injection layer 3, when the hole injection material is an inorganic material, a sputtering method, an electron beam evaporation method, or a plasma CVD method is used.
When the hole injection layer 3 is formed by a coating method, the layer can be formed in the same manner as the hole transport layer 4 except that a hole injection material is used instead of the hole transport material. Similarly, the hole injection layer 3 can be formed as a layer made of only the charge transport material of the present invention by using an appropriate binder resin or additive.
一方、真空蒸着法により正孔注入層3を形成する場合も、正孔輸送材料に代えて正孔注入材料を用いる他は、正孔輸送層4の形成と同様にして層形成を行なうことができる。
また、正孔注入層3の膜厚は任意であるが、通常3nm以上、好ましくは5nm以上、また、通常100nm以下、好ましくは50nm以下である。さらに、正孔注入層3も正孔輸送層4と同様、通常は真空蒸着法で形成される。
On the other hand, when the hole injection layer 3 is formed by the vacuum evaporation method, the layer formation can be performed in the same manner as the hole transport layer 4 except that the hole injection material is used instead of the hole transport material. it can.
The thickness of the hole injection layer 3 is arbitrary, but is usually 3 nm or more, preferably 5 nm or more, and usually 100 nm or less, preferably 50 nm or less. Further, the hole injection layer 3 is usually formed by a vacuum deposition method, similarly to the hole transport layer 4.
<9.その他>
なお、ここで示した有機EL素子の構成はあくまで一実施形態であり、本発明の有機EL素子は、上記の構成から任意に変形して実施することができる。
例えば、上記の有機EL素子は、上述した層のほかに、別の層を含んで構成されていてもよい。
<9. Other>
In addition, the structure of the organic EL element shown here is only one embodiment, and the organic EL element of the present invention can be arbitrarily modified from the above structure.
For example, the organic EL element may include another layer in addition to the above-described layers.
また、例えば、図1とは逆の構造、即ち、基板1上に陰極8、正孔阻止層6、発光層5、正孔輸送層4、陽極2の順に積層することも可能である。さらに、同様に、図2および図3に示した前記各層構成とは逆の構造に積層することも可能である。
また、例えば、既述したように少なくとも一方が透明性の高い2枚の基板1の間に本発明の有機EL素子を設けることも可能である。
In addition, for example, a structure opposite to that shown in FIG. Furthermore, similarly, it is also possible to laminate | stack to the structure opposite to the said each layer structure shown in FIG. 2 and FIG.
For example, as described above, the organic EL element of the present invention can be provided between two substrates 1 having at least one of which is highly transparent.
ところで、前述のように、有機EL素子は、通常、積層構造となっている。
したがって、その製造途中においては、有機EL素子は、本発明の電荷輸送材料のみから形成された層(例えば、正孔注入層3、正孔輸送層4、発光層5、正孔阻止層6、電子輸送層7のいずれか)を少なくとも有する積層体となっている場合がある。具体例を挙げれば、基板1上に、陽極2と、正孔輸送材料として本発明の電荷輸送材料のみを用い、その正孔輸送材料のみにより形成された正孔輸送層4とが積層された積層体となっている場合がある。
Incidentally, as described above, the organic EL element usually has a laminated structure.
Therefore, in the course of its manufacture, the organic EL element is a layer formed only from the charge transport material of the present invention (for example, hole injection layer 3, hole transport layer 4, light emitting layer 5, hole blocking layer 6, It may be a laminate having at least one of the electron transport layers 7). To give a specific example, an anode 2 and a hole transport layer 4 formed of only the hole transport material using only the charge transport material of the present invention as the hole transport material were laminated on the substrate 1. It may be a laminate.
また、有機EL素子は、例えば、本発明の電荷輸送材料と、ドーパントとから形成された有機発光層5を有する積層体となっている場合がある。具体例を挙げれば、基板1上に、陽極2と、正孔輸送層4と、ホスト材料として本発明の電荷輸送材料を用い、発光材料としてこのホスト材料及びドーパントのみを用いた発光層5とを積層された積層体となっている場合がある。
これらのような積層体をはじめ、本発明の電荷輸送材料のみから形成された層、及び、本発明の電荷輸送材料とドーパントとから形成された有機発光層の少なくともいずれかを有する積層体も、本発明の範囲に含むものとする。
Moreover, the organic EL element may be a laminated body which has the organic light emitting layer 5 formed from the charge transport material of this invention and the dopant, for example. As a specific example, on the substrate 1, the anode 2, the hole transport layer 4, the light-emitting layer 5 using the charge transport material of the present invention as the host material, and using only the host material and the dopant as the light-emitting material, In some cases.
In addition to laminates such as these, a laminate comprising at least one of a layer formed only from the charge transport material of the present invention and an organic light emitting layer formed from the charge transport material of the present invention and a dopant, It is intended to be included within the scope of the present invention.
<10.有機EL素子の用途>
前述した有機EL素子の構成は、単一の素子、アレイ状に配置された構造からなる素子、陽極と陰極とがX−Yマトリックス状に配置された構造を有する素子のいずれにおいても適用することができる。
<10. Applications of organic EL devices>
The configuration of the organic EL element described above is applicable to any of a single element, an element having a structure arranged in an array, and an element having a structure in which an anode and a cathode are arranged in an XY matrix. Can do.
次に、本発明を実施例によって更に具体的に説明するが、本発明はその要旨を逸脱しない限り、以下の実施例の記載に限定されるものではない。 EXAMPLES Next, although an Example demonstrates this invention further more concretely, this invention is not limited to description of a following example, unless it deviates from the summary.
<電荷輸送材料について>
(参考例1)
サンプル1〜4として、4,4′−ビス(N−カルバゾリル)ビフェニル(同仁堂社製;DCBP,Sublimed)のLot No.NL−851及びLot No.PY−748、並びに、これらを昇華法で再精製したものを使用した。具体的には、表1に示すとおりのサンプルを用いた。
( Reference Example 1 )
As samples 1 to 4, Lot No. of 4,4′-bis (N-carbazolyl) biphenyl (manufactured by Dojindo; DCBP, Sublimed) was used. NL-851 and Lot No. PY-748 and those repurified by sublimation were used. Specifically, samples as shown in Table 1 were used.
なお、上記サンプル2,4の昇華法による再精製は、表2に示す条件により行なった。
上記のサンプル1〜4それぞれについて、LC−MS法を用い、各LCピークのMSチャート、UV吸収スペクトル、及び滞留時間を標品と比較することなどから、各サンプル1〜4に含まれる不純物の構造を同定した。なお、ここで行なったLC−MS法の測定条件は、表3に示すとおりである。
各サンプル1〜4について分析した結果、サンプル1〜4には、それぞれ下記(i)〜(vii)に示す分子構造を有する化合物が不純物として含まれていることが分かった。また、これらの不純物(i)〜(vii)のうち、不純物(v)及び不純物(vi)が、CH基を有している。 As a result of analyzing each of the samples 1 to 4, it was found that the samples 1 to 4 each contained a compound having a molecular structure shown in the following (i) to (vii) as an impurity. Of these impurities (i) to (vii), the impurity (v) and the impurity (vi) have a CH group.
測定結果から、上記の式(6)〜(8)を用いて、CH基の存在割合PCHを計算した。計算に用いたPM、RCH、WA、WM、MCH及びMMの値を表4に示す。
さらに、各サンプル1〜4中における、これらの不純物(i)〜(vii)の存在割合、及び、各サンプル1〜4中のCH基の存在割合PCHを、下記表5に示す。なお、表5には、参考のため、各不純物(i)〜(vii)の存在割合も示してある。また、表5において、存在割合PCHは、カルボニル基に直接結合するものを含まない場合のCH基の存在割合を表わす。表5から、サンプル2はCH基の存在割合PCHが70ppm以下であることが確認された。 Furthermore, the presence ratio of these impurities (i) to (vii) in each sample 1 to 4 and the presence ratio P CH of CH group in each sample 1 to 4 are shown in Table 5 below. Table 5 also shows the abundance ratios of the impurities (i) to (vii) for reference. In Table 5, the abundance ratio P CH represents the abundance ratio of the CH group in the case where it does not include those directly bonded to the carbonyl group. From Table 5, it was confirmed that Sample 2 has a CH group existing ratio P CH of 70 ppm or less.
次に、酸化電位の測定方法として上述した方法により、サンプル1〜4の酸化電位及び還元電位を測定した。作用電極にはGC(グラッシーカーボン)を用い、参照電極にはAg線を用い、対極にはPtを用いた。また、溶媒には、酸化電位測定時及び還元電位測定時とも、アセトニトリル及びテトラヒドロフランの体積比1:1混合溶媒に、0.1MのTBAP(Tetrabutylammonium perchlorate)を含有させたものを用いた。さらに、測定対象であるサンプル1〜4の濃度は1×10-3Mとし、掃引速度は0.1V/secとした。また、内部標準にはFc(フェロセン)を使用し、Fcの酸化電位を+0.41Vvs.SCEとして換算し、電位測定を行なった。
その結果、サンプル1〜4の酸化電位はいずれも+1.27V、還元電位は−2.4Vであり、酸化電位が+0.8V以上であることが確認された。
Next, the oxidation potential and reduction potential of Samples 1 to 4 were measured by the method described above as a method for measuring the oxidation potential. GC (glassy carbon) was used for the working electrode, Ag wire was used for the reference electrode, and Pt was used for the counter electrode. The solvent used was a mixture of acetonitrile and tetrahydrofuran in a 1: 1 volume ratio of 0.1 M TBAP (Tetrabutylaluminum perchlorate) at both the oxidation potential measurement and the reduction potential measurement. Furthermore, the concentration of samples 1 to 4 to be measured was 1 × 10 −3 M, and the sweep rate was 0.1 V / sec. In addition, Fc (ferrocene) was used as an internal standard, and the oxidation potential of Fc was +0.41 Vvs. The potential was measured by converting as SCE.
As a result, it was confirmed that the oxidation potentials of Samples 1 to 4 were all +1.27 V, the reduction potential was -2.4 V, and the oxidation potential was +0.8 V or more .
(実施例2)
下記構造を有する化合物(M−1)を合成し、熱懸洗、再結晶、及び昇華法で精製することによりCH基を排除し、サンプル5とした。このサンプル5を、HPLCにより分析した。なお、HPLCの測定条件は、表6に示すとおりである。
(Example 2)
A compound (M-1) having the following structure was synthesized and purified by hot washing, recrystallization, and sublimation to eliminate the CH group, and sample 5 was obtained. Sample 5 was analyzed by HPLC. The HPLC measurement conditions are as shown in Table 6.
分析の結果、本実施例のサンプル5には、化合物(M−1)が99.95重量%、CH基を有する化合物(下記化合物(viii))が0.050重量%確認された。これから、参考例1と同様にしてサンプル5中のCH基の存在割合PCHを算出した。結果を表7に示す。なお、表7において、PCH※の欄の値はカルボニル基に直接結合するものを含まない場合のCH基の存在割合を表わし、PCH※※の欄の値はカルボニル基に直接結合するものを含む場合のCH基の存在割合を表わす。この結果、サンプル5はCH基の存在割合PCHが70ppm以下であることが確認された。
次に、酸化電位測定時の溶媒に、ジクロロメタンに0.1MのTBAPを含有させたものを用い、還元電位測定時の溶媒に、N,N−ジメチルホルムアミドに0.1MのTBAPを含有させたものを用いた他は参考例1と同様にして、サイクリックボルタンメトリーで、サンプル5の酸化電位及び還元電位を測定した。
その結果、サンプル5の酸化電位は+1.94V、還元電位は−2.06Vであり、酸化電位が+0.8V以上であることが確認された。
以上から、サンプル5は、本発明の電荷輸送材料としての条件を満たすことが分かる。
Next, a solvent in which 0.1 M TBAP was added to dichloromethane was used as the solvent for the oxidation potential measurement, and 0.1 M TBAP was added to N, N-dimethylformamide in the solvent for the reduction potential measurement. The oxidation potential and reduction potential of Sample 5 were measured by cyclic voltammetry in the same manner as in Reference Example 1 except that those were used.
As a result, it was confirmed that the oxidation potential of Sample 5 was +1.94 V, the reduction potential was −2.06 V, and the oxidation potential was +0.8 V or more.
From the above, it can be seen that Sample 5 satisfies the conditions as the charge transport material of the present invention.
(参考例2)
実施例2と同様の操作により、サンプル6を調製した。さらに、サンプル6を、実施例2と同様に分析した。分析の結果、サンプル6に含まれる化合物(M−1)は99.77重量%、CH基を有する化合物(上記化合物(viii))は0.093重量%であることが確認された。これから、実施例2と同様に、サンプル6のCH基の存在割合PCHを算出した。結果を表8に示す。なお、表8において、PCH※の欄の値はカルボニル基に直接結合するものを含まない場合のCH基の存在割合を表わし、PCH※※の欄の値はカルボニル基に直接結合するものを含む場合のCH基の存在割合を表わす。この結果、サンプル6はCH基の存在割合PCHが70ppm以下であることが確認された。
Sample 6 was prepared in the same manner as in Example 2. Further, Sample 6 was analyzed in the same manner as in Example 2. As a result of the analysis, it was confirmed that the compound (M-1) contained in Sample 6 was 99.77% by weight, and the compound having a CH group (the above compound (viii)) was 0.093% by weight. From this, as in Example 2, the CH group abundance P CH of Sample 6 was calculated. The results are shown in Table 8. In Table 8, the value in the column for P CH * indicates the abundance ratio of the CH group when not including those directly bonded to the carbonyl group, and the value in the column for P CH ** is a value directly bonded to the carbonyl group. The abundance ratio of the CH group in the case of containing As a result, it was confirmed that Sample 6 had a CH group existing ratio P CH of 70 ppm or less.
次に、実施例2と同様にして、サイクリックボルタンメトリーで、サンプル6の酸化電位及び還元電位を測定した。
その結果、サンプル6の酸化電位は+1.94V、還元電位は−2.06Vであり、酸化電位が+0.8V以上であることが確認された。
Next, in the same manner as in Example 2, the oxidation potential and the reduction potential of Sample 6 were measured by cyclic voltammetry.
As a result, it was confirmed that the oxidation potential of Sample 6 was +1.94 V, the reduction potential was −2.06 V, and the oxidation potential was +0.8 V or more .
(比較例1)
下記構造を有する化合物(M−2)を合成し、熱懸洗、再結晶、及び昇華法で精製したものをサンプル7とした。このサンプル7を、実施例2と同様に分析した。分析の結果、サンプル7はCH基を有する化合物の含有率が100.00重量%であることが確認された。これから、実施例2と同様に、サンプル7のCH基の存在割合PCHを算出した。結果を表9に示す。なお、表9において、存在割合PCHは、カルボニル基に直接結合するものを含まない場合のCH基の存在割合を表わす。表9のように、サンプル7のCH基の存在割合PCHは16126ppmであった。
A compound (M-2) having the following structure was synthesized and purified by hot washing, recrystallization, and sublimation method as Sample 7. Sample 7 was analyzed in the same manner as in Example 2. As a result of analysis, it was confirmed that the content of the compound having a CH group in Sample 7 was 100.00% by weight. From this, as in Example 2, the CH group abundance P CH of Sample 7 was calculated. The results are shown in Table 9. In Table 9, the abundance ratio P CH represents the abundance ratio of the CH group when it does not include those directly bonded to the carbonyl group. As shown in Table 9, the CH group existing ratio P CH in Sample 7 was 16126 ppm.
次に、還元電位測定時のサンプル7の濃度を1.0×10-3M以下としたこと以外は実施例2と同様にして、サイクリックボルタンメトリーで、サンプル7の酸化電位及び還元電位を測定した。
その結果、サンプル7の酸化電位は+1.9V、還元電位は−2.11Vであり、酸化電位が+0.8V以上であることが確認された。
以上から、サンプル7は酸化電位が、本発明の電荷輸送材料としての条件を満たすものの、CH基の存在割合が本発明の電荷輸送材料としての条件を満たさないことが分かる。
Next, the oxidation potential and reduction potential of sample 7 are measured by cyclic voltammetry in the same manner as in Example 2 except that the concentration of sample 7 at the time of reduction potential measurement is 1.0 × 10 −3 M or less. did.
As a result, it was confirmed that the oxidation potential of Sample 7 was +1.9 V, the reduction potential was −2.11 V, and the oxidation potential was +0.8 V or more.
From the above, it can be seen that Sample 7 does not satisfy the condition as the charge transporting material of the present invention although the oxidation potential satisfies the conditions as the charge transporting material of the present invention, but the presence ratio of the CH group.
(実施例4)
下記構造を有する化合物(M−3)を合成し、熱懸洗、再結晶、及び昇華法で精製することによりCH基を排除し、サンプル8とした。このサンプル8を、実施例2と同様に分析した。分析の結果、サンプル8は、化合物(M−3)の含有率が99.999重量%以上、CH基を有する化合物の含有率が0.001重量%未満であることが確認された。これから、実施例2と同様に、サンプル8のCH基の存在割合PCHを算出した。結果を表10に示す。なお、表10において、存在割合PCHは、カルボニル基に直接結合するものを含まない場合のCH基の存在割合を表わす。表10のように、サンプル8のCH基の存在割合PCHは0.22ppmであった。この結果、サンプル8はCH基の存在割合PCHが70ppm以下であることが確認された。
A compound (M-3) having the following structure was synthesized and purified by hot washing, recrystallization, and sublimation to eliminate CH groups, and sample 8 was obtained. Sample 8 was analyzed in the same manner as in Example 2. As a result of the analysis, it was confirmed that the content of the compound (M-3) in the sample 8 is 99.999% by weight or more and the content of the compound having a CH group is less than 0.001% by weight. From this, as in Example 2, the CH group abundance P CH of Sample 8 was calculated. The results are shown in Table 10. In Table 10, the abundance ratio P CH represents the abundance ratio of the CH group when it does not include those directly bonded to the carbonyl group. As shown in Table 10, the CH group abundance ratio P CH of Sample 8 was 0.22 ppm. As a result, it was confirmed that Sample 8 had a CH group existing ratio P CH of 70 ppm or less.
次に、参考例1と同様にして、サイクリックボルタンメトリーで、サンプル8の酸化電位及び還元電位を測定した。
その結果、サンプル8の酸化電位は+1.66V、還元電位は−2.07Vであり、酸化電位が+0.8V以上であることが確認された。
以上から、サンプル8は、本発明の電荷輸送材料としての条件を満たすことが分かる。
Next, in the same manner as in Reference Example 1 , the oxidation potential and reduction potential of Sample 8 were measured by cyclic voltammetry.
As a result, it was confirmed that the oxidation potential of Sample 8 was +1.66 V, the reduction potential was −2.07 V, and the oxidation potential was +0.8 V or more.
From the above, it can be seen that Sample 8 satisfies the conditions as the charge transport material of the present invention.
(比較例2)
下記構造を有する化合物(M−4)を合成し、熱懸洗、再結晶、及び昇華法で精製して、サンプル9とした。このサンプル9を、実施例2と同様に分析した。分析の結果、サンプル9は、CH基を有する化合物の含有率が100.00重量%であることが確認された。これから、実施例2と同様に、サンプル9のCH基の存在割合PCHを算出した。結果を表11に示す。なお、表11において、存在割合PCHは、カルボニル基に直接結合するものを含まない場合のCH基の存在割合を表わす。表11のように、サンプル9のCH基の存在割合PCHは16115ppmであった。
A compound (M-4) having the following structure was synthesized and purified by hot washing, recrystallization, and sublimation to prepare Sample 9. Sample 9 was analyzed in the same manner as in Example 2. As a result of the analysis, it was confirmed that the content of the compound having a CH group in Sample 9 was 100.00% by weight. From this, as in Example 2, the CH group abundance P CH of Sample 9 was calculated. The results are shown in Table 11. In Table 11, the abundance ratio P CH represents the abundance ratio of the CH group in the case where it does not include those directly bonded to the carbonyl group. As shown in Table 11, the CH group abundance ratio P CH of Sample 9 was 16115 ppm.
次に、実施例2と同様にして、サイクリックボルタンメトリーで、サンプル9の酸化電位及び還元電位を測定した。
その結果、サンプル9の酸化電位は+1.73V、還元電位は−2.01Vであり、酸化電位が+0.8V以上であることが確認された。
以上から、サンプル9は酸化電位が本発明の電荷輸送材料としての条件を満たすものの、CH基の存在割合が本発明の電荷輸送材料としての条件を満たさないことが分かる。
Next, in the same manner as in Example 2, the oxidation potential and the reduction potential of Sample 9 were measured by cyclic voltammetry.
As a result, it was confirmed that the oxidation potential of Sample 9 was +1.73 V, the reduction potential was −2.01 V, and the oxidation potential was +0.8 V or more.
From the above, it can be seen that Sample 9 does not satisfy the condition as the charge transporting material of the present invention, although the oxidation potential satisfies the condition as the charge transporting material of the present invention, but the abundance ratio of the CH group.
<有機EL素子>
(素子参考例1)
図3に示す構造を有する有機EL素子を以下の方法で作製した。
ガラス基板1の上に、陽極としてインジウム・スズ酸化物(ITO)透明導電膜2を150nm堆積したもの(スパッター成膜品;シート抵抗15Ω)を、通常のフォトリソグラフィ技術と塩酸エッチングとを用いて2mm幅のストライプにパターニングしてITO基板を形成した。パターン形成したITO基板を、アセトンによる超音波洗浄、純水による水洗、イソプロピルアルコールによる超音波洗浄の順で洗浄後、窒素ブローで乾燥させ、最後に紫外線オゾン洗浄を行なった。
<Organic EL device>
(Element Reference Example 1 )
An organic EL device having the structure shown in FIG. 3 was produced by the following method.
An indium tin oxide (ITO) transparent conductive film 2 deposited as a positive electrode on a glass substrate 1 with a thickness of 150 nm (sputtered film product; sheet resistance of 15Ω) is obtained using ordinary photolithography technology and hydrochloric acid etching. An ITO substrate was formed by patterning into stripes having a width of 2 mm. The patterned ITO substrate was cleaned in the order of ultrasonic cleaning with acetone, water with pure water, and ultrasonic cleaning with isopropyl alcohol, dried with nitrogen blow, and finally subjected to ultraviolet ozone cleaning.
次に、陽極2上に、以下のようにして正孔注入層3を形成した。
芳香族ジアミン含有ポリエーテルである上述した化合物(P−1)(重量平均分子量25300;ガラス転移温度171℃)、及び、下記構造の化合物(P−2)を、化合物(P−1)に対し化合物(P−2)の割合が10重量%となるようにして、下記表12に示す条件で、上記ITO基板の陽極2上にスピンコートした。このスピンコートにより、膜厚30nmの均一な薄膜(正孔注入層3)が形成された。
Next, the hole injection layer 3 was formed on the anode 2 as follows.
Compound (P-1) (weight average molecular weight 25300; glass transition temperature 171 ° C.), which is an aromatic diamine-containing polyether, and compound (P-2) having the following structure are combined with compound (P-1). It spin-coated on the anode 2 of the said ITO board | substrate on the conditions shown in following Table 12 so that the ratio of a compound (P-2) might be 10 weight%. By this spin coating, a uniform thin film (hole injection layer 3) having a thickness of 30 nm was formed.
次に、正孔注入層3上に、以下のようにして、正孔輸送層4を形成した。
まず、正孔注入層3を塗布成膜したITO基板を真空蒸着装置内に設置した。この装置の粗排気を油回転ポンプにより行なった後、装置内の真空度が8×10-5Pa以下になるまでクライオポンプを用いて排気した。
上記装置内に配置されたセラミックるつぼに、正孔輸送材料として、下記構造式(HT−1)で表わされる4,4′−ビス[N−(1−フェナンチル)−N−フェニルアミノ]ビフェニルを入れ、るつぼの周囲のタンタル線ヒーターで加熱して蒸着を行なった。この時のるつぼの温度は、319℃〜331℃の範囲で制御した。これにより、蒸着時の真空度8×10-5Pa、蒸着速度0.1nm/秒で、膜厚60nmの正孔輸送層4を得た。
Next, the hole transport layer 4 was formed on the hole injection layer 3 as follows.
First, the ITO substrate coated with the hole injection layer 3 was placed in a vacuum deposition apparatus. After roughly exhausting the apparatus with an oil rotary pump, the apparatus was evacuated with a cryopump until the degree of vacuum in the apparatus was 8 × 10 −5 Pa or less.
In the ceramic crucible arranged in the above apparatus, 4,4′-bis [N- (1-phenanthyl) -N-phenylamino] biphenyl represented by the following structural formula (HT-1) is used as a hole transport material. Then, vapor deposition was performed by heating with a tantalum wire heater around the crucible. The temperature of the crucible at this time was controlled in the range of 319 ° C to 331 ° C. Thus, a hole transport layer 4 having a film thickness of 60 nm was obtained at a vacuum degree of 8 × 10 −5 Pa and a deposition rate of 0.1 nm / second during the deposition.
引続き、以下の方法により、正孔輸送層4上に発光層5を形成した。
ホスト材料としてサンプル2を用い、また、ドーパントとして上記化合物(T−1)を用いて、これらホスト材料とドーパントとをそれぞれ別々のセラミックるつぼに設置し、2元同時蒸着法により成膜を行なった。
Subsequently, the light emitting layer 5 was formed on the hole transport layer 4 by the following method.
Using Sample 2 as the host material and using the compound (T-1) as a dopant, the host material and the dopant were each placed in separate ceramic crucibles, and a film was formed by a binary simultaneous vapor deposition method. .
蒸着の際、ホスト材料のるつぼ温度は298℃に、蒸着速度は0.07nm/秒に制御した。一方、ドーパントのるつぼ温度は248℃、蒸着速度は0.004nm/秒に制御した。この蒸着により、膜厚が30nm、ドーパントである化合物(T−1)がホスト材料であるサンプル2に5重量%含有された発光材料からなる発光層(有機発光層)5が積層された。なお、蒸着時の真空度は9×10-5Paであった。 During the deposition, the crucible temperature of the host material was controlled at 298 ° C., and the deposition rate was controlled at 0.07 nm / second. On the other hand, the crucible temperature of the dopant was controlled to 248 ° C., and the deposition rate was controlled to 0.004 nm / second. By this vapor deposition, a light emitting layer (organic light emitting layer) 5 made of a light emitting material having a film thickness of 30 nm and containing 5 wt% of the compound (T-1) as a dopant in the sample 2 as a host material was laminated. The degree of vacuum at the time of vapor deposition was 9 × 10 −5 Pa.
さらに、以下の方法により、発光層5上に正孔阻止層6を形成した。
正孔阻止材料として、以下に示す化合物(Py−1)を用い、この化合物(Py−1)をるつぼに設置し、正孔阻止材料の蒸着により成膜を行なった。蒸着の際、るつぼ温度は275℃、蒸着速度は0.1nm/秒として、10nmの膜厚で正孔阻止層6を積層した。蒸着時の真空度は7×10-5Paであった。
Further, the hole blocking layer 6 was formed on the light emitting layer 5 by the following method.
As the hole blocking material, the following compound (Py-1) was used, this compound (Py-1) was placed in a crucible, and a film was formed by vapor deposition of the hole blocking material. At the time of vapor deposition, the crucible temperature was 275 ° C., the vapor deposition rate was 0.1 nm / second, and the hole blocking layer 6 was laminated with a thickness of 10 nm. The degree of vacuum at the time of vapor deposition was 7 × 10 −5 Pa.
さらに、以下の方法により、正孔阻止層6上に電子輸送層7を形成した。
電子輸送材料として、以下に示すアルミニウムの8−ヒドロキシキノリン錯体である化合物(ET−1){組成式Al(C9H6NO)3}を用い、この化合物(ET−1)をるつぼに設置し、電子輸送材料の蒸着により成膜を行なった。蒸着の際、るつぼ温度は250℃、蒸着速度は0.2nm/秒として、35nmの膜厚で電子輸送層7を積層した。また、蒸着時の真空度は7×10-5Paであった。
Further, the electron transport layer 7 was formed on the hole blocking layer 6 by the following method.
The compound (ET-1) {composition formula Al (C 9 H 6 NO) 3 } which is an 8-hydroxyquinoline complex of aluminum shown below is used as an electron transport material, and this compound (ET-1) is placed in a crucible. The film was formed by vapor deposition of an electron transport material. At the time of vapor deposition, the crucible temperature was 250 ° C., the vapor deposition rate was 0.2 nm / second, and the electron transport layer 7 was laminated with a film thickness of 35 nm. Further, the degree of vacuum at the time of vapor deposition was 7 × 10 −5 Pa.
なお、上記の正孔輸送層4、発光層5、正孔阻止層6及び電子輸送層7を真空蒸着する時の基板1の温度は室温に保持した。
ここで、電子輸送層7までの蒸着を行なった積層体を、一度、上記真空蒸着装置内より大気中に取り出し、2mm幅のストライプ状シャドーマスクを、陰極蒸着用のマスクとして、陽極2のITOストライプとは直交するように積層体に密着させた。
In addition, the temperature of the board | substrate 1 at the time of vacuum-depositing said hole transport layer 4, the light emitting layer 5, the hole blocking layer 6, and the electron carrying layer 7 was hold | maintained at room temperature.
Here, the laminated body on which the electron transport layer 7 has been vapor-deposited is once taken out from the vacuum vapor deposition apparatus into the atmosphere, and a 2 mm wide stripe-shaped shadow mask is used as a mask for cathode vapor deposition. It was stuck to the laminate so as to be orthogonal to the stripe.
次いで、この積層体を別の真空蒸着装置内に設置し、正孔輸送層4などの有機層の場合と同様にして、装置内の真空度が5×10-4Pa以下になるまで排気した。
これに、以下の方法により、電子輸送層7上に陰極8を形成した。
先ず、フッ化リチウム(LiF)を、モリブデンボートを用いて、蒸着速度0.01nm/秒、真空度5×10-4Paで、0.5nmの膜厚で電子輸送層7の上に成膜した。次に、アルミニウムを同様にモリブデンボートにより加熱して、蒸着速度0.5nm/秒、真空度1×10-3Paで、80nmの膜厚でフッ化リチウム層の上に成膜した。これにより、フッ化リチウム層及びアルミニウム層からなる2層型陰極8を形成した。なお、蒸着時の基板温度は室温に保持した。
Next, this laminate was placed in another vacuum vapor deposition apparatus, and evacuated until the degree of vacuum in the apparatus was 5 × 10 −4 Pa or less in the same manner as in the case of an organic layer such as the hole transport layer 4. .
A cathode 8 was formed on the electron transport layer 7 by the following method.
First, lithium fluoride (LiF) is formed on the electron transport layer 7 with a film thickness of 0.5 nm at a deposition rate of 0.01 nm / second and a degree of vacuum of 5 × 10 −4 Pa using a molybdenum boat. did. Next, aluminum was similarly heated by a molybdenum boat, and deposited on the lithium fluoride layer at a deposition rate of 0.5 nm / second, a vacuum degree of 1 × 10 −3 Pa, and a thickness of 80 nm. Thus, a two-layer cathode 8 composed of a lithium fluoride layer and an aluminum layer was formed. In addition, the substrate temperature at the time of vapor deposition was kept at room temperature.
以上の様にして、2mm×2mmのサイズの発光面積部分を有する有機EL素子が得られた。
得られた有機EL素子を、室温下、初期輝度5000cd/m2として一定電流で連続駆動させ、輝度半減時間及び駆動電圧上昇(=輝度半減時駆動電圧−初期駆動電圧)を測定した。この測定結果を表13に示す。
また、初期輝度1000cd/m2として一定電流で連続駆動させた場合についても、輝度半減時間及び駆動電圧上昇を測定した。この測定結果は、後述する素子実施例2〜4及び素子比較例2,3の測定結果の基準値として用いることとし、表14に基準値1.0として示す。
As described above, an organic EL element having a light emitting area portion having a size of 2 mm × 2 mm was obtained.
The obtained organic EL element was continuously driven at a constant current at an initial luminance of 5000 cd / m 2 at room temperature, and the luminance half time and the driving voltage increase (= the luminance half-time driving voltage−initial driving voltage) were measured. The measurement results are shown in Table 13.
In addition, the luminance half-life time and the driving voltage increase were also measured when the device was continuously driven at a constant current with an initial luminance of 1000 cd / m 2 . This measurement result is used as a reference value for the measurement results of later-described device examples 2 to 4 and device comparison examples 2 and 3, and is shown as a reference value 1.0 in Table 14.
(素子比較例1−1)
素子参考例1において、サンプル2に代えてサンプル4を用いた以外は、同様にして有機EL素子を作製した。得られた有機EL素子を室温下、初期輝度5000cd/m2として一定電流で連続駆動させ、輝度半減時間及び駆動電圧上昇を測定した。この測定結果を表13に示す。
(Element Comparative Example 1-1)
An organic EL device was produced in the same manner except that Sample 4 was used instead of Sample 2 in Device Reference Example 1 . The obtained organic EL device was continuously driven at a constant current at an initial luminance of 5000 cd / m 2 at room temperature, and the luminance half time and the driving voltage increase were measured. The measurement results are shown in Table 13.
(素子比較例1−2)
素子参考例1において、サンプル2に代えてサンプル1を用い、正孔阻止材料として化合物(Py−1)に代えて上記化合物(HB−12)を用いた以外は、同様にして有機EL素子を作製した。得られた有機EL素子を室温下、初期輝度5000cd/m2として一定電流で連続駆動させ、輝度半減時間及び駆動電圧上昇を測定した。この測定結果を表13に示す。
(Element Comparative Example 1-2)
In element reference example 1 , sample 1 was used in place of sample 2, and the organic EL element was similarly prepared except that the compound (HB-12) was used in place of compound (Py-1) as the hole blocking material. Produced. The obtained organic EL device was continuously driven at a constant current at an initial luminance of 5000 cd / m 2 at room temperature, and the luminance half time and the driving voltage increase were measured. The measurement results are shown in Table 13.
(素子実施例2)
素子参考例1において、正孔阻止材料として化合物(Py−1)の代わりに実施例2のサンプル5を用いた以外は、同様にして有機EL素子を作製した。得られた有機EL素子を室温下、初期輝度1000cd/m2として一定電流で連続駆動させ、輝度半減時間及び駆動電圧上昇を測定した。この測定結果を、素子参考例1の測定結果を基準値「1.0」として規格化した。具体的には、本素子実施例の測定結果を素子参考例1の測定結果で割った値を算出した。規格化された輝度半減時間、及び、規格化された駆動電圧上昇を表14に示す。
(Element Example 2)
In the device reference example 1 , an organic EL device was produced in the same manner except that the sample 5 of Example 2 was used instead of the compound (Py-1) as the hole blocking material. The obtained organic EL device was continuously driven at a constant current at an initial luminance of 1000 cd / m 2 at room temperature, and the luminance half time and the driving voltage increase were measured. The measurement results were standardized with the measurement result of element reference example 1 as the reference value “1.0”. Specifically, a value obtained by dividing the measurement result of this device example by the measurement result of device reference example 1 was calculated. Table 14 shows the normalized luminance half time and the normalized drive voltage rise.
(素子参考例2)
素子参考例1において、正孔阻止材料として化合物(Py−1)の代わりに参考例2のサンプル6を用いた以外は、同様にして有機EL素子を作製した。得られた有機EL素子を室温下、初期輝度1000cd/m2として一定電流で連続駆動させ、輝度半減時間及び駆動電圧上昇を測定し、素子実施例2と同様に測定結果を規格化した。規格化された輝度半減時間、及び、規格化された駆動電圧上昇を表14に示す。
(Element Reference Example 2 )
In the device reference example 1 , an organic EL device was produced in the same manner except that the sample 6 of the reference example 2 was used instead of the compound (Py-1) as the hole blocking material. The obtained organic EL device was continuously driven at a constant current at an initial luminance of 1000 cd / m 2 at room temperature, the luminance half time and the drive voltage increase were measured, and the measurement results were normalized in the same manner as in Device Example 2. Table 14 shows the normalized luminance half time and the normalized drive voltage rise.
(素子実施例4)
素子参考例1において、正孔阻止材料として化合物(Py−1)の代わりに実施例4のサンプル8を用いた以外は、同様にして有機EL素子を作製した。得られた有機EL素子を室温下、初期輝度1000cd/m2として一定電流で連続駆動させ、輝度半減時間及び駆動電圧上昇を測定し、素子実施例2と同様に測定結果を規格化した。規格化された輝度半減時間、及び、規格化された駆動電圧上昇を表14に示す。
(Element Example 4)
In the device reference example 1 , an organic EL device was produced in the same manner except that the sample 8 of Example 4 was used instead of the compound (Py-1) as the hole blocking material. The obtained organic EL device was continuously driven at a constant current at an initial luminance of 1000 cd / m 2 at room temperature, the luminance half time and the drive voltage increase were measured, and the measurement results were normalized in the same manner as in Device Example 2. Table 14 shows the normalized luminance half time and the normalized drive voltage rise.
(素子比較例2)
素子参考例1において、正孔阻止材料として化合物(Py−1)の代わりに比較例1のサンプル7を用いた以外は、同様にして有機EL素子を作製した。得られた有機EL素子を室温下、初期輝度1000cd/m2として一定電流で連続駆動させ、輝度半減時間及び駆動電圧上昇を測定し、素子実施例2と同様に測定結果を規格化した。規格化された輝度半減時間、及び、規格化された駆動電圧上昇を表14に示す。
(Element comparison example 2)
In the device reference example 1 , an organic EL device was produced in the same manner except that the sample 7 of the comparative example 1 was used instead of the compound (Py-1) as the hole blocking material. The obtained organic EL device was continuously driven at a constant current at an initial luminance of 1000 cd / m 2 at room temperature, the luminance half time and the drive voltage increase were measured, and the measurement results were normalized in the same manner as in Device Example 2. Table 14 shows the normalized luminance half time and the normalized drive voltage rise.
(素子比較例3)
素子参考例1において、正孔阻止材料として化合物(Py−1)の代わりに比較例2のサンプル9を用いた以外は、同様にして有機EL素子を作製した。得られた有機EL素子を室温下、初期輝度1000cd/m2として一定電流で連続駆動させ、輝度半減時間及び駆動電圧上昇を測定し、素子実施例2と同様に測定結果を規格化した。規格化された輝度半減時間、及び、規格化された駆動電圧上昇を表14に示す。
(Element Comparison Example 3)
An organic EL device was produced in the same manner except that Sample 9 of Comparative Example 2 was used instead of Compound (Py-1) as the hole blocking material in Device Reference Example 1 . The obtained organic EL device was continuously driven at a constant current at an initial luminance of 1000 cd / m 2 at room temperature, the luminance half time and the drive voltage increase were measured, and the measurement results were normalized in the same manner as in Device Example 2. Table 14 shows the normalized luminance half time and the normalized drive voltage rise.
表13から、ホスト材料として、電荷輸送材料であるサンプル2を用いた素子参考例1の有機EL素子は、従来のホスト材料を用いた素子比較例1−1,1−2の有機EL素子に比べて、輝度半減時間が長いことが分かる。また、その駆動電圧上昇も、従来良好な正孔阻止材料として知られた化合物(HB−12)を使用した場合と同程度であることが分かる。したがって、発光層5を、電荷輸送材料であるサンプル2とドーパントとで形成した素子参考例1の有機EL素子によれば、輝度半減時間の向上と駆動電圧上昇の抑制とをともに行なうことができること確認された。 Table 13, as a host material, electric load organic EL element of the element with sample 2 Example 1 is transporting materials, organic EL elements of the element Comparative Examples 1-1 and 1-2 using a conventional host materials It can be seen that the luminance half time is longer than In addition, it can be seen that the increase in driving voltage is comparable to the case where the compound (HB-12) known as a good hole blocking material is used. Therefore, the light-emitting layer 5, conductive according to charge transport material and a sample 2 and an organic EL element of the element in Example 1 was formed with a dopant, it is carried out together with the suppression of the driving voltage increase and improve the luminance half-life It was confirmed that it was possible.
また、表14から、正孔阻止材料として本発明の電荷輸送材料であるサンプル5,8を用いた素子実施例2,4の有機EL素子は、従来の正孔阻止材料を用いた素子比較例2,3の有機EL素子に比べて、輝度半減時間が長く、駆動電圧上昇が小さいことが分かる。したがって、正孔阻止層6を、本発明の電荷輸送材料のみから形成した素子実施例2,4の有機EL素子によれば、輝度半減時間の向上と駆動電圧上昇の抑制とをともに行なうことができること確認された。 Further, from Table 14, the organic EL elements of the device examples 2 and 4 using the samples 5 and 8 which are the charge transport materials of the present invention as the hole blocking material are comparative device examples using the conventional hole blocking material. It can be seen that the luminance half-life is long and the drive voltage rise is small compared to a few organic EL elements. Therefore, according to the organic EL elements of the device examples 2 and 4 in which the hole blocking layer 6 is formed only from the charge transport material of the present invention, it is possible to improve both the luminance half-life and suppress the drive voltage rise. It was confirmed that it was possible.
本発明の電荷輸送材料は、電荷輸送材料が用いられる任意の分野において用いることができ、特に、有機電界発光素子の材料として用いて好適である。さらに、本発明の電荷輸送材料は、本発明の電荷輸送材料が有する高い性能に加えて、非晶質性、溶解性、耐熱性、耐久性に優れている。したがって、本発明の電荷輸送材料は、電荷輸送材料用としてだけでなく、発光材料用、太陽電池材料用、バッテリー材料(電解液、電極、分離膜、安定剤など)用、医療用、塗料材料用、コーティング材料用、有機半導体材料用、トイレタリー材料用、帯電防止材料用、熱電素子材料用などにおいても有用である。 The charge transport material of the present invention can be used in any field where the charge transport material is used, and is particularly suitable as a material for an organic electroluminescence device. Furthermore, in addition to the high performance of the charge transport material of the present invention, the charge transport material of the present invention is excellent in amorphousness, solubility, heat resistance, and durability. Therefore, the charge transport material of the present invention is not only for charge transport materials, but also for light emitting materials, solar cell materials, battery materials (electrolytes, electrodes, separation membranes, stabilizers, etc.), medical uses, and coating materials. It is also useful for coating materials, coating materials, organic semiconductor materials, toiletry materials, antistatic materials, thermoelectric element materials, and the like.
また、本発明の有機電界発光素子は、駆動寿命が長く、駆動電圧上昇が抑制されているという利点を有する。よって、従来の有機電界発光素子が用いられる各種の分野、即ち、フラットパネル・ディスプレイ(例えば、OAコンピュータ用や壁掛けテレビ)、車載表示素子、携帯電話表示や面発光体としての特徴を活かした光源(例えば、複写機の光源、液晶ディスプレイや計器類のバックライト光源)、表示板、標識灯などの分野で好適に利用することができ、産業上有用である。 Moreover, the organic electroluminescent element of this invention has the advantage that a drive life is long and a drive voltage rise is suppressed. Therefore, various fields where conventional organic electroluminescent elements are used, that is, light sources utilizing the characteristics of flat panel displays (for example, for OA computers and wall-mounted televisions), in-vehicle display elements, mobile phone displays and surface light emitters. (For example, a light source of a copying machine, a backlight light source of a liquid crystal display or an instrument), a display panel, a marker lamp, etc., can be suitably used and is industrially useful.
1 基板
2 陽極
3 正孔注入層
4 正孔輸送層
5 発光層(有機発光層)
6 正孔阻止層
7 電子輸送層
8 陰極
DESCRIPTION OF SYMBOLS 1 Substrate 2 Anode 3 Hole injection layer 4 Hole transport layer 5 Light emitting layer (organic light emitting layer)
6 Hole blocking layer 7 Electron transport layer 8 Cathode
Claims (8)
ことを特徴とする、有機電界発光素子用電荷輸送材料。
ことを特徴とする、有機電界発光素子用電荷輸送材料。
ことを特徴とする、請求項1または請求項2に記載の有機電界発光素子用電荷輸送材料。 The organic electric field according to claim 1 or 2, wherein the group represented by the formula (1) is a raw material or intermediate of the pyridine compound or a group that substitutes the pyridine compound. Charge transport material for light-emitting elements .
ことを特徴とする、請求項1〜3のいずれか1項に記載の有機電界発光素子用電荷輸送材料。 The charge transport material for an organic electroluminescent element according to claim 1, wherein the group represented by the formula (1) is a methyl group or a methylene group.
ことを特徴とする、有機電界発光素子用積層体。 It has at least the layer formed only from the charge transport material for organic electroluminescent elements of any one of Claims 1-4, The laminated body for organic electroluminescent elements characterized by the above-mentioned.
ことを特徴とする、有機電界発光素子用積層体。 It has an organic light emitting layer formed from the charge transport material for organic electroluminescent elements of any one of Claims 1-4, and a dopant at least , The laminated body for organic electroluminescent elements characterized by the above-mentioned.
更に、請求項1〜4のいずれか1項に記載の有機電界発光素子用電荷輸送材料のみから形成された層を少なくとも1層有する
ことを特徴とする、有機電界発光素子。 On the substrate, an anode, a cathode, and an organic light emitting layer provided between the anode and the cathode,
Furthermore, the organic electroluminescent element characterized by having at least 1 layer formed only from the charge transport material for organic electroluminescent elements of any one of Claims 1-4.
ことを特徴とする、有機電界発光素子。 An organic material formed on a substrate between an anode, a cathode, the anode and the cathode, and formed from the charge transport material for an organic electroluminescence device according to any one of claims 1 to 4 and a dopant. An organic electroluminescent device comprising a light emitting layer.