JP4982057B2 - 塗装物、印刷物及びそれらに使用する塗料、インキ - Google Patents
塗装物、印刷物及びそれらに使用する塗料、インキ Download PDFInfo
- Publication number
- JP4982057B2 JP4982057B2 JP2005224219A JP2005224219A JP4982057B2 JP 4982057 B2 JP4982057 B2 JP 4982057B2 JP 2005224219 A JP2005224219 A JP 2005224219A JP 2005224219 A JP2005224219 A JP 2005224219A JP 4982057 B2 JP4982057 B2 JP 4982057B2
- Authority
- JP
- Japan
- Prior art keywords
- titanium dioxide
- ink
- weight
- particle size
- glossy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
即ち、前記特許文献等には、所定の樹脂に、金属顔料(金属単体からなる顔料)と所定の粒径の金属酸化物顔料とが配合されてなる塗料が開示されており、該塗料の塗布された塗装物が、ダウンフロップ性を呈する旨も記載されている。
この種の優れたダウンフロップ性は、印刷物においても同様に要望されている。
ここで、二次粒子の個数の80%以上が0.03〜1.50μmの粒度分布内に含まれているとは、個数を基準とする粒度分布において累積10%(d10)が0.03μm以上、累積90%(d90)が1.50μm以下であって、二次粒子が100個あれば80個以上が該範囲内に含まれることを意味する。
本発明において、金属顔料及び二酸化チタンの配合割合は、塗料、インキの全固形分中における割合(重量%)を意味する。
本発明において、塗装物とは表面に塗装が施されてなるものを意味し、印刷物とは表面に印刷が施されてなるものを意味する。また、塗料とは、表面の塗装に用いる組成物を意味し、インキとは、印刷に用いる組成物を意味する。
本発明において、光沢物とは光沢を有する表面を備えたものを意味する。ここで、光沢を有するとは、通常、JIS Z 8741(85度鏡面光沢度、好ましくは60度鏡面光沢度)に基づく鏡面光沢度が測定可能な範囲であることを意味する。従って、測定可能である限り、表面が平滑でない艶消し面であっても光沢を有する表面に含まれる。
本発明において、一次粒子径とは、原料として用いる二酸化チタンの平均粒子径と同義である。
本発明において、光沢を有する表面は、金属からなるものである。前記金属としては、金、銀、銅、アルミニウム、ニッケル、チタニウム、クロム合金(ステンレス)等及びこれらを含有する合金が好ましい。特に、ダウンフロップ性に優れるという観点から、金、銀、銅、アルミニウム及びこれらを含有する合金が好ましい。
前記被塗装物又は被印刷物としては、金属、ガラス、セラミックス、アスベスト、木材、紙、石、更には、プラスチック材料などいずれのものから構成されていてもよい。
尚、被塗装物又は被印刷物自体が、光沢を有する表面を備えている場合には、そのまま光沢物として採用できる。例えば、光沢を有するアルミニウム板、アルミニウム箔、アルミ蒸着紙、金箔、銀箔、銅箔、クロム合金板等であれば、そのまま光沢物として採用できる。
金属塗装を用いる場合、使用する金属表面層形成用の塗料として、例えば、全固形分中、樹脂10〜95重量%、アルミニウム、黄銅、ステンレス、銀等の金属顔料(金属フレーク顔料)1〜40重量%配合されたものを用いることができる。
なお、該樹脂としては、熱可塑性或いは熱硬化性のものを用いることができる。
この着色被膜は、金属顔料表面に、異種金属又は異種、同種の金属酸化物や金属窒化物を蒸着やスパッタリング等により付与したり、或いは着色顔料と樹脂バインダとで形成された着色剤を金属顔料表面に付与したりすること等により形成できる。
前記二酸化チタンは、有機処理剤または無機処理剤で表面処理(即ち、表面コーティング)したものを用いてもよい。 有機処理剤としては、脂肪酸、脂肪酸エステル、界面活性剤、金属石鹸、シリコーン樹脂、フッ素樹脂、アクリル樹脂、ポリエステル樹脂、シランカップリング剤、チタンカップリング剤等を挙げることができる。また、無機処理剤としては、アルミナ、シリカ、ジルコニア等を挙げることができる。
具体的には、表面処理ルチル型酸化チタン、石原産業(株)製:商品名「TTOシリーズ」、テイカ(株)製:商品名「MTシリーズ」等を挙げることができる。
なお、前記二酸化チタンは、アナターゼ型よりもルチル型が好ましい。
また、該一次粒子径が1〜19nmの二酸化チタンを使用した場合は、一次粒子径が20nm以上の二酸化チタンを使用した場合に比べるとダウンフロップ性は若干劣りはするものの、一次粒子径が20nm以上の二酸化チタンを使用した場合に起こる光沢物の色が何色であれ、全体的に僅かに金色味を帯びて見えるという現象が殆ど起こらず、意匠性の幅が広がる。
尚、一次粒子径の変動係数は、60%以下が好ましく、更に好ましくは45%以下である。ここで変動係数は(一次粒子径の標準偏差)/(一次粒子径)×100(%)により定義される。
ここで、一次粒子径は、実施例記載の方法により測定される。
尚、所定粒子径の二酸化チタンは、コロイド法(化学処方)、硫酸法、塩素法等により調製される。
斯かる範囲であれば、より優れたダウンフロップ性を呈する。
一方、二酸化チタンの配合量が0.1重量%未満であれば、光沢物等への付着量を増やしても十分なダウンフロップ性を呈し得ず、70重量%を超える場合には、塗料等としての作業性、付着性等が極端に低下する。
二次粒子の粒径の80%以上が0.03〜1.50μmの粒度分布内に含まれておれば、深みがあり、且つ、透明感に優れたダウンフロップ性を呈する。更に、高級感を有するため意匠性にも優れている。
なお、二次粒子及び該二次粒子の粒度分布は、実施例記載の方法により測定される。
前記塗料用ビヒクルとしては、アクリル、アルキド、ポリエステル、アクリルメラミン、ウレタン、シリコーン、エポキシ、不飽和ポリエステル、アクリルモノマー、アクリルオリゴマー、フッ素系等の樹脂を挙げることができる。
また、前記インキ用ビヒクルとしては、アクリル、ポリアミド、不飽和ポリエステル、アクリルモノマー、アクリルオリゴマー、塩酢ビ(塩化ビニルと酢酸ビニルとの共重合物)、塩素化ポリプロピレン、ウレタン、セルロース誘導体、マレイン酸誘導体、ロジン誘導体、樹脂ワニス等を挙げることができる。
該ビヒクルは、二酸化チタンと顔料とを分散させるものである。
該ビヒクルは、前記樹脂と必要に応じて架橋剤等とから構成されている。
二酸化チタンの配合量が、0.5重量部未満であれば、ダウンフロップ性を示さなくなる。
二酸化チタンの配合量が、60重量部を超えると透明性を示さなくなる。 また、前記二酸化チタンと前記ビヒクルとの配合量は、インキの場合、ビヒクル100重量部に対して、二酸化チタン0.5〜200重量部であり、好ましくはビヒクル100重量部に対して、二酸化チタン10〜100重量部である。
二酸化チタンの配合量が、0.5重量部未満であれば、ダウンフロップ性を示さなくなる。二酸化チタンの配合量が、200重量部を超えると透明性を示さなくなる。
分散剤としては、ポリアクリル酸系、ポリアルキレンポリアミン系、ナフタレンスルホン酸ホルマリン縮合物、ポリスチレンスルホン酸塩、脂肪酸金属石鹸、ポリリン酸ソーダ、アルキルベンゼンスルホン酸、カルボキシメチルセルロース、ひまし油誘導体、ソルビタンエステル、コハク酸エステル、脂肪酸アミン系、スルホン酸アミド系、ε−カプロラクタム系、ハイドロステアリン酸系、ポリカルボン酸系、ポリビニルアルコール等の各種分散剤を用いることができる。
具体的には、アビシア社製:商品名「ソルスパース3000、9000、17000、20000、24000」、ビックケミー社製:商品名「Disperbyk−161、−162、−163、−164」等を挙げることができる。
分散剤を加えることにより、二次粒子の凝集を防止し、該二次粒子を安定化させることができる。
分散剤の配合量が、0.5重量部未満であれば、二次粒子の凝集を防止できず、該二次粒子の径が大きくなる虞がある。
分散剤の配合量が、10重量部を超えると、塗料やインキの耐光性、密着性等の諸物性を低下させる虞がある。
二次粒子の粒子径を調整する方法は、例えば、ボールミルを用いた場合には、粉砕時間、ボールミルの中に入れるボールの量等で調整することができる。
また、本実施形態の印刷物におけるインキの乾燥膜厚としては、該インキに含まれるビヒクル100重量部に対して二酸化チタンが0.5〜50重量部未満のインキを用いた場合は、0.5〜10μm、好ましくは5μm以下であり、該インキに含まれるビヒクル100重量部に対して二酸化チタンが50〜200重量部のインキを用いた場合は、2μm以下が好ましい。
ここで、金属顔料とは、酸化されていない金属単体からなる顔料を意味し、該金属顔料としては、金属フレーク、金属被覆粒子等を、具体的には、アルミニウムフレーク顔料を挙げることができる。
そのため、カラーコピー機等で複写しても、視角によって大きく色調が変化するものが得られないため、偽造が困難な印刷物等になる。
添加剤としては、例えば、消泡剤、沈降防止剤、つや消し剤、ブロッキング防止剤、レベリング剤等を挙げることができる。
また、予め前記塗料をフィルム状等の成形体に成形し、該成形体を光沢物の表面に積層させてもよく、さらに、前記成形体の裏側に液状の光沢物を塗布・硬化させてもよい。
前記樹脂フィルムとしては、着色顔料又は着色染料等が配合された有色透明な樹脂フィルムが好ましい。
斯かる構成からなる塗装物又は印刷物は、光沢物から金属光沢を呈すると共に、有色透明な層(樹脂フィルムの層)によって、メタリックカラーを呈するものとなり、しかも、前記二酸化チタンが配合された塗料等の層によって、偏光する色彩が更に多色化した装飾性の極めて優れたものとなる。
該クリヤー層を備えることにより、耐食性、耐候性、耐衝撃性に優れたものとなる。
従って、自動車の外装等にも適用できる。
前記クリヤー層は、例えば、熱硬化性樹脂、常温硬化性樹脂等の樹脂を吹き付けたり、はけ塗りしたり、更には、透明な樹脂フィルムを貼着すること等により形成できる。
尚、本発明に係る塗料及びインキは、例えば、自動車、缶、装飾品、コンテナ、看板、包装材、ラベル、カタログ、容器、家電製品、通信機器、筆記具、絵の具、マニキュア等の表面装飾に適用できる。
一次粒子の分布は、電子顕微鏡による一次粒子の画像を「画像解析装置(ルーゼックスAP、ニレコ社製)により解析し、ランダムに配向した一次粒子を一定軸方向の長さについて測定する「定方向径」を用いて、個数を基準でd10、d50、d90を求めた。
また、一次粒子径は、個数を基準で累積50%(d50)値とした。
二次粒子の粒度分布(d10、d90)は、マイクロトラックUPA150粒度分析計(日機装株式会社製、測定範囲0.003〜6μmの範囲をレーザードップラー/周波数解析法で測定)を用い、希釈溶剤10ml中に測定試料5滴をスポイトで滴下し、超音波をかけて均一に希釈してから、測定用セルに入れ、3分後に測定して求めた。
(インキ調整法)
表面処理ルチル型酸化チタン(一次粒子径0.040μm)15重量部、商品名「REX−21」(合同インキ製グラビアインキメジュウム、NV(非揮発成分)17%)100重量部、溶剤(トルエン/イソプロピルアルコール/酢酸エチルの混合溶媒)5重量部、1.6mm径チタンビーズ150重量部を200mlガラス製マヨネーズ瓶に仕込み、ペイントシェーカー(東洋精機社製)を用いて3時間分散した。
(粒度分布測定)
上記の方法で調整したインキの二次粒子の粒径の粒度分布は、個数を基準とする粒度分布において累積10%(d10)が0.04μm、累積90%(d90)が0.50μmであった。
(透明性測定)
ポリエチレンテレフタレート(PET)フィルムにバーコーターを用いて、上記方法で調整したインキを塗布、自然乾燥後のインキ厚が約1μmになるようにした。
塗布後のPETフィルムを透過濃度計(Kollmorgen社製、商品名「Macbeth TR927」)を用いて測定した。測定値は、0.21であった。
なお、測定値が0.23以上の場合には、透明性不良と判定した。
(ダウンフロップ性評価)
PETフィルムにバーコーターを用いて、上記方法で調整したインキを自然乾燥後のインキ厚が約1μmになるように、前記フィルムの一面に塗布し、該フィルムの他面にアルミ蒸着紙(パナック社製、商品名「メタルミー75TS」、厚み75μm)を積層した。
積層したフィルムを変角測色計(X−Rite社製、「MA60」)を用いて、観測角15度(フェイスカラー)と観測角110度(フロップカラー)の差(△b)を求めた。
その結果、△bは34であった。
△bが25以上あればダウンフロップ性が大きいとした。
上記測定及び評価の結果を表1に記載した。
ペイントシェーカー(東洋精機社製)を用いて5時間分散した以外は、実施例1と同様に行った。得られたフィルムを用いて実施例1と同様の測定及び評価を行った。
二次粒子の粒径の粒度分布は、個数を基準とする粒度分布において累積10%(d10)が0.03μm、累積90%(d90)が0.20μmであった。
測定及び評価の結果を表1に記載した。
表面処理ルチル型酸化チタン(一次粒子径0.015μm)3.5重量部、ATニス(武蔵塗料製アクリルメラミン塗料、NV48%)89重量部、溶剤(メトキシプロピルアセテート)6.5重量部、分散剤(ソルスパーズ20000)0.5重量部、1.6mm径チタンビーズ200重量部をガラス製マヨネーズ瓶に仕込み、ペイントシェーカー(東洋精機社製)を用いて3時間分散した。
(粒度分布測定)
上記の方法で調整した塗料の二次粒子の粒径の粒度分布は、個数を基準とする粒度分布において累積10%(d10)が0.06μm、累積90%(d90)が0.40μmであった。
(透明性測定及びダウンフロップ性評価)
ポリエチレンテレフタレート(PET)フィルムにバーコーターを用いて、上記方法で調整した塗料を塗布、自然乾燥後の塗膜厚が約10μmになるようにした以外、実施例1と同様の方法で測定及び評価を行い、その結果を表1に記載した。
表面処理ルチル型酸化チタン(一次粒子径0.035μm)を用いた以外は、実施例3と同様の方法により試料を作製し、同様の測定及び評価を行い、その結果を表1に示した。
二次粒子の粒径の粒度分布は、個数を基準とする粒度分布において累積10%(d10)が0.10μm、累積90%(d90)が1.00μmであった。
アルミナ、ジルコニア処理した表面処理ルチル型酸化チタン(一次粒子径0.055μm)25重量部、紫外線硬化樹脂(東南インキ社製、商品名「UVワニス」、ロジン変性フェノール樹脂とエポキシアクリレートの混合物)25重量部、トリメチロールプロパントリアクリレートとネオペンチルジアクリレートの1対1混合物)30重量部、光重合開始剤(チバスペシャルティー・ケミカルズ社製、商品名「イルガキュアー」)10重量部、補助剤(安定剤等の添加剤)5重量部を三本ミルで混練し、UVインキを作製した。
二次粒子の粒径の粒度分布は、個数を基準とする粒度分布において累積10%(d10)が0.08μm、累積90%(d90)が1.00μmであった。
前記UVインキを用いてPETフィルムに乾燥後のインキ厚が2μmになるようにオフセット印刷し、実施例1と同様の測定及び評価を行った。
その結果を表1に示した。
アルミナ、ジルコニア処理した表面処理ルチル型酸化チタン(一次粒子径0.054μm、一次粒子の分布は、個数を基準とする粒度分布において累積10%(d10)が0.03μm、累積90%(d90)が0.08μm)8重量部、インク樹脂((株)ミノグループ製、商品名「UPGL」、樹脂分50重量%)200重量部、分散剤(ソルスパース24000)4重量部を用いて実施例3と同様の方法を用いてインクを調整した。
二次粒子の粒径の粒度分布は、個数を基準とする粒度分布において累積10%(d10)が0.1μm、累積90%(d90)が0.7μmであった。
前記インクを用いてPETフィルムに300メッシュスクリーンを用いて該インクを塗布し、自然乾燥後のインク厚が約5μmになるように印刷し、実施例1と同様の測定及び評価を行った。
その結果を表1に示した。
ここで、一次粒子の分布は、個数を基準とする粒度分布において累積10%(d10)が0.03μm、個数を基準とする累積90%(d90)が0.08μmであって、一次粒子が100個あれば80個以上が該範囲内に含まれることを意味する。
表面処理ルチル型酸化チタン(一次粒子径0.15μm)4重量部、ATニス(武蔵塗料製アクリルメラミン塗料、NV48%)89重量部、溶剤(メトキシプロピルアセテート)7重量部、1.6mm径チタンビーズ200重量部をガラス製マヨネーズ瓶に仕込み、ペイントシェーカーを用いて3時間分散して試料を得た。
なお、二次粒子の粒径の粒度分布は、個数を基準とする粒度分布において累積10%
(d10)が0.07μm、累積90%(d90)が2.1μmであった。その内の75%が0.03〜1.50μmの粒度分布内に含まれていた。
上記試料を用いて実施例3と同様の測定及び評価を行った。
その結果を表1に示した。
表面処理ルチル型酸化チタン(一次粒子径0.015μm)を用いた以外は、比較例1と同様方法で試料を得て、該試料を用いて実施例3と同様の測定及び評価を行った。
なお、二次粒子の粒径の粒度分布は、個数を基準とする粒度分布において累積10%
(d10)が0.10μm、累積90%(d90)が3.4μmであった。
その内の31%が0.03〜1.50μmの粒度分布内に含まれていた。
その結果を表1に示した。
表面処理ルチル型酸化チタン(一次粒子径0.015μm)を用いた以外は、実施例5と同様方法で試料を得て、該試料を用いて実施例5と同様の測定及び評価を行った。
なお、二次粒子の粒径の粒度分布は、個数を基準とする粒度分布において累積10%
(d10)が0.01μm、累積90%(d90)が0.06μmであった。
その内の12%が0.03〜1.50μmの粒度分布内に含まれていた。
その結果を表1に示した。
表面処理ルチル型酸化チタン(一次粒子径0.16μm、一次粒子の分布は、個数を基準とする粒度分布において累積10%(d10)が0.10μm、累積90%(d90)が0.20μm)を用いた以外は、実施例5と同様方法で試料を得て、該試料を用いて実施例5と同様の測定及び評価を行った。
なお、二次粒子の粒径は、個数を基準とする粒度分布において累積10%(d10)が0.15μm、累積90%(d90)が1.82μmであった。
その結果を表1に示した。
ルチル型酸化チタン(一次粒子径0.19μm、一次粒子の分布は、個数を基準とする粒度分布において累積10%(d10)が0.03μm、累積90%(d90)が0.25μm)を用い、分散剤を用いなかった以外は、実施例6と同様方法で試料を得て、該試料を用いて実施例5と同様の測定及び評価を行った。
なお、二次粒子の粒径は、個数を基準とする粒度分布において累積10%(d10)が0.15μm、累積90%(d90)が1.40μmであった。
その結果を表1に示した。
Claims (11)
- 金属顔料と樹脂とを含有する金属表面層を備えた光沢物に塗料が塗布されてなる塗装物であって、
前記塗料は、一次粒子径10〜60nmの表面処理されたルチル型二酸化チタンが1〜55重量%配合されており、且つ、前記二酸化チタンが、ビヒクルに分散することで二次粒子となっており、該二次粒子の個数の80%以上が0.03〜1.50μmの粒度分布内に含まれていることを特徴とする塗装物。 - 前記二酸化チタンの一次粒子径が35〜55nmである請求項1記載の塗装物。
- 前記二酸化チタンをビヒクルに分散させる分散剤が用いられている請求項1又は2に記載の塗装物。
- 前記二酸化チタンは、アルミナ及びジルコニアで表面処理された表面処理ルチル型二酸化チタンである請求項1〜3の何れかに記載の塗装物。
- 前記光沢物は、全固形分中アルミニウム金属顔料が1〜40重量%、樹脂が10〜95重量%配合されてなる金属表面層形成用の塗料を塗装して形成されている請求項1〜4の何れかに記載の塗装物。
- 金属光沢を有する表面を備えた光沢物にインキが塗布されてなる印刷物であって、
前記インキは、一次粒子径10〜60nmの表面処理されたルチル型二酸化チタンが1〜55重量%配合されており、且つ、前記二酸化チタンが、ビヒクルに分散することで二次粒子となっており、該二次粒子の個数の80%以上が0.03〜1.50μmの粒度分布内に含まれていることを特徴とする印刷物。 - 前記二酸化チタンの一次粒子径が35〜55nmである請求項6記載の印刷物。
- 前記二酸化チタンをビヒクルに分散させる分散剤が用いられている請求項6又は7に記載の印刷物。
- 前記二酸化チタンは、アルミナ及びジルコニアで表面処理された表面処理ルチル型二酸化チタンである請求項6〜8の何れかに記載の印刷物。
- 前記インキを、オフセット印刷又はインクジェット印刷により前記光沢物に塗布する請求項6〜9の何れかに記載の印刷物。
- 前記光沢物は、アルミ蒸着物又はアルミニウム箔である請求項6〜10の何れかに記載の印刷物。