JP4919974B2 - サイド部補強層及びランフラットタイヤ及びサイド部補強層の製造方法 - Google Patents
サイド部補強層及びランフラットタイヤ及びサイド部補強層の製造方法 Download PDFInfo
- Publication number
- JP4919974B2 JP4919974B2 JP2008000113A JP2008000113A JP4919974B2 JP 4919974 B2 JP4919974 B2 JP 4919974B2 JP 2008000113 A JP2008000113 A JP 2008000113A JP 2008000113 A JP2008000113 A JP 2008000113A JP 4919974 B2 JP4919974 B2 JP 4919974B2
- Authority
- JP
- Japan
- Prior art keywords
- tire
- mass
- rubber
- carcass
- run
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
(ただし、Nは上撚り数(回/10cm)、Dはトータル表示デシテックス(繊度)、ρはコード材料の比重である。)
前記カーカスプライの前記トッピングゴムは、複素弾性率(E*)が5〜13MPaの範囲とすることが好ましい。
0.1< Y75 /SH ≦0.2
0.2< Y90 /SH ≦0.4
0.4< Y100/SH ≦0.7
なお前記「正規リム」とは、タイヤ規格を含む規格体系において、当該規格がタイヤごとに定めるリムであり、例えばJATMAであれば標準リム、TRAであれば "Design Rim" 、或いはETRTOであれば "Measuring Rim"を意味する。また前記「正規内圧」とは、前記規格がタイヤごとに定めている空気圧であり、JATMAであれば最高空気圧、TRAであれば表 "TIRE LOAD LIMITS AT VARIOUS COLD INFLATION PRESSURES" に記載の最大値、ETRTOであれば "INFLATION PRESSURE" を意味するが、乗用車用タイヤの場合には180kPaとする。
前記サイド部補強層のゴム組成物において、ゴム成分中における天然ゴム(NR)および/またはポリイソプレンゴム(IR)の含有率は20質量%〜80質量%であることが好ましい。天然ゴム(NR)および/またはポリイソプレンゴム(IR)の含有率が、20質量%未満では、ゴム組成物の伸び率が低く、生産性が低下する傾向がある。また、該含有率はゴム成分中に80質量%を超えるとランフラット走行時の発熱により、ゴムが劣化しランフラット性能が低下する傾向がある。
前記サイド部補強層のゴム組成物は、ゴム成分100質量部に対して、ポリパラフェニレンテレフタラミド(PPTA)の補強材を0.1〜50質量部配合される。ここで補強材は、ポリパラフェニレンテレフタラミド(PPTA)自体、あるいはポリパラフェニレンテレフタラミド(PPTA)とステアリン酸を含むマスターバッチとして使用される。
ゾリルスルフェンアミド)、DZ(N,N’−ジシクロヘキシル−2−ベンゾチアゾリルスルフェンアミド)などが挙げられる。その他の加硫促進剤としては、たとえば、MBT(メルカプトベンゾチアゾール)、MBTS(ジベンゾチアジルジスルフィド)、DPG(ジフェニルグアニジン)などを用いることができる。
本発明に用いられるカーボンブラックは、特に限定されないが、ゴム組成物を低発熱に維持するため、FEF、FPFなどのソフトカーボンが好ましい。例えば、窒素吸着比表面積(N2SA)は、30m2/g以上であり、好ましくは35m2/g以上である。N2SAが30m2/g未満では補強性が不足し、充分な耐久性が得られない。また、該カーボンブラックのN2SAは、100m2/g以下であり、好ましくは80m2/g以下、より好
ましくは60m2/g以下である。N2SAが100m2/gをこえると、発熱性が高くなる。
本発明のゴム組成物に用いられる硫黄または硫黄化合物としては、硫黄の表面析出を抑えるという観点から不溶性硫黄が好ましい。不溶性硫黄は、平均分子量が10000以上、特には100000以上で、500000以下、特には300000以下が好ましい。平均分子量が10000未満では、低温での分解が起こりやすく表面析出しやすい傾向があり、500000をこえるとゴム中での分散性が低下する傾向がある。
本発明のゴム組成物は、汎用ゴム一般に用いられているシリカを使用することができる。たとえば乾式法ホワイトカーボン、湿式法ホワイトカーボン、コロイダルシリカ等が挙げられる。なかでも含水ケイ酸を主成分とする湿式法ホワイトカーボンが好ましい。
前記サイド部補強層のゴム組成物の複素弾性率(E*)は、10Mpa以上であり、さらに損失弾性率(E")および複素弾性率(E*)は、下記式を満たすことが好ましい。
特に、 E"/(E*)2 ≦6.8×10-9Pa-1 であることが好ましい。
<ランフラットタイヤ>
以下、本発明の実施の一形態を、図示例とともに説明する。図1は、本発明のランフラットタイヤ1示す正規内圧状態におけるタイヤ子午断面図である。
そして、この撚り係数Tを0.5〜0.8の範囲まで高めることにより、アラミド繊維コードの欠点である耐疲労性を改善することができ、従来のレーヨンコードの場合に比して、ランフラット耐久性を大幅に向上することが可能となる。なお前記カーカスコード20の撚り係数Tが0.5を下回ると、耐疲労性の向上効果が少なく、ランフラット耐久性を充分に高めることができない。逆に、撚り係数Tが0.8を上回ると、コードの撚り加工が難しくなり生産性に不利となる。特に撚り係数Tの下限は0.6以上が好ましく、これによりコードの耐疲労性がさらに改善され、ランフラット耐久性をより向上しうる。
0.1< Y75 /SH ≦0.2
0.2< Y90 /SH ≦0.4
0.4< Y100 /SH ≦0.7
ここで、RY60=Y60/SH
RY75=Y75/SH
RY90=Y90/SH
RY100 =Y100 /SH
として前記関係を満足する範囲RYiを図4に例示する。図3、4のように前記関係を満足するプロファイルは、トレッドが非常に丸くなるため、フットプリントが、接地巾が小かつ接地長さを大とした縦長楕円形状となり、騒音性能とハイドロプレーニング性能とを向上しうることが、前記特許第2994989号公報で報告されている。なお前記RY60、RY75、RY90及びRY100 の値が、各下限値を下回ると、トレッド部2を中心としてタイヤ外面2Aが平坦化するため、従来タイヤとのプロファイルの差が少なくなる。逆に各上限値を上回ると、トレッド部2を中心としてタイヤ外面2Aが著しく凸状をなすため、接地巾が過小となり、通常走行において必要な走行性能を確保することができなくなる。
<ポリパラフェニレンテレフタラミド(PPTA)マスターバッチの調整>
ポリパラフェニレンテレフタラミド(PPTA)とステアリン酸を含むマスターバッチを表1の配合に基づき調整した。
(注3)加硫促進剤:大内新興化学工業社製の「NS」。
(注5)ステアリン酸:日本油脂(株)社製の「椿」。
<ゴム組成物の製造>
表2に示す配合内容にしたがって、バンバリーミキサーを用いて、不溶性硫黄および加硫促進剤以外の成分を、150℃で4分間混練りした。次のオープンロールを用いて、得られた混練物に硫黄と加硫促進剤を加えて、80℃で3分間練り込んで未加硫ゴム組成物1〜4を得て、タイヤの試作に用いた。
、破断時強度、粘弾性特性の評価を行った。
<ランフラットタイヤの製造>
サイド部補強層として、表2に示すはゴム配合1〜4を用いて、ライニングストリップ層の形状に成形し、タイヤの他の部材と共に貼り合わせて、診加硫タイヤを成形した。この成形タイヤを160℃で120分間プレス加硫をし、サイズが215/45ZR17のランフラットタイヤを製造した。
(注2)SBR−1:JSR社製の商品名「SL574」(1,2−シンジオタクチックポリブタジエン結晶含量は0質量%)。
(注3)BR:宇部興産社製の「VCR412」
(注4)カーボンブラック(FEF):三菱化学(株)製のダイヤブラックE(N2SA41m2/g、DBP吸油量115ml/100g)。
(注5)ステアリン酸:日本油脂(株)製の「椿」。
(注6)酸化亜鉛:三井金属鉱業(株)製の「酸化亜鉛2種」。
(注7)老化防止剤:住友化学工業(株)製のアンチゲン6C、N−(1,3−ジメチルブチル)−N’−フェニル−p−フェニレンジアミン。
(注8)ポリパラフェニレンテレフタラミド(PPTA)マスターバッチ:表1の配合による。
(注9)硫黄:四国化成工業(株)製の不溶性硫黄「ミュークロンOT」。
(注10)加硫促進剤:大内新興化学工業(株)製のノクセラーNS(N−tert−ブチル−2−ベンゾチアゾリルスルフェンアミド)。
<粘弾性特性>
前記配合1〜4によって調整されたサイド部補強層のゴム試験片を、(株)岩本製作所製の粘弾性スペクトロメータを用いて、測定温度70℃、初期歪み10%、動歪み±1%、周波数10HzにてE"(損失弾性率)、E*(複素弾性率)、tanδを測定し、E"/(E*)2をもとめた。
<破断時強度>
JIS−K6251「加硫ゴム及び熱可塑性ゴム−引張特性の求め方」に準じて、前記加硫ゴムシートからなる3号ダンベル型試験片を用いて、引張試験を実施し、23℃における破断時強度(TB)を測定した。
<ランフラット耐久性>
各供試タイヤを空気内圧0kPaにてドラム試験機上を、縦荷重(4.14kN)で、
速度80km/hで走行させ、タイヤが破壊するまでの走行距離を測定し、比較例1を100とする指数により、下記計算式により各実施例、比較例を評価した。数値が大きいほどランフラット耐久性は良好である。
実施例3〜7、比較例3〜7
実施例1、比較例1に用いた配合1と配合3のサイド部補強層を使用し、カーカスプライの材料、構造を変更したランフラットタイヤを実施例1と同様にして製造した。
ベルト層:スチールコードのベルトプライが2枚、コード角度はタイヤ周方向に24°で相互に反対方向に積層。
表3中、撚り係数Tは次式(1)で表される。
又レーヨン繊維コードの比重ρは1.51,アラミド繊維コードの比重ρは1.44である。
ランフラット耐久性は、実施例1と同様な方法で評価した。
Claims (9)
- トレッド部からサイドウォール部をとおりビード部のビードコアに至るカーカスと、トレッド部の内方かつ前記カーカスの半径方向外側に配されるベルト層と、サイドウォール部かつ前記カーカスの内側に配され最大厚さを有する中央部分から半径方向内外に厚さを減じて延びる断面三日月状のサイド部補強層を備えたランフラットタイヤ用のサイド部補強層であって、
天然ゴムおよび/またはポリイソプレンゴムを20〜80質量%と、ポリブタジエンゴムを80〜20質量%を含むゴム成分100質量部に対して、ポリパラフェニレンテレフタラミドの補強材を0.1〜50質量部、カーボンブラックを10〜80質量部およびシランカップリング剤を配合したゴム組成物よりなり、
前記補強材はポリパラフェニレンテレフタラミド10〜80質量%、ステアリン酸10〜60質量%、シランカプリング剤0.5〜15質量%、加硫促進剤0.1〜2質量%および0.05〜2質量%の硫黄を含むマスターバッチとして混合してなる、サイド部補強層。 - ゴム組成物の複素弾性率(E * )が10Mpa以上である請求項1に記載のサイド部補強層。
- 請求項1または2のサイド部補強層を用いたランフラットタイヤ。
- 前記カーカスは、タイヤ周方向に対して45〜90°の角度で配列したカーカスコードをトッピングゴムで被覆したカーカスプライからなるとともに、前記カーカスコードは、アラミド繊維コードである請求項3記載のランフラットタイヤ。
- 前記カーカスコードは、下撚りしたフィラメント束の2本を、上撚りにて互いに撚り合わせた2本撚り構造をなすことを特徴とする請求項4記載のランフラットタイヤ。
- 前記カーカスコードは、次式(1)で示す撚り係数Tを0.5〜0.8の範囲としたことを特徴とする請求項4または5記載のランフラットタイヤ。
T=N×√{(0.125×D/2)/ρ}×10-3 ・・・(1)
(ただし、Nは上撚り数(回/10cm)、Dはトータル表示デシテックス(繊度)、ρは
コード材料の比重である。) - 前記カーカスプライの前記トッピングゴムは、複素弾性率(E * )が5〜13MPaの範囲としたことを特徴とする請求項4〜6のいずれかに記載のランフラットタイヤ。
- 正規リムに装着され、かつ正規内圧を充填した正規内圧状態におけるタイヤ子午断面において、
タイヤ赤道面Cからタイヤ最大断面巾SWの45%の距離SPを隔てるタイヤ外面上の点をPとするとき、タイヤ外面の曲率半径RCが、前記タイヤ外面がタイヤ赤道面Cと交わる赤道点CPから前記点Pに至るまで徐々に減少するとともに、
前記タイヤ赤道面Cから前記タイヤ最大断面巾SWの半巾(SW/2)の60%、75%、90%及び100%の距離X60、X75、X90およびX100を夫々隔てるタイヤ外面上
の各点と、前記赤道点CPにおけるタイヤ赤道面Cに対する垂線CXとの間の各半径方向距離をそれぞれY60、Y75、Y90及びY100とし、かつタイヤ断面高さSHと以下の関係
満足することを特徴とする請求項3〜7のいずれかに記載のランフラットタイヤ。
0.05< Y60 /SH ≦0.1
0.1< Y75 /SH ≦0.2
0.2< Y90 /SH ≦0.4
0.4< Y100 /SH ≦0.7 - トレッド部からサイドウォール部をとおりビード部のビードコアに至るカーカスと、トレッド部の内方かつ前記カーカスの半径方向外側に配されるベルト層と、サイドウォール部かつ前記カーカスの内側に配され最大厚さを有する中央部分から半径方向内外に厚さを減じて延びる断面三日月状のサイド部補強層を備えたランフラットタイヤ用のサイド部補強層の製造方法であって、
ポリパラフェニレンテレフタラミド10〜80質量%、ステアリン酸10〜60質量%、シランカプリング剤0.5〜15質量%、加硫促進剤0.1〜2質量%および0.05〜2質量%の硫黄を含むマスターバッチを調整する工程と、
前記マスターバッチと、天然ゴムおよび/またはポリイソプレンゴムと、ポリブタジエンゴムと、カーボンブラックとを混合してゴム組成物を調整する工程を含み、
前記ゴム組成物は天然ゴムおよび/またはポリイソプレンゴムの20〜80質量%と、ポリブタジエンゴムの80〜20質量%を含むゴム成分100質量部に対して、ポリパラフェニレンテレフタラミドの補強材を0.1〜50質量部、カーボンブラックを10〜80質量部およびシランカップリング剤を配合したゴム組成物であるランフラットタイヤ用のサイド部補強層の製造方法。