JP4748470B2 - Decorative plastic molding - Google Patents

Decorative plastic molding Download PDF

Info

Publication number
JP4748470B2
JP4748470B2 JP2003183858A JP2003183858A JP4748470B2 JP 4748470 B2 JP4748470 B2 JP 4748470B2 JP 2003183858 A JP2003183858 A JP 2003183858A JP 2003183858 A JP2003183858 A JP 2003183858A JP 4748470 B2 JP4748470 B2 JP 4748470B2
Authority
JP
Japan
Prior art keywords
film
plastic molded
molded
vapor deposition
metal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP2003183858A
Other languages
Japanese (ja)
Other versions
JP2005015867A (en
Inventor
伸治 嶋田
英芳 川島
Original Assignee
株式会社吉野工業所
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社吉野工業所 filed Critical 株式会社吉野工業所
Priority to JP2003183858A priority Critical patent/JP4748470B2/en
Publication of JP2005015867A publication Critical patent/JP2005015867A/en
Application granted granted Critical
Publication of JP4748470B2 publication Critical patent/JP4748470B2/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Description

【0001】
【発明の属する技術分野】
本発明は、表面が金属を主体とする蒸着膜により加飾されたプラスチック成形品に関する。
【0002】
【従来の技術】
従来より、プラスチック成形品の外表面全体あるいは一部に金属を蒸着して、メタリック様に加飾したり、鏡状にしたり、あるいは所謂ハーフミラー状にしたりしてプラスチック成形品の加飾あるいは機能化が一般的に行なわれている。
【0003】
たとえば、特許文献1には車両用灯具の一部材として使用する、光透過性プラスチック成形品に金属を薄く蒸着(以下ハーフ蒸着という。)したハーフミラーに関する記載がある。
【0004】
【特許文献1】
特開2003−115206号公報
【0005】
【発明が解決しようとする課題】
しかしながら、特許文献1記載のハーフミラーにおいても、従来の技術は基本的には金属の蒸着によりプラスチックにメタリック様な感じを付与するものであるが、本願発明者らは、蒸着の条件等により特には光透過性プラスチックの成形品に様々な装飾的効果、特には出色効果を付与できることを発見し本願発明に至った。
【0006】
すなわち、本発明は、光透過性プラスチック成形品への金属蒸着による出色効果を付与することを技術的課題とし、もって独特の装飾性、高級感の付与されたプラスチック成形品を提供することを目的とする。
【0007】
【課題を解決するための手段】
上記技術的課題を解決する本発明の内、第1の発明の手段は、
表面に金属を主成分とする蒸着膜が形成された光透過性のプラスチック成形品であって、光線透過率を蒸着膜形成前の光線透過率の65〜75%の範囲とし、蒸着膜により金属の種類により特定される色合いを現出させて加飾したこと、にある。
【0008】
第1の発明の上記構成により、光線透過率を蒸着膜形成前の光線透過率の65〜75%の範囲とすることにより、すなわち反射鏡やハーフミラーにおけるよりも蒸着膜の膜厚を薄くすることにより、見る方向によっては若干のメタル様の感じを付与させながら、優れた透明性を保持した状態で、使用する金属による独特な色合いを出色させることができる。
【0009】
蒸着には各種の金属、合金化合物が適応でき、その材料に限定はなく、通常アルミニウム、銀、金、銅、ロジューム、クロム、ニッケル、白金、チタン、モリブデン、タングステン等の各種金属やその合金、あるいは酸化珪素、酸化スズ、酸化セリューム、酸化チタン、酸化亜鉛、硫化亜鉛、弗化マグネシューム等の各種化合物を目的に応じて使用できる。
【0010】
たとえばアルミニウムでは黒色、クロムおよびチタンでは青、鉄では赤系統の色を出色させることができる。
【0011】
ここで全光線透過率を蒸着膜形成前の全光線透過率の65〜75%の範囲としたのは75%を超えると出色が十分でなくなること、また65%未満では全体としてメタリック様の感触と成ってしまい、それぞれの金属に特有な出色性が損なわれるためである。
【0012】
また光透過性プラスチックとしては特に限定されるものでなく、たとえばポリカーボネイト樹脂、アクリル樹脂、ポリスチレン系樹脂、ポリエステル系樹脂等の透明または半透明な樹脂を使用することができ、また大きく透明性を損なわない範囲で着色のための染料あるいは顔料による着色したものを使用することもでき、金属による出色と組み合わせて様々な色合いを出すことができる。
【0013】
第2の発明の手段は第1の発明において、真空蒸着法により蒸着膜が形成されていること、にある。
【0014】
第2の発明の上記構成により、真空蒸着法により、例えば容器等の湾曲性の形状を有した成形品であっても、たとえば成形品を公転および自転を組み合わせた回転装置に取り付けることにより成形品の外表面全体に略均一に蒸着膜を形成することができる。
【0015】
第3の発明の手段は、第1または3の発明において、異種金属を組み合わせた蒸着法により蒸着膜が形成されていること、にある。
【0016】
第3の発明の上記構成により、金属により出色する色合いが異なり、また金属によって成形品表面への蒸着性が異なるので、特に本発明範囲でのハーフ蒸着においては、必ずしも両者の色が均一に平均化して出色するのでなく、たとえば2種の金属の蒸着による出色が縞模様状に発揮される等して、独特な装飾効果を付与することができる。
【0017】
異種の金属の真空蒸着方法としては、同一の電気抵抗加熱体上で加熱する、それぞれの別の電気抵抗加熱体上で同時にあるいは時間差を設けて加熱する、また真空蒸着を繰り返す等の方法があるが、この異種金属の蒸着方法、金属種選定により様々な装飾効果を付与することができる。
【0018】
第4の発明の手段は、第1、2または3の発明において、蒸着膜が透明性膜でトップクリアコートされていること、にある。
【0019】
第4の発明の上記構成により、蒸着膜の酸化等の変質、磨耗、傷付き等による装飾性の劣化を防ぐと共に、ハーフ蒸着ではあるものの、蒸着膜による若干の反射性と、UV硬化タイプのアクリル系トップコート剤等によるコート膜の薄膜性が相俟って、虹色に発色する薄膜による干渉模様、所謂油膜様の模様を出現せしめることができ、独特な装飾性を成形品に付与することができる。
【0020】
第5の発明の手段は、第1、2、3または4の発明において、プラスチック成形品内に光を反射する機能を有したフィラーが分散されていること、にある。
【0021】
第5の発明の上記構成により、たとえば金属紛、マイカの表面を金属でコーテイングしたフィラー等の光を反射する機能を有したフィラーをプラスチック成形品内に分散することにより、蒸着による蒸着膜とフィラーとの間で光が相互に反射するので、独特の装飾効果が発揮されると共に、特には蒸着膜の表面が薄膜状に透明性膜でトップクリアコートされている場合には、照明等の光の当たり方、あるいは見る角度により、薄膜による干渉模様が変化して動く様に見え、さらに独特な装飾効果を付与することができる。なお、フィラーの形状としては光の反射効果の点からマイカ等の扁平な形状とすることが好ましい。
【0022】
第6の発明の手段は、第1、2、3、4または5の発明において、プラスチック成形品が容器であること、にある。
【0023】
第6の発明の上記構成により、たとえば容器の装飾性が商品力の大きな部分を占める化粧品等の容器において、独特の装飾性を発揮させて商品イメージを大きく向上させることができる。
【発明の実施の形態】
【0024】
以下、本発明の実施の形態を、図面を参照しながら実施例を用いて説明する。なお、図1は本発明の効果を確認するためのモデル的な成形品1であり、スチレン系樹脂であるAS(アクリロニトリル−スチレン共重合)樹脂製の透明、有頂端円筒状成形品である。また図2は図1の成形品1の縦断面図であり、(a)はAS樹脂性の成形品本体2、(b)は成形品本体2に蒸着膜3が形成された状態、(c)はさらに蒸着膜3を透明性のコート膜5でトップクリアコートした状態を示すものである。
【0025】
【実施例】
実施例1は、金属としてアルミニウムを使用し、真空蒸着機で、蒸着量を全光線透過率が蒸着膜形成前の全光線透過量の65〜75%の範囲内となるように、成形品1について真空蒸着を実施して得られた、図2(b)に示す層構成を有した加飾プラスチック成形品であり、黒系統の色を出色した透明な成形品である。(以下の実施例においても蒸着量を全光線透過率が蒸着前の全光線透過量の65〜75%の範囲内となるようにしている。)なお、全光線透過率の測定は、JIS K7361−1997に準拠して図2(b)中の白抜き矢印で示される方向から光を入射して測定を実施したものである。
【0026】
実施例2〜5は実施例1と同様に、各種の金属を用いて成形品1について真空蒸着を実施して得た加飾プラスチック成形品であり、下に各実施例における使用金属と出色する色系統を示す。
実施例2 鉄 赤
実施例3 クロム 青
実施例4 チタン 青
実施例5 ステンレス 茶
【0027】
実施例6はアルミニウムおよび鉄の2種の金属を同一の電気抵抗加熱体上から蒸散させて真空蒸着を実施したものであり、アルミニウムによる黒系統の色と鉄による赤系統の色が縞模様状に出色する等して、今までにない独特な装飾効果を有した加飾プラスチック成形品となった。
【0028】
実施例7は、実施例1のアルミニウムを真空蒸着した層を、紫外線硬化性のアクリル系樹脂でトップクリアコートして、図2(c)に示すコート層5を形成した加飾プラスチック成形品であり、成形品の頂壁上面に照明等を反射させながら見ると、若干ではあるが光を反射する蒸着層2と薄膜であるコート層5とが相互作用して、図3に概略的に示したような虹色に発色した薄膜による干渉模様が見られ、独特の装飾性を発揮せしめることができる。
【0029】
実施例8は、成形品1がAS樹脂にマイカにアルミニウムをコートしたフィラーを数重量部分散させたものである以外は実施例7と同様の加飾プラスチック成形品であり、マイカ表面にコートしたアルミニウムによる光の反射効果も加味されて、照明を当てる方向、また見る方向により実施例7における虹色に発色した薄膜による干渉模様が変化して動くような感じを与えさらに独特の装飾性を発揮せしめることができる。
【0030】
【発明の効果】
本発明は、上記した構成となっているので、以下に示す効果を奏する。
第1の発明にあっては、光線透過率を蒸着膜形成前の光線透過率の65〜75%の範囲とすることにより、すなわち反射鏡やハーフミラーにおけるよりも膜厚を比較的薄くすることにより、若干のメタリック様の感じを付与させながら、透明な状態で、使用する金属による独特な色合いを出色させることができる。
【0031】
第2の発明にあっては、真空蒸着法により蒸着膜を形成することにより、例えば容器等の湾曲性の形状を有した成形品であっても、たとえば公転および自転を組み合わせた回転装置に取り付けることにより成形品の外表面全体に略均一に蒸着膜を形成することができる。
【0032】
第3の発明にあっては、異種金属を組み合わせた真空蒸着により蒸着膜を形成したことにより、金属により出色する色合いが異なり、また金属によって成形品表面への蒸着性が異なり、また必ずしも両者の色が均一に平均化して出色するのでなく、たとえば2種の金属の蒸着による出色が縞模様状等に出現されて独特な装飾効果を付与することができる。
【0033】
第4の発明の発明にあっては、蒸着膜の酸化等の変質、磨耗、傷つき等による装飾性の劣化を防ぐと共に、蒸着膜による若干の反射性と、コート膜の薄膜性が相俟って、虹色に発色する薄膜による干渉模様が出現して独特な装飾性を成形品に付与することができる。
【0034】
第5の発明にあっては、フィラー等の光を反射する機能を有したフィラーをプラスチック成形品内に分散することにより、蒸着による蒸着膜とフィラーとの間で光が相互に反射するので、独特の装飾効果が発揮されると共に、特には蒸着膜の表面が薄膜状にトップクリアコートされた場合には、照明等の光の当たり方、あるいは見る角度により、薄膜による干渉模様が変化して動くように見えるので、さらに独特な装飾効果を付与することができる。
【0035】
第6の発明にあっては、たとえば容器の装飾性が商品力の大きな部分を占める化粧品等の容器において、独特の装飾性を発揮させて商品イメージを大きく向上させることができる。
【図面の簡単な説明】
【図1】 本発明の実施例に用いる成形品を示す、斜視図。
【図2】 (a)図1の成形品の蒸着前の状態、(b)(a)に金属膜を蒸着した状態、および(c)(b)にさらにトップクリアコートした状態を示す縦断面図
【図3】 実施例7の成形品に見られる薄膜による干渉模様の模様を概略的に示す、平面図。
【符号の説明】
1 ; 成形品
2 ; 成形品本体
3 ; 蒸着膜
5 ; コート膜
[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a plastic molded product whose surface is decorated with a vapor deposition film mainly composed of metal.
[0002]
[Prior art]
Conventionally, metal is vapor-deposited on the whole or part of the outer surface of a plastic molded product and decorated like a metallic, mirrored, or so-called half mirror, or decorated or functions of a plastic molded product Generalization is generally performed.
[0003]
For example, Patent Document 1 describes a half mirror in which a metal is thinly vapor-deposited (hereinafter referred to as half vapor deposition) used as a member of a vehicle lamp.
[0004]
[Patent Document 1]
Japanese Patent Laid-Open No. 2003-115206
[Problems to be solved by the invention]
However, even in the half mirror described in Patent Document 1, the conventional technique basically gives a plastic-like feeling to the plastic by vapor deposition of metal. Discovered that various decorative effects, in particular, a color-developing effect, can be imparted to a molded article made of light-transmitting plastic.
[0006]
That is, the present invention aims to provide a plastic molded article having a unique decorative property and a high-class feeling, with the technical problem of imparting a color-developing effect by metal deposition to a light-transmitting plastic molded article. And
[0007]
[Means for Solving the Problems]
Of the present invention for solving the above technical problem, the means of the first invention is:
A metal light-permeable plastic molded articles deposited film mainly formed on the surface, a range of 65% to 75% of the light transmittance before the deposition film forming light transmittance, a metal by vapor deposition film The color specified by the type of color is displayed and decorated .
[0008]
By the said structure of 1st invention , the light transmittance is made into the range of 65 to 75% of the light transmittance before vapor deposition film formation, ie, the film thickness of a vapor deposition film is made thinner than in a reflective mirror or a half mirror. Thus, depending on the viewing direction, while giving a slight metal-like feeling, it is possible to produce a unique color by the metal used while maintaining excellent transparency.
[0009]
Various metals and alloy compounds can be applied for vapor deposition, and there are no limitations on the materials, usually various metals such as aluminum, silver, gold, copper, rhodium, chromium, nickel, platinum, titanium, molybdenum, tungsten and alloys thereof, Alternatively, various compounds such as silicon oxide, tin oxide, cerium oxide, titanium oxide, zinc oxide, zinc sulfide, and magnesium fluoride can be used depending on the purpose.
[0010]
For example, black can be used for aluminum, blue for chromium and titanium, and red for iron.
[0011]
Here it prominence exceeds 75% were in the range of 65% to 75% of the total light transmittance before the vapor is deposited on the total light transmittance becomes insufficient, and metallic-like feel as a whole is less than 65% This is because the coloration characteristic peculiar to each metal is impaired.
[0012]
The light-transmitting plastic is not particularly limited, and for example, a transparent or translucent resin such as polycarbonate resin, acrylic resin, polystyrene resin, polyester resin can be used, and the transparency is greatly impaired. Colored with a dye or pigment for coloring can be used within a range that is not limited, and various shades can be produced in combination with coloration by metal.
[0013]
The means of the second invention is that, in the first invention , the deposited film is formed by a vacuum deposition method.
[0014]
According to the above configuration of the second invention , even if the molded product has a curved shape, such as a container, by vacuum deposition, for example, the molded product is attached to a rotating device that combines revolution and rotation. A vapor deposition film can be formed substantially uniformly over the entire outer surface of the film.
[0015]
The means of the third invention is that, in the first or third invention , the vapor deposition film is formed by a vapor deposition method combining different metals.
[0016]
According to the above-described configuration of the third invention, the color to be colored varies depending on the metal, and the vapor deposition property on the surface of the molded article varies depending on the metal. Therefore, particularly in the half vapor deposition within the scope of the present invention, both colors are not necessarily uniformly averaged. For example, the coloration due to the vapor deposition of two kinds of metals is exhibited in a striped pattern, so that a unique decorative effect can be imparted.
[0017]
Examples of vacuum deposition methods for different kinds of metals include heating on the same electrical resistance heating body, heating on different electrical resistance heating bodies simultaneously or with a time difference, and repeated vacuum deposition. However, various decoration effects can be imparted by the vapor deposition method of this different metal and the selection of the metal species.
[0018]
According to a fourth aspect of the present invention , in the first, second, or third aspect , the deposited film is top-clear coated with a transparent film.
[0019]
According to the above configuration of the fourth aspect of the invention , the deterioration of the decorative property due to alteration, wear, scratches, etc. of the deposited film is prevented, and although it is half-deposited, there is some reflectivity by the deposited film, and the UV curing type Combined with the thin film properties of the acrylic film, such as an acrylic topcoat agent, interference patterns due to the rainbow-colored thin film, the so-called oil film-like pattern, can appear, giving a unique decorative property to the molded product. it is possible.
[0020]
According to a fifth aspect of the invention , in the first , second , third, or fourth aspect of the invention , a filler having a function of reflecting light is dispersed in the plastic molded article.
[0021]
According to the above-described configuration of the fifth invention , for example, a metal film, a filler having a function of reflecting light, such as a filler whose surface of mica is coated with a metal, is dispersed in a plastic molded product, whereby a deposited film and a filler by vapor deposition Because the light reflects between each other, a unique decorative effect is exhibited. Especially when the surface of the vapor deposition film is thinly transparent and top-clear coated with a transparent film, light such as lighting is used. The interference pattern by the thin film changes and moves depending on how it hits or the viewing angle, and it is possible to give a unique decorative effect. In addition, as a shape of a filler, it is preferable to set it as flat shapes, such as a mica, from the point of the light reflection effect.
[0022]
According to a sixth invention , in the first , second , third , fourth or fifth invention , the plastic molded product is a container.
[0023]
With the above-described configuration of the sixth aspect of the invention , for example, in a container such as a cosmetic product in which the decorativeness of the container occupies a large portion of the product power, the product image can be greatly improved by exhibiting unique decorativeness.
DETAILED DESCRIPTION OF THE INVENTION
[0024]
Hereinafter, embodiments of the present invention will be described using examples with reference to the drawings. FIG. 1 shows a model molded product 1 for confirming the effect of the present invention, which is a transparent, top-end cylindrical molded product made of AS (acrylonitrile-styrene copolymer) resin which is a styrene resin. 2 is a longitudinal sectional view of the molded product 1 of FIG. 1, (a) is an AS resin molded product main body 2, (b) is a state in which a vapor deposition film 3 is formed on the molded product main body 2, (c ) Shows a state where the vapor deposition film 3 is top-clear coated with a transparent coating film 5.
[0025]
【Example】
Example 1 uses aluminum as a metal and is a molded article 1 so that the total light transmittance is in the range of 65 to 75% of the total light transmittance before the deposition film is formed using a vacuum vapor deposition machine. 2 is a decorative plastic molded product having a layer structure shown in FIG. 2 (b), which is obtained by carrying out vacuum vapor deposition, and is a transparent molded product with a black color. (In the following examples, the amount of vapor deposition is such that the total light transmittance falls within the range of 65 to 75% of the total light transmittance before vapor deposition.) The measurement of the total light transmittance is JIS K7361. In accordance with -1997, light was incident from the direction indicated by the white arrow in FIG.
[0026]
Examples 2 to 5 are decorated plastic molded products obtained by performing vacuum deposition on the molded product 1 using various metals in the same manner as in Example 1, and are colored with the metal used in each example below. Indicates the color system.
Example 2 Iron Red Example 3 Chrome Blue Example 4 Titanium Blue Example 5 Stainless Steel Brown
In Example 6, two kinds of metals, aluminum and iron, were evaporated from the same electric resistance heating body and vacuum deposition was performed. The black color of the aluminum and the red color of the iron were striped. As a result, it became a decorative plastic molded product with a unique decorative effect.
[0028]
Example 7 is a decorative plastic molded product in which the layer obtained by vacuum-depositing aluminum in Example 1 was top-clear coated with an ultraviolet curable acrylic resin to form the coat layer 5 shown in FIG. When the light is reflected on the upper surface of the top wall of the molded product, the deposition layer 2 that reflects light slightly interacts with the coat layer 5 that is a thin film, and is schematically shown in FIG. Interference patterns due to the rainbow-colored thin film can be seen, making it possible to exhibit unique decoration.
[0029]
Example 8 is a decorative plastic molded product similar to Example 7 except that the molded product 1 is obtained by dispersing several parts by weight of an AS resin-coated mica-coated aluminum, and coated on the mica surface. Reflecting the light reflection effect of aluminum, the interference pattern due to the rainbow-colored thin film in Example 7 changes depending on the direction in which the light is applied and the direction in which it is viewed. It can be shown.
[0030]
【The invention's effect】
Since the present invention has the above-described configuration, the following effects can be obtained.
In the first invention , the light transmittance is in the range of 65 to 75% of the light transmittance before the deposition film formation, that is, the film thickness is made relatively thinner than in the reflecting mirror and the half mirror. Thus, while giving a slight metallic feeling, it is possible to produce a unique color by the metal used in a transparent state.
[0031]
In the second invention , by forming a deposited film by a vacuum deposition method, for example, even a molded product having a curved shape such as a container is attached to a rotating device that combines revolution and rotation, for example. Thereby, a vapor deposition film can be formed substantially uniformly over the entire outer surface of the molded product.
[0032]
In the third invention , since the deposited film is formed by vacuum deposition combining different kinds of metals, the color of the color produced by the metal is different, and the deposition property on the surface of the molded product is different depending on the metal. The color is not uniformly averaged and the color is produced, but the color produced by vapor deposition of two kinds of metals appears in a striped pattern or the like, for example, and a unique decoration effect can be given.
[0033]
In the invention of the fourth aspect, the deterioration of the decorative property due to the alteration such as oxidation of the deposited film, wear, and scratches is prevented, and the slight reflectivity due to the deposited film and the thin film property of the coat film are combined. Te, as possible out that the interference pattern due to a thin film to be colored in rainbow colors to give a unique decorative and appearance of the molded article.
[0034]
In the fifth invention , by dispersing the filler having a function of reflecting light, such as filler, in the plastic molded product, the light is mutually reflected between the deposited film and the filler by vapor deposition. In addition to exhibiting a unique decorative effect, especially when the surface of the deposited film is top-clear coated in a thin film shape, the interference pattern due to the thin film changes depending on how the light is applied or the angle of viewing. Since it seems to move, it can give a more unique decorative effect.
[0035]
In the sixth invention , for example, in a container such as a cosmetic that occupies a large portion of the product power, the product image can be greatly improved by exhibiting the unique decor.
[Brief description of the drawings]
FIG. 1 is a perspective view showing a molded product used in an embodiment of the present invention.
2A is a longitudinal cross-sectional view showing a state before vapor deposition of the molded product of FIG. 1, FIG. 2B is a state in which a metal film is vapor deposited on FIG. 1A, and FIG. FIG. 3 is a plan view schematically showing an interference pattern due to a thin film found in a molded article of Example 7. FIG.
[Explanation of symbols]
DESCRIPTION OF SYMBOLS 1; Molded article 2; Molded article main body 3; Deposition film 5; Coat film

Claims (4)

  1. 表面に少なくとも2種の異種金属を主成分として含有する蒸着膜(3)が形成された光透過性のプラスチック成形品(1)であって、全光線透過率が蒸着膜(3)形成前の全光線透過率の65〜75%の範囲とし、該蒸着膜(3)により前記
    少なくとも2種の異種金属より特定される異なる色合いを縞模様状に現出させて加飾したことを特徴とする加飾プラスチック成形品。
    A light-transmitting plastic molded article (1) having a vapor-deposited film (3) containing at least two different kinds of metals as a main component on its surface, wherein the total light transmittance is before the vapor-deposited film (3) is formed. The total light transmittance is in the range of 65 to 75%, and the deposited film (3)
    A decorative plastic molded product, wherein different shades specified from at least two kinds of different metals are displayed in a striped pattern and decorated.
  2. 蒸着膜(3)が透明性膜でトップクリアコートされた、請求項1記載の加飾プラスチック成形品。  The decorative plastic molded product according to claim 1, wherein the deposited film (3) is top-clear coated with a transparent film.
  3. プラスチック成形品(1)内に光を反射する機能を有したフィラーが分散された請求項1または2記載の加飾プラスチック成形品。  The decorative plastic molded product according to claim 1 or 2, wherein a filler having a function of reflecting light is dispersed in the plastic molded product (1).
  4. プラスチック成形品(1)が容器であることを特徴とする請求項1、2または3記載の加飾プラスチック成形品。  The decorative plastic molded product according to claim 1, 2 or 3, wherein the plastic molded product (1) is a container.
JP2003183858A 2003-06-27 2003-06-27 Decorative plastic molding Expired - Fee Related JP4748470B2 (en)