JP4730523B2 - インク廃液吸収体及びその製造方法 - Google Patents
インク廃液吸収体及びその製造方法 Download PDFInfo
- Publication number
- JP4730523B2 JP4730523B2 JP2005158492A JP2005158492A JP4730523B2 JP 4730523 B2 JP4730523 B2 JP 4730523B2 JP 2005158492 A JP2005158492 A JP 2005158492A JP 2005158492 A JP2005158492 A JP 2005158492A JP 4730523 B2 JP4730523 B2 JP 4730523B2
- Authority
- JP
- Japan
- Prior art keywords
- polyurethane foam
- binder
- surfactant
- ink
- waste liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
請求項1:
ポリオール、イソシアネート、発泡剤を含む発泡原料を用いて製造したポリウレタンフォームに、界面活性剤及びバインダーが含浸処理されたものであり、前記バインダーの含浸量が6,000〜50,000g/m3であることを特徴とするインク廃液吸収体。
請求項2:
前記ポリウレタンフォームが非圧縮フォームである請求項1記載の廃液吸収体。
請求項3:
前記ポリウレタンフォームが圧縮フォームである請求項1記載の廃液吸収体。
請求項4:
前記ポリウレタンフォームが、セル膜のないポリウレタンフォームである請求項1,2又は3記載のインク廃液吸収体。
請求項5:
前記バインダーがアクリル樹脂及び/又はポリウレタン樹脂である請求項1乃至4のいずれか1項に記載のインク廃液吸収体。
請求項6:
上記界面活性剤と上記バインダーの含浸量比が、(界面活性剤の含浸量)/(バインダーの含浸量)(質量比)値として1/10〜10/1である請求項1乃至5のいずれか1項に記載のインク廃液吸収体。
請求項7:
請求項1乃至6のいずれかに記載の廃液吸収体の製造方法であって、ポリオール、イソシアネート、発泡剤を含む発泡原料を用いてポリウレタンフォームを得、界面活性剤及びバインダーを分散乃至溶解した液中に上記ポリウレタンフォームを浸漬し、溶媒を乾燥して、ポリウレタンフォームに界面活性剤をバインダーと共に付着させることを特徴とするインク廃液吸収体の製造方法。
請求項8:
請求項1乃至6のいずれかに記載の廃液吸収体の製造方法であって、ポリオール、イソシアネート、発泡剤を含む発泡原料を用いてポリウレタンフォームを得、界面活性剤及びバインダーを分散乃至溶解した液をポリウレタンフォームにスプレー塗布後、溶媒を乾燥して、ポリウレタンフォームに界面活性剤をバインダーと共に付着させることを特徴とするインク廃液吸収体の製造方法。
請求項9:
請求項1乃至6のいずれかに記載の廃液吸収体の製造方法であって、ポリオール、イソシアネート、発泡剤を含む発泡原料を用いてポリウレタンフォームを得、界面活性剤を分散乃至溶解した液とバインダーを分散乃至溶解した液とをポリウレタンフォームに別々に又は同時にスプレー塗布後、溶媒を乾燥して、ポリウレタンフォームに界面活性剤をバインダーと共に付着させることを特徴とするインク廃液吸収体の製造方法。
請求項10:
界面活性剤を付着させたポリウレタンフォームを更に圧縮成型する請求項7,8又は9記載の製造方法。
本発明のインク廃液吸収体は、ポリオール、イソシアネート、発泡剤を含むポリウレタン発泡原料を用いて製造したポリウレタンフォームに、界面活性剤及びバインダーが含浸処理されたインク廃液吸収体である。
上記ポリオールを製造する際に使用する活性水素含有化合物としては、例えばポリアルコール類、ポリアミン類等であり、ポリアルコール類を例示すれば、エチレングリコール、プロピレングリコール、グリセリン、トリメチロールプロパン、1,2,6−ヘキサントリオール、ペンタエリスリトール、ソルビトール、蔗糖等がある。
このような触媒としては、例えば有機スズ化合物触媒、アミン系触媒等がある。有機スズ化合物触媒としては、スタナスオクトエート、スタナスオレエート、ジブチルジスズラウレート、ジブチルスズジ−2−エチルヘキソエート、ジブチルスズジアセテート等がある。一方、アミン系触媒としても、一般によく用いられるアミン系触媒、例えばトリエチルアミン、トリエチレンジアミン、N−エチルモルフォリン、ジメチルエタノールアミン、ジメチルベンジルアミン、1,8−ジアザビシクロ(5・4・0)ウンデセン−7及びそのフェノール塩、トリエチレンジアミンの蟻酸塩等をそのまま使用することができる。これらの触媒は単独或いは2種以上を混合して使用することができる。なお、アミン系触媒としては、通常、ポリウレタンフォーム発泡に使用されるアミン系触媒が用いられるが、溶出等が問題となる用途には反応性を有するアミン系触媒の使用が好ましい。触媒の使用量は特に限定されず広範囲に変えることができるが、通常ポリオール100質量部に対して0.005〜2質量部の範囲である。
(i)界面活性剤及びバインダーを分散乃至溶解した液中にポリウレタンフォームを浸漬し、過剰の液分を絞りとった後に溶媒を乾燥させる方法。
(ii)界面活性剤及びバインダーを分散乃至溶解した液をポリウレタンフォームに適量をもってスプレー塗布後、溶媒を乾燥させる方法。
(iii)界面活性剤を分散乃至溶解した液、及びバインダーを分散乃至溶解した液を、ポリウレタンフォームに別々又は同時に、それぞれ適量をもってスプレー塗布後、溶媒を乾燥させる方法。
ポリウレタンフォームAの製造
ポリオール(V3030・株式会社ダウ製)・100部、TDI80(日本ポリウレタン社製)・50部、水・4部、アミン系触媒(DABCO−33LV・三井エアプロダクツ製)・0.3部、スズ触媒(スタナスオクトエート・日東化成社製)・0.3部、シリコーン整泡剤(L−520・日本ユニカ社製)・1部を配合した発泡原料を用い、ワンショット法でポリウレタンフォームAを得た。得られたフォームの密度(JIS−K6400)は0.020g/cm3であり、セル数は55(1インチ当り)であった。また、通気度は18cc/cm2/secであった。
ポリウレタンフォームBの製造
上記ポリウレタンフォームAを50mm×100mm×100mmに切り出し、圧縮度5倍で熱圧縮(200℃,300秒)してポリウレタンフォームBを得た。得られたフォームの寸法は10mm×100mm×100mm、密度(JIS−K6400)は0.100g/cm3であり、セル数は275(1インチ当り)であった。
10mm×100mm×100mmの寸法のポリウレタンフォームA又はBを、以下の各溶液を混合した液に浸漬し、引き上げ、溶媒を130℃のオーブン中で5分間乾燥させてインク廃液吸収体を得た。得られたインク廃液吸収体のインク吸収性能を評価した。結果を表1に併記した。
ジ−(ノルマルオクチル)スルホコハク酸ナトリウム、リパール870P(ライオン社製)を水に溶解させ、濃度30質量%の溶液としたものを用いた。
界面活性剤2
ポリオキシエチレンアルキルエーテル、レオコールTD−150(ライオン社製)を水に溶解させ、濃度30質量%の溶液としたものを用いた。
バインダー1
タケラックWS−5000(樹脂濃度30質量%,三井武田ケミカル社製)を用いた。
バインダー2
TOCRYL W−461(樹脂濃度55質量%,東洋インキ製造社製)に水を加え、樹脂濃度30質量%としたものを用いた。
得られたインク廃液吸収体の質量からポリウレタンフォームの質量を差し引いて、含浸処理された界面活性剤とバインダーとの総量を算出した。界面活性剤、バインダー各々の含浸量については、含浸量比が使用した各液における各成分の配合比に等しいとして算出した。
吸収性能(初期、インク吸収後)
水平に置いたテスト片(厚さ10mm×100mm×100mm)の上面中央部に対し、テスト片上面から高さ5cmの位置にシリンジの針の先端をセットし、1ccのインクを約4秒間かけて滴下し終わった後、インクがテスト片表面から吸収されるまでの時間(秒)を測定した。
(初期)インク廃液吸収体を製造した状態の吸収性能。
(インク吸収後)テスト片上に黒色顔料インクを0.05cc滴下することを1回/秒間隔にて50回繰返し、更に3分間経過後に上記吸収性能を測定した。なお、吸収性能の低いサンプルでは3分間経過後も表面にインクが残存していた。
吸収性能(水浸漬後)
室温にて、500mlの水にテスト片を24時間浸漬後、水を絞り、130℃のオーブンにて3分間乾燥させた。水平に置いたテスト片(厚さ10mm×100mm×100mm)の上面中央部に対し、テスト片上面から高さ5cmの位置にシリンジの針の先端をセットし、1ccの水を約4秒間かけて滴下し終わった後、水がテスト片表面から吸収されるまでの時間(秒)を測定した。
Claims (10)
- ポリオール、イソシアネート、発泡剤を含む発泡原料を用いて製造したポリウレタンフォームに、界面活性剤及びバインダーが含浸処理されたものであり、前記バインダーの含浸量が6,000〜50,000g/m3であることを特徴とするインク廃液吸収体。
- 前記ポリウレタンフォームが非圧縮フォームである請求項1記載の廃液吸収体。
- 前記ポリウレタンフォームが圧縮フォームである請求項1記載の廃液吸収体。
- 前記ポリウレタンフォームが、セル膜のないポリウレタンフォームである請求項1,2又は3記載のインク廃液吸収体。
- 前記バインダーがアクリル樹脂及び/又はポリウレタン樹脂である請求項1乃至4のいずれか1項に記載のインク廃液吸収体。
- 上記界面活性剤と上記バインダーの含浸量比が、(界面活性剤の含浸量)/(バインダーの含浸量)(質量比)値として1/10〜10/1である請求項1乃至5のいずれか1項に記載のインク廃液吸収体。
- 請求項1乃至6のいずれかに記載の廃液吸収体の製造方法であって、ポリオール、イソシアネート、発泡剤を含む発泡原料を用いてポリウレタンフォームを得、界面活性剤及びバインダーを分散乃至溶解した液中に上記ポリウレタンフォームを浸漬し、溶媒を乾燥して、ポリウレタンフォームに界面活性剤をバインダーと共に付着させることを特徴とするインク廃液吸収体の製造方法。
- 請求項1乃至6のいずれかに記載の廃液吸収体の製造方法であって、ポリオール、イソシアネート、発泡剤を含む発泡原料を用いてポリウレタンフォームを得、界面活性剤及びバインダーを分散乃至溶解した液をポリウレタンフォームにスプレー塗布後、溶媒を乾燥して、ポリウレタンフォームに界面活性剤をバインダーと共に付着させることを特徴とするインク廃液吸収体の製造方法。
- 請求項1乃至6のいずれかに記載の廃液吸収体の製造方法であって、ポリオール、イソシアネート、発泡剤を含む発泡原料を用いてポリウレタンフォームを得、界面活性剤を分散乃至溶解した液とバインダーを分散乃至溶解した液とをポリウレタンフォームに別々に又は同時にスプレー塗布後、溶媒を乾燥して、ポリウレタンフォームに界面活性剤をバインダーと共に付着させることを特徴とするインク廃液吸収体の製造方法。
- 界面活性剤を付着させたポリウレタンフォームを更に圧縮成型する請求項7,8又は9記載の製造方法。