JP4594698B2 - Ocher powder, facial pack, bath composition, facial pack composition, and method for producing bath composition - Google Patents

Description

  The present invention relates to a face-only pack and bath composition using loess as a main raw material, and a method for producing the same. More specifically, the dried ocher is pulverized to 200 to 250 mesh after being dried by sunlight, and the ocher is put in a clay pot with red pine charcoal, paulownia, alum and ginkgo leaves and sealed, and is -5 to 40 ° C. The present invention relates to a face-only pack and a bath composition using ocher ripened at a temperature of 1 to 6 months. Use of the bath composition containing ocher of the present invention refreshes the head, prevents arteriosclerosis and fat accumulation in the body, is effective for suppuration diseases such as athlete's foot and dermatitis, and is effective in the metabolism and blood circulation system of the human body. Has the effect of smoothing.

  On the other hand, the face-only pack of the present invention has the advantages that the ocher has a fine particle size to eliminate irritation to the skin and does not adversely affect the skin even if it is used every day. In particular, the loess used in the present invention uses the special ripening method and additives in its pre-treatment, thereby maximizing the effect of the far infrared rays of the loess, thereby improving the health and beauty of the skin. Facilitate. In addition, the bathing composition of the present invention is a natural affinity invention in which the loess discharged after the bathing is finished flows into the drainage channel, purifies the contaminated river, and restores the soil strength of the contaminated soil. This is another feature.

  On the other hand, in addition to the ocher, the face-only pack ocher composition of the present invention can contain functional additives such as natural sunflower salt and pine bud extract essential oil.

  Traditionally, bathing agents consist of fragrances, colorants, plant fragrances, organic acids, etc. consisting of inorganic salts such as salt cake (eg, crystalline sodium sulfate), boric acid (eg: sodium borate), carbonates, and sulfur. Prepared by adding to the mixture. Such conventional bath preparations are used for the purpose of imparting a fragrance and color to hot water, giving proper stimulation to the skin, giving proper stimulation to the blood, and circulating the blood to restore fatigue and metabolism. To promote.

  On the other hand, hot springs scattered in various places in Korea include radioactive springs, sulfur springs, acidic springs, etc. depending on the characteristics of water veins and water quality and the inclusion of minerals, which are classified and used as cold and hot springs. Hot springs are used for various purposes such as treating various diseases. In this way, each hot spring is different in its efficacy and nature, and there is an inconvenience that consumers have to search around to use hot springs that suit their constitution. The present invention pays attention to such inconvenience and provides a bathing composition containing an extracted essential oil product of loess and / or pine needles and a natural salt so that each home can easily enjoy “medicine bath”. However, it is not disclosed in any known literature about each component and its content constituting the composition of the present invention, and the effects obtained thereby.

On the other hand, with regard to the face-only pack containing ocher, the conventional literature, for example, Patent Document 1 and Patent Document 2 below, disclose cosmetics containing ocher, but these simply mean that they contain ocher. There is no disclosure about using loess pre-treated in a specific way as in the present invention. In particular, conventional cosmetics including ocher that has undergone only washing, heating, particle sorting, and the like cannot transmit the superiority of ocher to the skin, and are therefore unique to the present invention. There was no effect.
US Pat. No. 6,254,858 Korean Published Patent 1999-0086959

  Most of the conventional bubble baths are made of carbonate, and the fragrance components volatilize into the air along with the carbon dioxide bubbles generated by decomposition of the carbonate in hot water, reducing the effect of the fragrance. There was a problem to do. Also, since the bathing agent itself is one of the synthetic surfactants, there has been a problem of deepening environmental pollution when discharged into the drainage channel after the bathing.

  An object of the present invention is to provide a bathing composition using only natural raw materials with less such problems. Another object is to find the optimum content of each constituent component in order to maximize the effects of the present composition. Thereby, the bathing satisfaction which cannot be predicted from the conventional bathing composition is obtained.

  In addition, for face-only packs containing ocher, provide a face-only pack that has less skin irritation, which is a disadvantage of conventional ocher packs, and has soft skin and excellent effects on facial skin diseases, etc. Is an issue.

  The bathing composition of the present invention is a mixture of ocher powder and / or natural salt, pine bud extract essential oil (hereinafter referred to as each component of the present composition), and then mixed at a certain ratio. It is in powder form and can be used in the form of taking a certain amount in a bathtub when bathing. In addition, since each component of the present invention is manufactured separately, each component itself can be one invention, and a part of the component of the present invention can be taken and applied during bathing. Of course. Further, the facial pack composition of the present invention comprises ocher powder and / or natural salt, and extracted essential oils of pine buds. In particular, the loess for the facial pack composition is subjected to thorough pretreatment. The feature of the present invention is that the functions of the loess can be maximized.

  When bathing with the composition of the present invention, the scent of pine is smelled and the head is light and refreshing. This pine scent (terpene scent) contains unsaturated fatty acids, prevents arteriosclerosis and fat accumulation in the body, replenishes anions that are deficient with natural salt, and prevents poisons and inflammation of athlete's foot and dermatitis. Treated, the influence of ocher far-infrared rays will smooth the metabolism and blood circulation of the human body. Also, the loess water discharged after pine forest bathing is a natural-friendly product that flows into the drainage channel to purify the contaminated river and restore the soil power of the contaminated soil. In addition, in the case of the face-only pack, the moisturizing effect is excellent, the skin irritation is small, and the effect of removing oil from the facial skin is excellent, so that clean skin can be maintained.

  Hereinafter, each component of the barber / beauty composition and bath composition of the present invention will be described. The present invention is not limited to the embodiments described below, and various modifications can be made within the scope described in the claims.

First, the ocher powder will be described.
The technical feature of the present invention lies in the pretreatment step of loess, and the gist of the invention is to use such pretreated loess in a face-only pack or bathing composition.

  It is desirable to use a high quality ocher that is 90 cm or less from the ground surface. Loess is a silicon mineral that has been exposed to solar energy for a long time, and has the characteristics of releasing far infrared rays and anions. It is effective for active metabolism to facilitate metabolism and prevent aging and adult diseases. It is known. Loess is made of fine sand, contains a large amount of calcium carbonate, and cannot be easily broken, so it has a high viscosity and has the property of turning into clay when kneaded with water. In addition, about 200 million microorganisms are alive in one spoon of ocher, and various enzymes are causing circulatory action, and it has been known that ocher is a living organism.

  Loess emits a large amount of far-infrared rays, and contains catalase, diphenol oxidase, sacharase, and protease as beneficial component enzymes, and these have a toxin removal action and a soil purification action.

  In the metabolic process of the human body, if a toxin called lipid peroxide is produced, an aging phenomenon occurs. Catalase, an enzyme in loess, has an action of neutralizing and diluting this lipid peroxide to prevent skin aging. Protease is an enzyme that hydrolyzes proteins into amino acids when the nitrogen in the protein is mineralized, and decomposes and destroys cancer, products, and other corrupt cells to detoxify damaged wounds and toxins in the body. is there.

In the present invention, the method for producing ocher powder is as follows.
Remove the soil on the surface at the designated loess producing area and collect only good quality loess 90 cm or less from the ground surface. The introduced ocher is put into a pulverizer and primary pulverization is performed. The ground ocher powder is thinly and evenly spread on the bottom to remove toxins and air-dried. The naturally dried ocher powder is put into an ocher making machine to remove foreign substances such as stones, and the ocher is dried by solar heat. In the present invention, such natural drying is distinguished from the conventional method of mechanically drying by heating. Next, the naturally dried ocher is put into an ocher powder making machine to remove small foreign substances to make a fine secondary powder. After the secondary powder is made, it is naturally dried by solar heat and then put into a pulverizer to make a powder of 150 to 200 mesh. Ocher powder with that particle size is used in bathing compositions. Further, the ocher powder is put into a pulverizer to make a powder of 250 to 1,000 mesh, preferably about 1,000 mesh. The resulting product is used in a face-only pack, that is, a hairdressing / beauty composition of the present invention. The ocher powder dried in this manner is subsequently subjected to an aging step which is a feature of the present invention. In the aging step, the dried ocher powder is put in a clay pot and sealed, and then aged for 1 to 6 months. You can also put the red pine charcoal, paulownia, agate and ginkgo leaves in a coarse gauze towel. On the other hand, with respect to the aging period and aging temperature as described above, there has been an attempt to use loess that has undergone aging for about 1 to 2 weeks in the past, but by setting the aging period to 4 weeks or more, In addition, it should be noted that the surprising finding that the far-infrared divergence function of loess can be remarkably improved by setting the aging temperature to -5 ° C to 40 ° C. By such ripening of the ocher, the ocher of the present invention becomes a 'living ocher' different from the conventional ocher, and when included in the composition of the present invention, the original function of the ocher can be sufficiently exhibited. It becomes possible.

Second, natural salt will be described.
The salt we use is the sun salt, that is, the salt made by drawing seawater into the salt field, evaporating it by receiving heat from sunlight. This salt is rich in minerals because the mud mixed sea water is exposed to hot sunlight and the harmful substances are evaporated by the wind. There are good and bad salts. If the shape of the particles is identified by the eye and is square, it is certainly made on the day of noon. Bad salt is a hexahedron of particles that are exposed to the night wind and contains a lot of poison. The salt we use is a square particle sun salt, which is heated for 1 hour or more at high heat (1,000 ° C) to remove the impurities and remove impurities to use it in fine particles. Make sun salt and use it as a raw material.

  Use only the first salt produced on a salty soil with a temperature of 30 ° C on a sunny day with good seawater. Natural sun salt has the property of decomposing oils and fats. Natural salt has more role and function than soap, shampoo, rinse, treatment and lotion by accelerating skin physiology and skin respiration. Therefore, it can be the best skin care and hair care product. In addition, it is a natural hair nourishing and hair growth aid that prevents dandruff, hair loss, and young white hair. Salt also has a detoxifying and bactericidal action, increasing the resistance of the human body to prevent cells and blood vessels from entering the body even if harmful substances or bacteria enter the body. The manufacturing method of the sun salt used for this invention is as follows. Only the first salt produced by combining sun-dried salt from mud-mixed seawater and evaporating it with wind and then adding a water temperature of 25-35 ° C. on the soil of the salt field is used. In this case, what is mainly made from the salt fields on the west coast is recognized as a first-class product, but this is confirmed and delivered to the site. 5-15 kg of natural sun-dried salt is put into a salt heat processing machine and heated at 300-400 ° C. for about 1 hour. This is to remove the moisture of solar salt and remove arsenic, which is a toxin in solar salt. The particles formed at that time are about 100 mesh. 5-15 kg of the baked salt is put in a pulverizer and pulverized again. At that time, it is crushed and passed through a 200-mesh sieve.

Third, the extracted essential oil of pine buds will be described.
The pine needles are blue because of the substance called turpentine contained in the essential oil that is also the main component of pine oil. Turpin oil is rich in unsaturated fatty acids. Pine includes alcohol, esters, phenolic compounds and glycoginin. There are also tonics based on perpentin, vitamin A, vitamin C and glorotyl extracted from pine. Alcohols, esters, etc. in it expel waste products and further promote metabolism. Vitamin A has an effect of solidifying mucous membranes, and glycoginin has an effect of lowering blood glucose, and is therefore effective for diabetes. Black pine and red pine contain a large amount of vitamin C, and Kumersekin contained in vitamin C has an effect on blood pressure. Pine leaf extract eliminates cholesterol. High altitude emia with increased blood fat is caused by a Western diet that consumes a large amount of animal fat and causes arteriosclerosis, cerebral infarction, angina and myocardial infarction. When bathing with Matsuba-yu, vitamin A, vitamin C, parthenic acid, stearic acid and the like promote blood circulation and are effective for cold, neuralgia, anemia, neurogenic gastritis and the like.

Hereinafter, the manufacturing method of the pine bud extract used for this composition is demonstrated.
The pine buds are newly pushed up around the beginning of March to May. Cut about 5 cm in length and wash with running water to remove dust. It is dried and steamed with hot steam. At that time, steam can be collected to obtain an extracted essential oil of pine buds.

In the above, each component of this composition was demonstrated. Next, mixing of the composition of the present invention will be described.
The extracted essential oil of pine buds per 10 parts by weight of natural salt is placed in a material mixer and mixed for about 10 to 50 minutes, and this mixture is mixed with 30 to 50 parts by weight of the ocher flour of the present invention. Mix with parts by weight. The mixed result is put in a packaging container and sealed with a vinyl bonding machine so that Matsuka does not leak.

Hereafter, the usage method and effect of the bathing composition of this invention are demonstrated.
When bathing, it is desirable to put hot water of about 38 to 40 ° C. in about half of the bathtub, and about 100 to 300 g of the bathing composition, and then bathe half of the body down to the chest. After soaking your body in the bathtub for about 10 to 15 minutes and sweating, you can get out of the bathtub. For whole body massage, take an appropriate amount of ocher powder in a container, knead it with water and apply it to your whole body with your hand or brush. After about 15 minutes, the whole body will be tightened, so take a bath again. You can enjoy a natural pine forest bath with a unique Korean pine scent and ocher, and after 10-15 minutes, you can finish the pine forest bath by showering with clean water.

  How to use the face pack is to clean the face makeup and wash it, then apply a small amount of skin cream, mix well with 1 to 2 spoons (about 10 g) of the face pack composition, Apply evenly to face and neck. After about 10 minutes, the skin is tightened and the pack is washed with soap or foam cleansing.

  Further, the ocher powder of the present invention can be applied as a general cosmetic material other than a face-only pack or a bath composition. For example, an ocher soap can be produced by adding the ocher powder of the present invention to a cosmetic soap. Specifically, fats and oils are hydrolyzed in advance to higher fatty acids and glycerol, and the fatty acids are neutralized with sodium hydroxide or sodium carbonate to make a base soap. In addition to the ocher powder of the present invention, conventional additives required for this base soap, that is, antioxidants, colorants, fragrances, stimulant mitigants, builders for enhancing detergency (condensed sodium phosphate, sodium carbonate , Sodium silicate) and the like and stirred for 30 minutes. After that, a 100-mesh net was put in a soap molding press, the mixture was pulverized three or more times, pressed, and then shaped into soap using a stamping machine. And commercialize.

  The sample of the Example which belongs to this invention, and the sample as a comparative example outside this invention were manufactured, and the comparison experiment was conducted. First, manufacturing conditions for each sample will be described.

Example 1-1 Manufacture of loess powder After collecting only good quality loess of 90 cm or less from the ground surface in the loess production area, primary pulverization is performed in a pulverizer. The ground ocher powder is thinly and evenly spread on the bottom and is naturally dried by sunlight. The naturally dried ocher powder is put into an ocher making machine to remove foreign substances such as stones and dried by solar heat. The naturally dried ocher is put into an ocher powder making machine to remove small foreign substances and make a fine secondary powder. After the secondary powder is made, it is naturally dried by solar heat and then put into a pulverizer to make a 200 mesh powder. The dried ocher powder is put into a clay grilled bowl, and together with 5 parts by weight of red pine charcoal, 5 parts by weight of paulownia, 5 parts by weight of agate and 5 parts by weight of ginkgo leaves per 100 parts by weight of ocher, the mixture is heated at 10 ° C. Aged for 6 months. Then, the ocher powder was put into a pulverizer to make a 300 mesh powder. For the face pack composition, the powder was about 1,000 mesh.

-Example 1-2 Production of ocher powder Ocher powder was produced using the method of Example 1-1. However, the aging period was 1 month and the aging temperature was 10 ° C.
-Example 1-3 Manufacture of ocher powder Ocher powder was manufactured using the method of Example 1-1. However, the aging period was 2 months and the aging temperature was 10 ° C.
-Example 1-4 Manufacture of ocher powder Ocher powder was manufactured using the method of Example 1-1. However, the aging period was 3 months and the aging temperature was 10 ° C.
-Example 1-5 Manufacture of ocher powder Ocher powder was manufactured using the method of Example 1-1. However, the aging period was 4 months and the aging temperature was 10 ° C.
-Example 1-6 Manufacture of ocher powder Ocher powder was manufactured using the method of Example 1-1. However, the aging period was 5 months and the aging temperature was 10 ° C.
Comparative Example 1-1
An ocher powder was produced using the method of Example 1-1. However, mechanical drying was used without natural drying.
Comparative Example 1-2
An ocher powder was produced using the method of Example 1-1. However, the aging period was 1 week and the aging temperature was 10 ° C.
Comparative Example 1-3
An ocher powder was produced using the method of Example 1-1. However, the aging period was 2 weeks and the aging temperature was 10 ° C.
Comparative Example 1-4
An ocher powder was produced using the method of Example 1-1. However, the aging period was 3 weeks and the aging temperature was 10 ° C.
Comparative Example 1-5
An ocher powder was produced using the method of Example 1-1. However, the aging period was 7 months and the aging temperature was 10 ° C.

Example 2 Production of Natural Salt 10 kg of natural solar salt was placed in a salt heat processing machine and heated at 350 ° C. for 1 hour. At that time, the resulting particles were about 100 mesh. 10 kg of the baked salt was put in a grinder and ground again. The final natural salt was obtained by grinding and passing through a 200 mesh sieve.

Example 3 Manufacture of Extracted Essential Oil of Pine Bud Cut leaves about 5 cm long newly grown around the beginning of March to May, and wash with running water to remove dust. This was dried and then steamed with hot steam to collect steam and obtain an extract essential oil of pine buds. Although the steam distillation method is used in this embodiment, various other methods can be used. For example, a fatty oil extraction method, an expression method or the like may be used.

Example 4 Production of Bathing Composition 10 kg of natural salt and 1.5 kg of pine bud extract essential oil were placed in a material mixer and mixed for about 20 minutes, and this mixture was mixed with 200 mesh ocher powder (Examples 1-1 to 1-6 ocher flour) and 40 kg. The resulting product was placed in a packaging container and sealed tightly so that Matsukaka did not leak to obtain the final product.

Example 5 Manufacture of face-only pack composition 10 kg of natural salt and 1.5 kg of extracted essential oil of pine buds were placed in a material mixer and mixed for about 20 minutes, and this mixture was mixed with 1,000 mesh ocher powder (Example) 1-1 to 1-6 ocher flour) and 40 kg. The resulting product was placed in a packaging container and sealed tightly so that Matsukaka did not leak to obtain the final product.

Comparative Example 2 Production of Bath Composition A bath composition was produced using the method of Example 4. However, the ocher powder of Comparative Examples 1-1 to 1-5 was used.
Comparative Example 3 Preparation of a face-only pack composition A bathing composition was prepared using the method of Example 5. However, the ocher powder of Comparative Examples 1-1 to 1-5 was used.

  100 specialist panels were selected and subjected to comparative experiments on skin irritation, waste discharge effect, moisturizing feeling, healing of skin troubles, etc. The results are as shown in Table 1 below. The numbers of the following examples (and comparative examples) refer to the face-only pack composition made of ocher and manufactured in the examples of the corresponding numbers.

  As can be seen from the above results, the face-only pack using the ocher of the present invention is less irritating to the skin than the conventional face-only pack using the ocher that did not go through the aging conditions of the present invention, It has a very good clinching effect, good moisturizing, and has a healing effect on dermatitis and the like.

Claims (7)

Crush the ocher that has been dried by sunlight, and seal it in a clay pot together with 5 parts by weight of red pine charcoal, 5 parts by weight of paulownia, 5 parts by weight of agate and 5 parts by weight of ginkgo leaves per 100 parts by weight of the ocher. An ocher powder used in a face-only pack or bathing composition, which is aged for 1 to 6 months at a temperature of -5 ° C to 40 ° C.   A face-only pack comprising ocher powder as defined in claim 1. Face dedicated pack natural salt, further comprising the extract essential oil of Matsume, extracts the essential oil was 0.5 part by weight to 3 parts by weight of natural salt 10 parts by weight per Matsume, 1, 000 mesh loess powder 30 parts by weight or of The face-only pack according to claim 2, comprising 50 parts by weight.   A bath composition comprising ocher powder as defined in claim 1.   The bath composition further comprises natural salt and pine bud extract essential oil, 0.5 to 3 parts by weight of pine bud extract essential oil per 10 parts by weight of natural salt, and 30 to 30 parts by weight of 200 to 300 mesh ocher powder. 5. The bath composition according to claim 4, comprising 50 parts by weight. A method for producing a bathing composition comprising:
(A) Crush the ocher after drying by sunlight with 200-250 mesh and earthen it with 5 parts by weight of Akamatsu charcoal, 5 parts by weight of paulownia, 5 parts by weight of alum and 5 parts by weight of ginkgo leaves per 100 parts by weight of the ocher. A maturing step of sealing in a bowl and maturing at -5 ° C to 40 ° C for 1 to 6 months;
(B) a natural solar salt processing step of heating natural solar salt at a temperature of 300 ° C. to 400 ° C. for 1 to 2 hours;
(C) after drying the pine bud, steaming it with steam to collect the water vapor to obtain an extracted essential oil of pine bud;
(D) a step of adding 0.5 to 3 parts by weight of an extracted essential oil product of pine buds per 10 parts by weight of natural natural salt in a material mixer and mixing for 10 to 50 minutes;
(E) The mixture in step (d) is mixed with 30 to 50 parts by weight of ocher powder, and then stirred for 10 to 50 minutes with a material kneader. Method. A method for producing a facial pack composition comprising:
(A) The ocher dried by sunlight is pulverized with about 1,000 mesh, and the soil together with 5 parts by weight of red pine charcoal, 5 parts by weight of paulownia, 5 parts by weight of alum and 5 parts by weight of ginkgo leaves per 100 parts by weight of the ocher. An aging step of sealing in a shochu cake and aging at -5 ° C to 40 ° C for 1 to 6 months;
(B) a natural solar salt processing step of heating natural solar salt at a temperature of 300 ° C. to 400 ° C. for 1 to 2 hours;
(C) after drying the pine bud, steaming it with steam to collect the water vapor to obtain an extracted essential oil of pine bud;
(D) a step of adding 0.5 to 3 parts by weight of an extracted essential oil product of pine buds per 10 parts by weight of natural natural salt in a material mixer and mixing for 10 to 50 minutes;
(E) After mixing the mixture in the step (d) with 30 to 50 parts by weight of ocher powder, the mixture is stirred for 10 to 50 minutes with a material kneader, and then the facial exclusive pack composition Manufacturing method.