JP4556017B2 - Absorbent water resistance sheet, their preparation and absorbent product using the same - Google Patents

Absorbent water resistance sheet, their preparation and absorbent product using the same Download PDF

Info

Publication number
JP4556017B2
JP4556017B2 JP2001135238A JP2001135238A JP4556017B2 JP 4556017 B2 JP4556017 B2 JP 4556017B2 JP 2001135238 A JP2001135238 A JP 2001135238A JP 2001135238 A JP2001135238 A JP 2001135238A JP 4556017 B2 JP4556017 B2 JP 4556017B2
Authority
JP
Japan
Prior art keywords
sheet
absorbent
water
according
sap
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2001135238A
Other languages
Japanese (ja)
Other versions
JP2002325799A (en
Inventor
磨 鈴木
Original Assignee
株式会社日本吸収体技術研究所
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社日本吸収体技術研究所 filed Critical 株式会社日本吸収体技術研究所
Priority to JP2001135238A priority Critical patent/JP4556017B2/en
Publication of JP2002325799A publication Critical patent/JP2002325799A/en
Application granted granted Critical
Publication of JP4556017B2 publication Critical patent/JP4556017B2/en
Application status is Active legal-status Critical
Anticipated expiration legal-status Critical

Description

【0001】 [0001]
【発明の属する技術分野】 BACKGROUND OF THE INVENTION
本発明は、高通気性の防漏効果を得ることが可能な吸水性耐水性シートに関する。 The present invention relates to absorbent water-resistant sheet capable of providing a leak-proof effect of the highly air-permeable. さらに本発明は、この吸水性耐水性シートを製造する方法、および吸水性耐水性シートを用いた吸収体製品に関する。 The present invention relates to a method for manufacturing the water-absorbing water-resistant sheet, and to absorbent products using absorbent water-resistant sheet.
【0002】 [0002]
【従来の技術】 BACKGROUND OF THE INVENTION
液体透過性の表面シートと液体不透過性の裏面シートとの間に吸収体本体を介在させた構造を有する従来の吸収体製品においては、吸収体本体のみが尿便や体液の吸収に関与するので、液を受ける入口である表面シート側のみをオープンとし、両側面は耐水性のある立体ギャザー、下面は防水性のあるバックシートでカバーした構造が採用され、したがって吸収体本体はその周囲に位置するサラウンド部から隔離された状態になっている。 In conventional absorbent article having a structure obtained by interposing the absorbent body between the liquid-permeable topsheet and a liquid impermeable back sheet, only the absorber body is involved in the absorption of urine and feces and body fluids since, to open only the surface sheet side is an inlet for receiving a liquid, standing gathers both sides with a water-resistant, the lower surface is adopted structure was covered with back sheet with a waterproof, therefore the absorber body on the periphery It is in a state that is isolated from the surround portion located. この隔離状態に不都合を来すと、モレが発生するということになるのが現状である。 When causing an inconvenience to the quarantine, at present, it comes to leakage occurs.
【0003】 [0003]
このため吸収体本体には次のような役割が担わされている。 Are Ninawasa roles such as the following in this order absorbent body.
【0004】 [0004]
1) 着用者のあらゆる状態に対応できるだけの大きい吸収能力を持つこと。 1) to have a much larger absorption capacity can respond to any state of the wearer. すなわち着用者の着用体位、水分摂取量、季節などの環境変化、体調変化、交換時間変化に対応できるための吸収余力を持つこと。 That wear Positions of the wearer, fluid intake, environmental changes, such as seasonal, physical condition change, to have the absorption margin for that can correspond to exchange time change. これに単純に対応すると、極めて非効率な製品を作ることになり、例えば現在のMサイズ、Lサイズの子供用オムツで測定すると、平均的な吸収体の実利用率は35%前後であり、実に65%が使用状況に対応するための吸収余力という非効率な製品となっている。 If this simply corresponds to, we will be making a very inefficient product, for example, the current size M, as measured by children's diapers L size, the actual utilization of the average absorber is around 35%, It has become inefficient product called absorption margin for indeed 65% corresponds to a condition. この非効率性をいかに改善するかは重要な課題である。 How to improve this inefficiency is an important issue.
【0005】 [0005]
2) 特に大量の尿便を処理することが必要な子供用、大人用オムツなどの吸収体製品では、腰部全体を前後から被覆し、しかも弾性糸列で押さえつけることにより、吸収体本体との密着状態を保ち、モレを防ぐことを基本コンセプトとしている。 2) In particular a large amount of children's need to handle urine and feces, the absorbent products such as adult diapers, by pressing the whole lumbar covered from the front and back, yet an elastic yarn columns, adhesion between the absorbent body keeping the state, it is the basic concept that prevent leakage. 下の表1は、日本の平均的なMサイズ、Lサイズの子供用オムツの全面積と吸収体面積を調査した結果を示したものである。 Table 1 below, the average M size of Japan, shows the results of the examination of the absorber area to the total area of ​​children's diapers of L size. オムツのタイプはテープタイプとはかせるタイプの代表的な2種類で比較した。 Type of diapers were compared in a typical two types of Kassel is a tape type.
【0006】 [0006]
【表1】 [Table 1]
【0007】 [0007]
【発明が解決しようとする課題】 [Problems that the Invention is to Solve
上記の調査結果から、オムツの全面積に対して、必要部位をカバーするのに直接使用されている面積は僅か10%以下であることがわかる。 From the above findings, the total area of ​​the diaper, the area that is directly used to cover the required site is found to be at only 10% or less. このような低い面積利用効率を、どのようにして向上させることができるかは、多くの吸収体製品の材料の節約とコストの低減にとって大きな課題である。 Such a low area utilization efficiency, is how the can be improved by a major challenge for the reduction of savings and cost of materials of many absorbent products.
【0008】 [0008]
上記の表1のデータで示したように、身体を被覆する面積が大きく、しかも全体に防漏機能を持たせるということは、必然的に、極めて蒸れやすく、カブレやすい吸収体製品をもたらすということになる。 As shown in Table 1 data above, that the larger the area that covers the body, yet the fact that to have a leak-proof function throughout inevitably tends very stuffiness, resulting in skin irritation easily absorbent product become.
【0009】 [0009]
このような吸収体製品の着用環境(オムツ内気候)の改善のためには、身体のオムツにより被覆されている面積を可及的に少なくするか、あるいは吸収体部を含めたオムツ全体に通気・換気機能を付与することが重要になる。 For such improved absorbent product worn in an environment (diaper in climate), either reduce as much as possible the area that is covered by the body of the diaper, or vented to the entire diaper, including the absorber section - it is granted become important ventilation function.
【0010】 [0010]
従来、このような吸収体製品の着用環境を改善し、ムレ・カブレを防止するために、少しでも大きい通気性を持つバックシートを用意し、一方、防バイ剤、カブレ防止剤などの添加物をトップシートに加工して、ムレ・カブレ対策を行っている。 Conventionally, to improve the wear environment of such absorbent products, in order to prevent stuffiness-rash, prepared backsheet with large breathability at all, whereas, antifungal agents, additives such as rash agents a is processed into a top sheet, it is carried out Mouret rash measures.
【0011】 [0011]
しかし、通気性バックシートは、ピンホールの発生を防ぎ、また臭気のモレを防ぐための密閉性を保ちながら、通気性を確保するという極めて矛盾に満ちた条件をクリアする材料でなければならない。 However, breathable backsheet is to prevent generation of pinholes, also while maintaining the sealing performance for preventing the leakage of odors, it must be a material which clears the condition filled extremely contradiction that ensure proper ventilation.
【0012】 [0012]
したがって、結果として発現できる通気レベル(MVTR)は、2.0〜4.0m 3 /24hr・m 2であって、一般の下着が2.0m 3 /min・m 2程度であるのと比較すると、1/1000以下の量に過ぎず、このような通気性レベルでは、ムレ・カブレが解決できないのは当然といえよう。 Therefore, the ventilation level which can be expressed as a result (MVTR) is a 2.0~4.0m 3 / 24hr · m 2, the general underwear compares it to the at 2.0m 3 / min · m 2 about, 1/1000 only the following amounts, in such a breathable level, the Mouret rash can not be resolved will say for granted.
【0013】 [0013]
また物流コストの増大、販売店等における棚効率の向上等を目標として、現在、超薄型といわれている、パルプに対してSAP粒子の含有量を高めた吸収体製品が主流となってきているが、SAP粒子の含有量をさらに上げて、より薄い、いわゆるスーパー超薄型になると、吸収速度の低さが大きな障害となってくる。 The increase in distribution costs, the goal of improvement of shelf efficiency in a shop or the like, currently, it is said that ultra-thin, and absorbent product with enhanced content of the SAP particles is becoming the mainstream on pulp are, but further increasing the content of the SAP particles, thinner, at a so-called super ultra-thin, low absorption rate becomes a major obstacle. この障害は、SAP粒子の膨潤、吸収スピードと体液の排出スピードがマッチしないために生ずる問題であって、このような吸収スピードを調整する新たな機能を有する素材が必要になってきている。 This disorder is swelling of the SAP particles, a problem arises because the discharge speed of absorption speed and fluid do not match, the material having a new function to adjust such absorption speed has become necessary.
【0014】 [0014]
【課題を解決するための手段】 In order to solve the problems]
本発明は、このような従来の効率の悪い、しかもムレ・カブレの生じやすい吸収体製品の欠陥を解消し、バックシート部分にも吸収能力を付与することにより、吸収支援能力を持ち、しかも高吸水性樹脂(SAP粒子)の持つ水ブロック性を耐水バリヤーとして利用し、不織布の持つ多孔質構造を利用してフィルムを用いない高通気性を持った新しいコンセプトにもとづく、吸収支援能力を有するバックアップシートを提供する。 The present invention is bad the conventional efficiency, yet eliminate the defect-prone absorbent product stuffy-rash, by also imparting absorption capacity to backsheet portion has an absorbing support capabilities, and highly water blocking property possessed by the water-absorbing resin (SAP particles) was used as a water barrier, based on a new concept with a high air permeability of not using the film by using a porous structure with a non-woven fabric, backed with an absorbent support capacity to provide a sheet.
【0015】 [0015]
本発明はさらに、吸収支援能力を有するバックアップシートに、吸収スピードを上げるための液量のコントロールや、リーク液の均一分配、そして圧力緩和の役割を持つバッファーシートを組合せ、これを吸収体本体と組合せることにより、従来の吸収体製品と比較して、面積効率、容積効率および重量効率が極めて高く、しかもムレ・カブレの少ない吸収体製品を提供する。 The present invention further provides a backup sheet having an absorption ability to support, control and liquid volume for increasing the absorption speed, uniform distribution of the leakage liquid, and combining the buffer sheet with the role of pressure relief, and absorbent body of this by combining, as compared with conventional absorbent products, area efficiency, the volumetric efficiency and weight efficiency is extremely high and provides less absorbent product stuffy-rash.
【0016】 [0016]
【発明の実施の形態】 DETAILED DESCRIPTION OF THE INVENTION
本発明の目的を達成するためには、吸収体本体からリークしてバックアップシートに吸収されるリーク液のコントロール(入口)とそれを受けるバックアップシート機能(出口)が重要であり、バックアップシートは、次のような基本要件を満たすことが必要である。 To achieve the object of the present invention, the leakage fluid control to be absorbed by the backup sheet leaks from the absorbent body (inlet) and the backup sheet function of receiving it (outlet) is important, a backup sheet, it is necessary to satisfy the basic requirements such as:.
1) 吸水性と耐水性を併せ持ち、通気性に優れていること。 1) has both water-absorbing and water resistance, it is highly breathable.
2) 下着並みの換気性と通気性を有していること。 2) to have a ventilation and breathability underwear par.
【0017】 [0017]
また、このようなバックアップシートに組合されるバッファーシートが組合せされる場合には、下記の条件を考慮することが望まれる。 Further, when the buffer sheet are combined in such a backup sheet is combined, it is desirable to consider the following conditions.
1) バックアップシートと吸収体本体間に介在して吸収体本体からのリーク液の量とその分布をコントロールするバッファーシートの性状。 1) The amount and nature of the buffer sheet to control the distribution of the leakage liquid from the absorbent body interposed between the backup sheet and the absorbent body.
2) バックアップシートとバッファーシートに組合される望ましい吸収体本体の性状。 2) the backup sheet and the properties of the absorber body should be combined into a buffer sheet.
【0018】 [0018]
バックアップシートの基本構成は、次の3成分から成り立っている。 The basic configuration of the backup sheet is made up of the following three components. すなわち、第1の成分はSAPの複合基材として、また同時に耐水材料として働く通気性と耐水性を持つ疎水性不織布層、第2の成分としては吸水成分としてのSAP層、第3の成分はその吸水成分であるSAP層を被覆し、SAP層全体に均一に水性液を供給するような役割を担う親水性シート層の3成分層が必要である。 That is, the hydrophobic nonwoven layer and the first component having breathability and water resistance which acts as a composite matrix of SAP, and as water material simultaneously, SAP layer as water-absorbing component as a second component, the third component its SAP layer is water-absorbing component is coated, it is necessary 3-component layer of the hydrophilic sheet layer responsible so as to uniformly supply the aqueous solution to the entire SAP layer.
バックアップシートの性能はこの3成分の適切な選択とその組合せの正確さによって決定づけられる。 Performance of the backup sheet is dictated an appropriate selection of the 3 components by the accuracy of the combination.
【0019】 [0019]
まず通気性、耐水性のある疎水性不織布として代表的なものは、PE、PP、PET、ナイロン等の疎水性合成繊維から構成される不織布であるが、望ましいのは薄くて緻密な構造を持つPP、PE、PET等のスパンボンド不織布やメルトブローン不織布であり、さらに望ましくはスパンボンドSとメルトブローンMの積層体であるSMS構造、SMMS構造が望ましく、これらの不織布はある程度の耐水抵抗を持つが、本発明の目的を達成するためには、少なくとも150mmH 2 O以上の耐水圧、好ましくは200mmH 2 O以上の耐水圧を持つものが望ましい。 First breathability, typical example hydrophobic nonwoven fabric with a water resistance, PE, PP, PET, is a nonwoven fabric composed of hydrophobic synthetic fibers such as nylon, desirable has a dense structure thin PP, PE, a spun bond nonwoven fabric or a melt blown nonwoven fabric, such as PET, SMS structures more desirably a laminate of spunbond S and meltblown M, is desirable SMMS structure, these nonwovens are have some water resistance, to achieve the object of the present invention, at least 150mmH 2 O or more water pressure resistance, preferably those with 200 mm 2 O or more water pressure resistance desired. このため目付は、好ましくは15g/m 2 〜50g/m 2の範囲のものが選択される。 Thus the basis weight is preferably selected in the range of 15g / m 2 ~50g / m 2 .
【0020】 [0020]
通常、オムツ等の吸収体製品のバックシートとして安定に使用するためには、耐水圧で表すと少なくとも400mmH 2 O以上、好ましくは600mmH 2 O以上の耐水性が必要とされている。 Usually, in order to stably used as a back sheet of absorbent products such as diapers, expressed in a water pressure resistance of at least 400MmH 2 O or more, preferably there is a need for 2 O or more water-resistant 600MmH. 通気性フィルムといわれるミクロポーラスなPEフィルムも、1000mmH 2 O〜1500mmH 2 Oの耐水性を持つのが一般的である。 Microporous PE film called breathable films also, it is common to have a water resistance of 1000mmH 2 O~1500mmH 2 O. パルプ/SAP粒子の混合吸収体からなる従来の吸収体製品では、加圧下ではフリーな水が大量に存在し、しかもそれが直接的にバックシートに接触して加圧耐水負荷が大きくかかるため、上記のような耐圧性が必要であるが、本発明のようなSAP粒子含有量の多い吸収体本体の場合には、SAP粒子が水分を安定に担持するため、未吸収水が極めて少なく、その上バッファー層を介してリークされる液量も少なく、しかもそのリークした液もバックアップシートのSAP粒子に吸収されて、未吸収水の存在量はさらにごく僅かとなるため、基材不織布としては150mmH 2 O以上の耐水圧があれば十分に対応できる。 In conventional absorbent products comprising a mixed absorbent pulp / SAP particles, free water is present in large amounts under pressure, and since it takes a large direct contact with the backsheet compression resistance water load, it is necessary to pressure resistance as described above, in the case of many absorbent body of the SAP particle content, such as in the present invention, since the SAP particles are supported in a stable moisture, unabsorbed water is extremely small, its amount of liquid leaks through the upper buffer layer is small and moreover the leaked liquid is also absorbed into the SAP particles of the backup sheet, since the abundance of unabsorbed water becomes more negligible, 150MmH as base nonwoven if there are 2 O or more water pressure sufficient to cover.
【0021】 [0021]
上記のような不織布は、通気性という意味では、普通の下着並みの1.0〜4m 3 /min・m 2の通気性を持ち、この不織布の通気性をできるだけSAP加工時に維持すれば、通常の肌着と同等の通気性を確保できる。 Nonwoven as described above, in the sense that breathability has a breathable 1.0~4m 3 / min · m 2 comparable ordinary underwear, be maintained as much as possible breathability of the nonwoven fabric during SAP processing, normal underwear It can ensure the same breathable and.
【0022】 [0022]
ここで、不織布基材に複合させるSAP粒子(以下、単にSAPという)について説明する。 Here, SAP particles to be combined to the nonwoven substrate (hereinafter, simply referred to as SAP) will be described. SAPは現在、繊維状、顆粒状、フレーク状および造粒SAP等にその形状が分類されるが、液の抵抗性を保つためには、ある程度緻密な組織を持つことが望ましい。 SAP is currently fibrous, granular, although its shape into flakes and granulated SAP or the like is classified, in order to maintain the resistance of the liquid, it is desirable to have a somewhat dense tissue. そのためには、最密充填に近い構造をとりやすい球状粒子状の比較的細かい粒子の粒度分布を持つものが望ましい。 Therefore, the ones having a particle size distribution of the relatively fine particles in the form easy to take spherical particles a structure proximate to a closest packing is desired.
【0023】 [0023]
本発明に用いるSAPとしては、水系塊状重合で得られるSAPでは、粉砕後、篩別して500μm以下にした粉状のものが望ましい。 The SAP used in the present invention, the SAP obtained in aqueous bulk polymerization, after grinding, shall hereinafter with powdery 500μm and sieved desirable. 溶媒系サスペンジョン重合で得られるSAPでは、単粒で500μm以上の粒子を取り除いたものが望ましい。 In SAP obtained in the solvent system suspension polymerization, it is desirable to remove the 500μm or more particles in a single particle. 細かい方は、100μm以下の微粉と言われるもので差し支えない。 Finer one is, no problem in what is said to be less of fine powder 100μm. また比較的粗い粒子でも、微粉体を混合することによって緻密な構造にすることができる。 Also a relatively coarse particles, can be dense structure by mixing the fine powder.
【0024】 [0024]
本発明において、SAPは、吸収体本体に使用されるSAPと違い、ゲル強度や表面架橋度はほとんど問題でなく、むしろ吸収体本体に使用する場合には敬遠される、ゲルブロックを起こしやすい低AULの、表面架橋度の低いSAPの方がむしろ望ましい。 In the present invention, SAP, unlike SAP used in the absorbent body, the gel strength and surface cross-linking degree is not almost problem is avoided in the case of use rather absorber body prone to gel block low of AUL, towards the lower surface degree of cross-linking SAP is rather desirable. AULは、30ml/g (20g/cm 2加圧下)以下であることが望ましい。 AUL is, 30ml / g (20g / cm 2 pressure) is desirably less. さらに好ましくは、平均粒径が300μm以下でAULは20ml/g以下の微粉SAPが望ましい。 More preferably, the average particle size of at 300μm or less AUL following fines SAP 20 ml / g is desirable. なおバックアップシートにおけるSAPの目付は吸収体本体とは異なり、柔軟性も確保する必要もあることから、10g/m 2 〜100g/m 2と低目付に設定される。 Note the SAP having a basis weight in the backup sheet unlike absorbent body, since the flexibility is also necessary to ensure, is set to 10g / m 2 ~100g / m 2 to a low basis weight.
【0025】 [0025]
さらに第3の成分である親水性シート層の存在は、バックアップシートの内層、すなわちバッファーシートからにじみ出したリーク液を、局部に滞らせず拡散して、均一にSAP層に吸収固定させる役割として重要である。 Furthermore the presence of the third component is a hydrophilic sheet layer of the inner layer of the backup sheet, i.e. the leakage liquid that has exuded from the buffer sheet diffuses not stagnate the local, important role to uniformly absorbed secured to SAP layer it is.
【0026】 [0026]
親水性シート層としては、レーヨン不織布、パルプと合繊添加不織布、あるいはティッシュのようなセルロース系の水分吸収性と拡散性に優れたシート状不織布が選択されるが、好ましい素材は、サイズ剤で若干耐水性を付与した、目付10g/m 2 〜40g/m 2のティッシュである。 The hydrophilic sheet layer, rayon nonwoven fabric, pulp and synthetic additives nonwoven, or is a cellulose-based water absorbent and diffusive excellent sheet nonwoven such as tissues are selected, the preferred material is slightly sizing imparted with water resistance, a tissue having a basis weight of 10g / m 2 ~40g / m 2 .
【0027】 [0027]
次に、本発明の吸水性耐水性シートの具体的な構成の一例について図面を参照して説明する。 Next, an example of a specific configuration of the water-absorbent water-resistant sheet of the present invention will be described with reference to the drawings.
【0028】 [0028]
図1は、上述したような3成分、すなわち第1の成分としての、例えばSMS構造のような疎水性不織布層1と、この不織布層1の全面に展開する第2の成分である吸水成分としてのSAP層2と、このSAP層2を覆うように配置された、第3の成分としての、例えばティッシュのような親水性シート層3とを備えた吸水性耐水性シートを示している。 1, three components described above, i.e. as a first component, for example a hydrophobic nonwoven fabric layer 1, such as SMS structure, as water-absorbing component is a second component to expand to the entire surface of the nonwoven fabric layer 1 a SAP layer 2, the SAP layer 2 is disposed so as to cover, shows as a third component, a water-absorbing water-resistant sheet for example with a hydrophilic sheet layer 3, such as tissue.
【0029】 [0029]
一方、図2に示した例では、不織布層1上にSAP層2はライン状に配置され、このライン状のSAP層3とその間に露出している不織布層1とを覆うように、親水性シート層3が配置されている。 Meanwhile, in the example shown in FIG. 2, SAP layer 2 on the nonwoven fabric layer 1 is disposed in a line shape, so as to cover the non-woven fabric layer 1 exposed with SAP layer 3 of the linear therebetween, hydrophilic sheet layer 3 is disposed.
【0030】 [0030]
図1の例のように、SAP層2を不織布層1表面の全体に配置した場合には、この吸水性耐水性シートをバックシートとして使用する場合、耐水性は比較的容易に得やすいが、剛性が大きくなるので、これを緩和するために相対的に低目付とすることが望ましい。 As in the example of FIG. 1, when the SAP layer 2 is disposed on the entire of the nonwoven fabric layer 1 surface when using this water-absorbent water-resistant sheet as a back sheet, water resistance is relatively easily easily obtained, the rigidity is increased, it is desirable that the relatively low basis weight in order to mitigate this. これに対して図2の例のように、不織布層1だけの領域と、不織布層1およびSAP層2からなる領域とが交互に配置されている場合には、不織布層1のみの領域が薄くて折りたたみしやすく、通気性がそのまま活かせるので、柔軟でしかも大きな通気性が確保される。 In contrast, as in the example of FIG. 2, a region of only the nonwoven fabric layer 1, if the a region consisting of the nonwoven fabric layer 1 and the SAP layer 2 are arranged alternately, thin regions of only the nonwoven fabric layer 1 easily folded Te, since breathability Ikaseru as a flexible, yet large ventilation is ensured. 通気性は大きい方が望ましく、3層が積層された領域で、少なくとも0.5m 3 /min・m 2以上、好ましくは1m 3 /min・m 2以上の通気性を持つことが望ましい。 Breathable it is desirable large, three layers are stacked regions, at least 0.5m 3 / min · m 2 or more, it is desirable that preferably has a 1m 3 / min · m 2 or more breathable.
【0031】 [0031]
良好な特性を有する吸水性・耐水性シートを構成するためには、3層構造を一体化、安定化する方法もまた重要な要素である。 To configure the water resistance, water resistance sheet having good properties, integrated three-layer structure, a method for stabilizing is also important factor.
【0032】 [0032]
例えば、耐水性疎水性不織布としてSMS構造のものを用い、親水性シートとしてティッシュを用いた例で説明すると、SMS構造の層(以下、SMS層という)とSAPとの接合、SAPとティッシュ層との接合、およびSAP相互の接合という3つの接合系が存在することになるが、バックアップシートの3層構造を形成する上で特に重要な要素は、SMS層とSAP層との接合、およびSAP層とティッシュ層との接合である。 For example, used as the SMS structure as a water-resistant hydrophobic nonwoven fabric, to describe an example using a tissue as a hydrophilic sheet, the layer of SMS structure (hereinafter, referred to as SMS layer) bonding between the SAP, SAP and tissue layers and bonding, and three junctions that SAP mutual joining will be present, a particularly important factor in forming the three-layer structure of the backup sheet, bonding of the SMS layer and the SAP layer, and SAP layer and a junction between the tissue layers.
【0033】 [0033]
SMS層とSAP層との接合の方法について例示すると、1つは、カードウェブとの接合、物理的擦過加工などの手段を用いて、SMS層の表面に起毛状の空隙組織を形成し、その空隙内にSAP粒子を捕捉する方法である。 To illustrate the method of bonding of the SMS layer and the SAP layer, one, joining the card webs, using means such as physical abrasion process to form a raised shaped voids tissue on the surface of the SMS layer, the a method of capturing the SAP particles into the gap. 他の方法は、SMS層の表面に粘着性のあるホットメルトを塗布し、その粘着性を利用してSAP粒子を固定する方法である。 Other methods, by applying a hot melt with a sticky surface of the SMS layer, a method of fixing the SAP particles by utilizing the stickiness.
【0034】 [0034]
次にティッシュ層とSAP層との接合方法について例示すると、SMS層との接合の場合と同様にホットメルトで固定する方法と、SAP層の中に、SAPに対して2〜3%のミクロフィブリル状セルロース(MFC)を共存させ、このMFCの持つ強力な水素結合力によりSAP粒子相互とSAP層とティッシュ層を結合する方法がある。 Now it will be illustrated method of joining the tissue layer and the SAP layer, and a method of fixing in a similar hot-melt bonding of the SMS layer, into the SAP layer, 2-3% microfibrils against SAP Jo cellulose (MFC) coexist, there is a way to combine SAP particles interact with SAP layer and the tissue layer by strong hydrogen bonding with the this MFC.
【0035】 [0035]
図3は、耐水性疎水性不織布層1、SAP層2および親水性シート層3を備えた吸水性耐水性シートにおいて、SAP層2と親水性シート3とをホットメルト層4によって接合して構成した吸水性耐水性シートの断面図である。 3, the absorbent waterproof sheet having a water-resistant hydrophobic nonwoven layer 1, SAP layer 2 and the hydrophilic sheet layer 3, formed by joining the SAP layer 2 and the hydrophilic sheet 3 by hot melt layer 4 it is a cross-sectional view of the absorbent waterproof sheets.
【0036】 [0036]
また図4、図5および図6に、耐水性疎水性不織布層、SAP層および親水性シート層からなる図3に示した層構成のバックアップシートを製造するプロセス例を示す。 The 4, 5 and 6 show water resistance hydrophobic non-woven layer, a process example of manufacturing a backup sheet having a layer structure shown in FIG. 3 comprising a SAP layer and a hydrophilic sheet layer. 図4は、ホットメルトのみで接合するプロセス例、図5は起毛構造とホットメルトの組合せプロセス例、図6はSAP/MFC系にホットメルトを組合せたプロセス例である。 Figure 4 is an example process for bonding only a hot-melt, Figure 5 is a combination example process of raising structures and hot-melt, Fig. 6 is an example process that combines hot melt to the SAP / MFC system.
【0037】 [0037]
図4のプロセス例は、不織布層1を準備するステップ(a)、この不織布層1の表面にホットメルトを塗布してホットメルト層5を形成するステップ(b)、このホットメルト層5上にSAPパウダーを散布してSAP層2を形成するステップ(c)、このSAP層2上にホットメルトを塗布してホットメルト層4を形成するステップ(d)、およびこのホットメルト層4の接着性を利用して親水性シートであるティッシュ3を接合するステップ(e)を備えている。 Process example of FIG. 4, the step of preparing a nonwoven fabric layer 1 (a), forming a hot melt layer 5 by applying a hot melt on the surface of the nonwoven fabric layer 1 (b), on the hot-melt layer 5 forming a SAP layer 2 by dispersing the SAP powder (c), forming a hot melt layer 4 by applying a hot melt on the SAP layer 2 (d), and adhesion of the hot melt layer 4 the uses and a step (e) joining the tissue 3 is hydrophilic sheet.
【0038】 [0038]
図5のプロセス例は、不織布層1を準備するステップ(a)、この不織布層1上にカードウェブを積層して起毛状構造6を形成するステップ(b)、この起毛面にSAPパウダーを散布してSAP層2を形成するステップ(c)、このSAP層2上にホットメルトを塗布してホットメルト層4を形成するステップ(d)、およびこのホットメルト層4の接着性を利用して親水性シートであるティッシュ3を接合するステップ(e)を備えている。 Process example of FIG. 5, the step of preparing a nonwoven fabric layer 1 (a), this on the nonwoven layer 1 by stacking carded web forming a napped-like structure 6 (b), spraying the SAP powder in this brushed forming a SAP layer 2 and (c), forming a hot melt layer 4 by applying a hot melt on the SAP layer 2 (d), and by utilizing the adhesion of the hot melt layer 4 and a step (e) joining the tissue 3 is hydrophilic sheet.
【0039】 [0039]
また図6のプロセス例は、親水性シートとしてのティッシュ7を準備するステップ(a)、このティッシュ7の表面に、SAP/MFCスラリーを塗布してSAP層2を形成するステップ(b)、このSAP層2中の溶媒成分を除去してSAP粒子を固定するステップ(c)、SAP層2上にスプレーコート等の手段でホットメルトを塗布してホットメルト層5を形成するステップ(d)、およびこのホットメルト層5上にSMS構造のような不織布層1を重ねて接合するステップ(e)を備えている。 The example process of FIG. 6, the step of preparing the tissue 7 as a hydrophilic sheet (a), the surface of the tissue 7, forming a SAP layer 2 by applying a SAP / MFC slurry (b), the the step of fixing the SAP particles to remove the solvent component in the SAP layer 2 (c), forming a hot melt layer 5 by applying a hot melt by means such as spray coating on SAP layer 2 (d), and a step (e) joining overlapping the nonwoven layer 1, such as SMS structures on the hot melt layer 5.
【0040】 [0040]
図4〜図6に示したプロセスにおいて重要なことは、耐水性疎水性不織布層にピンホールの発生等のダメージを与えないことであり、その意味では、ホットメルトの粘着性を利用し接合することが望ましく、しかも繊維状ネットワークを持ったホットメルトの得られるカーテンスプレー法によるアプリケータを使用することが望ましい。 Importantly in the process shown in FIGS. 4-6 is that it does not damage such as occurrence of pinholes in water hydrophobic nonwoven layer, in that sense, we are joined using the adhesion of the hot melt it is desirable, moreover it is desirable to use the applicator by a curtain spray method capable of obtaining a hot melt having a fibrous network.
【0041】 [0041]
上述のようにして得られたバックアップシートは、図7(a)、(b)および(c)に示すように、吸収体本体と組合せて使用される。 Backup sheet obtained as described above, FIG. 7 (a), the use in combination with (b) as shown in and (c), the absorber body. 図7(a)は最も一般的な例で、吸収体本体11の下面部からサイドにわたってバックアップするようにバックアップシート12を配置して構成した例、図7(b)はセンター部分のみにフィルム13を加えてバックアップシート12を適用した例、(c)は吸収体本体11の下面側には従来のバックシートとしてフィルム13を使用し、サイド部にバックアップシート12を組合せた例である。 7 (a) is most common example, the absorber example constructed by placing the backup sheet 12 to back up over the side of the lower surface of the main body 11, and FIG. 7 (b) only in the center portion Film 13 examples of applying the backup sheet 12 by the addition of an example in which the lower surface side using a film 13 as a conventional backsheet, a combination of the backup sheet 12 to the side portion of (c) the absorbent body 11.
【0042】 [0042]
吸収体本体とバックアップシートの間に介在させるバッファーシートのコンセプトとその効果について説明する。 Buffer sheet concept to be interposed between the absorbent body and the backup sheet and its effects will be described.
【0043】 [0043]
本発明の吸水性耐水性シートで構成されたバックアップシートは、吸水機能を持つ、高通気性の防漏性シート材料であり、前述のように吸収体本体と組合せて使用されるが、加圧状態で一時的に多量な水性液がバックアップシートに直接供給されると、漏れを完全には防止できないという点で、通常のフィルム系バックシートとは異なる。 Backup sheet made of a water-absorbent water-resistant sheet of the present invention has a water absorption capability, a high breathability of the leakage preventive sheet material, it is used in combination with absorbent body as described above, the pressure temporarily large amount of aqueous liquid in a state is directly supplied to the backup sheet, in that it can not be completely prevented leakage differs from the conventional film-based backsheet. この欠点は、前述の図7(b)および(c)に示したように、従来のフィルムタイプのバックシートを組合せることで解消できるが、せっかくの通気性がある程度犠牲になる。 This drawback is, as shown in FIG. 7 of the aforementioned (b) and (c), can be solved by combining the backsheet of the conventional film type, precious breathability is sacrificed to some extent.
【0044】 [0044]
したがって、吸収体本体に一時的に多量の液が供給され、吸収体本体の保有能力を一時的にオーバーしてバックアップシートに溢流(flooding)する場合には、系外に漏らすことなく、しかもバックアップシートに大きい負荷をかけずに効率的に吸収機能を発揮させるためには、バックアップシートに広い面積にわたって均一に、かつ徐々に液が供給されるという条件を満たすように、時間的、量的あるいは圧力的な緩和機能を持った新たな機能部分を設けることが望ましい。 Therefore, temporarily supply a large amount of liquid in the absorbent body, when the overflow (flooding) to backup sheet temporarily over the holdings capacity of the absorbent body, without leaking to the outside of the system, yet in order to exhibit effectively absorbing function without the large load to the backup sheet is uniform over a large area in the backup sheet, and so as to gradually meet the condition that the liquid is supplied, temporal, quantitative Alternatively it is desirable to provide a new functional portion having the pressure mitigation functions.
【0045】 [0045]
このような機能を持った層は、バッファーシートと称されるが、このバッファーシートをバックアップシートに組合せることにより、バックアップシートの機能を効果的に発揮させることが可能になる。 Layer having such a function is referred to as a buffer sheet, by combining the buffer sheet in the backup sheet, it becomes possible to effectively exhibit the function of the backup sheet.
【0046】 [0046]
このような機能を持つバッファーシートに必要とされる主な条件は次の通りである。 The main conditions needed for buffer sheet having such a function is as follows.
(1) バックアップシートの持つ高通気性を阻害することがないような、十分な透湿、透気性(通気構造)を持つこと。 (1) so as not to inhibit high breathability with the backup sheet, sufficient moisture permeation, having a gas permeable (breathable structure).
(2) 吸収体本体からの一時的な液の受け入れ能力を持ち、バックアップシートに対する時間的、流量負荷に対する底部一時貯留機能(Bottom Acquisition効果)を持つこと。 (2) has a temporary liquid receiving capacity from the absorbent body, the temporal for backup sheet, having a bottom temporary retention feature to the flow rate load (Bottom Acquisition effect).
(3) 一時的に貯留した液を、多数の細孔構造(開孔フィルム、あるいはフォームセル等)により、バックアップシート全体に均一に分配して放流する機能(分配、放流効果)を持つこと。 (3) temporarily storing the liquid, by a number of pore structure (porous film, or foam cells, etc.), the ability to discharge uniformly distributed throughout the backup sheet (distribution, stocking effect) to have.
(4) 望ましくは、バックアップシートに着用者の体重が直接かかるのを軽減するための、圧力緩和効果を持つこと。 (4) Preferably, to reduce such the weight of the wearer directly to the backup sheet, having a pressure relief effect.
【0047】 [0047]
第一の要素である通気構造について説明する。 The vent structure which is the first element will be described.
【0048】 [0048]
本発明の吸水性耐水性シートの最大の特徴は、バックアップシートが下着と同等の大きい通気性を持っているということである。 The biggest feature of the water-absorbent water-resistant sheet of the present invention is that the backup sheet has a comparable high breathability and undergarments. この特徴を阻害しないためには、これに組合されるバッファーシートにも、下着と同等の通気度が必要であり、後述する吸収体本体についても同様なことが言える。 In order not to inhibit this feature, even a buffer sheet are combined in this requires equivalent air permeability and underwear can be said that also applies to the absorber body, which will be described later. 通気性が大きく、上述したような4つの条件を満たす素材は限られていて、凹凸を持った開孔ネット、開孔フィルム、および連続気泡で高発泡のフォーム(スポンジ)類のような多孔性素材の3種である。 Large breathable, four conditions are satisfied the material as described above is limited, apertured net having unevenness, perforated film, and porous, such as in open cell high expansion foam (sponge) such is a three materials.
【0049】 [0049]
本発明の目的を達成するためには、通気度が1.5m 3 /min・m 2 (ASTM D-737)以上のものが望ましく、開孔ネットおよび開孔フィルムの場合には、開孔数および開孔率を、発泡フォームであれば厚さおよび発泡度を調節して対応する。 To achieve the object of the present invention is 1.5m 3 / min · m 2 ( ASTM D-737) or more of the desirable air permeability, if the hole nets and apertured films, apertured number and the porosity, corresponding to adjust the thickness and degree of foaming, if expanded foam.
【0050】 [0050]
第二の条件である、底部一時貯留機能(Bottom Acquisition)とは、従来から超薄型吸収体に使用されてきたトップ層に設ける上部一時貯留機能(Surface Acquisition)に対比した表現であって、本発明に適するようなシート状のSAPが主構成成分であるような超々薄型吸収体では、表面に供給された水性液は、SAPの吸収速度が遅いために、急速に吸収体本体のSAP層を通過して下層側に移動する。 A second condition, the bottom temporary holding function and (Bottom Acquisition) is a versus the top temporary storage function provided in the top layer which has been used in the ultra-thin absorbent conventionally (Surface Acquisition) representation, in in certain such ultra thin absorbent main constituents sheet SAP as are suited to the present invention, the aqueous liquid supplied to the surface, because the absorption rate of the SAP is slow, rapid SAP layer of the absorbent body through the movement to the lower side. 液の一部はSAP層に吸収されるが、大略半分以上は下層に移動して防漏シート上に一時的に滞留する。 Although part of the liquid is absorbed by the SAP layer, more than half approximately the temporarily retained in the leak-proof sheet to move to the lower layer. 滞留した未吸収水は、SAPの膨潤によってSAP層に再び移動し、そこで吸収固定される。 Unabsorbed water staying moves again to the SAP layer by SAP swelling, where it is absorbed fixed.
【0051】 [0051]
防漏体に代わって適用される本発明の吸水性耐水性シートで構成されたバックアップシートは、高い通気性および吸収性を有しているが、吸収能力には限界を持っている。 Backup sheet made of a water-absorbent water-resistant sheet of the present invention applied in place of the leak preventer is has a high air permeability and absorbency, have limits to the absorption capacity. 従って吸収体本体のSAPに未だ十分な吸収余力がある場合には、一時的に下部に滞留した未吸収水を時間の経過とともにSAPに再吸収させ、一時的に安定にトラップさせた未吸収水を、バックアップシートには直接的に移行させないような工夫が必要である。 Therefore, when the SAP of the absorbent body there is still sufficient absorption margin is temporarily resorbed SAP unabsorbed water staying in the lower portion with the passage of time, unabsorbed water temporarily stably trapped a, it is necessary to devise so as not to directly migrate to the backup sheet. しかしトラップ能力を超えたために止むを得ずバックアップシートに吸収される水性液部分については、部分的に偏ることなく、平均的にしかも均一に液をコントロールされた状態でバックアップシートに移行させることが重要である。 However, for aqueous liquid portion to be absorbed by the backup sheet is unavoidable due to exceeding the trapping performance without biased partially be averagely and uniform transition to the backup sheet in a state of being controlled liquid is important. これによってバックアップシートの能力を安定にしかも十分発揮させることができる。 This makes it possible to stably yet sufficiently exhibit the capability of the backup sheet.
【0052】 [0052]
このように通気性を保ちながら未吸収水のトラップ機能とトラップ水位の調整機能を備えた、いわばダムのような効果を発揮するのが、バッファーシートの役割である。 Thus with a function of adjusting trapping and trap water level unabsorbed water while maintaining breathability, so to speak is given to exhibit the effects such as dams, the role of a buffer sheet.
【0053】 [0053]
このような効果は、凹凸構造を持った網目構造体、凹凸構造を持った開孔フィルムあるいは連続発泡フォームなどの嵩高で多孔性である素材を巧妙に利用することによって実現することができる。 Such effect can be achieved by ingeniously utilizing the network structure having an uneven structure, which is bulky and porous, such as porous film or continuous expanded foam having an uneven structure material.
【0054】 [0054]
次に、バッファーシートの嵩高性と多孔性についてより詳しく説明する。 It will be explained in more detail below bulkiness and porous buffer sheet.
【0055】 [0055]
嵩高性については、機能的な面ではいくら嵩高であっても構わないが、一方、製品のハンドリングに関しては、コンパクトで薄い方がよい。 For bulkiness, but may be in the functional aspects matter how bulky, whereas, with regard to the handling of the product, better thin compact. 本発明に好んで用いられる吸収体本体は、前述したようなSAPを主体とするシート状吸収体であり、製品厚み(乾燥時)は3mm以下の超薄型であり、さらには製品厚み1mm前後のスーパー超薄型吸収体のような薄さを特長とするものである。 Absorbent body is preferably used in the present invention is a sheet-like absorber made mainly of SAP as described above, the product thickness (dry) is the following ultra-thin 3 mm, more product thickness 1mm longitudinal a thin, such as the super-ultra-thin absorber are those that feature. 従ってこれらの吸収体本体の機能をサポートする役割のバッファーシートの厚さも、最大でも3mm以下、好ましくは1mm以下が好ましい。 Thus the thickness of the buffer sheet serves to support the functionality of these absorbent body also, up to 3mm or less, preferably 1mm or less.
【0056】 [0056]
好ましい嵩高状態とは、製品として包装された状態はもちろん、開封された状態でも、着用状態でもできるだけ薄い状態を保ち、体液の排出時に生起する吸水湿潤化に伴って吸収体の膨潤、膨化に相呼応するように、このバッファーシートも膨化、嵩高化することである。 The preferred bulky state, the state of being packaged as a product, of course, also in the state of being opened, kept as thin as possible state even under wearing conditions, the swelling of the absorber with the water wetting that occurs during discharge of the fluid phase in the swelling as response to this buffer sheet also swelling is to bulking. 例えば、高圧プレスすることによって圧力緩和、いわゆる「へたり」を起こしやすいレオロジカルな性質を利用して、上述したような厚さ1mm以上の凹凸化開孔ネット、開孔フィルム、あるいは発泡スポンジを1mm以下に高圧圧縮して仮セットしてバッファーシートとして使用し、製品としての薄物化を達成し、使用時には吸水、湿潤化に伴って嵩を回復するような性状を賦与することが好んで行われている。 For example, pressure relief by pressure pressing, by using the easy rheological properties undergo a so-called "sag" thickness of 1mm or more texturing apertures net as described above, porous film, or a foamed sponge 1mm temporarily set in high-pressure compressed below was used as a buffer sheet, achieving thin of a product, water absorption at the time of use, I prefer it to impart properties such as to recover the bulk with the wetting line are we.
【0057】 [0057]
したがって本発明に適用される凹凸シートとしては、特開2001-19777号公報に示されているような、圧縮回復性のある嵩高性のものよりは、むしろ厚くて安定にへたりやすいものか、薄くても圧力変形しないものの方が望ましい。 As uneven sheet to be applied to the present invention is therefore, as shown in JP 2001-19777, than those of the bulkiness of compression recovery property is stable or not easy fatigue rather thick, thin person of those that do not pressure deformation even if desirable. 厚いシートの圧縮薄層化は、発泡スポンジのような例では比較的容易に実現できる。 Thick compression thinning the sheet can relatively easily realized in the example, such as foam sponge. 例えばPE、PPなどの熱可塑性ポリマーの発泡体であれば、ガラス転移点以上の温度で、しかも熱溶融温度以下で加圧プレスすることによって、1/10〜1/5程度まで圧縮が可能となる。 For example PE, if the foam of a thermoplastic polymer such as PP, at a temperature higher than the glass transition point, moreover by pressure press under the following thermal melting temperature, can be compressed to about 1 / 10-1 / 5 and Become. 可塑化温度の高いポリウレタンフォームの場合も、加熱下に高圧で処理することによって1/5程度に圧縮することが可能になる。 In the case of high polyurethane foams of plasticizing temperature, it is possible to compress to about 1/5 by treatment with high pressure under heating. またセルローススポンジのような熱可塑性のないスポンジでも、湿分を持った状態で加熱加圧処理することで、やはり1/5程度まで圧縮することができる。 Also in the thermoplastic without sponge, such as cellulose sponge, by heating and pressurizing treatment in a state having a moisture it can be compressed to a still 1/5. これらの圧縮化されたスポンジも、使用時体重のかかった加圧下で吸水すると、発泡セルの抱水により嵩が元のレベル近くまで回復する。 Also these compacted sponge, when water under pressure to hazy during weight used, the bulk is restored to near its original level by chloral of foam cells.
【0058】 [0058]
次に多孔性について詳しく説明する。 Next will be described in detail porous. 本発明の吸水性耐水性シートとともに使用されるバッファーシートにおいて、多孔性は、耐水性を保持しながら同時に通気性を保つために重要な要素である。 In the buffer sheet for use with water-absorbing water-resistant sheet of the present invention, porosity is an important factor to keep the same time breathability while maintaining water resistance. 多孔性バッファーシートは、常圧では、疎水性素材の表面張力で水性液が遮断され、加圧下では液が滲み出てくるような大きさの細孔が必要である。 The porous buffer sheet is a normal pressure, the aqueous solution is blocked by the surface tension of the hydrophobic material, under pressure is required size pores, such as the liquid emerges bleeding. 例えば凹凸成型ネットであれば、少なくとも50mesh以下、好ましくは100mesh以下で、しかも水の濡れ現象の少ないPE、PP、PETなどの疎水性素材、あるいはシリコーンまたはテフロン(登録商標)処理により疎水化した表面を持たせたものが望ましい。 For example, if the uneven molding net, at least 50mesh less, preferably below 100 mesh, yet it made hydrophobic with a hydrophobic material or silicone or Teflon processing, such as less PE, PP, PET wettability phenomenon of water surfaces those which gave is desirable.
【0059】 [0059]
発泡フォームであれば、PE、PP、ポリウレタンなどの連続気泡を有するもので、例えば、セル数は20個/25mm(20ppi)以上、好ましくは30個/25mm〜100個/25mmであり、発泡度でいえば20〜40倍発泡したものが望ましい。 If foam forms, those which have PE, PP, continuous air bubbles such as polyurethane, for example, the number of cells is 20/25 mm (20 ppi) or, preferably 30 / 25Mm~100 pieces / 25 mm, the degree of foaming those 20 to 40-fold foaming in terms of the desirable. 凹凸構造を持った開孔フィルムとして代表的なものは、底部と頂部が開孔径の異なるいわゆる漏斗状形状を持つ開孔フィルムである。 Typical examples perforated film having an uneven structure, the bottom and the top is a porous film having a so-called funnel-shape having different pore size. このような開孔フィルムは従来から、生理用ナプキンのトップシートとして、開孔径の大きいサイドを上にして液の受け入れ側に配置し、液の流入を容易にすると同時に逆流を防ぐように配置し、ステンフリー性の高い表面材として多用されている。 Such apertured films are conventionally as a topsheet of the sanitary napkin, and placed on the receiving side of the liquid in the top large side opening diameter, arranged to prevent at the same time backflow when facilitating the flow of liquid , it is widely used as a highly Sten free surface material.
【0060】 [0060]
これに対して本発明では、前述とは逆の方向、すなわち開孔径の小さい側を上に向けて配置し、ロート状の周壁で吸収体本体を下部から支えるように配置される。 In the present invention, on the other hand, is configured to support the direction opposite to the above, i.e. the small end of the pore size is arranged facing upward, the absorbent body is funnel-shaped wall from the bottom. 図8は、本発明に好んで用いられる、凹凸を持った開孔フィルムからなるバッファーシート20の外観を示し、図9はその拡大断面を示している。 8, is preferably used in the present invention, showing the appearance of a buffer sheet 20 formed of perforated film having irregularities, FIG. 9 shows the enlarged section. この開孔フィルムは、適当な厚さのフィルム21を、その厚さ方向に裁頭円錐形に膨出させてロート状周壁22を形成し、その頂部に円形の開孔23を開けた膨出部24を、適当な密度で多数設けたものである。 The perforated film is a film 21 of a suitable thickness, is bulged in truncated conical in its thickness direction to form a funnel-shaped wall 22, spaced circular apertures 23 in the top thereof protruding the part 24 is obtained by providing multiple at an appropriate density.
【0061】 [0061]
開孔フィルムで重要なのは、第一に、膨出部の頂部に形成された23の開孔径である。 An important part perforated film is primarily a pore size of formed in the top portion of the bulging portion 23. 図10に示すように、バッファーシート20が吸収体本体10とバックアップシート12との間に配置された吸収体製品において、吸収体本体10に吸収された水性液の量が吸収体本体10の吸収能力を超えたとき、この開孔から溢れた水性液をバックアップシート12側へ排出する排出孔として作用するため、開孔23の開孔径は、通気性を損なわない範囲で小さい方がよい。 As shown in FIG. 10, the absorbent product buffer sheet 20 is placed between the absorbent body 10 and the backup sheet 12, the amount of aqueous liquid absorbed into the absorbent body 10 of the absorbent body 10 absorbs when exceeding the ability to act as a discharge hole for discharging the overflow aqueous solution from the opening to the backup sheet 12 side, pore size of the aperture 23, it is smaller in the range not inhibiting aeration. この開孔径は、開孔形状を真円に近似させたとき、その好ましい直径は少なくとも2mm以下、好ましくは1mm以下である。 The opening diameter, when allowed to approximate the aperture shape to a true circle, the preferred diameter of at least 2mm or less, preferably 1mm or less.
【0062】 [0062]
このような条件では、吸収体本体を通過して下層に滲み出た水性液は、凹凸開孔フィルムの凹部に一旦トラップされ、そこから溢れるまでは開孔の抵抗により、直接バックアップシートに流出することが防止される。 Under these conditions, aqueous liquid exuded to the lower layer through the absorber body is temporarily trapped in the concave portions of the concavo-convex porous film, until overflowing therefrom by the resistance of the apertures, flows out directly backup sheet it is possible to prevent. しかし開孔径が1mm以上、特に2mm以上になると、吸収体本体から下層に移行した水性液は、ほとんど抵抗を受けることなく直接的にバッファーシート20内の空隙を通してバックアップシート12へとバイパスしてしまい、トラップ効果、すなわち底部一時貯留機能(Bottom Acquisition効果)を意味のないものにしてしまう場合がある。 But opening diameter of 1mm or more, especially equal to or greater than 2 mm, an aqueous solution of the transition to lower the absorber body will be bypassed to the backup sheet 12 through the gap directly buffer sheet 20 without receiving little resistance , which may result in meaningless the trapping effect, or bottom temporary retention function (bottom Acquisition effect).
【0063】 [0063]
第二に重要な点は、開孔フィルムに設けられる開孔の数である。 The important point in the second, the number of apertures provided in the perforated film. 凹凸メッシュや発泡フォームの場合には、開孔面積の小さい多数の開孔が全体に均一分布しているが、開孔フィルムの場合には相対的に開孔数が少ないので、開孔径との関係もあり、開孔数が重要になる。 In the case of irregularities mesh or expanded foam is smaller number of apertures of the aperture area is uniformly distributed throughout, so small relative aperture number in the case of porous film, the opening diameter There is also a relationship, the opening number is important. また開孔数は、バックアップシート側へ溢れて流出する水性液の分割、分流数にも密接に関係する。 The opening number, the division of the aqueous liquid flowing overflowing to the backup sheet side, closely related to shunt number. このような観点から、開孔は、個数/cm 2で表現すると、5個/cm 2以上が好ましく、さらに好ましくは10個〜100個/cm 2である。 From this point of view, the opening, when expressed in number / cm 2, preferably 5 / cm 2 or more, further preferably 10 to 100 pieces / cm 2. 5個/cm 2以下では、均一な分配放流効果を出すことが難しくなる。 5 / cm 2 or less, it is difficult to produce uniform distribution discharge effect.
【0064】 [0064]
図11は、PE開孔フィルムの頭頂部の開孔の分布例を示したものである。 Figure 11 is a graph showing a distribution example of the opening of the top of the head of the PE porous film. 図11(a)に示すサンプルAは、Tredegar社(米国)製の、比較的目の粗くて厚いものであり、図11(b)に示すサンプルBはAvgol社(イスラエル)製の比較的目の細かいものである。 Sample A shown in FIG. 11 (a), Tredegar Corporation (USA), and has a thicker relatively eye coarse, relatively eye Sample B Avgol Ltd. (Israel) Ltd. shown in Fig. 11 (b) it is fine ones of. 頭頂部の直径(φt)が0.75mmと目が細かく、開孔数55個/cm 2のサンプルBは、単独層として用いても十分なトラップ効果および分配放流効果を示すが、φtが1.2mmと開孔径が大きく、開孔数15個/cm 2のサンプルAは、SMS構造を有する耐水性不織布を抵抗シートとして積層接合して用いられる。 Parietal diameter (.phi.t) is 0.75mm and the eye finely, sample B of the opening number 55 / cm 2 is also used as a single layer exhibits sufficient trapping effect and distribution stocking effect, .phi.t is 1.2mm and pore size is large, the sample a of the opening number 15 / cm 2 is used in laminating bonded water resistant nonwovens with a SMS structure as resistive sheet.
【0065】 [0065]
次にバックアップシートとしての開孔フィルムの厚さとクッション効果について説明する。 It will now be described thickness and cushioning effect of the perforated film as a backup sheet. 吸収体製品を実用に供する場合、着用者の体重を直接受ける部分には、当然厚みが厚く、圧縮回復性があり、クッション効果が大きい方が、吸収体本体に対する負荷は少なくなるという点で望ましい。 When subjecting the absorbent product practical, portions receiving the body weight of the wearer directly, naturally thick thickness, there is a compression recovery property, the larger cushioning effect is desirable in that the load is reduced on the absorption body . しかし本発明では、上述したクッション性よりも、形状保持性の方がより重要である。 In the present invention, however, than the cushioning described above, towards the shape retention is more important.
【0066】 [0066]
凹凸の度合いは、図9に符号Hで示したような厚みで表現される。 Degree of unevenness is expressed by thickness, as indicated at H in Figure 9. 発泡フォーム等は圧縮状態で用いられるので、へたりやすいものでよいが、開孔フィルムの場合には、厚みは薄くても、膨出部が潰れないような、変形の少ないものが望ましく、生理用品のトップシートに使用されるような薄くて柔らかいものは不適当である。 Since expanded foam or the like is used in a compressed state, it has enough easily may be one, but to, if the porous film is also thin thickness, so as not collapse bulge portion, it is desirable with less deformation, physiological those thin and soft, such as those used in supplies top sheet is inadequate. また原料フィルムの材質も、メタロセン系やエラストマー系をブレンドした比較的柔らかい弾性のあるものではなく、通常の高圧および低圧PE、あるいはPPのような、目付の割には安価で硬い素材の方が望ましい。 Also the material of the film material, and not with a relatively soft elastic blended with metallocene-based or elastomer-based, conventional high and low pressure PE or as PP,, is more hard materials less expensive in spite of the weight per unit area desirable. 凹凸を形成する膨出部の数はフィルムの厚さにも関係する。 The number of the bulging portion for forming the unevenness is also related to the thickness of the film. 厚いフィルムを原料にした場合には、大きなクレープ状の波形でもよく、薄いフィルムを用いる場合には、剛性を保つために凹凸数を多くしてコントロールすることが可能である。 In the case where the thick film material may be a large crepe-like waveform, in the case of using a thin film can be controlled by increasing the unevenness number to keep the stiffness.
【0067】 [0067]
バックアップシートとバッファーシートの組合せ実施態様上述したようなバックアップシートとバッファーシートを組合せて吸収体製品を構成する場合の具体的な配置例について説明する。 Specific arrangement example for configuring the absorbent product in combination backup sheet and the buffer sheet as described above combination embodiments of the backup sheet and the buffer sheet will be described.
【0068】 [0068]
図12は、吸収体本体11、バックアップシート12およびバッファーシート20の相対配置の具体例を断面図で示したもので、図12(a)は吸収体本体11の下面全体にバッファーシート20を配置した例、図12(b)は吸収体本体11の下面からサイド部にわたって吸収体本体11全体をバッファーシート20で包んだ例、図12(c)は吸収体本体11のセンター部分のみにバッファーシート20を配置した図、図12(d)は吸収体本体11のサイド部分のみをバッファーシート20で包んだ例をそれぞれ示している。 Figure 12 is a specific example of a relative placement of the absorbent body 11, the backup sheet 12 and the buffer sheet 20 which was shown in cross-section, arranged buffer sheet 20 on the entire lower surface in FIG. 12 (a) absorbent body 11 described example, and FIG. 12 (b) buffers from the lower surface of the absorbent body 11 examples wrapped entire absorbent body 11 with the buffer sheet 20 over the side portions, only the center portion of FIG. 12 (c) absorbent body 11 sheet Figure placing the 20, FIG. 12 (d) shows examples wrapped only side portions of the absorbent body 11 with the buffer sheet 20, respectively.
【0069】 [0069]
図13はバックアップシートとバッファーシートと吸収体本体との相対配置について、その実施態様を平面図で示したものである。 Figure 13 is the relative placement of the absorber body and the backup sheet and the buffer seat, showing its embodiments in plan view. (a)はバックアップシート12に対してバッファーシート20が吸収体11全体をカバーするように重ねて配置した場合、(b)はバックアップシート12が全面にあるが、バッファーシート20を縦方向の中央のみに配置した場合、(c)はバックアップシート12を全面に、バッファーシート20は横方向の中央のみに配置した場合を示す例である。 (A) if the buffer sheet 20 is arranged to overlap to cover the entire absorbent body 11 relative to the backup sheet 12, (b) is the backup sheet 12 is on the entire surface, a central buffer sheet 20 in the longitudinal direction If you place only, (c) the entire surface of the backup sheet 12, the buffer sheet 20 is an example showing the case of arranging only the center of the lateral direction.
【0070】 [0070]
前述の図13は、バッファーシートを単独で使用した場合、すなわち前述の開孔フィルムサンプルBのように比較的小さい開孔の開孔フィルムと組合せた場合の例である。 Figure 13 described above, when using a buffer sheet alone, that is, an example of a case in combination with perforated film of relatively small apertures, as described above the perforated film samples B. 図14は、前述の図11(a)に示した開孔フィルムサンプルAのように比較的大きな開孔を持つ開孔フィルムからなるバッファーシート20を、吸収体本体11およびバックアップシート12と組合せる場合において、バッファーシート20にさらに抵抗シート30を組合せて、バックアップシート12にかかる負荷の低減と、スムーズな分流とを実現するための耐水抵抗を保つことを目指している例である。 Figure 14 combines the buffer sheet 20 made of perforated film with a relatively large opening as porous film sample A shown in the aforementioned FIG. 11 (a), the the absorber body 11 and the backup sheet 12 in the case, a combination of more resistive sheet 30 to the buffer sheet 20, an example in which aims to keep the reduction of load on the backup sheet 12, the water resistance to achieve a smooth diversion.
【0071】 [0071]
ここで「抵抗シート」とは、開孔フィルムや凹凸メッシュ等のバッファーシートと組合せて、さらにバッファーシートの効果を増強させる役割を担うものである。 Here, "resistance sheet", in combination with a buffer sheet such as a porous film or irregularities mesh, which plays a role to further enhance the effect of the buffer sheet. したがって抵抗シートとして使用される素材は、開孔フィルムや凹凸メッシュと比較して、はるかに微細な多孔構造を持ち、しかも高通気性を持つことが要求される。 Thus the material to be used as resistive sheet, compared to perforated film or uneven mesh has a much finer porous structure, moreover it is required to have a high breathability. このような性能を持つものの例として、構成繊維デニールの細い不織布がある。 Examples of those having such performance, there is a constituent fibers deniers thin nonwoven.
【0072】 [0072]
このような不織布には、上述のような多孔性とともに、水に対して濡れ性が少なく、浸透抵抗を持つできるだけ薄くて均一な疎水性、撥水性不織布が望ましい。 Such nonwoven fabric with porous as described above, less wettability for water, as thin and uniform hydrophobic with penetration resistance, water repellency nonwoven is preferable. それらは例えば、PE、PP、ポリウレタン等のメルトブローン不織布、スパンボンド不織布、あるいはその複合体であるSMS構造やSMMS構造を有するものである。 They are, for example, those having PE, PP, melt blown nonwoven fabric and polyurethane, spunbonded nonwoven fabric, or SMS structure or SMMS structure is complex thereof. 用いる不織布の目付は、5g/m 2 〜20g/m 2のものが望ましい。 Basis weight of the nonwoven fabric to be used are those of 5g / m 2 ~20g / m 2 is desirable. 耐水圧は高くてもよいが、バックアップシートの耐水性材料として用いるほどの耐水圧は必須ではない。 Water pressure may be higher, but the water pressure resistance of more use as waterproof material of the backup sheet is not essential.
【0073】 [0073]
抵抗シートとバッファーシートとは、密着状態で一体化して機能することが重要であり、そのためには、バッファーシートと抵抗シートとを接合剤や融着により接合して使用するのが好ましい。 The resistive sheet and the buffer sheet, it is important to function integrally with close contact, in order to do this, it is preferable to use bonded by a bonding agent or fusion of the buffer sheet and the resistive sheet. たとえば特表2001-501883(Tredegar社)のようにキャリアと開孔フィルムとの複合材料を製造するのと同様なプロセスで開孔フィルムとメルトブローンをその製造工程で一体化した開孔フィルム/メルトブローン複合体を使用してもよいし、吸収体製品の加工工程にバッファーシートと抵抗シートとの接合行程を組み込ませてもよい。 For example perforated film / meltblown composite that integrates perforated film and meltblown with the manufacturing process in the same process as for preparing the composite material of the carrier and perforated film as Kohyo 2001-501883 (Tredegar, Inc.) use may be made of a body, it may be incorporated a bonding process between the buffer sheet and the resistive sheet in processing steps of the absorbent product.
【0074】 [0074]
図14に戻って説明すると、図14(a)は、バッファーシート20の下面全体、すなわちバッファーシート20とバックアップシート12との間に、バッファーシート20とほぼ同一サイズの抵抗シート30を配した例である。 Referring back to FIG. 14, FIG. 14 (a), the entire bottom surface of the buffer sheet 20, i.e. between the buffer sheet 20 and the backup sheet 12, arranged a resistive sheet 30 of approximately the same size as the buffer sheet 20 cases it is.
【0075】 [0075]
図14(b)は、抵抗シート30として用いられる不織布により吸収体本体11全体を包む(Core Wrapping)ように応用した例、図14(c)は抵抗シート30をバッファーシート20の上面、すなわち吸収体本体11とバッファーシート20の間に抵抗シート30を配した例である。 FIG. 14 (b), examples of applying to wrap the entire absorbent body 11 (Core Wrapping) of the nonwoven fabric used as the resistive sheet 30, FIG. 14 (c) a resistive sheet 30 top surface of the buffer sheet 20, i.e. the absorption it is an example where we arranged resistive sheet 30 between the body main body 11 and the buffer sheet 20. また図14(d)および(e)は、ともに抵抗シート30をバッファーシート20の一部に配した例で、(d)は圧力を受けやすいサイドエッジ部分のみに抵抗シート30を配した例、(e)は抵抗シート30を液がバイパスしやすいセンター部分のみに配した例である。 Examples The Figure 14 (d) and (e) is an example in which both arranged resistive sheet 30 on a part of the buffer sheet 20, which arranged resistive sheet 30 only in (d) are susceptible side edge portion of pressure, (e) is an example of a resistive sheet 30 liquid is arranged only to pass easily center portion.
【0076】 [0076]
図14(d)および(e)に示した例のように、バッファーシート20の下面の一部分のみに抵抗シート30を使用する場合には、全体の通気バランスを阻害しないような範囲で、その抵抗シート30を不織布ではなく、PE、PPまたはPETフィルムのような、無孔で通気性のないフィルム素材を使用して、部分的に耐水性を増強することも可能である。 Examples such as the illustrated FIG. 14 (d) and (e), when using the resistive sheet 30 only on the lower surface of a portion of the buffer sheet 20 is in a range that does not inhibit the overall ventilation balance, the resistance not a sheet 30 of a nonwoven fabric, PE, such as PP or PET film, using the film material without breathable nonporous, it is also possible to enhance the partially water resistance.
【0077】 [0077]
次に、本発明の吸水性耐水性シートを用いた吸収体製品に適用される吸収体本体について説明する。 Next, discussion will be made on an absorbent body which is applied to absorbent products using absorbent water-resistant sheet of the present invention.
【0078】 [0078]
SAP含有量が50%以上を占めるようなSAP含有量の高い系では、吸収体の厚みが従来品の1/2程度、すなわち2.0〜3.0mmの超薄型と呼ばれている吸収体になり、特にパルプレスといわれる、SAP含有量が80%以上を占めるようなシート状吸収体の場合には、吸収体の厚みが従来品の1/5、すなわち1mm程度の超々薄型の吸収体の開発が行われている。 The high SAP content of SAP content to occupy 50% or more based, the thickness of the absorber about 1/2 of the conventional products, i.e. becomes absorbers are called ultra-thin 2.0~3.0mm , in particular is said to Parupuresu, in the case of the sheet-shaped absorbent body, such as SAP content 80% or more, the thickness of the absorber is 1/5 of the conventional products, i.e. the development of 1mm about ultra-thin absorber It has been made.
【0079】 [0079]
しかし、例えばエアレイド法によって不織布に大量のSAPを添加する方法や、本発明者らが提案した特許第P3046367号(日本吸収体技術研究所)のような方法で得られた、メガシン(登録商標)と呼ばれているシート状吸収体などの超々薄型吸収体の場合には、そのまま従来通りの利用法に従えば、100ccの液を吸収するのに90秒程度を要する。 However, for example, a method of adding a large amount of SAP to non-woven fabric by air-laid process, obtained by the method such as the present inventors proposed by Patent No. P3046367 (Japan absorber Technology Institute), Megashin ® in the case of the ultra-thin absorber, such as a sheet-like absorber it is called is, as it is in accordance with the conventional manner of usage, takes about 90 seconds to absorb the liquid of 100cc. これに対して、健康な幼児の排尿は100ccについて20秒間程度の高スピードで排出する。 In contrast, urination of healthy infants discharged at high speed of about 20 seconds for 100 cc. したがって当然、その間のスピード差を調節する機能が必要になる。 Therefore of course, it is necessary to function to adjust the meantime of the speed difference. 本発明はこのような使用形態において特に効果的である。 The present invention is particularly effective in such a usage pattern.
【0080】 [0080]
吸収スピードの差を調節する方法としては、その第一は、本発明者らが特願2001-043494号で提案したように、液体分配ユニットを用いて吸収体の表面全体に液を急速に拡散させ、面積利用効率を上げる方法、第二には本発明のようにバッファーシートのBottom Acquisition効果を利用して未吸収水をトラップして時間を稼ぐ方法が挙げられる。 As a method of adjusting the difference in absorption speed, the first, as the present inventors have proposed in Japanese Patent Application No. 2001-043494, rapidly spreading the liquid on the entire surface of the absorber with the liquid distribution unit is allowed, a method of increasing the area efficiency, the second Bottom Acquisition how to make duration traps the unabsorbed water by utilizing the buffer sheet and the like as in the present invention. 本発明の吸水性耐水性シートからなるバッファーシートは、さらに液体分配ユニットと組合せて利用することにより、吸収スピードはさらに大幅に向上する。 Buffer sheet made of water-absorbing water-resistant sheet of the present invention, by utilizing further combination with a liquid dispensing unit, the absorption speed is further significantly improved.
【0081】 [0081]
次に耐水性の評価方法について説明する。 Next, a description will be given of an evaluation method of water resistance.
【0082】 [0082]
図17は評価装置の全体を示す図である。 Figure 17 is a diagram showing an overall evaluation device. 図18は評価サンプル装着部分の詳細を示す図である。 Figure 18 is a diagram showing the details of the evaluation sample mounting portion.
【0083】 [0083]
サンプルサイズは5cm×5cm以上とする。 The sample size and 5cm × 5cm or more.
【0084】 [0084]
サンプルの設置は以下のとおり行う。 Sample of the installation is carried out as follows.
【0085】 [0085]
ジャッキ上のガラス板にろ紙(型:No.2、サイズ:15cm×15cm、以下、同様とする。)を2枚重ねて敷く。 Filter paper on a glass plate on the jack (type: No.2, size:. To 15cm × 15cm, hereinafter the same as that) the lay overlapped two.
【0086】 [0086]
ろ紙の中心部に、SAPコート面が上になるように、サンプルを置く。 In the center of the filter paper, so that SAP coated surface facing up, placing the sample.
【0087】 [0087]
サンプルの上にサンプルより小さめのティッシュ(4cm×4cm以上)を敷く。 Lay a sample from the smaller of the tissue (4cm × 4cm or more) on top of the sample.
【0088】 [0088]
つぎにアクリルパイプを以下のとおり設置する。 Then placed in the following acrylic pipe.
【0089】 [0089]
パイプと一体化したアクリル台座の下面の穴(20mmφ)に合わせたクッション用パッキンを貼り付ける。 Paste the cushion packing to match the lower surface of the hole in the acrylic base integrated with the pipe (20mmφ).
【0090】 [0090]
スタンドのクランプにてアクリルパイプを保持して、サンプルの中心部にパイプの下端の穴が合うように位置を調節する。 Holding the acrylic pipe with the clamp of the stand, to adjust the position to fit the lower end hole of the pipe in the center of the sample. この場合にサンプルに対して垂直になるように保持する。 Held to be perpendicular to the sample in this case.
【0091】 [0091]
パイプの位置決めに続いてクランプを締めてパイプの位置を固定する。 Tighten the clamp Following positioning of the pipe to fix the position of the pipe.
【0092】 [0092]
ジャッキを上昇させてガラス板とアクリルパイプの下端の台座との間にクッション用パッキンを介して液漏れのないように締め付ける。 Jack to raise the by tightening so leakproof via a cushion packing between the lower end of the pedestal of the glass plate and acryl pipe.
【0093】 [0093]
次に以下の手順で耐水圧の測定を行い、耐水性を評価する。 Then perform the measurement of the water pressure resistance in the following procedure, to evaluate the water resistance.
【0094】 [0094]
アクリルパイプの上方先端から洗浄ビンに入れた測定液(0.9NaCl水溶液、食用青色1号で着色)を静かに少量(例えば、2〜3ml)入れる。 Test solution were placed in the washing bottle from above the tip of the acrylic pipe (0.9 NaCl aqueous solution, colored with Food Blue No. 1) gently small amount (e.g., 2-3 ml) placed. この場合サンプル面が十分に吸液していることを確認する。 In this case the sample surface is to make sure that you are sufficiently liquid absorption.
【0095】 [0095]
1分間放置してサンプル面のSAP粒子を膨潤させる。 And left for 1 minute to swell the SAP particles of the sample surface. この場合測定液が漏れていないことを確認する。 To make sure that in this case the measurement solution is not leaking.
【0096】 [0096]
アクリルパイプの上方先端にロートを付け、測定液を加えていく。 With a funnel above the tip of the acrylic pipe, gradually adding the test solution. ガラス板上のろ紙に液漏れが発生したときのアクリルパイプの目盛りを読み、耐水圧(P)とする。 Read the scale of the acrylic pipe when liquid leakage filter paper on the glass plate is generated, the water pressure resistance (P). 10mmH 2 O単位で読み取るものとする。 It shall be read by 10 mm H 2 O units.
【0097】 [0097]
【実施例】 【Example】
本発明の吸水性耐水性シートをバックアップシートとし、このバッファーシートを吸収体本体と重ね合わせて吸収体製品モデルとする。 The absorbent water-resistant sheet of the present invention as a backup sheet, the buffer sheet superimposed with absorbent body and the absorbent product model. この製品モデルに、100mlずつ3回、計300mlの生理食塩水を添加し、吸液量、バックアップシートへの移行量等の液の物質収支を検証した。 This product model, 100 ml three times, physiological saline was added a total of 300 ml, liquid absorption amount was verified mass balance of the liquid transition amount, and the like to the backup sheet.
【0098】 [0098]
まず吸収体製品モデルの構成について説明する。 First, description will be given of a configuration of the absorbent product model.
【0099】 [0099]
・バックアップシートの調整特許第3046367号の製造方法に従い、20g/m 2のティッシュを基材として、微粒SAP(三菱化学製、商品名「AP211-D」、平均粒径200μm)、MFC(特種製紙製、商品名「S-MFC」)を複合させてシート状吸収体を下記の条件で調製した。 - according to the manufacturing method of the backup sheet of the adjusting Patent No. 3046367, the tissue of 20 g / m 2 as a base material, fine SAP (manufactured by Mitsubishi Chemical Corporation, trade name "AP 211-D", average particle size 200 [mu] m), MFC (Tokushuseishi Ltd., to prepare a sheet-shaped absorbent body under the following conditions are combined the trade name "S-MFC").
【0100】 [0100]
すなわち、前記SAPおよびMFCからなる固形物を、エタノール/水(70/30)混合溶媒系に分散して、SAP濃度20%、MFC濃度0.6%のスラリーを用意した。 That is, the solids consisting of the SAP and MFC, and dispersed in ethanol / water (70/30) mixed solvent system, SAP concentration of 20% was prepared MFC concentration of 0.6% slurry. このスラリーを、前記基材に7mm/3mmの幅で(SAP層7mm、3mm間隔)でライン状パターンにコーティングした後、脱溶媒、乾燥した。 The slurry width (SAP layer 7 mm, 3 mm spacing) of 7 mm / 3 mm to the substrate was coated in a line pattern, desolvation, and dried. 乾燥シートにカーテンスプレー式ホットメルトアプリケーターからEVA系ホットメルトを2g/m 2になるよう繊維状に塗工して、SAP 50g/m 2 、EVA 2g/m 2 、MFC 1.5g/m 2 、基材 20g/m 2の、全目付 73.5g/m 2のシート状吸収体を調製した。 In dry sheet from the curtain spray type hot-melt applicator by coating the EVA-based hot-melt fibrous so as to be 2g / m 2, SAP 50g / m 2, EVA 2g / m 2, MFC 1.5g / m 2, based on of wood 20 g / m 2, to prepare a sheet-shaped absorbent of the total basis weight 73.5 g / m 2.
【0101】 [0101]
このシート状吸収体に、PPスパンボンドSとPPメルトブローンMの積層体であるSMMS構造を有するもの(Avgol社製)を重ね合わせ、熱プレスをして接合一体化し、これをバックアップシートとした。 This sheet-shaped absorbent body, superimposed one having a SMMS structure is a laminate of PP spunbond S and PP meltblown M (Avgol Ltd.), a hot press to integrally joined, which was used as a backup sheet. なお、用いたSMMS構造のものの目付は 20g/m 2で、その耐水圧は200mmH 2 Oであった。 Incidentally, the basis weight of that of the SMMS structure used in 20 g / m 2, the water pressure resistance of 200 mm 2 O. SAPの存在しない基材のみの層が連続して存在するため、通気性は阻害されない。 Because a layer of only the substrate in the absence of SAP are present continuously, breathability is not inhibited.
【0102】 [0102]
・バッファーシートの用意図10(b)に示した開孔フィルムサンプルB(Avgol社製)を用いた。 · Perforated film sample B (manufactured by Avgol Corporation) shown in the buffer sheet prepared Figure 10 (b) was used. このシートも、ほとんど通気抵抗を示さないほどに通気性は高い。 The sheet also has high air permeability enough show little flow resistance.
【0103】 [0103]
・吸収体本体の用意スパンレース基材上にSAPをコーティングしたシート状吸収体(特種製紙製、商品名「メガシン」)を用意する。 And absorption body of available spun lace sheet-shaped absorbent body coated with SAP on a substrate to provide a (Tokushuseishi, Ltd. under the trade name "Megashin"). このシート状吸収体の構成は、SAP 150g/m 2 、不織布基材40g/m 2 、SAPのコート幅7mm、間隔3mm(7/3)で、全目付 190g/m 2であった。 The configuration of the sheet-shaped absorbent body, SAP 150g / m 2, the nonwoven fabric substrate 40g / m 2, SAP coat width 7 mm, at intervals 3 mm (7/3), and a total basis weight of 190 g / m 2.
【0104】 [0104]
このシート状吸収体を100mm×270mmにカットしたものを2枚重ねて、ティッシュで包んだものを吸収体本体とした。 The sheet-shaped absorbent body superposed 2 sheets of which was cut to 100 mm × 270 mm, and the absorber body those wrapped in tissue. この吸収体本体の吸収量は450ml、保持量は320mlであった。 Absorption of the absorbent body 450 ml, amount was 320 ml. この吸収体本体も、不織布基材部分が連続的に存在するため、通気性を阻害しない。 The absorbent body also, since the nonwoven substrate portions are continuously present, do not inhibit breathability.
【0105】 [0105]
前記の吸収体本体の下面全体にバッファーシートを、その開孔径の小さい頭頂部が吸収体本体に対面する図10のように配置し、これにバックアップシートを、ティッシュ面がバッファーシートに接するように配置して吸収体製品モデルを調製した。 The buffer sheet across the lower surface of the absorber body, a small top portion of that pore size is arranged as shown in FIG. 10 facing the absorbent body, to which the backup sheet, as tissue surface contact with the buffer sheet placed to prepare a absorbent product model.
【0106】 [0106]
この製品モデルに、300mlの生理食塩水を100ccずつ10分間隔で3回に分けて添加し、吸収液の存在状態を解析して物質収支を比較した。 This product model, the saline 300ml was added in three portions at 100cc ten minute intervals, were compared mass balance analyzes the existing state of the absorption liquid. バッファーシートがない場合と、バッファーシートがある場合についての物質収支をそれぞれ図15および図16に示す。 And when the buffer sheet is not present, it shows the material balance for the case where there is a buffer sheet in FIGS. 15 and 16.
【0107】 [0107]
図15のバッファーシートを使用しない系では、吸収体で捕捉できなかった水性液はバックアップシートへと流出した。 In the system that does not use the buffer sheet 15, an aqueous solution which can not be captured in absorber has flowed into the backup sheet. 吸水直後と放置して10分後の変化は、トップシートに含まれたわずかな未吸収液が吸収体本体に再吸収されるのみであった。 Left to after 10 minutes change after water absorption was only slight unabsorbed liquid contained in the top sheet is re-absorbed into the absorbent body. 吸収されずに放出された流出量は、1回目23ml、2回目25ml、3回目30mlと、300mlのうち合計78mlがバックアップシートに流出し、バックアップシートはこの量を確実に処理しなければならなかった。 Outflow released without being absorbed, and the first 23 ml, 2 time 25 ml, 3 time 30 ml, a total of 78ml flows out the backup sheet of 300 ml, the backup sheet is had to handle this amount ensures It was. その分バックアップシートに大きな負荷がかかり、漏水の危険性も高くなった。 Takes a big load to the minute backup sheet, also became high risk of leakage.
【0108】 [0108]
ところがバッファーシートを用いた図16(b)の系で観測すると、まず1回目の100mlが供給されると吸収直後の供給液はトップシートに5ml、吸収体に75ml、そして未吸収の19mlがバッファーシートにトラップされ、それからリークした1mlだけがバックアップシートに吸収処理された。 However, when observed in the system of Figure 16 using buffered sheets (b), first, first 100ml feed immediately absorbed and is supplied in 5ml topsheet, 75 ml in the absorber and 19ml of unabsorbed buffer, trapped in the sheet, then only leaked 1ml was absorbed processed backup sheet. 第2回目の供給が行われる間に吸収体本体のSAPが膨潤し吸収余力を持つようになり、トップシートとバッファーシートから液を吸い上げて再吸収した。 SAP of the absorbent body is to have the swollen absorbent surplus during the second round of the supply is carried out, and re-absorbed sucked up liquid from the topsheet and the buffer seat. これによりバッファーシートのトラップ水は空になって、第2回目の液を受け入れる準備が整った。 Thus the trap water of the buffer sheet is empty, ready to accept the second round of the liquid.
【0109】 [0109]
このようにして第3回目の液の吸収を終了すると、1回目 1ml、2回目 2ml、3回目1mlと300mlのうち5mlだけがバックアップシートの負荷として処理された。 In this manner, when the ends of the absorption of the third liquid, the only 5ml of first 1ml, 2 time 2 ml, 3rd 1ml and 300ml was processed as a load of the backup sheet.
【0110】 [0110]
結果的に、バッファーシートの配置によって、バックアップシートへの負荷を78mlから5mlに大幅に減少させるとともに、バックアップシートとしていつでもトラブル時の予備吸収体としての機能を温存させることができた。 Consequently, the arrangement of the buffer sheet, a slight proportion the load on the backup sheet significantly in 5ml of 78 ml, was able to preserve the function of the preliminary absorber in case of trouble at any time as a backup sheet.
【0111】 [0111]
【発明の効果】 【Effect of the invention】
本発明の吸水性耐水性シートによれば、SAPを含有するバックアップシートの採用により防水フィルムを用いることなしに、高通気性の防漏効果を得ることが可能になる。 According to the water-absorbing water-resistant sheet of the present invention, without using the waterproof film by adopting backup sheet containing SAP, it is possible to obtain the leakage preventing effect of the highly air-permeable. さらに、このバックアップシートと多孔性のバッファーシートを接合し、これとSAPを主体とする吸収体本体とを組合せることによりアクイジション機能を発揮させることになり、吸収スピードや拡散の問題点を解決することができる。 Furthermore, this backup joining sheet and the porous buffer sheet, will be exerted the acquisition function by combining the absorbent body composed mainly of this with SAP, to solve the problems of absorption speed and diffusion be able to. これにより通気性にすぐれた超コンパクトな吸収体製品を実現することができる。 Thus it is possible to realize a super-compact absorbent product with excellent breathability.
【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS
【図1】本発明の一実施の形態による吸水性耐水性シートの層構成を示す概略的断面図である。 1 is a schematic sectional view showing a layer structure of the water-absorbent water-resistant sheet according to an embodiment of the present invention.
【図2】本発明の他の実施の形態による吸水性耐水性シートの層構成を示す概略的断面図である。 2 is a schematic sectional view showing a layer structure of the water-absorbent water-resistant sheet according to another embodiment of the present invention.
【図3】本発明のさらに他の実施の形態による吸水性耐水性シートの層構成を示す概略的断面図である。 Figure 3 is a further schematic cross-sectional view showing the layer construction of water-absorbing water resistant sheet according to another embodiment of the present invention.
【図4】本発明の吸水性耐水性シートを製造するプロセスを示す説明図である。 4 is an explanatory diagram showing a process for producing a water-absorbent water-resistant sheet of the present invention.
【図5】本発明の吸水性耐水性シートを製造する他のプロセスを示す説明図である。 FIG. 5 is an explanatory view showing another process for manufacturing a water-absorbing water-resistant sheet of the present invention.
【図6】本発明の吸水性耐水性シートを製造するさらに他のプロセスを示す説明図である。 6 is an explanatory view showing another process for manufacturing a water-absorbing water-resistant sheet of the present invention.
【図7】 (a)、(b)および(c)は、本発明の吸水性耐水性シートを応用した吸収体製品のそれぞれ異なる形態を示す概略的平面図と縦断面図である。 7 (a), (b) and (c) is a longitudinal sectional view and a schematic plan view showing a different embodiment of the absorbent product by applying the water-absorbent water-resistant sheet of the present invention.
【図8】本発明に用いられる、凹凸を持った開孔フィルムの外観を示す斜視図である。 [8] used in the present invention, it is a perspective view showing an appearance of a porous film having irregularities.
【図9】図8の開孔フィルムの部分切欠側面図である。 9 is a partial cutaway side view of a perforated film of FIG.
【図10】吸収体本体に吸収された水性液が開孔フィルムの開孔からバックアップシート側へ排出される状態を示す説明図である。 10 is an explanatory view showing a state in which the aqueous liquid that has been absorbed into the absorbent body is discharged to the backup sheet side from the opening of the perforated film.
【図11】 (a)および(b)は、互いに異なるPE開孔フィルムの頭頂部の開孔の分布例を示す説明図である。 11 (a) and (b) is an explanatory diagram showing a distribution example of the opening of the top of the head of the different PE porous film to each other.
【図12】 (a)〜(d)は、互いに異なるバックアップシート、バッファーシートおよび吸収体本体の相対配置の具体例を示す縦断面図である。 [12] (a) ~ (d) is a longitudinal sectional view showing different backup sheet, a specific example of a relative placement of the buffer sheet and the absorbent body with one another.
【図13】 (a)〜(e)は、吸収体本体、バックアップシートおよびバッファーシートの相対配置の互いに異なる具体例を示す平面図である。 13 (a) ~ (e), the absorber body is a plan view showing a different example of the relative arrangement of the backup sheet and the buffer seat.
【図14】 (a)〜(e)は、吸収体本体、バックアップシート、バッファーシートおよび抵抗シートの相対配置の互いに異なる具体例を示す縦断面図である。 [14] (a) ~ (e), the absorber body is a longitudinal sectional view showing a different example of the backup sheet, relative placement of the buffer sheet and resistive sheet.
【図15】バッファーシートがない場合についての物質収支を示すブロック図である。 15 is a block diagram showing the material balance for when the buffer sheet is not.
【図16】バッファーシートがある場合についての物質収支を示すブロック図である。 16 is a block diagram showing the material balance for the case where there is a buffer sheet.
【図17】評価装置の全体を示す図である。 17 is a diagram showing an overall evaluation device.
【図18】評価サンプル装着部分の詳細を示す図である。 FIG. 18 is a diagram showing the details of the evaluation sample mounting portion.
【符号の説明】 DESCRIPTION OF SYMBOLS
1 疎水性不織布層2 SAP層3 親水性シート層4,5 ホットメルト層6 起毛構造7 ティッシュ11 吸収体本体12 バックアップシート20 バッファーシート21 フィルム22 ロート状周壁23 開口24 膨出部30 抵抗シート 1 hydrophobic nonwoven layer 2 SAP layer 3 hydrophilic sheet layers 4 and 5 hot-melt layer 6 brushed structure 7 tissue 11 absorbent body 12 backup sheet 20 buffer sheet 21 film 22 funnel-shaped wall 23 opening 24 bulge portion 30 resistive sheet

Claims (29)

  1. 少なくとも150mmH 2 O以上の耐水性を有する疎水性不織布と、水分拡散性を有する親水性シートと、前記疎水性不織布と前記親水性シートとの間に介在する、平均粒径が500μm以下のSAP粒子と該SAP粒子のそれぞれを相互に結合するミクロフィブリル状セルロースとから構成されている SAP層とで構成された、3層構造を持つことを特徴とする吸水性耐水性シート。 A hydrophobic nonwoven fabric having at least 150mmH 2 O or more water-resistant, and a hydrophilic sheet having a moisture diffusivity, intervening, average particle size less 500 [mu] m SAP particles between the hydrophobic nonwoven fabric and the hydrophilic sheet and the composed of the SAP layer is composed of a microfibrillar cellulose to bind to each other each of the SAP particles, the water-absorbent water-resistant sheet characterized by having a three-layer structure.
  2. 前記SAP層が、実質的に全面に均一な厚みで存在する請求項1に記載の吸水性耐水性シート。 The SAP layer, absorbent waterproof sheet according to claim 1 which is present in a uniform thickness substantially over the entire surface.
  3. 前記SAP層が、部分的に目付の異なる目付分布を持っている請求項1に記載の吸水性耐水性シート。 The SAP layer, absorbent waterproof sheet according to claim 1 which have a partially different basis weight distribution of basis weight.
  4. 前記SAP層が、前記SAP粒子の存在域と前記SAP粒子の非存在域からなる請求項1に記載の吸水性耐水性シート。 The SAP layer, absorbent waterproof sheet according to claim 1, existent region of the SAP particles made of a non-existent region of the SAP particles.
  5. 前記SAP粒子の存在域と前記SAP粒子の非存在域とが交互にライン状に分布している請求項4に記載の吸水性耐水性シート。 Absorbent waterproof sheet according to claim 4 in which the non-existent region of the SAP particles and the presence area of ​​the SAP particles are distributed in a line shape alternately.
  6. 前記疎水性不織布が、スパンボンド不織布をSで表し、メルトブローン不織布をMで表した場合に、SMSまたはSMMSの順序で配置されたものである請求項1〜5のいずれかに記載の吸水性耐水性シート。 Wherein the hydrophobic nonwoven fabric, represent spunbonded nonwoven fabric S, when the meltblown nonwoven fabric expressed in M, absorbent water according to any one of claims 1 to 5, which has been arranged in order of SMS or SMMS gender sheet.
  7. 前記親水性シートが、木材パルプ、レーヨンおよびコットンのいずれかのセルロース系繊維を含むものである請求項1〜5のいずれかに記載の吸水性耐水性シート。 The hydrophilic sheet, absorbent waterproof sheet according to claim 1 is intended to include wood pulp, any of cellulosic fibers of rayon and cotton.
  8. 前記親水性シートが、木材パルプからなるティッシュペーパーである請求項1〜7のいずれかに記載の吸水性耐水性シート。 The hydrophilic sheet, absorbent waterproof sheet according to claim 1 is a tissue paper made from wood pulp.
  9. 前記SAP粒子が、平均粒径300μm以下、AUL30ml/g以下のゲルブロッキング性を有する微粉状SAP粒子である請求項1〜8のいずれかに記載の吸水性耐水性シート。 The SAP particles, average particle size below 300 [mu] m, the water-absorbent water-resistance sheet according to claim 1 is a pulverulent SAP particles having the following gel blocking AUL30ml / g.
  10. 通気度が0.5m 3 /min・m 2以上である請求項1〜9のいずれかに記載の吸水性耐水性シート。 Absorbent waterproof sheet according to any one of claims 1 to 9 ventilation degree is 0.5m 3 / min · m 2 or more.
  11. 前記疎水性不織布と前記SAP層との間、および前記親水性シートと前記SAP層との間の接合が繊維状ホットメルト樹脂によってなされている請求項1〜 10のいずれかに記載の吸水性耐水性シート。 Between the SAP layer and the hydrophobic nonwoven fabric, and water-absorbing water according to any one of claims 1 to 10, joining is made by a fibrous hot-melt resin between the hydrophilic sheet and the SAP layer gender sheet.
  12. 前記SAP層と前記セルロース系繊維を含む前記親水性シートの接合が、前記SAP層に含まれるミクロフィブリル状セルロースによって行われ、前記SAP層と前記疎水性不織布との接合が繊維状ホットメルト樹脂によって行われている請求項7〜 11のいずれかに記載の吸水性耐水性シート。 Bonding of the hydrophilic sheet containing the cellulosic fibers and the SAP layer, the carried out by the microfibrillar cellulose contained in SAP layer, bonding between the hydrophobic nonwoven fabric and the SAP layer is the fibrous hot-melt resin absorbent waterproof sheet according to any one of claims 7-11 being carried out.
  13. ティッシュペーパーからなる基材の表面に、ミクロフィブリル状セルロース、SAP粒子およびエタノール/水系の混合溶媒からなるスラリーを塗工し、ついで前記スラリー中の溶媒を除去したのち乾燥することにより、シート状吸収体を調製する工程と、前記シート状吸収体の前記SAP粒子の露出面にホットメルト樹脂を繊維状にスプレーし、このホットメルト樹脂の上に耐水性不織布を重ね合わせ、次に加熱して前記ホットメルト樹脂により前記シート状吸収体と前記耐水性不織布とを接合することを特徴とする吸水性耐水性シートの製造法。 On the surface of a substrate made of tissue paper, microfibrillar cellulose, by coating the slurry of a mixed solvent of SAP particles and ethanol / water and then dried after removing the solvent of the slurry, a sheet-shaped absorbent preparing a body, sprayed with hot-melt resin to the fibrous on the exposed surface of the SAP particles of the sheet-shaped absorbent body, superimposed water resistance nonwoven fabric over the hot-melt resin, and then heated to the preparation of water-absorbent water-resistant sheet, which comprises bonding the water-resistant nonwoven fabric and the sheet-shaped absorbent body by a hot-melt resin.
  14. 請求項1〜 12の吸水性耐水性シートの前記疎水性シート面を外面、前記親水性シート面が内面になるように配置してバックアップシートとし、このバックアップシートの内面側に、シート状の吸収体本体を組合せて構成したことを特徴とする吸収体製品。 The hydrophobic sheet surface of the water-absorbing water resistant sheet according to claim 1 to 12 an outer surface, wherein the hydrophilic sheet surface and the backup sheet was disposed so that the inner surface, the inner surface of the backup sheet, a sheet-like absorbent absorbent product characterized by being configured by combining body body.
  15. 前記吸収体本体が、前記SAP粒子を50%以上含有するシート状吸収体である請求項14に記載の吸収体製品。 The absorbent product of claim 14 wherein the absorbent body, the SAP particles is a sheet-shaped absorbent bodies containing 50% or more.
  16. 前記吸収体本体と前記バックアップシートの間に、圧力緩和および流量制御のための高通気性のバッファーシートが介在している請求項14または15に記載の吸収体製品。 Wherein between the absorbent body of the backup sheet, absorbent product according to claim 14 or 15 highly air-permeable buffer sheet for pressure relief and flow control are interposed.
  17. 前記バッファーシートが多数の開孔を有し、各開孔の周壁が他の部分から表面起立して凹凸表面を形成している開孔フィルムである請求項16に記載の吸収体製品。 The absorbent product of claim 16 wherein the buffer sheet has a large number of apertures, a perforated film which peripheral wall of each aperture forms an uneven surface by surface rising from the other portions.
  18. 前記開孔フィルムの前記開孔の周壁が、その一端から他端に向かうにしたがって順次減少するテーパー面を形成し、前記開孔フィルムが、その開孔の開孔径の小さい側を吸収体本体面に接して配置され、開孔径の大きい側が前記バックアップシート面に接して配置されている請求項17に記載吸収体製品。 Wherein the peripheral wall of the opening of the porous film forms a sequentially decreasing tapered surface toward the other end from one end, the porous film is, the absorber body surface the small end of the aperture diameter of the aperture to be placed in contact with absorbent product of claim 17 side larger opening diameter is placed in contact with the backup sheet surface.
  19. 前記開孔の開孔面積の総和が、前記開孔フィルムの全面積の10%〜50%である請求項17または18に記載の吸収体製品。 Absorbent product according to claim 17 or 18 is 10% to 50% of the total area of the sum, the porous film of the open area of the apertures.
  20. 前記開孔フィルムの開孔数が1〜100個/cm 2であり、前記開孔の周壁の高さを含む前記開孔フィルムの厚みが1mm以下である請求項1719のいずれかに記載の吸収体製品。 The opening speed of the porous film is 1 to 100 a / cm 2, according to any of claims 17-19 the thickness of the porous film is 1mm or less including the height of the peripheral wall of the opening absorbent products.
  21. 前記バッファーシートが、加圧状態で水性液の透過を許容する連続気泡を持った厚み3mm以下、セル数20個/25mm以上の発泡スポンジシートである請求項16に記載の吸収体製品。 Absorbent product according to the buffer sheet, according to claim 16 which is a pressure below 3mm thick having an open cell that allows the transmission of aqueous fluid in the pressure condition, the number 20 cell / 25mm or more foamed sponge sheet.
  22. 前記発泡スポンジシートが、着用時の乾燥時には厚さが1mm以下であり、使用時の吸水により厚みが1mm以上に膨化するように圧着処理されている請求項21に記載の吸収体製品。 The foam sponge sheet, is not less 1mm or less in thickness when dry when worn, absorbent product according to claim 21 in which the thickness by water absorption during use is crimped processed to swelling above 1mm.
  23. 前記発泡スポンジシートが、疎水性のポリエチレンフォーム、ポリプロピレンフォームまたはポリウレタンフォームのいずれかである請求項21または22に記載の吸収体製品。 The foam sponge sheet, absorbent product according to claim 21 or 22 is either polyethylene foam, polypropylene foam or polyurethane foam of hydrophobic.
  24. 前記バッファーシートが、前記吸収体本体の下面全体をカバーするように配置されている請求項1623のいずれかに記載の吸収体製品。 Absorbent product according to any one of the buffer sheet, the absorber according disposed so as to cover the entire lower surface of the main body section 16-23.
  25. 前記バッファーシートが、前記吸収体本体の下面部において中央部位から後身頃相当部位の一部をカバーするように配置されている請求項1623のいずれかに記載の吸収体製品。 Absorbent product according to any one of the buffer sheet, the absorber according disposed so as to cover a portion of the back body corresponding portion from the central portion in the lower surface of the main body section 16-23.
  26. 前記バッファーシートが、前記吸収体本体の下面部において中央部位から前見頃相当部位の一部をカバーするように配置されている請求項1623のいずれかに記載の吸収体製品。 Absorbent product according to any one of the buffer sheet, the absorber according the lower surface of the body are arranged so as to cover a part of the previous best time corresponding site from the central site to claim 16-23.
  27. 前記バッファーシートが、前記吸収体本体の両側面部位と両側面下部位のみをカバーするように配置されている請求項1626のいずれかに記載の吸収体製品。 Absorbent product according to any one of the buffer sheet, the absorber claims is arranged to cover only the sides sites and both sides the lower position of the body 16-26.
  28. 前記バッファーシートおよび前記バックアップシートに、抵抗シートとして耐水性不織布がさらに配置されている請求項1627のいずれかに記載の吸収体製品。 Absorbent product according to any one of the buffer sheet and the backup to the sheet, resistive sheet waterproof nonwoven fabric according to claim 16 to which is further arranged 27 as.
  29. 前記バッファーシートの多孔性領域の一部に、耐水性不織布または非水透過性フィルムをさらに重ねてなる請求項1628のいずれかに記載の吸収体製品。 Absorbent product according to any one of the buffer portion of the porous area of the sheet, Motomeko 16-28 comprising further stacked waterproof nonwoven fabric or non-aqueous permeable film.
JP2001135238A 2001-05-02 2001-05-02 Absorbent water resistance sheet, their preparation and absorbent product using the same Active JP4556017B2 (en)