JP4492868B2 - Bandage or adhesive dressing - Google Patents

Bandage or adhesive dressing Download PDF

Info

Publication number
JP4492868B2
JP4492868B2 JP2004339822A JP2004339822A JP4492868B2 JP 4492868 B2 JP4492868 B2 JP 4492868B2 JP 2004339822 A JP2004339822 A JP 2004339822A JP 2004339822 A JP2004339822 A JP 2004339822A JP 4492868 B2 JP4492868 B2 JP 4492868B2
Authority
JP
Japan
Prior art keywords
adhesive
portion
substrate
skin
bandage
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2004339822A
Other languages
Japanese (ja)
Other versions
JP2006141908A (en
Inventor
浩太郎 下林
治 大平
Original Assignee
日東電工株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日東電工株式会社 filed Critical 日東電工株式会社
Priority to JP2004339822A priority Critical patent/JP4492868B2/en
Publication of JP2006141908A publication Critical patent/JP2006141908A/en
Application granted granted Critical
Publication of JP4492868B2 publication Critical patent/JP4492868B2/en
Application status is Active legal-status Critical
Anticipated expiration legal-status Critical

Description

本発明は、伸縮性を有する基材と粘着層を含む皮膚貼付材に関し、例えば水仕事の後に取り替えることなく継続して使用しても、貼付部分の皮膚のふやけ(以下、「白化現象」ともいう。)が軽減化された皮膚貼付材に関する。 The present invention relates to a skin patch that includes an adhesive layer with a substrate having an elasticity, for example be continuously used without replacing after wet work, maceration of the skin of the patch portion (hereinafter, both "whitening" say.) on the adhesive skin patch that has been mitigation is.

皮膚貼付材である救急絆創膏や粘着ドレッシング類は、通常医療用テープとして用いられる。 Bandage or adhesive dressings is a skin patch is usually used as a medical tape. 該皮膚貼付材は、基材と皮膚貼付用の粘着層からなる粘着テープを略長方形に打ち抜き、中央部にガーゼ等からなる当て材(パッド部)を設け、更に剥離ライナーを貼り合わせ、一枚ごとに包装され市販されているものが一般的である。 The skin patch is punched adhesive tape comprising the pressure-sensitive layer of the substrate and the skin attached to the substantially rectangular abutting member made of gauze or the like (the pad portion) provided in the central portion, bonded to further release liner, one those packaged marketed each is common. これらの医療用テープは人体に貼付するものであるため、その基材としては、柔軟性、強度、風合い、皮膚(患部)への密封性などの問題を考慮して選択されている。 Since these medical tapes are those stuck to the human body, as its base material, flexibility, strength, texture, and is selected in consideration of problems such as tightness of the skin (affected part). パッド部は、創傷部位の血液・膿を吸収・吸液するためのに設けることができ、素材として、レーヨン不織布、脱脂綿、ガーゼ等が例示される。 Pad portion may be provided in order to absorb and liquid absorbing blood-pus wound site, as a material, rayon nonwoven, absorbent cotton, gauze and the like.
皮膚貼付材である救急絆創膏については、既に一般に使用されており、各種工夫されたものについて既に多くの開示がある(特許文献1〜3)。 The first-aid adhesive tape is adhesive skin patch, already commonly used, there are already a number of disclosures for those various devised (Patent Documents 1 to 3).

各種基材の中でも通気性及び伸縮性を有する不織布や織布や編布は、粘着ドレッシングや救急絆創膏などの医療用テープの基材として優れた特性を発揮することができる。 Nonwoven or woven fabric or knitted fabric having air permeability and stretchability among various substrates can exhibit excellent characteristics as a base material of a medical tape, such as adhesive dressings and bandage. 最近では、ポリウレタン(PU)、スチレン−イソプレン−スチレン共重合体(SIS)、スチレン−エチレン−ブチレン−スチレン共重合体(SEBS)などの伸縮性と通気性を備えたメルトブロー法による不織布が使用されている。 Recently group consisting of polyurethane (PU), styrene - isoprene - styrene copolymer (SIS), styrene - ethylene - butylene - nonwoven is used by styrene copolymer (SEBS) elasticity and melt blow method with a breathable such ing. また近時、ポリエステル熱可塑性エラストマー等を用いたスパンボンド法による伸縮不織布が使用される。 Also recently, stretchable nonwoven fabric is used by the spunbond method using a polyester thermoplastic elastomer.

ポリウレタンゴムを芯にし、これをカバーリングしてなる伸縮糸を伸びる方向に打ち込んだスパンディックス織物や伸びる方向に糸を強撚糸を打ち込んだ強撚布やポリエステル糸を丸編機で編み込んだ伸縮性編布が、通気性強度面及び皮膚へのフィット性・感温比がよい点で有用な基材として使用される。 A polyurethane rubber to the core, this stretch braided a strong twist cloth or polyester yarn implanted a strong twisting the yarn to span Dix textiles and extending direction that is implanted in the direction of extending the stretch yarn made by covering with a circular knitting machine knitted fabrics are used as useful substrates in terms good fit-temperature sensitive ratio for breathability of strength and skin.

上述の不織布、織布、編布等の基材は通気性はあるものの、これらが水に濡れた場合は、パッド部まで水が浸入し、水を吸収したパッド部には水分の逃げ道がなく、パッド部分に接触した皮膚がふやけた状態(白化現象;マセレーション)を生じ、余計に皮膚刺激を生じ、皮膚の損傷部分をさらに傷めかねない場合があった。 Above nonwoven, woven, substrate, such as knitted fabric although breathable some, if they were exposed to water, the water infiltrates to the pad part, no escape route water to the pad portion having absorbed water , state of skin in contact with the pad portion is swollen (whitening phenomenon; maceration) occur, extra cause skin irritation, there is a case that could further damage the damaged portion of the skin.

一般に皮膚貼付材である救急絆創膏は、軽度の切り傷・スリ傷・サシ傷・創傷面の殺菌・消毒・被覆などに使用されるが、例えば水仕事など水中で使用すること等により救急絆創膏が濡れた後は貼りかえるのが一般的である。 In general first-aid adhesive tape is adhesive skin patch is used in such disinfection-coated mild cut-scratches, punctures, the wound surface, e.g., first-aid adhesive tape is wetted by such underwater use such as kitchen work is it is common frog stuck after. これは、水中で使用することによるパッド部分への水浸入の影響が非常に大きいことによる。 This effect of water penetration into the pad portion by using in water due to the very large.

極薄の20〜30μmポリウレタンフィルム等を基材とするフィルムドレッシングでも、指関節などの動きがある部分に貼付したときには、密着貼付されていない僅かな部分から毛細管現象的に水が浸入してしまう。 Be a film dressing to the substrate a 20~30μm polyurethane films such extremely thin, when attached to a portion where there is movement of the finger joints, capillary action of water from the small portion that is not in close contact patch resulting in intrusion . 一旦水が浸入すると、パッド部では水分を吸水してしまうため、本来損傷部位の血液・膿などを吸収することに支障が生じ、パッド部位に接触する皮膚は白化現象を生じ、その影響により患部をさらに悪化させるという問題がある。 Once the water enters, since the pad portion thereby to water moisture, create an obstacle to absorb such as blood, pus original injury site, skin contact with the pad portion produces a whitening phenomenon, the affected area by the influence there is a problem that further exacerbate.

傷口の完全防水のために、極薄フィルムドレッシングを使用する場合がある。 For waterproof the wound may use a very thin film dressings. このような皮膚貼付材は、皮膚に密着させて貼付すれば防水性は得られる。 Such adhesive skin patch is waterproof when attached in close contact with the skin is obtained. しかし、該フィルムは非通気性であり、例えば透湿性は300〜800g/mm 2 、24時間、40℃×75RH%程度あるものの、使用性や扱いが難しい。 However, the film is non-breathable, for example moisture permeability 300 to 800 g / mm 2, 24 hours, although about 40 ° C. × 75 RH%, it is difficult usability and handling. 例えば使用することの多い指先などの部位では発汗が多く、このような発汗によっても、皮膚は白化現象を生じる場合がある。 For example perspiration at the site of such large finger be used many, even by such perspiration, skin may occur whitening phenomenon.

特開2000-237295号公報 JP 2000-237295 JP 特開平10-179710号公報 JP 10-179710 discloses 特開平09-206369号公報 JP 09-206369 discloses

本発明の目的は、水中で使用すること等により水が浸透しても、皮膚が白化現象を起こし難い皮膚貼付材を提供することを課題とする。 An object of the present invention, even if water penetrates the like can be used in water, the skin is an object of the present invention to provide a hard skin patch to cause whitening. さらに、使用中の接着性なども良好で、フィット性・通気性が良好で、違和感が少ない皮膚貼付材を提供することを課題とする。 Furthermore, also good, such as adhesion in use, fit breathable is good, and to provide a sense of discomfort is less skin patch.

本発明者らは、上記課題を解決するために鋭意研究した結果、略長方形の皮膚貼付材の長辺側に対して垂直になるように、連続すじ状の粘着剤非塗布部分を設けることにより、当該部分が排水溝及び/又は通気孔としての役割を果たし、基材及び/又はパッド部への吸水が抑制され、皮膚が白化現象を起こし難くなることを見出し、本発明を完成した。 The present inventors have made intensive studies to solve the above problems, to be perpendicular to the long side of the skin patch of substantially rectangular, by providing the continuous streak-like adhesive uncoated portion serves as the partial drainage ditch and / or vents, are water suppression to the substrate and / or the pad unit, skin found that hardly cause a whitening phenomenon, and have completed the present invention.

すなわち本発明は以下からなる。 Namely, the present invention comprises the following.
1. 1. 伸縮性を有する基材と粘着層を含む皮膚貼付材において、基材に粘着剤の非塗布部分が連続すじ状に設けられていることを特徴とする皮膚貼付材。 In the adhesive skin patch comprising a substrate adhesive layer having elasticity, adhesive skin patch, wherein the uncoated portion of the adhesive is provided in a continuous stripe shape on the substrate.
2. 2. 皮膚貼付材が長辺と短辺を有する形状からなり、該皮膚貼付材が少なくとも長辺方向に伸縮し、粘着剤の非塗布部分が該長辺方向に対して垂直方向に設けられている前項1に記載の皮膚貼付材。 Skin patch is a shape having long sides and short sides, preceding said skin patch is stretchable at least in the long side direction, are provided in the vertical direction uncoated portions of the adhesive with respect to the long side direction skin patch material according to 1.
3. 3. 連続すじ状の粘着剤の非塗布部分が、0.5〜1.5mm幅の直線又はウェイブ状であり、そのピッチが2〜5mm間隔で設けられてなる前項1又は2に記載の皮膚貼付材。 Uncoated portions of the continuous stripe-like adhesive is a linear or wave-shaped 0.5~1.5mm width, adhesive skin patch according to item 1 or 2 that pitch is provided by 2~5mm intervals.
4. 4. 伸縮性を有する基材が、長辺方向の50%伸張時における伸張回復率が80%以上であり、引張強度が10N/19mm幅以上である前項2又は3に記載の皮膚貼付材。 A substrate having a stretchability, stretch recovery ratio at 50% elongation in the long side direction is not less than 80%, a tensile strength of the adhesive skin patch according to item 2 or 3 is 10 N / 19 mm width or more.
5. 5. 剥離紙に粘着剤溶液を塗布し、基材を該粘着剤溶液を塗布した剥離紙と貼り合わせ、櫛状刃を充てて移動させ、基材に連続すじ状の粘着剤の非塗布部分を設ける工程を含む前項1〜4のいずれか一に記載の皮膚貼付材の製造方法。 The adhesive solution was applied to a release paper, is bonded to a release paper coated with a pressure-sensitive adhesive solution substrate is moved devotes comb blade, providing the non-coating portion of the continuous stripe-like adhesive to a substrate method for producing a skin patch according to any one of the preceding 1-4 including step.

本発明の皮膚貼付材は、粘着剤非塗布部分を有するため、当該部分が通気孔及び/又は排水路の役割を果たし、水が入りがたく比較的出やすくなる。 Skin patch of the present invention has a pressure-sensitive adhesive non-coated portion, this portion serves as a vent and / or drainage, water tends out relatively Gataku entered. これにより、皮膚の白化現象が抑制され、創傷部位を快適に維持して治療することができる。 Accordingly, whitening of the skin is suppressed, it can be treated to maintain comfortable the wound site. 本発明に用いられる皮膚貼付材の基材は、水分を吸水し難くかつ伸縮性を有するので、優れた粘着性を有する。 The substrate of the skin patch to be used in the present invention has a water absorption hardly and stretch of water, have excellent tack.

本発明の皮膚貼付材は、具体的には救急絆創膏、粘着ドレッシング等が挙げられる。 Skin patch of the present invention is specifically bandage, adhesive dressings, and the like. 該皮膚貼付材は、基材と粘着層が設けられており、さらにパッド部を有するものが好適である。 The skin patch is the adhesive layer is provided with a substrate, it is preferable to further have a pad portion.

本発明の皮膚貼付材は基材と粘着層を有し、例えば図4に示すように長辺と短辺を有する略長方形からなり、救急絆創膏、フィルムドレッシングとして通常用いられている形状であれば良く、特に限定されない。 Skin patch of the present invention has an adhesive layer and the substrate, for example, a substantially rectangular shape to have a long side and a short side as shown in FIG. 4, first-aid adhesive tape, have a shape which is generally used as a film dressing well, not particularly limited.
本発明の皮膚貼付材は、基材の長辺方向に対して垂直方向に連続した粘着剤非塗布部分を設けることを特徴とする。 Skin patch of the present invention is characterized by providing a continuous adhesive uncoated portion in a direction perpendicular to the longitudinal direction of the substrate. 粘着剤非塗布部分は、例えば連続した直線若しくはウェイブ状の形状とすることができ、該非塗布部分の幅は0.5〜1.5mmで、そのピッチは2〜5mm間隔とすることができる。 Uncoated portions adhesive, for example, can be a continuous linear or wave-like shape, the width of the non-coating portion is 0.5 to 1.5 mm, its pitch may be 2~5mm interval.
粘着剤非塗布部分は、必要に応じてパッド部に相応する部分にのみ設けても良く、皮膚貼付材の全面に設けても良い。 Uncoated portion adhesive may be provided only in the portion corresponding to the pad portion may optionally be provided over the entire surface of the skin patch. 粘着剤非塗布部分の大きさは、皮膚の白化現象の軽減化と皮膚貼付材の皮膚への粘着度との関係において適宜決定することができる。 The size of the adhesive non-application portion may be appropriately determined in relation to the tackiness to the skin of Mitigation and skin patch of bleaching the skin. 皮膚への粘着度を考慮すると、パッド部に相応する部分にのみ設けることが好ましい。 Considering the tackiness to the skin, it is preferable to provide only a portion corresponding to the pad portion.

本発明における基材は、通気性及び伸縮性を有し、皮膚貼付材で使用可能な材料であれば良い。 Substrate in the present invention, breathable and stretchable may be a material that can be used in the skin patch. このような性状を有する公知の基材の例として、合成繊維よりメルトブロー法で得られるポリウレタン不織布、スパンボンド法で得られるポリエステル不織布、ナイロン不織布、ポリエステル・綿混紡の織布より得られるスパンディクス伸縮布、並びに縦、横方向に伸縮性を有する伸縮性ポリエステル編布等を挙げることができる。 Examples of known substrates having such properties, a polyurethane non-woven fabric obtained by melt-blowing method of synthetic fibers, non-woven polyester fabric obtained by the spunbond method, a nylon nonwoven fabric, Supandikusu stretch obtained from woven polyester cotton blend cloth, as well as vertical, stretchable polyester knitted fabric or the like having stretchability in the transverse direction may be mentioned. これらの不織布の中で超極細フィラメントよりなるポリウレタン伸縮不織布が好ましく、平均繊維径が7〜16μmのポリウレタンフィラメントよりなるものが強度面で特に好ましい。 Polyurethane elastic nonwoven fabric made of ultrafine filaments are preferred among these nonwoven fabric having an average fiber diameter of a polyurethane filament of 7~16μm is particularly preferred in terms of strength.

ポリウレタンゴムをコアー芯に合成繊維若しくは綿と合成繊維との混紡した糸でカバーリングした糸を打ち込んだスパンディクス織物、原糸自体の結晶構造が伸びる方向にジグザグ状になった繊維を打ち込んだ織物、捲縮加工され、伸縮性能をもつポリエステル若しくはナイロン伸縮布、又はポリエステル糸若しくはナイロン糸を丸編機で編み込んだ全方向伸縮編布等の疎水性の合成繊維等の伸縮する素材が、通気性、強度面及びフィット性・感温比等が良いので、基材として好適に用いられる。 Blended yarn in Supandikusu fabric implanted a covering yarn, fabric implanted fibers become zigzag in the direction of the crystal structure of the raw yarn itself extends with synthetic fibers or cotton polyurethane rubber core core and synthetic fibers is crimped, stretch performance polyester or nylon stretch fabric with or polyester yarns or stretch to the material, such as hydrophobic synthetic fibers such as omnidirectional stretch knitted fabric woven with nylon yarn in circular knitting machines, breathable since the strength plane and fit-temperature sensitive ratios, etc. are good, it is suitably used as a substrate.
本発明の基材の坪量は特に限定はされないが、50〜100g/m 2の範囲内であることが好ましい。 The basis weight of the base material of the present invention is not particularly limited, it is preferably in the range of 50 to 100 g / m 2. 該基材の厚みは、100〜500μm程度である。 The thickness of the substrate is about 100~500μm.

本発明における基材は伸縮性を有するので、直接基材に粘着剤の塗布部分及び非塗布部分を設けることは困難である。 Since the base material in the present invention has a stretchable, it is difficult to directly substrate provided with a coating portion and a non-coating portion of the adhesive. そこで、剥離紙の上に粘着剤溶液を塗布し、上述の基材と該剥離紙を貼り合わせ、その上に上述のピッチ幅、大きさの櫛状刃を充てて移動させることで、櫛状刃のあたった部分にのみ基材に粘着剤が塗布され、基材に粘着剤の塗布部分と非塗布部分を設けることができる。 Therefore, the pressure-sensitive adhesive solution was coated on a release paper, bonding the substrate and the release paper mentioned above, the pitch width of the above thereon, by moving devotes comb blade size, comb is adhesive applied to only substrate to hit parts of the blade may be provided a coating portion and a non-coating portion of the adhesive to the substrate.
直線状の連続すじ状の粘着剤非塗布部分は、櫛状刃をほぼ一定速度で移動させることにより設けることができ、ウェイブ状の粘着剤非塗布部分は、同様に櫛状刃をほぼ一定間隔で振幅させながら移動させることにより設けることができる。 Linear continuous streaky adhesive uncoated portion of the comb-shaped blades can be a provided by moving substantially at a constant speed, wave-like adhesive uncoated portion is likewise substantially constant spacing comb blade in can be provided by moving while amplitude.
粘着剤乾燥は、基材と粘着剤を絡ませる(投錨力を維持させる)ため粘着剤がウェットの状態で剥離紙を貼り合わせることができる。 Adhesive drying, entangling substrate and the adhesive (to maintain the anchor force) because it is possible to adhesive bond the release paper in a wet state. 基材と粘着剤を絡ませる必要がない場合は、完全に溶媒が乾燥後に該基材と剥離紙を貼り合わせることができる。 If it is not necessary to entangle the base material and the adhesive are completely solvent can be attached to release paper and the substrate after drying.
本明細書において、基材に粘着剤が塗布された状態のものを便宜上粘着シートという。 In this specification, those of the state where the adhesive is applied to the substrate for convenience of pressure-sensitive adhesive sheet.

本発明の皮膚貼付材における粘着剤は、アクリル系粘着剤、ゴム系粘着剤、シリコーン系粘着剤を用いることができ、刺激性の少ないものが好適である。 Adhesive in the skin patch of the present invention, acrylic adhesive, rubber adhesive, can be used a silicone adhesive, it is preferred with less irritation. アクリル系粘着剤は、例えばイソノニルアクリレート、2エチルヘキシルアクリレート、2ヒドロキシアクリレート等のアクリル酸エステル系モノマーの単独又は共重合体あるいはこれらのモノマーと酢酸ビニル、アクリル酸、メタクリル酸などのモノマーとの共重合体などが挙げられる。 Acrylic adhesive, for example, isononyl acrylate, 2-ethylhexyl acrylate, acrylic acid ester monomers such as 2-hydroxy acrylate homo- or copolymers, or these monomers with vinyl acetate, acrylic acid, co with a monomer such as methacrylic acid such as polymers and the like. ゴム系粘着剤としては例えば合成ゴムポリイソプレンゴム、スチレン−イソプレン−スチレンブロック共重合体などのゴム基材に粘着付与剤、軟化剤などを配合した組成物が挙げられる。 Rubber As the adhesive, for example, synthetic rubbers polyisoprene rubber, styrene - isoprene - tackifier to a rubber substrate, such as a styrene block copolymer, composition containing such a softening agent. 該連続したすじ状の粘着剤非塗布部分を得る為に、上記粘着剤の溶液粘度は30〜80pa/sが適しており、粘着剤の塗布前形態はエマルジョンタイプでも溶液タイプであっても所望の粘着剤非塗布部分のある連続すじ状の部分を得ることができる。 In order to obtain the continuous streak adhesive uncoated portion, the solution viscosity of the adhesive is suitably 30~80pa / s, coating pre-form of the adhesive as a solution type in emulsion type desired it is possible to obtain a continuous stripe-like portion of the viscous agent-coated part. ただし30pa/s以下の低粘度では粘着剤が流れてしまい、また80pa/s以上では高粘度の為、すじが描けなくなる。 However, in the following low viscosity 30 Pa / s would be adhesive to flow, and because of the high viscosity of 80 Pa / s or more, streaks will not draw.

次に、前記剥離紙を剥がし、基材に連続すじ状に設けられた粘着剤の非塗布部分を有する粘着シートに、必要に応じてパッド部を設けることができる。 Then, peeling the release paper, the adhesive sheet having the non-coated portions of the adhesive provided on the substrate in continuous stripes can be provided with a pad portion as necessary.

パッド部を設けた粘着シートの上に、粘着面及びパッド部を保護するための剥離ライナーを貼り合わせたのち、皮膚貼付材の長辺を粘着シートの幅方向に、皮膚貼付材の短辺を同様に長手方向に一致させて、例えば図4の救急絆創膏の形状に打ち抜き加工し、救急絆創膏を製造することができる。 On the adhesive sheet provided with a pad portion, after attaching a release liner to protect the adhesive surface and the pad portion, the long sides of the adhesive skin patch in the width direction of the pressure-sensitive adhesive sheet, the short side of the skin patch Similarly to match the longitudinal direction, for example, punched into a shape of adhesive bandage of Figure 4, it is possible to produce a bandage. このように打ち抜くことで、皮膚貼付材の長辺方向に対して垂直方向に連続すじ状の粘着非塗布部分を設けることができる。 By punching this way, it is possible to provide a continuous stripe-like adhesive uncoated portion in a direction perpendicular to the longitudinal direction of the adhesive skin patch.

本発明の皮膚貼付材は、使用時に剥離ライナーを剥がした後、基材を伸張させて皮膚に貼付する。 Skin patch of the present invention, after removal of the release liner during use, by stretching the substrate adhered to the skin. 救急絆創膏を人体に貼付する場合、例えば指の屈曲部に巻きつける等、動きある部位に貼られることが主であり、該伸縮する皮膚貼付材は張力がかかった状態で貼付されるのが通常である。 When sticking the adhesive bandage to the human body, for example, such as wound the bent portion of the finger, is mainly to be attached to a site in motion, usually the adhesive skin patch to the expansion and contraction is attached under tension it is.

以下に実施例及び比較例を設けて本発明についてより具体的にする。 To more specifically for the present invention by providing examples and comparative examples below. 本発明はこれらの限定されるものではなく、本技術思想を逸脱しない範囲で種々の応用が可能である。 The present invention is not intended to be those limited, and can be variously applied without departing from the present technical concept.

(実施例1)救急絆創膏1)材料 (Example 1) bandage 1) Materials
a)基材: a) a base:
平均繊維径が7〜16μmの超極細のポリウレタンフィラメントよりなるポリウレタン繊維を用いてメルトブロー法により調製した秤量が75g/m 2の不織布(商品名:エスパシオーネ(F13X-75/120):カネボウ株式会社製)を用いた。 Average fiber diameter weighed prepared by melt-blown method using a polyurethane fiber comprising a polyurethane filament of ultra-fine of 7~16μm of 75 g / m 2 nonwoven fabric (trade name: Espacio Rondane (F13X-75/120): Kanebo Ltd. Etsu Chemical Co., Ltd.) was used.
b)粘着剤: b) a pressure-sensitive adhesive:
ジエチルヘキシルアクリレート90部及びアクリル酸10部からなる単量体混合物を不活性ガス雰囲気下で酢酸エチルのようの共重合することにより、アクリル系粘着剤溶液を得た。 By copolymerization as ethyl acetate 90 parts of di-ethylhexyl acrylate and a monomer mixture consisting of 10 parts of acrylic acid in an inert gas atmosphere to obtain an acrylic pressure-sensitive adhesive solution. このとき粘着剤溶液は53pa/sであった。 In this case the pressure-sensitive adhesive solution was 53 Pa / s.
c)パッド部: c) pad section:
レーヨン、ポリエステル、ポリオレフィンよりなる不織布に非固着性ポリエチレンネットを積層し、厚さが400μ、坪量85g/m 2で吸水性12g/100cm 2のパッド部を用いた。 Rayon, polyester, non-sticking property polyethylene net nonwoven fabric made of polyolefin laminated thickness was used 400 [mu], basis weight 85 g / m 2 the pad portion of the absorbent 12 g / 100 cm 2.

2)救急絆創膏の製造 上記粘着剤溶液をシリコーン処理が施された剥離紙の処理面に乾燥後の糊の厚さが50μmになるように塗布した。 2) The thickness of the adhesive after drying manufacturing the pressure-sensitive adhesive solution adhesive bandage on the treated surface of the release paper silicone treatment is performed is applied so that the 50 [mu] m.
この粘着剤を塗布した剥離紙に、上記基材を貼り合わせた。 A release paper coated with this adhesive, bonding the said substrate. 該貼り合わせた基材と剥離紙の上に、パッド部の幅20mmに相応する位置に、ピッチが2mm間隔で、粘着剤の未塗布部分の幅が1mmの直線状のすじが8本施されるように櫛状の刃をあて、連続すじ状の粘着剤非塗布部分を設け、粘着シートを得た(図2)。 On the release paper and the bonded substrate at a position corresponding to the width 20mm of the pad portion, the pitch is at 2mm intervals, the width of the uncoated portions of the adhesive is applied 1mm linear streaks of this 8 applying a comb-like blade so that, provided the continuous stripe-like adhesive uncoated portion, to obtain a pressure-sensitive adhesive sheet (Figure 2).
次に、該粘着シートから剥離紙を剥がし、上記で得られた連続すじ状の粘着剤非塗布部を設けた部分に、20mm×13mmのパッド部を図2のように積層した。 Then, removing the release paper from the pressure-sensitive adhesive sheet, the portion provided with the non-coated portion continuous streak-like adhesive obtained above was laminated pad of 20 mm × 13 mm as shown in FIG. その後、図1のように剥離ライナーを貼り合わせ、図4の形状に打ち抜き加工し、19mm幅×72mm長さの救急絆創膏を得た。 Thereafter, bonding a release liner as shown in Figure 1, and stamped into the shape of FIG. 4, to obtain a first-aid adhesive tape of 19mm width × 72 mm in length.

(実施例2) (Example 2)
a)基材としてスパンディクス伸縮織物(素材ポリエステル、綿との混紡)を使用し、b)粘着剤として天然ゴム、エチレンブタジエンゴム、テルペン樹脂、液状イソプレン系であるトルエン溶液43%よりなる60pa/s粘度の粘着剤を使用した他は実施例1と同様にした。 a) Supandikusu stretch fabric (Polyester as the base material, using a blend of cotton), b) a natural rubber as an adhesive, ethylene butadiene rubber, terpene resin, consisting of 43% toluene solution is a liquid isoprene 60 Pa / other using an adhesive of s viscosity in the same manner as in example 1.
ピッチが4mm間隔で、連続すじ状の粘着剤非塗布部分が1mmの直線すじが6本施されるようにし、その他は実施例1と同様にして図4に示す救急絆創膏を得た。 Pitch at 4mm intervals, continuous streak adhesive uncoated portion as linear streaks 1mm is performed six, others give the bandage shown in FIG. 4 in the same manner as in Example 1.

(比較例1) (Comparative Example 1)
基材に、素材がポリエステルからなるスパンレース非伸縮不織布(ソンタラ#8010 坪量44g/m 2 :東レ、デュポン(株)製)を用い、実施例1と同じ粘着剤を全面に塗布し、図4に示す救急絆創膏を得た。 The substrate, spun lace non-stretchable nonwoven fabric material made of polyester: using (Sontara # 8010 basis weight 44 g / m 2 Toray Du Pont Co., Ltd.), was applied the same adhesive as in Example 1 on the entire surface, Fig. to obtain a first-aid adhesive tape shown in 4.

(比較例2) (Comparative Example 2)
粘着剤を全面に塗布したほかは、実施例1と同じ粘着剤と基材を用いて同様に図4に示す救急絆創膏を得た。 Besides the application of the adhesive to the entire surface to obtain a bandage shown in Figure 4 in a similar manner using the same adhesive and the substrate as in Example 1.

(比較例3) (Comparative Example 3)
粘着シート全体に実施例1と同様の粘着剤の塗布パターン、即ちピッチが2mm間隔で、連続すじ状の粘着剤非塗布部分が1mmの直線すじであるほかは、実施例1と同じ粘着剤と基材を用いて同様に図4に示す救急絆創膏を得た。 Application pattern similar adhesive as in Example 1 throughout the adhesive sheet, i.e. pitch at 2mm intervals, addition continuous streak adhesive uncoated portion is a linear stripe of 1mm has a same adhesive as in Example 1 to obtain a bandage shown in FIG. 4 similarly using the substrate.

(実験例1) 物性の比較 各実施例及び各比較例に従って製造して得られた救急絆創膏を試料とし、その物性試験を次のように行った。 (Experimental Example 1) The bandage obtained compared prepared according Examples and Comparative Examples of the physical properties and samples were the physical testing as follows. その結果を表1に示した。 The results are shown in Table 1.
A)厚さ:1/1000mmの精度の5mm幅粒子径のダイヤルゲージ使用した。 A) Thickness: Using a dial gauge accuracy 5mm width particle size of 1/1000 mm.
B)粘着力:JIS20237に従い温度23℃相対湿度65%の条件下で測定した。 B) adhesion was measured under the conditions of temperature 23 ° C. and 65% relative humidity in accordance with JIS20237. ただし被着体はベークライト板状体にし、各救急絆創膏の長辺方向に測定した。 However adherend to Bakelite plate-like body was measured in the longitudinal direction of the bandage.
C)自背面接着力:ベークライト板状に各実施例及び各比較例の救急絆創膏を貼付け、該背面に各救急絆創膏を貼付け JIS20237に準じて測定した。 C) own back side adhesion: Paste the aid adhesive tape of the examples and comparative examples to Bakelite plate was measured according to the first-aid adhesive tape to sticking JIS20237 on the back surface.
D)引張強度及び伸び:各救急絆創膏を長辺方向に幅19mm×長さ150mmに切り取り、100mmの標線を入れたものを各試料とした。 D) Tensile strength and elongation: Cut each emergency width bandage to long side 19 mm × length 150 mm, those put marked lines 100mm and with each sample. この試料を引張速度300mm/minで引張り、破断時の引っ張り応力を引張り強度とし、またそのときの伸び量の比率を伸びとした。 The sample pulled at a tensile speed of 300 mm / min, the tensile stress as the tensile strength at break, also was extended the ratio of the amount of elongation at that time.
F)伸張回復率:各救急絆創膏を長辺方向に幅19mm×長さ150mmに切り取り、100mmの標線を入れたものを各試料とした。 F) extension recovery rate: Cut each emergency width bandage to long side 19 mm × length 150 mm, those put marked lines 100mm and with each sample. 150(a)mmになるまで引張った後、緩和させ、直ちに標線の間隔(b)を測定した。 After pulling until 0.99 (a) mm, to relax, and immediately measuring the interval marked line (b).
伸張回収率=150-b/50×100(%)で表した。 Expressed in elongation recovery rate = 150-b / 50 × 100 (%).

(実験例2)実用貼付試験 ボランティア被験者20名に、各実施例及び各比較例の救急絆創膏を左右の人差し指と中指及び薬指の第2関節部にラップして貼付し、次の評価基準に従い評価した。 In Experimental Example 2 Practical application test volunteers 20 persons, affixed to wrap the aid adhesive tape of the examples and comparative examples in the second joint of the left and right index and middle fingers and ring fingers, evaluated according to the following evaluation criteria did. その結果を表2に示した。 The results are shown in Table 2.

(皮膚接着性) (Skin adhesive)
a)テープ全体に剥がれなく接触しているb)一部に剥がれありc)1/3以上剥がれありd)剥がれた a) b in contact without peeling the entire tape) Yes peeling part c) 1/3 Yes peeling or d) exfoliated

(ラップ接着性) (Lap adhesion)
a)ラップ部全体に剥がれなしb)ラップ部一部に剥がれありc)ラップ部1/3以上剥がれありd)ラップ部全体が剥がれた a) Nashi peeling the entire wrap portion b) Yes peeling lap portion Yes peeling in a part c) wrap portion 1/3 or more d) total wrap portion is peeled off

(パッド部分での皮膚のふやけ(白化現象)) (Maceration of the skin of a pad portion (whitening))
a)ふやけなしb)かすかにふやけありc)明らかにふやけあり a) sodden Nashi b) Yes faintly soggy c) clearly soggy Yes

実施例1に準じて作成した救急絆創膏は、表2の実用性評価で示すように吸収パッドである当て材部分での白化現象が殆どみられなかった(95%)。 Bandage was prepared in accordance with Example 1, the whitening phenomenon in abutting material portion is absorbent pad as shown by practical evaluation in Table 2 were hardly observed (95%). これに対し、比較例2で作成したものは、接着剤が全面にべた塗りしたほかは実施例1と同様の救急絆創膏であるが、実用性評価では約50%以上で白化現象が認められた。 In contrast, those prepared in Comparative Example 2, but in addition the adhesive has solid fill on the entire surface has the same adhesive bandage as in Example 1, whitening at about 50% or more by practicality evaluation were observed . これは、パッド部の接着剤が全面塗りのため、一旦パッド部に水が吸収した後、吸収した水の逃げ道がなく貯留することにより皮膚への白化が促進されたと考えられる。 This is because the adhesive of the pad portion of the entire surface coating, after once absorbed water in the pad portion, whitening of the skin is considered to have been facilitated by the reservoir without escape of the absorbed water.

また、実施例2の救急絆創膏は、表2の実用貼付結果のように当て材部分ではややわずかな白化現象がみられるものの、有効であると考えられた。 Also, first-aid adhesive tape of Example 2, although somewhat slight whitening is observed in the hit material portion as practical sticking results in Table 2, were considered to be effective. これら実施例1及び2は、いずれも伸縮性ある伸張回復性のある合成繊維からなるものであり、比較例1の非伸縮性のポリエステル合成繊維基材は、基材を除いて実施例と同一構成の救急絆創膏基材であるが、パッド部分での約50%以上が白化現象が認められた。 These Examples 1 and 2, which both consist of stretch is stretch recovery properties of certain synthetic fibers, non-stretchable polyester synthetic fiber substrate of Comparative Example 1 are the same as in Example except substrate a first-aid adhesive tape base material of the structure, but more than about 50% of the pad portion was observed bleaching. このことから、基材に伸縮性と伸張回復性があることが、白化現象の軽減化に有効であることが見出された。 Therefore, it is stretchable and extension recovery properties to the substrate, has been found to be effective in reducing of the whitening phenomenon.

以上説明したように、本発明の皮膚貼付材は、粘着剤非塗布部分を有するため、当該部分が通気孔及び/又は排水路の役割を果たし、水が入りがたく比較的出やすくなる。 As described above, the skin patch of the present invention has a pressure-sensitive adhesive non-coated portion, this portion serves as a vent and / or drainage, water tends out relatively Gataku entered. さらに、次の効果を有するため、非常に実用的である。 Furthermore, since it has the following advantages, it is very practical.
1. 1. 所定の伸縮回復率であるため、皮膚にしっかり粘着され、使用中に緩むことなく固定性能を有し、特に吸収パッド部分(当て材部分)の皮膚の白化現象は著しく抑えられ、ムレに起因する皮膚刺激性を抑制でき、常に快適な環境を維持できる。 For a given stretch recovery ratio, it is firmly adhered to the skin, has a fixed performance without loosening during use, in particular bleaching of the skin of the absorbent pad portion (against material portion) is suppressed significantly, due to stuffiness it is possible to suppress the skin irritation, you can always maintain a comfortable environment.
2. 2. 更にこの皮膚貼付材は、合成繊維を主としているので、非侵水、撥水性を有しており、施部を確実に保護することができる。 Furthermore this adhesive skin patch, since there synthetic fibers primarily non 侵水 has water repellency, it is possible to reliably protect the 施部.

本発明の皮膚貼付材の断面図である。 It is a cross-sectional view of the skin patch of the present invention. (実施例1,2) (Examples 1 and 2) 本発明の皮膚貼付材用粘着シートを示す図である。 It is a diagram showing a pressure-sensitive adhesive sheet for skin patch of the present invention. 粘着剤非塗布部分は直線状である。 Uncoated portions adhesive is linear. (実施例1,2) (Examples 1 and 2) 本発明の皮膚貼付材用粘着シートを示す図である。 It is a diagram showing a pressure-sensitive adhesive sheet for skin patch of the present invention. 粘着剤非塗布部分はウェイブ状である。 Uncoated portions adhesive is wave-shaped. 救急絆創膏を示す図である。 It is a diagram showing a first-aid adhesive tape. (実施例1,2、比較例1〜3) (Examples 1 and 2, Comparative Examples 1 to 3)

符号の説明 DESCRIPTION OF SYMBOLS

1 基材2 粘着剤3 当て材(パッド部) 1 substrate 2 adhesive 3 against material (pad portion)
4 剥離ライナー5 粘着剤非塗布部分6 ピッチ幅(粘着剤非塗布部分と粘着剤非塗布部分の間隔) 4 release liner 5 pressure-sensitive adhesive non-coated portion 6 pitch width (distance between the adhesive uncoated portion adhesive non-application portion)

Claims (2)

  1. 伸縮性を有する基材、粘着層及びパット部を含む絆創膏又は粘着ドレッシングにおいて、該パッド部に相応する位置のみに粘着剤の非塗布部分が連続すじ状に設けられていることを特徴とする絆創膏又は粘着ドレッシング。 Substrate having stretchability, the plaster or adhesive dressing comprising an adhesive layer and a pad portion, wherein the uncoated portions of the adhesive only in a position corresponding to the pad portion is provided in a continuous striped bandage or adhesive dressing.
  2. 絆創膏又は粘着ドレッシングが長辺と短辺を有する形状からなり、該絆創膏又は粘着ドレッシングが少なくとも長辺方向に伸縮し、粘着剤の非塗布部分が該長辺方向に対して垂直方向に設けられている請求項1に記載の絆創膏又は粘着ドレッシング。 Bandage or adhesive dressing is a shape having a long side and a short side, the bandage or adhesive dressing is stretchable in at least the long side direction, uncoated portions of the adhesive provided in the direction perpendicular to the long side direction bandage or adhesive dressing of claim 1 are.
JP2004339822A 2004-11-25 2004-11-25 Bandage or adhesive dressing Active JP4492868B2 (en)