JP4025454B2 - Cosmetics raw materials, cosmetics, and cosmetics manufacturing method - Google Patents

Cosmetics raw materials, cosmetics, and cosmetics manufacturing method Download PDF

Info

Publication number
JP4025454B2
JP4025454B2 JP07676799A JP7676799A JP4025454B2 JP 4025454 B2 JP4025454 B2 JP 4025454B2 JP 07676799 A JP07676799 A JP 07676799A JP 7676799 A JP7676799 A JP 7676799A JP 4025454 B2 JP4025454 B2 JP 4025454B2
Authority
JP
Japan
Prior art keywords
oil
silicone
weight
cosmetic
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP07676799A
Other languages
Japanese (ja)
Other versions
JP2000281523A (en
Inventor
和男 小林
勝 尾崎
好次 森田
隆司 橘
禎 濱地
Original Assignee
東レ・ダウコーニング株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to JP19250798 priority Critical
Priority to JP1627799 priority
Priority to JP11-16447 priority
Priority to JP1644799 priority
Priority to JP11-16277 priority
Priority to JP10-192507 priority
Priority to JP07676799A priority patent/JP4025454B2/en
Application filed by 東レ・ダウコーニング株式会社 filed Critical 東レ・ダウコーニング株式会社
Publication of JP2000281523A publication Critical patent/JP2000281523A/en
Application granted granted Critical
Publication of JP4025454B2 publication Critical patent/JP4025454B2/en
Anticipated expiration legal-status Critical
Application status is Expired - Lifetime legal-status Critical

Description

【0001】 [0001]
【発明の属する技術分野】 BACKGROUND OF THE INVENTION
本発明は、化粧品原料、化粧品、および化粧品の製造方法に関し、詳しくは、化粧品中にシリコーンオイルまたは有機オイルと架橋シリコーン粒子を均一に分散させることができる化粧品原料、この化粧品原料と他の化粧品原料とからなり、シリコーンオイルまたは有機オイルと架橋シリコーン粒子を均一に分散し、指や肌への感触、伸び、および使用感が良好であり、また、ハネ毛や浮き毛、もつれやからまりを防止し、髪をまとまり易くできるとともに、べたつきのないさらさら感を付与できる化粧品、およびこのような化粧品を効率よく製造する方法に関する。 The present invention, cosmetic ingredients, cosmetics, and to a method for producing a cosmetic, details, cosmetic raw material that can be in cosmetics uniformly disperse the crosslinked silicone particles and the silicone oil or organic oil, the cosmetic raw material and other cosmetic raw materials consists of a, a cross-linked silicone particles and silicone oil or organic oil dispersed uniformly, feel to the fingers and skin, elongation, and feeling is good and also prevent Mari wings hairs or floating hair, tangled Ya from and, it is possible to easily grouped hair, stickiness-free smooth cosmetics sensitive can impart, and such cosmetic relates to a method for efficiently producing.
【0002】 [0002]
【従来の技術】 BACKGROUND OF THE INVENTION
化粧品の皮膚への感触や滑り性を向上させたり、毛髪化粧品の使用感や滑り性を向上させるための化粧品原料として、シリコーンオイル、有機オイル、あるいは架橋シリコーン粒子を配合することは周知であり、シリコーンオイルまたは有機オイルと架橋シリコーン粒子とを併用して配合することも周知である。 Or to improve the feel and slipperiness of the cosmetic to the skin, as a cosmetic raw material for improving the usability and slipperiness of the hair cosmetics, blending silicone oils, organic oils, or crosslinked silicone particles are well known, it is also known to formulate in combination with silicone oil or organic oil and crosslinked silicone particles. シリコーンオイルと架橋シリコーン粒子を含有する化粧品としては、三次元網状構造を有する架橋シリコーン粒子と高粘度あるいは低粘度のシリコーンオイルを含有する化粧品(特開平1−165509号公報、および特開平1−190757号公報参照)、ヒドロシリル化架橋反応性シリコーン組成物の架橋物と低粘度シリコーンオイル含有する化粧品(特開平1−207354号公報参照)、シリコーン架橋物、低粘度シリコーンオイル、ポリオキシアルキレン変成シリコーン系界面活性剤、および水からなるシリコーンオイルエマルジョンを含有する化粧品(特開平3−79669号公報参照)、低粘度シリコーンオイルと常温で固形状のシリコーンとのシリコーンオイルエマルジョンを含有する下地化粧料(特開平3−271211号公報参照 The cosmetics containing the silicone oil and crosslinked silicone particles, containing a silicone oil of high viscosity or low viscosity and crosslinked silicone particles having a three-dimensional network structure cosmetic (JP-A-1-165509 and JP and Hei 1-190757 No. see Japanese), crosslinked product of a hydrosilylation crosslinkable silicone composition and a low viscosity silicone oil-containing makeup product (see Japanese Patent Laid-Open No. 1-207354), silicone crosslinked product, a low viscosity silicone oil, polyoxyalkylene-modified silicone surfactants, and cosmetics containing the silicone oil emulsion consisting of water (see Japanese Patent Laid-Open No. 3-79669), base cosmetic containing a silicone oil emulsion and solid silicone with low viscosity silicone oil and room temperature (JP No. 3-271211 see JP )、シリコーンゴムとシリコーンオイルを含有する皮膚クレンジング剤(特表平6−502646号公報参照)、高分子量シリコーンとシリコーンゴムからなる化粧品(特開平7−330537号公報参照)が知られている。 ), Skin cleansing agents containing silicone rubber and silicone oil (see JP Hei 6-502646), a high molecular weight silicone and cosmetics made of silicone rubber (see JP-A-7-330537) are known.
【0003】 [0003]
また、シリコーンオイルと架橋シリコーン粒子を含有する毛髪化粧料としては、特開平2−172906号公報、特開平5−139932号公報、および特開平10−36228号公報が提案されており、特に、シリコーンオイルを含有する架橋シリコーン粒子を含有する毛髪化粧料としては、特開平2−243612号公報、および特開平5−262987号公報が提案されている。 As the hair cosmetic containing a silicone oil and crosslinked silicone particles, JP-A-2-172906, JP-A No. 5-139932 and JP and Hei 10-36228 discloses has been proposed, in particular, silicone the hair cosmetic composition containing crosslinked silicone particles containing oil, JP 2-243612 and JP and Hei 5-262987 Patent Publication has been proposed.
【0004】 [0004]
さらに、有機オイルと架橋シリコーン粒子を含有する化粧品としては、特開昭61−194009号公報、特開昭63−313710号公報、特開平7−258027号公報、および特開平7−267820号公報が提案されている。 Further, as the cosmetics containing an organic oil and crosslinked silicone particles, JP 61-194009, JP-Sho 63-313710, JP-A No. 7-258027 and JP and Hei 7-267820 Patent Publication No. Proposed.
【0005】 [0005]
しかし、これらの化粧品は、化粧品原料としてシリコーンオイルまたは有機オイルと架橋シリコーン粒子をその他の化粧品原料と配合するため、架橋シリコーン粒子が化粧品中に十分に分散されず、また、シリコーンオイルまたは有機オイルと架橋シリコーン粒子のなじみも悪く、本来の特性をいかんなく発揮できないという問題があった。 However, these cosmetics, for formulating the silicone oils or organic oils and crosslinked silicone particles and other cosmetic raw material as a cosmetic material and is not sufficiently dispersed in the crosslinked silicone particles cosmetics, also a silicone oil or organic oil familiar of crosslinked silicone particles or worse, there is a problem that can not exhibit the inherent characteristics Ikan'naku. 特に、水系の化粧品においては、シリコーンオイルまたは有機オイルと架橋シリコーン粒子をその他の化粧品原料に分散させる際に、十分なせん断力をかけることができないため、化粧品の安定性が十分でなかったり、化粧品の使用感が悪かったりするという問題があった。 In particular, in a water-based cosmetics, in dispersing the crosslinked silicone particles and the silicone oil or organic oil other cosmetic raw materials, it is not possible to apply a sufficient shearing force, or not the stability of the cosmetics is insufficient, Cosmetics there has been a problem that the use feeling or bad.
【0006】 [0006]
また、化粧品原料として、シリコーンオイルまたは有機オイルと架橋シリコーン粒子を配合してなる毛髪化粧品においては、架橋シリコーン粒子が毛髪化粧品中に十分に分散されず、また、シリコーンオイルまたは有機オイルと架橋シリコーン粒子のなじみも悪く、本来の特性をいかんなく発揮できないという問題があった。 Further, as a cosmetic raw material, in the hair cosmetic article obtained by blending a cross-linked silicone particles and silicone oil or organic oil is not sufficiently dispersed in the crosslinked silicone particles in hair cosmetics, also silicone oils or organic oils and crosslinked silicone particles also familiar worse, there is a problem that can not exhibit the inherent characteristics Ikan'naku. 特に、水系の毛髪化粧品においては、シリコーンオイルまたは有機オイルと架橋シリコーン粒子をその他の毛髪化粧品原料に分散させる際に、十分なせん断力をかけることができないため、毛髪化粧品の安定性が十分でなかったり、毛髪化粧品の使用感が悪かったりするという問題があった。 In particular, in a water based hair cosmetics, in dispersing the crosslinked silicone particles and the silicone oil or organic oil other hair cosmetic raw materials, it is not possible to apply a sufficient shearing force, the stability of the hair cosmetics is poorly or, there is a problem that or poor feeling of hair cosmetics.
【0007】 [0007]
【発明が解決しようとする課題】 [Problems that the Invention is to Solve
本発明者らは、上記の課題について鋭意検討した結果、本発明に到達した。 The present inventors have made extensive studies on the above problems, and have reached the present invention.
すなわち、本発明の目的は、化粧品中にシリコーンオイルまたは有機オイルと架橋シリコーン粒子を均一に分散させることができる化粧品原料、この化粧品原料と他の化粧品原料とからなり、シリコーンオイルまたは有機オイルと架橋シリコーン粒子を均一に分散し、指や肌への感触、伸び、および使用感が良好であり、また、ハネ毛や浮き毛、もつれやからまりを防止し、髪をまとまり易くできるとともに、べたつきのないさらさら感を付与できる化粧品、およびこのような化粧品を効率よく製造する方法を提供することにある。 An object of the present invention, the cosmetic raw material can be uniformly dispersed crosslinked silicone particles and the silicone oil or organic oil in cosmetics consists this cosmetic raw material and other cosmetic raw materials, crosslinked silicone oil or organic oil the silicone particles were uniformly dispersed, the feel of the fingers and skin, stretch, and a feeling of use is good, also wings hairs and lifting hair to prevent tangling Ya from Mari, it is possible to easily grouped hair, stickiness no intention cosmetics sensitive can impart, and such cosmetics to provide a method for efficiently manufacturing.
【0008】 [0008]
【課題を解決するための手段】 In order to solve the problems]
本発明の化粧品原料は、 非架橋性のシリコーンオイルまたは有機オイルを含有している架橋性シリコーン組成物 ( 但し、非架橋性のシリコーンオイルまたは有機オイルの含有量は、架橋性シリコーン組成物の架橋物がこの非架橋性のシリコーンオイルまたは有機オイルを保持し得る量をこえる量である。 ) を水中に分散させて架橋反応してなる、水中に分散している平均粒径0.1〜500μmのシリコーンオイルまたは有機オイルの液滴中に、平均粒径0.05〜100μmの球状の架橋シリコーン粒子(但し、架橋シリコーン粒子の粒径はシリコーンオイルまたは有機オイルの液滴の粒径より小さい。)を含有しているシリコーンオイルまたは有機オイルのエマルジョンからなることを特徴とする。 Cosmetic raw material of the present invention, the content of non-crosslinkable silicone oil or crosslinkable silicone composition containing an organic oil (provided that non-crosslinkable silicone oil or organic oil, crosslinking of the crosslinkable silicone composition object is an amount that exceeds the amount that can hold the non-crosslinkable silicone oil or organic oil.) was the dispersed in water by crosslinking reaction, the average particle size 0.1~500μm dispersed in water the silicone oil or in droplets of the organic oil, an average particle diameter 0.05~100μm spherical crosslinked silicone particles (provided that the particle size of the crosslinked silicone particles is smaller than the particle diameter of droplets of the silicone oil or organic oil. ) characterized by comprising the emulsion of silicone oil or organic oil containing the.
また、本発明の化粧品原料は、上記のエマルジョンから水を除去してなる、シリコーンオイルまたは有機オイル中に球状の架橋シリコーン粒子を分散してなるオイル組成物からなることを特徴とする。 Moreover, the cosmetic raw material of the present invention is obtained by removing water from the emulsion, characterized by comprising the oil composition prepared by dispersing the crosslinked silicone particles spherical in silicone oil or organic oil.
また、本発明の化粧品は、上記のエマルジョンからなる化粧品原料と他の化粧品原料とからなることを特徴とする。 Further, the cosmetic of the present invention is characterized by comprising the cosmetic raw material and other cosmetic raw material consisting of the above emulsion.
また、本発明の化粧品は、上記のオイル組成物からなる化粧品原料と他の化粧品原料とからなることを特徴とする。 Further, the cosmetic of the present invention is characterized by comprising the cosmetic raw material and other cosmetic raw material consisting of the above oil composition.
さらに、本発明の化粧品の製造方法は、上記のエマルジョンからなる化粧品原料と他の化粧品原料を配合することを特徴とする。 Furthermore, the cosmetic manufacturing method of the present invention is characterized by formulating the cosmetic raw material and other cosmetic raw material consisting of the above emulsion.
【0009】 [0009]
【発明の実施の形態】 DETAILED DESCRIPTION OF THE INVENTION
はじめに、本発明の化粧品原料を詳細に説明する。 First, to explain the cosmetic raw material of the present invention will be described in detail.
本発明の化粧品原料は、水中に分散しているシリコーンオイルまたは有機オイルの液滴中に架橋シリコーン粒子を含有しているシリコーンオイルまたは有機オイルのエマルジョンからなることを特徴とする。 Cosmetic raw material of the present invention is characterized in that it consists of an emulsion of silicone oil or organic oil containing the crosslinked silicone particles in the droplets in the silicone oil or organic oil dispersed in water. このエマルジョンにおいて、この架橋シリコーン粒子は架橋性シリコーン組成物を架橋させものであり、架橋性シリコーン組成物を、例えば、ヒドロシリル化架橋反応させたもの、縮合架橋反応させたもの、有機過酸化物架橋反応させたもの、高エネルギー線架橋反応させたものが挙げられ、特には、ヒドロシリル化架橋反応させたもの、あるいは縮合架橋反応させたものであることが好ましい。 In this emulsion, the crosslinked silicone particles are those obtained by crosslinking a crosslinkable silicone composition, a crosslinkable silicone composition, for example, those obtained by hydrosilylation crosslinking reaction, and a condensation crosslinking reaction, an organic peroxide those obtained by cross-linking reaction, and is a high-energy beam crosslinking reaction. in particular, it is preferable obtained by hydrosilylation crosslinking reaction, or is obtained by condensation crosslinking reaction.
【0010】 [0010]
また、このエマルジョンにおいて、シリコーンオイルの種類は限定されないが、直鎖状、一部分岐を有する直鎖状、環状、分岐鎖状等の分子構造を有するものが好ましく、特に、直鎖状、あるいは環状の分子構造を有するものが好ましい。 Further, in the emulsion, but the type of silicone oil is not limited, linear, linear with partial branching, cyclic, those having a molecular structure of branched such preferred, linear, or cyclic preferably it has a molecular structure. このシリコーンオイルとしては、架橋シリコーン粒子を形成する架橋性シリコーン組成物に相溶性のあるものが好ましい。 As the silicone oil, there is preferable compatibility crosslinkable silicone composition to form a crosslinked silicone particles. また、このシリコーンオイルは、架橋シリコーン粒子を形成する際の架橋反応に関与しないものが好ましく、この架橋シリコーン粒子がヒドロシリル化架橋反応したものである場合には、分子中にアルケニル基やケイ素原子結合水素原子を有しない、例えば、分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン、分子鎖両末端トリメチルシロキシ基封鎖メチルフェニルポリシロキサン、分子鎖両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルフェニルシロキサン共重合体、分子鎖両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチル(3,3,3−トリフルオロプロピル)シロキサン共重合体、環状ジメチルシロキサン、環状メチルフェニルシロキサンが挙げられ、また、この架橋シリコーン粒子が縮合架橋 Further, the silicone oil is preferably that does not participate in the crosslinking reaction during the formation of the crosslinked silicone particles, when the crosslinked silicone particles are obtained by hydrosilylation crosslinking reaction, an alkenyl group or silicon-bonded in the molecule having no hydrogen atom, for example, both ends of the molecular chain blocked by trimethylsiloxy groups dimethylpolysiloxane with both molecular chain terminals blocked with trimethylsiloxy groups methylphenyl polysiloxane with both molecular chain terminals blocked with trimethylsiloxy groups dimethylsiloxane-methylphenylsiloxane copolymer both molecular chain terminals blocked with trimethylsiloxy groups dimethylsiloxane-methyl (3,3,3-trifluoropropyl) siloxane copolymers, cyclic dimethylsiloxane, include cyclic methylphenylsiloxane, also the crosslinked silicone particles are condensation-crosslinking 応したものである場合には、分子中にシラノール基やケイ素原子結合水素原子やケイ素原子結合加水分解性基を有しない、前記と同様のシリコーンオイルの他に、例えば、分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルポリシロキサン、分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルシロキサン・メチルビニルシロキサン共重合体、分子鎖両末端トリメチルシロキシ基封鎖メチルビニルポリシロキサン、環状メチルビニルシロキサンが挙げられる。 If is obtained by response has no silanol or silicon-bonded hydrogen atoms or silicon-bonded hydrolyzable groups in the molecule, in addition to the same silicone oil, for example, dimethylpolysiloxane with both molecular chain terminals vinyl siloxy group-blocked dimethylpolysiloxane, both molecular terminals with dimethylvinylsiloxy groups dimethylsiloxane-methylvinylsiloxane copolymer, both ends of the molecular chain blocked by trimethylsiloxy groups methylvinylpolysiloxane, and cyclic methylvinylsiloxane. このようなシリコーンオイルの粘度は、25℃において1〜100,000,000mPa・sの範囲内であることが好ましく、特には、25℃において2〜10,000,000mPa・sの範囲内であることが好ましい。 The viscosity of the silicone oil is preferably in the range of 1~100,000,000mPa · s at 25 ° C., in particular, in the range of from 2~10,000,000mPa · s at 25 ° C. it is preferable.
【0011】 [0011]
また、このエマルジョンにおいて、有機オイルの種類は限定されないが、架橋シリコーン粒子を形成する架橋性シリコーン組成物に相溶性のあるものが好ましい。 Further, in the emulsion, but the type of organic oil is not limited, there is preferable compatibility crosslinkable silicone composition to form a crosslinked silicone particles. この有機オイルは、直鎖状、一部分岐を有する直鎖状、環状、分岐鎖状等の分子構造を有する脂肪族系オイル、あるいは芳香族系オイルであることが好ましく、特には、直鎖状、あるいは環状の分子構造を有する有機オイルであることが好ましい。 The organic oils may be linear, linear with partial branching, cyclic, preferably an aliphatic oil or aromatic oil has a molecular structure of branched like, in particular, linear it is preferred, or an organic oil having a cyclic molecular structure. また、この有機オイルは揮発性を有していてもよい。 Further, organic oils may have a volatility. このような有機オイルは、架橋シリコーン粒子を形成する際の架橋反応に関与しないものが好ましく、この架橋シリコーン粒子がヒドロシリル化架橋反応したものである場合には、分子中にアルケニル基を有しないものであり、例えば、ヘキサン、ヘプタン、パラフィン、イソパラフィン等のアルカン類;トルエン、キシレン等の芳香族類;四塩化炭素、塩化メチレン等の塩素化物;メチルイソブチルケトン等のケトン類;ウンデシルアルコール等のアルコール類;ジブチルエーテル等のエーテル類;イソプロピルラウレート、イソプロピルパルミテート等のエステル類が挙げられ、特に、揮発性を有するアルカン類であることが好ましい。 Such organic oils is preferably that does not participate in the crosslinking reaction during the formation of the crosslinked silicone particles, when the crosslinked silicone particles are obtained by hydrosilylation crosslinking reaction, having no alkenyl group in a molecule , and the example, hexane, heptane, paraffins, alkanes such as isoparaffin; toluene, aromatics such as xylene; carbon tetrachloride, chlorinated, such as methylene chloride, ketones such as methyl isobutyl ketone; such as undecyl alcohol alcohols; ethers such as dibutyl ether; isopropyl laurate, include esters such as isopropyl palmitate and particularly preferably is in alkanes having volatility. このような有機オイルの粘度は、25℃において1〜100,000,000mPa・sの範囲内であることが好ましく、特には、25℃において2〜10,000,000mPa・sの範囲内であることが好ましい。 The viscosity of such an organic oil, preferably in the range of 1~100,000,000mPa · s at 25 ° C., in particular, in the range of from 2~10,000,000mPa · s at 25 ° C. it is preferable.
【0012】 [0012]
また、このようなシリコーンオイルまたは有機オイルはそれぞれを併用してもよく、また、他の成分を溶解していてもよく、シリコーンオイルまたは有機オイルが揮発性を有する場合には、得られるシリコーンオイルまたは有機オイルのエマルジョンから水および揮発性のシリコーンオイルまたは有機オイルを除去することにより、架橋シリコーン粒子とシリコーンオイルまたは有機オイルに溶解していた他の成分との混合物、あるいは、他の成分を含有している架橋シリコーン粒子を調製することができる。 Also, such silicone oils or organic oils may be used in combination, respectively, also may be dissolved with the other ingredients, when the silicone oil or organic oil has a volatility, the resulting silicone oil or a mixture of the emulsion of the organic oil by removal of water and volatile silicone oils or organic oils, and other components dissolved in the crosslinked silicone particles and the silicone oil or organic oil, or contain other components to which crosslinked silicone particles can be prepared. このシリコーンオイルまたは有機オイル中に溶解することのできる他の成分としては、シリコーンオイルまたは有機オイルに可溶であるものであれば特に限定されず、例えば、室温で固体状のシリコーンレジン、室温でゴム状のシリコーンオイル等の有機ケイ素化合物;カルナウバロウ、キャンデリラロウ、モクロウ、鯨ロウ、ホホバ油、モンタンロウ、ミツロウ、ラノリン等のロウ類;流動パラフィン、イソパラフィン、ラウリン酸ヘキシル、ミリスチン酸イソプロピル、ミリスチン酸ミリスチル、ミリスチン酸セチル、ミリスチン酸2−オクチルドデシル、パルミチン酸イソプロピル、パルミチン酸2−エチルヘキシル、ステアリン酸ブチル、オレイン酸デシル、オレイン酸2−オクチルドデシル、乳酸ミリスチル、乳酸セチル、酢酸ラ Other ingredients that can be dissolved in the silicone oil or organic oil is not particularly limited as long as it is soluble in the silicone oil or organic oil, for example, solid silicone resin at room temperature, at room temperature organosilicon compounds, such as rubber-like silicone oil; carnauba wax, candelilla wax, Japan wax, spermaceti, jojoba oil, montan wax, beeswax, wax and lanolin; liquid paraffin, isoparaffin, hexyl laurate, isopropyl myristate, myristyl myristyl, cetyl myristate, 2-octyldodecyl myristate, isopropyl palmitate, 2-ethylhexyl palmitate, butyl stearate, decyl oleate, 2-octyldodecyl oleate, myristyl lactate, cetyl lactate, acetate La リン、ステアリルアルコール、セトステアリルアルコール、オレイルアルコール、アボガド油、アーモンド油、オリブ油、カカオ油、ホホバ油、ゴマ油、サフラワー油、大豆油、ツバキ油、スクワラン、パーシック油、ヒマシ油、ミンク油、綿実油、ヤシ油、卵黄油、豚脂等の油脂;ポリプロピレングリコールモノオレート、ネオペンチルグリコール−2−エチルヘキサノエート等のグリコールエステル油;イソステアリン酸トリグリセライド、椰子油脂肪酸トリグリセライド等の多価アルコールエステル油;ポリオキシエチレンラウリルエーテル、ポリオキシプロピレンセチルエーテル等のポリオキシアルキレンエーテル油が挙げられる。 Phosphorus, stearyl alcohol, cetostearyl alcohol, oleyl alcohol, avocado oil, almond oil, olive oil, cacao oil, jojoba oil, sesame oil, safflower oil, soybean oil, camellia oil, squalane, persic oil, castor oil, mink oil, cottonseed oil, coconut oil, egg yolk oil, oil of lard and the like; polypropylene glycol monooleate, glycol ester oil, such as neopentyl glycol 2-ethylhexanoate; isostearic acid triglyceride, polyhydric alcohol ester oils such as coconut oil fatty acid triglyceride ; polyoxyethylene lauryl ether, polyoxyalkylene ether oils such as polyoxypropylene cetyl ether.
【0013】 [0013]
このエマルジョンにおいて、シリコーンオイルまたは有機オイルの液滴の平均粒径は0.1〜500μmの範囲内であることが必要であり、好ましくは、0.2〜500μmの範囲内であり、より好ましくは、0.5〜500μmの範囲内であり、特に好ましくは、0.5〜200μmの範囲内である。 In this emulsion, the average particle diameter of droplets of the silicone oil or organic oil is required to be in the range of 0.1 to 500 [mu] m, preferably in the range of 0.2~500Myuemu, more preferably , in the range of 0.5 to 500, particularly preferably in the range of 0.5 to 200. これは、液滴の平均粒径が上記範囲の下限未満であるエマルジョンを調製することが困難である傾向があり、一方、上記範囲の上限をこえるエマルジョンは、化粧品原料としての安定性が低下する傾向があるからである。 This tends average particle diameter of the droplets is difficult to prepare an emulsion which is below the recommended lower limit, while the emulsion that exceeds the upper limit, the stability of the cosmetic material is reduced This is because there is a trend.
【0014】 [0014]
また、このエマルジョンにおいて、架橋シリコーン粒子の平均粒径は0.05〜100μmの範囲内であることが必要であり、好ましくは、0.1〜100μmの範囲内であり、特に好ましくは、0.1〜50μmの範囲内である。 Further, in the emulsion, the average particle size of the crosslinked silicone particles must lie within the range of 0.05~100Myuemu, preferably in the range of 0.1 to 100 [mu] m, particularly preferably 0. it is within the range of 1~50μm. また、シリコーンオイルまたは有機オイルの液滴の平均粒径が0.2〜500μmの範囲内である場合には、架橋シリコーン粒子の平均粒径は0.1〜100μmの範囲内であることが好ましく、特に、0.1〜50μmの範囲内であることが好ましい。 Further, when the average particle diameter of droplets of the silicone oil or organic oil is in the range of 0.2~500μm preferably has an average particle size of the crosslinked silicone particles is in the range of 0.1~100μm , particularly preferably in the range of 0.1 to 50 [mu] m. また、シリコーンオイルまたは有機オイルの液滴の平均粒径が0.5〜500μmの範囲内である場合には、架橋シリコーン粒子の平均粒径は0.1〜100μmの範囲内であることが好ましく、特に、0.1〜50μmの範囲内であることが好ましい。 Further, when the average particle diameter of droplets of the silicone oil or organic oil is in the range of 0.5~500μm preferably has an average particle size of the crosslinked silicone particles is in the range of 0.1~100μm , particularly preferably in the range of 0.1 to 50 [mu] m. さらに、シリコーンオイルまたは有機オイルの液滴の平均粒径が0.5〜200μmの範囲内である場合には、架橋シリコーン粒子の平均粒径は0.1〜100μmの範囲内であることが好ましく、特に、0.1〜50μmの範囲内であることが好ましい。 Further, when the average particle diameter of droplets of the silicone oil or organic oil is in the range of 0.5~200μm preferably has an average particle size of the crosslinked silicone particles is in the range of 0.1~100μm , particularly preferably in the range of 0.1 to 50 [mu] m. これは、平均粒径が上記範囲の下限未満である架橋シリコーン粒子を調製することが困難である傾向があり、一方、上記範囲の上限をこえる架橋シリコーン粒子は、化粧品原料としてのエマルジョンの安定性を低下させ、また、化粧品原料として他の化粧品原料と配合する際に均一に混合し難かったり、得られる化粧品の感触が不十分であったりするからである。 This tends average particle size is difficult to prepare the crosslinked silicone particles is less than the lower limit of the above range, on the other hand, cross-linked silicone particles exceeding the upper limit of the above range, stability of the emulsion as a cosmetic raw material lowering the, also because or hardly uniformly mixed when blended with other cosmetic raw materials as a cosmetic raw material, the feel of the cosmetic obtained or insufficient.
【0015】 [0015]
このエマルジョンの性状としては、液状、クリーム状、ペースト状が例示される。 The properties of this emulsion, a liquid, creamy, pasty is exemplified. また、このエマルジョンにおいて、架橋シリコーン粒子の粒径はシリコーンオイルまたは有機オイルの液滴の粒径より小さいことは無論である。 Further, in the emulsion, the particle size of the crosslinked silicone particles is smaller than the particle size of droplets of the silicone oil or organic oil is course. この架橋シリコーン粒子の形状は、例えば、球状、紡錘形状、偏平形状、不定形状が挙げられ、好ましくは、球状である。 The shape of the crosslinked silicone particles, for example, spherical, spindle-shaped, flat-shaped, include irregular shape, preferably a spherical shape.
【0016】 [0016]
このようなエマルジョンを調製する方法としては、例えば、非架橋性のシリコーンオイルまたは有機オイルを含有している架橋性シリコーン組成物(但し、非架橋性のシリコーンオイルまたは有機オイルの含有量は、架橋性シリコーン組成物の架橋物がこの非架橋性のシリコーンオイルまたは有機オイルを保持し得る量をこえる量である。)を水中に分散させて架橋反応する方法が好ましい。 As a method for preparing such emulsions, for example, non-crosslinkable silicone oil or crosslinkable silicone composition containing an organic oil (however, the content of the non-crosslinkable silicone oil or organic oil, crosslinking crosslinked product of sex silicone composition is an amount that exceeds the amount that can hold the non-crosslinkable silicone oil or organic oil.) method of crosslinking reaction by dispersing in water are preferred. この方法で用いることのできる架橋性シリコーン組成物は、架橋反応により、ゴム状、ゲル状等のエラストマー状の架橋物を形成するような組成物であることが好ましく、例えば、ヒドロシリル化架橋反応型のもの、縮合架橋反応型のもの、有機過酸化物架橋反応型のもの、高エネルギー線架橋反応型のものが挙げられ、好ましくは、ヒドロシリル化架橋反応型のもの、あるいは縮合架橋反応型のものである。 Crosslinkable silicone compositions which can be used in this method, the crosslinking reaction, rubber-like, is preferably a composition such as to form a elastomeric crosslinked product of gel such as, for example, hydrosilylation crosslinking reaction type ones, those condensation crosslinking reaction type, those of the organic peroxide crosslinking reaction type, that of high-energy radiation crosslinking reaction type and the like, preferably of a hydrosilylation crosslinking reaction type, or that of a condensation crosslinking reaction type it is.
【0017】 [0017]
このヒドロシリル化架橋反応型シリコーン組成物としては、例えば、一分子中に少なくとも2個のアルケニル基を有するオルガノポリシロキサン、一分子中に少なくとも2個のケイ素原子結合水素原子を有するオルガノポリシロキサン、およびヒドロシリル化反応用触媒から少なくともなるものが挙げられる。 As the hydrosilylation crosslinking reaction type silicone composition, for example, an organopolysiloxane having at least 2 alkenyl groups in one molecule, an organopolysiloxane having at least two silicon-bonded hydrogen atoms in each molecule, and It includes those consisting of at least a hydrosilylation reaction catalyst. この方法において、上記のヒドロシリル化反応用触媒を予め配合した架橋性シリコーン組成物を水中に分散させてもよく、また、この触媒を除いた架橋性シリコーン組成物を水中に分散させた後、この触媒を水中に添加することにより、水中でヒドロシリル化反応用触媒を配合した架橋性シリコーン組成物を調製することもできる。 In this method, may be dispersed crosslinkable silicone composition in advance blending the above hydrosilylation reaction catalyst in water, also after dispersing the crosslinkable silicone composition, excluding this catalyst in water, the catalyze by adding to the water, it can also be prepared crosslinkable silicone composition containing a hydrosilylation reaction catalyst in water. この際、ヒドロシリル化反応用触媒を平均粒径1μm以下に分散した水分散液を用いることが好ましい。 In this case, it is preferable to use an aqueous dispersion obtained by dispersing a hydrosilylation reaction catalyst to the average particle size of not more than 1 [mu] m.
【0018】 [0018]
また、縮合架橋反応型シリコーン組成物としては、例えば、一分子中に少なくとも2個のケイ素原子に結合する水酸基またはアルコキシ基、オキシム基、アセトキシ基、アミノキシ基等の加水分解性基を有するオルガノポリシロキサン、一分子中に少なくとも3個のケイ素原子に結合するアルコキシ基、オキシム基、アセトキシ基、アミノキシ基等の加水分解性基を有するシラン系架橋剤、および有機錫化合物、有機チタン化合物等の縮合反応用触媒から少なくともなるものが挙げられる。 As the condensation crosslinking reaction type silicone composition, for example, Oruganopori having at least two hydroxyl groups or alkoxy groups bonded to the silicon atom, an oxime group, acetoxy group, hydrolyzable group such as an aminoxy groups per molecule siloxane, alkoxy groups bonded to at least three silicon atoms in one molecule, oxime group, acetoxy group, a silane crosslinking agent having hydrolyzable groups such as aminoxy groups, and an organic tin compound, the condensation of an organic titanium compound It includes those consisting of at least reaction catalyst.
【0019】 [0019]
また、上記の架橋性シリコーン組成物には、その流動性を調節したり、得られる架橋シリコーン粒子の機械強度を向上させるための任意の成分として充填剤を配合してもよい。 Further, in the above-described crosslinkable silicone composition, the or adjust the fluidity may be blended a filler as an optional component for is to improve the mechanical strength of the crosslinked silicone particles obtained. この充填剤としては、沈澱シリカ、フュームドシリカ、焼成シリカ、フュームド酸化チタン等の補強充填剤;粉砕石英、ケイ藻土、アルミノケイ酸、酸化鉄、酸化亜鉛、炭酸カルシウム等の非補強充填剤、これらの表面をヘキサメチルシラザン、トリメチルクロルシラン、ポリジメチルシロキサン、ポリメチルハイドロジェンシロキサン等の有機ケイ素化合物により処理してなる充填剤が例示される。 As the filler, precipitated silica, fumed silica, calcined silica, reinforcing fillers such as fumed titanium oxide, ground quartz, diatomaceous earth, aluminosilicates, iron oxide, zinc oxide, non-reinforcing fillers such as calcium carbonate, these surfaces hexamethyldisilazane, trimethylchlorosilane, polydimethylsiloxane, fillers obtained by treating with an organosilicon compound such as polymethyl hydrogen siloxane can be exemplified.
【0020】 [0020]
この架橋性シリコーン組成物中に含有される非架橋性のシリコーンオイルは、この組成物の架橋反応に関与しないものであり、直鎖状、一部分岐を有する直鎖状、環状、分岐鎖状等の分子構造を有するものが好ましく、特には、直鎖状、あるいは環状の分子構造を有するものが好ましい。 Non-crosslinkable silicone oil contained in the crosslinkable silicone composition, which does not participate in the crosslinking reaction of the composition, linear, linear with partial branching, cyclic, branched, etc. preferably those having a molecular structure, in particular, linear or having a cyclic molecular structure is preferred. このシリコーンオイルとしては、この架橋性シリコーン組成物に相溶性のあるものが好ましい。 As the silicone oil, which is compatible to the crosslinkable silicone composition. この非架橋性シリコーンオイルは、この組成物がヒドロシリル化架橋反応型のものである場合には、分子中にアルケニル基やケイ素原子結合水素原子を有しない、例えば、分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン、分子鎖両末端トリメチルシロキシ基封鎖メチルフェニルポリシロキサン、分子鎖両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルフェニルシロキサン共重合体、分子鎖両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチル(3,3,3−トリフルオロプロピル)シロキサン共重合体、環状ジメチルシロキサン、環状メチルフェニルシロキサン、グリシドキシプロピル変性ポリオルガノシロキサンが挙げられ、また、この組成物が縮合架橋反応型のものである場合には、分子中にシラノ The non-crosslinkable silicone oil, when the composition is of the hydrosilation crosslinking reaction type has no alkenyl group or silicon-bonded hydrogen atoms in the molecule, for example, both ends of the molecular chain blocked by trimethylsiloxy groups dimethylpolysiloxane with both molecular chain terminals blocked with trimethylsiloxy groups methylphenyl polysiloxane with both molecular chain terminals blocked with trimethylsiloxy groups dimethylsiloxane-methylphenylsiloxane copolymers, both molecular terminals with trimethylsiloxy groups dimethylsiloxane-methyl (3, 3,3-trifluoropropyl) siloxane copolymers, cyclic dimethylsiloxane, cyclic methylphenylsiloxane, include glycidoxypropyl modified polyorganosiloxane, and when this composition is of the condensation crosslinking reaction type It is, Cyrano in the molecule ル基やケイ素原子結合水素原子やケイ素原子結合加水分解性基を有しない、前記と同様のシリコーンオイルの他に、例えば、分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルポリシロキサン、分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルシロキサン・メチルビニルシロキサン共重合体、分子鎖両末端トリメチルシロキシ基封鎖メチルビニルポリシロキサン、環状メチルビニルシロキサンである。 No Le group or silicon-bonded hydrogen atoms or silicon-bonded hydrolyzable group, in addition to the same silicone oil, for example, dimethylpolysiloxane with both molecular chain terminals blocked with dimethylvinylsiloxy groups, dimethylpolysiloxane with both molecular chain terminals vinylsiloxy group dimethylsiloxane-methylvinylsiloxane copolymer, both ends of the molecular chain blocked by trimethylsiloxy groups methylvinylpolysiloxane is a cyclic methylvinylsiloxane. さらに、エチレンオキシドやプロピレンオキシドなどで変性されたポリエーテル変性ポリオルガノシロキサンやヘキシルやドデシルを含有したアルキル変性ポリオルガノシロキサンが例示される。 Moreover, alkyl-modified polyorganosiloxanes containing modified polyether modified polyorganosiloxane and hexyl or dodecyl, etc. ethylene oxide and propylene oxide are exemplified. このような非架橋性シリコーンオイルの粘度は、25℃において1〜100,000,000mPa・sの範囲内であることが好ましく、特には、25℃において2〜10,000,000mPa・sの範囲内であることが好ましい。 The viscosity of such a non-crosslinkable silicone oil is preferably in the range of 1~100,000,000mPa · s at 25 ° C., in particular in the range of 2~10,000,000mPa · s at 25 ° C. it is preferable that an internal.
【0021】 [0021]
また、この架橋性シリコーン組成物中に含有される非架橋性の有機オイルは、この組成物の架橋反応に関与しないものであり、この架橋シリコーン粒子がヒドロシリル化架橋反応したものである場合には、分子中にアルケニル基を有しないものである。 Further, non-crosslinkable organic oil contained in the crosslinkable silicone composition, which does not participate in the crosslinking reaction of the composition, when the crosslinked silicone particles are obtained by hydrosilylation crosslinking reaction those that do not have alkenyl groups in the molecule. また、この有機オイルは、この架橋性シリコーン組成物に相溶性のあるものが好ましい。 Further, organic oil, which is compatible to the crosslinkable silicone composition. このような非架橋性の有機オイルとしては、例えば、ヘキサン、ヘプタン、パラフィン、イソパラフィン等のアルカン類;トルエン、キシレン等の芳香族類;四塩化炭素、塩化メチレン等の塩素化物類;メチルイソブチルケトン等のケトン類;ウンデシルアルコール等のアルコール類;ジブチルエーテル等のエーテル類;イソプロピルラウレート、イソプロピルパルミテート等のエステル類が挙げられ、特に、揮発性を有するアルカン類であることが好ましい。 Such non-crosslinking organic oils, such as hexane, heptane, paraffins, alkanes such as isoparaffin; toluene, aromatics such as xylene; carbon tetrachloride, chlorinated compounds such as methylene chloride; methyl isobutyl ketone etc. ketones; alcohols such as undecyl alcohol; ethers such as dibutyl ether; isopropyl laurate, include esters such as isopropyl palmitate and particularly preferably is in alkanes having volatility. このような非架橋性有機オイルの粘度は、25℃において1〜100,000,000mPa・sの範囲内であることが好ましく、特には、25℃において2〜10,000,000mPa・sの範囲内であることが好ましい。 The viscosity of such a non-crosslinkable organic oil, preferably in the range of 1~100,000,000mPa · s at 25 ° C., in particular in the range of 2~10,000,000mPa · s at 25 ° C. it is preferable that an internal.
【0022】 [0022]
上記の架橋性シリコーン組成物中の非架橋性のシリコーンオイルまたは有機オイルの含有量は、この架橋性シリコーン組成物の架橋物が、その架橋物中に非架橋性のシリコーンオイルまたは有機オイルを保持することができる量、すなわち、その架橋物が含有できる非架橋性のシリコーンオイルまたは有機オイルの量をこえる量であることが必要である。 The content of the non-crosslinkable silicone oil or organic oil in the crosslinkable silicone composition, the crosslinked product of this crosslinkable silicone composition, held the non-crosslinkable silicone oil or organic oil in the crosslinked product the amount which can be, i.e., it is necessary that the crosslinked product is an amount that exceeds the amount of non-crosslinkable silicone oil or organic oil that can be contained. この保持し得る量は、架橋性シリコーン組成物と非架橋性のシリコーンオイルまたは有機オイルとの組み合わせにより異なるが、一般には、架橋性シリコーン組成物100重量部に対して、非架橋性のシリコーンオイルまたは有機オイルを200〜5,000重量部の範囲内であることが好ましく、特には、250〜2,000重量部の範囲内であることが好ましい。 The amount that may be the holding differs by the combination of the crosslinkable silicone composition non-crosslinkable silicone oil or organic oil, in general, to the crosslinkable silicone composition 100 parts by weight, non-crosslinkable silicone oil or preferably in the range of organic oil in the 200 to 5,000 parts by weight, particularly preferably in the range of 250~2,000 parts.
【0023】 [0023]
また、この架橋性シリコーン組成物中の非架橋性のシリコーンオイルまたは有機オイルには、予め他の成分を溶解していてもよい。 In addition, the non-crosslinkable silicone oil or organic oil of this crosslinkable silicone composition, may be dissolved in advance other components. この成分としては、上記で例示したものが挙げられる。 As this component include those exemplified above. 架橋性シリコーン組成物中に配合可能な他の成分の含有量は、架橋性シリコーン組成物と非架橋性のシリコーンオイルまたは有機オイルとの組み合わせにより異なるが、一般には、架橋性シリコーン組成物100重量部に対して、他の成分を0.001〜200重量部の範囲内で配合することができるが、好ましくは、0.1〜50重量部の範囲内である。 The content of the other components that can be incorporated into the crosslinkable silicone composition varies depending on the combination of the crosslinkable silicone composition non-crosslinkable silicone oil or organic oil, in general, the crosslinkable silicone composition 100 wt against part, although other ingredients may be formulated in a range of 0.001 to 200 parts by weight, preferably in the range of 0.1 to 50 parts by weight.
【0024】 [0024]
この方法では、このような非架橋性のシリコーンオイルまたは有機オイルを含有している架橋性シリコーン組成物を水中に分散させた後、これを架橋反応させる。 In this method, after the crosslinkable silicone composition containing such a non-crosslinkable silicone oil or organic oil dispersed in water, thereby crosslinking the same. この架橋性シリコーン組成物を水中に分散させる方法としては、ホモミキサー、パドルミキサー、ヘンシェルミキサー、ホモディスパー、コロイドミル、プロペラ攪拌機、ホモジナイザー、インライン式連続乳化機、超音波乳化機、真空式練合機等の装置によりこの組成物を水中に分散させる方法が例示される。 As a method of dispersing the crosslinkable silicone composition in water, a homomixer, paddle mixer, Henschel mixer, homodisperser, colloid mill, a propeller stirrer, a homogenizer, an inline type continuous emulsifier, ultrasonic emulsifier, vacuum kneading the method of dispersing the composition in water is illustrated by the apparatus of the machine, or the like.
【0025】 [0025]
また、この方法において、水の使用量は限定されないが、エマルジョン全体の5〜99重量%の範囲内であることが好ましく、特には、10〜80重量%の範囲内であることが好ましい。 Further, in this method, the amount of water is not limited but is preferably in the range of 5 to 99% by weight of the total emulsion, particularly preferably in the range of 10 to 80 wt%.
【0026】 [0026]
さらに、架橋性シリコーン組成物を水中に安定性よく分散させるためには、ノニオン系界面活性剤、カチオン系界面活性剤、あるいはアニオン系界面活性剤を用いることが好ましく、特には、ノニオン系界面活性を用いることが好ましい。 Furthermore, in order to stabilize good dispersion of the crosslinkable silicone composition in water, nonionic surfactant, cationic surfactant or it is preferable to use an anionic surfactant, especially nonionic surfactant it is preferably used. この界面活性剤としては、シリコーン系や有機系が例示され、この使用量は、非架橋性のシリコーンオイルまたは有機オイルを含有している架橋性シリコーン組成物100重量部に対して0.1〜20重量部の範囲内であることが好ましく、特には、0.5〜10重量部の範囲内であることが好ましい。 As the surfactant, a silicone-based or organic-based and the like, the amount used is 0.1 with respect to the crosslinkable silicone composition 100 parts by weight containing a non-crosslinkable silicone oil or organic oil it is preferably in the range of 20 parts by weight, particularly preferably in the range of 0.5 to 10 parts by weight.
【0027】 [0027]
このようにして調製された架橋性シリコーン組成物のエマルジョンを加熱、あるいは室温で放置したり、高エネルギー線を照射したりすることによって、水中に分散している架橋性シリコーン組成物を架橋反応させることができる。 Thus an emulsion of the crosslinkable silicone composition prepared heated or or left at room temperature, by or irradiated with high energy radiation to crosslink reaction of the crosslinkable silicone composition dispersed in water be able to.
【0028】 [0028]
また、本発明の化粧品原料には、必要に応じて、例えば、流動パラフィン、イソパラフィン、ラウリン酸ヘキシル、ミリスチン酸イソプロピル、ミリスチン酸ミリスチル、ミリスチン酸セチル、ミリスチン酸2−オクチルドデシル、パルミチン酸イソプロピル、パルミチン酸2−エチルヘキシル、ステアリン酸ブチル、オレイン酸デシル、オレイン酸2−オクチルドデシル、乳酸ミリスチル、乳酸セチル、酢酸ラノリン、ステアリルアルコール、セトステアリルアルコール、オレイルアルコール、アボガド油、アーモンド油、オリブ油、カカオ油、ホホバ油、ゴマ油、サフラワー油、大豆油、ツバキ油、スクワラン、パーシック油、ヒマシ油、ミンク油、綿実油、ヤシ油、卵黄油、豚脂、ポリプロピレングリコールモノオレート、ネオペンチ Furthermore, the cosmetic raw material of the present invention, as needed, for example, liquid paraffin, isoparaffin, hexyl laurate, isopropyl myristate, myristyl myristate, cetyl myristate, 2-octyldodecyl myristate, isopropyl palmitate, 2-ethylhexyl, butyl stearate, decyl oleate, 2-octyldodecyl oleate, myristyl lactate, cetyl lactate, lanolin acetate, stearyl alcohol, cetostearyl alcohol, oleyl alcohol, avocado oil, almond oil, olive oil, cacao oil , jojoba oil, sesame oil, safflower oil, soybean oil, camellia oil, squalane, persic oil, castor oil, mink oil, cottonseed oil, coconut oil, egg yolk oil, lard, polypropylene glycol monooleate, neopentyl グリコール−2−エチルヘキサノエート等のグリコールエステル油;イソステアリン酸トリグリセライド、椰子油脂肪酸トリグリセライド等の多価アルコールエステル油;ポリオキシエチレンラウリルエーテル、ポリオキシプロピレンセチルエーテル等のポリオキシアルキレンエーテル油等の有機オイル、さらにはシリコーンオイルを別途配合してもよい。 Glycol 2-ethylhexanoate glycol ester oils such as benzoate; isostearic acid triglyceride, polyhydric alcohol ester oils such as coconut oil fatty acid triglyceride; polyoxyethylene lauryl ether, polyoxyalkylene ether oil such as polyoxypropylene cetyl ether organic oil, furthermore may be separately blended silicone oil.
【0029】 [0029]
なお、架橋シリコーン粒子をシリコーンオイルまたは有機オイルに分散した後、エマルジョン化することによってもシリコーンオイルまたは有機オイルのエマルジョンを調製することができるが、架橋シリコーン粒子とシリコーンオイルまたは有機オイルの液滴とがそれぞれ単独で分散してしまい、水中に分散しているシリコーンオイルまたは有機オイルの液滴中に架橋シリコーン粒子を含有するようなシリコーンオイルまたは有機オイルのエマルジョンを調製することは困難であり、このようなシリコーンオイルまたは有機オイルのエマルジョンを化粧品原料として用いても、化粧品中にシリコーンオイルまたは有機オイルと架橋シリコーン粒子を均一に分散させることができるものではなく、また、均一に分散させることは非常に困難で Note that after the cross-linked silicone particles dispersed in a silicone oil or organic oil, can be prepared an emulsion of silicone oil or organic oil also by emulsification, and droplets of crosslinked silicone particles and the silicone oil or organic oil There will be distributed solely respectively, it is difficult to prepare an emulsion of silicone oil or organic oil, such as those containing cross-linked silicone particles in the droplets in the silicone oil or organic oil dispersed in water, the be used an emulsion of silicone oil or organic oil, such as a cosmetic raw material, not silicone oils or organic oils and crosslinked silicone particles can be uniformly dispersed in the cosmetic, also very able to uniformly disperse It is difficult to った。 Was Tsu.
【0030】 [0030]
また、このようにして調製されたシリコーンオイルまたは有機オイルのエマルジョンは、水中に分散したシリコーンオイルまたは有機オイルの液滴の平均粒径が0.1〜500μmの範囲内であることが必要であり、好ましくは、0.2〜500μmの範囲内であり、より好ましくは、0.5〜500μmの範囲内であり、特に好ましくは、0.5〜200μmの範囲内である。 Further, an emulsion of the thus silicone oil or organic oil is prepared, the average particle diameter of the droplets of the dispersed silicone oil or organic oil in water should be in the range of 0.1~500μm , preferably in the range of 0.2~500Myuemu, more preferably, in the range of 0.5 to 500, particularly preferably in the range of 0.5 to 200. これは、液滴の平均粒径が上記範囲の下限未満であるエマルジョンを調製することが困難である傾向があり、一方、上記範囲の上限をこえるエマルジョンは、化粧品原料としての安定性が低下する傾向があるからである。 This tends average particle diameter of the droplets is difficult to prepare an emulsion which is below the recommended lower limit, while the emulsion that exceeds the upper limit, the stability of the cosmetic material is reduced This is because there is a trend.
【0031】 [0031]
また、このエマルジョンにおいて、架橋シリコーン粒子の平均粒径は0.05〜100μmの範囲内であることが必要であり、好ましくは、0.1〜100μmの範囲内であり、特に好ましくは、0.1〜50μmの範囲内である。 Further, in the emulsion, the average particle size of the crosslinked silicone particles must lie within the range of 0.05~100Myuemu, preferably in the range of 0.1 to 100 [mu] m, particularly preferably 0. it is within the range of 1~50μm. また、シリコーンオイルまたは有機オイルの液滴の平均粒径が0.2〜500μmの範囲内である場合には、架橋シリコーン粒子の平均粒径は0.1〜100μmの範囲内であることが好ましく、特に、0.1〜50μmの範囲内であることが好ましい。 Further, when the average particle diameter of droplets of the silicone oil or organic oil is in the range of 0.2~500μm preferably has an average particle size of the crosslinked silicone particles is in the range of 0.1~100μm , particularly preferably in the range of 0.1 to 50 [mu] m. また、シリコーンオイルまたは有機オイルの液滴の平均粒径が0.5〜500μmの範囲内である場合には、架橋シリコーン粒子の平均粒径は0.1〜100μmの範囲内であることが好ましく、特に、0.1〜50μmの範囲内であることが好ましい。 Further, when the average particle diameter of droplets of the silicone oil or organic oil is in the range of 0.5~500μm preferably has an average particle size of the crosslinked silicone particles is in the range of 0.1~100μm , particularly preferably in the range of 0.1 to 50 [mu] m. さらに、シリコーンオイルまたは有機オイルの液滴の平均粒径が0.5〜200μmの範囲内である場合には、架橋シリコーン粒子の平均粒径は0.1〜100μmの範囲内であることが好ましく、特に、0.1〜50μmの範囲内であることが好ましい。 Further, when the average particle diameter of droplets of the silicone oil or organic oil is in the range of 0.5~200μm preferably has an average particle size of the crosslinked silicone particles is in the range of 0.1~100μm , particularly preferably in the range of 0.1 to 50 [mu] m. これは、平均粒径が上記範囲の下限未満である架橋シリコーン粒子を調製することが困難である傾向があるからであり、一方、上記範囲の上限をこえる架橋シリコーン粒子は、化粧品原料としてのエマルジョンの安定性を低下させる傾向があるからである。 This average particle size is because there tends to be difficult to prepare the crosslinked silicone particles is less than the lower limit of the above range, on the other hand, cross-linked silicone particles exceeding the upper limit of the above range, the emulsion as a cosmetic raw material They tend to reduce the stability of the. このエマルジョンにおいて、架橋シリコーン粒子の粒径はシリコーンオイルまたは有機オイルの液滴の粒径より小さいことは無論である。 In this emulsion, the particle size of the crosslinked silicone particles is smaller than the particle size of droplets of the silicone oil or organic oil is course. この架橋シリコーン粒子の形状は、例えば、球状、紡錘形状、偏平形状、不定形状が挙げられ、好ましくは、球状である。 The shape of the crosslinked silicone particles, for example, spherical, spindle-shaped, flat-shaped, include irregular shape, preferably a spherical shape.
【0032】 [0032]
また、このようにして調製されたエマルジョンから水を除去して得られる、シリコーンオイルまたは有機オイル中に架橋シリコーン粒子が分散しているオイル組成物を化粧品原料とすることもできる。 It is also possible to thus obtained by removing water from the emulsion prepared by the oil composition crosslinked silicone particles in silicone oil or organic oil is dispersed as cosmetic raw materials. このエマルジョンから水を除去する方法としては、風乾、熱風乾燥、真空乾燥、加熱乾燥等の手段が挙げられる。 As a method for removing water from the emulsion, air-dried, hot air drying, vacuum drying, and a means of drying by heating. このような化粧品原料は、シリコーンオイルまたは有機オイル中に架橋シリコーン粒子が均一に分散しているという特徴があり、その形状としては、例えば、液状、クリーム状、ペースト状、グリース状、粉状、あるいは塊状が挙げられる。 Such cosmetic ingredients, is characterized in that cross-linked silicone particles in silicone oil or organic oil is uniformly dispersed, as is the shape, for example, liquid, creamy, pasty, greasy, powder, or the like is massive. このようなシリコーンオイル組成物または有機オイルの組成物からなる化粧品原料は非水系の化粧品原料として有用である。 Cosmetic raw material consisting of the composition of the silicone oil composition or organic oil is useful as a cosmetic raw material for non-aqueous.
【0033】 [0033]
また、このような化粧品原料には、必要に応じて、例えば、流動パラフィン、イソパラフィン、ラウリン酸ヘキシル、ミリスチン酸イソプロピル、ミリスチン酸ミリスチル、ミリスチン酸セチル、ミリスチン酸2−オクチルドデシル、パルミチン酸イソプロピル、パルミチン酸2−エチルヘキシル、ステアリン酸ブチル、オレイン酸デシル、オレイン酸2−オクチルドデシル、乳酸ミリスチル、乳酸セチル、酢酸ラノリン、ステアリルアルコール、セトステアリルアルコール、オレイルアルコール、アボガド油、アーモンド油、オリブ油、カカオ油、ホホバ油、ゴマ油、サフラワー油、大豆油、ツバキ油、スクワラン、パーシック油、ヒマシ油、ミンク油、綿実油、ヤシ油、卵黄油、豚脂、ポリプロピレングリコールモノオレート、ネオペン Furthermore, such a cosmetic raw material, if necessary, for example, liquid paraffin, isoparaffin, hexyl laurate, isopropyl myristate, myristyl myristate, cetyl myristate, 2-octyldodecyl myristate, isopropyl palmitate, 2-ethylhexyl, butyl stearate, decyl oleate, 2-octyldodecyl oleate, myristyl lactate, cetyl lactate, lanolin acetate, stearyl alcohol, cetostearyl alcohol, oleyl alcohol, avocado oil, almond oil, olive oil, cacao oil , jojoba oil, sesame oil, safflower oil, soybean oil, camellia oil, squalane, persic oil, castor oil, mink oil, cottonseed oil, coconut oil, egg yolk oil, lard, polypropylene glycol monooleate, neopentyl ルグリコール−2−エチルヘキサノエート等のグリコールエステル油;イソステアリン酸トリグリセライド、椰子油脂肪酸トリグリセライド等の多価アルコールエステル油;ポリオキシエチレンラウリルエーテル、ポリオキシプロピレンセチルエーテル等のポリオキシアルキレンエーテル油等の有機オイル、さらにはシリコーンオイルを配合してもよい。 Isostearic acid triglyceride, polyhydric alcohol ester oils such as coconut oil fatty acid triglyceride; glycol ester oils such as glycol 2-ethylhexanoate polyoxyethylene lauryl ether, polyoxyethylene ethers of polyoxypropylene cetyl ether oils the organic oil, and further may be blended with silicone oil.
【0034】 [0034]
次に、本発明の化粧品を詳細に説明する。 Next, the cosmetics of the present invention will be described in detail.
本発明の化粧品は、上記のシリコーンオイルまたは有機オイルのエマルジョンからなる化粧品原料と他の化粧品原料からなることを特徴とする。 Cosmetics of the present invention is characterized in that it consists of a cosmetic raw material and other cosmetic raw material consisting of the emulsion of the silicone oil or organic oil. 本発明の化粧品の類型としては、石鹸、ボディシャンプー、洗顔クリーム等の洗浄用化粧品、化粧水、クリーム・乳液、パック等の基礎化粧品;おしろい、ファンデーション等のベースメークアップ化粧品、口紅、ほほ紅、アイシャドー、アイライナー、マスカラ等の眉目化粧品、マニキュア等のメークアップ化粧品;シャンプー、ヘアリンス、ヘアコンディショナー、ヘアトリートメント、セットローション、ブロースタイリングローション、ヘアスプレー、泡状スタイリング剤、ジェル状スタイリング剤、ヘアリキッド、ヘアトニック、ヘアクリーム、育毛剤、養毛剤、染毛剤、整髪料等の毛髪化粧品;香水、オー・デ・コロン等の芳香性化粧品;歯磨き;浴用剤;脱毛剤、髭剃り用ローション、制汗・消臭剤、日焼け防止剤等の特殊化 The type of cosmetic product of the present invention, soap, body shampoo, facial cream, etc. of the cleaning cosmetics, lotion, cream, lotion, foundation cosmetics such as pack, face powder, the base of the foundation, such as make-up cosmetics, lipstick, blusher, eye shadow, eyeliner, mascara, etc. of Bimoku cosmetics, make-up cosmetics such as nail polish; shampoo, hair rinses, hair conditioners, hair treatments, setting lotions, blow styling lotion, hair spray, foam-like styling agents, gel-like styling agents, hair liquid, hair tonic, hair cream, hair tonic, hair tonic, hair dye, hair cosmetics hair dressing and the like; perfume, fragrant cosmetics such as Eau de colon; toothpaste; bath agent; depilatories, shaving lotion, antiperspirant deodorant, specialization, such as sun protection agents 品が例示され、特に、基礎化粧品、メークアップ化粧品等の皮膚化粧品、あるいは毛髪化粧品であることが好ましい。 Goods are exemplified, in particular, basic cosmetics, it is preferable makeup cosmetics skin cosmetic or a hair cosmetic. また、この化粧品の剤形としては、水性液状、油性液状、乳液状、クリーム状、フォーム状、半固形状、固形状、粉状が例示される。 Further, As the dosage form of cosmetics, aqueous liquid, oily liquid, milky lotion, cream, foam, semi-solid, solid, powdery form is exemplified. また、この化粧品をスプレーにより用いることができる。 In addition, it is possible to use the spray this cosmetics.
【0035】 [0035]
この化粧品は、上記の架橋シリコーン粒子を含有するシリコーンオイルまたは有機オイルのエマルジョンからなる化粧品原料と他の化粧品原料からなるが、この化粧品原料としては、アボガド油、アルモンド油、オリブ油、カカオ脂、ゴマ油、小麦胚芽油、サフラワー油、シアバター、タートル油、椿油、パーシック油、ヒマシ油、ブドウ油、マカデミアナッツ油、ミンク油、卵黄油、モクロウ、ヤシ油、ローズヒップ油、硬化油等の油脂;オレンジラフィー油、カルナウバロウ、キャンデリラロウ、鯨ロウ、ホホバ油、モンタンロウ、ミツロウ、ラノリン等のロウ類;流動パラフィン、ワセリン、パラフィン、セレシン、マイクロクリスタリンワックス、スクワラン等の炭化水素;ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸 The cosmetic is comprised of cosmetic raw material and other cosmetic raw material consisting of the emulsion of silicone oil or organic oil containing the crosslinked silicone particles, as the raw material for cosmetics, avocado oil, almond oil, olive oil, cacao butter, sesame oil, wheat germ oil, safflower oil, shea butter, turtle oil, camellia oil, persic oil, castor oil, grapeseed oil, macadamia nut oil, mink oil, egg yolk oil, Japan wax, coconut oil, rose hip oil, fats and oils of hydrogenated oil, etc. ; orange roughy oil, carnauba wax, candelilla wax, spermaceti, jojoba oil, montan wax, beeswax, wax and lanolin; liquid paraffin, vaseline, paraffin, ceresin, microcrystalline wax, hydrocarbons such as squalane; lauric acid, myristic acid, palmitic acid, stearic acid オレイン酸、ベヘニン酸、ウンデシレン酸、オキシステアリン酸、リノール酸、ラノリン酸、合成脂肪酸等の高級脂肪酸;エチルアルコール、イソプロピルアルコール、ラウリルアルコール、セチルアルコール、セトステアリルアルコール、ステアリルアルコール、オレイルアルコール、ベヘニルアルコール、ラノリンアルコール、水素添加ラノリンアルコール、ヘキシルデカノール、オクチルドデカノール、イソステアリルアルコール等のアルコール;コレステロール、ジヒドロコレステロール、フィトステロール等のステロール;リノール酸エチル、ミリスチン酸イソプロピル、ラノリン脂肪酸イソプロピル、ラウリン酸ヘキシル、ミリスチン酸ミリスチル、ミリスチン酸セチル、ミリスチン酸オクチルドデシル、オレイン酸デシル、 Oleic acid, behenic acid, undecylenic acid, oxystearic acid, linoleic acid, lanolin acid, higher fatty acids such as synthetic fatty acids; ethyl alcohol, isopropyl alcohol, lauryl alcohol, cetyl alcohol, cetostearyl alcohol, stearyl alcohol, oleyl alcohol, behenyl alcohol, cholesterol, dihydrocholesterol, sterols such as phytosterols; lanolin alcohol, hydrogenated lanolin alcohol, hexyl decanol, octyl dodecanol, alcohols such as isostearyl alcohol ethyl linoleate, isopropyl myristate, isopropyl lanolate, hexyl laurate, myristyl myristate , cetyl myristate, octyldodecyl myristate, decyl oleate, レイン酸オクチルドデシル、ジメチルオクタン酸ヘキシルデシル、イソオクタン酸セチル、パルミチン酸セチル、トリミリスチン酸グリセリン、トリ(カプリル・カプリン酸)グリセリン、ジオレイン酸プロピレングリコール、トリイソステアリン酸グリセリン、トリイソオクタン酸グリセリン、乳酸セチル、乳酸ミリスチル、リンゴ酸ジイソステアリル等の脂肪酸エステル;グリセリン、プロピレングリコール、1,3−ブチレングリコール、ポリエチレングリコール、d,l−ピロリドンカルボン酸ナトリウム、乳酸ナトリウム、ソルビトール、ヒアルロン酸ナトリウム等の保湿剤;高級脂肪酸石鹸、高級アルコール硫酸エステル塩、N−アシルグルタミン酸塩、リン酸エステル塩等のアニオン界面活性剤、カチオン界面活性剤、ベタイ Rain octyldodecyl, hexyldecyl dimethyloctanoate, cetyl isooctanoate, cetyl palmitate, trimyristate glycerol, tri (caprylic-capric acid) glyceryl dioleate propylene glycol, triisostearate glycerin, triisooctanoate glycerin, cetyl lactate , myristyl lactate, fatty acid esters such as diisostearyl malate; glycerol, propylene glycol, 1,3-butylene glycol, polyethylene glycol, d, l-pyrrolidone carboxylate, sodium lactate, sorbitol, humectants such as sodium hyaluronate ; higher fatty acid soaps, higher alcohol sulfuric ester salts, N- acyl glutamates, anionic surfactants such as phosphoric acid ester salts, cationic surfactants, Betai ン型、アミノ酸型、イミダゾリン型、レシチン等の両性界面活性剤、多価アルコールエステル型、酸化エチレン縮合型等の非イオン界面活性剤等の界面活性剤;酸化鉄等の有色顔料、酸化亜鉛、酸化チタン、酸化ジリコニウム等の白色顔料、マイカ、タルク、セリサイト等の体質顔料等の顔料;ジメチルポリシロキサン、メチルフェニルポリシロキサン、オクタメチルテトラシクロシロキサン、デカメチルシクロペンタシロキサン、ポリエーテル変性シリコーンオイル、アミノ変性シリコーンオイル等のシリコーンオイル;精製水;カラギーナン、アルギン酸、アラビアゴム、トラガント、ペクチン、デンプン、キサンタンガム、ポリビニルアルコール、ポリビニルピロリドン、ポリアクリル酸ソーダ、ポリエチレングリコール等の増粘剤、 Emission type, amino acid type, imidazoline type amphoteric surface active agents such as lecithin, a polyhydric alcohol ester type surface active agents, such as non-ionic surfactants such as ethylene oxide condensation type; colored pigments such as iron oxide, zinc oxide, titanium oxide, white pigments such as oxide Jirikoniumu, mica, talc, pigments such as extender pigments such as sericite, dimethyl polysiloxane, methylphenyl polysiloxane, octamethyltetracyclosiloxane, decamethylcyclopentasiloxane, polyether modified silicone oil , silicone oils such as amino-modified silicone oil; purified water; carrageenan, alginic acid, gum arabic, tragacanth, pectin, starch, xanthan gum, polyvinyl alcohol, polyvinyl pyrrolidone, sodium polyacrylate, thickeners such as polyethylene glycol, らには、紫外線吸収剤、抗菌剤、坑炎症剤、制汗剤、防腐剤、香料、酸化防止剤、pH調節剤、噴射剤が例示される。 Raniwa, UV absorbers, antimicrobial agents, anti-inflammatory agents, antiperspirants, preservatives, perfumes, antioxidants, pH regulators, propellants and the like.
【0036】 [0036]
また、この化粧品が毛髪化粧品である場合には、他の毛髪化粧品原料として、油脂、界面活性剤、皮膜形成剤、ふけ止め剤、酸化防止剤、湿潤剤等を配合することができるこの油脂としては、マイクロクリスタリンワックス、パラフィンワックス、ゲイろう、ビーズワックス、ジャパンワックス、ショ糖ワックス等のワックス類、またはこれらの混合物;流動パラフィン、α−オレフィンオリゴマー、スクワラン、スクワレン等の炭化水素油、またはこれらの混合物;セタノール、ステアリルアルコール、イソステアリルアルコール、硬化ヒマシ油誘導アルコール、ベヘニルアルコール、ラノリンアルコール等の直鎖状あるいは分岐状、飽和あるいは不飽和、ヒドロキシ置換あるいは非置換の高級アルコール、またはこれらの混合物;パルミ Further, when the cosmetic is a hair cosmetic, as other hair cosmetic raw materials, oil, surfactant, film-forming agents, anti-dandruff agents, antioxidants, as this fat may be blended with wetting agents and the like is microcrystalline wax, paraffin wax, Gay wax, beeswax, Japan wax, waxes sucrose wax or mixtures thereof; liquid paraffin, alpha-olefin oligomers, squalane, hydrocarbon oils such as squalene, or they mixture; cetanol, stearyl alcohol, isostearyl alcohol, hydrogenated castor oil-induced alcohol, behenyl alcohol, linear or branched, such as lanolin alcohols, saturated or unsaturated, higher alcohols hydroxy-substituted or unsubstituted, or mixtures thereof; Palmi ン酸、ミリスチン酸、オレイン酸、ステアリン酸、ヒドロキシステアリン酸、イソステアリン酸、ベヘニン酸、ヒマシ油脂肪酸、ヤシ油脂肪酸等の直鎖状あるいは分岐状、飽和あるいは不飽和、ヒドロキシ置換あるいは非置換の高級脂肪酸、またはこれらの混合物;オリーブ油、ヤシ油、なたね油、パーム油、パーム核油、ヒマシ油、硬化ヒマシ油、落花生油、牛脂、水添牛脂、ホホバ油、硬化ホホバ油、モノステアリン酸グリセリド、モノオレイン酸グリセリド、ジパルミチン酸グリセリド、トリミリスチン酸グリセリド、オレイルオレート、イソステアリルイソステアレート、パルミチルベヘネート、イソプロピルパルミテート、ステアリルアセテート、ジヒドロキシステアリン酸エステル等のエステル類;直鎖状、分枝状、または環状 Phosphate, myristic acid, oleic acid, stearic acid, hydroxystearic acid, isostearic acid, behenic acid, castor oil fatty acid, such as coconut oil fatty acid linear or branched, saturated or unsaturated, hydroxy substituted or unsubstituted higher fatty acids or mixtures thereof; olive oil, coconut oil, rapeseed oil, palm oil, palm kernel oil, castor oil, hardened castor oil, peanut oil, beef tallow, water tallow, jojoba oil, hydrogenated jojoba oil, monostearate glyceride, mono glycerides of oleic acid, dipalmitate glycerides, trimyristate glyceride, oleyl oleate, isostearyl isostearate, palmityl behenate, isopropyl palmitate, stearyl acetate, esters such as dihydroxy stearic acid ester; linear, minute branched, or cyclic の低分子量シリコーンオイル;アミノ変性シリコーンオイル、脂肪酸変性シリコーンオイル、アルコール変性シリコーンオイル、ポリエーテル変性シリコーンオイル、リン酸(塩)基含有シリコーンオイル、硫酸(塩)基含有シリコーンオイル、フッ素変性アルキル基含有シリコーンオイル、アルキル変性シリコーンオイル、エポキシ変性シリコーンオイル等のシリコーンオイル;溶剤に可溶で、室温で液状や生ゴム状の高分子量シリコーンオイル、熱可塑性を有するシリコーンレジン、またはこれらの混合物が例示される。 Amino-modified silicone oil, fatty acid-modified silicone oil, alcohol-modified silicone oil, polyether-modified silicone oil, phosphoric acid (salt) group-containing silicone oil, sulfuric acid (salt) group-containing silicone oil, fluorine-modified alkyl group; low molecular weight silicone oil containing silicone oil, alkyl-modified silicone oil, silicone oils such as epoxy-modified silicone oil; soluble in a solvent, the liquid or gum-like high molecular weight silicone oil, silicone resin having a thermoplastic or a mixture thereof, is illustrated at room temperature that.
【0037】 [0037]
また、この界面活性剤としては、グリセリンモノステアレート等のグリセリン脂肪酸エステル;ソルビタンモノパルミテート等のソルビタン脂肪酸エステル;ポリオキシエチレンセチルエーテル等のポリオキシエチレンアルキルエーテル;ポリオキシエチレンステアリン酸エステル、ポリオキシエチレンソルビタンモノラウレート等のポリオキシエチレン脂肪酸エステル;その他、ポリオキシエチレンアルキルフェニルエーテル、ポリオキシエチレンヒマシ油、ポリオキシエチレン硬化ヒマシ油、脂肪酸アルキロールアミド等の非イオン性界面活性剤;塩化ステアリルトリメチルアンモニウム、塩化ベヘニルトリメチルアンモニウム等のモノアルキルトリメチルアンモニウム塩;塩化ジステアリルジメチルアンモニウム、塩化ジベヘニルジメ Further, As the surfactant, glycerin fatty acid esters such as glycerol monostearate; polyoxyethylene alkyl ethers such as polyoxyethylene cetyl ether; sorbitan sorbitan fatty acid esters such as monopalmitate polyoxyethylene stearic acid esters, poly polyoxyethylene fatty acid esters such as polyoxyethylene sorbitan monolaurate and the like; polyoxyethylene alkyl phenyl ethers, polyoxyethylene castor oil, polyoxyethylene hardened castor oil, anionic surfactants such as fatty acid alkylolamides; chloride stearyl trimethyl ammonium, monoalkyl trimethyl ammonium salts such as behenyltrimethylammonium chloride; distearyl dimethyl ammonium chloride, Jibehenirujime ルアンモニウム等のジアルキルジメチルアンモニウム塩等の陽イオン性界面活性剤、あるいは、両性界面活性剤が例示される。 Cationic surfactants such as dialkyl dimethyl ammonium salts such as Le ammonium, or amphoteric surfactants.
【0038】 [0038]
また、この皮膜形成剤としては、(メタ)アクリル系ラジカル重合性モノマーの重合体やシリコーン系化合物との共重合体、ポリ(N―アシルアルキレンイミン)、ポリ(N−メチルピロリドン)、フッ素基含有有機基やアミノ基で変性したシリコーンレジン、無変性のシリコーンレジンが例示される。 Further, as the film-forming agent, a copolymer of (meth) polymers and silicone-based compounds of the acrylic radical polymerizable monomer, poly (N- acylalkyleneimine), poly (N- methylpyrrolidone), fluorine group silicone resins modified with containing organic group or an amino group, unmodified silicone resin are exemplified. また、このふけ止め剤としては、イオウ、硫化セレン、ジンクピリチオン、オクトピロックス、ジンクピリジウム−1−チオール−N−オキサイド、サリチル酸、2,4,4'−トリクロロ−2'−ヒドロキシジフェニルエーテル、1−ヒドロキシ−2−ピリドン化合物が例示される。 Further, as the anti-dandruff agent, sulfur, selenium sulfide, zinc pyrithione, octopirox, zinc pyridium-1-thiol -N- oxide, salicylic acid, 2,4,4'-trichloro-2'-hydroxydiphenyl ether, 1 - hydroxy-2-pyridone compounds. また、この酸化防止剤としては、BHA、BHT、γ−オリザノールが例示される。 Further, as the antioxidant, BHA, BHT, .gamma.-oryzanol are exemplified. また、湿潤剤としては、ヘキシレングリコール、ポリエチレングリコール、ピログルタミン酸ソーダ、プロピレングリコール、ソルビトール、グリセリンが例示される。 As the wetting agent, hexylene glycol, polyethylene glycol, pyroglutamic acid sodium, propylene glycol, sorbitol, glycerin and the like.
【0039】 [0039]
さらに、毛髪化粧品には、その他任意の成分として、スクワレン、ラノリン、パーフルオロポリエーテル、カチオン性ポリマー等の感触向上剤;エタノール、イソプロピルアルコール、1、3 −ブチレングリコール、エチレングリコール、プロピレングリコール、グリセリン等の凍結防止剤;エチレンジアミン4酢酸、クエン酸、エタン−1−ヒドロキシ−1,1−ジホスホニックアシッド、およびこれらの塩等のキレート剤;2−ヒドロキシ−4−メトキシベンゾフェノン等のベンゾフェノン誘導体、2−(2'−ヒドロキシ−5'−メチル−フェニル)−ベンゾトリアゾール等のベンゾトリアゾール誘導体、桂皮酸エステル等の紫外線吸収剤;トリクロサン、トリクロロカルバン等の殺菌剤;グリチルリチン酸カリウム、酢酸トコフェロール等の Further, the hair cosmetics, as any other components, squalene, lanolin, perfluoropolyethers, feel improvers, such as cationic polymers; ethanol, isopropyl alcohol, 1,3 - butylene glycol, ethylene glycol, propylene glycol, glycerin benzophenone derivatives such as 2-hydroxy-4-methoxybenzophenone; antifreeze and the like; chelating agents ethylenediaminetetraacetic acid, citric acid, ethane-1-hydroxy-1,1-diphosphonate Nick acid, and the like salts thereof 2- (2'-hydroxy-5'-methyl - phenyl) - benzotriazole derivatives such as benzotriazole ultraviolet absorbers such as cinnamic acid esters; triclosan, fungicides such as trichloroacetic Calvin; potassium glycyrrhizinate, such as tocopherol acetate 抗炎症剤;メチルパラベン、ブチルパラベン等の防腐剤;パール化剤、色素、染料等の着色料;噴霧剤、ビタミン、養毛料、ホルモン、香料、その他Encyclopedia of Shampoo Ingredients(Micelle press、1985)に収載されている成分等を配合することができる。 Anti-inflammatory agents; methylparaben, preservatives such as butylparaben; listed propellants, vitamins, hair tonic, hormones, fragrances, and other Encyclopedia of Shampoo Ingredients (Micelle press, 1985); pearlizing agents, dyes, colorants such as dyes such component being able to incorporate.
【0040】 [0040]
また、この毛髪化粧品が水系である場合には、精製水等の水の他に、分散安定化、あるいは整髪のためにキサンタンガム、グアーガム、カルボキシメチルセルロース、ポリビニルアルコール、ポリビニルピロリドン、カルボキシビニルポリマー、ヒドロキシエチルセルロース、ポリオキシエチレングリコールジステアレート等の水溶性高分子、また、水系毛髪化粧品の粘度調節剤として、これらの水溶性高分子、あるいはエタノールを配合することができる。 Further, when the hair cosmetic is water based, in addition to water, such as purified water, xanthan gum for dispersion stabilization, or hair, guar gum, carboxymethylcellulose, polyvinyl alcohol, polyvinyl pyrrolidone, carboxyvinyl polymer, hydroxyethyl cellulose water-soluble polymers such as polyoxyethylene glycol distearate also, as a viscosity modifier of the aqueous hair cosmetic, can be compounded these water-soluble polymers or ethanol.
【0041】 [0041]
本発明の化粧品において、上記のようなシリコーンオイルまたは有機オイルのエマルジョンからなる化粧品原料の配合量は、その水分以外の成分換算(固形分換算)として、化粧品中の0.1〜99.9重量%であることが好ましく、特に、0.5〜99重量%の範囲内であることが好ましい。 In the cosmetic of the present invention, the amount of cosmetic raw material consisting of the emulsion of silicone oil or organic oil, such as described above, as a component in terms other than the water (in terms of solid content), 0.1 to 99.9 weight in Cosmetics % is preferably, particularly preferably in the range of 0.5 to 99 wt%. これは、上記のエマルジョンからなる化粧品原料の配合量が上記範囲の上限をこえる場合には、化粧品としての効果が失われる傾向があるからであり、一方、上記範囲の下限未満であると、上記のエマルジョンを配合することによる化粧品の使用感等が改善されにくくなる傾向があるからである。 This is because when the amount of cosmetic raw material having upper Symbol of the emulsion exceeds the recommended upper limit is because there is a tendency that the effect as a cosmetic is lost, whereas, is below the recommended lower limit, They tend to feel like is less likely to be improved cosmetic by blending the above emulsion.
【0042】 [0042]
また、本発明の化粧品は、上記のオイル組成物からなる化粧品原料と他の化粧品原料とからなることを特徴とする。 Further, the cosmetic of the present invention is characterized by comprising the cosmetic raw material and other cosmetic raw material consisting of the above oil composition. このオイル組成物からなる化粧品原料は上記の通りである。 Cosmetic raw material consisting of the oil composition are as described above. また、他の化粧品原料としては、上記と同様の原料が例示される。 As other cosmetic raw materials, the same material as described above is exemplified.
【0043】 [0043]
この化粧品において、上記のようなオイル組成物からなる化粧品の配合量は化粧品中の0.5〜99.0重量%の範囲内であることが好ましく、特に、1.0〜95重量%の範囲内であることが好ましい。 In this cosmetic, it is preferable that the amount of cosmetic comprising the oil composition as described above is in the range of 0.5 to 99.0% by weight of the cosmetic, in particular, the range of 1.0 to 95 wt% it is preferable that an internal. これは、上記のオイル組成物からなる化粧品原料の配合量が上記範囲の上限をこえる場合には、化粧品としての効果が失われる傾向があるからであり、一方、上記範囲の下限未満であると、上記のオイル組成物を配合することによる化粧品の使用感等が改善されにくくなる傾向があるからである。 This is because when the amount of cosmetic raw material consisting of the above oil composition exceeds the recommended upper limit is because there is a tendency that the effect as a cosmetic is lost, whereas, is below the recommended lower limit , they tend to feel like is less likely to be improved cosmetic by blending the oil composition.
【0044】 [0044]
次に、本発明の化粧品の製造方法を詳細に説明する。 Next, a method for manufacturing the decorative article of the present invention in detail.
本発明の製造方法は、上記のシリコーンオイルまたは有機オイルのエマルジョンからなる化粧品原料を他の化粧品原料と配合することを特徴とする。 Production method of the present invention is characterized by formulating the cosmetic raw material consisting of the emulsion of the silicone oils or organic oils and other cosmetic ingredients. 本発明の化粧品の製造方法によると、特殊な装置や高せん断をかけることなく、化粧品中にシリコーンオイルまたは有機オイルと架橋シリコーン粉末を均一に分散させることができるという効果がある。 According to the cosmetic manufacturing method of the present invention, without applying the special equipment or high shear, there is an effect that it is possible to in cosmetics uniformly disperse the crosslinked silicone powder with a silicone oil or organic oil. 本発明の製造方法では、例えば、回分式、連続式により化粧品を製造するが、このような方法で用いる装置としては、ホモミキサー、パドルミキサー、ヘンシェルミキサー、ホモディスパー、コロイドミル、プロペラ攪拌機、ホモジナイザー、インライン式連続乳化機、超音波乳化機、真空式練合機が例示される。 In the production method of the present invention, for example, batch type, but the production of cosmetics through the continuous, as the apparatus used in such a method, a homomixer, paddle mixer, Henschel mixer, homodisperser, colloid mill, a propeller stirrer, a homogenizer in-line type continuous emulsifier, ultrasonic emulsifier, vacuum kneader can be exemplified.
【0045】 [0045]
また、本発明の化粧品において、上記のようなシリコーンオイルまたは有機オイルのエマルジョンからなる化粧品原料と他の化粧品原料の一部もしくは全部を混合した後、水分を除去して、必要に応じて、さらに他の化粧品原料を配合することにより、シリコーンオイルまたは有機オイルと架橋シリコーン粒子を均一に分散した化粧品を調製することができる。 Also, in the cosmetic of the present invention, after mixing a part or all of the cosmetic raw material and other cosmetic raw material consisting of the emulsion of silicone oil or organic oil described above, the water is removed, if necessary, further by blending other cosmetic raw materials can be prepared cosmetics uniformly dispersed a crosslinked silicone particles and the silicone oil or organic oil. この方法において、水を除去する方法としては、減圧、加熱、もしくは風乾する方法、水分吸収剤と接触させる方法が例示される。 In this method, as a method of removing water under reduced pressure, heating, or a method of air-drying, a method of contacting with moisture absorbing agent are exemplified.
【0046】 [0046]
この化粧品は、上記の架橋シリコーン粒子を含有するシリコーンオイルまたは有機オイルのエマルジョンからなる化粧品原料と他の化粧品原料からなるが、この化粧品原料としては、アボガド油、アルモンド油、オリブ油、カカオ脂、ゴマ油、小麦胚芽油、サフラワー油、シアバター、タートル油、椿油、パーシック油、ヒマシ油、ブドウ油、マカデミアナッツ油、ミンク油、卵黄油、モクロウ、ヤシ油、ローズヒップ油、硬化油等の油脂;オレンジラフィー油、カルナウバロウ、キャンデリラロウ、鯨ロウ、ホホバ油、モンタンロウ、ミツロウ、ラノリン等のロウ類;流動パラフィン、ワセリン、パラフィン、セレシン、マイクロクリスタリンワックス、スクワラン等の炭化水素;ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸 The cosmetic is comprised of cosmetic raw material and other cosmetic raw material consisting of the emulsion of silicone oil or organic oil containing the crosslinked silicone particles, as the raw material for cosmetics, avocado oil, almond oil, olive oil, cacao butter, sesame oil, wheat germ oil, safflower oil, shea butter, turtle oil, camellia oil, persic oil, castor oil, grapeseed oil, macadamia nut oil, mink oil, egg yolk oil, Japan wax, coconut oil, rose hip oil, fats and oils of hydrogenated oil, etc. ; orange roughy oil, carnauba wax, candelilla wax, spermaceti, jojoba oil, montan wax, beeswax, wax and lanolin; liquid paraffin, vaseline, paraffin, ceresin, microcrystalline wax, hydrocarbons such as squalane; lauric acid, myristic acid, palmitic acid, stearic acid オレイン酸、ベヘニン酸、ウンデシレン酸、オキシステアリン酸、リノール酸、ラノリン酸、合成脂肪酸等の高級脂肪酸;エチルアルコール、イソプロピルアルコール、ラウリルアルコール、セチルアルコール、セトステアリルアルコール、ステアリルアルコール、オレイルアルコール、ベヘニルアルコール、ラノリンアルコール、水素添加ラノリンアルコール、ヘキシルデカノール、オクチルドデカノール、イソステアリルアルコール等のアルコール;コレステロール、ジヒドロコレステロール、フィトステロール等のステロール;リノール酸エチル、ミリスチン酸イソプロピル、ラノリン脂肪酸イソプロピル、ラウリン酸ヘキシル、ミリスチン酸ミリスチル、ミリスチン酸セチル、ミリスチン酸オクチルドデシル、オレイン酸デシル、 Oleic acid, behenic acid, undecylenic acid, oxystearic acid, linoleic acid, lanolin acid, higher fatty acids such as synthetic fatty acids; ethyl alcohol, isopropyl alcohol, lauryl alcohol, cetyl alcohol, cetostearyl alcohol, stearyl alcohol, oleyl alcohol, behenyl alcohol, cholesterol, dihydrocholesterol, sterols such as phytosterols; lanolin alcohol, hydrogenated lanolin alcohol, hexyl decanol, octyl dodecanol, alcohols such as isostearyl alcohol ethyl linoleate, isopropyl myristate, isopropyl lanolate, hexyl laurate, myristyl myristate , cetyl myristate, octyldodecyl myristate, decyl oleate, レイン酸オクチルドデシル、ジメチルオクタン酸ヘキシルデシル、イソオクタン酸セチル、パルミチン酸セチル、トリミリスチン酸グリセリン、トリ(カプリル・カプリン酸)グリセリン、ジオレイン酸プロピレングリコール、トリイソステアリン酸グリセリン、トリイソオクタン酸グリセリン、乳酸セチル、乳酸ミリスチル、リンゴ酸ジイソステアリル等の脂肪酸エステル;グリセリン、プロピレングリコール、1,3−ブチレングリコール、ポリエチレングリコール、d,l−ピロリドンカルボン酸ナトリウム、乳酸ナトリウム、ソルビトール、ヒアルロン酸ナトリウム等の保湿剤;高級脂肪酸石鹸、高級アルコール硫酸エステル塩、N−アシルグルタミン酸塩、リン酸エステル塩等のアニオン界面活性剤、カチオン界面活性剤、ベタイ Rain octyldodecyl, hexyldecyl dimethyloctanoate, cetyl isooctanoate, cetyl palmitate, trimyristate glycerol, tri (caprylic-capric acid) glyceryl dioleate propylene glycol, triisostearate glycerin, triisooctanoate glycerin, cetyl lactate , myristyl lactate, fatty acid esters such as diisostearyl malate; glycerol, propylene glycol, 1,3-butylene glycol, polyethylene glycol, d, l-pyrrolidone carboxylate, sodium lactate, sorbitol, humectants such as sodium hyaluronate ; higher fatty acid soaps, higher alcohol sulfuric ester salts, N- acyl glutamates, anionic surfactants such as phosphoric acid ester salts, cationic surfactants, Betai ン型、アミノ酸型、イミダゾリン型、レシチン等の両性界面活性剤、多価アルコールエステル型、酸化エチレン縮合型等の非イオン界面活性剤等の界面活性剤;酸化鉄等の有色顔料、酸化亜鉛、酸化チタン、酸化ジリコニウム等の白色顔料、マイカ、タルク、セリサイト等の体質顔料等の顔料;ジメチルポリシロキサン、メチルフェニルポリシロキサン、オクタメチルテトラシクロシロキサン、デカメチルシクロペンタシロキサン、ポリエーテル変性シリコーンオイル、アミノ変性シリコーンオイル等のシリコーンオイル;精製水;カラギーナン、アルギン酸、アラビアゴム、トラガント、ペクチン、デンプン、キサンタンガム、ポリビニルアルコール、ポリビニルピロリドン、ポリアクリル酸ソーダ、ポリエチレングリコール等の増粘剤、 Emission type, amino acid type, imidazoline type amphoteric surface active agents such as lecithin, a polyhydric alcohol ester type surface active agents, such as non-ionic surfactants such as ethylene oxide condensation type; colored pigments such as iron oxide, zinc oxide, titanium oxide, white pigments such as oxide Jirikoniumu, mica, talc, pigments such as extender pigments such as sericite, dimethyl polysiloxane, methylphenyl polysiloxane, octamethyltetracyclosiloxane, decamethylcyclopentasiloxane, polyether modified silicone oil , silicone oils such as amino-modified silicone oil; purified water; carrageenan, alginic acid, gum arabic, tragacanth, pectin, starch, xanthan gum, polyvinyl alcohol, polyvinyl pyrrolidone, sodium polyacrylate, thickeners such as polyethylene glycol, らには、紫外線吸収剤、抗菌剤、坑炎症剤、制汗剤、防腐剤、香料、酸化防止剤、pH調節剤、噴射剤が例示される。 Raniwa, UV absorbers, antimicrobial agents, anti-inflammatory agents, antiperspirants, preservatives, perfumes, antioxidants, pH regulators, propellants and the like.
【0047】 [0047]
本発明の化粧品において、上記のようなシリコーンオイルまたは有機オイルのエマルジョンからなる化粧品原料の配合量は、その水分以外の成分換算(固形分換算)として、化粧品中の0.1〜99.9重量%であることが好ましく、特に、0.5〜99重量%の範囲内であることが好ましい。 In the cosmetic of the present invention, the amount of cosmetic raw material consisting of the emulsion of silicone oil or organic oil, such as described above, as a component in terms other than the water (in terms of solid content), 0.1 to 99.9 weight in Cosmetics % is preferably, particularly preferably in the range of 0.5 to 99 wt%. これは、上記のシリコーンオイルまたは有機オイルのエマルジョンからなる化粧品原料の配合量が上記範囲の上限をこえる場合には、化粧品としての効果が失われる傾向があるからであり、一方、上記範囲の下限未満であると、シリコーンオイルまたは有機オイルのエマルジョンを配合することによる化粧品の使用感等が改善されにくくなる傾向があるからである。 This is because when the amount of cosmetic raw material consisting of the emulsion of the silicone oil or organic oil exceeds the recommended upper limit is because there is a tendency that the effect as a cosmetic is lost, whereas, the lower limit of the range by weight, they tend to feel like is less likely to be improved cosmetic by blending the emulsion of silicone oil or organic oil.
【0048】 [0048]
【実施例】 【Example】
本発明の化粧品原料、化粧品、および化粧品の製造方法を実施例により詳細に説明する。 Cosmetic raw material of the present invention, the cosmetic, and will be described in detail cosmetics manufacturing method according to Example. なお、実施例中の粘度は25℃における値である。 The viscosity in the examples were measured at 25 ° C..
【0049】 [0049]
また、シリコーンオイルエマルジョンの平均粒径や安定性、架橋シリコーン粒子の平均粒径、およびシリコーンオイル組成物の特性は次のようにして求めた。 The average particle size and stability of the silicone oil emulsion, the properties of the average particle diameter, and the silicone oil composition of the crosslinked silicone particles was determined as follows.
[シリコーンオイルエマルジョンの平均粒径] Average particle size of the silicone oil emulsion]
シリコーンオイルエマルジョンをレーザー回折式粒度分布測定器(堀場製作所のLA−500)により測定し、得られたメジアン径(累積分布の50%に相当する粒径)を平均粒径とした。 The silicone oil emulsion was measured by a laser diffraction particle size distribution measuring apparatus (LA-500 of Horiba), resulting median diameter (particle diameter corresponding to 50% of cumulative distribution) was defined as the average particle diameter.
[シリコーンオイルエマルジョンの安定性] Stability of the silicone oil emulsion]
シリコーンオイルエマルジョン180mLを225mLのガラスビン(深さ105mm、口径50mm)に密閉して、室温で1週間放置した。 Glass bottle 225mL silicone oil emulsion 180 mL (depth 105 mm, diameter 50 mm) was sealed in, and allowed to stand for one week at room temperature. 放置後、シリコーンオイルエマルジョンから分離した水層の厚さを測定した。 After standing, to measure the thickness of the water layer separated from the silicone oil emulsion.
[架橋シリコーン粒子の分散性] [Dispersibility of the crosslinked silicone particles]
シリコーンオイルエマルジョンをガラス板状で風乾し、実体顕微鏡下で架橋シリコーン粒子の形状、凝集状態、および分布について観察した。 Air-dried silicone oil emulsion with a glass plate, and observed the shape of the crosslinked silicone particles under a stereoscopic microscope, aggregation state, and the distribution. すべての架橋シリコーン粒子が1次粒子として分散していれば○とし、数100μmの凝集粒子や500μm以上の1次粒子があれば×とし、これらの間を△とした。 Until all of the crosslinked silicone particles with ○ if dispersed as primary particles, and × if the number 100μm agglomerated particles and 500μm or more primary particles of were between these △ and.
[架橋シリコーン粒子の平均粒径] Average particle size of the crosslinked silicone particles]
シリコーンオイルエマルジョンをガラス板状で風乾し、実体顕微鏡下で架橋シリコーン粒子を集めて試料を作成し、これを電子顕微鏡下で観察して、10個の粒子径から平均粒径を求めた。 Air-dried silicone oil emulsion with a glass plate, attracting crosslinked silicone particles under a stereoscopic microscope to create a sample which was observed under an electron microscope to determine the average particle size from 10 particle size.
[シリコーンオイル組成物の粘弾性] [Viscoelastic silicone oil composition]
シリコーンオイル組成物の貯蔵弾性率G'(×10 3 dyne/cm 2 )、損失弾性率G''(×10 3 dyne/cm 2 )、さらに損失正接tanδをARES粘弾性測定装置(Reometric Scientific社製)により測定した。 Storage modulus G of the silicone oil composition '(× 10 3 dyne / cm 2), the loss modulus G' '(× 10 3 dyne / cm 2), further loss tangent tanδ an ARES viscoelasticity measuring apparatus (Reometric Scientific Co. It was measured by Etsu Chemical Co., Ltd.). なお、測定の条件は、室温、25mmパラレルプレート、ギャップ:0.5〜0.6mm、歪み:10%、振動数:0.1〜50rad/sである。 The conditions of the measurement, room temperature, 25 mm parallel plate, gap: 0.5-0.6 mm, strain: 10%, Frequency: a 0.1~50rad / s.
【0050】 [0050]
[化粧品原料の調製] [Preparation of cosmetics raw materials]
化粧品原料(A)〜(D)を次のようにして調製した。 Cosmetic raw material (A) ~ (D) was prepared as follows. これらの化粧品原料の特性を表1に示した。 The properties of these cosmetics raw materials shown in Table 1.
[参考例1] [Reference Example 1]
粘度400mPa・sの分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルポリシロキサン18.8重量部、粘度30mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体(ケイ素原子結合水素原子の含有量=0.5重量%)1.2重量部、粘度100mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン80重量部を混合して架橋性シリコーン組成物を調製した。 Dimethylpolysiloxane with both molecular chain terminals blocked with dimethylvinylsiloxy groups 18.8 parts by weight of a viscosity 400 mPa · s, both molecular terminals with trimethylsiloxy groups dimethylsiloxane-methylhydrogensiloxane copolymer with a viscosity 30 mPa · s (silicon-bonded content = 0.5 wt.%) 1.2 parts by weight of the hydrogen atoms to prepare a cross-linkable silicone composition by mixing both molecular chain terminals blocked by trimethylsiloxy groups dimethylpolysiloxane 80 parts by weight of a viscosity 100 mPa · s. 次いで、この架橋性シリコーン組成物に3重量%−ポリオキシエチレンノニルフェニルエーテル(HLB=13.1)水溶液53重量部を加えてコロイドミルにより乳化した後、さらに純水50重量部を加えて架橋性シリコーン組成物の水系エマルジョンを調製した。 Then, 3 wt% crosslinkable silicone composition - was emulsified by polyoxyethylene nonylphenyl ether colloid mill (HLB = 13.1) aqueous solution of 53 parts by weight by adding further pure water was added to 50 parts by weight of crosslinking the aqueous emulsion of sex silicone composition was prepared.
【0051】 [0051]
別に調製しておいた、白金の1,1−ジビニル−1,1,3,3−テトラメトキシジシロキサン錯体を主成分とする白金系触媒の水系エマルジョン(白金系触媒の平均粒径=0.05μm、白金金属濃度=0.05重量%)を、上記の架橋性シリコーン組成物の水系エマルジョンに、このエマルジョン中の分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルポリシロキサンに対して、白金金属が重量単位で20ppmとなる量、均一に混合して架橋性シリコーン組成物の水系エマルジョンとした。 Had been separately prepared, the average particle size = 0 of the aqueous emulsion (platinum catalyst platinum catalyst mainly composed of 1,1-divinyl-1,1,3,3-tetramethoxy disiloxane complex of platinum. 05Myuemu, platinum metal concentration = 0.05 wt%), the aqueous emulsion of the crosslinkable silicone composition, with respect dimethylpolysiloxane with both molecular chain terminals blocked with dimethylvinylsiloxy groups of the emulsion, of platinum metal by weight the amount to be 20ppm in the unit, and an aqueous emulsion of the crosslinkable silicone composition was uniformly mixed.
【0052】 [0052]
このエマルジョンを室温で1日間放置することにより、架橋性シリコーン組成物のヒドロシリル化架橋反応を行い、水中に分散しているシリコーンオイル液滴中に架橋シリコーン粒子を含有しているシリコーンオイルエマルジョンを調製し、これを化粧品原料(A)とした。 By standing at room temperature for one day the emulsion performs hydrosilylation crosslinking reaction of the crosslinkable silicone composition, the silicone oil emulsion containing crosslinked silicone particles in drops of silicone oil dispersed in water preparation and, which was used as a cosmetic raw material (a).
【0053】 [0053]
次に、このエマルジョンを直径5cmのアルミ皿に移して、ドラフト内で3日間風乾することにより水を除去して、シリコーンオイルと架橋シリコーン粒子からなるシリコーンオイル組成物を調製した。 Then transferred to the emulsion in an aluminum dish with a diameter of 5 cm, to remove water by 3 days air dry in a fume hood, to prepare a silicone oil composition of silicone oil and crosslinked silicone particles. このシリコーンオイル組成物はクリーム状であった。 The silicone oil composition was a cream-like. このシリコーンオイル組成物を実体顕微鏡で観察したところ、シリコーンオイル中に架橋シリコーン粒子が均一に分散しており、この架橋シリコーン粒子の形状が球状であることがわかった。 The observation of the silicone oil composition under a stereoscopic microscope, crosslinked silicone particles in silicone oil is uniformly dispersed, the shape of the crosslinked silicone particles were found to be spherical.
【0054】 [0054]
[参考例2] [Reference Example 2]
参考例1において、粘度100mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン80重量部の代わりに、粘度6mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン80重量部を用いた以外は参考例1と同様にして、架橋性シリコーン組成物の水系エマルジョンを調製した。 Reference Example 1 in place of the both molecular chain terminals blocked by trimethylsiloxy groups dimethylpolysiloxane 80 parts by weight of a viscosity 100 mPa · s, with both molecular chain terminals blocked by trimethylsiloxy groups dimethylpolysiloxane 80 parts by weight of a viscosity 6 mPa · s otherwise in the same manner as in reference example 1, to prepare an aqueous emulsion of the crosslinkable silicone composition. このエマルジョンを参考例1と同様にしてヒドロシリル化架橋反応を行い、水中に分散しているシリコーンオイル液滴中に架橋シリコーン粒子を含有しているシリコーンオイルエマルジョンを調製した。 The emulsion in the same manner as in Reference Example 1 performs hydrosilylation crosslinking reaction, thereby preparing a silicone oil emulsion containing crosslinked silicone particles in drops of silicone oil dispersed in water.
【0055】 [0055]
次に、このエマルジョンを参考例1と同様にして水を除去して、シリコーンオイルと架橋シリコーン粒子からなるシリコーンオイル組成物を調製し、これを化粧品原料(B)とした。 Then, the emulsion in the same manner as in Reference Example 1 to remove the water, a silicone oil composition of silicone oil and crosslinked silicone particles was prepared, which was used as cosmetic raw material (B). このシリコーンオイル組成物はクリーム状であった。 The silicone oil composition was a cream-like. このシリコーンオイル組成物を実体顕微鏡で観察したところ、シリコーンオイル中に架橋シリコーン粒子が均一に分散しており、この架橋シリコーン粒子の形状が球状であることがわかった。 The observation of the silicone oil composition under a stereoscopic microscope, crosslinked silicone particles in silicone oil is uniformly dispersed, the shape of the crosslinked silicone particles were found to be spherical.
【0056】 [0056]
[参考例3] [Reference Example 3]
粘度1,000mPa・sの分子鎖両末端水酸基封鎖ジメチルポリシロキサン(水酸基の含有量=1.3重量%)100重量部、粘度10mPa・sの分子鎖両末端トリメチルシロキシ基封鎖メチルハイドロジェンポリシロキサン(ケイ素原子結合水素原子の含有量=1.5重量%)10重量部、粘度1,000mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン50重量部を均一に混合して混合物(I)を調製した。 Viscosity 1,000 mPa · s in capped at both molecular terminals with hydroxyl groups dimethylpolysiloxane (hydroxyl content = 1.3 weight%) 100 parts by weight, both molecular chain terminals by trimethylsiloxy viscosity 10 mPa · s siloxy group methylhydrogenpolysiloxane capped (silicon atom content of the bonded hydrogen atoms = 1.5 wt%) 10 parts by weight, both molecular chain terminals by trimethylsiloxy viscosity 1,000 mPa · s siloxy group-blocked dimethylpolysiloxane 50 parts by weight of uniformly mixed to mixture (I ) was prepared.
【0057】 [0057]
また、粘度1,000mPa・sの分子鎖両末端水酸基封鎖ジメチルポリシロキサン(水酸基の含有量=1.3重量%)100重量部、粘度1,000mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン50重量部、およびジブチル錫ジオクテート1.5重量部を均一に混合して混合物(II)を調製した。 The molecular chain terminal hydroxyl dimethylpolysiloxane having a viscosity of 1,000 mPa · s (hydroxyl content = 1.3 weight%) 100 parts by weight, both molecular chain terminals by trimethylsiloxy viscosity 1,000 mPa · s siloxy group-blocked dimethyl polysiloxane 50 parts by weight, and dibutyltin dioctoate 1.5 parts by weight evenly mixed to the mixture (II) was prepared.
【0058】 [0058]
この混合物(I)と混合物(II)を重量比1:1で均一に混合した後、これにタージトールTMN−6(ユニオンカーバイド社製、トリメチルノナノールのエチレンオキサイド付加物)5重量%とイオン交換水1,700重量部の混合物を加えてコロイドミルにより乳化した。 The mixture (I) a mixture (II) weight ratio of 1: After uniformly mixed in 1, this Tergitol TMN-6 (Union Carbide Co., an ethylene oxide adduct of trimethyl nonanol) 5 wt% and ion exchange It added a mixture of water 1,700 parts by weight was emulsified by a colloid mill. この乳化物をスプレードライヤー(入り口温度:300℃、出口温度:100℃)で噴霧して、水を除去したところ、収率98%で架橋シリコーン粒子を得ることができた。 The emulsion was spray dryer (inlet temperature: 300 ° C., outlet temperature: 100 ° C.) was sprayed in, where the water was removed, it was possible to obtain a cross-linked silicone particles in 98% yield. これを化粧品原料(C)とした。 This was used as a cosmetic raw material (C). この架橋シリコーン粒子はゴム状であり、その形状は球状であった。 The crosslinked silicone particles are rubber-like, and the shape was spherical. また、この架橋シリコーン粒子からのシリコーンオイルのブリードは観察されなかった。 Further, bleeding of silicone oil from the crosslinked silicone particles was observed.
【0059】 [0059]
[参考例4] [Reference Example 4]
プラネタリーミキサーに、粘度5mPa・sの分子鎖両末端ビニルメチルシロキシ基封鎖ジメチルポリシロキサン44.5重量部、粘度20mPa・sの分子鎖両末端トリメチルシロキシ基封鎖メチルハイドロジェンポリシロキサン(ケイ素原子結合水素原子の含有量=1.5重量%)100重量部、粘度6mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン758重量部を混合した後、これに塩化白金酸の2重量%−イソパノール溶液を0.5重量部添加して架橋性シリコーン組成物を調製した。 A planetary mixer, with both molecular chain terminals vinylmethylsiloxy groups dimethylpolysiloxane 44.5 parts by weight of the viscosity 5 mPa · s, with both molecular chain terminals blocked with trimethylsiloxy groups methylhydrogenpolysiloxane (silicon-bonded viscosity 20 mPa · s content = 1.5 wt%) 100 parts by weight of the hydrogen atom, was mixed with both molecular chain terminals blocked by trimethylsiloxy groups dimethylpolysiloxane 758 parts by weight of a viscosity 6 mPa · s, this 2 wt% of chloroplatinic acid - Isopanoru solution was added 0.5 parts by weight to prepare a cross-linkable silicone composition. この架橋性シリコーン組成物を70〜80℃に加熱しながら、2時間攪拌することにより、架橋性シリコーン組成物のヒドロシリル化架橋反応を行い、やわらかなシリコーン組成物を調製した。 While heating the crosslinkable silicone composition in 70 to 80 ° C., followed by stirring for 2 hours, subjected to hydrosilylation crosslinking reaction of the crosslinkable silicone composition was prepared soft silicone composition. このシリコーン組成物を3ロールによりせん断力下で混練したところ、ペースト状のシリコーン組成物を調製した。 It was kneaded under shearing force the silicone composition by 3 rolls to prepare a paste-like silicone composition. これを化粧品原料(D)とした。 This was used as a cosmetic raw material (D). このシリコーン組成物を実体顕微鏡で観察したところ、シリコーンオイル中に不定形状の架橋シリコーン粒子が分散していたが、その分散は不均一であり、この架橋シリコーン粒子の粒径は約100〜500μmと大きいことがわかった。 Observation of the silicone composition under a stereoscopic microscope, although cross-linked silicone particles of irregular shape in the silicone oil was dispersed, the dispersion is a heterogeneous, particle size of the crosslinked silicone particles is about 100~500μm big it was found.
【0060】 [0060]
【表1】 [Table 1]
【0061】 [0061]
[化粧品の製造方法および化粧品について] [About the cosmetics of the method of manufacturing and cosmetics]
化粧品を次のようにして調製して、その特性を評価した。 The cosmetics was prepared in the following manner, and its characteristics were evaluated.
[化粧品の指への感触] [Feeling to cosmetics finger]
パネラー10人に化粧品を使用してもらい、化粧品の感触が良好であると感じた人数が8〜10人である場合を○、これが4〜7人である場合を△、また、これが3人以下である場合を×として評価した。 Panelists to 10 people asked to use the cosmetics, the case number of people feel of cosmetics was felt to be good is 8 to 10 people ○, the case this is a 4 to 7 people △, also, this is 3 or fewer It was evaluated the case is as ×.
[化粧品の肌への感触] [Feel to the cosmetic skin]
パネラー10人に化粧品を使用してもらい、化粧品の感触が良好であると感じた人数が8〜10人である場合を○、これが4〜7人である場合を△、また、これが3人以下である場合を×として評価した。 Panelists to 10 people asked to use the cosmetics, the case number of people feel of cosmetics was felt to be good is 8 to 10 people ○, the case this is a 4 to 7 people △, also, this is 3 or fewer It was evaluated the case is as ×.
[化粧品中の架橋粒子の分散状態] [State of dispersion of crosslinked particles in cosmetics]
化粧品をガラス板に薄く塗布して、化粧品中の架橋シリコーン粒子の粒子径を光学顕微鏡により観察して、この粒子径が10μm以下である架橋シリコーン粒子の比率、10μmをこえ、50μm以下である架橋シリコーン粒子の比率、50μmをこえる架橋シリコーン粒子の比率をそれぞれ求めることにより、化粧品中の架橋シリコーン粒子の分散性を評価した。 Cosmetics and thinly coated on a glass plate, a particle size of crosslinked silicone particles in the cosmetic was observed with an optical microscope, the ratio of the cross-linked silicone particles the particle size is 10 [mu] m or less, exceeded 10 [mu] m, is 50μm or less crosslinked by determining the ratio of the silicone particles, the ratio of the crosslinked silicone particles exceeding 50μm respectively, to evaluate the dispersibility of the crosslinked silicone particles in cosmetics.
【0062】 [0062]
[実施例1] [Example 1]
化粧品原料(A)52重量部、p−メトキシ桂皮酸オクチル5重量部、α−モノイソステアリルグリセリルエーテルポリオキシエチレンソルビタンモノオレイン酸エステル1重量部、ミツロウ2重量部、ラノリン2重量部、スクワラン10重量部、流動パラフィン10重量部、精製水19重量部、防腐剤適量、および香料適量をホモディスパーにより2500rpmで3分間撹拌して乳液状化粧品を調製した。 Cosmetic raw material (A) 52 parts by weight, p- octyl methoxycinnamate 5 parts by weight, alpha-mono-isostearyl glyceryl ether polyoxyethylene sorbitan monooleate, 1 part by weight of beeswax, 2 parts by weight of lanolin 2 parts by weight, squalane 10 parts, liquid paraffin 10 parts by weight, purified water 19 parts by weight, to prepare an emulsified cosmetic was stirred 3 min preservative qs, and perfume qs by homodisper at 2500 rpm. この化粧品の評価結果を表2に示した。 The evaluation results of this cosmetics is shown in Table 2.
【0063】 [0063]
[実施例2] [Example 2]
化粧品原料(B)52重量部、p−メトキシ桂皮酸オクチル5重量部、α−モノイソステアリルグリセリルエーテルポリオキシエチレンソルビタンモノオレイン酸エステル1重量部、ミツロウ2重量部、ラノリン2重量部、スクワラン10重量部、流動パラフィン10重量部、精製水19重量部、防腐剤適量、および香料適量をホモディスパーにより2500rpmで3分間撹拌して乳液状化粧品を調製した。 Cosmetic raw material (B) 52 parts by weight, p- octyl methoxycinnamate 5 parts by weight, alpha-mono-isostearyl glyceryl ether polyoxyethylene sorbitan monooleate, 1 part by weight of beeswax, 2 parts by weight of lanolin 2 parts by weight, squalane 10 parts, liquid paraffin 10 parts by weight, purified water 19 parts by weight, to prepare an emulsified cosmetic was stirred 3 min preservative qs, and perfume qs by homodisper at 2500 rpm. この化粧品の評価結果を表2に示した。 The evaluation results of this cosmetics is shown in Table 2.
【0064】 [0064]
[比較例1] [Comparative Example 1]
化粧品原料(C)3重量部、架橋シリコーン粒子の4倍量となる、粘度100mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサンのエマルジョン(濃度50重量%)12重量部、24重量部、p−メトキシ桂皮酸オクチル5重量部、α−モノイソステアリルグリセリルエーテルポリオキシエチレンソルビタンモノオレイン酸エステル1重量部、ミツロウ2重量部、ラノリン2重量部、スクワラン10重量部、流動パラフィン10重量部、精製水54重量部、防腐剤適量、および香料適量をホモディスパーにより2500rpmで3分間撹拌して乳液状化粧品を調製した。 Cosmetic raw material (C) 3 parts by weight, crosslinking becomes 4 times the amount of silicone particles, both molecular terminals trimethyl viscosity 100 mPa · s siloxy group-blocked dimethylpolysiloxane emulsion (concentration 50 wt%) 12 parts by weight, 24 parts by weight , p- octyl methoxycinnamate 5 parts by weight, alpha-1 part by weight mono-isostearyl glyceryl ether polyoxyethylene sorbitan monooleate, beeswax 2 parts by weight, 2 parts by weight of lanolin, squalane, 10 parts by weight of liquid paraffin 10 parts by weight , parts by weight of purified water 54 were prepared emulsified cosmetic was stirred 3 min preservative qs, and perfume qs by homodisper at 2500 rpm. この化粧品の評価結果を表2に示した。 The evaluation results of this cosmetics is shown in Table 2.
【0065】 [0065]
【表2】 [Table 2]
【0066】 [0066]
[実施例3] [Example 3]
化粧品原料(B)40重量部、シリコーン処理酸化チタン1重量部、p−メトキシ桂皮酸オクチル5重量部、粘度20mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン10重量部、ポリオキシエチレン(40モル付加物)硬化ヒマシ油3重量部、スクワラン30重量部、グリセリン5重量部、ミツロウ3重量部、防腐剤適量、香料適量、および精製水適量をヘンシェルミキサーにより1500rpmで5分間撹拌してクリーム状化粧品を調製した。 Cosmetic raw material (B) 40 parts by weight, the silicone treated titanium oxide 1 part by weight, p- octyl methoxycinnamate 5 parts by weight, both molecular chain terminals blocked by trimethylsiloxy groups dimethylpolysiloxane 10 parts by weight of a viscosity 20 mPa · s, polyoxyethylene 3 parts by weight (40 mol adduct) hydrogenated castor oil, squalane, 30 parts by weight of glycerin, 5 parts by weight of beeswax 3 parts by weight, preservative qs, stirred for 5 minutes perfume qs, and purified water appropriate amount by a Henschel mixer at 1500rpm a creamy cosmetics were prepared. この化粧品の評価結果を表3に示した。 The evaluation results of this cosmetics is shown in Table 3.
【0067】 [0067]
[比較例2] [Comparative Example 2]
化粧品原料(D)20重量部、シリコーン処理酸化チタン1重量部、p−メトキシ桂皮酸オクチル5重量部、粘度20mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン10重量部、ポリオキシエチレン(40モル付加物)硬化ヒマシ油3重量部、スクワラン30重量部、グリセリン5重量部、ミツロウ3重量部、防腐剤適量、香料適量、および精製水適量をヘンシェルミキサーにより1500rpmで5分間撹拌してクリーム状化粧品を調製した。 Cosmetic raw material (D) 20 parts by weight, the silicone treated titanium oxide 1 part by weight, p- octyl methoxycinnamate 5 parts by weight, both molecular chain terminals blocked by trimethylsiloxy groups dimethylpolysiloxane 10 parts by weight of a viscosity 20 mPa · s, polyoxyethylene 3 parts by weight (40 mol adduct) hydrogenated castor oil, squalane, 30 parts by weight of glycerin, 5 parts by weight of beeswax 3 parts by weight, preservative qs, stirred for 5 minutes perfume qs, and purified water appropriate amount by a Henschel mixer at 1500rpm a creamy cosmetics were prepared. この化粧品の評価結果を表3に示した。 The evaluation results of this cosmetics is shown in Table 3.
【0068】 [0068]
【表3】 [Table 3]
【0069】 [0069]
[実施例4] [Example 4]
化粧品原料(B)14重量部、1,3−ブチレングリコール2重量部、エタノール50重量部、ポリエーテル変性シリコーンオイル(東レ・ダウコーニング・シリコーン株式会社製のSH3771)1重量部、プロピレングリコール4重量部、ポリオキシエチレン(15モル付加物)ノニルエーテル1重量部、シリコーン処理酸化チタン1重量部、防腐剤微量、香料微量、および精製水適量をヘンシェルミキサーにより1500rpmで5分間撹拌して水性化粧品を調製した。 Cosmetic raw material (B) 14 parts by weight, 1,3-butylene glycol 2 parts by weight of ethanol 50 parts by weight, the polyether-modified silicone oil (Dow Corning Toray Silicone Co., Ltd. SH3771) 1 part by weight of propylene glycol 4 wt parts of polyoxyethylene (15 mol adduct) nonyl ether, 1 part by weight, the silicone treated titanium oxide 1 part by weight, a preservative trace, perfume trace, and the purified water qs Henschel mixer and stirred for 5 minutes at 1500rpm aqueous cosmetic It was prepared. この化粧品の評価結果を表4に示した。 The evaluation results of this cosmetics is shown in Table 4.
【0070】 [0070]
[比較例3] [Comparative Example 3]
化粧品原料(C)1重量部、粘度100mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサンのエマルジョン(濃度50重量%)2重量部、精製水4重量部、1,3−ブチレングリコール2重量部、エタノール50重量部、ポリエーテル変性シリコーンオイル(東レ・ダウコーニング・シリコーン株式会社製のSH3771)1重量部、プロピレングリコール4重量部、ポリオキシエチレン(15モル付加物)オイルエーテル1重量部、シリコーン処理酸化チタン1重量部、防腐剤微量、香料微量、および精製水適量をヘンシェルミキサーにより1500rpmで5分間撹拌して水性化粧品を調製した。 Cosmetic raw material (C) 1 part by weight, both molecular chain terminals by trimethylsiloxy viscosity 100 mPa · s siloxy group-blocked dimethylpolysiloxane emulsion (concentration 50 wt%), 2 parts by weight of purified water, 4 parts by weight of 1,3-butylene glycol 2 parts, ethanol 50 parts by weight, 1 part by weight (SH3771 by Toray Dow Corning silicone Co., Ltd.) polyether-modified silicone oil, propylene glycol 4 parts by weight of polyoxyethylene (15 mol adduct) oil ether 1 part by weight , silicone-treated titanium oxide 1 part by weight, to prepare an aqueous cosmetic and stirred for 5 minutes at 1500rpm by preservatives trace, perfume trace, and purified water qs a Henschel mixer. この化粧品の評価結果を表4に示した。 The evaluation results of this cosmetics is shown in Table 4.
【0071】 [0071]
【表4】 [Table 4]
【0072】 [0072]
[実施例5] [Example 5]
参考例1で調製した化粧品原料(A)を金属皿に厚さ5mmに広げて、1週間、室温で風乾することにより、シリコーンオイル中に架橋シリコーン粒子が均一に分散しているペ−スト状のシリコーンオイル組成物を調製した。 Spread cosmetic material prepared in Reference Example 1 (A) to a thickness of 5mm in the metal dish 1 week, by air drying at room temperature, Bae crosslinked silicone particles in silicone oil are homogeneously dispersed - strike shaped the silicone oil composition was prepared. このシリコーン組成物を化粧品原料(A')とした。 The silicone composition was cosmetic raw material (A '). この化粧品原料(A')の105℃、30分加熱した場合の加熱減量は0.2重量%であった。 The 105 ° C. of cosmetic raw material (A '), the heat loss after heating 30 min was 0.2 wt%.
【0073】 [0073]
化粧品原料(A')10重量部、デカメチルシクロペンタシロキサン10重量部、シリコーン処理二酸化チタン10重量部、および適量の香料をヘンシェルミキサーで混合し、これにシリコーン処理亜鉛華5重量部、シリコーン処理タルク55重量部、シリコーン処理顔料と適量の香料を混合して頬紅を調製した。 Cosmetic raw material (A ') 10 parts by weight, 10 parts by weight of decamethylcyclopentasiloxane, 10 parts by weight of silicone treated titanium dioxide, and an appropriate amount of fragrance were mixed in a Henschel mixer, to which silicone treated zinc oxide 5 parts by weight, silicone treated talc 55 parts by weight, to prepare a rouge by mixing a silicone treated pigment and an appropriate amount of flavor. この頬紅の特性を表5に示した。 The characteristics of the rouge are shown in Table 5.
【0074】 [0074]
[比較例4] [Comparative Example 4]
実施例5において、化粧品原料(A')の代わりに化粧品原料(D)を使用した以外は実施例5と同様にして頬紅を調製した。 In Example 5, except for using cosmetic raw material (D) instead of cosmetic raw material (A ') was prepared rouge in the same manner as in Example 5. この頬紅の特性を表5に示した。 The characteristics of the rouge are shown in Table 5.
【0075】 [0075]
【表5】 [Table 5]
【0076】 [0076]
[実施例6] [Example 6]
参考例2で調製した化粧品原料(B)100重量部と平均粒子径が4μmであるシリコーンゴム粉末(東レ・ダウコーニング・シリコーン社製のトレフィルE-506C)10重量部をプラネタリーミキサーで混合した後、50℃で減圧して水を除去して、均一なペースト状シリコーンオイル組成物を調製した。 It was mixed cosmetic raw material (B) a silicone rubber powder (produced by Dow Corning Toray Silicone Co. Trefil E-506C) 10 parts by weight of average particle size of 4μm and 100 parts by weight of the prepared in Reference Example 2 in a planetary mixer after, to remove in vacuo at 50 ° C. water to prepare a homogeneous paste-like silicone oil composition. このペースト状シリコーンオイル組成物は105℃で30分間加熱した後の加熱減量が0.3重量%以下であった。 The pasty silicone oil compositions heating loss after heating at 105 ° C. 30 minutes was 0.3% by weight or less. このペースト状シリコーンオイル組成物40重量部、セリサイト10重量部、シリコーン処理二酸化チタン10重量部、シリコーン処理ベンガラ1.5重量部、シリコーン処理黄色酸化鉄4重量部、シリコーン処理黒色酸化鉄0.3重量部、アリストワックス4重量部、カルナバロウ1.3重量部、スクワラン33重量部、セスキオレイン酸ソルビタン1重量部、カオリン3重量部、および適量の香料をヘンシェルミキサーで混合してファンデーションを調製した。 The pasty silicone oil composition 40 parts by weight, sericite 10 parts by weight, 10 parts by weight of silicone treated titanium dioxide, silicone-treated red iron oxide 1.5 parts by weight, silicone-treated yellow iron oxide, 4 parts by weight of silicone treated black iron oxide 0. 3 parts by weight, Aristo wax 4 parts by weight, carnauba wax 1.3 parts by weight, squalane 33 parts by weight, sorbitan 1 part by weight sesquioleate, kaolin 3 parts by weight, and was prepared foundation by mixing an appropriate amount of perfume in a Henschel mixer . このファンデーションの特性を表6に示した。 The properties of the foundation shown in Table 6.
【0077】 [0077]
[比較例5] [Comparative Example 5]
実施例6において、ペースト状シリコーンオイル組成物の代わりに化粧品原料(D)を同量配合した以外は実施例6と同様にしてファンデーションを調製した。 In Example 6, except that a cosmetic raw material (D) was the same amount blended instead of pasty silicone oil composition was prepared foundation in the same manner as in Example 6. このファンデ−ションの特性を表6に示した。 The van - the characteristics of Deployment shown in Table 6.
【0078】 [0078]
【表6】 [Table 6]
*なお、比較例5での架橋シリコーン粒子の分散状況には、他の化粧品原料として配合したシリコーンゴム粉末(E−506C)も含まれている。 * Note that the dispersion status of the crosslinked silicone particles in Comparative Example 5, other silicone rubber powder (E-506C) formulated as a cosmetic raw material is also included.
【0079】 [0079]
[毛髪化粧品原料の調製] [Preparation of hair cosmetics raw materials]
毛髪化粧品原料(E)〜(J)を次のようにして調製した。 Hair cosmetic raw material (E) ~ a (J) was prepared in the following manner. これらの毛髪化粧品原料の特性を表7に示した。 The properties of these hair cosmetics raw materials shown in Table 7.
[参考例5] [Reference Example 5]
粘度400mPa・sの分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルポリシロキサン15.7重量部、粘度30mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体(ケイ素原子結合水素原子の含有量=0.5重量%)1.0重量部、粘度20mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン83.3重量部を混合して架橋性シリコーン組成物を調製した。 Dimethylpolysiloxane with both molecular chain terminals blocked with dimethylvinylsiloxy groups 15.7 parts by weight of a viscosity 400 mPa · s, both molecular terminals with trimethylsiloxy groups dimethylsiloxane-methylhydrogensiloxane copolymer with a viscosity 30 mPa · s (silicon-bonded content = 0.5 wt.%) 1.0 parts by weight of the hydrogen atom, prepared by mixing 83.3 parts by weight both molecular chain terminals blocked by trimethylsiloxy groups dimethylpolysiloxane having a viscosity of 20 mPa · s crosslinkable silicone composition did. 次いで、この架橋性シリコーン組成物に3重量%−ポリオキシエチレンノニルフェニルエーテル(HLB=13.1)水溶液53重量部を加えてコロイドミルにより乳化した後、さらに純水50重量部を加えて架橋性シリコーン組成物の水系エマルジョンを調製した。 Then, 3 wt% crosslinkable silicone composition - was emulsified by polyoxyethylene nonylphenyl ether colloid mill (HLB = 13.1) aqueous solution of 53 parts by weight by adding further pure water was added to 50 parts by weight of crosslinking the aqueous emulsion of sex silicone composition was prepared.
【0080】 [0080]
別に調製しておいた、白金の1,1−ジビニル−1,1,3,3−テトラメトキシジシロキサン錯体を主成分とする白金系触媒の水系エマルジョン(白金系触媒の平均粒径=0.05μm、白金金属濃度=0.05重量%)を、上記の架橋性シリコーン組成物の水系エマルジョンに、このエマルジョン中の分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルポリシロキサンに対して、白金金属が重量単位で20ppmとなる量、均一に混合して、架橋性シリコーン組成物の水系エマルジョンとした。 Had been separately prepared, the average particle size = 0 of the aqueous emulsion (platinum catalyst platinum catalyst mainly composed of 1,1-divinyl-1,1,3,3-tetramethoxy disiloxane complex of platinum. 05Myuemu, platinum metal concentration = 0.05 wt%), the aqueous emulsion of the crosslinkable silicone composition, with respect dimethylpolysiloxane with both molecular chain terminals blocked with dimethylvinylsiloxy groups of the emulsion, of platinum metal by weight the amount to be 20ppm in units, and uniformly mixed to obtain a water-based emulsion of the crosslinkable silicone composition.
【0081】 [0081]
このエマルジョンを室温で1日間放置することにより、架橋性シリコーン組成物のヒドロシリル化架橋反応を行い、水中に分散しているシリコーンオイル液滴中に架橋シリコーン粒子を含有しているシリコーンオイルエマルジョンを調製し、これを毛髪化粧品原料(E)とした。 By standing at room temperature for one day the emulsion performs hydrosilylation crosslinking reaction of the crosslinkable silicone composition, the silicone oil emulsion containing crosslinked silicone particles in drops of silicone oil dispersed in water preparation and, which was used as a hair cosmetic raw material (E).
【0082】 [0082]
次に、このエマルジョンを直径5cmのアルミ皿に移して、ドラフト内で3日間風乾することにより水を除去して、シリコーンオイルと架橋シリコーン粒子からなるシリコーンオイル組成物を調製した。 Then transferred to the emulsion in an aluminum dish with a diameter of 5 cm, to remove water by 3 days air dry in a fume hood, to prepare a silicone oil composition of silicone oil and crosslinked silicone particles. このシリコーンオイル組成物はクリーム状であった。 The silicone oil composition was a cream-like. このシリコーンオイル組成物を実体顕微鏡で観察したところ、シリコーンオイル中に架橋シリコーン粒子が均一に分散しており、この架橋シリコーン粒子の形状が球状であることがわかった。 The observation of the silicone oil composition under a stereoscopic microscope, crosslinked silicone particles in silicone oil is uniformly dispersed, the shape of the crosslinked silicone particles were found to be spherical.
【0083】 [0083]
[参考例6] [Reference Example 6]
参考例5において、粘度20mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン83.3重量部の代わりに、デカメチルペンタシロキサン80重量部と粘度2000万mPa・s分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン3.3重量部とからなり、粘度が300mP・sである混合物83.3重量部を用いた以外は参考例5と同様にして架橋性シリコーン組成物の水系エマルジョンを調製した。 Reference Example 5, instead of 83.3 parts by both molecular chain terminals blocked by trimethylsiloxy groups dimethylpolysiloxane having a viscosity of 20 mPa · s, decamethylpentasiloxane 80 parts by weight and the viscosity 20 million mPa · s at both molecular terminals with trimethylsiloxy consists of a group-blocked dimethylpolysiloxane 3.3 part by weight, the viscosity is except for using mixture 83.3 parts by weight of 300mP · s to prepare an aqueous emulsion of the crosslinkable silicone composition in the same manner as in reference example 5 . このエマルジョンを参考例5と同様にしてヒドロシリル化架橋反応を行い、水中に分散しているシリコーンオイル液滴中に架橋シリコーン粒子を含有するシリコーンオイルエマルジョンを調製した。 The emulsion in the same manner as in Reference Example 5 performs hydrosilylation crosslinking reaction, the silicone oil emulsion containing crosslinked silicone particles in drops of silicone oil dispersed in water was prepared.
【0084】 [0084]
次に、このエマルジョンを参考例5と同様にして水を除去して、シリコーンオイルと架橋シリコーン粒子からなるシリコーンオイル組成物を調製し、これを毛髪化粧品原料(F)とした。 Then, the emulsion in the same manner as in Reference Example 5 to remove the water, a silicone oil composition of silicone oil and crosslinked silicone particles was prepared, which was used as hair cosmetic material (F). このシリコーンオイル組成物はクリーム状であった。 The silicone oil composition was a cream-like. このシリコーンオイル組成物を実体顕微鏡で観察したところ、シリコーンオイル中に架橋シリコーン粒子が均一に分散しており、この架橋シリコーン粒子の形状が球状であることがわかった。 The observation of the silicone oil composition under a stereoscopic microscope, crosslinked silicone particles in silicone oil is uniformly dispersed, the shape of the crosslinked silicone particles were found to be spherical.
【0085】 [0085]
[参考例7] [Reference Example 7]
粘度400mPa・sの分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルシロキサン・メチルビニルシロキサン共重合体(ケイ素原子結合ビニル基の含有量=1.18重量%)15.0重量部、粘度50mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体(ケイ素原子結合水素原子の含有量=0.44重量%)1.7重量部、粘度20mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン83.3重量部を混合して架橋性シリコーン組成物を調製した。 Both molecular terminals with dimethylvinylsiloxy groups dimethylsiloxane-methylvinylsiloxane copolymer having a viscosity of 400 mPa · s (silicon-bonded vinyl content = 1.18 wt%) 15.0 parts by weight, a viscosity of 50 mPa · s both molecular terminals with trimethylsiloxy groups dimethylsiloxane-methylhydrogensiloxane copolymer (content of silicon-bonded hydrogen atoms = 0.44 wt%) 1.7 parts by weight, a viscosity of 20 mPa · s both molecular terminals trimethyl to prepare a crosslinkable silicone composition by mixing siloxy group-blocked dimethylpolysiloxane 83.3 parts by weight. 次いで、この架橋性シリコーン組成物に3重量%−ポリオキシエチレンノニルフェニルエーテル(HLB=13.1)水溶液53重量部を加えてコロイドミルにより乳化した後、さらに純水50重量部を加えて架橋性シリコーン組成物の水系エマルジョンを調製した。 Then, 3 wt% crosslinkable silicone composition - was emulsified by polyoxyethylene nonylphenyl ether colloid mill (HLB = 13.1) aqueous solution of 53 parts by weight by adding further pure water was added to 50 parts by weight of crosslinking the aqueous emulsion of sex silicone composition was prepared.
【0086】 [0086]
別に調製しておいた、白金の1,1−ジビニル−1,1,3,3−テトラメトキシジシロキサン錯体を主成分とする白金系触媒の水系エマルジョン(白金系触媒の平均粒径=0.05μm、白金金属濃度=0.05重量%)を、上記の架橋性シリコーン組成物の水系エマルジョンに、このエマルジョン中の分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルポリシロキサンに対して、白金金属が重量単位で20ppmとなる量、均一に混合して、架橋性シリコーン組成物の水系エマルジョンとした。 Had been separately prepared, the average particle size = 0 of the aqueous emulsion (platinum catalyst platinum catalyst mainly composed of 1,1-divinyl-1,1,3,3-tetramethoxy disiloxane complex of platinum. 05Myuemu, platinum metal concentration = 0.05 wt%), the aqueous emulsion of the crosslinkable silicone composition, with respect dimethylpolysiloxane with both molecular chain terminals blocked with dimethylvinylsiloxy groups of the emulsion, of platinum metal by weight the amount to be 20ppm in units, and uniformly mixed to obtain a water-based emulsion of the crosslinkable silicone composition.
【0087】 [0087]
このエマルジョンを室温で1日間放置することにより、架橋性シリコーン組成物のヒドロシリル化架橋反応を行い、水中に分散しているシリコーンオイル液滴中に架橋シリコーン粒子を含有するシリコーンオイルエマルジョンを調製し、これを毛髪化粧品原料(G)とした。 By leaving the emulsion at room temperature for 1 day, subjected to hydrosilylation crosslinking reaction of the crosslinkable silicone composition, the silicone oil emulsion containing crosslinked silicone particles in drops of silicone oil dispersed in water was prepared, This was used as a hair cosmetic raw material (G).
【0088】 [0088]
次に、このエマルジョンを直径5cmのアルミ皿に移して、ドラフト内で3日間風乾することにより水を除去して、シリコーンオイルと架橋シリコーン粒子をからなるシリコーンオイル組成物を調製した。 Then transferred to the emulsion in an aluminum dish with a diameter of 5 cm, to remove water by 3 days air dry in a fume hood, to prepare a silicone oil composition consisting of the silicone oil and crosslinked silicone particles. このシリコーンオイル組成物はクリーム状であった。 The silicone oil composition was a cream-like. このシリコーンオイル組成物を実体顕微鏡で観察したところ、シリコーンオイル中に架橋シリコーン粒子が均一に分散しており、この架橋シリコーン粒子の形状が球状であることがわかった。 The observation of the silicone oil composition under a stereoscopic microscope, crosslinked silicone particles in silicone oil is uniformly dispersed, the shape of the crosslinked silicone particles were found to be spherical.
【0089】 [0089]
[参考例8] [Reference Example 8]
粘度400mPa・sの分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルポリシロキサン94.0重量部、粘度30mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体(ケイ素原子結合水素原子の含有量=0.5重量%)6.0重量部を混合して架橋性シリコーン組成物を調製した。 94.0 parts by weight of dimethylpolysiloxane with both molecular chain terminals blocked with dimethylvinylsiloxy groups with a viscosity 400 mPa · s, both molecular terminals with trimethylsiloxy groups dimethylsiloxane-methylhydrogensiloxane copolymer with a viscosity 30 mPa · s (silicon-bonded the content of hydrogen atoms = 0.5 wt%) were mixed 6.0 parts by weight to prepare a cross-linkable silicone composition. 次いで、この架橋性シリコーン組成物に3重量%−ポリオキシエチレンノニルフェニルエーテル(HLB=13.1)水溶液53重量部を加えてコロイドミルにより乳化した後、さらに純水50重量部を加えて架橋性シリコーン組成物の水系エマルジョンを調製した。 Then, 3 wt% crosslinkable silicone composition - was emulsified by polyoxyethylene nonylphenyl ether colloid mill (HLB = 13.1) aqueous solution of 53 parts by weight by adding further pure water was added to 50 parts by weight of crosslinking the aqueous emulsion of sex silicone composition was prepared.
【0090】 [0090]
別に調製しておいた、白金の1,1−ジビニル−1,1,3,3−テトラメトキシジシロキサン錯体を主成分とする白金系触媒の水系エマルジョン(白金系触媒の平均粒径=0.05μm、白金金属濃度=0.05重量%)を、上記の架橋性シリコーン組成物の水系エマルジョンに、このエマルジョン中の分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルポリシロキサンに対して、白金金属が重量単位で20ppmとなる量、均一に混合して、架橋性シリコーン組成物の水系エマルジョンとした。 Had been separately prepared, the average particle size = 0 of the aqueous emulsion (platinum catalyst platinum catalyst mainly composed of 1,1-divinyl-1,1,3,3-tetramethoxy disiloxane complex of platinum. 05Myuemu, platinum metal concentration = 0.05 wt%), the aqueous emulsion of the crosslinkable silicone composition, with respect dimethylpolysiloxane with both molecular chain terminals blocked with dimethylvinylsiloxy groups of the emulsion, of platinum metal by weight the amount to be 20ppm in units, and uniformly mixed to obtain a water-based emulsion of the crosslinkable silicone composition.
【0091】 [0091]
このエマルジョンを室温で1日間放置することにより、架橋性シリコーン組成物のヒドロシリル化架橋反応を行い、水中に架橋シリコーン粒子が分散している水分散液を調製し、これを毛髪化粧品原料(H)とした。 By standing at room temperature for one day the emulsion, crosslinkable performed hydrosilylation crosslinking reaction of silicone composition, an aqueous dispersion of crosslinked silicone particles in water are dispersed is prepared, which hair cosmetic raw material (H) and the.
【0092】 [0092]
次に、このエマルジョンを直径5cmのアルミ皿に移して、ドラフト内で3日間風乾することにより水を除去すると、架橋シリコーン粒子が得られた。 Then transferred to the emulsion in an aluminum dish with a diameter of 5 cm, the water is removed by air drying for 3 days in a fume hood, crosslinked silicone particles were obtained. これをトルエン抽出し、抽出液を分析したところ、この架橋シリコーン粒子のシリコーンオイル含有量は5重量%以下であった。 It is extracted toluene, where extract was analyzed, silicone oil content of the crosslinked silicone particles was 5% by weight or less.
【0093】 [0093]
[参考例9] [Reference Example 9]
プラネタリーミキサーに、粘度5mPa・sの分子鎖両末端ビニルジメチルシロキシ基封鎖ジメチルポリシロキサン44.5重量部、粘度20mPa・sの分子鎖両末端トリメチルシロキシ基封鎖メチルハイドロジェンポリシロキサン(ケイ素原子結合水素原子の含有量=1.5重量%)100重量部、粘度6mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン758重量部を混合した後、これに塩化白金酸の2重量%−イソパノール溶液を0.5重量部添加して架橋性シリコーン組成物を調製した。 A planetary mixer, with both molecular chain terminals vinyldimethylsiloxy-dimethylpolysiloxane 44.5 parts by weight of the viscosity 5 mPa · s, with both molecular chain terminals blocked with trimethylsiloxy groups methylhydrogenpolysiloxane (silicon-bonded viscosity 20 mPa · s content = 1.5 wt%) 100 parts by weight of the hydrogen atom, was mixed with both molecular chain terminals blocked by trimethylsiloxy groups dimethylpolysiloxane 758 parts by weight of a viscosity 6 mPa · s, this 2 wt% of chloroplatinic acid - Isopanoru solution was added 0.5 parts by weight to prepare a cross-linkable silicone composition. この架橋性シリコーン組成物を70〜80℃に加熱しながら、2時間攪拌することにより、架橋性シリコーン組成物のヒドロシリル化架橋反応を行い、やわらかなシリコーン組成物を調製した。 While heating the crosslinkable silicone composition in 70 to 80 ° C., followed by stirring for 2 hours, subjected to hydrosilylation crosslinking reaction of the crosslinkable silicone composition was prepared soft silicone composition. このシリコーンオイル組成物を3ロールによりせん断力下で混練して、ペースト状のシリコーンオイル組成物を調製した。 The silicone oil composition was kneaded under a shearing force by a three roll mill to prepare a paste-like silicone oil composition. これを毛髪化粧品原料(I)とした。 This was used as a hair cosmetic raw material (I). このシリコーンオイル組成物を実体顕微鏡で観察したところ、シリコーンオイル中に不定形状の架橋シリコーン粒子が分散していたが、その分散は不均一であり、この架橋シリコーン粒子の粒径は約100〜500μmと大きいことがわかった。 Observation of the silicone oil composition under a stereoscopic microscope, although cross-linked silicone particles of irregular shape in the silicone oil was dispersed, the dispersion is a heterogeneous, particle size of the crosslinked silicone particles is about 100~500μm it was found a large and.
【0094】 [0094]
[参考例10] [Reference Example 10]
粘度が100万mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ポリジメチルシロキサン360重量部と、粘度が20mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ポリジメチルシロキサン240重量部を均一に混合し、これにポリオキシエチレンラウリルエーテル(HLB:10.5)15重量部、ポリオキシエチレンラウリルエーテル(HLB:16.7)35重量部、純水40重量部を加えて乳化した後、さらに純水310重量部を加えてシリコーンオイルエマルジョンを調製し、これを毛髪化粧品原料(J)とした。 Viscosity mixed 1,000,000 and mPa · s at both molecular chain terminals blocked by trimethylsiloxy groups polydimethylsiloxane 360 ​​parts by weight, the viscosity is uniformly 240 parts by weight both molecular chain terminals blocked by trimethylsiloxy groups polydimethylsiloxane 20 mPa · s, of polyoxyethylene lauryl ether (HLB: 10.5) 15 parts by weight of polyoxyethylene lauryl ether (HLB: 16.7) 35 parts by weight, were emulsified by adding pure water 40 parts by weight, more pure water 310 the silicone oil emulsion was prepared by adding parts by weight, which was used as a hair cosmetic material (J).
【0095】 [0095]
【表7】 [Table 7]
【0096】 [0096]
[実施例7〜9、比較例6、7] [Examples 7-9, Comparative Examples 6 and 7]
参考例で調製した毛髪化粧品原料(E)、(F)、(G)、(H)、および(J)を用いて表8に示した組成のシャンプーを調製した。 Hair cosmetic material prepared in Reference Example (E), were prepared (F), (G), a shampoo having the composition shown in Table 8 using (H), and (J). このシャンプーを使用して毛髪を洗浄し、洗浄後の感触向上性、およびくし通り性向上率を次の通り評価して、それらの結果を表8に示した。 The hair was washed with this shampoo, feel enhancing after washing, and combing improvement rate was evaluated as follows. The results are shown in Table 8.
[毛髪の感触向上評価法] [Feeling improved evaluation method of hair]
長さ20cmの毛髪束10gを2.5重量%−ポリオキシエチレンラウリルエーテル硫酸ナトリウム水溶液にて洗浄後、温水ですすぎ、25℃の条件下で12時間乾燥し、毛髪の前処理を行った。 2.5% by weight of the hair bundle 10g Length 20 cm - was washed with sodium polyoxyethylene lauryl ether sulfate aqueous solution, rinsed with warm water, then dried 12 hours under the condition of 25 ° C., pretreated hair. この前処理した毛髪を30秒間水に浸漬した後、水切りし、これをシャンプー1gにて1分間洗浄後、温水によるすすぎを20秒間にて2回行い水切り後その感触を評価した。 After soaking the pre-treated hair to water for 30 seconds, drained, washed 1 minute it at shampoo 1g, to evaluate its feel after draining is performed twice with a rinsing with hot water for 20 seconds. その後、25℃の条件下にて12時間乾燥し、その感触を評価した。 Then, it dried for 12 hours under the conditions of 25 ℃, to evaluate its feel.
[毛髪のくし通り性向上率評価法] [Combing of hair improvement rate evaluation method]
長さ20cmの毛髪束10gを2.5重量%−ポリオキシエチレンエーテル硫酸ナトリウム水溶液にて洗浄後、温水ですすぎ、25℃の条件下で12時間乾燥する。 2.5% by weight of the hair bundle 10g Length 20 cm - was washed with polyoxyethylene ether sodium sulfate aqueous solution, rinsed with warm water and dried under conditions of 25 ° C. 12 hours. これを30秒間水に浸漬後タオルでくるみ20kgf/314cm 2の圧力下で5秒間水切りし、引っかかりがなくなるまでブラッシングして毛髪の前処理を行った。 This was 5 seconds drained under a pressure of walnuts 20 kgf / 314 cm 2 by a dip after towel water for 30 seconds, then brushed until caught disappeared pretreated hair. この前処理した毛髪をシャンプー1gにて1分間洗浄後、温水によるすすぎを20秒間にて2回行った後、タオルでくるみ20kgf/314cm 2の圧力下で5秒間水切りし、引っかかりがなくなるまでブラッシングした。 After this washing pretreated hair for 1 minute at shampoo 1g, after twice rinsing with warm water at 20 seconds, and 5 seconds drained under a pressure of walnuts 20 kgf / 314 cm 2 with a towel, brushing until caught disappears did.
次に、テスター産業社製の引張り万能試験機を用いて移動台にくしをセットし、処理した毛髪の一端を固定し、この毛髪束を移動台のくしに通し、移動台を200mm/minで移動させた時の引張り力の最大値を測定した。 Then, set the comb to the mobile platform using the Tester Sangyo tensile universal testing machine, one end of the treated hair was fixed, through the hair bundle moving base comb, the moving table at 200 mm / min the maximum value of the tensile force when the moved was measured. また、これを前処理のみの毛髪、およびシャンプー処理後の毛髪に対してそれぞれ測定し、次の計算式により、くし通り性向上率を求めた。 It also measures the respective hair pretreatment only, and with respect to the hair after shampooing, by the following equation to determine the combing improvement rate.
くし通り性向上率(%)=100×(A−B)/A Combing improvement rate (%) = 100 × (A-B) / A
A=前処理のみの毛髪の引張り力B=シャンプー処理毛髪の引張り力【0097】 The tensile force of the tension force B = shampooing the hair of the hair of A = pre-treatment only [0097]
[比較例8] [Comparative Example 8]
実施例5において、毛髪化粧品原料(E)の代わりに毛髪化粧品原料(I)を用いた以外は同様にしてシャンプーを調製しようとしたが、毛髪化粧品原料(I)の分散性が悪く、凝集粒子(100〜200μm)が発生し、均一なシャンプーを調製できなかった。 In Example 5, but except for the use of hair cosmetic raw material (I) in place of hair cosmetic raw material (E) tried to prepare a shampoo in the same manner, poor dispersibility of the hair cosmetic raw material (I), the aggregated particles (100-200 [mu] m) is generated, it was unable to prepare a uniform shampoo.
【0098】 [0098]
【表8】 [Table 8]
【0099】 [0099]
[実施例10、比較例9、10] [Example 10, Comparative Examples 9 and 10]
毛髪化粧品原料(E)、および(H)をそれぞれ2重量%と精製水98重量%を混合してリンスを調製した。 Hair cosmetic raw material (E), and (H) were respectively prepared rinsed by mixing 98 wt% 2 wt% with purified water. このリンスを使用して毛髪の指への感触、処理毛髪への架橋シリコーン粒子の付着量を次のように評価し、それらの結果を表3に示した。 Feel of using this rinsing hair to the finger, the adhesion amount of crosslinked silicone particles to treated hair was evaluated as follows. The results are shown in Table 3. また、比較例として、毛髪化粧品原料(E)の代わりに精製水を増量したリンスを調製して同様に評価し、その結果を表9に示した。 As a comparative example, the rinse was increased purified water in place of hair cosmetic raw material (E) was prepared and evaluated in the same manner, and the results are shown in Table 9.
[毛髪の指への感触] [Feel of the hair to the finger]
長さ20cmの毛髪束10gを2.5重量%−ポリオキシエチレンラウリルエーテル硫酸ナトリウム水溶液にて洗浄後、温水ですすぎ、25℃の条件下で12時間乾燥して毛髪の前処理を行った。 Tress 10g of 2.5 wt% of the length 20 cm - was washed with sodium polyoxyethylene lauryl ether sulfate aqueous solution, rinsed with warm water, pretreated hair was dried for 12 hours under the condition of 25 ° C.. 次に、この毛髪束を上記のリンスにそれぞれ浸漬したのち、25℃の条件下で12時間乾燥して毛髪を処理した。 Next, after the tresses were immersed respectively in rinse described above and treat the hair and dried under conditions of 25 ° C. 12 hours. この毛髪のすべりとなめらかさを次のように評価した。 The slip and smoothness of the hair was evaluated in the following manner.
◎:大変良好○:良好△:どちらともいえない×:悪い[毛髪への架橋シリコーン粒子の付着量] ◎: Very good ○: good △: either the × not say: [adhesion amount of cross-linked silicone particles to the hair] bad
リンスした毛髪を電子顕微鏡で観察し、毛髪の長さ100μmの中に付着された架橋シリコーン粒子の個数を毛髪の側面を片側からだけの観察して、カウントした。 The rinsed hair was observed with an electron microscope, the number of the deposited crosslinked silicone particles in the length 100μm hair was only observed side of the hair from one side, it was counted.
【0100】 [0100]
【表9】 [Table 9]
【0101】 [0101]
次に、有機オイルエマルジョンの平均粒径や安定性、架橋シリコーン粒子の平均粒径、および有機オイル組成物の特性を次のようにして求めた。 Next, obtained by the average particle size and stability of the organic oil emulsion, the average particle size of the crosslinked silicone particles, and the characteristics of the organic oil composition as follows.
[有機オイルエマルジョンの平均粒径] Average particle size of the organic oil emulsion]
有機オイルエマルジョンをレーザー回折式粒度分布測定器(堀場製作所のLA−500)により測定し、得られたメジアン径(累積分布の50%に相当する粒径)を平均粒径とした。 The organic oil emulsion was measured by a laser diffraction particle size distribution measuring apparatus (LA-500 of Horiba), resulting median diameter (particle diameter corresponding to 50% of cumulative distribution) was defined as the average particle diameter.
[有機オイルエマルジョンの安定性] Stability of the organic oil emulsions]
有機オイルエマルジョン180mLを225mLのガラスビン(深さ105mm、口径50mm)に密閉して、室温で1週間放置した。 The organic oil emulsion 180 mL 225 mL glass bottle (depth 105 mm, diameter 50 mm) was sealed in, and allowed to stand for one week at room temperature. 放置後、有機オイルエマルジョンから分離した水層の厚さを測定した。 After standing, to measure the thickness of separated aqueous layer from the organic oil emulsion.
[架橋シリコーン粒子の分散性] [Dispersibility of the crosslinked silicone particles]
有機オイルエマルジョンをガラス板上で風乾し、実体顕微鏡下で架橋シリコーン粒子の形状、凝集状態、および分布について観察した。 The organic oil emulsion air dried on a glass plate, and observed the shape of the crosslinked silicone particles under a stereoscopic microscope, aggregation state, and the distribution. すべての架橋シリコーン粒子が1次粒子として分散していれば○とし、数100μmの凝集粒子や500μm以上の1次粒子があれば×とし、これらの間を△とした。 Until all of the crosslinked silicone particles with ○ if dispersed as primary particles, and × if the number 100μm agglomerated particles and 500μm or more primary particles of were between these △ and.
[架橋シリコーン粒子の平均粒径] Average particle size of the crosslinked silicone particles]
有機オイルエマルジョンをガラス板上で風乾し、実体顕微鏡下で架橋シリコーン粒子を集めて試料を作成し、これを電子顕微鏡下で観察して、10個の粒子径から平均粒径を求めた。 The organic oil emulsion air dried on a glass plate, attracting crosslinked silicone particles under a stereoscopic microscope to create a sample which was observed under an electron microscope to determine the average particle size from 10 particle size.
[有機オイル組成物の粘弾性] [Viscoelastic organic oil composition]
有機オイルエマルジョンをアルミ皿に約10gとり、1週間、室温で風乾し、水分を除去した有機オイル組成物の貯蔵弾性率G'(×10 3 dyne/cm 2 )、損失弾性率G''(×10 3 dyne/cm 2 )、さらに損失正接tanδと複素粘度(η*)をARES粘弾性測定装置(Reometric Scientific社製)により測定した。 The organic oil emulsion takes about 10g on an aluminum dish, 1 week, air-dried at room temperature, the storage modulus G of the organic oil composition to remove water '(× 10 3 dyne / cm 2), the loss modulus G' '( × 10 3 dyne / cm 2) , it was measured by further loss tangent tanδ and the complex viscosity (eta *) of the ARES viscoelasticity measurement device (Reometric Scientific Inc.). なお、測定の条件は、室温、25mmパラレルプレート、ギャップ:0.5〜0.6mm、歪み:10%、振動数:0.1〜50rad/sである。 The conditions of the measurement, room temperature, 25 mm parallel plate, gap: 0.5-0.6 mm, strain: 10%, Frequency: a 0.1~50rad / s.
【0102】 [0102]
[化粧品原料の調製] [Preparation of cosmetics raw materials]
化粧品原料については、次のようにして調製した。 For the cosmetics raw materials, it was prepared in the following manner. また、この化粧品原料の特性を表10に示した。 In addition, the characteristics of the cosmetics raw materials shown in Table 10.
[参考例11] [Reference Example 11]
粘度400mPa・sの分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルシロキサン・メチルビニルシロキサン共重合体(ケイ素原子結合ビニル基の含有量=1.18重量%)9.01重量部、粘度50mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体(ケイ素原子結合水素原子の含有量=0.44重量%)0.99重量部、イソパラフィン(日本石油化学社製のアイソゾール400K、C 1634 )85重量部、粘度1,000万mPa・s分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン5重量部を混合して架橋性シリコーン組成物を調製した。 Both molecular terminals with dimethylvinylsiloxy groups dimethylsiloxane-methylvinylsiloxane copolymer having a viscosity of 400 mPa · s (silicon-bonded vinyl content = 1.18 wt%) 9.01 parts by weight, a viscosity of 50 mPa · s both molecular terminals with trimethylsiloxy groups dimethylsiloxane-methylhydrogensiloxane copolymer (content of silicon-bonded hydrogen atoms = 0.44 wt%) 0.99 parts by weight, isoparaffin (Nippon Petrochemicals Co. Isosol 400K was C 16 H 34) 85 parts by weight, a viscosity of 10 million mPa · s at both molecular terminals with trimethylsiloxy groups dimethylpolysiloxane 5 parts by weight of crosslinking silicone composition was prepared. 次いで、この架橋性シリコーン組成物に3重量%−ポリオキシエチレンノニルフェニルエーテル(HLB=13.1)水溶液30重量部を加えてコロイドミルにより乳化した後、さらに純水25重量部を加えて架橋性シリコーン組成物を含む有機オイルの水系エマルジョンを調製した。 Then, 3 wt% crosslinkable silicone composition - was emulsified by polyoxyethylene nonylphenyl ether colloid mill (HLB = 13.1) by adding an aqueous solution 30 parts by weight, further pure water was added to 25 parts by weight of crosslinking the aqueous emulsion of organic oils including sex silicone composition was prepared.
【0103】 [0103]
別に調製しておいた、白金の1,1−ジビニル−1,1,3,3−テトラメトキシジシロキサン錯体を主成分とする白金系触媒の水系エマルジョン(白金系触媒の平均粒径=0.05μm、白金金属濃度=0.05重量%)を、上記の架橋性シリコーン組成物を含む有機オイルの水系エマルジョンに、このエマルジョン中の分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルポリシロキサンに対して、白金金属が重量単位で20ppmとなる量(約1重量部)を均一に混合して、架橋性シリコーン組成物を含む有機オイルの水系エマルジョンとした。 Had been separately prepared, the average particle size = 0 of the aqueous emulsion (platinum catalyst platinum catalyst mainly composed of 1,1-divinyl-1,1,3,3-tetramethoxy disiloxane complex of platinum. 05Myuemu, platinum metal concentration = 0.05 wt%), the water-based emulsion of the organic oils containing the above-described crosslinkable silicone composition, with respect to both molecular terminals dimethylpolysiloxane of the emulsion siloxy group-blocked dimethylpolysiloxane, platinum metal mixed uniformly an amount (about 1 part by weight) as a 20ppm in weight units, and an aqueous emulsion of an organic oil containing cross-linkable silicone composition.
【0104】 [0104]
このエマルジョンを室温で1日間放置することにより、架橋性シリコーン組成物のヒドロシリル化架橋反応を行い、水中に分散している有機オイル液滴中に架橋シリコーン粒子を含有している有機オイルエマルジョンを調製し、これを化粧品原料(K)とした。 By leaving the emulsion at room temperature for 1 day, subjected to hydrosilylation crosslinking reaction of the crosslinkable silicone composition, an organic oil emulsion containing crosslinked silicone particles in an organic oil droplets dispersed in the water preparation and, which was used as a cosmetic raw material (K).
【0105】 [0105]
次に、このエマルジョンを直径5cmのアルミ皿に移して、ドラフト内で1週間風乾することにより水を除去してクリーム状の有機オイル組成物を得た。 Then transferred to the emulsion in an aluminum dish with a diameter of 5 cm, water was removed to obtain a creamy organic oil composition by 1 week air dry in a fume hood. この有機オイル組成物を実体顕微鏡で観察したところ、イソパラフィンと高粘度のシリコーンオイル中に架橋シリコーン粒子が均一に分散しており、架橋シリコーン粒子の形状が球状であることが確認された。 Observation of the organic oil composition under a stereoscopic microscope, crosslinked silicone particles in silicone oil of isoparaffin and high viscosity is uniformly dispersed, the shape of the crosslinked silicone particles were confirmed to be spherical.
【0106】 [0106]
[参考例12] [Reference Example 12]
粘度400mPa・sの分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルシロキサン・メチルビニルシロキサン共重合体(ケイ素原子結合ビニル基の含有量=1.18重量%)22.0重量部、粘度75mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体(ケイ素原子結合水素原子の含有量=0.05重量%)8.0重量部、イソパラフィン(日本石油化学社製のアイソゾール400K、C 1634 )80重量部を混合して架橋性シリコーン組成物を調製した。 Both molecular terminals with dimethylvinylsiloxy groups dimethylsiloxane-methylvinylsiloxane copolymer having a viscosity of 400 mPa · s (silicon-bonded vinyl content = 1.18 wt%) 22.0 parts by weight, a viscosity of 75 mPa · s both molecular terminals with trimethylsiloxy groups dimethylsiloxane-methylhydrogensiloxane copolymer (content of silicon-bonded hydrogen atoms = 0.05 wt%) 8.0 parts by weight, isoparaffin (Nippon Petrochemicals Co. Isosol 400K and the C 16 H 34) 80 parts by weight with crosslinkable silicone composition was prepared. 次いで、この架橋性シリコーン組成物に3重量%−ポリオキシエチレンノニルフェニルエーテル(HLB=13.1)水溶液30重量部を加えてコロイドミルにより乳化した後、さらに純水25重量部を加えて架橋性シリコーン組成物を含む有機オイルの水系エマルジョンを調製し、参考例11と同様にして有機オイルエマルジョンを調製。 Then, 3 wt% crosslinkable silicone composition - was emulsified by polyoxyethylene nonylphenyl ether colloid mill (HLB = 13.1) by adding an aqueous solution 30 parts by weight, further pure water was added to 25 parts by weight of crosslinking the aqueous emulsion of organic oils including sex silicone composition was prepared, preparing an organic oil emulsion in the same manner as in reference example 11. この有機オイルエマルジョンを化粧品原料(L)とした。 The organic oil emulsion was a cosmetic raw material (L).
【0107】 [0107]
次に、このエマルジョンを直径5cmのアルミ皿に移して、ドラフト内で1週間風乾することにより水を除去してクリーム状の有機オイル組成物を得た。 Then transferred to the emulsion in an aluminum dish with a diameter of 5 cm, water was removed to obtain a creamy organic oil composition by 1 week air dry in a fume hood. この有機オイル組成物を実体顕微鏡で観察したところ、イソパラフィン中に架橋シリコーン粒子が均一に分散しており、架橋シリコーン粒子の形状が球状であることが確認された。 Observation of the organic oil composition under a stereoscopic microscope, crosslinked silicone particles in isoparaffin is uniformly dispersed, the shape of the crosslinked silicone particles were confirmed to be spherical.
【0108】 [0108]
[参考例13] [Reference Example 13]
架橋シリコーン粒子(東レ・ダウコーニング・シリコーン社製のトレフィルE-506、平均粒径=4μm)15重量部とイソパラフィン(日本石油化学社製のアイソゾール400K、C 1634 )85重量部を攪拌・混合して、チクソ性を有するペースト状の有機オイル組成物を調製した。 Cross-linked silicone particles (manufactured by Dow Corning Toray Silicone Co., Trefil E-506, average particle diameter = 4 [mu] m) 15 parts by weight of isoparaffin (manufactured by Nippon Petrochemicals Co. Isosol 400K, C 16 H 34) stirred and 85 parts by weight by mixing, to prepare a paste-like organic oil composition having thixotropic properties. この有機オイル組成物に3重量%−ポリオキシエチレンノニルフェニルエーテル(HLB=13.1)水溶液53重量部を加えた後、さらに純水50重量部を加えて有機オイルエマルジョンを調製した。 The organic oil composition 3 wt% - after the addition of polyoxyethylene nonylphenyl ether (HLB = 13.1) aqueous solution of 53 parts by weight, to prepare an organic oil emulsion further pure water was added to 50 parts by weight. このエマルジョンを化粧品原料(M)とした。 The emulsion was a cosmetic raw material (M). この有機オイルエマルジョンの表面には、イソパラフィンで膨潤した架橋シリコーン粒子が凝集しており、不均一なものであった。 On the surface of the organic oil emulsion, swollen cross-linked silicone particles in isoparaffin are aggregated, was not uniform.
【0109】 [0109]
[参考例14] [Reference Example 14]
粘度100万mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン360重量部と粘度20mPa・sの分子鎖両末端トリメチルシロキシ基封鎖ジメチルポリシロキサン240重量部を均一に混合し、これにポリオキシエチレンラウリルエーテル(HLB=10.5)15重量部、ポリオキシエチレンラウリルエーテル(HLB=16.7)35重量部、および水40重量部を加えて混合し、さらに水310重量部を加えて混合してシリコーンオイルエマルジョンを調製した。 Viscosity 1,000,000 mPa · s at both molecular chain terminals blocked by trimethylsiloxy groups dimethylpolysiloxane 360 ​​parts by weight and viscosity of 20 mPa · s at both molecular terminals capped with trimethylsiloxy groups of dimethylpolysiloxane 240 parts by weight were uniformly mixed, poly thereto polyoxyethylene lauryl ether (HLB = 10.5) 15 parts by weight of polyoxyethylene lauryl ether (HLB = 16.7) 35 parts by weight, and 40 parts by weight of water was added to and mixed, further added 310 parts by weight of water mixed to prepare a silicone oil emulsion. このシリコーンオイルエマルジョンを化粧品原料(N)とした。 The silicone oil emulsion was cosmetic raw material (N).
【0110】 [0110]
【表10】 [Table 10]
なお、参考例13では架橋シリコーン粒子が凝集粒子となっていた(一次粒径は4μm)。 Incidentally, crosslinked silicone particles in Reference Example 13 has been a aggregated particles (primary particle size is 4 [mu] m).
【0111】 [0111]
[実施例11、12、比較例11] [Examples 11 and 12, Comparative Example 11]
表11に示した組成でホモディスパーにより2500rpmで3分間攪拌して、乳液状の皮膚化粧品を調製した。 The disperser in the composition shown in Table 11 and stirred for 3 minutes at 2500 rpm, to prepare a milky skin cosmetic. この皮膚化粧品を次のように評価して、その結果を表11に示した。 The skin cosmetic and evaluated as follows, and the results are shown in Table 11.
[皮膚化粧品の指への感触] [Feel to the skin cosmetics finger]
パネラー10人に化粧品を使用してもらい、皮膚化粧品の感触が良好であると感じた人数が8〜10人である場合を○、これが4〜7人である場合を△、また、これが3人以下である場合を×として評価した。 To 10 panelists asked to use the cosmetics, ○ the case number of people feel of skin cosmetics was felt to be good is 8 to 10 people, a case this is a 4 to 7 people △, also, this is 3 people It was evaluated the case is less than or equal to as ×.
[皮膚化粧品の肌への感触] [Feel to the skin cosmetics skin]
パネラー10人に化粧品を使用してもらい、皮膚化粧品の感触が良好であると感じた人数が8〜10人である場合を○、これが4〜7人である場合を△、また、これが3人以下である場合を×として評価した。 To 10 panelists asked to use the cosmetics, ○ the case number of people feel of skin cosmetics was felt to be good is 8 to 10 people, a case this is a 4 to 7 people △, also, this is 3 people It was evaluated the case is less than or equal to as ×.
[皮膚化粧品中の架橋シリコーン粒子の分散状態] [State of dispersion of crosslinked silicone particles in the skin cosmetics]
皮膚化粧品をガラス板に薄く塗布して、この皮膚化粧品中の架橋シリコーン粒子の粒子径を光学顕微鏡により観察して、この粒子径が10μm以下である架橋シリコーン粒子の比率、10μmをこえ、50μm以下である架橋シリコーン粒子の比率、50μmをこえる架橋シリコーン粒子の比率をそれぞれ求めることにより、この皮膚化粧品中の架橋シリコーン粒子の分散性を評価した。 Skin cosmetics thinly coated on a glass plate, the particle size of the crosslinked silicone particles in the skin in cosmetic and observed with an optical microscope, beyond a ratio of the crosslinked silicone particles the particle size is 10 [mu] m or less, a 10 [mu] m, 50 [mu] m or less the ratio of the crosslinked silicone particles is, by obtaining respective proportion of crosslinked silicone particles exceeding 50 [mu] m, were evaluated dispersibility of the crosslinked silicone particles in the skin cosmetic.
【0112】 [0112]
【表11】 [Table 11]
【0113】 [0113]
[実施例13、14、比較例12] [Examples 13 and 14, Comparative Example 12]
表12に示した組成でシャンプーを調製した。 Were prepared shampoo composition shown in Table 12. このシャンプーを次のように評価して、その結果を表12に示した。 The shampoo was evaluated as follows, and the results are shown in Table 12.
[毛髪の感触向上評価法] [Feeling improved evaluation method of hair]
長さ20cmの毛髪束10gを2.5重量%−ポリオキシエチレンラウリルエーテル硫酸ナトリウム水溶液にて洗浄後、温水ですすぎ、25℃の条件下で12時間乾燥し、毛髪の前処理を行った。 2.5% by weight of the hair bundle 10g Length 20 cm - was washed with sodium polyoxyethylene lauryl ether sulfate aqueous solution, rinsed with warm water, then dried 12 hours under the condition of 25 ° C., pretreated hair. この前処理した毛髪を30秒間水に浸漬した後、水切りし、これをシャンプー1gにて1分間洗浄後、温水によるすすぎを20秒間にて2回行い水切り後その感触を評価した。 After soaking the pre-treated hair to water for 30 seconds, drained, washed 1 minute it at shampoo 1g, to evaluate its feel after draining is performed twice with a rinsing with hot water for 20 seconds. その後、25℃の条件下にて12時間乾燥し、その感触を評価した。 Then, it dried for 12 hours under the conditions of 25 ℃, to evaluate its feel.
[毛髪のくし通り性向上率評価法] [Combing of hair improvement rate evaluation method]
長さ20cmの毛髪束10gを2.5重量%−ポリオキシエチレンエーテル硫酸ナトリウム水溶液にて洗浄後、温水ですすぎ、25℃の条件下で12時間乾燥する。 2.5% by weight of the hair bundle 10g Length 20 cm - was washed with polyoxyethylene ether sodium sulfate aqueous solution, rinsed with warm water and dried under conditions of 25 ° C. 12 hours. これを30秒間水に浸漬後タオルでくるみ20kgf/314cm 2の圧力下で5秒間水切りし、引っかかりがなくなるまでブラッシングして毛髪の前処理を行った。 This was 5 seconds drained under a pressure of walnuts 20 kgf / 314 cm 2 by a dip after towel water for 30 seconds, then brushed until caught disappeared pretreated hair. この前処理した毛髪をシャンプー1gにて1分間洗浄後、温水によるすすぎを20秒間にて2回行った後、タオルでくるみ20kgf/314cm 2の圧力下で5秒間水切りし、引っかかりがなくなるまでブラッシングした。 After this washing pretreated hair for 1 minute at shampoo 1g, after twice rinsing with warm water at 20 seconds, and 5 seconds drained under a pressure of walnuts 20 kgf / 314 cm 2 with a towel, brushing until caught disappears did.
次に、テスター産業社製の引張り万能試験機を用いて移動台にくしをセットし、処理した毛髪の一端を固定し、この毛髪束を移動台のくしに通し、移動台を200mm/minで移動させた時の引張り力の最大値を測定した。 Then, set the comb to the mobile platform using the Tester Sangyo tensile universal testing machine, one end of the treated hair was fixed, through the hair bundle moving base comb, the moving table at 200 mm / min the maximum value of the tensile force when the moved was measured. また、これを前処理のみの毛髪、およびシャンプー処理後の毛髪に対してそれぞれ測定し、次の計算式により、くし通り性向上率を求めた。 It also measures the respective hair pretreatment only, and with respect to the hair after shampooing, by the following equation to determine the combing improvement rate.
くし通り性向上率(%)=100×(A−B)/A Combing improvement rate (%) = 100 × (A-B) / A
A=前処理のみの毛髪の引張り力B=シャンプー処理毛髪の引張り力【0114】 The tensile force of the tension force B = shampooing the hair of the hair of A = pre-treatment only [0114]
【表12】 [Table 12]
【0115】 [0115]
[比較例13] [Comparative Example 13]
実施例13において、化粧品原料(K)の代わりに化粧品原料(M)を用いた以外は同様にしてシャンプーを調製しようとしたが、化粧品原料(M)の分散性が悪く、凝集粒子(100〜200μm)が発生し、均一なシャンプーを調製できなかった。 In Example 13, but except for using, instead of Cosmetic Ingredients of Cosmetic Ingredients (K) (M) tried to prepare a shampoo in the same manner, poor dispersibility of cosmetic raw material (M), the aggregated particles (100 200 [mu] m) is generated, it was unable to prepare a uniform shampoo.
【0116】 [0116]
【発明の効果】 【Effect of the invention】
本発明の化粧品原料は、化粧品中にシリコーンオイルまたは有機オイルと架橋シリコーン粒子を均一に分散させることができるという特徴がある。 Cosmetic raw material of the present invention is characterized in that it is possible to in cosmetics uniformly disperse the crosslinked silicone particles and the silicone oil or organic oil. また、本発明の化粧品は、この化粧品原料と他の化粧品原料とからなり、シリコーンオイルまたは有機オイルと架橋シリコーン粒子が均一に分散しており、指や肌への感触、伸び、および使用感が良好であり、また、ハネ毛や浮き毛、もつれやからまりを防止し、髪をまとまり易くできるとともに、べたつきのないさらさら感を付与することができるという特徴がある。 Further, the cosmetic of the invention consists of this cosmetic raw material and other cosmetic raw materials, and silicone oils or organic oils and crosslinked silicone particles are uniformly dispersed, feel to the fingers and skin, elongation, and feeling of use is good, also wings hairs and lifting hair to prevent tangling Ya from Mari, it is possible to easily grouped hair is characterized in that it is possible to impart silkiness without stickiness. さらに、本発明の化粧品の製造方法は、このような化粧品を効率よく製造することができるという特徴がある。 Further, the production method of the cosmetic of the present invention is characterized in that it is possible to produce good such cosmetic efficiency.

Claims (11)

  1. 非架橋性のシリコーンオイルまたは有機オイルを含有している架橋性シリコーン組成物 ( 但し、非架橋性のシリコーンオイルまたは有機オイルの含有量は、架橋性シリコーン組成物の架橋物がこの非架橋性のシリコーンオイルまたは有機オイルを保持し得る量をこえる量である。 ) を水中に分散させて架橋反応してなる、水中に分散している平均粒径0.1〜500μmのシリコーンオイルまたは有機オイルの液滴中に、平均粒径0.05〜100μmの球状の架橋シリコーン粒子(但し、架橋シリコーン粒子の粒径はシリコーンオイルまたは有機オイルの液滴の粒径より小さい。)を含有しているシリコーンオイルまたは有機オイルのエマルジョンからなる化粧品原料。 Non-crosslinkable silicone oil or crosslinkable silicone composition containing an organic oil (however, the content of the non-crosslinkable silicone oil or organic oil, the crosslinked product of the crosslinkable silicone composition of the non-crosslinked is an amount that exceeds the amount capable of retaining silicone oil or organic oil.) were dispersed in water by crosslinking reaction, the average particle size 0.1~500μm dispersed in water of the silicone oil or organic oil in the droplet, crosslinked silicone particles of spherical average particle size 0.05~100Myuemu (provided that the particle size of the crosslinked silicone particles is a particle size smaller than. the droplets of the silicone oil or organic oil) containing silicone cosmetic raw material made from the emulsion of oil or an organic oil.
  2. 非架橋性のシリコーンオイルまたは有機オイルの25℃における粘度が1〜100,000,000mPa・sであることを特徴とする、請求項記載の化粧品原料。 Wherein the viscosity at 25 ° C. of non-crosslinkable silicone oil or organic oil is 1~100,000,000mPa · s, cosmetic raw material according to claim 1, wherein.
  3. 架橋性シリコーン組成物がヒドロシリル化架橋反応型または縮合架橋反応型のものであることを特徴とする、請求項記載の化粧品原料。 Wherein the crosslinkable silicone composition is of the hydrosilation crosslinking reaction type or condensation crosslinking reaction type, according to claim 1, wherein the cosmetic raw material.
  4. 皮膚化粧品原料であることを特徴とする、請求項1乃至のいずれか1項に記載の化粧品原料。 Characterized in that it is a skin cosmetic material, cosmetic material according to any one of claims 1 to 3.
  5. 毛髪化粧品原料であることを特徴とする、請求項1乃至のいずれか1項に記載の化粧品原料。 Characterized in that it is a hair cosmetic material, cosmetic material according to any one of claims 1 to 3.
  6. 請求項1乃至いずれか1項に記載のエマルジョンから水を除去してなる、シリコーンオイルまたは有機オイル中に球状の架橋シリコーン粒子を分散しているオイル組成物からなることを特徴とする化粧品原料。 Cosmetic raw materials according to claim comprising removing water from the emulsion according to 1 to 3 any one, characterized by comprising the oil composition dispersed crosslinked silicone particles spherical in silicone oil or organic oil .
  7. 請求項1乃至のいずれか1項に記載の化粧品原料と他の化粧品原料とからなる化粧品。 Cosmetics comprising the cosmetic raw material and other cosmetic raw material according to any one of claims 1 to 3.
  8. 皮膚化粧品であることを特徴とする、請求項記載の化粧品。 It characterized in that it is a skin cosmetic, according to claim 7, wherein the cosmetic.
  9. 毛髪化粧品であることを特徴とする、請求項記載の化粧品。 Characterized in that it is a hair cosmetic according to claim 7, wherein the cosmetic.
  10. 請求項記載の化粧品原料と他の化粧品原料とからなる化粧品。 Claim 6, wherein the cosmetic raw material and other cosmetic raw material consisting of a cosmetic.
  11. 請求項1乃至のいずれか1項に記載の化粧品原料と他の化粧品原料を配合することを特徴とする化粧品の製造方法。 Cosmetic method of manufacturing, which comprises mixing the cosmetic raw material and other cosmetic raw material according to any one of claims 1 to 3.
JP07676799A 1998-06-23 1999-03-19 Cosmetics raw materials, cosmetics, and cosmetics manufacturing method Expired - Lifetime JP4025454B2 (en)