JP3639715B2 - Fine dispersion composition of wax and the hair cosmetic and polishes - Google Patents

Fine dispersion composition of wax and the hair cosmetic and polishes Download PDF

Info

Publication number
JP3639715B2
JP3639715B2 JP9406298A JP9406298A JP3639715B2 JP 3639715 B2 JP3639715 B2 JP 3639715B2 JP 9406298 A JP9406298 A JP 9406298A JP 9406298 A JP9406298 A JP 9406298A JP 3639715 B2 JP3639715 B2 JP 3639715B2
Authority
JP
Grant status
Grant
Patent type
Prior art keywords
wax
poe
fine dispersion
oil
surfactant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP9406298A
Other languages
Japanese (ja)
Other versions
JPH10324617A (en )
Inventor
康成 中間
義浩 塩島
孝之 大村
文則 春沢
Original Assignee
株式会社資生堂
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Grant date

Description

【0001】 [0001]
【発明の属する技術分野】 BACKGROUND OF THE INVENTION
本発明はワックスの微細分散組成物、特に安定性に優れ、かつ皮膚刺激の少ない安全性の良好なワックスの微細分散組成物およびそれを含有する毛髪化粧料ならびにつや出し剤に関する。 The present invention is a fine dispersion composition of wax, particularly excellent in stability, and fine dispersion composition of good wax less safe skin irritation and to a hair cosmetic composition and polish containing the same.
【0002】 [0002]
【従来の技術】 BACKGROUND OF THE INVENTION
ワックスは常温で固体ないし半固体の油分であり、その皮膜は撥水性を有するため、化粧品、塗料などの分野に広く用いられている。 Wax is an oily solid or semi-solid at room temperature, the coating for water-repellent cosmetics are widely used in the field of paints.
たとえば化粧品に用いる場合、ワックス自体をベースとして用いる場合もあるが、塗布部分のべたつきが著しくなり、またギラツキ等を生じることもあるため、各種エマルションとして用いることが多い。 For example, when used in cosmetics, there is a case of using a wax itself as the base, stickiness of the coating portion becomes remarkable, also because sometimes cause glare or the like, is often used as various emulsions.
ワックスを微細分散させる技術として、従来はたとえば特開平3−2112、特開平4−230616、特開平5−220383、特開平7−173025号などに示されるものがあった。 As a technique for wax finely dispersed, conventionally for example, JP-A 3-2112, JP-A-4-230616, JP-A-5-220383, there is one shown in such Japanese Unexamined Patent Publication No. 7-173025.
【0003】 [0003]
【発明が解決しようとする課題】 [Problems that the Invention is to Solve
しかしながら、これらに示されているものは、非イオン系又はアニオン系、あるいはカチオン系界面活性剤を用いて微細分散物を調製するものであり、非イオン界面活性剤単独では、皮膚刺激等安全性は良好なものの、温度により、系のHLBが変化し、経時安定性が損なわれる欠点がある。 However, what is shown in these, nonionic or anionic, or is intended to prepare a cationic surfactant with fine dispersion, the nonionic surfactant alone, skin irritation Safety although good, the temperature, HLB of the system is changed, there is a disadvantage that storage stability is impaired.
【0004】 [0004]
また、非イオン界面活性剤とアニオン界面活性剤との組合せやアニオン界面活性剤単独、あるいはカチオン界面活性剤単独で微細分散物を調製する場合においては、温度安定性は向上するものの、皮膚刺激等の安全性に対して問題が生じることが考えられる。 Further, when the combination or anionic surfactant alone and a nonionic surfactant and an anionic surfactant or a cationic surfactant alone, to prepare a fine dispersion, although improved temperature stability, skin irritation, etc. it is considered that the problem with respect to safety occurs.
本発明は前記従来技術の課題に鑑みなされたものであり、その目的は、広い温度範囲で安定であり、かつ皮膚刺激等、安全性の良好なワックスの微細分散組成物およびそれを含有する毛髪化粧料ならびにつや出し剤を提供することにある。 The present invention has been made in view of the problems of the prior art, the hair that purpose are stable over a wide temperature range, and skin irritation or the like, a fine dispersion composition of good wax safety and containing the same It is to provide a cosmetic as well as polish.
【0005】 [0005]
【課題を解決するための手段】 In order to solve the problems]
前記目的を達成するために本発明者らが鋭意検討を行ったところ、非イオン界面活性剤と両性界面活性剤を併用することにより、ワックスの微細分散組成物を調製することが可能であることを見出し、さらに本微細分散組成物は、安全性が高く、特に毛髪化粧料として利用すると調整力、毛髪の滑らかさ等に関し優れた特徴を持つこと及びつや出し剤としても優れていることを見出し、本発明を完成するに至った。 When the present inventors to achieve the above object has conducted extensive studies, it the combined use of nonionic surfactant and amphoteric surfactant, it is possible to prepare a fine dispersion composition of wax headings, further the fine dispersion composition has high safety, found to be excellent in particular the adjusting force used as hair cosmetics, as it and polish with superior characteristics relates smoothness, etc. of the hair, this has led to the completion of the present invention. すなわち、本発明にかかるワックスの微細分散組成物は、両性界面活性剤および/又は半極性界面活性剤と、非イオン界面活性剤と、 常温で固体ないし半固体の油分であるワックスと、水系分散媒とを含み、両性界面活性剤/(両性界面活性剤+非イオン界面活性剤)の重量比が0.03〜0.5であり、水系分散媒中にワックスが固体ないし半固体状で微細分散していることを特徴とする。 That is, a fine dispersion composition of wax according to the present invention, the amphoteric surfactant and / or semipolar surfactant, and a nonionic surfactant, a wax is oil solid or semi-solid at room temperature, an aqueous dispersion look containing a medium, the weight ratio of amphoteric surfactant / (amphoteric surfactant + nonionic surfactant) is 0.03 to 0.5, in an aqueous dispersion medium wax in solid or semi-solid characterized in that finely dispersed.
【0006】 [0006]
また、前記ワックス微細分散組成物においては、非イオン界面活性剤はHLBが6〜12であることが好適である。 Also, in the finely dispersed wax compositions, the nonionic surfactant is preferable that HLB is 6-12. また、本発明にかかるワックスの微細分散組成物においては、非イオン界面活性剤としてポリオキシエチレンポリオキシプロピレンアルキルエーテルを含むことが好適である。 Further, in the fine dispersion composition of wax according to the present invention, it is preferable to include a polyoxyethylene polyoxypropylene alkyl ether as the nonionic surfactant. また、前記ワックスの微細分散組成物においては、ポリオキシエチレンポリオキシプロピレンアルキルエーテルが下記一般式(1): Further, in the fine dispersion composition of the wax, polyoxyethylene polyoxypropylene alkyl ether is represented by the following general formula (1):
(化3) (Of 3)
および/または、下記一般式(2): And / or the following general formula (2):
(化4) (Of 4)
(ただし、Rは炭素数12〜24のアルキル基またはアルケニル基を表し、mは5≦m≦30、nは0<n≦5の範囲にある)で表されることが好適である。 (Wherein, R represents an alkyl or alkenyl group having 12 to 24 carbon atoms, m is 5 ≦ m ≦ 30, n is in the range of 0 <n ≦ 5) is preferable to be represented by. また、本発明にかかるワックス微細分散組成物においては、系をワックスの融点以上、可溶化温度範囲に加温した後、常温に冷却して得ることができる。 In the finely dispersed wax composition according to the present invention, it is possible system wax above the melting point, followed by heating to solubilize the temperature range, obtained by cooling to room temperature. また、本発明にかかるワックス微細分散組成物は、ワックスの融点以上で高剪断力乳化機を用いても調製することができる。 Also, finely dispersed wax composition according to the present invention can also be prepared using a high shear emulsifying machine with wax above the melting point. また、本発明にかかる毛髪化粧料は、前記ワックスの微細分散組成物を含むことを特徴とする。 Furthermore, hair cosmetic composition according to the present invention is characterized by comprising a fine dispersion composition of the wax. また、本発明にかかるつや出し剤は、前記ワックスの微細分散組成物を含むことを特徴とする。 Further, polish of the present invention is characterized by comprising a fine dispersion composition of the wax.
【0007】 [0007]
【発明の実施の形態】 DETAILED DESCRIPTION OF THE INVENTION
以下、本発明の実施形態をさらに詳細に説明する。 Hereinafter, further detailed description of the embodiments of the present invention.
固形ワックス Solid wax
本発明においてワックスとは常温にて固形の油分を意味し、具体的にはミツロウ、キャンデリラロウ、綿ロウ、カルナウバロウ、ベイベリーロウ、イボタロウ、鯨ロウ、モンタンロウ、ヌカロウ、ラノリン、カポックロウ、モクロウ、酢酸ラノリン、液状ラノリン、サトウキビロウ、ラノリン脂肪酸イソプロピル、ラウリン酸ヘキシル、還元ラノリン、ジョジョバロウ、硬質ラノリン、セラックロウ、ビースワックス、マイクロクリスリンワックス、パラフィンワックス、POEラノリンアルコールエーテル、POEラノリンアルコールアセテート、POEコレステロールエーテル、ラノリン脂肪酸ポリエチレングリコール、脂肪酸クリセリド、硬化ヒマシ油、ワセリン、POE水素添加ラノリンアルコールエーテル等がある。 Means oil solid at room temperature and the wax in the present invention, specifically beeswax, candelilla wax, cotton wax, carnauba wax, bayberry wax, insect wax, whale wax, montan wax, bran wax, lanolin, kapok wax, Japan wax, lanolin acetate , liquid lanolin, sugar cane wax, lanolin fatty acid isopropyl, hexyl laurate, reduced lanolin, jojoba wax, hard lanolin, shellac wax, beeswax, micro Chris phosphorus wax, paraffin wax, POE lanolin alcohol ether, POE lanolin alcohol acetate, POE cholesterol ether , lanolin fatty acid polyethylene glycol, fatty acid Kuriserido, hydrogenated castor oil, vaseline, a POE hydrogenated lanolin alcohol ether.
なお、これらのワックスは混合して用いることが可能であり、他の固形状あるいは液状油分などを混合しても常温において固形である範囲で使用可能である。 Incidentally, these waxes it is possible to use a mixture, can be used in the range is also solid at room temperature by mixing and other solid or liquid oil.
【0008】 [0008]
このような油性成分としては、次のようなものが挙げられる。 Such oily components include the following.
液体油脂としては、アボガド油、ツバキ油、タートル油、マカデミアナッツ油、トウモロコシ油、ミンク油、オリーブ油、ナタネ油、卵黄油、ゴマ油、パーシック油、小麦胚芽油、サザンカ油、ヒマシ油、アマニ油、サフラワー油、綿実油、エノ油、大豆油、落花生油、茶実油、カヤ油、コメヌカ油、シナギリ油、日本キリ油、ホホバ油、胚芽油、トリグリセリン、トリオクタン酸グリセリン、テトラオクタン酸ペンタエリスリット、トリイソパルミチン酸グリセリン等がある。 As liquid oil, avocado oil, camellia oil, turtle oil, macadamia nut oil, corn oil, mink oil, olive oil, rapeseed oil, egg yolk oil, sesame oil, persic oil, wheat germ oil, sasanqua oil, castor oil, linseed oil, Sa safflower oil, cottonseed oil, perilla oil, soybean oil, peanut oil, tea seed oil, kaya oil, rice bran oil, Chinese tung oil, Japanese tung oil, jojoba oil, germ oil, triglycerol, trioctanoate glycerin, tetra-octane acid pentaerythritol , there is a triisopalmitate acid glycerin and the like.
【0009】 [0009]
固体油脂としては、カカオ脂、ヤシ油、硬化ヤシ油、パーム油、パーム核油、モクロウ核油、硬化油等がある。 As solid fat, cacao butter, coconut oil, hardened coconut oil, palm oil, palm kernel oil, Japan wax kernel oil, hardened oil and the like.
炭化水素油としては、流動パラフィン、オゾケライト、スクワレン、プリスタン、パラフィン、スクワラン等がある。 Examples of hydrocarbon oils include liquid paraffin, ozokerite, squalene, pristane, paraffin, there is squalane.
【0010】 [0010]
非イオン界面活性剤 Nonionic surfactant
本発明において非イオン界面活性剤が必須であり、好適な非イオン界面活性剤のHLBは6〜12、特に好適なHLBは7〜11である。 Nonionic surfactant in the present invention are mandatory, HLB of suitable non-ionic surfactants are 6-12, particularly preferred HLB is 7-11.
このような非イオン界面活性剤としては、POEソルビタンモノオレエート、POEソルビタンモノステアレート、POEソルビタンテトラオレエート等のPOEソルビタン脂肪酸エステル類、POEソルビットモノラウレート、POEソルビットモノオレエート、POEソルビットペンタオレエート、POEソルビットモノステアレートなどのPOEソルビット脂肪酸エステル類、POEグリセリンモノステアレート、POEグリセリンモノイソステアレート、POEグリセリントリイソステアレートなどのPOEグリセリン脂肪酸エステル類、POEモノオレエート、POEジステアレート、POEジオレエート、ジステアリン酸エチレングリコールなどのPOE脂肪酸エステル類、POEラウリルエーテル、POEオレイルエーテル、 Such nonionic surfactants, POE sorbitan monooleate, POE sorbitan monostearate, POE sorbitan fatty acid esters such as POE sorbitan tetraoleate, POE sorbit monolaurate, POE sorbit monooleate, POE sorbit pentaoleate, POE POE sorbit fatty acid esters such as sorbitol monostearate, POE glycerin monostearate, POE glycerin monoisostearate, POE glycerin fatty acid esters such as POE glycerin triisostearate, POE monooleate, POE distearate, POE dioleate, POE fatty acid esters, POE lauryl ether, such as ethylene glycol distearate, POE oleyl ether, OEステアリルエーテル、POEベヘニルエーテル、POE2−オクチルドデシルエーテル、POEコレスタノールエーテル等のPOEアルキルエーテル類、POEオクチルフェニルエーテル、POEノニルフェニルエーテル、POEジノニルフェニルエーテル等のPOEアルキルフェニルエーテル類、プルロックなどのプルロニック類、テトロニック等のテトラPOE・テトラPOPエチレンジアミン縮合物類、POEヒマシ油、POE硬化ヒマシ油、POE硬化ヒマシ油モノイソステアレート、POE硬化ヒマシ油トリイソステアレート、POE硬化ヒマシ油モノピログルタミン酸モノイソステアリン酸ジエステル、POE硬化ヒマシ油マレイン酸などのPOEヒマシ油硬化ヒマシ油誘導体、POEソルビットミツロウ等のPOEミツ OE stearyl ether, POE behenyl ether, POE2- octyl dodecyl ether, POE alkyl ethers such as POE cholestanol ether, POE octylphenyl ether, POE nonylphenyl ether, POE alkylphenyl ethers such as POE dinonyl phenyl ether, Pururokku etc. pluronics, tetra POE · tetra POP ethylenediamine condensates such as tetronic, POE castor oil, POE hardened castor oil, POE hydrogenated castor oil monoisostearate, POE hydrogenated castor oil triisostearate, POE hydrogenated castor oil mono pyroglutamic acid monoisostearate diester, POE castor oil hydrogenated castor oil derivatives such as POE castor oil maleate, POE Mitsu such POE sorbitol beeswax ウ・ラノリン誘導体、ヤシ油脂肪酸ジエタノールアミド、ラウリン酸モノエタノールアミド、脂肪酸イソプロパノールアミドなどのアルカノールアミド、POEプロピレングリコール脂肪酸エステル、POEアルキルアミン、POE脂肪酸アミド、ショ糖脂肪酸エステル、POEノニルフェニルホルムアルデヒド縮合物、アルキルエトキシジメチルアミンオキシド、トリオレイルリン酸などが挙げられる。 Woo lanolin derivatives, coconut oil fatty acid diethanolamide, lauric acid monoethanolamide, alkanolamides such as fatty acid isopropanol amide, POE propylene glycol fatty acid esters, POE alkyl amine, POE fatty acid amides, sucrose fatty acid esters, POE nonylphenyl formaldehyde condensate alkyl ethoxy dimethylamine oxide, such as trioleyl phosphate.
【0011】 [0011]
また、非イオン界面活性剤として、ポリオキシエチレンポリオキシプロピレンアルキルエーテルを用いると、同じオキシエチレン鎖長のポリオキシエチレンアルキルエーテルと比較して、調製されたワックス微細分散物の経時安定性がよく、経時で微細粒子の凝集等による外観の変化(透明性の低下)や分散粒子のクリーミングが改善されるのでより好適である。 Further, as the non-ionic surfactant, the use of polyoxyethylene polyoxypropylene alkyl ether, as compared to the same oxyethylene chain length polyoxyethylene alkyl ethers, temporal stability of the prepared wax microdispersion well , is more preferable since creaming over time a change in appearance due to aggregation of very fine particles (decrease in transparency) and dispersed particles can be improved.
上記ポリオキシエチレンポリオキシプロピレンアルキルエーテルとしては、 As the polyoxyethylene polyoxypropylene alkyl ether,
【化5】 [Of 5]
および/または【化6】 And / or ## of 6]
(ただし、Rは炭素数12〜24のアルキル基またはアルケニル基を表し、 (Wherein, R represents an alkyl or alkenyl group having 12 to 24 carbon atoms,
mは5≦m≦30、nは0<n≦5の範囲にある) m is 5 ≦ m ≦ 30, n is in the range of 0 <n ≦ 5)
で表されるものが好適である。 In those represented are preferred.
そして、このようなポリオキシエチレンポリオキシプロピレンアルキルエーテルとしては、例えば、上記m、nの値が前記範囲にあるPOE・POPセチルエーテル、POE・POPベヘニルエーテル、POE・POP2−デシルテトラデシルエーテル、POE・POPモノブチルエーテル、POE・POP水添ラノリン、POE・POPグリセリンエーテルなどが挙げられる。 Then, as such polyoxyethylene polyoxypropylene alkyl ethers, for example, the m, POE · POP cetyl ether value of n is in the range, POE · POP behenyl ether, POE · POP2- decyl tetradecyl ether, POE · POP monobutyl ether, POE · POP hydrogenated lanolin, etc. POE · POP glycerin ether.
【0012】 [0012]
両性界面活性剤および半極性界面活性剤 Amphoteric surfactants and semi-polar surfactants
本発明において両性界面活性剤としては、下記一般式(3)〜(7)で示したものが、半極性界面活性剤としては、下記一般式(8)で示したものが例示される。 Examples of the amphoteric surfactant in the present invention, those shown by the following general formula (3) to (7), as the semi-polar surfactants, those shown by the following general formula (8) can be exemplified.
一般式(3): The general formula (3):
【化7】 [Omitted]
で表されるアミドベタイン型両性界面活性剤(市販品としてレボン2000(三洋化成株式会社製)、アノンBDF(日本油脂株式会社製)などが挙げられる)。 In represented by amide betaine amphoteric surfactant (Rebon 2000 commercially (manufactured by Sanyo Kasei Co., Ltd.), Anon BDF (manufactured by NOF Corporation) and the like).
一般式(4): The general formula (4):
【化8】 [Of 8]
で表されるアミドスルホベタイン型両性界面活性剤(市販品としてロンザイン−CS(ロンザ社製)、ミラタインCBS(ミラノール社製)などが挙げられる)。 In represented by amido sulfobetaine type amphoteric surfactants (commercially available as Ronzain -CS (produced by Lonza), and the like Miratain CBS (Miranol, Inc.)).
【0013】 [0013]
一般式(5): The general formula (5):
【化9】 [Omitted]
で表されるベタイン型両性界面活性剤(市販品としてアノンBL(日本油脂株式会社製)、デハイントンAB−30(ヘンケル社製)などが挙げられる)。 In represented betaine amphoteric surfactant (commercially available as Anon BL (manufactured by NOF Corporation), Dehainton AB-30 (Henkel), and the like).
一般式(6): The general formula (6):
【化10】 [Of 10]
で表されるスルホベタイン型両性界面活性剤(市販品としてロンザイン12CS(ロンザ社製)などが挙げられる)。 In represented by sulfobetaine type amphoteric surfactants (Ronzain 12CS commercially (produced by Lonza), and the like).
【0014】 [0014]
一般式(7): The general formula (7):
【化11】 [Of 11]
で表されるイミダゾリニウム型両性界面活性剤(市販品としてオバゾリン662−N(東邦化学株式会社製)、アノンGLM(日本油脂株式会社製)などが挙げられる)。 In imidazolinium type amphoteric surfactants represented (Obazorin 662-N as a commercial product (manufactured by Toho Chemical Co., Ltd.), Anon GLM (NOF Corporation) and the like).
一般式(8): The general formula (8):
【化12】 [Of 12]
で表される第三級アミンオキサイド型半極性界面活性剤(市販品としてユニセーフA−LM(日本油脂株式会社製)、ワンダミンOX−100(新日本株式会社製)などが挙げられる)。 In tertiary amine oxide-type semipolar surfactants represented (Unisafe A-LM commercially (manufactured by NOF Corporation), Wandamin OX-100 (manufactured by Shin Nippon Co., Ltd.)).
【0015】 [0015]
ただし、一般式(3)〜(8)で、R 1は平均炭素原子数9〜21のアルキル基またはアルケニル基が好ましく、より好ましくは平均炭素原子数11〜17のアルキル基またはアルケニル基、さらに好ましくは平均炭素原子数11ないし13のアルキル基またはアルケニル基である。 However, in general formula (3) ~ (8), R 1 is preferably an alkyl group or alkenyl group having an average carbon number 9 to 21, more preferably an average alkyl or alkenyl group having a carbon number of 11 to 17, further preferably an alkyl or alkenyl group having an average carbon number 11 to 13. 平均炭素原子数が9未満では親水性が強すぎ、一方21を越えると水への溶解性が悪くなる。 Is less than the average number of carbon atoms is 9 too is strongly hydrophilic, whereas exceeding 21, the solubility in water becomes poor.
2及びR 3は平均炭素原子数10ないし18のアルキル基またはアルケニル基を表す。 R 2 and R 3 represents an alkyl group or alkenyl group having 10 average carbon atoms 18.
pは2〜4の整数、qは0〜3の整数、sは1または2の整数を表す。 p is an integer of 2 to 4, q is an integer of 0 to 3, s is an integer of 1 or 2.
本発明においては、これらの両性界面活性剤及び/または半極性界面活性剤のうち任意の一種または二種以上が選ばれて用いられる。 In the present invention, or any one or two or one of these amphoteric surfactants and / or semi-polar surfactant is used is selected.
【0016】 [0016]
水系分散媒 Aqueous dispersion medium
本発明において、微細ワックス粒は水系分散媒中に分散されることが好ましく、この水系分散媒としては、水を単独で、或いは、水とエタノール、グリセリン、ポリエチレングリコール、プロピレングリコール、ジプロピレングリコール、1,3−ブタンジオール、キシリトール、ソルビトール、マルチト−ル、コンドロイチン硫酸、ヒアルロン酸、ムコイチン硫酸、カロニン酸、アテロコラーゲン、コレステリル−12−ヒドロキシステアレート、乳酸ナトリウム、胆汁酸塩、dl−ピロリドンカルボン酸塩、短鎖可溶性コラーゲン、ジグリセリン(EO)PO付加物、イザヨイバラ抽出液、セイヨウノコギリソウ抽出液、メリロート抽出液等が挙げられる。 In the present invention, the fine wax particles is is preferably dispersed in an aqueous dispersion medium, as the aqueous dispersion medium, water alone, or water and ethanol, glycerin, polyethylene glycol, propylene glycol, dipropylene glycol, 1,3-butanediol, xylitol, sorbitol, multitrack - Le, chondroitin sulfate, hyaluronic acid, mucoitin sulfuric acid, charonic acid, atelocollagen, cholesteryl 12-hydroxystearate, sodium lactate, bile salt, dl-pyrrolidone carboxylate , short-chain soluble collagen, diglycerin (EO) PO adducts, chestnut rose extract, yarrow extract, sweet clover extract, and the like.
【0017】 [0017]
微細分散物の調製 Preparation of microdispersion
まず、本発明者らは下記のような試験を行い、ワックスの微細分散組成物の調製を試みた。 First, the present inventors have conducted tests as described below, it was tried the preparation of fine dispersion composition of wax.
【0018】 [0018]
【表1】 [Table 1]
【0019】 [0019]
<製法> <Process>
イオン交換水に前記非イオン界面活性剤及び両性界面活性剤を水に溶解し、80〜90℃に加熱してキャンデリラワックスを添加し、1時間プロペラ撹拌する。 The ion-exchanged water nonionic surfactant and amphoteric surfactant were dissolved in water, was added candelilla wax was heated to 80-90 ° C., stirred for 1 hour propeller. その後、氷冷し、組成物を得る。 Thereafter, ice-cooled, to obtain a composition.
【0020】 [0020]
<結果> <Result>
上記表1より明らかなように、カチオン界面活性剤、アニオン界面活性剤、非イオン界面活性剤、両性界面活性剤ともに、各単独では乳化組成物が白濁する傾向にあり、安定性も好ましくない(試験例1〜4)。 As is apparent from Table 1, cationic surfactants, anionic surfactants, nonionic surfactants, both amphoteric surfactants, each alone tends to emulsified composition becomes cloudy, stability unfavorable ( test example 1-4). また、カチオン乃至アニオン界面活性剤と非イオン界面活性剤を組み合わせた場合(試験例5,6)、あるいはカチオン乃至アニオン界面活性剤と両性界面活性剤を組み合わせた場合(試験例8,9)にも同様である。 Further, when combined with cationic or when combining anionic surfactant and nonionic surfactant (Test Examples 5 and 6), or a cationic or anionic surfactant and amphoteric surfactant (Test Examples 8 and 9) the same is true.
しかしながら、非イオン界面活性剤と両性界面活性剤を組み合わせた場合(試験例7)には、乳化組成物の外観が透明となり、ワックスの微細分散組成物が得られたことが示唆される。 However, when combined with non-ionic surfactant and an amphoteric surfactant (Test Example 7), the appearance of the emulsified composition becomes transparent, the fine dispersion composition of wax was obtained is indicated.
動的光散乱法による測定の結果、この微細分散物の粒子径は約30nmであった。 Results of the measurement by dynamic light scattering method, the particle size of the fine dispersion was about 30 nm.
【0021】 [0021]
非イオン界面活性剤の検討 Study of non-ionic surfactants
次に本発明者らは非イオン界面活性剤の至適HLBについて検討を進めた。 Then the present inventors have proceeded examined optimum HLB of nonionic surfactants.
すなわち、下記組成を基本処方に、非イオン界面活性剤のHLBを変化させてその乳化状態を検討した。 That is, the basic formulation of the following composition was investigated its emulsified state by changing the HLB of nonionic surfactants.
<基本処方1> <Basic Formulation 1>
キャンデリラワックス 10% Candelilla wax 10%
アミドベタイン型両性界面活性剤 5% Amido betaine type amphoteric surfactant 5%
非イオン界面活性剤 10% Nonionic surfactant 10%
イオン交換水 残 部合計 100% Ion exchange water remaining portion total of 100%
(両性界面活性剤/(両性界面活性剤+非イオン界面活性剤)の配合重量比= (Amphoteric surfactant / (amphoteric surfactant + nonionic surfactant) the weight ratio of formulation of =
約0.33) About 0.33)
結果を次の表2に示す。 The results are shown in the following Table 2.
【0022】 [0022]
【表2】 [Table 2]
【0023】 [0023]
前記表より明らかなように、両性界面活性剤/(両性界面活性剤+非イオン界面活性剤)の重量比が約0.33においては、非イオン界面活性剤のHLBが6〜12で均一な乳化系の形成が可能であるが、特にHLBが7〜11で半透明乃至透明な一液相が形成される。 As is apparent from Table, the weight ratio of about 0.33 amphoteric surfactant / (amphoteric surfactant + nonionic surfactant), HLB of nonionic surfactant is uniform 6-12 Although it is possible to form the emulsifying system, translucent or transparent one liquid phase is formed, especially an HLB of at 7-11.
従って、両性界面活性剤/(両性界面活性剤+非イオン界面活性剤)の重量比が約0.33においては、非イオン界面活性剤のHLBは6〜12、特に半透明、透明系を得るためには7〜11であることが理解される。 Accordingly, in a weight ratio of about 0.33 amphoteric surfactant / (amphoteric surfactant + nonionic surfactant), HLB of nonionic surfactant 6-12, obtained in particular translucent, transparent system it is understood to be 7 to 11 for.
【0024】 [0024]
次に、本発明者らは非イオン界面活性剤の種類と分散状態について検討を進めた。 Then, the present inventors have proceeded examined types and dispersion condition of nonionic surfactants. まず、基本処方1の組成における結果を次に示す。 First, the following results in the composition of the basic formulation 1.
【0025】 [0025]
【表3】 [Table 3]
【0026】 [0026]
なお、前記表において、○は透明な一液相を形成した状態を意味し、△は半透明乃至均一なクリーム状を、×は分離をそれぞれ表す。 In the above table, ○ means a state of forming a clear one-liquid phase, △ is a semi-transparent or uniform creamy, × represents each separation.
上記表より、基本処方1、すなわち、両性界面活性剤/(両性界面活性剤+非イオン界面活性剤)の重量比が約0.33においては、各非イオン界面活性剤を単独で用いた場合には、概ねHLBが9〜11で透明な一液相を形成し得ることが理解される。 From the above table, the basic formulation 1, i.e., when the weight ratio of amphoteric surfactant / (amphoteric surfactant + nonionic surfactant) is at approximately 0.33, with each non-ionic surfactant alone the, it is understood that generally HLB can form a clear one-liquid phase at 9-11.
また、前記表2を参酌すると、複数の非イオン界面活性剤を組み合わせて用いることも可能である。 Also, when reference to Table 2, it is also possible to combine a plurality of non-ionic surfactants.
【0027】 [0027]
さらに、本発明者らはPOEコレステリル、POEグリセリル、POE硬化ヒマシ油等について検討を行ったが、これらの多鎖型非イオン界面活性剤単独では、透明な一液相を調製することは困難であった。 Furthermore, the present inventors have POE cholesteryl, POE glyceryl, were examined POE hardened castor oil, in these multi chain nonionic surfactants alone, it is difficult to prepare a clear one-liquid phase there were. 無論、これらの多鎖型非イオン界面活性剤にあっても他の非イオン界面活性剤との組み合わせにより好適な分散系を得ることは可能であるが、特にPOE直鎖乃至POE分岐脂肪酸エーテルが好適に用いられる。 Of course, it is possible to obtain a suitable dispersion by a combination of these multi chain even in non-ionic surfactants other nonionic surfactants, in particular POE straight-chain or POE branched fatty ether It is preferably used.
【0028】 [0028]
両性界面活性剤と非イオン界面活性剤の相関 Correlation of amphoteric surfactant and nonionic surfactant
次に本発明者らは両性界面活性剤と非イオン界面活性剤との相関について検討を進めた。 Then the present inventors have proceeded examined correlation between amphoteric surfactant and nonionic surfactant.
すなわち、下記基本処方に基づき、アミドベタイン型両性界面活性剤(商品名レボン2000SF)、非イオン界面活性剤(POE(10)ベヘニルエーテル)の配合比、配合量を変化させてワックス分散系を調製した。 That is, prepared based on the following basic formulation, amide betaine type amphoteric surfactants (trade name Rebon 2000SF), the blending ratio of the nonionic surfactant (POE (10) behenyl ether), a wax dispersion by changing the amount did.
【0029】 [0029]
結果を図1に示す。 The results are shown in Figure 1.
同図より明らかなように、界面活性剤比=両性界面活性剤/(両性界面活性剤+非イオン界面活性剤)は0.3付近のところが極めて良好な比として存在するが、その比の範囲は(両性界面活性剤+非イオン界面活性剤)の量が増加するにつれ広くなる傾向にある。 As apparent from the figure, the surfactant ratio = amphoteric surfactant / (amphoteric surfactant + nonionic surfactant) is present as a very good ratio at the vicinity of 0.3, the range of the ratio It is widely tends as it increases the amount of (amphoteric surfactant + nonionic surfactant).
なお、当然のことながら、非イオン界面活性剤のHLB値を変化させることにより好ましい界面活性剤比は異なり、前記の至適な非イオン界面活性剤のHLB範囲では、0.03〜0.5が好ましい。 As a matter of course, preferred surfactants ratio by changing the HLB value of the nonionic surfactant varies, in HLB range of said optimum nonionic surfactants, 0.03 to 0.5 It is preferred. 0.03未満では、系への非イオン界面活性剤の寄与が大きくなり、温度安定性が損なわれる。 Is less than 0.03, the greater the contribution of nonionic surfactant to the system, the temperature stability is impaired.
一方、0.5を超えると、ワックスの微細分散物は得られにくくなる。 On the other hand, when it exceeds 0.5, a fine dispersion of the wax is hardly obtained.
次に本発明者らは、安全性および安定性について検討した。 Then the present inventors studied about safety and stability.
【0030】 [0030]
安全性 safety
安全性については卵白アルブミン変性率から評価した。 It was voted ovalbumin modification ratio for safety.
【0031】 [0031]
<試験方法> <Test Method>
水系高速液体クロマトグラフィを利用し、卵白アルブミンpH緩衝溶媒に、試料濃度1%になるように試料を加えた場合の、卵白アルブミン変性率220nmの吸収ピークを用いて測定した。 Using aqueous HPLC, ovalbumin pH buffering solvent, when the sample was added in the concentration of 1% sample concentration was measured using an absorption peak of ovalbumin modification ratio 220 nm.
[(Ho−Hs)/Ho]×100 [(Ho-Hs) / Ho] × 100
Ho:卵白アルブミンの220nm吸収ピークの高さHs:卵白アルブミン緩衝溶媒に試料を加えた時の220nm吸収ピークの高さ評価は以下の4段階評価で行った。 Ho: height of 220nm absorption peak of ovalbumin Hs: height Evaluation of 220nm absorption peak upon addition of the sample to ovalbumin buffering solvent was conducted according to the following 4-stage evaluation.
◎・・・皮膚刺激性が非常に少ない−卵白アルブミン変性率30%未満○・・・皮膚刺激性が少ない−卵白アルブミン変性率30%以上60%未満△・・・皮膚刺激性が中程度−卵白アルブミン変性率60%以上80%未満 ×・・・皮膚刺激性が強い−卵白アルブミン変性率80%以上結果を表4に示す。 ◎ · · · skin irritation is very small - ovalbumin modification ratio less than 30% ○ · · · less skin irritation - ovalbumin modification ratio 30% or more and less than 60% △ · · · Skin irritation moderate - ovalbumin modification ratio is stronger than 80% × · · · skin irritation than 60% - ovalbumin modification ratio 80% Table 4 shows the results.
【0032】 [0032]
【表4】 [Table 4]
【0033】 [0033]
上記の結果から両性界面活性剤と非イオン界面活性剤の組合せは、非イオン界面活性剤と同レベルで皮膚刺激性が少なく安全性が高い。 The combination of amphoteric surface active agents and nonionic surface active agents from the above results, it is highly less safe skin irritation nonionic surfactant and the same level. 従って、両界面活性剤を併用したワックスの微細分散物は安全性が高いことが示唆される。 Therefore, fine dispersion of wax in combination with both the surfactant is suggested that high safety.
【0034】 [0034]
安定性 Stability
以下に示す処方でワックスの微細分散物を調製し、50℃、1週間の経時安定性を評価した。 The following formulation fine dispersion of the wax was prepared as shown in, 50 ° C., it was assessed 1 week aging stability. 結果を表5に示す。 The results are shown in Table 5.
<基本処方2> <Basic Prescription 2>
キャンデリラワックス 10% Candelilla wax 10%
界面活性剤 約10〜20% Surfactant about 10-20%
イオン交換水 残部【0035】 Ion-exchanged water balance [0035]
【表5】 [Table 5]
【0036】 [0036]
上記表5より明らかなように、非イオン界面活性剤単独および界面活性剤比(前記規定)が0.03未満では、経時安定性は損なわれる。 As is apparent from Table 5, the nonionic surfactant alone and surfactant ratio (the normal) is less than 0.03, stability over time is compromised.
一方、好ましい界面活性剤比中の両性界面活性剤と非イオン界面活性剤の組合せでは安定性は良好であった。 On the other hand, the combination of amphoteric surfactant in the surfactant ratio and a non-ionic surfactant was good stability.
【0037】 [0037]
なお、本発明の微細分散組成物を毛髪化粧料として用いる場合、通常毛髪化粧料の成分とし使用する油分(ツバキ油、ナタネ油、ゴマ油、サフラワー油、綿実油、ヒマシ油、大豆油、ヤシ油、パーム油、ミツロウ、モンタンロウ、ラノリン、炭化水素油、エステル油、シリコーン油等)、界面活性剤(アルキルベンゼンスルホン酸塩、ポリオキシアルキレンアルキル硫酸エステル、アルキル硫酸エステル、アルカンスルホン酸塩、アルキルエトキシカルボン酸塩、コハク酸誘導体、アルキルアミンオキサイド、イミダゾリン型化合物、ポリオキシエチレンアルキル又はアルケニルエーテル、ポリオキシエチレンアルキルフェニルエーテル、高級脂肪酸アルカノールアミド又はそのアルキレオキサイド付加物等)、高分子化合物(ヒドロキシエ In the case of using the fine dispersion composition of the present invention as a hair cosmetic, oil used as normal hair cosmetic composition of the component (camellia oil, rapeseed oil, sesame oil, safflower oil, cotton seed oil, castor oil, soybean oil, coconut oil , palm oil, beeswax, montan wax, lanolin, hydrocarbon oils, ester oils, silicone oil, etc.), a surfactant (alkylbenzene sulfonate, polyoxyalkylene alkyl sulfates, alkyl sulfates, alkane sulfonates, alkyl ethoxy carboxylate salt, succinic acid derivatives, alkylamine oxide, imidazoline compounds, polyoxyethylene alkyl or alkenyl ethers, polyoxyethylene alkyl phenyl ethers, higher fatty acid alkanolamides or Al sharp oxide adduct), the polymer compound (hydroxymethyl d レンセルロース、ヒドロキシプロピルセルロース、ヒドロキシプロピルメチルセルロース、メチルセルロース、カチオン化セルロース、カチン化高分子、ポリビニルピロリドン、ピニルピロリドンと酢酸ビニルの共重合体、ビニルピロリドン−酢酸ビニル−アルキルアミノアクリレート共重合体、メチルビニルエーテル−無水マレイン酸共重合体の低級アルキル−N−アルキルアクリルアミド共重合体等)、酸化防止剤、紫外線吸収剤、保湿剤、香料、染料、顔料、色素、防腐剤、ビタミン剤、ホルモン剤、消臭剤、pH調製剤、固着剤等を配合してもよい。 Ren cellulose, hydroxypropyl cellulose, hydroxypropyl methyl cellulose, methyl cellulose, cationized cellulose, cathine of polymers, polyvinyl pyrrolidone, copolymers of Pinirupiroridon and vinyl acetate, vinylpyrrolidone - vinyl acetate - alkylamino acrylate copolymers, methyl vinyl - lower alkyl -N- alkyl acrylamide copolymer of maleic anhydride copolymer, etc.), antioxidants, ultraviolet absorbers, humectants, perfumes, dyes, pigments, dyes, preservatives, vitamins, hormonal agents, deodorants, pH adjusting agents, may be blended sticking agent.
これら成分と本微細分散組成物と混合することにより本微細分散組成物を含有する毛髪化粧料を得ることができる。 By mixing these components with the fine dispersion composition can be obtained hair cosmetic composition containing the fine dispersion composition. また、本発明では毛髪化粧料以外にも、つや出し剤等を得ることが可能である。 Further, in the present invention other than the hair cosmetic composition, it is possible to obtain a polishing agent.
【0038】 [0038]
ワックスの微細分散物の調製方法 Process for the preparation of a fine dispersion of the wax
本発明のワックスの微細分散組成物は、マイクロエマルションの調製法を用いて得ることができる。 Fine dispersion composition of wax of the present invention can be obtained using the preparation of the microemulsion. マイクロエマルションの調製方法としては、例えば特公平6−61454号公報、特公平6−57316号公報が挙げられる。 The process for the preparation of the microemulsion, for example Kokoku 6-61454 JP include KOKOKU 6-57316 JP. これらに記載される技術は、液体の油滴超微粒子を調製するものであるが、本発明のような固形ワックスの超微粒子の調製も行うことができる。 The techniques described in these, but is intended to prepare an oil droplet ultrafine particles of the liquid, it can also be carried out the preparation of ultrafine particles, such solid wax as in the present invention.
すなわち、系をワックスの融点以上、可溶化温度範囲に加温し、常温に冷却することにより、調製することができる。 That is, the system of the wax above the melting point, warmed to solubilize temperature range, by cooling to room temperature can be prepared.
【0039】 [0039]
また、本発明のワックスの微細分散組成物は、強力な剪断力を与え得る乳化機、例えば高圧ホモジナイザー、あるいは超音波乳化機等の機械力を用いて調製することもできる。 Further, the fine dispersion composition of wax of the present invention can also be prepared using an emulsifying machine capable of providing a strong shearing force, for example a high-pressure homogenizer, or a mechanical force such as an ultrasonic emulsifier. 高圧ホモジナイザーを用いる場合には、400気圧以上の圧力下で乳化するのが好ましいが、さらに好ましくは、ワックスの融点以上の温度で600気圧以上の圧力下で乳化することが好ましい。 In the case of using a high-pressure homogenizer, it is preferable to emulsify under a pressure of more than 400 atmospheres, more preferably, it is preferable to emulsify under a pressure of more than 600 atmospheres at a temperature above the melting point of the wax.
【0040】 [0040]
【実施例】 【Example】
次に、本発明の具体的な配合例を示す。 Next, a specific formulation of the present invention.
実施例1 セットローション Example 1 setting lotion
【0041】 [0041]
<製法> <Process>
(1)〜(3)と(4)の一部を約95℃で撹拌混合し、透明性を帯びた後、氷冷し、ワックスの微細分散物を得、その後、(4)の残部、(5)〜(9)の混合物をワックスの微細分散物に添加し、セットローションを得た。 (1) to (3) and (4) were mixed by stirring portion at about 95 ° C., and after tinged transparency, cooled with ice, to obtain a fine dispersion of the wax, then the remainder of (4), a mixture of (5) to (9) were added to a fine dispersion of the wax, to obtain a set lotion.
【0042】 [0042]
実施例2 ヘアムース Example 2 hair mousse
【0043】 [0043]
<製法> <Process>
(1)〜(4)と(5)の一部を約95℃で撹拌混合し、透明性を帯びた後、氷冷し、ワックスの微細分散物を得、その後、(5)の残部、(6)〜(9)の混合物をワックスの微細分散物に添加し、ヘアムース原液とし、次いで、この原液をエアゾール用缶に添加し、弁をした後、噴射剤液化石油ガスを充填し、ヘアムースを得た。 (1) to (4) and (5) were mixed by stirring portion at about 95 ° C., and after tinged transparency, cooled with ice, to obtain a fine dispersion of the wax, then the remainder of (5), a mixture of (6) to (9) were added to a fine dispersion of the wax, and hair mousse stock solution, then the stock solution was added to an aerosol can, after the valve, filling the propellant liquefied petroleum gas, hair mousse It was obtained.
【0044】 [0044]
実施例3 ヘアジェル Example 3 hair gel
【0045】 [0045]
<製法> <Process>
(1)〜(4)と(5)の一部を560気圧の圧力下、85℃において高圧ホモジナイザーで乳化し、透明性を帯びた後、氷冷し、ワックスの微細分散物を得、その後、(5)の残部、(6)〜(12)の混合物にをワックスの微細分散物に添加した後、(13)を添加して、ヘアジェルを得た。 (1) to (4) and (5) under a pressure of some 560 atm, emulsified in a high-pressure homogenizer at 85 ° C., after tinged transparency, cooled with ice, to obtain a fine dispersion of the wax, then , the remainder of (5), was added to the microdispersion of wax to a mixture of (6) to (12), with the addition of (13) to give a hair gel.
【0046】 [0046]
実施例4 カーワックス Example 4 car wax
【0047】 [0047]
<製法> <Process>
(1)〜(4)と(5)、(8)の一部を約95℃で攪拌混合し、透明性を帯びた後、氷冷し、ワックスの微細分散物を得、その後、(5)、(8)の残部、(6)、(7)で得られる乳化物を微細分散物に添加し、カーワックスを得た。 (1) to (4) and (5) were mixed and stirred at a portion of about 95 ° C. (8), after tinged transparency, cooled with ice, to obtain a fine dispersion of the wax, then, (5 ), (remainder of 8), (6), was added to the emulsion of fine dispersion obtained in (7), to give a car wax.
【0048】 [0048]
実施例5 つや出し剤 Example 5 polishes
【0049】 [0049]
<製法> <Process>
(1)〜(5)と(6)、(10)の一部を約95℃で攪拌混合し、透明性を帯びた後、氷冷し、ワックスの微細分散物を得、その後、(6)、(10)の残部、(7)、(8)、(9)で得られる乳化物を微細分散物に添加し、つや出し剤を得た。 (1) to (5) and (6), were mixed and stirred at a portion of about 95 ° C. (10), after tinged transparency, cooled with ice, to obtain a fine dispersion of the wax, then, (6 ), (remainder of 10), (7), (8), was added to the emulsion of fine dispersion obtained in (9), to give a polish.
【0050】 [0050]
【発明の効果】 【Effect of the invention】
以上説明したように本発明にかかる分散組成物によれば、非イオン界面活性剤及び両性界面活性剤を併用することにより、極めて微細なワックス粒を容易に調製することができる。 According to the dispersion composition according to the present invention described above, the combined use of nonionic surfactants and amphoteric surfactants can be prepared very fine wax particles easily.
【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS
【図1】本発明において、界面活性剤の組成とその量及び分散状態の関係を示す説明図である。 In [1] the present invention, it is an explanatory diagram showing the relationship between the composition and the amount thereof and the state of dispersion of the surfactant.

Claims (8)

  1. 両性界面活性剤および/又は半極性界面活性剤と、非イオン界面活性剤と、 常温で固体ないし半固体の油分であるワックスと、水系分散媒とを含み、 And amphoteric surface active agent and / or semi-polar surfactant, a nonionic surfactant, a wax is oil solid or semi-solid at room temperature, see contains an aqueous dispersion medium,
    両性界面活性剤/(両性界面活性剤+非イオン界面活性剤)の重量比が0.03〜0.5であり、 The weight ratio of amphoteric surfactant / (amphoteric surfactant + nonionic surfactant) is 0.03 to 0.5,
    水系分散媒中にワックスが固体ないし半固体状で微細分散していることを特徴とするワックスの微細分散組成物。 Fine dispersion composition of wax, wherein the wax in the aqueous dispersion medium is finely dispersed in solid or semisolid.
  2. 請求項1に記載の組成物において、全非イオン界面活性剤の加重平均したHLBが6〜12であることを特徴とするワックスの微細分散組成物。 A composition according to claim 1, a fine dispersion composition of wax, wherein the weighted average HLB of total nonionic surfactant is 6 to 12.
  3. 請求項1または2に記載の組成物において、非イオン界面活性剤としてポリオキシエチレンポリオキシプロピレンアルキルエーテルを含むことを特徴とするワックスの微細分散組成物。 A composition according to claim 1 or 2, fine dispersion composition of wax comprising a polyoxyethylene polyoxypropylene alkyl ether as the nonionic surfactant.
  4. 請求項に記載の組成物において、ポリオキシエチレンポリオキシプロピレンアルキルエーテルが下記一般式(1): A composition according to claim 3, polyoxyethylene polyoxypropylene alkyl ether is represented by the following general formula (1):
    および/または、下記一般式(2): And / or the following general formula (2):
    (ただし、Rは炭素数12〜24のアルキル基またはアルケニル基を表し、 (Wherein, R represents an alkyl or alkenyl group having 12 to 24 carbon atoms,
    mは5≦m≦30、nは0<n≦5の範囲にある) m is 5 ≦ m ≦ 30, n is in the range of 0 <n ≦ 5)
    で表されることを特徴とするワックスの微細分散組成物。 Fine dispersion composition of wax, characterized in that it is represented in.
  5. 請求項1〜 のいずれかに記載の組成物において、系をワックスの融点以上、可溶化温度範囲に加温した後、常温に冷却して得られることを特徴とするワックスの微細分散組成物。 A composition according to any one of claims 1-4, the system of the wax above the melting point, followed by heating to solubilize the temperature range, fine dispersion composition of wax which is characterized in that it is obtained by cooling to room temperature .
  6. 請求項1〜 のいずれかに記載の組成物において、ワックスの融点以上で高剪断力乳化機を用いて調製することを特徴とするワックスの微細分散組成物。 A composition according to any one of claims 1-4, fine dispersion composition of wax which is characterized in that prepared using high shear emulsifying machine with wax above the melting point.
  7. 請求項1〜 のいずれかに記載のワックスの微細分散組成物を含むことを特徴とする毛髪化粧料。 Hair cosmetic which comprises a fine dispersion composition of wax according to any one of claims 1-6.
  8. 請求項1〜 のいずれかに記載のワックスの微細分散組成物を含むことを特徴とするつや出し剤。 Polish which comprises a fine dispersion composition of wax according to any one of claims 1-6.
JP9406298A 1997-03-21 1998-03-23 Fine dispersion composition of wax and the hair cosmetic and polishes Expired - Lifetime JP3639715B2 (en)