JP3254249B2 - Bluing method of transparent resin molded article - Google Patents

Bluing method of transparent resin molded article

Info

Publication number
JP3254249B2
JP3254249B2 JP21822692A JP21822692A JP3254249B2 JP 3254249 B2 JP3254249 B2 JP 3254249B2 JP 21822692 A JP21822692 A JP 21822692A JP 21822692 A JP21822692 A JP 21822692A JP 3254249 B2 JP3254249 B2 JP 3254249B2
Authority
JP
Japan
Prior art keywords
molded article
pigment
transparent resin
resin molded
liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP21822692A
Other languages
Japanese (ja)
Other versions
JPH0639868A (en
Inventor
健太郎 大山
Original Assignee
アイリスオーヤマ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by アイリスオーヤマ株式会社 filed Critical アイリスオーヤマ株式会社
Priority to JP21822692A priority Critical patent/JP3254249B2/en
Publication of JPH0639868A publication Critical patent/JPH0639868A/en
Application granted granted Critical
Publication of JP3254249B2 publication Critical patent/JP3254249B2/en
Anticipated expiration legal-status Critical
Application status is Expired - Fee Related legal-status Critical

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【産業上の利用分野】本発明は、透明樹脂成形品のブルーイング方法に関する。 The present invention relates to a brewing method of the transparent resin molded article.

【0002】 [0002]

【従来の技術】今日においては、衣料品等の収納に用いられる収納ボックスのように、PPで成形され外部から収納物を視認し得る透明樹脂成形品が多用されるに至っている。 BACKGROUND OF THE INVENTION Today, has led to such a storage box to be used for storage of clothing Hinto, transparent resin molded article capable of viewing the stored product from outside is molded of PP is frequently used. この透明樹脂成形品の成形に際しては、所謂ブルーイングと称されるように、微少量のブルー系顔料を成形品に混入し、これにより外見上の清涼感を増加させる手法が用いられている。 In the transparent resin molded article of the molding, as called so-called bluing, mixed with blue pigment of a small amount of the molded article, thereby it is used a technique to increase the cooling sensation in appearance. このブルーイングに際しては、予めPP原料に微量のブルー顔料を添加し、押出機で混練してペレットを製造し、そのペレットを使用して、成形機を用いて成形品を成形する。 In this brewing advance PP material was added a small amount of blue pigment, and kneaded by an extruder to prepare pellets, using the pellets, a molded article using a molding machine. これにより、成形品には所定量のブルー顔料が混入され、外見上の清涼感を向上させることができる。 Thus, the molded product is mixed into a predetermined amount of blue pigment, it is possible to improve the freshness in appearance.

【0003】 [0003]

【発明が解決しようとする課題】このように従来において、ブルーイングを行う際には、成形前にブルー顔料の練り込みを行う必要がある。 [Problems that the Invention is to Solve Thus, in the prior art, when performing brewing, it is necessary to kneading of blue pigment prior to molding. しかも、ブルーイングを行う際には、製品の肉厚に応じてブルー顔料の製品当たりの含有量を変更しなければならないことから、成形される製品ごとにブルー顔料の混合量を変更して、顔料の混練を行わなければならず、ブルーイングを行う際の工程が煩雑となってしまう。 Moreover, when performing brewing, since it must change the content per product blue pigment according to the thickness of the product, by changing the mixing amount of the blue pigment for each product to be molded, must be carried out kneading of a pigment, a process for performing a bluing becomes complicated.

【0004】また、前記ペレットを製造する工程において、使用する顔料は極く微量であり、製造ロッド毎、着色度合のフレが大きく、一定の品質を維持することが非常に困難である。 [0004] Further, in the step of preparing said pellets, the pigment used is a trace amount, each manufacturing rod, deflection of the coloring degree is large, it is very difficult to maintain a constant quality. すなわち、ブルーイングに必要な顔料は1個の製品に対して微少量であることから、ブルー顔料が過剰に混入されていた場合には、却って清涼感が阻害された製品が成形され、ブルー顔料が過少に混入された場合には、所要の清涼感が得られない製品が成形されてしまい、製品の歩留りが低下しているのが実情であった。 That is, since the pigment required for brewing a small amount for one product, when the blue pigment had been excessively mixed in, the shaped product rather cooling sensation was inhibited, blue pigment is when it is under-contamination, the required coolness can not be obtained product will be molded, the yield of products is reduced was circumstances.

【0005】本発明は、このような従来の課題に鑑みてなされたものであり、成形の前工程にてブルー顔料の混入を伴うことなく、しかも、製品当たり適正量のブルー顔料を混入して歩留りよくブルーイングされた透明樹脂成形品の成形を行うことができる透明樹脂成形品のブルーイング方法を提供することを目的とするものである。 [0005] The present invention has been made in view of such conventional problems, without contamination of the blue pigment in the previous step of the molding, moreover, by mixing a blue pigment of a proper amount per product it is an object to provide a high yield bluing been brewing method of the transparent resin molded article can be carried out molding of transparent resin molded product.

【0006】 [0006]

【課題を解決するための手段】前記課題を解決するため本発明にあっては、 透明樹脂成形品の成形時に、ブルー Means for Solving the Problems] To solve the above problems in the present invention, at the time of molding the transparent resin molded article, Blue
系液体顔料を1ショット毎に予め設定されている量をも Also the amount that has been previously set the system liquid pigment in every shot
ってインジェクション成形機の加熱スクリュー内に注入 Injected into the heating screw of injection molding machine I
し、該加熱スクリュー内で溶融する樹脂と混合した後、 And, after mixing with a resin that melts at a heating screw,
金型内に射出するように構成され、前記液体顔料は、9 Is configured to injected into the mold, the liquid pigment, 9
5〜97重量%の界面活性剤と、3〜5重量%の顔料とからなる。 5 to 97% by weight of surfactant, consisting of 3-5% by weight of pigment. また、前記顔料は、無機系の群青系色素であり、さらに、液状の帯電防止剤に前記液体顔料を混合して混合液を生成し、該混合液を前記加熱スクリュー内に Also, the pigments are inorganic ultramarine dye, further, a mixture of the liquid pigment antistatic agent liquid to produce the mixture, the mixture within the heating screw
注入し、前記混合液は、帯電防止剤に対して、液体顔料を5〜15重量%混合するように構成され、この混合液を、成形品に対して0.1〜0.5重量%注入するように構成されている。 Injecting the mixture, relative to antistatic agent, a liquid pigment is configured to mix 5 to 15 wt%, the mixture, 0.1 to 0.5 wt% injected into the molded article It is configured to.

【0007】 [0007]

【作用】前記構成において、 ブルー系液体顔料は、樹脂成形品の成形時に1ショット毎に予め設定されている量 [Action] In the arrangement, Blue Liquid pigment, the amount that is preset for each shot when the resin molded product molded
をもってインジェクション成形機の加熱スクリュー内に Have in the heating screw of injection molding machine
注入され、 該加熱スクリュー内で溶融する樹脂と混合し It is injected and mixed with the resin to be melted in the heating screw
た後、金型内に射出することから、予め成形用の樹脂に顔料を練り込んだり、ブレンドする必要はない。 After, since it is injected into the mold, Dari kneaded pigment resin for pre-molding, it is not necessary to blend. また、 Also,
注入量を適宜設定すれば、製品の肉厚に応じて、適正量の顔料注入が可能となり、ここで前記顔料が、無機系の群青系色素である場合には、ブルーイング効果が顕著となる。 By setting the injection amount appropriately in accordance with the thickness of the product, it is possible to pigment injection appropriate amount, wherein the pigment is in the case of inorganic ultramarine based dyes, bluing effect is conspicuous .

【0008】また、液状の帯電防止剤に顔料を混合して混合液を生成し、該混合液を成形時に加熱スクリュー内 Further, by mixing a pigment into antistatic agent liquid to produce the mixture, the heating screw to the mixture during molding
注入することにより、微少量の顔料が製品全体に均等に混入され、むらなく製品全体に均一なブルーイング効果が生ずる。 By injecting the, small amounts of pigment can be uniformly mixed throughout the product, occurs uniformly bluing effect throughout evenly product. なお、前記混合液は、帯電防止剤に対して液体顔料を5〜15重量%混合したものであり、この混合液を、成形品に対して0.1〜0.5重量%注入する構成によれば、ブルーイング効果が最も適正に発揮される。 Incidentally, the mixed liquid, a liquid pigment is obtained by mixing 5 to 15% by weight with respect to the antistatic agent, the mixture, in the configuration of injecting 0.1 to 0.5 wt% with respect to the molded article According, bluing effect is most properly exhibited.

【0009】 [0009]

【実施例】図1は、本発明にかかる樹脂製造方法を適用した実施例の工程を示す工程図であり、本実施例は、投入工程1、混合工程2、及び注入工程3で構成されている。 DETAILED DESCRIPTION FIG. 1 is a process diagram showing the procedure of Example of applying the resin production method according to the present invention, this embodiment is constituted by adding step 1, mixing step 2, and implantation step 3 there. 投入工程1には、所定量(例えば18リットル)ずつ容器内に収容された液体帯電防止剤とブルー系の液体顔料とが用意されており、この投入工程1に用意されている液体帯電防止剤とブルー系の液体顔料とは、次の混合工程2にて所定の比率をもって混合される。 The adding step 1, a predetermined amount (example, 18 liters) by a liquid antistatic agent contained in the container and the liquid pigment blue system are prepared, the liquid antistatic agent provided in this adding step 1 and the liquid pigment blue system, is mixed with a predetermined ratio in the next mixing step 2.

【0010】一方、注入工程3には、射出成形機7が配置されている。 On the other hand, the implantation step 3, the injection molding machine 7 is disposed. 該射出成形機7は、所定の樹脂成形品、 Injection-molding machine 7, predetermined resin molded article,
例えば衣類収納容器を成形し得る固定側5および可動側6とで構成された金型4と、該金型4内に樹脂を注入する樹脂注入部9とが設けられている。 For example a garment container stationary 5 and the movable 6 may molding the mold 4 composed of a, a resin injection portion 9 for injecting resin is provided in the mold 4. また、該樹脂注入部9は、加熱シリンダスクリュー10、該加熱シリンダスクリュー10内に供給される粒状の樹脂原料を収容するホッパー8が設けられており、該ホッパー8と加熱シリンダスクリュー10間には着色剤注入機構部11が設けられている。 Furthermore, the resin injection portion 9 includes a heating cylinder screw 10, a hopper 8 for containing the resin material particulate fed is provided in the heating cylinder screw 10, between the heating cylinder screw 10 and the hopper 8 coloring agent injection mechanism portion 11 is provided. 該着色剤注入機構部11は、前記混合液を、予め設定されている量をもって1ショットごとに加熱シリンダスクリュー10に供給し得る機構を有している。 Colorant injection mechanism portion 11, the pre-Symbol mixture has a mechanism capable of supplying the heating cylinder screw 10 amounts to have in every shot that is set in advance.

【0011】以上の構成にかかる本実施例において、投入工程1に搬入された18リットル入りの液体帯電防止剤とブルー系の液体顔料とは、混合工程2において液体顔料が液体帯電防止剤に対して10%の割合で混合された後、この混合液は、1ショット毎に予め設定されている量をもって、着色剤注入機構部11から加熱シリンダスクリュー10内に注入され、該加熱シリンダスクリュー10内で熔融する樹脂に混合された後、金型4内に射出される。 [0011] In this embodiment according to the above configuration, the liquid pigment turned carried-18-liter of a liquid antistatic agent in step 1 and Blue, inhibitor liquid charging liquid pigment in the mixing step 2 to after being mixed in a ratio of 10% Te, the mixture, with an amount that is preset for each shot is injected into the heating cylinder screw 10 in a colorant injection mechanism portion 11, the heating cylinder screw 10 in in after being mixed in the molten resin-is injected into the mold 4.

【0012】したがって、金型4の冷却が行われた後、 [0012] Therefore, after the cooling of the mold 4 has been made,
取り出される成形品にあっては、顔料とともに帯電防止剤が混入されていることから、帯電防止効果を得ることができるのみならずブルー系の顔料の混入によるブルーイング効果を得ることができる。 In the molded product taken out, since the antistatic agent is mixed with pigments, it is possible to obtain the brewing effect due to mixing of the pigment not only Blue can be obtained an antistatic effect. すなわち、このように着色剤注入機構部11から、ブルー系の顔料が混入された混合液を注入することにより、ブルーイング効果を有する製品を成形し得ることから、成形前にブルー系顔料の練り込み、あるいは混合を目的としたブレンドを行う必要はない。 That is, from such a colorant injection mechanism portion 11, by injecting a mixed solution pigment blue system is mixed, since it can mold a product having a bluing effect, blue pigment prior to molding paste Inclusive, or there is no need to perform a blend for the purpose of mixing.

【0013】また、透明樹脂成形品は、大きさや用途により肉厚が1.5mm〜3.0mmの厚さを有するが、 [0013] The transparent resin molded article, the thickness depending on the size and applications has a thickness of 1.5Mm~3.0Mm,
着色剤注入機構部11を調整して、前記混合液の注入量を設定変更すれば、当該製品において所要のブルーイング効果が得られるに適正量の顔料注入が可能となる。 Adjust the colorant injection mechanism portion 11, setting change injection quantity of the liquid mixture, it is possible to pigment the injection of the proper amount to the required brewing effect in the product is obtained. したがって、ブルーイング効果を有する成形品の成形効率を高めることができるとともに、同成形品の製造コストを低下させることができる。 Therefore, it is possible to it is possible to increase the molding efficiency of the molded article having a bluing effect, reducing the manufacturing cost of the molded article. しかも、前記混合液において、液体顔料は10倍に希釈されて、製品に注入されることから注入量の計量精度が高まり、また、微少量の顔料製品全体に均等に行き渡り、製品各部において均等なブルーイング効果を得ることができる。 Evenly Moreover, in the mixed solution, a liquid pigment is diluted 10-fold increases the injection quantity metering accuracy from being injected into the product, also a small amount of pigment spreads evenly throughout the product, the Product parts it is possible to obtain a bluing effect.

【0014】実施例1 次に、本発明者が実際に行ったより具体的な実施例について述べる。 [0014] Example 1 will now be described more specific embodiment the present inventor has actually performed. この実施例においては、97重量%の界面活性剤と3重量%の顔料とが配合された液体顔料を用いた。 In this embodiment, a is using liquid pigment formulated 97% by weight of a surfactant and 3% by weight of pigment. なお、顔料は無機系の群青系色素である。 In addition, the pigment is ultramarine blue based dye of inorganic. また、液体帯電防止剤は、ポリオキシエチレンアルキルアミンを用いた。 The liquid antistatic agent, was used polyoxyethylene alkylamine. そして、混合工程2では、帯電防止剤と液体顔料とを10:1の割合でポンプにて混合した。 Then, in the mixing step 2, the antistatic agent and the liquid pigment 10 were mixed at the pump at a ratio of 1.

【0015】また、金型4としては、衣料品等の収納に用いられる肉厚が1.7mmの収納ボックスを成形し得るキャビティを有するものを使用し、着色剤注入機構部11としては(株)シスコ・ノボシステムを用い、樹脂注入部9からPP原料とともに、製品に対して0.3重量%の前記混合液を注入した。 Further, as the mold 4, using the one having a cavity thickness used for storing clothing Hinto may molding the storage box of 1.7 mm, as the coloring agent injection mechanism portion 11 (strain ) using Cisco Novo system, with PP raw material from the resin injection portion 9, and injecting the mixture of 0.3% by weight with respect to the product. その結果、製品は各部において透明度が均一なブルーイング効果が得られ、帯電防止効果も全体に亙って均一であった。 As a result, the product transparency uniform bluing effect is obtained in each part, the antistatic effect was uniform throughout.

【0016】実施例2 この実施例2においては、前述した実施例1と同一の液体顔料と液体帯電防止剤および着色剤注入機構部11とを用いたが、金型4としては、肉厚が2.7mmの収納ボックスを成形し得るキャビティを有するものを使用した。 [0016] In Example 2 Example 2, was used as in Example 1 and the same liquid pigment and a liquid antistatic agent and a colorant injection mechanism portion 11 described above, as the mold 4, wall thickness It was used having a cavity capable of forming a storage box 2.7 mm. そして、1ショットごとに、製品に対して0.2重量%の前記混合液を注入した。 Then, for each shot, and injecting the mixture of 0.2% by weight with respect to the product. その結果、製品は透明度が均一なブルーイング効果及び帯電防止効果が得られた。 As a result, the product transparency uniform bluing effect and antistatic effect was obtained. つまり、この実施例2のように製品の肉厚が厚い場合には、製品に対する混合液の配合率を低下させることにより、過剰なブルー顔料の混入に起因する透明感の低下が防止されて、適正なブルーイング効果が得られた。 That is, when the thickness of the product as in the second embodiment is thick, by reducing the compounding ratio of the mixed liquid to the product, with reduction in transparency due to the incorporation of the excess blue pigment is prevented, proper bluing effect was obtained.
よって、混合液の配合比率を変更させずとも、混合液の注入量を製品の肉厚に応じて変更すれば、適正なブルーイング効果が得られることが判明した。 Thus, even without changing the mixing ratio of the mixed liquid, changing in accordance with the injection amount of the mixed solution to the wall thickness of the product, that proper brewing effect is obtained it has been found.

【0017】 [0017]

【発明の効果】以上説明したように本発明は、 透明樹脂 As described above, according to the present invention, a transparent resin
成形品の成形時に、ブルー系液体顔料を1ショット毎に At the time of the molded product molding, a blue-based liquid pigment to every shot
予め設定されている量をもってインジェクション成形機 Injection molding machine with an amount set in advance
の加熱スクリュー内に注入し、該加熱スクリュー内で溶 And the injection in the heating screw, soluble in the heating screw
融する樹脂と混合した後、金型内に射出するようにした。 After mixing with the resin to melt and to be injected into the mold. よって、透明樹脂成形品にブルーイング効果を付加する際に、成形前にブルー系の顔料を練り込んだり、あるいはブレンドする必要がなく、また、製品の肉厚に応じてブルー顔料の製品当たりの含有量を変更することも自在となり、よって、ブルーイングを行う際の工程の簡略化を図ることができる。 Thus, a transparent when adding bluing effect on resin moldings, Dari kneaded pigment blue system before molding, or it is not necessary to blend, also per product blue pigment according to the thickness of the product It becomes freely changing the content, therefore, it is possible to simplify the process of making the brewing. また、顔料を精度良く製品全 In addition, the accuracy of the pigment good product all
体に均一に行き亙らせて、製品全体に均一なブルーイン By span went to the uniform in the body, uniform blue in to the entire product
グ効果を得ることができる。 It is possible to obtain the grayed effect.

【0018】また、製品当たりのブルー原料の混入量が各製品ごとに均一となることから、ブルー顔料が過剰に混入されて透明感が阻害された製品や、ブルー顔料が過少に混入されて所要の清涼感が得られない製品が成形されてしまうことがなく、各製品ごとに適正なブルーイング効果が得られ、製品の歩留りを向上させることができる。 Further, since the mixed amount of blue material per product is uniform for each product, product or the transparency blue pigment is excessively mixed therein was inhibited, blue pigment is mixed under-required of without refreshing feeling can not be obtained product from being formed, proper brewing effect is obtained for each product, it is possible to improve the yield of products. また、顔料として無機系の群青系色素を使用することにより、ブルーイング効果が顕著となるとともに、液状の帯電防止剤に液体顔料を混合した混合液を成形品内へ注入することによって、微少量の顔料を精度良く、計量注入することにより製品全体に均一に行き亙らせて、 Further, by using an inorganic ultramarine-based pigments as pigments, with blueing effect it becomes conspicuous, by injecting a liquid mixture of liquid pigment was mixed with the antistatic agent of the liquid into the molded article within a small amount good pigment accuracy, thereby span go uniformly throughout the product by metering,
製品全体に均一なブルーイング効果を得ることができる。 It is possible to obtain a uniform bluing effect to the entire product.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】本発明の一実施例にかかる帯電防止効果を有する樹脂成形品の製造工程を示す工程図である。 1 is a process diagram showing the manufacturing process of the resin molded article having antistatic effect according to an embodiment of the present invention.

【符号の説明】 DESCRIPTION OF SYMBOLS

1 投入工程 2 混合工程 3 注入工程 4 金型 7 射出成形機 9 樹脂注入部 11 着色剤注入機構部 1 adding step 2 mixing step 3 implantation step 4 mold 7 an injection molding machine 9 resin injection portion 11 colorant injection mechanism portion

Claims (6)

    (57)【特許請求の範囲】 (57) [the claims]
  1. 【請求項1】 透明樹脂成形品の成形時に、ブルー系液 1. A time for molding a transparent resin molded article, Blue solution
    体顔料を1ショット毎に予め設定されている量をもって With an amount set in advance the body pigment in every shot
    インジェクション成形機の加熱スクリュー内に注入し、 Injected into the heated screw injection molding machine,
    該加熱スクリュー内で溶融する樹脂と混合した後、金型 After mixing with a resin that melts at a heating screw, die
    内に射出することを特徴とする透明樹脂成形品のブルーイング方法。 Brewing method of the transparent resin molded article characterized by injection within.
  2. 【請求項2】 前記液体顔料は、95〜97重量%の界面活性剤と、3〜5重量%の顔料とからなることを特徴とする請求項1記載の透明樹脂成形品のブルーイング方法。 Wherein said liquid pigment, 95-97% by weight of surfactant, 3-5 wt% of the brewing method of the transparent resin molded article according to claim 1, wherein the comprising a pigment.
  3. 【請求項3】 前記顔料は、無機系の群青系色素であることを特徴とする請求項2記載の透明樹脂成形品のブルーイング方法。 Wherein the pigment is a bluing method of claim 2 the transparent resin molded article, wherein it is a inorganic ultramarine-based pigments.
  4. 【請求項4】 液状の帯電防止剤に前記液体顔料を混合して混合液を生成し、該混合液を前記加熱スクリュー内 Wherein said antistatic agent liquid liquid colors are mixed to produce the mixture, the mixture within the heating screw
    注入することを特徴とする請求項記載の透明樹脂成形品のブルーイング方法。 Brewing method of claim 1 transparent resin molded article, wherein the injection into.
  5. 【請求項5】 前記混合液は、帯電防止剤に対して、液体顔料を5〜15重量%混合することを特徴とする請求項記載の透明樹脂成形品のブルーイング方法。 Wherein said mixture, relative to antistatic agents, claim 4 brewing method of the transparent resin molded article, wherein a mixing liquid pigment 5 to 15 wt%.
  6. 【請求項6】 請求項記載の混合液を、成形品に対して0.1〜0.5重量%注入することを特徴とする透明樹脂成形品のブルーイング方法。 6. The method of claim 5 the mixture according, brewing method of the transparent resin molded article characterized by injecting 0.1 to 0.5 wt% with respect to formed molded article.
JP21822692A 1992-07-24 1992-07-24 Bluing method of transparent resin molded article Expired - Fee Related JP3254249B2 (en)