JP3077318B2 - Shaped sheet and continuous production method of decorative board using the shaped sheet - Google Patents
Shaped sheet and continuous production method of decorative board using the shaped sheetInfo
- Publication number
- JP3077318B2 JP3077318B2 JP28636391A JP28636391A JP3077318B2 JP 3077318 B2 JP3077318 B2 JP 3077318B2 JP 28636391 A JP28636391 A JP 28636391A JP 28636391 A JP28636391 A JP 28636391A JP 3077318 B2 JP3077318 B2 JP 3077318B2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- resin
- decorative board
- roll
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】[0001]
【産業上の利用分野】本発明は、家具、デスク、テーブ
ル、建築内装材等に幅広く使用される表面に微細な凹凸
模様を有する熱硬化性樹脂化粧板において、ロール状の
賦型シート及びロール状の賦型シートを用いた、ジアリ
ルフタレート樹脂化粧板の連続製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a thermosetting resin decorative plate having a fine uneven pattern on its surface, which is widely used for furniture, desks, tables, building interior materials and the like. The present invention relates to a method for continuously producing a diallyl phthalate resin decorative board using a shaped imprint sheet.
【0002】[0002]
【従来の技術と問題点】従来から熱硬化性樹脂を用いた
化粧板の表面に凹凸模様を有するものとしては、エンボ
ス金型や樹脂凹凸板により凹凸模様を形成したものと、
賦型シートにより凹凸模様を形成したものがある(特公
平2−38398号公報参照)。しかし、エッチング、
サンドブラスト、彫刻等の処理により表面に微細な凹凸
模様を形成した、エンボス金型を用いた場合は、熱硬化
性樹脂化粧板製造時に、多段プレス機の段数分の枚数の
高価な金型及び予備の金型が必要であり、費用の負担が
増える。また、柄替え時に金型を取り替える必要もあ
り、製造コストも大幅に増加し製品が高価なものとな
る。また、樹脂凹凸板の場合は、熱硬化性樹脂化粧板と
が剥離しにくいために、型板との間に、アルミニウム
箔、ポリプロピレン、ポリエステル等のプラスチックフ
ィルム等を挟む必要があり、このために、微細な凹凸模
様を形成することは困難であった。2. Description of the Related Art Conventionally, a decorative plate made of a thermosetting resin having an uneven pattern on its surface includes an uneven pattern formed by an embossing die or a resin uneven plate.
There is a sheet in which a concavo-convex pattern is formed by a shaping sheet (see Japanese Patent Publication No. 2-38398). But etching,
When using an embossed mold with a fine uneven pattern formed on the surface by sandblasting, engraving, etc., when manufacturing a thermosetting resin decorative board, expensive molds and spare Mold is required, and the cost burden increases. In addition, it is necessary to change the mold at the time of changing the pattern, which significantly increases the manufacturing cost and makes the product expensive. In the case of a resin uneven plate, it is necessary to sandwich a plastic film such as an aluminum foil, a polypropylene, or a polyester between the mold plate and the thermosetting resin decorative plate, since the decorative plate is difficult to peel off. However, it was difficult to form a fine uneven pattern.
【0003】又、賦型シートを用いた場合においても既
存技術では、微細な凹凸模様を形成することは難しく、
例えば、熱可塑性樹脂フィルムに微細な凹凸模様を形成
した賦型シートを用いて、熱硬化性樹脂化粧板を製造し
ようとしても、耐熱性、耐圧性が化粧板製造時の熱圧よ
り劣っているため、凹凸模様を保持することができず、
表面の凹凸がなくなってしまう。又、融点が高くても、
樹脂の塑性流動により賦型シートと化粧板が融着状態に
なり易く、賦型シートの剥離が困難になってしまう。ま
た、一度使用した賦型シートは繰り返して使用すること
ができない。[0003] In addition, even when a shaping sheet is used, it is difficult to form a fine uneven pattern by the existing technology.
For example, using a shaped sheet in which a fine uneven pattern is formed on a thermoplastic resin film, even if an attempt is made to produce a thermosetting resin decorative board, the heat resistance and pressure resistance are inferior to the hot pressure during the production of the decorative board. Therefore, it is not possible to maintain the uneven pattern,
Surface irregularities disappear. Also, even if the melting point is high,
Due to the plastic flow of the resin, the shaping sheet and the decorative board are likely to be in a fused state, and it is difficult to peel off the shaping sheet. Further, the shaping sheet used once cannot be used repeatedly.
【0004】[0004]
【発明が解決しようとする課題】本発明は、上記従来技
術の問題点を解決し、化粧板製造時の熱圧に耐える特性
を持ち、かつ、剥離の軽いロール状の賦型シートと該ロ
ール状の賦型シートを用いて、表面に微細な凹凸模様を
形成した、熱硬化性樹脂化粧板の連続製造方法の提供を
目的とする。DISCLOSURE OF THE INVENTION The present invention solves the above-mentioned problems of the prior art, and provides a roll-shaped shaping sheet having the property of withstanding the heat and pressure during the production of a decorative board and having a light peeling property. It is an object of the present invention to provide a method for continuously producing a thermosetting resin decorative board having a fine uneven pattern formed on the surface thereof by using a shaped imprint sheet.
【0005】[0005]
【課題を解決するための手段】本発明は、上記課題を解
決するために考えられたもので、基材シート上に厚さ1
0μm〜40μmの耐熱性樹脂層を設け、該耐熱性樹脂
層の表面に深さ1〜60μmの連続した微細な凹凸模様
を設けたロール状の賦型シートにおいて、前記耐熱性樹
脂層に0.5%〜5%の離型剤を添加混合したことを特
徴とする熱硬化性樹脂化粧板の連続製造用のロール状の
賦型シートである。SUMMARY OF THE INVENTION The present invention has been conceived in order to solve the above problems, and has a thickness of 1 mm on a base sheet.
In a roll-shaped imprinting sheet provided with a heat-resistant resin layer having a thickness of 0 μm to 40 μm, and a continuous fine uneven pattern having a depth of 1 to 60 μm provided on the surface of the heat-resistant resin layer, the heat-resistant resin layer has a thickness of 0.1 μm . It is a roll-shaped shaped sheet for continuous production of a thermosetting resin decorative board, characterized in that 5% to 5% of a release agent is added and mixed.
【0006】また、ロール状の賦型シートの微細な凹凸
模様面を、熱硬化性樹脂を含浸した樹脂含浸紙に接する
ように重ね、加熱加圧成形し、樹脂含浸紙の樹脂が硬化
したあと、賦型シートを剥離することからなる熱硬化性
樹脂化粧板の連続製造方法において、前記ロール状の賦
型シートとして上記のロール状の賦型シートを使用する
と共に、前記樹脂含浸紙の樹脂中に0.5%〜5%の離
型剤を添加混合したことを特徴とする熱硬化性樹脂化粧
板の連続製造方法である。[0006] Further , the fine uneven surface of the roll-shaped imprinting sheet is overlapped so as to be in contact with a resin-impregnated paper impregnated with a thermosetting resin, and is heated and pressed to form a resin. , Thermosetting consisting of exfoliating the molding sheet
In the continuous production method for a resin decorative board, the roll-shaped
Use the above roll-shaped imprint sheet as the mold sheet
And a method for continuously producing a thermosetting resin decorative board , wherein 0.5% to 5% of a release agent is added to and mixed with the resin of the resin-impregnated paper.
【0007】また、前記樹脂含浸紙の熱硬化性樹脂が、
ジアリルフタレート樹脂であることを特徴とする上記の
熱硬化性樹脂化粧板の連続製造方法である。 Further, thermosetting resin in the resin-impregnated paper,
The above, which is a diallyl phthalate resin
This is a method for continuously producing a thermosetting resin decorative board.
【0008】[0008]
【0009】図に基づき詳細に説明する。図1(a)は
エンボスフィルムの断面図である。このエンボスフィル
ム(1)は、図1(b)に示す積層シート(2)の表面
に凹凸模様を精度良く型押しするもので、表面に凹凸模
様(1b)を形成させた熱可塑性フィルム(1a)であ
る。熱可塑性フィルム(1a)は、賦型シートの表面を
形成するものであり、表面が平滑で凹凸形成の可能なも
のであることが必要である。例えば、ポリ塩化ビニルフ
ィルム、アクリル樹脂フィルム等が使用できる。This will be described in detail with reference to the drawings. FIG. 1A is a cross-sectional view of the embossed film. This embossed film (1) is used to accurately emboss a concave and convex pattern on the surface of the laminated sheet (2) shown in FIG. 1 (b), and a thermoplastic film (1a) having a concave and convex pattern (1b) formed on the surface. ). The thermoplastic film (1a) forms the surface of the imprinting sheet, and needs to have a smooth surface and be capable of forming irregularities. For example, a polyvinyl chloride film, an acrylic resin film, or the like can be used.
【0010】このエンボスフィルム(1)は、公知の方
法により形成できる。すなわち、ロール状のエンボス金
型等を用いて熱可塑性フィルムに重ね、熱圧することに
より凹凸模様を形成することが出来る。この凹凸模様
は、万線模様を小片にしてランダムに組み合わせて形成
した、例えば、深さ1〜60μmの微細な凹凸模様(図
5参照)であり意匠効果が優れたものである。The embossed film (1) can be formed by a known method. That is, an uneven pattern can be formed by laminating on a thermoplastic film using a roll-shaped embossing die or the like and applying heat and pressure. The concavo-convex pattern is, for example, a fine concavo-convex pattern having a depth of 1 to 60 μm (see FIG. 5) formed by randomly combining the line pattern into small pieces, and has an excellent design effect.
【0011】図1(b)は、積層シートの断面図であ
る。積層シート(2)は賦型シートの基になるもので、
基材シート(2a)と、耐熱性樹脂層(2b)とからな
る。基材シート(2a)は、耐熱性樹脂層の支持体とな
って、破れたり、伸縮したりすることを防ぐものであ
る。基材シート(2a)としては、耐熱性樹脂層(2
b)形成時の熱、あるいは、エンボスフィルム(1)と
重ねて微細な凹凸模様を形成する際、あるいは、化粧板
製造時の熱圧によって破れたり、融着したり、伸縮した
りしないことが要求される。この様な基材シートとして
は、紙、ポリエステルフィルム、アルミ箔等の金属箔、
または、その積層シート等が使用できる。FIG. 1B is a cross-sectional view of the laminated sheet. The laminated sheet (2) is the base of the shaped sheet,
It comprises a base sheet (2a) and a heat-resistant resin layer (2b). The base sheet (2a) serves as a support for the heat-resistant resin layer, and prevents the base sheet from being torn or stretched. As the base sheet (2a), a heat-resistant resin layer (2
b) It is not broken, fused or expanded or contracted by heat at the time of formation, or when forming a fine uneven pattern by overlapping with the embossed film (1), or by heat and pressure at the time of manufacturing a decorative board. Required. Such base sheets include paper, polyester film, metal foil such as aluminum foil,
Alternatively, the laminated sheet or the like can be used.
【0012】耐熱性樹脂層(2b)は、軟化状態でエン
ボスフィルム(1)の表面の凹凸模様を再現するもので
あり、その表面にエンボスフィルム(1)と重ねるさい
に軟化して、凹凸模様が精度良く反転再現できること、
化粧板製造時に凹凸形状を保持することが必要である。
すなわち、化粧板成型時の熱圧条件を超える耐熱性、耐
圧性があれば凹凸形状の保持には問題なく、また、耐熱
性が、化粧板製造時の最高温度より低くても形状が保持
できる場合もある。例えば、この耐熱性樹脂として、ポ
リメチルペンテン樹脂、ポリプロピレン樹脂、ポリエチ
レン樹脂等が使用することができる。The heat-resistant resin layer (2b) is for reproducing an embossed pattern on the surface of the embossed film (1) in a softened state. Can be inverted and reproduced with high accuracy,
It is necessary to maintain the uneven shape during the production of the decorative board.
That is, there is no problem in maintaining the uneven shape if there is heat resistance and pressure resistance exceeding the heat and pressure conditions at the time of decorative board molding, and the heat resistance can maintain the shape even if it is lower than the maximum temperature at the time of decorative board production. In some cases. For example, a polymethylpentene resin, a polypropylene resin, a polyethylene resin, or the like can be used as the heat-resistant resin.
【0013】この耐熱性樹脂層(2b)は、任意の方法
にて形成できるが、溶融状態の合成樹脂を押し出しダイ
から押し出して、基材シート(2a)上に積層する方法
(押し出しラミネーション法)が好ましい。この耐熱性
樹脂中に、離型剤(2c)を添加混合するが、添加混合
の場合ペレット状の時や、溶融状態のときに行うとよ
い。又、離型剤としては、シリコン樹脂やふっ素樹脂等
の離型性の良い樹脂を使用することができる。又、添加
量は0.5%〜5%の範囲がよい。引き続いて、エンボ
スフィルム(1)を重ねることにより、耐熱性樹脂層
(2b)の形成と、その表面に微細な凹凸模様の形成を
するが、一連の工程で可能になる。耐熱性樹脂層(2
b)は、その材質に応じて150℃〜330℃の温度で
ダイから押し出される。厚みは、凹凸の深さに応じて5
μm〜50μmの厚みを設定するとよい。The heat-resistant resin layer (2b) can be formed by any method, but a method of extruding a synthetic resin in a molten state from an extrusion die and laminating it on a base sheet (2a) (extrusion lamination method). Is preferred. The release agent (2c) is added and mixed into the heat-resistant resin. The addition and mixing may be performed in a pellet form or in a molten state. Further, as the release agent, a resin having a good release property such as a silicone resin or a fluororesin can be used. The addition amount is preferably in the range of 0.5% to 5%. Subsequently, the heat-resistant resin layer (2b) is formed by superimposing the embossed film (1), and a fine uneven pattern is formed on the surface thereof. Heat resistant resin layer (2
b) is extruded from the die at a temperature between 150 ° C. and 330 ° C. depending on its material. The thickness is 5 according to the depth of the unevenness.
It is preferable to set a thickness of μm to 50 μm.
【0014】図1(c)は、エンボスフィルム(1)と
積層シート(2)を重ね合わせて加圧した状態の説明図
である。賦型シート(3)は、前記の耐熱性樹脂層(2
b)に離型剤(2c)を添加混合した後、加熱軟化した
状態で、エンボスフィルム(1)を重ね、加圧して、凹
凸模様(1b)を耐熱性樹脂層(2b)上に転写して得
られるものである。 前述したように、溶融した耐熱性
樹脂を基材シート(2a)上に押し出しラミネーション
する工程に続いて、エンボスフィルム(1)を耐熱性樹
脂層(2b)に重ねて加圧する方法が好適であり、均一
に軟化した耐熱性樹脂層(2b)を利用することが出来
る。エンボスフィルム(1)は、溶融した耐熱性樹脂が
50℃〜150℃の温度になったときに重ねればよく、
加圧は2本のニップロールもしくはニップロールと冷却
ロールの間で行われる。耐熱性樹脂層(2b)が充分に
冷却して固化した後、エンボスフィルム(1)を剥離除
去して賦型シート(3)が得られる(図1(d)参
照)。FIG. 1C is an explanatory view showing a state in which the embossed film (1) and the laminated sheet (2) are overlaid and pressed. The shaping sheet (3) is made of the heat-resistant resin layer (2)
After the release agent (2c) is added to and mixed with b), the embossed film (1) is overlaid in a state of being heated and softened, and pressed to transfer the concavo-convex pattern (1b) onto the heat-resistant resin layer (2b). It can be obtained by As described above, following the step of extruding and laminating the melted heat-resistant resin onto the base sheet (2a), a method in which the embossed film (1) is overlaid on the heat-resistant resin layer (2b) and pressed is preferable. It is possible to use the heat-resistant resin layer (2b) softened uniformly. The embossed film (1) may be stacked when the melted heat-resistant resin reaches a temperature of 50C to 150C.
The pressure is applied between two nip rolls or between the nip roll and the cooling roll. After the heat-resistant resin layer (2b) is sufficiently cooled and solidified, the embossed film (1) is peeled off to obtain a shaped sheet (3) (see FIG. 1 (d)).
【0015】次に、賦型シート(3)は熱硬化性樹脂化
粧板、例えば、ジアリルフタレート樹脂化粧板等の加熱
加圧を必要とする化粧板を製造する際、その表面に重ね
ることにより、熱硬化性樹脂化粧板の表面に微細な凹凸
模様が転写される。図2は、ジアリルフタレート化粧板
の製造方法における積層構成を示す説明図である。すな
わち、図2において、上下熱板(10,10)、耐熱ク
ッションシート(9,9)、鏡面板(8,8)の間に下
記のものを下から順に積層する。(7)はバッカー紙で
あり坪量55g/m2 〜160g/m2のチタン紙にジ
アルフタレート樹脂を40%〜100%含浸させ乾燥し
た含浸紙であり、化粧板の反り防止の役割を果たす。コ
アー紙(6)はジアリルフタレート樹脂化粧板の基材と
なるものであり、坪量140g/m2 〜180g/m2
の紙にフェノール樹脂を30%〜100%含浸させて乾
燥したものである。コアー紙(6)は、ジアリルフタレ
ート樹脂化粧板の厚みを決定するものであり、1〜4枚
程度重ねて使用するとよい。樹脂含浸チタン紙(5)
は、チタン紙に、場合により絵柄を印刷し、ジアリルフ
タレート樹脂を40%〜100%含浸させ乾燥したもの
である。尚、前記の樹脂含浸チタン紙(5)は、チタン
紙にジアリルフタレート樹脂を含浸するときに、離型剤
として、シリコーン樹脂やふっ素樹脂、等のいずれかを
添加し混合しておいたものである。但し、離型剤は賦型
シートの耐熱性樹脂層に添加混合しておくことで、樹脂
含浸チタン紙のジアリルフタレート樹脂への添加はしな
くてもよい。Next, when the decorative sheet (3) is manufactured on a thermosetting resin decorative board, for example, a decorative board which requires heating and pressurizing, such as a diallyl phthalate resin decorative board, it is superimposed on the surface thereof. A fine uneven pattern is transferred to the surface of the thermosetting resin decorative board. FIG. 2 is an explanatory view showing a lamination structure in the method for producing a diallyl phthalate decorative board. That is, in FIG. 2, the following are laminated in order from the bottom between the upper and lower heating plates (10, 10), the heat-resistant cushion sheets (9, 9), and the mirror plates (8, 8). (7) is impregnated paper in which the is basis weight 55g / m 2 ~160g / m 2 of titanium paper Jiarufutareto resin a backer paper impregnated 40% to 100% dry, serve warp preventive veneer . The core paper (6) serves as a base material of the diallyl phthalate resin decorative board, and has a basis weight of 140 g / m 2 to 180 g / m 2.
Is impregnated with 30% to 100% of a phenolic resin and dried. The core paper (6) determines the thickness of the diallyl phthalate resin decorative board, and it is preferable to use about 1 to 4 sheets of the decorative paper. Resin-impregnated titanium paper (5)
Is a paper obtained by printing a picture on titanium paper as necessary, impregnating with 40% to 100% of diallyl phthalate resin, and drying. The resin-impregnated titanium paper (5) is prepared by adding and mixing a silicone resin or a fluorine resin as a release agent when impregnating a diallyl phthalate resin into titanium paper. is there. However, it is not necessary to add the release agent to the diallyl phthalate resin of the resin-impregnated titanium paper by adding and mixing the release agent to the heat-resistant resin layer of the molding sheet.
【0016】図4は一実施例によるロール状の賦型シー
トを使用して化粧板の連続製造方法を示す説明図であ
る。 前記に示したように、積層セット(図3参照)さ
れた化粧板基材(20)を図4に示すようなプレス装置
に入れて、加熱加圧し、最高温度110℃〜130℃、
圧力は10kgf/cm2 〜30kgf/cm2 、プレ
ス時間1分〜10分間加熱加圧成形した後、前記の樹脂
含浸紙(5)からバッカー紙(7)間の樹脂を硬化させ
て、ロール状の賦型シート(3)を剥がすと一体化した
ジアリルフタレート樹脂化粧板を得ることができる。こ
の時、ロール状の賦型シート(3)は、ジアリルフタレ
ート樹脂化粧板から容易に剥離することができる。FIG. 4 is an explanatory view showing a continuous production method of a decorative board using a roll-shaped forming sheet according to one embodiment. As described above, the decorative board base material (20) that has been laminated and set (see FIG. 3) is placed in a press device as shown in FIG. 4, and heated and pressed to a maximum temperature of 110 ° C. to 130 ° C.
Pressure 10kgf / cm 2 ~30kgf / cm 2 , after pressing time heat pressure molding 1 minute to 10 minutes, to cure the resin between the backer sheet (7) from the resin-impregnated paper (5), a roll When the shaping sheet (3) is peeled off, an integrated diallyl phthalate resin decorative board can be obtained. At this time, the roll-shaped shaping sheet (3) can be easily peeled off from the diallyl phthalate resin decorative board.
【0017】[0017]
【作用】本発明は、以上の構成になっており、深さ1μ
m〜60μmの微細な凹凸模様を設けたジアリルフタレ
ート樹脂化粧板であり、光の反射方向により立体感が現
出し充分に意匠効果が優れたものになる。又、微細な凹
凸模様と調和した絵柄を印刷することにより優れた視覚
的効果を現出し、かつ、加熱加圧成型後、化粧板から賦
型シートを容易に剥離することができる。又、ロール状
の賦型シートとジアリルフタレート樹脂を用いることで
加熱加圧の時間が大幅に短縮することができる。即ち、
他の熱硬化性樹脂化粧板と比べ、熱、圧力とも低いとこ
ろで成形でき、しかも短時間プレスが可能である。この
ことで、賦型シートの剥離のよさとの相乗効果により化
粧板の連続生産が可能となる。The present invention has the above-described structure and has a depth of 1 μm.
This is a diallyl phthalate resin decorative plate provided with a fine uneven pattern of m to 60 μm, and a three-dimensional effect appears according to the direction of light reflection, and the design effect is sufficiently excellent. In addition, by printing a pattern that is in harmony with the fine uneven pattern, an excellent visual effect can be obtained, and the shaping sheet can be easily peeled off from the decorative plate after the heat and pressure molding. Further, by using the roll-shaped imprinting sheet and the diallyl phthalate resin, the time for heating and pressing can be greatly reduced. That is,
Compared to other thermosetting resin decorative boards, it can be molded in places where both heat and pressure are low, and can be pressed for a short time. This enables continuous production of decorative boards due to a synergistic effect with the good peelability of the shaping sheet.
【0018】[0018]
<実施例1> エンボスフィルム エンボスフィルムは、厚さ70μmのポリ塩化ビニルフ
ィルム表面に、微細な凹凸模様を有するエンボス金型を
用いて、熱圧プレスにより図5に示すような凹凸模様を
成形する。<Example 1> Embossed film An embossed film is formed on a surface of a polyvinyl chloride film having a thickness of 70 µm by using an embossing die having a fine unevenness pattern by hot-pressing to form an unevenness pattern as shown in Fig. 5. .
【0019】ロール状の賦型フィルム ロール状の賦型シートは、坪量100g/m2 のクラフ
ト紙に押出し温度290℃で、ポリメチルペンテン樹脂
を厚さ20μmに押し出しラミネートした後、離型剤と
してシリコン樹脂を3%添加混合し、約140℃に加熱
した後、ニップロールと冷却ロール間で加圧するととも
に冷却をした。充分に冷却した後、エンボスフィルムで
あるポリ塩化ビニルフィルムのみを剥離除去してロール
状の賦型シートを得た。Roll-shaped forming film The roll-shaped forming sheet is extruded onto kraft paper having a basis weight of 100 g / m 2 at a temperature of 290 ° C., extruded with a polymethylpentene resin to a thickness of 20 μm, laminated, and then subjected to a release agent. Then, after adding and mixing 3% of a silicon resin and heating to about 140 ° C., pressure was applied between a nip roll and a cooling roll and cooling was performed. After sufficiently cooling, only the polyvinyl chloride film as the embossed film was peeled off to obtain a roll-shaped imprinted sheet.
【0020】ジアリルフタレート樹脂化粧板 ジアリルフタレート樹脂化粧板は、下部熱盤上に順次、
耐熱クッションシート、鏡面板と、バッカー紙、4枚の
コアー紙、坪量80g/m2 のチタン紙にストライプ柄
を印刷し、ジアリルフタレート樹脂を含浸した含浸紙の
化粧板基材(20)と、更に前記のロール状の賦型シー
ト、鏡面板、耐熱クッションシートを積層し、上部及び
下部熱盤により加熱加圧した。加熱は最高温度130
℃、圧力30kgf/cm2 の条件で5分間行ない、そ
の後圧力を開放し賦型シートを剥離してジアリルフタレ
ート樹脂化粧板を製造した。この化粧板は前記エンボス
フィルム(1)、賦型シート(3)の微細な凹凸模様を
反転した凹凸模様をもち、更に、下層に印刷したストラ
イプ柄をもつ極めて意匠効果の高いジアリルフタレート
樹脂化粧板が得られた。なお、凹凸模様は本実施例のも
のに限定するものではなく、例えば幾何学的模様等でも
よい。又、賦型シートはロール状であるため一回加熱加
圧成形した後、順次取り出すことにより連続でジアリル
フタレート樹脂化粧板を製造することができる。又、本
発明の賦型シートは8回〜10回程度の連続して使用で
き、更にロール状になっているので連続してシートを供
給でき作業効率がよい。The diallyl phthalate resin decorative plate is sequentially placed on the lower heating plate.
Heat-resistant cushion sheet, mirror plate, backer paper, 4 core papers, decorative paper substrate (20) of impregnated paper impregnated with diallyl phthalate resin printed with stripe pattern on titanium paper of 80 g / m 2 basis weight Further, the above-mentioned roll-shaped forming sheet, mirror surface plate, and heat-resistant cushion sheet were laminated, and heated and pressed by the upper and lower heating plates. Heating temperature up to 130
° C., carried out for 5 minutes under a pressure of 30 kgf / cm 2, to produce a diallyl phthalate resin decorative plate was subsequently peeled open Fugata sheet pressure. This decorative board has a concave and convex pattern obtained by inverting the fine concave and convex pattern of the embossed film (1) and the shaping sheet (3), and further has a very high design effect diallyl phthalate resin decorative board having a stripe pattern printed on the lower layer. was gotten. Note that the uneven pattern is not limited to that of the present embodiment, and may be, for example, a geometric pattern. Further, since the shaping sheet is in the form of a roll, it is heated and pressed once, and then is sequentially taken out, whereby a decorative diallyl phthalate resin decorative board can be manufactured continuously. In addition, the shaped sheet of the present invention can be used continuously for about 8 to 10 times, and since it is in the form of a roll, the sheet can be continuously supplied and the working efficiency is good.
【0021】<比較例1>剥離性を比較するため、シリ
コン樹脂添加量を変化させて、剥離性とジアリルフタレ
ート樹脂化粧板の表面状態(凹凸模様)の再現性を比較
した。Comparative Example 1 In order to compare the releasability, the releasability and the reproducibility of the surface state (concavo-convex pattern) of the diallyl phthalate resin decorative board were compared by changing the amount of the silicone resin added.
【0022】[0022]
【表1】 [Table 1]
【0023】なお、実施例1と比較例Cは、10回加熱
加圧成形して化粧板を製造しても剥離性は充分に保たれ
ていた。In Example 1 and Comparative Example C, the releasability was sufficiently maintained even when a decorative plate was manufactured by heating and pressing 10 times.
【0024】[0024]
【発明の効果】本発明は以上の構成になっているので表
面に微細な(深さ1〜60μ)凹凸模様を有する賦型シ
ートが得られ、その賦型シートを用いることにより、視
覚的効果の優れた微細な凹凸模様を有する化粧板を得る
ことができる。又、賦型シートがロール状であるため、
加熱加圧成形を連続して行うことができ、化粧板を短時
間に能率よく生産することが可能となった。又、ロール
状の賦型シートには離型剤が添加混合してあるため、加
熱加圧成形後に化粧板から賦型シートを剥離するとき、
剥離が軽いので損傷しにくく、又表面の凹凸模様が消え
にくいため(他の熱硬化性樹脂化粧板と比較して、低
温、低圧で短時間で成形できるため)同じ賦型シートを
8回〜10回程度繰り返し使用することができる。According to the present invention, a shaping sheet having a fine (depth 1 to 60 .mu.) Irregular pattern on the surface can be obtained, and the visual effect can be obtained by using the shaping sheet. A decorative board having a fine uneven pattern excellent in the above can be obtained. Also, since the shaping sheet is in the form of a roll,
Heat-press molding can be performed continuously, and it has become possible to efficiently produce decorative boards in a short time. Also, since the release agent is added and mixed in the roll-shaped imprinting sheet, when peeling off the imprinting sheet from the decorative sheet after hot press molding,
Since the peeling is light, it is difficult to damage, and the uneven pattern on the surface is hard to disappear (because it can be molded in a short time at low temperature and low pressure compared to other thermosetting resin decorative boards), the same imprint sheet is repeated 8 times ~ It can be used repeatedly about 10 times.
【図面の簡単な説明】[Brief description of the drawings]
【図1】(a)一実施例によるエンボスフィルムの断面
図である。(b)一実施例による積層シートの断面図で
ある。(c)積層シートにエンボスフィルムを重ね合わ
せ加圧した状態示す説明図である。(d)エンボスフィ
ルムを剥離してできあがった賦型シートの構成を示す断
面図である。FIG. 1A is a cross-sectional view of an embossed film according to one embodiment. (B) It is sectional drawing of the laminated sheet by one Example. (C) It is explanatory drawing which shows the state which superimposed and pressed the embossed film on the laminated sheet. (D) It is sectional drawing which shows the structure of the shaping sheet completed by peeling an embossed film.
【図2】一実施例によるジアリルフタレート樹脂化粧板
の製造方法における積層構成を示す説明図である。FIG. 2 is an explanatory view showing a lamination structure in a method for manufacturing a diallyl phthalate resin decorative board according to one embodiment.
【図3】一実施例によるジアリルフタレート樹脂化粧板
基材の積層構成を示す説明図である。FIG. 3 is an explanatory view showing a laminated structure of a diallyl phthalate resin decorative board substrate according to one embodiment.
【図4】一実施例によるロール状の賦型シートを使用し
て化粧板の連続製造方法を示す説明図である。FIG. 4 is an explanatory view showing a method for continuously manufacturing a decorative board using a roll-shaped imprinting sheet according to one embodiment.
【図5】一実施例によるジアリルフタレート樹脂化粧板
表面の微細な凹凸模様を拡大した平面図である。FIG. 5 is an enlarged plan view of a fine concavo-convex pattern on a diallyl phthalate resin decorative plate surface according to one embodiment.
1 …エンボスフィルム 1(a)…熱可塑性樹脂フィルム 1(b)…凹凸模様 2 …積層シート 2(a)…基材シート 2(b)…耐熱性樹脂層 2(c)…離型剤 3 …ロール状の賦型シート 5 …チタン紙(含浸紙) 6 …フェノールコア紙 7 …バッカー紙 8 …鏡面板 9 …耐熱クッションシート 10 …熱盤 20 …セットされた化粧板基材 DESCRIPTION OF SYMBOLS 1 ... Embossed film 1 (a) ... Thermoplastic resin film 1 (b) ... Concavo-convex pattern 2 ... Laminated sheet 2 (a) ... Base sheet 2 (b) ... Heat resistant resin layer 2 (c) ... Release agent 3 … Roll-shaped imprinting sheet 5… Titanium paper (impregnated paper) 6… Phenolic paper 7… Backer paper 8… Mirror plate 9… Heat-resistant cushion sheet 10… Hot plate 20… Set decorative board base material
───────────────────────────────────────────────────── フロントページの続き (58)調査した分野(Int.Cl.7,DB名) B32B 1/00 - 35/00 B44C 1/24 ──────────────────────────────────────────────────続 き Continued on the front page (58) Field surveyed (Int. Cl. 7 , DB name) B32B 1/00-35/00 B44C 1/24
Claims (3)
耐熱性樹脂層を設け、該耐熱性樹脂層の表面に深さ1〜
60μmの連続した微細な凹凸模様を設けたロール状の
賦型シートにおいて、前記耐熱性樹脂層に0.5%〜5
%の離型剤を添加混合したことを特徴とする熱硬化性樹
脂化粧板の連続製造用のロール状の賦型シート。1. A heat-resistant resin layer having a thickness of 10 μm to 40 μm is provided on a substrate sheet, and a surface of the heat-resistant resin layer having a depth of 1 to 40 μm is provided.
In a roll-shaped imprinting sheet provided with a continuous fine uneven pattern of 60 μm, the heat-resistant resin layer has a thickness of 0.5% to 5%.
% Thermosetting resin characterized by adding and mixing a mold release agent
Roll-shaped imprinting sheet for continuous production of fat decorative boards .
を、熱硬化性樹脂を含浸した樹脂含浸紙に接するように
重ね、加熱加圧成形し、樹脂含浸紙の樹脂が硬化したあ
と、賦型シートを剥離することからなる熱硬化性樹脂化
粧板の連続製造方法において、前記ロール状の賦型シー
トとして、請求項1に記載のロール状の賦型シートを使
用すると共に、前記樹脂含浸紙の樹脂中に0.5%〜5
%の離型剤を添加混合したことを特徴とする熱硬化性樹
脂化粧板の連続製造方法。2. The method according to claim 1, wherein the finely patterned surface of the roll-shaped imprinting sheet is overlapped so as to be in contact with a resin-impregnated paper impregnated with a thermosetting resin. Thermosetting resin by peeling off the molding sheet
In the continuous production method of decorative board, the roll-shaped forming sheet is provided.
The roll-shaped shaping sheet according to claim 1 is used as the
And 0.5% to 5% in the resin of the resin-impregnated paper.
% Thermosetting resin characterized by adding and mixing a mold release agent
Continuous production method of fat decorative board.
樹脂であることを特徴とする請求項2に記載の熱硬化性
樹脂化粧板の連続製造方法。3. The thermosetting resin according to claim 2, wherein the thermosetting resin is a diallyl phthalate resin .
Continuous production method of resin decorative board.