JP2991333B2 - Substrate for concrete slab and method of manufacturing the same - Google Patents

Substrate for concrete slab and method of manufacturing the same

Info

Publication number
JP2991333B2
JP2991333B2 JP8200461A JP20046196A JP2991333B2 JP 2991333 B2 JP2991333 B2 JP 2991333B2 JP 8200461 A JP8200461 A JP 8200461A JP 20046196 A JP20046196 A JP 20046196A JP 2991333 B2 JP2991333 B2 JP 2991333B2
Authority
JP
Japan
Prior art keywords
concrete
substrate
embedding material
hole
filling
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP8200461A
Other languages
Japanese (ja)
Other versions
JPH1044125A (en
Inventor
典行 一柳
雅之 太田
悟 小林
成太郎 海老
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kanayama Kasei Co Ltd
Original Assignee
Kanayama Kasei Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
Application filed by Kanayama Kasei Co Ltd filed Critical Kanayama Kasei Co Ltd
Priority to JP8200461A priority Critical patent/JP2991333B2/en
Publication of JPH1044125A publication Critical patent/JPH1044125A/en
Application granted granted Critical
Publication of JP2991333B2 publication Critical patent/JP2991333B2/en
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=16424700&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=JP2991333(B2) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【発明の属する技術分野】本発明は、コンクリート基板
の上に合成樹脂の発泡成形品からなる埋込材が配置され
て固定されている構造のコンクリートスラブ用基板及び
その製造方法に関するものである。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a concrete slab substrate having a structure in which an embedding material made of a synthetic resin foam molded article is arranged and fixed on a concrete substrate, and a method of manufacturing the same.

【0002】[0002]

【従来の技術】最近、建築物の床材,天井材として、コ
ンクリート基板の上に合成樹脂の発泡成形品からなる埋
込材を配置して係止具で固定した構造のコンクリートス
ラブ用基板が提案されている。
2. Description of the Related Art Recently, a concrete slab substrate having a structure in which an embedding material made of a synthetic resin foam molded product is arranged on a concrete substrate and fixed with a fastener as a floor material and a ceiling material of a building. Proposed.

【0003】このようなコンクリートスラブ用基板を用
いて、その上に現場にてコンクリートを打設して建築物
の床,天井を構成することにより、建築物の床,天井の
構築の省力化や軽量化が図れ、かつ優れた遮音性能が得
られる等の利点がある。このような構造のコンクリート
スラブ用基板の製造は、型枠内にコンクリート基板を形
成するコンクリートを打設した後、該コンクリート基板
が未だ硬化していない養生過程中に、凝結の度合いをみ
ながら、その上面に埋込材を配設し、該埋込材を係止具
で該コンクリート基板に固定することにより行われてい
た。
[0003] By using such a substrate for concrete slab and pouring concrete on site to construct the floor and ceiling of a building, labor saving of building floor and ceiling can be achieved. There are advantages such as weight reduction and excellent sound insulation performance. In the production of a substrate for a concrete slab having such a structure, after placing concrete for forming a concrete substrate in a formwork, during the curing process in which the concrete substrate is not yet hardened, while observing the degree of coagulation, An embedding material is provided on the upper surface, and the embedding material is fixed to the concrete substrate with a locking tool.

【0004】[0004]

【発明が解決しようとする課題】しかしながら、このよ
うなコンクリートスラブ用基板の製造では、作業員がコ
ンクリート基板の養生の状態を監視していて、適度な凝
結の度合いのときに埋込材をコンクリート基板の上に配
設し、半乾きの状態で係止具を打って該埋込材をコンク
リート基板に固定していたので、熟練の作業員の判断で
作業を進めなければならない問題点があった。
However, in the production of such a substrate for concrete slab, an operator monitors the state of curing of the concrete substrate, and when the degree of coagulation is moderate, the embedding material is removed from the concrete. Since the embedding material was fixed on the concrete board by arranging it on the board and hitting the locking member in a semi-dry state, there was a problem that the work had to be proceeded at the discretion of a skilled worker. Was.

【0005】また、この製造方法では、係止具が必ず必
要になって、コストアップの原因となる問題点があっ
た。
[0005] Further, in this manufacturing method, there is a problem that a locking tool is necessarily required, which causes an increase in cost.

【0006】本発明の目的は、コストの低減を図れる構
造のコンクリートスラブ用基板を提供することにある。
An object of the present invention is to provide a concrete slab substrate having a structure capable of reducing costs.

【0007】本発明の他の目的は、埋込材のコンクリー
ト基板への固定強度を向上できるコンクリートスラブ用
基板を提供することにある。
Another object of the present invention is to provide a concrete slab substrate capable of improving the fixing strength of an embedding material to a concrete substrate.

【0008】本発明の他の目的は、熟練を要しないで容
易に製造を行える構造のコンクリートスラブ用基板の製
造方法を提供することにある。
Another object of the present invention is to provide a method of manufacturing a concrete slab substrate having a structure that can be easily manufactured without requiring skill.

【0009】[0009]

【課題を解決するための手段】本発明は、コンクリート
基板の上に合成樹脂の発泡成形品からなる埋込材が配置
されて固定されているコンクリートスラブ用基板を改良
するものである。
SUMMARY OF THE INVENTION The present invention is to improve a concrete slab substrate in which an embedding material made of a synthetic resin foam molded article is arranged and fixed on a concrete substrate.

【0010】請求項1に記載のコンクリートスラブ用基
板においては、埋込材は底面側に開口する複数の空間が
設けられているとともに上下方向に貫通するコンクリー
ト充填貫通孔が設けられ、該コンクリート充填貫通孔
は、その水平断面におけるいずれかの箇所において上側
開口断面積が下側開口断面積より大きく形成され、該コ
ンクリート充填貫通孔内にはコンクリートが充填されて
コンクリート基板に一体となって固定されていることを
特徴とする。
[0010] In the concrete slab substrate according to the first aspect, the embedding material has a plurality of spaces opening to the bottom side.
Are concrete filled through hole penetrating in the vertical direction together are provided arranged, the concrete filled through hole, the upper opening cross-sectional area is larger than the lower opening cross-sectional area at any point in the horizontal section, the The concrete filling through hole is filled with concrete and is fixed integrally with the concrete substrate.

【0011】このように埋込材に上下方向に貫通するコ
ンクリート充填貫通孔を設け、該コンクリート充填貫通
孔を、その水平断面におけるいずれかの箇所において上
側開口断面積を下側開口断面積より大きい形状とし、該
コンクリート充填貫通孔内にコンクリートを充填する
と、該コンクリート充填貫通孔内のコンクリートがコン
クリート基板に一体となって固定され、そして該コンク
リート充填貫通孔内のコンクリートは、該コンクリート
充填貫通孔の形状から上部が下部より大きいため埋込材
を押さえることになり、該コンクリート充填貫通孔内の
コンクリートが埋込材をコンクリート基板に固定する。
Thus, the concrete filling through hole penetrating the embedding material in the up-down direction is provided, and the concrete filling through hole has an upper opening cross-sectional area larger than a lower opening cross-sectional area at any point in the horizontal cross section. When the concrete is filled into the concrete filling through hole, the concrete in the concrete filling through hole is fixed integrally to the concrete substrate, and the concrete in the concrete filling through hole is filled with the concrete filling through hole. Since the upper portion is larger than the lower portion, the embedding material is pressed down, and the concrete in the concrete filling through hole fixes the embedding material to the concrete substrate.

【0012】このように本発明のコンクリートスラブ用
基板は、係止具がなくても埋込材をコンクリート基板に
固定できるので、コストの低減を図ることができる。
As described above, in the concrete slab substrate of the present invention, since the embedding material can be fixed to the concrete substrate without the use of the locking member, the cost can be reduced.

【0013】請求項2に記載のコンクリートスラブ用基
板においては、埋込材の下面にコンクリート基板に食込
む食込み部が設けられていることを特徴とする。
According to a second aspect of the present invention, there is provided a concrete slab substrate, wherein a lower surface of the embedding material is provided with a cut-in portion which cuts into the concrete substrate.

【0014】このように埋込材の下面に食込み部を設け
ていると、型枠内にコンクリート基板を形成するコンク
リートを打設した後、該コンクリートの上面に埋込材を
配設したとき、食込み部がコンクリート基板に食込み、
埋込材が流動性をもつコンクリート上で移動するのを食
込み部で阻止でき、該埋込材の位置決めを容易に行うこ
とができる。
If the undercut portion is provided on the lower surface of the embedding material as described above, after the concrete forming the concrete substrate is cast in the formwork, when the embedding material is disposed on the upper surface of the concrete, The bite part cuts into the concrete board,
The embedding material can be prevented from moving on the concrete having fluidity by the bite portion, and the embedding material can be easily positioned.

【0015】請求項3に記載のコンクリートスラブ用基
板においては、その下縁に前記空間と外部とを連通する
連通溝が設けられていることを特徴とする。
The concrete slab substrate according to a third aspect of the present invention is characterized in that a communication groove for communicating the space with the outside is provided at a lower edge thereof.

【0016】このように底面側に開口する複数の空間が
設けられた埋込材の下縁に前記空間と外部とを連通する
連通溝を設けていると、型枠内に打設したコンクリート
基板を形成するコンクリートの上面に埋込材を配設した
とき、前記空間で覆われた部分のコンクリート上にある
水は埋込材の下縁に設けられた連通溝から外部に流れ出
すので、空間内の水溜りを防止できる。
When a communication groove for communicating the space with the outside is provided at the lower edge of the embedding material provided with the plurality of spaces opening to the bottom side as described above, the concrete substrate cast in the formwork is provided. When the embedding material is arranged on the upper surface of the concrete forming the water, the water on the concrete in the portion covered with the space flows out from the communication groove provided on the lower edge of the embedding material, so that Water can be prevented.

【0017】請求項4に記載のコンクリートスラブ用基
板においては、埋込材は、コンクリート充填貫通孔内に
係止された係止頭部と該係止頭部に一体に設けられてい
てコンクリート基板内に埋設されるアンカー脚部とを備
えた補強材でコンクリート基板に定着されていることを
特徴とする。
In the concrete slab substrate according to a fourth aspect of the present invention, the embedding material is provided integrally with the locking head locked in the concrete filling through-hole and the locking head. And anchoring to the concrete substrate with a reinforcing material having an anchor leg buried therein.

【0018】このようにコンクリート充填貫通孔内に係
止された係止頭部と該係止頭部に一体に設けられていて
コンクリート基板内に埋設されるアンカー脚部とを備え
た補強材で埋込材をコンクリート基板に定着させると、
コンクリート充填貫通孔内のコンクリートによる埋込材
のコンクリート基板に対する定着強度を一層向上させる
ことができる。
The reinforcing member having the locking head locked in the concrete filling through hole and the anchor leg integrally provided on the locking head and embedded in the concrete substrate. When the embedding material is fixed on the concrete substrate,
The fixing strength of the embedding material made of concrete in the concrete filling through hole to the concrete substrate can be further improved.

【0019】また、本発明は、コンクリート基板の上に
合成樹脂の発泡成形品からなる埋込材が配置されて固定
されている構造のコンクリートスラブ用基板の製造方法
を改良するものである。
The present invention also improves a method of manufacturing a concrete slab substrate having a structure in which an embedding material made of a synthetic resin foam molded article is arranged and fixed on a concrete substrate.

【0020】請求項5に記載のコンクリートスラブ用基
板の製造方法においては、埋込材としては底面側に開口
する複数の空間が設けられているとともに上面側開口部
が下面側開口部より大きい形状のコンクリート充填貫通
孔が上下方向に貫通して設けられている構造のものを用
い、コンクリート基板を形成するコンクリートを型枠内
に打設した後、該コンクリートの上面に埋込材を配設
し、次に該埋込材のコンクリート充填貫通孔内にコンク
リートを充填して下側のコンクリート基板を形成するコ
ンクリートと一体化させることを特徴とする。
In the method for manufacturing a substrate for a concrete slab according to a fifth aspect, the embedding material has an opening on the bottom side.
Concrete structure forming a concrete substrate using a structure in which a plurality of spaces are provided and a concrete filling through hole having a shape in which the upper side opening is larger than the lower side opening is provided penetrating vertically. After the concrete is cast into the formwork, an embedding material is disposed on the upper surface of the concrete, and then concrete is filled in the concrete filling through hole of the embedding material to form a concrete substrate on the lower side. It is characterized by being integrated with.

【0021】このように埋込材として、上面側開口部が
下面側開口部より大きい形状のコンクリート充填貫通孔
が上下方向に貫通して設けられている構造のものを用い
て、コンクリート基板を形成するコンクリートを型枠内
に打設した後、該コンクリートの上面に埋込材を配設
し、次に該埋込材のコンクリート充填貫通孔内にコンク
リートを充填して下側のコンクリート基板を形成するコ
ンクリートと一体化させる方法をとると、埋込材はコン
クリート基板を形成するコンクリートが未硬化で流動性
をもつ状態で配設することができ、従来のようにコンク
リート基板を形成するコンクリートの凝結の度合いに応
じて作業を進める必要がなく、未熟練者でも容易に所要
の性能のコンクリートスラブ用基板を製造することがで
きる。
As described above, a concrete substrate is formed by using an embedding material having a structure in which a concrete filling through hole having a shape whose upper side opening is larger than that of the lower side opening penetrates vertically. After the concrete to be cast is poured into the formwork, an embedding material is disposed on the upper surface of the concrete, and then the concrete is filled in the concrete filling through hole of the embedding material to form a lower concrete substrate. When the method of integrating with the concrete to be used is adopted, the embedding material can be disposed in a state where the concrete forming the concrete substrate is uncured and has fluidity, and the setting of the concrete forming the concrete substrate as in the past is performed. It is not necessary to proceed with the operation according to the degree of the slab, and even an unskilled person can easily manufacture a concrete slab substrate having required performance.

【0022】また、この製造方法によれば、型枠内への
コンクリートの打設,埋込材の配設、該埋込材のコンク
リート充填貫通孔へのコンクリートの充填作業を連続し
て行い、その後に養生工程に入るので、コンクリート充
填貫通孔へのコンクリートの充填作業の後はその作業現
場を離れて別のコンクリートスラブ用基板の製造を行う
ことができ、このため従来よりもコンクリートスラブ用
基板製造の量産性を向上させることができ、また人件費
を削減することができる。
Further, according to this manufacturing method, the operation of placing concrete in the formwork, arranging the embedding material, and filling the concrete into the concrete filling through hole of the embedding material is performed continuously. After that, the curing process starts, so after the work of filling concrete into the concrete filling through hole, it is possible to leave the work site and manufacture another concrete slab substrate, so that the concrete slab substrate is The mass productivity of manufacturing can be improved, and labor costs can be reduced.

【0023】[0023]

【発明の実施の形態】図1乃至図5は、本発明に係るコ
ンクリートスラブ用基板の実施の形態の一例を示すもの
である。図面において、1は所定の大きさに形成された
コンクリート基板、2はコンクリート基板1の上面に配
置されて固定されている合成樹脂の発泡成形品からなる
埋込材である。
1 to 5 show an embodiment of a concrete slab substrate according to the present invention. In the drawings, reference numeral 1 denotes a concrete substrate formed in a predetermined size, and reference numeral 2 denotes an embedding material formed of a synthetic resin foam molded product disposed and fixed on the upper surface of the concrete substrate 1.

【0024】前記埋込材2は、例えばポリスチレン発泡
体等の独立気泡を有する合成樹脂の発泡成形品で形成さ
れ、底面側に開口させて複数の空間3が素材節約や軽量
化のために設けられている点は従来と同様である。な
お、この埋込材2は、充実形のもの等であってもよい。
The embedding material 2 is formed of a synthetic resin foam molded article having closed cells, such as a polystyrene foam, and is opened on the bottom side to provide a plurality of spaces 3 for material saving and weight reduction. This is the same as in the prior art. The embedding material 2 may be of a solid type or the like.

【0025】本例の埋込材2には、幅方向の中央に位置
して上下方向に貫通するコンクリート充填貫通孔4が長
手方向の複数箇所に設けられている。これらコンクリー
ト充填貫通孔4は、その水平断面におけるいずれかの箇
所において上側開口断面積が下側開口断面積より大きく
形成されている。本例のコンクリート充填貫通孔4は、
上面側開口部4aが下面側開口部4bより大きく形成さ
れており、各コンクリート充填貫通孔4は、四角錐台形
状に4つのテーパ面により形成されており、上面側開口
部4aの開口寸法が100mm 、下面側開口部4bの開口寸
法が60mmとなつている。該コンクリート充填貫通孔4内
にはコンクリートが充填されてコンクリート基板1に一
体となって固定されている。また、前記埋込材2の各縁
部は、上面に向かって開くテーパ面5となっている。前
記埋込材2の下縁には前記空間3と外部とを連通する連
通溝16が設けられている。
In the embedding material 2 of this embodiment, concrete filling through holes 4 which are located at the center in the width direction and penetrate vertically are provided at a plurality of locations in the longitudinal direction. These concrete filling through-holes 4 are formed such that the upper opening cross-sectional area is larger than the lower opening cross-sectional area at any point in the horizontal cross section. The concrete filling through hole 4 of this example is
The upper surface side opening 4a is formed larger than the lower surface side opening 4b, and each concrete filling through hole 4 is formed by four tapered surfaces in a truncated square pyramid shape, and the opening dimension of the upper surface side opening 4a is reduced. The opening size of the lower opening 4b is 60 mm. The concrete filling through hole 4 is filled with concrete and fixed integrally with the concrete substrate 1. Each edge of the embedding material 2 is a tapered surface 5 that opens toward the upper surface. A communication groove 16 for communicating the space 3 with the outside is provided at the lower edge of the embedding material 2.

【0026】このように埋込材2の下縁に前記空間3と
外部とを連通する連通溝16を設けていると、型枠内に
打設したコンクリート基板1を形成するコンクリートの
上面に埋込材を配設したとき、前記空間で覆われた部分
のコンクリート上にある水は埋込材2の下縁に設けられ
た連通溝16から外部に流れ出すので、空間内の水溜り
を防止できる。
When the communication groove 16 for communicating the space 3 with the outside is provided in the lower edge of the embedding material 2 as described above, the embedding material 2 is embedded in the upper surface of the concrete forming the concrete substrate 1 cast in the formwork. When the filling material is provided, the water on the concrete in the portion covered with the space flows out to the outside from the communication groove 16 provided on the lower edge of the filling material 2, so that the water pool in the space can be prevented. .

【0027】次に、このような埋込材1を用いたコンク
リートスラブ用基板の製造方法について図6を参照して
説明する。型枠6内に鉄筋7を配筋した後、該型枠6内
にコンクリート基板1を形成するためのコンクリート8
を打設する。該コンクリート8の上面に前述した埋込材
2を所定間隔で配設する。この埋込材2の配置は、コン
クリート8の打設直後に行う。次に、該埋込材2の各コ
ンクリート充填貫通孔4内にコンクリート9を充填して
下側の、コンクリート基板1を形成するコンクリート8
と一体化させる。
Next, a method of manufacturing a concrete slab substrate using such an embedding material 1 will be described with reference to FIG. After arranging the reinforcing bars 7 in the formwork 6, the concrete 8 for forming the concrete substrate 1 in the formwork 6 is formed.
Is installed. The above-mentioned embedding material 2 is arranged on the upper surface of the concrete 8 at a predetermined interval. The placement of the embedding material 2 is performed immediately after the concrete 8 is cast. Next, concrete 9 is filled in each concrete filling through hole 4 of the embedding material 2 to form the concrete substrate 1 on the lower side.
And integrated.

【0028】このように埋込材2に上下方向に貫通する
コンクリート充填貫通孔4を設け、該コンクリート充填
貫通孔4を上面側開口部4aが下面側開口部4bより大
きい形状とし、該コンクリート充填貫通孔4内にコンク
リート9を充填すると、該コンクリート充填貫通孔4内
のコンクリート9がコンクリート基板1を形成するコン
クリート8と一体となって固定される。該コンクリート
充填貫通孔4内のコンクリート9は、埋込材2を押さえ
ることになり、該コンクリート充填貫通孔4内のコンク
リート9が埋込材2をコンクリート基板1に固定する。
As described above, the concrete filling through hole 4 penetrating the embedding material 2 in the up-down direction is formed, and the concrete filling through hole 4 is formed such that the upper opening 4a is larger than the lower opening 4b. When the concrete 9 is filled in the through hole 4, the concrete 9 in the concrete filling through hole 4 is fixed integrally with the concrete 8 forming the concrete substrate 1. The concrete 9 in the concrete filling through hole 4 presses the embedding material 2, and the concrete 9 in the concrete filling through hole 4 fixes the embedding material 2 to the concrete substrate 1.

【0029】このように、本例のコンクリートスラブ用
基板は、係止具がなくても埋込材2をコンクリート基板
1に固定できるので、その分コストの低減を図ることが
できる。
As described above, in the concrete slab substrate of the present embodiment, since the embedding material 2 can be fixed to the concrete substrate 1 without any locking member, the cost can be reduced accordingly.

【0030】また、埋込材2はコンクリート基板1を形
成するコンクリート8が流動性をもつ状態で配設するこ
とができ、従来のようにコンクリート基板1を形成する
コンクリート8の凝結の度合いに応じて作業を進める必
要がなく、未熟練者でも容易に所要の性能のコンクリー
トスラブ用基板を製造することができる。
Further, the embedding material 2 can be disposed in a state where the concrete 8 forming the concrete substrate 1 has fluidity, and according to the degree of coagulation of the concrete 8 forming the concrete substrate 1 as in the prior art. It is not necessary to proceed with the work, and even an unskilled person can easily manufacture a concrete slab substrate having required performance.

【0031】また、この製造方法によれば、型枠6内へ
のコンクリート8の打設,埋込材2の配設、該埋込材2
のコンクリート充填貫通孔4へのコンクリート9の充填
作業を連続して行い、その後に養生工程に入るので、コ
ンクリート充填貫通孔4へのコンクリート9の充填作業
の後はその作業現場を離れて別のコンクリートスラブ用
基板の製造を行うことができ、このため従来よりもコン
クリートスラブ用基板製造の量産効率の向上と人件費の
削減が図れる。
According to this manufacturing method, the concrete 8 is poured into the form 6, the embedding material 2 is provided, and the embedding material 2 is disposed.
The concrete filling operation of the concrete filling through hole 4 is performed continuously after that, and then the curing process is started. It is possible to manufacture a substrate for concrete slab, and therefore, it is possible to improve the mass production efficiency and reduce labor costs of manufacturing a substrate for concrete slab as compared with the related art.

【0032】図7は、本発明で用いる埋込材2の他例を
示したものである。本例の埋込材2は、図2に示した構
造の埋込材2の下面の縁部に沿ってエッジ状の食込み部
10が設けられている。この食込み部10は、埋込材2
の下面に適宜間隔で突設してもよい。
FIG. 7 shows another example of the embedding material 2 used in the present invention. The embedding material 2 of this example is provided with an edge-shaped biting portion 10 along the edge of the lower surface of the embedding material 2 having the structure shown in FIG. The bite portion 10 is provided with the embedding material 2
May be provided at appropriate intervals on the lower surface of the device.

【0033】このように埋込材2の下面の縁部にエッジ
状の食込み部10を設けていると、前述した図6に示す
ように型枠6内にコンクリート基板1を形成するコンク
リート8を打設した後、該コンクリート8の上面に埋込
材2を配設したとき、食込み部10がコンクリート基板
1を形成するコンクリート8に食込み、埋込材2が流動
性をもつコンクリート8上で移動するのを食込み部10
で阻止でき、該埋込材2の位置決めを容易に行うことが
できる。
When the edge-shaped biting portion 10 is provided at the edge of the lower surface of the embedding material 2 as described above, the concrete 8 forming the concrete substrate 1 in the formwork 6 as shown in FIG. When the embedding material 2 is arranged on the upper surface of the concrete 8 after the casting, the biting portion 10 bites into the concrete 8 forming the concrete substrate 1 and the embedding material 2 moves on the concrete 8 having fluidity. Digging part 10
And the positioning of the embedding material 2 can be easily performed.

【0034】図8乃至図10は、本発明で用いる埋込材
2の他例を示したものである。本例の埋込材2は、横幅
に対して縦幅が1.5倍程度の長さに成形されている。
コンクリートスラブ用基板の製造工程で、コンクリート
8,9の硬化促進のために、水蒸気養生をする場合があ
る。かかる場合に、横幅に対して縦幅が長いと、水蒸気
養生の際、その加熱温度で埋込材2に変形や歪みが生
じ、かかる埋込材2に変形や歪みにより、コンクリート
充填貫通孔4内のコンクリート9とコンクリート基板1
を形成するコンクリート8との間にひび割れが生じる恐
れがある。そこで、本例のように、埋込材2を、横幅に
対して縦幅が1.5倍程度の長さに成形することによ
り、コンクリートスラブ用基板の製造工程で、コンクリ
ート8,9の硬化促進のために、水蒸気養生しても、そ
の加熱温度で埋込材2に生じる変形や歪み量が小さく、
コンクリート充填貫通孔4内のコンクリート9とコンク
リート基板1を形成するコンクリート8との間のひび割
れの発生を抑えることができる。
FIGS. 8 to 10 show other examples of the embedding material 2 used in the present invention. The embedding material 2 of the present example is formed to have a length about 1.5 times as long as the width.
In the manufacturing process of the concrete slab substrate, steam curing may be performed to accelerate hardening of the concretes 8 and 9. In this case, if the vertical width is longer than the horizontal width, deformation or distortion occurs in the embedded material 2 at the heating temperature during steam curing, and the embedded material 2 is deformed or distorted by the concrete filling through hole 4. Concrete 9 and concrete board 1 inside
There is a possibility that cracks may occur between the concrete and the concrete 8 that forms the cracks. Thus, as in the present example, the embedding material 2 is formed to have a length approximately 1.5 times as long as the width, so that the concrete 8, 9 is hardened in the manufacturing process of the concrete slab substrate. For promotion, even if steam curing is performed, the amount of deformation and distortion generated in the implant 2 at the heating temperature is small,
The occurrence of cracks between the concrete 9 in the concrete filling through hole 4 and the concrete 8 forming the concrete substrate 1 can be suppressed.

【0035】また、本例では、埋込材2の縦方向の一方
の端部に突部11が突設され、他方の端部には突部11
に遊嵌合可能な形状の凹部12が設けられている。この
ような形状にすることにより、コンクリートスラブ用基
板の製造工程で埋込材2をコンクリート基板1を形成す
るコンクリート8の上に配置する際、埋込材2の突部1
1と他の埋込材2の凹部12を遊嵌合させることによ
り、縦方向の方向性が出し易くなる。
In this embodiment, a protrusion 11 is provided at one end of the embedding material 2 in the longitudinal direction, and the protrusion 11 is provided at the other end.
Is provided with a concave portion 12 having a shape that can be loosely fitted. With such a shape, when the embedding material 2 is arranged on the concrete 8 forming the concrete substrate 1 in the manufacturing process of the concrete slab substrate, the protrusion 1 of the embedding material 2 is used.
By loosely fitting the concave portion 12 of 1 with the embedding material 2, it is easy to obtain a vertical direction.

【0036】図11は、本発明に係るコンクリートスラ
ブ用基板の他の例を示したものである。本例では、埋込
材2は、コンクリート充填貫通孔4内面に係止された係
止頭部13と該係止頭部13に一体に設けられていてコ
ンクリート基板1を形成するコンクリート8内に埋設さ
れるアンカー脚部14とを備えた補強材15でコンクリ
ート基板1に定着されている。アンカー脚部14は、コ
ンクリート基板1から抜け出し難いように屈曲されてい
る。
FIG. 11 shows another example of the concrete slab substrate according to the present invention. In this example, the embedding material 2 is inserted into the concrete head 8 fixed to the inner surface of the concrete filling through hole 4 and the concrete 8 provided integrally with the head 13 to form the concrete substrate 1. It is fixed to the concrete substrate 1 by a reinforcing member 15 having an embedded anchor leg 14. The anchor leg 14 is bent so that it is difficult to get out of the concrete substrate 1.

【0037】このようにコンクリート充填貫通孔4内に
係止された係止頭部13と該係止頭部13に一体に設け
られていてコンクリート基板1内に埋設されるアンカー
脚部14とを備えた補強材15で埋込材2をコンクリー
ト基板1に定着させると、コンクリート充填貫通孔4内
のコンクリート9による埋込材2のコンクリート基板1
に対する定着強度を一層向上させることができる。
The locking head 13 thus locked in the concrete filling through hole 4 and the anchor leg 14 provided integrally with the locking head 13 and embedded in the concrete substrate 1 are combined. When the embedding material 2 is fixed to the concrete substrate 1 by the reinforcing material 15 provided, the concrete substrate 1 of the embedding material 2 by the concrete 9 in the concrete filling through hole 4 is provided.
Can be further improved.

【0038】上記した各例では、コンクリート充填貫通
孔4の形状を4つの面がテーパ面となっている四角錐台
形状としたが、コンクリート充填貫通孔4の形状はこれ
に限定されるものではなく、対向する1対の面がテーパ
面となっていて、他の1対の面が平行面となっている形
状のもの、或いは円錐台形状のもの、若しくは上面側開
口部が下面側開口部より大きい状態で、内面が階段状に
変化している形状のもの等、その水平断面におけるいず
れかの箇所において上側開口断面積が下側開口断面積よ
り大きく形成されていればよい。
In each of the above embodiments, the shape of the concrete filling through hole 4 is a truncated quadrangular pyramid having four tapered surfaces. However, the shape of the concrete filling through hole 4 is not limited to this. Instead, a pair of opposing surfaces is a tapered surface, and the other pair of surfaces is a parallel surface, or a truncated cone shape, or an upper opening is a lower opening. It is sufficient that the upper opening cross-sectional area is larger than the lower opening cross-sectional area at any point in the horizontal cross section, such as a shape in which the inner surface changes stepwise in a larger state.

【0039】[0039]

【発明の効果】請求項1に記載のコンクリートスラブ用
基板においては、埋込材に、底面側に開口する複数の空
間が設けられているとともに上下方向に貫通するコンク
リート充填貫通孔を設け、該コンクリート充填貫通孔
を、その水平断面におけるいずれかの箇所において上側
開口断面積を下側開口断面積より大きく形成し、該コン
クリート充填貫通孔内にコンクリートを充填しているの
で、該コンクリート充填貫通孔内のコンクリートをコン
クリート基板に一体となって固定され、そして該コンク
リート充填貫通孔内のコンクリートは、該コンクリート
充填貫通孔の形状から上部が下部より大きいため埋込材
を押さえていて、該埋込材がコンクリート基板から外れ
なくなり、係止具を用いなくても埋込材をコンクリート
基板に固定することができ、このように係止具を省略で
きることにより、その分コストの低減を図ることができ
る。
According to the first aspect of the present invention, in the concrete slab substrate, a plurality of vacancies opened on the bottom side are formed in the embedding material.
A concrete filling through hole is provided in which a space is provided and penetrates vertically, and the concrete filling through hole is formed such that the upper opening cross-sectional area is larger than the lower opening cross-sectional area at any point in the horizontal cross section thereof, Since the concrete in the concrete filling through hole is filled with concrete, the concrete in the concrete filling through hole is fixed integrally to the concrete substrate, and the concrete in the concrete filling through hole is removed from the concrete filling through hole. Because the upper part is larger than the lower part, the embedding material is held down, so that the embedding material does not come off the concrete substrate, and the embedding material can be fixed to the concrete substrate without using a locking tool. By omitting the locking member as described above, the cost can be reduced accordingly.

【0040】請求項2に記載のコンクリートスラブ用基
板においては、埋込材の下面に食込み部を設けているの
で、型枠内にコンクリート基板を形成するコンクリート
を打設した後、該コンクリートの上面に埋込材を配設し
ても、該埋込材が流動性をもつコンクリート上で移動す
るのを該食込み部で阻止でき、該埋込材の位置決めを容
易に行うことができる。
In the concrete slab substrate according to the second aspect of the present invention, since the undercut portion is provided on the lower surface of the embedding material, the concrete forming the concrete substrate is poured into the formwork, and then the upper surface of the concrete is formed. Even if an embedding material is provided, the embedding material can be prevented from moving on the concrete having fluidity by the bite portion, and the embedding material can be easily positioned.

【0041】請求項3に記載のコンクリートスラブ用基
板においては、埋込材は、その下縁に前記空間と外部と
を連通する連通溝が設けられているので、型枠内に打設
したコンクリート基板を形成するコンクリートの上面に
埋込材を配設したとき、前記空間で覆われた部分のコン
クリート上にある水は埋込材の下縁に設けられた連通溝
から外部に流れ出すので、空間内の水溜りを防止するこ
とができる。
In the concrete slab substrate according to a third aspect of the present invention, the embedding material is provided with a communication groove for communicating the space with the outside at a lower edge thereof. When the embedding material is disposed on the upper surface of the concrete forming the substrate, the water on the concrete in the portion covered with the space flows out from the communication groove provided on the lower edge of the embedding material to the outside. Puddles in the interior can be prevented.

【0042】請求項4に記載のコンクリートスラブ用基
板においては、コンクリート充填貫通孔内に係止された
係止頭部と該係止頭部に一体に設けられていてコンクリ
ート基板内に埋設されるアンカー脚部とを備えた補強材
で埋込材をコンクリート基板に定着させているので、コ
ンクリート充填貫通孔内のコンクリートによる埋込材の
コンクリート基板に対する定着強度を一層向上させるこ
とができる。
In the concrete slab substrate according to the fourth aspect, a locking head locked in the concrete filling through hole and the locking head are provided integrally and embedded in the concrete substrate. Since the embedding material is fixed to the concrete substrate by the reinforcing material having the anchor leg, the fixing strength of the embedding material by the concrete in the concrete filling through hole to the concrete substrate can be further improved.

【0043】また、請求項5に記載のコンクリートスラ
ブ用基板の製造方法においては、埋込材として、その底
面側に開口する複数の空間が設けられているとともに
面側開口部が下面側開口部より大きい形状のコンクリー
ト充填貫通孔が上下方向に貫通して設けられている構造
のものを用いて、コンクリート基板を形成するコンクリ
ートを型枠内に打設した後、該コンクリートの上面に埋
込材を配設し、次に該埋込材のコンクリート充填貫通孔
内にコンクリートを充填して下側のコンクリート基板を
形成するコンクリートと一体化させる方法をとっている
ので、コンクリート基板を形成するコンクリートを型枠
内に打設した後、直ちに埋込材を配設することができ、
従来のようにコンクリート基板を形成するコンクリート
の凝結の度合いに応じて作業を進める必要がなく、未熟
練者でも容易に所要の性能のコンクリートスラブ用基板
を製造することができる。
Further, in the method of manufacturing a substrate for a concrete slab according to claim 5, the embedding material has a bottom surface.
A structure in which a plurality of spaces that open to the front side are provided, and a concrete filling through-hole having a shape in which the upper side opening is larger than the lower side opening is provided vertically. After the concrete forming the concrete substrate is cast into the formwork, an embedding material is disposed on the upper surface of the concrete, and then the concrete is filled into the concrete filling through hole of the embedding material. Since the method is integrated with the concrete forming the lower concrete substrate, the concrete forming the concrete substrate is cast into the formwork, and then the embedding material can be arranged immediately,
It is not necessary to proceed with the operation according to the degree of setting of the concrete forming the concrete substrate as in the related art, and even an unskilled person can easily manufacture a concrete slab substrate having required performance.

【0044】また、この製造方法によれば、型枠内への
コンクリートの打設,埋込材の配設、該埋込材のコンク
リート充填貫通孔へのコンクリートの充填作業を連続し
て行い、その後に養生工程に入るので、コンクリート充
填貫通孔へのコンクリートの充填作業の後はその作業現
場を離れて別のコンクリートスラブ用基板の製造を行う
ことができ、このため従来よりもコンクリートスラブ用
基板製造の量産効率の向上と人件費の削減を図ることが
できる。
Further, according to this manufacturing method, the operation of placing concrete in the formwork, disposing the embedding material, and filling concrete into the concrete filling through hole of the embedding material is performed continuously. After that, the curing process starts, so after the work of filling concrete into the concrete filling through hole, it is possible to leave the work site and manufacture another concrete slab substrate, so that the concrete slab substrate is It is possible to improve the mass production efficiency of manufacturing and reduce labor costs.

【図面の簡単な説明】[Brief description of the drawings]

【図1】本発明に係るコンクリートスラブ用基板の実施
の形態の一例を示す一部省力断面図。
FIG. 1 is a partial labor-saving sectional view showing an example of an embodiment of a concrete slab substrate according to the present invention.

【図2】図1に示す埋込材の上面側からの斜視図。FIG. 2 is a perspective view of the embedding material shown in FIG. 1 from the upper surface side.

【図3】図1に示す埋込材の下面側からの斜視図。FIG. 3 is a perspective view of the embedding material shown in FIG. 1 as viewed from the lower surface side.

【図4】図3のA−A線断面図。FIG. 4 is a sectional view taken along line AA of FIG. 3;

【図5】図3のB−B線断面図。FIG. 5 is a sectional view taken along line BB of FIG. 3;

【図6】本発明に係るコンクリートスラブ用基板の製造
時の一例を示す断面図である。
FIG. 6 is a cross-sectional view showing one example of a concrete slab substrate according to the present invention during manufacture.

【図7】本発明で用いる埋込材の他例を示す断面図。FIG. 7 is a sectional view showing another example of an embedding material used in the present invention.

【図8】本発明で用いる埋込材の他例を示す上面側から
の斜視図。
FIG. 8 is a top perspective view showing another example of an embedding material used in the present invention.

【図9】図8に示す埋込材の上面側からの斜視図。9 is a perspective view of the embedding material shown in FIG. 8 as viewed from the upper surface side.

【図10】図8に示す埋込材の配設の一例を示す斜視
図。
FIG. 10 is a perspective view showing an example of the arrangement of the embedding material shown in FIG. 8;

【図11】本発明に係るコンクリートスラブ用基板の他
の例を示す要部拡大断面図
FIG. 11 is an enlarged sectional view of a main part showing another example of the concrete slab substrate according to the present invention.

【符号の説明】[Explanation of symbols]

1 コンクリート基板 2 埋込材 3 空間 4 コンクリート充填貫通孔 4a 上面側開口部 4b 下面側開口部 5 テーパ面 6 型枠 7 鉄筋 8 コンクリート 9 コンクリート 10 食込み部 11 突部 12 凹部 13 係止頭部 14 アンカー脚部 15 補強材 16 連結溝 REFERENCE SIGNS LIST 1 concrete substrate 2 embedding material 3 space 4 concrete filling through hole 4 a upper surface side opening 4 b lower surface side opening 5 tapered surface 6 formwork 7 reinforcing bar 8 concrete 9 concrete 10 bite portion 11 protrusion 12 recess 13 locking head 14 Anchor leg 15 Reinforcement 16 Connection groove

───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平8−35279(JP,A) 特開 平4−220308(JP,A) 特開 平8−284298(JP,A) 特開 平9−111940(JP,A) (58)調査した分野(Int.Cl.6,DB名) B28B 23/00 - 23/22 ──────────────────────────────────────────────────続 き Continuation of the front page (56) References JP-A-8-35279 (JP, A) JP-A-4-220308 (JP, A) JP-A 8-284298 (JP, A) JP-A 9- 111940 (JP, A) (58) Field surveyed (Int. Cl. 6 , DB name) B28B 23/00-23/22

Claims (5)

(57)【特許請求の範囲】(57) [Claims] 【請求項1】 コンクリート基板の上に合成樹脂の発泡
成形品からなる埋込材が配置されて固定されているコン
クリートスラブ用基板において、前記埋込材は、底面側
に開口する複数の空間が設けられているとともに、上下
方向に貫通するコンクリート充填貫通孔が設けられ、該
コンクリート充填貫通孔は、その水平断面におけるいず
れかの箇所において上側開口断面積が下側開口断面積よ
り大きく形成され、該コンクリート充填貫通孔内にはコ
ンクリートが充填されて前記コンクリート基板に一体と
なって固定されていることを特徴とするコンクリートス
ラブ用基板。
1. A concrete slab substrate in which an embedding material made of a synthetic resin foam molded article is arranged and fixed on a concrete substrate, wherein the embedding material is on a bottom side.
And a concrete filling through hole is provided, which penetrates in the vertical direction, and the concrete filling through hole has an upper opening cross-sectional area of a lower cross section at any point in a horizontal cross section thereof. A concrete slab substrate, wherein the substrate is formed so as to have a larger cross-sectional area, and concrete is filled in the concrete filling through hole, and is fixed integrally with the concrete substrate.
【請求項2】 前記埋込材の下面には前記コンクリート
基板に食込む食込み部が設けられていることを特徴とす
る請求項1に記載のコンクリートスラブ用基板。
2. The concrete slab substrate according to claim 1, wherein a cut-in portion that cuts into the concrete substrate is provided on a lower surface of the embedding material.
【請求項3】 前記埋込材は、その下縁に前記空間と外
部とを連通する連通溝が設けられていることを特徴とす
る請求項1または2に記載のコンクリートスラブ用基
板。
3. The concrete slab substrate according to claim 1, wherein the embedding material is provided with a communication groove at a lower edge thereof for communicating the space with the outside.
【請求項4】 前記埋込材は、前記コンクリート充填貫
通孔内に係止された係止頭部と該係止頭部に一体に設け
られていて前記コンクリート基板内に埋設されるアンカ
ー脚部とを備えた補強材で前記コンクリート基板に定着
されていることを特徴とする請求項1、2または3に記
載のコンクリートスラブ用基板。
4. An embedding material, comprising: a locking head locked in the concrete filling through hole; and an anchor leg integrated with the locking head and embedded in the concrete substrate. The concrete slab substrate according to claim 1, wherein the substrate is fixed to the concrete substrate with a reinforcing material having the following.
【請求項5】 コンクリート基板の上に合成樹脂の発泡
成形品からなる埋込材が配置されて固定されている構造
のコンクリートスラブ用基板の製造方法において、前記
埋込材としては底面側に開口する複数の空間が設けられ
ているとともに上面側開口部が下面側開口部より大きい
形状のコンクリート充填貫通孔が上下方向に貫通して設
けられている構造のものを用い、前記コンクリート基板
を形成するコンクリートを型枠内に打設した後、該コン
クリートの上面に前記埋込材を配設し、次に該埋込材の
前記コンクリート充填貫通孔内にコンクリートを充填し
て下側の前記コンクリート基板を形成するコンクリート
と一体化させることを特徴とするコンクリートスラブ用
基板の製造方法。
5. A method for manufacturing a concrete slab substrate having a structure in which an embedding material made of a synthetic resin foam molded article is arranged and fixed on a concrete substrate, wherein the embedding material has an opening on the bottom side. Multiple spaces are provided
Using top-side opening with which to take a structure in which concrete filling through-holes of larger shape than the lower surface side opening is provided through in the vertical direction, hitting the concrete mold frame which forms the concrete substrate After that, the embedding material is disposed on the upper surface of the concrete, and then the concrete is filled in the concrete filling through hole of the embedding material and integrated with the concrete forming the lower concrete substrate. A method of manufacturing a substrate for a concrete slab.
JP8200461A 1996-07-30 1996-07-30 Substrate for concrete slab and method of manufacturing the same Expired - Fee Related JP2991333B2 (en)