JP2920443B2 - Keratin plug remover - Google Patents

Keratin plug remover

Info

Publication number
JP2920443B2
JP2920443B2 JP8703392A JP8703392A JP2920443B2 JP 2920443 B2 JP2920443 B2 JP 2920443B2 JP 8703392 A JP8703392 A JP 8703392A JP 8703392 A JP8703392 A JP 8703392A JP 2920443 B2 JP2920443 B2 JP 2920443B2
Authority
JP
Japan
Prior art keywords
plug
skin
keratotic
meth
present
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP8703392A
Other languages
Japanese (ja)
Other versions
JPH0597627A (en
Inventor
智浩 植村
昌則 棚橋
愛行 室井
良直 光野
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kao Corp
Original Assignee
Kao Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kao Corp filed Critical Kao Corp
Priority to JP8703392A priority Critical patent/JP2920443B2/en
Publication of JPH0597627A publication Critical patent/JPH0597627A/en
Priority to US08/210,778 priority patent/US5512277A/en
Priority to US08/748,549 priority patent/US6306382B1/en
Application granted granted Critical
Publication of JP2920443B2 publication Critical patent/JP2920443B2/en
Priority to US09/843,857 priority patent/US6607719B2/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【産業上の利用分野】本発明は、毛孔に形成された角栓
を良好に除去することのできる角栓除去剤に関する。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a plug removing agent which can remove plugs formed in pores well.

【0002】[0002]

【従来の技術及び発明が解決しようとする課題】最近の
女性の肌の悩みで、上位を占めるものの一つとして毛孔
の目立ちが挙げられる。この原因としては、毛孔に形成
される角栓に起因するところが大きい。角栓は皮脂と共
に汚れを含んで角化して毛孔につまったものであり、こ
れを放置することは、毛孔の目立ちのみならず、肌の種
々のトラブルをひき起こす。従って、角栓を除去するこ
とが、美容上及び肌の健康上好ましい。
2. Description of the Related Art One of the most recent problems in the skin of women is the appearance of pores. This is largely due to the horn plug formed in the pores. The keratin plugs are dirt and dirt together with sebum, and are keratinized and clogged in the pores. Leaving the keratin not only makes the pores noticeable but also causes various troubles on the skin. Therefore, removing the keratotic plug is preferable for cosmetics and skin health.

【0003】しかしながら、通常用いられる洗顔料、メ
イク落しでは、角栓を充分除去することができない。一
方、ピールオフタイプのパック剤は、皮膚に塗付し、乾
燥後、皮膚から剥離するものであるが、これに用いる皮
膜形成剤としては、ポリビニルアルコール、ポリビニル
ピロリドン等が用いられている。しかしながら、これら
非イオン性のポリマーを主成分としたものも、取れにく
い毛孔の汚れの除去には充分でなく、特に角栓の除去に
関しては、ほとんど効果を示さないものであった。
[0003] However, the face plugs and makeup removers usually used cannot sufficiently remove the keratotic plug. On the other hand, the peel-off type pack agent is applied to the skin, peels off from the skin after drying, and polyvinyl alcohol, polyvinyl pyrrolidone, and the like are used as a film forming agent used for this. However, those containing these nonionic polymers as a main component were not enough to remove dirt from pores which were difficult to remove, and showed almost no effect particularly in removing keratotic plugs.

【0004】従って、角栓を効果的に除去することがで
きる角栓除去剤が望まれていた。
[0004] Accordingly, there has been a demand for a plug removal agent capable of effectively removing a plug.

【0005】[0005]

【課題を解決するための手段】斯かる実情に鑑み、本発
明者らは鋭意研究を行った結果、塩生成基を有する合成
高分子を配合した角栓除去剤が、効果的に角栓及び汚れ
を除去することを見出し本発明を完成した。
Means for Solving the Problems In view of such circumstances, the inventors of the present invention have conducted intensive studies, and as a result, a plug stopper removing agent containing a synthetic polymer having a salt-forming group can be effectively used as a plug and a plug. The present inventors have found that dirt is removed and completed the present invention.

【0006】すなわち、本発明は、四級化したジアルキ
ルアミノ基を有する(メタ)アクリル酸エステル又は
(メタ)アクリルアミドを重合して得られる高分子化合
物を含有することを特徴とする角栓除去剤を提供するも
のである。
That is, the present invention provides a keratotic plug removing agent comprising a polymer compound obtained by polymerizing a (meth) acrylic acid ester or a (meth) acrylamide having a quaternized dialkylamino group. Is provided.

【0007】[0007]

【0008】[0008]

【0009】[0009]

【0010】[0010]

【0011】[0011]

【0012】[0012]

【0013】[0013]

【0014】[0014]

【0015】本発明で用いられる高分子化合物として
は、ジメチルアミノエチルアクリレート(DMAE
A)、ジメチルアミノエチルメタクリレート(DMAE
MA)、ジメチルアミノプロピルアクリルアミド(DM
APAAm)、ジメチルアミノプロピルメタクリルアミ
ド(DMAPMAAm)等のジアルキルアミノ基を有す
る(メタ)アクリル酸エステル又は(メタ)アクリルア
ミド類をハロゲン化アルキル、ハロゲン化ベンジル、ア
ルキル若しくはアリールスルホン酸又は硫酸ジアルキル
等の公知の四級化剤で四級化したモノマーを重合したも
のが挙げられる。これらのうち、ポリメタクリロイルオ
キシエチルトリメチルアンモニウムクロライド及びポリ
(メタ)アクリルアミドプロピルトリメチルアンモニウ
ムクロライドが好ましい。
The polymer compound used in the present invention is dimethylaminoethyl acrylate (DMAE).
A), dimethylaminoethyl methacrylate (DMAE
MA), dimethylaminopropylacrylamide (DM
(APAAm), dimethylaminopropyl methacrylamide (DMAPMAAAm) and other known dialkylamino group-containing (meth) acrylic esters or (meth) acrylamides such as alkyl halides, benzyl halides, alkyl or aryl sulfonic acids, and dialkyl sulfates. And a polymerized monomer quaternized with a quaternizing agent. Of these, polymethacryloyloxyethyltrimethylammonium chloride and poly (meth) acrylamidopropyltrimethylammonium chloride are preferred.

【0016】また、これらの高分子化合物の分子量は、
1万〜300万の範囲のものが好ましく、特に10万〜
100万のものが好ましい。分子量が1万未満である
と、造膜したフィルムの強度が不充分で、皮膚に対する
緊張感が弱くなり、剥離時に破れ易くなり、一方300
万を超えるものの製造は難しい。
The molecular weight of these high molecular compounds is
Those having a range of 10,000 to 3,000,000 are preferable, and especially 100,000 to
One million is preferred. If the molecular weight is less than 10,000, insufficient strength of the film-forming films, weakens the tension to the skin, is easily broken at the time of peeling, whereas 300
Manufacturing of more than ten thousand is difficult.

【0017】本発明の角栓除去剤に用いる上記高分子化
合物の配合量は0.01〜70重量%、特に5〜40重量%
とすることが好ましい。
The amount of the polymer compound used in the keratotic plug remover of the present invention is 0.01 to 70% by weight, particularly 5 to 40% by weight.
It is preferable that

【0018】上記の合成高分子化合物は、溶剤に溶解せ
しめて使用されるが、この溶剤としては、揮発性であ
り、該高分子化合物を安定に溶解でき更に皮膚に安全な
ものであれば特に限定されず、例えば水、エタノール、
イソプロピルアルコール(IPA)等が単独で又は2種
以上組み合わせて用いられる。この溶剤の配合量は、高
分子化合物、任意成分、剤型により適宜決定すればよい
が、一般的には30〜99.99重量%、特に60〜9
5重量%が好ましい。
The synthetic polymer compound mentioned above, are used by dissolving in a solvent, as the solvent, volatile der
The polymer is not particularly limited as long as it can stably dissolve the polymer compound and is safe for the skin. For example, water, ethanol,
Isopropyl alcohol (IPA) alone or in combination
These are used in combination . The amount of the solvent may be appropriately determined depending on the polymer compound, optional components, and dosage form, but is generally 30 to 99.99% by weight, particularly 60 to 9% by weight.
5% by weight is preferred.

【0019】本発明の角栓除去剤には上記成分のほか、
通常の化粧料に用いられる成分、例えばエチレングリコ
ール、ジエチレングリコール、トリエチレングリコー
ル、それ以上のポリエチレングリコール類、プロピレン
グリコール、ジプロピレングリコール、それ以上のポリ
プロピレングリコール類、1,3−ブチレングリコー
ル、1,4−ブチレングリコール等のブチレングリコー
ル類、グリセリン、ジグリセリン、それ以上のポリグリ
セリン類、ソルビトール、マンニトール、キシリトー
ル、マルチトール等の糖アルコール類、グリセリン類の
エチレンオキシド(以下、EOと略記)、プロピレンオ
キシド(以下、POと略記)付加物、糖アルコール類の
EO、PO付加物、ガラクトース、グルコース、フルク
トース等の単糖類とそのEO、PO付加物、マルトー
ス、ラクトース等の多糖類とそのEO、PO付加物など
の多価アルコール;流動パラフィン、スクワラン、ワセ
リン、固形パラフィン等の炭化水素、オリーブ油、ホホ
バ油、月見草油、ヤシ油、牛脂等の天然油、イソプロピ
ルミリステート、セチルイソオクタノエート、ジカプリ
ン酸ネオペンチルグリコールなどのエステル油、メチル
シリコン、メチルフェニルシリコン等のシリコン油、イ
ソステアリン酸、オレイン酸等の高級脂肪酸などの油性
成分;POEアルキルエーテル、POB分岐アルキルエ
ーテル、POEソルビタンエステル、POBグリセリン
脂肪酸エステル、POE硬化ヒマシ油、ソルビタンエス
テル、グリセリン脂肪酸エステル、ポリグリセリン脂肪
酸エステルなどの界面活性剤;ビタミン類、消炎剤、殺
菌剤、賦活剤、紫外線吸収剤などの薬剤;モンモリ
イト、サポナイト、ヘクトライトなどの水膨潤性粘度鉱
物;カラギーナン、キサンタンガム、アルギン酸ナトリ
ウム、プルラン、メチルセルロース、カルボキシメチル
セルロース、ヒドロキシエチルセルロース、ヒドロキシ
プロピルセルロース等の多糖類、カルボキシビニルポリ
マー、ポリビニルピロリドン、ポリビニルアルコール等
の合成高分子などの他の高分子;酸化チタン、カオリ
ン、マイカ、セリサイト、亜鉛華、タルク等の体質顔
料、ポリメチルメタクリル酸、ナイロンパウダー等の高
分子粉体などの顔料等を、本発明の効果を損なわない範
囲で適宜配合することができる。これらの成分のうち、
油性成分を配合した場合、乾燥時に形成される膜の剥離
強度を調節でき、皮膚に刺激を与えることなく良好に膜
の剥離をすることができる。また、多価アルコールは全
組成中に0.01〜50重量%配合するのが好ましい。
The keratotic plug remover of the present invention contains, in addition to the above components,
Components used in ordinary cosmetics, for example, ethylene glycol, diethylene glycol, triethylene glycol, higher polyethylene glycols, propylene glycol, dipropylene glycol, higher polypropylene glycols, 1,3-butylene glycol, 1,4 -Butylene glycols such as butylene glycol, glycerin, diglycerin, and higher polyglycerins, sugar alcohols such as sorbitol, mannitol, xylitol, maltitol, ethylene oxide of glycerin (hereinafter abbreviated as EO), propylene oxide ( (Hereinafter abbreviated as PO) adducts, EO of sugar alcohols, PO adducts, monosaccharides such as galactose, glucose, fructose and polysaccharides such as EO, PO adducts, maltose and lactose Polyhydric alcohols such as EO and PO adducts; hydrocarbons such as liquid paraffin, squalane, petrolatum, and solid paraffin; natural oils such as olive oil, jojoba oil, evening primrose oil, coconut oil, tallow, isopropyl myristate, and cetyl isoocta Oily components such as ester oils such as neoate and neopentyl glycol dicaprate, silicone oils such as methyl silicone and methyl phenyl silicone, and higher fatty acids such as isostearic acid and oleic acid; POE alkyl ether, POB branched alkyl ether, POE sorbitan ester Surfactants such as glycerin fatty acid ester of POB, POE hydrogenated castor oil, sorbitan ester, glycerin fatty acid ester, and polyglycerin fatty acid ester; agents such as vitamins, anti-inflammatory agents, bactericides, activators, and ultraviolet absorbers; Mori b Na <br/> site, saponite, water-swellable clay minerals, such as hectorite; carrageenan, xanthan gum, sodium alginate, pullulan, methylcellulose, carboxymethylcellulose, hydroxyethylcellulose, polysaccharides such as hydroxypropylcellulose, carboxyvinyl polymers, Other polymers such as synthetic polymers such as polyvinylpyrrolidone and polyvinyl alcohol; extender pigments such as titanium oxide, kaolin, mica, sericite, zinc white, and talc; polymer powders such as polymethylmethacrylic acid and nylon powder; Can be appropriately blended within a range not to impair the effects of the present invention. Of these ingredients,
When an oil component is added, the peel strength of a film formed during drying can be adjusted, and the film can be peeled well without causing irritation to the skin. Further, it is preferable that the polyhydric alcohol is incorporated at 0.01 to 50% by weight in the whole composition.

【0020】本発明の角栓除去剤の剤型は、パック剤の
他、綿布、スフ布、テトロン、ナイロン等の織布又はプ
ラスチックシート等に塗り、パップ剤としてもよい。
た本発明の角栓除去剤を用いて角栓を除去するには、例
えば上記パック剤又はパップ剤を皮膚(例えば鼻、額、
あご等の角栓の存在する部分)に塗布又は貼布し、乾燥
後、皮膚から剥離すればよい。
The dosage form of the keratotic plug removal agent of the present invention is
Besides, it may be applied as a poultice to a woven fabric such as a cotton cloth, a staple cloth, a tetron, a nylon, or a plastic sheet. Ma
Example of removing a keratotic plug using the keratotic plug removing agent of the present invention
For example, the above pack or cataplasm is applied to the skin (eg, nose, forehead,
Apply or paste to the area where horn plugs such as jaws exist) and dry
Later, it may be peeled off from the skin.

【0021】[0021]

【発明の効果】本発明の角栓除去剤を用いると、有効に
角栓が除去されるため、毛孔の目立ちが押さえられ、毛
孔内を清潔に保つことができ、更に皮膚を痛めることが
ない。
The use of the keratotic plug-removing agent of the present invention effectively removes keratotic plugs so that the pores are less noticeable, the pores can be kept clean, and the skin is not damaged. .

【0022】[0022]

【実施例】以下、実施例を挙げて本発明を更に詳細に説
明するが、本発明はこれらに限定されるものではない。
EXAMPLES The present invention will be described in more detail with reference to the following Examples, but it should not be construed that the invention is limited thereto.

【0023】実施例1 表1のポリマーを用い、下記パック処方により角栓除去
剤を調製した。これを洗顔後のパネラーに 0.1ml/cm2
で塗付し、25℃湿度50%で30分放置し、剥離し
た。これから次式により角栓除去率を求め評価した。結
果を表1に示す。
Example 1 Using the polymers shown in Table 1, a keratotic plug remover was prepared according to the following pack formulation. 0.1ml / cm 2 on the panel after washing face
And left for 30 minutes at 25 ° C. and 50% humidity, and peeled off. From this, the keratin plug removal rate was obtained and evaluated by the following equation. Table 1 shows the results.

【0024】[0024]

【数1】 (Equation 1)

【0025】評価: ○:角栓除去率が20%を超える △:角栓除去率が5〜20% ×:角栓除去率が5%未満Evaluation: :: The plug removal rate exceeds 20% Δ: The plug removal rate is 5 to 20% ×: The plug removal rate is less than 5%

【0026】 パック処方: ポリマー 15〜20(重量%) グリセロール 5 HCO60 (ポリオキシエチレン硬化ヒマシ油60EO付加) 1 エタノール 5 香料 0.5 防腐剤 適量 精製水 68.5〜73.5 計 100.0Pack formulation: polymer 15-20 (wt%) glycerol 5 HCO60 (polyoxyethylene hydrogenated castor oil 60EO added) 1 ethanol 5 fragrance 0.5 preservative qs purified water 68.5-73.5 total 100.0

【0027】[0027]

【表1】 [Table 1]

【0028】実施例2 表2のポリマーを用い、角栓除去率及び剥離時の痛みに
ついて評価した。 評価方法:表2のポリマーを20〜30重量%水溶液に
し、これを洗顔後のパネラーに0.1ml/cm2 で塗布
し、25℃、湿度50%で30分放置した後、剥離し
た。角栓除去率は実施例1と同様にして求めた。 (角栓除去率) 5%未満:× 5〜19%:△ 20〜34%:○ 35%以上:◎ (剥離時の痛み) やや痛みを感じる :+ かなり痛みを感じる :++
Example 2 The polymers shown in Table 2 were used to evaluate the keratotic plug removal rate and the pain at the time of peeling. Evaluation method: A 20 to 30% by weight aqueous solution of the polymer shown in Table 2 was applied to a face-washed panel at 0.1 ml / cm 2 , left at 25 ° C. and 50% humidity for 30 minutes, and then peeled off. The angle plug removal rate was determined in the same manner as in Example 1. (Square plug removal rate) Less than 5%: × 5-19%: △ 20-34%: ○ 35% or more: ◎ (Pain when peeling) Slightly painful: + Feeling quite painful: ++

【0029】[0029]

【表2】 [Table 2]

【0030】実施例3 下記組成の角栓除去剤を製造した。 ポリメタクリロイルオキシトリメチルアンモニウム クロライド(QDM)(分子量40万) 27.0(重量%) ソルビトール 3.0 セリサイト 3.0 エタノール 5.0 防腐剤 適量 水 バランスExample 3 A plug removing agent having the following composition was produced. Polymethacryloyloxytrimethylammonium chloride (QDM) (Molecular weight 400,000) 27.0 (% by weight) Sorbitol 3.0 Sericite 3.0 Ethanol 5.0 Preservatives Appropriate amount Water Balance

【0031】実施例4 下記組成の角栓除去剤を製造した。 ポリメタクリロイルオキシトリメチルアンモニウム クロライド(QDM)(分子量25万) 27.0(重量%) ポリオキシエチレン硬化ヒマシ油(E.O.20) 2.0 スクワラン 0.5 1−イソステアロイル−3−ミリストイル グリセロール(DGMI) 1.5 86%グリセロール 2.0 プロピレングリコール 1.0 セリサイト 3.0 エタノール 5.0 防腐剤 適量 水 バランスExample 4 A plug removing agent having the following composition was produced. Polymethacryloyloxytrimethylammonium chloride (QDM) (molecular weight 250,000) 27.0 (wt%) Polyoxyethylene hydrogenated castor oil (EO20) 2.0 squalane 0.5 1-isostearoyl-3-myristoyl glycerol (DGMI) 1.5 86% glycerol 2.0 propylene Glycol 1.0 sericite 3.0 ethanol 5.0 preservative qs water balance

【0032】実施例5 下記組成の角栓除去剤を製造した。 ポリメタクリロイルオキシトリメチルアンモニウム クロライド(QDM)(分子量20万) 15.0(重量%) ポリメタクリルアミドプロピルトリメチル アンモニウムクロライド(MAPTAC)(分子量30万) 15.0 ポリオキシエチレン硬化ヒマシ油(E.O.40) 1.5 スクワラン 0.5 2−エチルヘキサン酸トリグリセリド 2.0 ソルビトール 3.0 カオリン 7.0 酸化チタン 2.0 エタノール 5.0 防腐剤 適量 水 バランスExample 5 A plug removing agent having the following composition was produced. Polymethacryloyloxytrimethylammonium chloride (QDM) (Molecular weight 200,000) 15.0 (wt%) Polymethacrylamidopropyltrimethylammonium chloride (MAPTAC) (Molecular weight 300,000) 15.0 Polyoxyethylene hydrogenated castor oil (EO40) 1.5 Squalane 0.5 2- Ethylhexanoic acid triglyceride 2.0 Sorbitol 3.0 Kaolin 7.0 Titanium oxide 2.0 Ethanol 5.0 Preservative qs water balance

───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平2−258713(JP,A) 特開 昭62−93210(JP,A) 特開 昭56−131511(JP,A) 特開 昭54−49334(JP,A) 特開 昭49−132247(JP,A) 特開 昭58−180408(JP,A) 特開 昭63−57509(JP,A) 特開 昭61−15813(JP,A) (58)調査した分野(Int.Cl.6,DB名) A61K 7/00 - 7/50 ──────────────────────────────────────────────────続 き Continuation of front page (56) References JP-A-2-258713 (JP, A) JP-A-62-93210 (JP, A) JP-A-56-131511 (JP, A) JP-A-54-131 49334 (JP, A) JP-A-49-132247 (JP, A) JP-A-58-180408 (JP, A) JP-A-63-57509 (JP, A) JP-A-61-15813 (JP, A) (58) Field surveyed (Int. Cl. 6 , DB name) A61K 7/00-7/50

Claims (2)

(57)【特許請求の範囲】(57) [Claims] 【請求項1】 四級化したジアルキルアミノ基を有する
(メタ)アクリル酸エステル又は(メタ)アクリルアミ
ドを重合して得られる高分子化合物を含有することを特
徴とする角栓除去剤。
1. A keratotic plug removing agent comprising a polymer compound obtained by polymerizing a (meth) acrylic ester or a (meth) acrylamide having a quaternized dialkylamino group.
【請求項2】 請求項1の角栓除去剤を皮膚に塗布し、
乾燥後、皮膚から剥離して角栓を除去する方法。
2. Applying the keratotic plug remover of claim 1 to the skin,
A method of removing keratin plugs by peeling from the skin after drying.
JP8703392A 1991-05-15 1992-04-08 Keratin plug remover Expired - Lifetime JP2920443B2 (en)