JP2913062B2 - ポリテトラフルオロエチレンの一軸延伸成形物 - Google Patents

ポリテトラフルオロエチレンの一軸延伸成形物

Info

Publication number
JP2913062B2
JP2913062B2 JP9006190A JP9006190A JP2913062B2 JP 2913062 B2 JP2913062 B2 JP 2913062B2 JP 9006190 A JP9006190 A JP 9006190A JP 9006190 A JP9006190 A JP 9006190A JP 2913062 B2 JP2913062 B2 JP 2913062B2
Authority
JP
Japan
Prior art keywords
stretching
ptfe
molded
heated
film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP9006190A
Other languages
English (en)
Other versions
JPH02286220A (en
Inventor
アーダルベルト・ゲオルク・ヴィメル
クリスチャン・ハー・エフ・シュロスニクル
フランツ・ザースホーフェル
ラインハルト・ラインミューラー
Original Assignee
レンツィング・アクチエンゲゼルシャフト
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to AT81389A priority Critical patent/AT391473B/de
Priority to AT813/89 priority
Application filed by レンツィング・アクチエンゲゼルシャフト filed Critical レンツィング・アクチエンゲゼルシャフト
Publication of JPH02286220A publication Critical patent/JPH02286220A/ja
Application granted granted Critical
Publication of JP2913062B2 publication Critical patent/JP2913062B2/ja
Anticipated expiration legal-status Critical
Application status is Expired - Lifetime legal-status Critical

Description

【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、ポリテトラフルオロエチレン(PTFE)の一
軸延伸成形物及びその製造方法に関する。

〔従来の技術・発明が解決しようとする課題〕

PTFEは熱安定性を有し化学的に不活性であることか
ら、優れた特性を有する材料である。しかし、機械強度
が大きくかつ高密度のPTFE成形物の製造にはだれも成功
していないため、分野によってはその利用が制限されて
いる。

このような材料をたとえば織り糸に加工すれば、特に
耐磨耗性の優れたPTFE織物を製造することができる。絶
縁破壊強度は密度とともに増加するため、優れた強度と
高密度を組み合わせると電気伝導体の包装に好都合であ
る。

現在、最高250N/mm2の強度を有するPTFE成形物が市販
されているが、その密度は1g/cm3以下にとどまってい
る。これらの成形物は未焼結のPTFEに延伸することによ
り製造される。一方、今日知られているPTFE焼結体は約
2g/cm3の密度を有するが、強度は約50N/mm2以下であ
る。

AT−B 370 674から焼結PTFEの一軸延伸フィルムが公
知であるが、その延伸方向強度は50N/mm2〜140N/mm2
ある。これらのフィルムの製造は、まずPTFE粉末を円筒
状に圧縮成形した後、成形物を焼結し、ただちにフィル
ムをはぎ取り、少なくとも327℃の温度まで加熱し、延
伸させることによって行なわれる。

GB−A 2 025 835には、ペースト押出し法による多孔
性PTFE成形物の製造が述べられている。この方法では、
実質的にPTFE粉末と潤滑剤を含有するペースト塊をスピ
ナレットに通して圧縮した後、潤滑剤を乾燥除去する。
次いで、成形物をPTFEの結晶融点(327℃)以上の温度
に加熱し、同時に延伸を行なう。得られる成形物の強度
は延伸率に比例して増大するが、密度は逆に低下し、例
えば550%の延伸率では、強度は約42N/mm2に達するが、
密度は約0.4g/cm3に低下する。

本発明の目的は、上記の欠点を有しない、機械強度と
密度のいずれも高い値を示すPTFE成形物を提供すること
である。

〔課題を解決するための手段〕

本発明の製造方法によって得られたPTFE成形物は、一
軸延伸されており、その延伸方向の強度値は少なくとも
500N/mm2、好ましくは少なくとも700N/mm2であり、密度
は1.80g/cm3〜2.30g/cm3,好ましくは2.00g/cm3〜2.20g
/cm3であり、好ましくはフィルム、テープ、織り糸、あ
るいはミシン糸状に調製される。上記の強度値では、糸
は3%〜50%の伸び率を示す。

本発明においては、PTFE粉末を含有するペースト塊を
連続的に成形体に成形し、該成形体を複数のローラーま
たはロールに送り、該成形体を延伸する前に、該成形体
を327〜450℃、好ましくは350〜390℃の温度に加熱して
焼結し、次いで延伸することにより、該成形体を加熱延
伸し、少なくとも500N/mm2の延伸方向における強度値お
よび1.80〜2.30g/cm3の密度を有するPTFEの一軸延伸成
形物の製造方法であって、327〜450℃、好ましくは350
〜390℃の温度に加熱された1本のロールまたは1組の
ロール(3′,3″)と、加熱されていない引取装置
(4)との間で成形体を延伸する製造方法〔ただし、前
記延伸前に、軸方向における配向度が0.7以上となるま
であらかじめ延伸をしない。配向度は特願平1−186085
号明細書(特願平2−127509号公報)に記載の方法で測
定〕により、PTFEの一軸延伸成形物が製造される。

延伸は、1対5ないし1対30、好ましくは1対10ない
し1対20の延伸率で行なうことが有用であることが分か
った。延伸率を1対30として延伸を行なうと、約1150N/
mm2の強度が得られる。

本発明の方法の態様を図面によりさらに詳しく説明す
る。

まず、公知の方法でPTFE粉末を潤滑剤と混合し、20〜
50℃の温度で数時間保存し、10〜50バールの圧力で圧縮
して成形物を得る。次いで、同じく公知の方法でこの成
形体を単穴スピナレットに通して棒状に押出し成形し、
さらにロールにかけてフィルム状とし、潤滑剤を乾燥除
去する。

次いで、乾燥したフィルムを図面に示した焼結延伸装
置に連続的に送り込む。この装置は、本質的に送り手段
1、2個の加熱ロール3′及び3″、及び加熱しない引
取装置4′よりなる。図面中の矢印は、加熱ロール3′
及び3″の回転方向及びフィルムの引き抜き方向を示
す。

送り手段1に送られたフィルムは、加熱ロール3′及
び3″に連続的に送られ、ロール状で焼結される。その
間、フィルムは両面から加熱されるようにS字状にロー
ルに巻き付くのが好ましい。ロールは少なくとも327℃
の温度まで加熱されている。焼結工程終了後ただちに、
フィルムを延伸する。フィルムは、図面に示したように
数個のリールからなる加熱しない引取装置4により引き
抜かれる。最後に、延伸物を適当な一連のボビンに巻き
つける。

テープを製造する場合は、乾燥フィルムを送り装置1
に通す前に、カッターで切断しておくのが有利である。

〔実施例〕

以下に本発明を実施例によりさらに詳しく説明する。

実施例1 PTFEエマルジョン粉末100部とペトロール(融点範囲1
86〜214℃)23部を圧縮して円筒棒状とし、カレンダー
処理して厚さ0.1mmのフィルムを得、乾燥した。次い
で、フィルムを送り手段1に送り、切断して幅6mmの細
長い帯状とし、380℃に加熱したロール3′及び3″に
送り、焼結し、これらのロールにより1対15の延伸率で
延伸を行なった。得られたテープの強度は、5.6%の伸
び率で835N/mm2、密度は2.12g/cm3であった。延伸後の
厚みは0.0236mmに、幅は1.4mmになった。

得られたPTFEテープを織り糸(撚糸または非撚糸)及
びミシン糸(2重撚糸)にすることができた。

実施例2 実施例1と同様にして棒状に圧縮したPTFEをロールに
かけ、厚さ0.114mmのフィルムとし、乾燥した。このフ
ィルムを、幅200mmで、375℃に加熱したロール3′及び
3″に送り、同時に焼結を行なった。焼結開始後ただち
に1対15の延伸率で延伸を行なった。得られたフィルム
の強度は7.5%の伸び率で692N/mm2、密度は2.17g/cm3
あった。絶縁破壊密度は190kV/mmであったフィルムの幅
は46.6mm、厚さは0.024mmであった。

フィルムは小孔がなく、良好な走行特性と優れた電気
絶縁性を示し、電気伝導体の包装に最適であった。

実施例3 実施例1と同様にして棒状に圧縮したPTFEをロールに
かけ、厚さ0.05mmのフィルムとし、乾燥した。このフィ
ルムを切断して幅25mmの細長い帯とし、385℃に加熱し
たロール3′及び3″に送り、同時に焼結を行なった。
次いで、1対15の延伸率で延伸したところ、5.6%の伸
び率で703N/mm2の強度と1.93g/cm3の密度を有するフィ
ルムが得られた。フィルムは幅は5.8mm、厚さは0.013mm
であった。

【図面の簡単な説明】

図は本発明の実施例に係る焼結延伸装置の概略構成図で
ある。

フロントページの続き (51)Int.Cl.6 識別記号 FI B29L 7:00 (72)発明者 クリスチャン・ハー・エフ・シュロスニ クル オーストリア国 アー‐4840 フェック ラブルック、オーベルスタットグリース 5/4/18 (72)発明者 アーダルベルト・ゲオルク・ヴィメル オーストリア国 アー‐4840 フェック ブルック、アム・テニスプラツ 1 (56)参考文献 特開 平1−192812(JP,A) 特開 平2−127509(JP,A) 米国特許4064214(US,A) (58)調査した分野(Int.Cl.6,DB名) B29C 55/02 - 55/28 D01F 6/12

Claims (2)

    (57)【特許請求の範囲】
  1. 【請求項1】ポリテトラフルオロエチレン(PTFE)粉末
    を含有するペースト塊を連続的に成形体に成形し、該成
    形体を複数のローラーまたはロールに送り、該成形体を
    延伸する前に、該成形体を327〜450℃、好ましくは350
    〜390℃の温度に加熱して焼結し、次いで延伸すること
    により、該成形体を加熱延伸し、少なくとも500N/mm2
    延伸方向における強度値および1.80〜2.30g/cm3の密度
    を有するPTFEの一軸延伸成形物の製造方法であって、32
    7〜450℃、好ましくは350〜390℃の温度に加熱された1
    本のロールまたは1組のロール(3′,3″)と、加熱さ
    れていない引取装置(4)との間で成形体を延伸する
    (ただし、前記延伸前に、軸方向における配向度が0.7
    以上となるまであらかじめ延伸をしない)ことを特徴と
    するPTFEの一軸延伸成形物の製造方法。
  2. 【請求項2】1対5ないし1対30、好ましくは1対10な
    いし1対20の延伸率で成形体を延伸することを特徴とす
    る請求項1記載の製造方法。
JP9006190A 1989-04-06 1990-04-03 ポリテトラフルオロエチレンの一軸延伸成形物 Expired - Lifetime JP2913062B2 (ja)