JP2587760B2 - Processing method by laser light - Google Patents

Processing method by laser light

Info

Publication number
JP2587760B2
JP2587760B2 JP4358831A JP35883192A JP2587760B2 JP 2587760 B2 JP2587760 B2 JP 2587760B2 JP 4358831 A JP4358831 A JP 4358831A JP 35883192 A JP35883192 A JP 35883192A JP 2587760 B2 JP2587760 B2 JP 2587760B2
Authority
JP
Japan
Prior art keywords
parts
processing
manufactured
coating
solid content
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP4358831A
Other languages
Japanese (ja)
Other versions
JPH06198461A (en
Inventor
信一 中村
卓也 増澤
清志 岩本
良招 鏑木
Original Assignee
オー・ジー株式会社
株式会社巴川製紙所
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by オー・ジー株式会社, 株式会社巴川製紙所 filed Critical オー・ジー株式会社
Priority to JP4358831A priority Critical patent/JP2587760B2/en
Publication of JPH06198461A publication Critical patent/JPH06198461A/en
Application granted granted Critical
Publication of JP2587760B2 publication Critical patent/JP2587760B2/en
Anticipated expiration legal-status Critical
Application status is Expired - Fee Related legal-status Critical

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【産業上の利用分野】本発明は、レーザー光によって各種素材、特に金属を加工する方法に関し、更に詳しくは、レーザー光による加工の際に素材表面に生じるドロスの付着を防止する加工方法に関するものである BACKGROUND OF THE INVENTION This invention, various materials by laser light, relates particularly to a method for processing a metal, more particularly, it relates to a processing method for preventing the adhesion of dross generated in the material surface during processing by a laser beam it is.

【0002】 [0002]

【従来の技術】従来、各種材料特に金属材料に対して切断、穴開け等の加工を行なうにはボール盤、フライス盤、旋盤等の各種加工機械が用いられてきているが、最近になってレーザー光を使用した加工方法も実用化され普及してきている。 Conventionally, various materials in particular cutting the metal materials, drilling machine to perform the processing such as drilling, milling, various processing machines have been used such as a lathe, a laser beam has recently processing method using have also been put into practical use spread. レーザー光は小さな面積に高いエネルギーを集中できるため、特に工作精度を要求される分野では非常に有効な加工手段である。 Since laser light can concentrate the high energy in a small area, a very effective working means in the field to a particular request working accuracy. このようなレーザー光による加工は、被加工物に照射した光エネルギーを熱エネルギーに変換し、照射部を溶融させて行なわれるものである。 Processing with a laser beam, the light energy irradiated to the workpiece is converted into thermal energy, is to be performed by melting the irradiated portion. 従って、金属材料をそのままレーザー加工して切断、穴あけ、溶接、焼入をすると、溶融した金属クズ、いわゆるドロスが加工部周辺に付着し加工精度を著しく低下させ品質を落としたり、後工程でドロスの除去が必要になりコストアップする等の問題を生じるものであった。 Therefore, cut directly laser processing of metal material, drilling, welding, when the hardenability, molten metal debris, dropped or the quality significantly reduce the adhered machining accuracy so-called dross around the processed portion, the dross in a subsequent step removal of was achieved resulting in problems such as increasing costs required. このような加工部周辺へのドロスの付着を防止するために、従来は、例えば特開平4−203616 To prevent adhesion of dross to such processing unit neighborhood, conventionally, for example, JP-A-4-203616
号公報に記載されているようにシリコーン化合物等を金属材料の表面に塗布したり、特開平1−298113号公報に記載されているように、耐熱性を有する各種の無機顔料を塗料化して金属材料の表面に塗布したりして、 Like or applied to the surface of the metallic material of the silicone compounds as described in JP, as described in JP-A-1-298113, a metal various inorganic pigments having heat resistance and paint with or applied to the surface of the material,
これらをレーザー加工後にドロスとともに除去する方法が提案され実用化されている。 Method of removing with dross them after laser processing has been put into practical use is proposed. しかし、これらの方法はドロス付着防止には有効な手段であるが、加工後にシリコーン化合物や無機顔料塗料等の処理剤を除去するのに手間がかかり、また該処理剤を完全に除去するためには長時間の洗浄や有機溶剤による洗浄を要したり、特殊な洗浄器具が必要である等の問題点を有するものであった。 However, although these methods are effective means to dross adhesion prevention, time consuming to remove the treatment agent of the silicone compound or the like inorganic pigment coating after processing, also in order to completely remove the treatment agent or require cleaning by prolonged washing or organic solvents, had a problem of equal requires special cleaning implement. また、ステンレス板にはその表面保護の目的で、必要に応じて保護フィルムが粘着された状態で出荷されているものもあり、レーザー光による加工時には、これらの保護フィルムを剥離した後、前記処理剤を塗布することになるので、作業性に問題が残るものであった。 Further, the stainless steel plate for the purpose of the surface protection, while others protective film optionally is shipped with a pressure-sensitive adhesive, at the time of processing by the laser beam, after separating these protective films, said process it means to apply the agent was achieved, leaving a problem in workability.

【0003】 [0003]

【発明が解決しようとする課題】本発明は上記の如き事情に鑑みなされたもので、各種材料、特に金属材料をレーザー加工する際の加工部周辺へのドロスの付着の防止処理に関し、特にレーザー加工後の材料の後処理が非常に容易に行い得る加工方法を提供することを目的とするものである。 SUMMARY OF THE INVENTION It is an object of the present invention has been made in view of the above-mentioned circumstances, various materials, relates in particular to prevent the process of adhesion of dross to the working area around the time of laser processing of metal material, in particular a laser that it is subjected Hisage processing method aftertreatment of the material after processing can very easily performed and it is an object.

【0004】 [0004]

【課題を解決するための手段】 本発明は、加工しようとする金属材料等材料の被加工物の表面(少なくともレーザー光が照射される面もしくはその反対側の面)に、再剥離可能な工程紙をあらかじめ貼り合わせておき、レーザー加工を行なうことを特徴とし、加工後に該工程紙を剥離する加工方法である。 This onset Akira [Summary of] is the surface of the workpiece such as a metal material material to be machined (a surface at least a laser beam is irradiated or the opposite surface thereof), which can be removable the process paper advance bonded, characterized by performing laser processing, a processing method for peeling the casting papers after processing. ここに本発明で用いられる工程紙とは支持体の少なくとも片面に、耐熱性粒子を含有する再剥離可能な粘着層を有するもので、レーザー加工を行なう前に加工しようとする材料の前記表面に貼り合わせて使用するものである。 On at least one surface of the support with casting paper for use in the present invention herein, those having a re-peelable pressure-sensitive adhesive layer containing heat-resistant particles, the surface of the material to be processed before performing the laser processing it is intended to be used by bonding. このような工程紙をあらかじめ貼り合わせておくことによって、ドロスの付着を防止することができ、レーザー加工後には該工程紙を剥すだけでよいので、従来のドロス防止塗料に比較して、レーザー加工後の後処理に要する手間を大幅に改善できるという効果を有するものである。 By keeping bonding such steps paper advance, it is possible to prevent the dross deposition in, it is only peeled off the casting papers after laser processing, compared to the conventional dross prevention coating, laser processing those having the effect that the labor required for post-treatment after can be greatly improved. また、必要に応じて使用されていたステンレス板の保護フィルムの代わりにも使用できるので、従来のようなレーザー光による加工時に保護フィルムを剥してから処理剤を塗布するという手間を省き、作業性を大きく改善する効果も合わせ持つものである。 Since it is also used in place of the protective film of the stainless steel plate was used as needed, eliminating the trouble of applying the treatment agent from the peeled protective film during processing by conventional such a laser beam, workability greatly improved to effect those having combined.

【0005】 発明で使用する工程紙は、その構成として支持体の少なくとも片面に、耐熱性粒子を含有する再剥離可能な粘着層を設けたものである。 [0005] Step paper used in the present invention, on at least one surface of a support as a constituent is the ash provided re peelable adhesive layer containing a heat-resistant particles. ここで使用される耐熱性粒子としては有機化合物や無機化合物からなる微粒子等の使用が可能であり、これらの具体例としては遷移金属や非遷移金属、およびそれらの酸化物、硫化物、窒化物、フッ化物、炭化物、ハロゲン化物、硫酸塩、炭酸塩、硝酸塩、クロム酸塩、重クロム酸塩、しゅう酸塩、燐酸塩等の各種金属化合物や、チャンネルブラック、ファーネスブラック、ランプブラック、ボーンブラック等のカーボンブラック、及び鱗状黒鉛、土状黒鉛、人造黒鉛等の黒鉛、更に雲母、クレイ、タルク、カオリン、ベントナイト、シリカ等のケイ酸塩化合物が挙げられる。 Here the use of such fine particles composed of an organic compound or an inorganic compound as a refractory particles used are possible, these Examples the transition metal and non-transition metals, and their oxides, sulfides, nitrides , fluorides, carbides, halides, sulfates, carbonates, nitrates, chromates, dichromates, oxalate, and various metal compounds such as phosphates, channel black, furnace black, lamp black, bone black carbon black, and scaly graphite etc., earthy graphite, graphite such as artificial graphite, further mica, clay, talc, kaolin, bentonite, silicate compounds such as silica. これらの中でも特にアルミニウム、鉄、銅、 Aluminum JP Among them, iron, copper,
ニッケル、スズ、しんちゅう、ステンレス等の金属、合金類、酸化アルミニウム、二酸化チタン、酸化クロム、 Nickel, tin, brass, metal such as stainless steel, alloys, aluminum oxide, titanium dioxide, chromium oxide,
酸化バナジウム、二酸化マンガン、酸化鉄、酸化コバルト、酸化銅等の金属酸化物、黒鉛及びケイ酸塩化合物がコストおよび特性上から好ましい。 Vanadium oxide, manganese dioxide, iron oxide, cobalt oxide, metal oxides such as copper oxide, graphite and silicate compound is preferable from the cost and characteristics.

【0006】本発明で用いられる工程紙の粘着層に再剥離性を付与するのに使用される粘着剤としては、従来一般に用いられているゴム系、アクリル系、シリコーン系等各種粘着剤の使用が可能であるが、特に再剥離性を考えた場合には、(メタ)アクリル酸、マレイン酸、フマル酸、イタコン酸、2−ヒドロキシエチル(メタ)アクリレート、N−メチロール(メタ)アクリルアミド、アクリルアミド、N,N−ジエチルアミノエチル(メタ) [0006] As an adhesive used to impart removability to the adhesive layer of casting paper for use in the present invention, a rubber used for a conventional general, acrylic, use of silicone-based such as various adhesives Although possible, especially when considering the re-peelability, (meth) acrylic acid, maleic acid, fumaric acid, itaconic acid, 2-hydroxyethyl (meth) acrylate, N- methylol (meth) acrylamide, acrylamide , N, N-diethylaminoethyl (meth)
アクリレート、N,N−ジメチルアミノエチル(メタ) Acrylate, N, N-dimethylaminoethyl (meth)
アクリレート、グリシジル(メタ)アクリレート等の架橋性官能基を有するビニル重合性モノマーを共重合成分として含有するアクリル系粘着剤が好適であり、イソシアネート系、エポキシ系、金属キレート系等の架橋剤を使用することが更に好ましい。 Acrylate, glycidyl (meth) a vinyl-polymerizable monomer having a crosslinking functional group acrylate suitable acrylic pressure-sensitive adhesive containing as a copolymerization component, using an isocyanate-based, epoxy-based, metal chelate or the like crosslinking agent it is most preferable to set.

【0007】本発明で用いられる工程紙を構成する支持体としては、紙、布、不織布、ポリエチレンテレフタレート、ジアセテートセルロース、トリアセテートセルロース、アクリル系ポリマー、セロハン、セルロイド、ポリ塩化ビニル、ポリカーボネート、ポリイミド等のプラスチックからなるフィルム等の各種シート状物を適宜使用することができるものである。 [0007] As the support constituting the process paper used in the present invention include paper, cloth, nonwoven fabric, polyethylene terephthalate, diacetate cellulose, triacetate cellulose, acrylic polymers, cellophane, celluloid, polyvinyl chloride, polycarbonate, polyimide it is capable of a variety of sheet-like material such as a film of plastic used as appropriate. 特に支持体として紙を使用する場合には、粘着剤塗布時の支持体への浸透を抑えるためにあらかじめバリヤー層を設けることが好ましい。 Particularly in the case of using paper as a support, it is preferable to provide a pre-barrier layer in order to suppress the penetration of the support during adhesive application. バリヤー層は、従来一般に用いられているコーティング用の樹脂と、必要に応じて従来使用されている各種顔料より形成すればよい。 Barrier layer, and a resin for coating used in the conventional general, may be formed from various pigments which are conventionally used as needed. これらのコーティング用の樹脂の具体例としては、アクリル系樹脂、ポリエステル樹脂、ポリウレタン樹脂、スチレン−ブタジエン共重合体樹脂、アクリロニトリル−ブタジエン共重合体樹脂、ポリビニルアルコール系樹脂、水溶性ポリビニルアセタール樹脂、ポリビニルブチラール樹脂、その他のビニル系樹脂、アミド系樹脂、酸化でんぷん、カゼイン、ポリエチレンオキサイド、ポリビニルピロリドン、シリコーン系樹脂、ロジン変性マレイン酸樹脂、ロジン変性フェノール樹脂、アルキッド樹脂、クマロン−インデン樹脂等を単独あるいはこれらを2種以上組み合わせて用いることができる。 Specific examples of the resins for the coatings, acrylic resins, polyester resins, polyurethane resins, styrene - butadiene copolymer resins, acrylonitrile - butadiene copolymer resins, polyvinyl alcohol resin, water-soluble polyvinyl acetal resin, polyvinyl butyral resin, other vinyl-based resin, amide resin, oxidized starch, casein, polyethylene oxide, polyvinyl pyrrolidone, silicone resin, rosin-modified maleic acid resin, rosin-modified phenolic resins, alkyd resins, coumarone - indene resins alone or in it can be used in combination of two or more of these. 更にメラミン系、エポキシ系、グリオキザール等の架橋剤を含有させても良い。 Moreover melamine, epoxy, may contain a crosslinking agent such as glyoxal. また、同様にバリヤー層に使用される顔料の具体例としては、例えば、シリカ、クレー、マイカ、タルク、カオリン、ケイソウ土、炭酸カルシウム、硫酸カルシウム、硫酸バリウム、 Specific examples of pigments used in the barrier layer as well, for example, silica, clay, mica, talc, kaolin, diatomaceous earth, calcium carbonate, calcium sulfate, barium sulfate,
ケイ酸アルミニウム、合成ゼオライト、アルミナ、酸化亜鉛、リトポン、サチンホワイト等を単独使用するかあるいはこれらの2種以上を組み合せて使用することが可能である。 Aluminum silicate, synthetic zeolite, alumina, zinc oxide, lithopone, it is possible to use a combination of one or two or more of these is used alone satin white and the like.

【0008】本発明で用いられる工程紙の粘着層における耐熱性粒子の好ましい配合比率としては、粘着層の全固形分に対して6〜60重量%、特に好ましくは10〜 [0008] Preferred mixing ratio of the heat-resistant particles in the adhesive layer of casting paper for use in the present invention, 6 to 60 percent by weight relative to the total solids of the adhesive layer, particularly preferably 10 to
50重量%である。 50% by weight. ここで、耐熱性粒子の比率が6重量%未満では粘着層の耐熱性が不十分で、レーザー光加工後に材料表面からの剥離が困難になる。 Here, the proportion of refractory particles is insufficient heat resistance of the adhesive layer is less than 6 wt%, peeling of the material surface becomes difficult after laser beam machining. また添加量が6 The added weight of 6
0重量%を越えて多いと粘着層の粘着性が失われ、材料表面に貼着することができない。 0 sticky and often beyond wt% adhesive layer is lost, it can not be attached to the material surface. 支持体に粘着層、必要に応じてバリヤー層を設けるには、前述の各層を形成するための材料を、水又は適当な溶媒中に溶解もしくは分散させて調製した塗工液をロールコーティング法、ブレードコーティング法、エアナイフコーティング法、ロッドコーティング法等の方法により塗工し、これを乾燥させる方法や、前記の粘着層を形成することのできる材料を均一に混合した混合物を、前記支持体上にホットメルトコーティング法、ラミネートコーティング法等により積層して形成する方法などを適用することができる。 Adhesive layer on the support, the provision of the barrier layer as needed, the material for forming each layer described above, a roll coating method a coating solution prepared by dissolving or dispersing in water or in a suitable solvent, blade coating, air knife coating method, was coated by a method such as rod coating method, or a method of drying this mixture material were uniformly mixed capable of forming the adhesive layer, on the support hot melt coating method, a method of forming laminated by lamination coating method can be applied. 粘着層の塗布量としては、5g/m 〜50g/m 、好ましくは15〜30g/m 、またバリヤー層の塗布量としては、3〜20g/m 、好ましくは5〜15g/ The coating amount of the adhesive layer, 5g / m 2 ~50g / m 2, preferably as a coating weight of 15 to 30 g / m 2, also a barrier layer, 3~20g / m 2, preferably from 5 to 15 g /
である。 a m 2. 粘着層の塗布量が5g/m 未満では材料表面に貼着するに十分な粘着性を付与することができない。 The coating amount of the adhesive layer can not be provided with sufficient tack to adhere to the material surface is less than 5 g / m 2. また、50g/m を越えて多く塗布しても、塗布量に見合う特性が得られないばかりか、カッティング時の粘着剤のはみ出し等、後工程で支障を生じる恐れがあるので好ましくない。 Further, even if most applied beyond 50 g / m 2, not only impossible to obtain characteristics commensurate with the coating amount, etc. protruding cutting time of the adhesive, there is a possibility of causing a trouble in the subsequent step is not preferable.

【0009】 [0009]

【実施例】以下、実施例について説明する。 EXAMPLES In the following, a description will be given of an embodiment. 以下部とあるはすべて重量部を表わす。 All that there is less part by weight.

【0010】実施例1 支持体として90g/m の上質紙を使用し、その両面に下記組成よりなるバリヤー層用塗料を塗布、乾燥して塗布量10g/m のバリヤー層を設けた後にカレンダー処理を施した。 [0010] Using the high-quality paper of 90 g / m 2 as a first embodiment the support, a barrier layer coating consisting of the following composition on both surfaces thereof coated and dried after providing a barrier layer coating weight 10 g / m 2 It was subjected to a calender treatment. ・スチレンブタジエン系共重合ラテックス 150部 (ラックスターDS405、 大日本インキ化学工業社製、固形分45%) ・白雲母(A−11、山口雲母工業社製) 32部 ・水 100部 ・メラミン系架橋剤 13部 (スミレーズSR613、住友化学工業社製、固形分80%) Styrene butadiene copolymer latex 150 parts (LACSTER DS405, manufactured by Dainippon Ink and Chemicals, Inc., solid content 45%), white mica (A-11, manufactured by Yamaguchi Mica Co., Ltd.) 32 parts Water 100 parts melamine crosslinking agent 13 parts (Sumirezu SR613, manufactured by Sumitomo Chemical Co., Ltd., solid content 80%)

【0011】次に、上記バリヤー層の面に、下記組成よりなる粘着層用塗料を塗布、乾燥して塗布量20g/m [0011] Next, the surface of the barrier layer, applying an adhesive layer coating consisting of the following composition and dried to a coating weight 20 g / m
の粘着層を設けて本発明で用いる工程紙を作製した。 To prepare a casting papers for use in the present invention provided with a second adhesive layer. ・アクリル系粘着剤(カルボキシル基含有) 127部 (ファインタックSPS−1014、大日本インキ化学工業社製、 固形分44%) ・イソシアネート系架橋剤 10部 (バーノックD−750−45、大日本インキ化学工業社製、 固形分45%) ・酢酸エチル 80部 ・酸化アルミニウム(和光純薬社製) 22部 こうして得られた工程紙をステンレス板の片面に貼着し、工程紙を貼り合わせた面とは反対側の面からレーザー光(出力250W、発振パルス400Hz)を照射し窒素雰囲気中で切断速度400mm/minの条件でステンレス板を切断した。 Acrylic pressure-sensitive adhesive (carboxyl group-containing) 127 parts (Fine tack SPS-1014, manufactured by Dainippon Ink and Chemicals, Inc., solid content 44%) Isocyanate type crosslinking agent 10 parts (BURNOCK D-750-45, by Dainippon Ink chemical industry Co., Ltd., solid content 45%) ethyl acetate 80 parts aluminum oxide (product of Wako Pure chemical Industries, Ltd.) 22 parts the thus obtained casting paper adhered to one surface of the stainless steel plate was bonded to step paper surface was cut stainless steel plate on the opposite side of the laser light from the surface (output 250 W, oscillation pulses 400 Hz) conditions cutting speed 400 mm / min and in irradiated nitrogen atmosphere with.

【0012】実施例2 粘着層用塗料として下記組成のものを使用した以外は、 [0012] except that the following were used composition as a coating for Example 2 adhesive layer,
実施例1と全く同様にして本発明で用いる工程紙を作製し、ステンレス板に貼着後実施例1と同様の条件でステンレス板を切断した。 To prepare a casting papers for use in the present invention in the same manner as in Example 1, it was cut stainless steel plate under the same conditions as after sticking Example 1 a stainless steel plate. ・アクリル系粘着剤(カルボキシル基含有) 127部 (ファインタックSPS−1014、大日本インキ化学工業社製、 固形分44%) ・イソシアネート系架橋剤 10部 (バーノックD−750−45、大日本インキ化学工業社製、 固形分45%) ・酢酸エチル 80部 ・シリカ(アエロジルR805、日本アエロジル社製) 14.5部 Acrylic pressure-sensitive adhesive (carboxyl group-containing) 127 parts (Fine tack SPS-1014, manufactured by Dainippon Ink and Chemicals, Inc., solid content 44%) Isocyanate type crosslinking agent 10 parts (BURNOCK D-750-45, by Dainippon Ink chemical industry Co., Ltd., solid content 45%) ethyl acetate 80 parts silica (Aerosil R805, manufactured by Nippon Aerosil Co.) 14.5 parts

【0013】実施例3 粘着層用塗料として下記組成のものを使用した以外は、 [0013] except that the following were used composition as a coating for Example 3 the adhesive layer,
実施例1と全く同様にして本発明で用いる工程紙を作製し、ステンレス板に貼着後実施例1と同様の条件でステンレス板を切断した。 To prepare a casting papers for use in the present invention in the same manner as in Example 1, it was cut stainless steel plate under the same conditions as after sticking Example 1 a stainless steel plate. ・アクリル系粘着剤(カルボキシル基含有) 127部 (ファインタックSPS−1014、大日本インキ化学工業社製、 固形分44%) ・イソシアネート系架橋剤 10部 (バーノックD−750−45、大日本インキ化学工業社製、 固形分45%) ・酢酸エチル 80部 ・二酸化チタン(和光純薬社製) 36部 Acrylic pressure-sensitive adhesive (carboxyl group-containing) 127 parts (Fine tack SPS-1014, manufactured by Dainippon Ink and Chemicals, Inc., solid content 44%) Isocyanate type crosslinking agent 10 parts (BURNOCK D-750-45, by Dainippon Ink chemical industry Co., Ltd., solid content 45%) - ethyl 80 parts of titanium dioxide acetic acid (manufactured by Wako Pure chemical Industries, Ltd.) 36 parts

【0014】実施例4 粘着層用塗料として下記組成のものを使用した以外は、 [0014] except that the following were used composition as a coating for Example 4 adhesive layer,
実施例1と全く同様にして本発明で用いる工程紙を作製し、ステンレス板に貼着後実施例1と同様の条件でステンレス板を切断した。 To prepare a casting papers for use in the present invention in the same manner as in Example 1, it was cut stainless steel plate under the same conditions as after sticking Example 1 a stainless steel plate. ・アクリル系粘着剤(カルボキシル基含有) 127部 (ファインタックSPS−1014、大日本インキ化学工業社製、 固形分44%) ・イソシアネート系架橋剤 10部 (バーノックD−750−45、大日本インキ化学工業社製、 固形分45%) ・酢酸エチル 80部 ・二硫化モリブデン(スミパウダーPA、住鉱潤滑剤社製) 10部 Acrylic pressure-sensitive adhesive (carboxyl group-containing) 127 parts (Fine tack SPS-1014, manufactured by Dainippon Ink and Chemicals, Inc., solid content 44%) Isocyanate type crosslinking agent 10 parts (BURNOCK D-750-45, by Dainippon Ink chemical industry Co., Ltd., solid content 45%) ethyl acetate 80 parts molybdenum disulfide (charcoal powder PA, manufactured by Sumikojunkatsuzai Ltd.) 10 parts

【0015】施例5 粘着層用塗料として下記組成のものを使用した以外は、 [0015] except that the following were used composition as a coating for 施例 5 adhesive layer,
実施例1と全く同様にして本発明で用いる工程紙を作製し、ステンレス板に貼着後実施例1と同様の条件でステンレス板を切断した。 To prepare a casting papers for use in the present invention in the same manner as in Example 1, it was cut stainless steel plate under the same conditions as after sticking Example 1 a stainless steel plate. ・アクリル系粘着剤(カルボキシル基含有) 127部 (ファインタックSPS−1014、大日本インキ化学工業社製、 固形分44%) ・イソシアネート系架橋剤 10部 (バーノックD−750−45、大日本インキ化学工業社製、 固形分45%) ・酢酸エチル 80部 ・白雲母(A−11、山口雲母工業社製) 43部 Acrylic pressure-sensitive adhesive (carboxyl group-containing) 127 parts (Fine tack SPS-1014, manufactured by Dainippon Ink and Chemicals, Inc., solid content 44%) Isocyanate type crosslinking agent 10 parts (BURNOCK D-750-45, by Dainippon Ink chemical industry Co., Ltd., solid content 45%) ethyl acetate 80 parts muscovite (A-11, manufactured by Yamaguchi mica Co., Ltd.) 43 parts

【0016】実施例6 粘着層用塗料として下記組成のものを使用した以外は、 [0016] except that the following were used composition as a coating for Example 6 adhesive layer,
実施例1と全く同様にして本発明で用いる工程紙を作製し、ステンレス板に貼着後実施例1と同様の条件でステンレス板を切断した。 To prepare a casting papers for use in the present invention in the same manner as in Example 1, it was cut stainless steel plate under the same conditions as after sticking Example 1 a stainless steel plate. ・アクリル系粘着剤(カルボキシル基含有) 127部 (ファインタックSPS−1014、大日本インキ化学工業社製、 固形分44%) ・イソシアネート系架橋剤 10部 (バーノックD−750−45、大日本インキ化学工業社製、 固形分45%) ・酢酸エチル 80部 ・黒鉛(和光純薬社製) 22部 Acrylic pressure-sensitive adhesive (carboxyl group-containing) 127 parts (Fine tack SPS-1014, manufactured by Dainippon Ink and Chemicals, Inc., solid content 44%) Isocyanate type crosslinking agent 10 parts (BURNOCK D-750-45, by Dainippon Ink chemical industry Co., Ltd., solid content 45%) ethyl acetate 80 parts graphite (manufactured by Wako Pure chemical Industries, Ltd.) 22 parts

【0017】実施例7 粘着層用塗料として下記組成のものを使用した以外は、 [0017] except that the following were used composition as a coating for Example 7 the adhesive layer,
実施例1と全く同様にして本発明で用いる工程紙を作製し、ステンレス板に貼着後実施例1と同様の条件でステンレス板を切断した。 To prepare a casting papers for use in the present invention in the same manner as in Example 1, it was cut stainless steel plate under the same conditions as after sticking Example 1 a stainless steel plate. ・アクリル系粘着剤(カルボキシル基含有) 127部 (ファインタックSPS−1014、大日本インキ化学工業社製、 固形分44%) ・イソシアネート系架橋剤 10部 (バーノックD−750−45、大日本インキ化学工業社製、 固形分45%) ・酢酸エチル 80部 ・黒鉛(和光純薬社製) 36部 Acrylic pressure-sensitive adhesive (carboxyl group-containing) 127 parts (Fine tack SPS-1014, manufactured by Dainippon Ink and Chemicals, Inc., solid content 44%) Isocyanate type crosslinking agent 10 parts (BURNOCK D-750-45, by Dainippon Ink chemical industry Co., Ltd., solid content 45%) ethyl acetate 80 parts graphite (manufactured by Wako Pure chemical Industries, Ltd.) 36 parts

【0018】実施例8 粘着層用塗料として下記組成のものを使用した以外は、 [0018] except that the following were used composition as a coating for Example 8 adhesive layer,
実施例1と全く同様にして本発明で用いる工程紙を作製し、ステンレス板に貼着後実施例1と同様の条件でステンレス板を切断した。 To prepare a casting papers for use in the present invention in the same manner as in Example 1, it was cut stainless steel plate under the same conditions as after sticking Example 1 a stainless steel plate. ・アクリル系粘着剤(カルボキシル基含有) 127部 (ファインタックSPS−1014、大日本インキ化学工業社製、 固形分44%) ・イソシアネート系架橋剤 10部 (バーノックD−750−45、大日本インキ化学工業社製、 固形分45%) ・酢酸エチル 80部 ・カーボンブラック(#40、三菱化成社製) 25部 Acrylic pressure-sensitive adhesive (carboxyl group-containing) 127 parts (Fine tack SPS-1014, manufactured by Dainippon Ink and Chemicals, Inc., solid content 44%) Isocyanate type crosslinking agent 10 parts (BURNOCK D-750-45, by Dainippon Ink chemical industry Co., Ltd., solid content 45%) ethyl acetate 80 parts carbon black (# 40, manufactured by Mitsubishi chemical Industries, Ltd.) 25 parts

【0019】実施例9 粘着層用塗料として下記組成のものを使用した以外は、 [0019] except that the following were used composition as a coating for Example 9 adhesive layer,
実施例1と全く同様にして本発明で用いる工程紙を作製し、ステンレス板に貼着後実施例1と同様の条件でステンレス板を切断した。 To prepare a casting papers for use in the present invention in the same manner as in Example 1, it was cut stainless steel plate under the same conditions as after sticking Example 1 a stainless steel plate. ・アクリル系粘着剤(カルボキシル基含有) 127部 (ファインタックSPS−1014、大日本インキ化学工業社製、 固形分44%) ・キレート系架橋剤 8部 (ファインタックTA−101−CL、大日本インキ化学工業社製) ・酢酸エチル 80部 ・アルミニウム粉 36部 Acrylic pressure-sensitive adhesive (carboxyl group-containing) 127 parts (Fine tack SPS-1014, manufactured by Dainippon Ink and Chemicals, Inc., solid content 44%) chelate crosslinking agent 8 parts (Fine tack TA-101-CL, Dainippon ink chemical Co., Ltd.), 80 parts of aluminum powder and 36 parts of ethyl acetate

【0020】実施例10 粘着層用塗料として下記組成のものを使用した以外は、 [0020] except that the following were used composition as a coating for Example 10 the adhesive layer,
実施例1と全く同様にして本発明で用いる工程紙を作製し、ステンレス板に貼着後実施例1と同様の条件でステンレス板を切断した。 To prepare a casting papers for use in the present invention in the same manner as in Example 1, it was cut stainless steel plate under the same conditions as after sticking Example 1 a stainless steel plate. ・アクリル系粘着剤(カルボキシル基含有) 127部 (ファインタックSPS−1014、大日本インキ化学工業社製、 固形分44%) ・キレート系架橋剤 8部 (ファインタックTA−101−CL、大日本インキ化学工業社製) ・酢酸エチル 80部 . Acrylic pressure-sensitive adhesive (carboxyl group-containing) 127 parts (Fine tack SPS-1014, manufactured by Dainippon Ink and Chemicals, Inc., solid content 44%) chelate crosslinking agent 8 parts (Fine tack TA-101-CL, Dainippon ink chemical Co., Ltd.) ethyl acetate 80 parts. 銅粉 36部 Copper powder 36 parts

【0021】実施例11 粘着層用塗料として下記組成のものを使用した以外は、 [0021] except that the following were used composition as a coating for Example 11 the adhesive layer,
実施例1と全く同様にして本発明で用いる工程紙を作製し、ステンレス板に貼着後実施例1と同様の条件でステンレス板を切断した。 To prepare a casting papers for use in the present invention in the same manner as in Example 1, it was cut stainless steel plate under the same conditions as after sticking Example 1 a stainless steel plate. ・アクリル系粘着剤(カルボキシル基含有) 100部 (AS−15,一方社油脂工業社製、固形分40%) ・エポキシ系架橋剤 12部 (架橋剤P、一方社油脂工業社製) ・酢酸エチル 80部 ・鉄粉 36部 Acrylic pressure-sensitive adhesive (carboxyl group-containing) 100 parts (AS-15, Ipposha Oil Industries Co., Ltd., solid content: 40%) epoxy-based crosslinking agent 12 parts (manufactured crosslinker P, Ipposha Oil Industries Co., Ltd.) acetate ethyl 80 parts, iron powder 36 parts

【0022】実施例12 粘着層用塗料として下記組成のものを使用した以外は、 [0022] except that the following were used composition as a coating for Example 12 the adhesive layer,
実施例1と全く同様にして本発明で用いる工程紙を作製し、ステンレス板に貼着後実施例1と同様の条件でステンレス板を切断した。 To prepare a casting papers for use in the present invention in the same manner as in Example 1, it was cut stainless steel plate under the same conditions as after sticking Example 1 a stainless steel plate. ・シリコーン系粘着剤 100部 (X−40−3004A、信越化学工業社製、固形分60%) ・架橋剤 10部 (DX−3004、信越化学工業社製、固形分0.8%) ・トルエン 120部 ・タルク(関東化学社製試薬) 30部 Silicone based pressure-sensitive adhesive 100 parts (X-40-3004A, manufactured by Shin-Etsu Chemical Co., 60% solids) crosslinker 10 parts (DX-3004, Shin-Etsu Chemical Co., Ltd., solid content 0.8%) Toluene 120 parts talc (reagent produced by Kanto Kagaku Co., Ltd.) 30 parts

【0023】実施例13 粘着層用塗料として下記組成のものを使用した以外は、 [0023] except that the following were used composition as a coating for Example 13 the adhesive layer,
実施例1と全く同様にして本発明で用いる工程紙を作製し、ステンレス板に貼着後実施例1と同様の条件でステンレス板を切断した。 To prepare a casting papers for use in the present invention in the same manner as in Example 1, it was cut stainless steel plate under the same conditions as after sticking Example 1 a stainless steel plate. ・シリコーン系粘着剤 100部 (X−40−3004A、信越化学工業社製、固形分60%) ・架橋剤 10部 (DX−3004、信越化学工業社製、固形分0.8%) ・トルエン 225部 ・黒鉛(FUG−10、昭和電工社製) 4.5部 Silicone based pressure-sensitive adhesive 100 parts (X-40-3004A, manufactured by Shin-Etsu Chemical Co., 60% solids) crosslinker 10 parts (DX-3004, Shin-Etsu Chemical Co., Ltd., solid content 0.8%) Toluene 225 parts graphite (FUG-10, manufactured by Showa Denko KK) 4.5 parts

【0024】比較例1 ステンレス板に何も処理を行なわない以外は、実施例1 [0024] Except that does not perform any processing in Comparative Example 1 a stainless steel plate, Example 1
と同様の条件でステンレス板を切断した。 It was cut stainless steel plate under the same conditions as.

【0025】比較例2 粘着層用塗料として下記組成のものを使用した以外は、 [0025] except that the following were used composition as a coating for Comparative Example 2 The adhesive layer
実施例1と全く同様にして比較用の工程紙を作製し、ステンレス板に貼着後実施例1と同様の条件でステンレス板を切断した。 In the same manner as in Example 1 to prepare a process paper for comparison was cut stainless steel plate under the same conditions as after sticking Example 1 a stainless steel plate. ・アクリル系粘着剤 120部 (オリバインBPS3841、東洋インキ製造社製、固形分46.5%) ・架橋剤 3部 (オリバインBPS3841B、東洋インキ製造社製、固形分81%) ・酢酸エチル 120部 Acrylic adhesive 120 parts (Oribain BPS3841, from Toyo Ink Mfg. Co., solid content 46.5%) Crosslinking agent 3 parts (olivine BPS3841B, Toyo Ink Mfg. Co., solid content 81%) Ethyl acetate 120 parts

【0026】比較例3 ドロス防止用塗料として下記組成のものを調製し、ステンレス板の片面に塗布した。 [0026] were prepared as the following composition as Comparative Example 3 dross prevention paint was applied to one side of a stainless steel plate. 塗料を塗布した面とは反対側の面から、実施例1と同様の条件でステンレス板を切断した。 Paint from the surface opposite to the coated surface was cut stainless steel plate under the same conditions as in Example 1. ・シリコーンオイル(KF96、信越化学工業社製) 100部 ・白雲母(A−11、山口雲母工業社製) 30部 ・酢酸エチル 50部 Silicone oil (KF96, manufactured by Shin-Etsu Chemical Co., Ltd.) 100 parts muscovite (A-11, manufactured by Yamaguchi Mica Co., Ltd.) 30 parts Ethyl acetate 50 parts

【0027】以上、実施例1〜13、及び比較例2で得られたサンプルから工程紙を剥して、切断部の状態について、以下の各項目で評価した。 The above, and peeled off the casting papers from samples obtained in Examples 1 to 13, and Comparative Example 2, the state of the cut portion was evaluated in the following items. 又比較例1および3については、切断後の状態をそのまま評価した。 The Comparative Examples 1 and 3, a state after the cutting was directly assessed. <ドロスの付着> 切断面のドロスの付着状態を目視で確認した。 It confirmed the adhesion state of the dross of the cut surface <adherence of dross> visually. 切断部にドロスが付着しているものを×、付着していないものを〇とした。 × what is dross adheres to the cutting unit, was a 〇 those not attached. <切断部の変色> 切断部の高熱による変色状態を目視で確認した。 It confirmed the color change due to high heat of the cut <discoloration of the cut> visually. 切断部に変色が生じているものを×、変色していないものを〇、中間程度を△とした。 × what discoloration to the cutting portion has occurred, what is not discolored 〇, it was an intermediate degree △. <工程紙の剥離状態> 工程紙を剥す際の状況を判断した。 Determining a situation when peeling the casting papers <Peeling state of step feeding>. 容易に剥がれるものを〇、剥がれないものを×、中間程度を△とした。 Those easily peeled 〇, × those that do not come off, and the intermediate degree △. 評価結果は表1に示すとおりである。 The evaluation results are shown in Table 1.

【0028】 [0028]

【表1】 [Table 1]

【0029】表1の結果から明らかなように、本発明の加工方法はドロス付着防止や変色等の問題を全く生じないという優れた性能を有していることが確認された。 As is apparent from the results in Table 1, the processing method of the present invention was confirmed to have an excellent performance that no completely cause problems such as dross adhesion prevention and discoloration. それに対して比較例1の方法ではドロスの付着及び切断部の変色が発生していた。 Discoloration of attachment and the cutting portion of the dross has been generated in the method of Comparative Example 1 with respect to it. また比較例2では、工程紙の耐熱性が不十分なためステンレス板表面に工程紙が固着し工程紙を剥離することができなかった。 In Comparative Example 2, Step paper heat resistance insufficient for stainless steel plate the surface of casting paper could not be peeled off the sticking to process paper. また従来の塗料タイプのドロス防止方法である比較例3の方法ではドロス付着、切断部の変色とも問題ないレベルであったが、 The dross adhesion with conventional paint type dross preventing method in which Comparative Example 3 of the method, but was at a level no problem with discoloration of the cut,
加工後の塗料の除去に溶剤を含ませたウエスで拭き取るという方法を取らざるを得ず、また完全にシリコーン分を除去するには何回もの拭き取り作業を必要とし作業性に問題を有するものであった。 Forced to take a method of wiping with cloth moistened with a solvent for the removal of paint after processing without obtaining, also in order to remove the silicone component completely as it has a problem needed to workability even wiping work times there were.

【0030】 [0030]

【発明の効果】本発明の工程紙を使用するレーザー光加工方法及びこれに用いられる工程紙は、従来問題とされていた加工時のドロスの付着を防止できる優れた加工方法を提供できる。 Laser beam machining method using the casting papers of the present invention, according to the present invention and process paper used in this can provide excellent processing method capable of preventing the adhesion of dross during processing which has been the conventional problem. また加工後は工程紙を剥せば良いだけなので加工工程全体の作業性も非常に良好である。 Also after processing operations of the entire processing steps because only it peel off the casting papers it is also very good. それに加えて、本発明で用いる工程紙は保護シートの役割を果たすこともできるので、従来ステンレス板の場合その製造時に必要に応じて使用されていた保護フィルムに置き換えて使用することも可能であり、作業性を一層改善することができる。 In addition, since the casting paper for use in the present invention may also serve a protective sheet, it may be employed by replacing when the protective film is used as necessary at the time of manufacture of the conventional stainless steel plate , it is possible to further improve the workability.

───────────────────────────────────────────────────── フロントページの続き (72)発明者 増澤 卓也 大阪市淀川区宮原四丁目1番43号 オ ー・ジー株式会社内 (72)発明者 中村 信一 大阪市淀川区宮原四丁目1番43号 オ ー・ジー株式会社内 (56)参考文献 特開 昭58−34881(JP,A) ────────────────────────────────────────────────── ─── of the front page continued (72) inventor Masuzawa Takuya Yodogawa-ku, Osaka Miyahara chome No. 1 No. 43 Wow Gee within Co., Ltd. (72) inventor Nakamura, Shinichi Yodogawa-ku, Osaka Miyahara chome No. 1 43 No. Wow Gee within Co., Ltd. (56) reference Patent Sho 58-34881 (JP, a)

Claims (2)

    (57)【特許請求の範囲】 (57) [the claims]
  1. 【請求項1】 レーザー光を用いて材料を加工する方法において、あらかじめ被加工物の少なくともレーザー光の照射面もしくはその反対面のいずれか一方の面に、耐熱性粒子を含有する再剥離可能な粘着層を有する工程紙を貼り合わせてからレーザー加工を行なうことを特徴とするレーザー光による加工方法。 1. A method for processing a material using a laser beam, on one side either irradiation surface or the opposite surface thereof at least a laser beam in advance the workpiece, which can be re-peeled containing a heat-resistant particles working method using a laser beam and performing laser processing after attaching the casting papers having an adhesive layer.
  2. 【請求項2】 前記耐熱性粒子が少なくとも金属、金属酸化物、ケイ酸塩化合物及び黒鉛からなる群より選ばれる1種類であることを特徴とする請求項1記載のレーザー光による加工方法。 Wherein said heat-resistant particles is at least a metal, a metal oxide, a processing method by laser beam according to claim 1, characterized in that one kind selected from the group consisting of silicate compound and graphite.
JP4358831A 1992-12-28 1992-12-28 Processing method by laser light Expired - Fee Related JP2587760B2 (en)