JP2584230B2 - Metal wood golf club head and a method of manufacturing the same - Google Patents

Metal wood golf club head and a method of manufacturing the same

Info

Publication number
JP2584230B2
JP2584230B2 JP13347487A JP13347487A JP2584230B2 JP 2584230 B2 JP2584230 B2 JP 2584230B2 JP 13347487 A JP13347487 A JP 13347487A JP 13347487 A JP13347487 A JP 13347487A JP 2584230 B2 JP2584230 B2 JP 2584230B2
Authority
JP
Grant status
Grant
Patent type
Prior art keywords
club head
synthetic resin
golf club
metal
resin material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP13347487A
Other languages
Japanese (ja)
Other versions
JPS63300776A (en )
Inventor
隆治 奥本
達生 西本
Original Assignee
横浜ゴム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Grant date

Description

【発明の詳細な説明】 〔産業上の利用分野〕 この発明は、メタルウッドゴルフクラブヘッド及びその製造方法に係わり、更に詳しくはヘッド重量を増加させずに、メタルヘッドのフェイス部の強度を高め、かつ成形を容易にしたメタルウッドゴルフクラブヘッド及びその製造方法に関するものである。 BACKGROUND OF THE INVENTION [Field of the Industrial] This invention relates to a metal wood golf club head and a manufacturing method thereof, and more particularly without increasing head weight, increasing the strength of the face portion of the metal head and it relates to a metal wood golf club head and a manufacturing method thereof to facilitate molding.

〔従来の技術〕 [Prior art]

一般的に使用されているメタルウッドゴルフクラブのヘッド1は、第1図乃び第2図に示すように、スチール,ステンレス等の材料を使用して内部2が中空状に構成され、そしてその製造方法としては、クラブヘッドを2ないし3つに分割して鋳造し、これらを溶接で接合させて一体的に構成するロストワックス法が殆どである。 Head 1 metal wood golf club, which is commonly used, as shown in the first Zu乃 beauty Figure 2, steel, internal 2 using a material such as stainless steel configured in a hollow shape, and that as production method, casting is divided into three 2 to the club head, lost wax process which constitutes integrally by joining the welding is almost.

また、打球音を改善する目的から、クラブヘッド1の中空部2に、硬質ポリウレタンフォーム等のフォーム材を注入発泡させて充填したものも知られている。 Further, for the purpose of improving the hitting sound, the hollow portion 2 of the club head 1, it is also known that by filling the foam material of rigid polyurethane foam or the like by injection foaming.

ところで、メタルウッドゴルフクラブヘッド1は、上述したように金属材料を素材とするため重量が大きくなり易く、そのため肉厚を厚いものとすることができない上に、クラブヘッドの大きさは、パーシモンやカーボン繊維強化プラスチック等のクラブヘッドに比較して小さく構成されるのが一般的である。 By the way, metal wood golf club head 1, easy weight increases for the metal material as the material as described above, and therefore on that can not be made thick wall thickness, the size of the club head, persimmon Ya it is generally configured to be smaller as compared to the club head, such as carbon fiber reinforced plastic.

然しながら、あまり肉厚を薄いものにすると強度的な問題があって極端には薄いものとすることができず、特にボールを強打するフェイス部は強度を必要とするため、他の壁厚よりも肉厚しているが、それでも1.0mm〜 However, can not be extreme to those thin, there is a strength problem and make them too thin wall thickness, especially for the face portion to swipe the ball is in need of strength, than the other wall thickness Although the thick, but still 1.0mm~
2.5mmが限度である。 2.5mm is the limit. また一方、肉厚を限度近くの厚いものにするとクラブバランスの関係からクラブヘッドの大きさは、小型のものにしなければならず、するとゴルファーの心理的な影響が大きくなると言う問題が生じる。 On the other hand, the size of the club head from the relationship between the club balance when the wall thickness to those thick limit nearby is, must be a thing of the small, Then a problem that the psychological impact of the golfer becomes large.

従って、従来のメタルウッドゴルフクラブヘッドにおいては、軽量でかつ形状の大きい物とするためには、ボールを強打するフェイス部の肉厚も薄いものとせざるをえず、以下のような問題があった。 Therefore, in the conventional metal wood golf club head, in order to those of the light weight and shape large, there pictorial, the following problems forced to those thinner the thickness of the face portion to swipe the ball It was.

(a). (A). フェイス部の強度が弱くなり易く、またフェイス裏面側にリブ等を使用して補強した場合には重心が前方に移動して、ウッドクラブヘッドの特徴の一つとしての重心深度が不利となる問題がある。 Likely strength of the face portion becomes weak, and when reinforced using ribs or the like on the face back surface side moves the center of gravity forward, the depth of the center of gravity as one of the features of the wood club head is disadvantageous problem there is. 即ち、重心深度は、深い方がスウィートエリアが広くなる。 In other words, the depth of the center of gravity is, the deeper is the sweet area becomes wider.

(b). (B). 打球時のフェイス面の凹み等の変形によるエネルギーロスが大きく、ボールの飛距離が低下する。 Large energy loss due to dent deformation such as the face of the hitting, the flight distance of the ball is reduced.

(c). (C). 打球音が悪く、フォーム材を充填しても大きな改善は期待することができない。 Poor hitting sound, significant improvement can not be expected to be filled with a foam material.

〔発明の目的〕 [The purpose of the invention]

この発明は、かかる従来の課題に着目して案出されたもので、ヘッド重量の増加を微少にとどめ、クラブヘッドの重心深度を不利にすることなくフェイス部の強度を高めることが出来ると共に、成形を容易にしたメタルウッドゴルフクラブヘッド及びその製造方法を提供することを目的とするものである。 The present invention has been proposed in view of such conventional problems, with an increase in head weight minutely kept, it is possible to increase the strength of the face portion without penalizing depth of the center of gravity of the club head, it is an object to provide a metal wood golf club head and a manufacturing method thereof to facilitate molding.

〔発明の構成〕 [Configuration of the Invention

上記目的を達成する本発明によるメタルウッドゴルフクラブヘットは、金属材料で中空状に成形したクラブヘッド本体のフェイス部の裏面側に、該裏面側の壁面全域にわたり合成樹脂材を板状に密着させ、該合成樹脂材を平面状の裏面を有する略均一の肉厚にしたことを特徴とするものである。 Metal wood golf club Head according to the invention to achieve the above object, on the back side of the face portion of the club head body molded in a hollow shape by a metal material, it is brought into close contact with the synthetic resin material into a plate over the wall throughout the back surface side and is characterized in that the said synthetic resin material to a thickness substantially uniform with the rear surface of the plane.

また、本発明によるメタルウッドゴルフクラブヘッドの製造方法は、金属材料で中空状に成形したクラブヘッド本体を、そのフェイス部を下向きの略水平状態にするように設定し、該クラブヘッド本体のホーゼル部からヘッドの中空部内に注入パイプを挿入し、該注入パイプから液状末硬化の合成樹脂材を前記フェイス部の裏面側の壁面全域にわたるように注入し、該合成樹脂材を液面を平面状態に維持して硬化することにより略均一肉厚の樹脂補強層にすることを特徴とするものである。 The manufacturing method for a metal wood golf club head according to the invention, the club head body molded in a hollow shape by a metal material, set to the face portion in a substantially horizontal state downward, of the club head body hosel insert the filler pipe into the hollow portion of the head from the part, the synthetic resin material of the liquid powder curing implanted to span the back side of the wall the whole area of ​​the face portion from the infusion pipe, planar state the liquid level of the synthetic resin material it is characterized in that the reinforcing resin layer of substantially uniform thickness by curing while maintaining the.

〔発明の実施例〕 EXAMPLE OF THE INVENTION

以下添付図面に基づいて、この発明の実施例を説明する。 Based on the accompanying drawings, an embodiment of the present invention.

第3図は、この発明の第1実施例を示すメタルウッドゴルフクラブヘッドの断面図を示し、クラブヘッド本体 Figure 3 shows a cross-sectional view of a metal wood golf club head showing a first embodiment of the invention, the club head body
11は、スチール,スレンレス等の材料を使用して内部12 11 interior 12 is steel, using a material such as Surenresu
が中空状に構成されている。 There has been configured in a hollow shape.

前記クラブヘッド本体11のフェイス面13の裏面側側壁部13aには、衝撃強度が高く、かつ硬度が高い熱可塑性もしくは熱硬化性の合成樹脂材14が密着固着させてある。 Wherein the rear surface side wall portion 13a of the face surface 13 of the club head body 11, the impact strength is high and hardness is high thermoplastic or thermosetting synthetic resin material 14 are brought into close contact sticking. 合成樹脂材14は、フェイス面13の裏面側の壁面全域に、板状に密着し、かつ裏面14aが平面状となり、略均一の肉厚に形成されている。 Synthetic resin member 14, the wall surface throughout the back side of the face surface 13, in close contact with the plate, and the rear surface 14a becomes a flat shape, and is formed to a thickness of substantially uniform. このような平面状の略均一な肉厚であることより、重心深度を不利にせず、また打球時の衝撃荷量を均一に分散し、応力集中のない高強度にしている。 Than that such is flat substantially uniform wall thickness, without penalizing the centroid depth, also the impact load volume was uniformly dispersed at the time of hitting, and high strength without stress concentration.

前記、合成樹脂材14としては、エポキシ系の樹脂やウレタン系の樹脂を使用し、裏打ちされる合成樹脂材14の厚さとしては、3〜15mmが良く、ヘッド重量の増加を最小限に止め、かつ衝撃強度が高く、かつ硬度の高いものとする為には、5〜10mmが好ましい。 Wherein, as the synthetic resin material 14, using epoxy resin or urethane resin, the thickness of the synthetic resin material 14 to be lined, well 3 to 15 mm, kept to a minimum to increase the head weight and high impact strength, and in order to have high hardness, 5 to 10 mm is preferred.

また、上記の効果を更に大きいものとするためには、 Further, in order to make larger the effect of the above,
メタルフェイス部15と合成樹脂材14とは強固に密着させる点が重要であり、かつ長期に亘る使用(打球)に対して、合成樹脂材14が脱落,破壊等に耐え得ることが必要である。 It is important that to firmly adhere to the metal face portion 15 and the synthetic resin material 14, and against prolonged use (hitting), a synthetic resin material 14 is falling off, it is necessary to withstand destruction . このため第4図に示すように、メタルフェイス部15と合成樹脂材14との密着,固着を目的として、フェイス面13の裏面側側壁部13aに、合成樹脂材14の脱落防止用のリブ16を複数本設けるのが好ましい。 Therefore, as shown in Figure 4, the adhesion between the metal face portion 15 and the synthetic resin material 14, fixing purposes, on the back side wall portion 13a of the face surface 13, ribs for drop-off prevention of the synthetic resin material 14 16 preferably, a plurality of provided.

なお、リブ16の形状としては、フェイス面13に対して水平または垂直に複数本、または網目状,ハニカム状にすることも可能である。 As the shape of the rib 16, a plurality of horizontally or vertically with respect to the face surface 13 or mesh, it can also be in a honeycomb shape. 更に、上記の構成に加えて打球音を改善するため、第5図に示すようにクラブヘッド本体11の中空内部12に、硬質ポリウレタンフォーム等のフォーム材17を注入発泡させて充填させることも可能である。 Further, for improving the hitting sound in addition to the above configuration, the hollow interior 12 of the club head body 11 as shown in FIG. 5, it can also be filled by injecting foam foam material 17 of the rigid polyurethane foam, etc. it is.

更に、合成樹脂材14は、フェイス面13の裏面側側壁部 Further, the synthetic resin member 14, the rear surface side wall portion of the face surface 13
13aに均一の厚さで裏打ちする他に、第6図に示すようにクラブヘッド本体11の低重心を目的として、下方のみを肉厚にして構成することも可能である。 In addition to backing in a uniform thickness 13a, for the purpose of lowering the center of gravity of the club head body 11 as shown in FIG. 6, it is also possible to configure by only downward thick.

次に、メタルウッドゴルフクラブヘッドの製造方法について説明する。 Next, a method for manufacturing a metal wood golf club head.

まず第1の製造方法としては、スチール,ステンレス等の材料を使用して内部12が中空状に構成されたクラブヘッド本体11を、第7図に示すように、フェイス面13を下向きにして略水平状態に配置し、クラブヘッド本体11 The first of the manufacturing process, steel, a club head body 11 interior 12 is configured in a hollow shape by using a material such as stainless steel, as shown in FIG. 7, and the face surface 13 downwardly substantially placed in a horizontal state, the club head body 11
のホーゼル部17からヘッド内部12に注入パイプ18を挿入して、未硬化の合成樹脂材14を所定位置に所定量注入し、加熱硬化,自然硬化させて裏面側側壁部13a及びリブ16に密着硬化させ、樹脂補強層をわずか1工程で一気に成形することができる。 Insert the injection pipe 18 into the head interior 12 from the hosel portion 17 of the synthetic resin material 14 in uncured predetermined amount injected into place, heat curing, the adhesion to the rear surface side wall portion 13a and the ribs 16 and naturally cured cured, it is possible to stretch molding the resin reinforcing layer in just one step.

なお、合成樹脂材14は、上記のように中空状に構成されたクラブヘッド本体11の内部12に注入させることから、注入が出来る流動性を有するものであることが必要であり、従って注入後に硬化する熱硬化性または熱可塑性の合成樹脂材14を使用する。 Incidentally, the synthetic resin member 14, since it is injected into the interior 12 of the club head body 11 formed in a hollow shape as described above, it is necessary injection and has a fluidity which can, therefore after injection using the thermosetting or thermoplastic synthetic resin material 14 is cured.

また、合成樹脂材14が硬化した後、打球音を改善するためには、前記ホーゼル部17からヘッド内部12に硬質ポリウレタンフォーム等のフォーム材17を注入発泡させて充填させることも可能である。 Furthermore, after the synthetic resin material 14 is cured, in order to improve the hitting sound, it is also possible to fill with a foam material 17 of the rigid polyurethane foam or the like injected to foam the head interior 12 from the hosel part 17.

次に、この発明をエポキシ系樹脂とウレタン系樹脂を使用してクラブヘッド本体11を製造して実験した結果について説明する。 Next, the present invention uses the epoxy resin and urethane resin for the outcome of the experiment to produce a club head body 11.

〔実施例〕…エポキシ系の合成樹脂材を使用 TETRAD−X,三菱ガス化学製 (N,N,N′,N′−テトラグリシジルメタキシレンジアミン)・・・31,7重量部 日立化成製 (無水メチルハイミック酸)…68.3重量部 宇部興産製 (カルボキシ ターミネーテッド ブタヂエンアクリロニトル)…5.0重量部 〔実施例2〕…注型用ウレタン系樹脂を使用 エッチアンド・ケー(株)製…ハィーキャスト3070 ハィーキャストA液及びB液を重量比1:1で計算し、室温にて均一に混合し、メタルウ ッドクラブのヘッドフェイス面の裏面側側壁部に所定量注入し、60℃の恒温槽中で2時間加熱硬化させた。 EXAMPLES ... an epoxy-based synthetic resin material of TETRAD-X, manufactured by Mitsubishi Gas Chemical Company (N, N, N ', N'- tetraglycidyl metaxylene diamine) ... 31,7 parts by Hitachi Chemical Co., Ltd. ( anhydrous methyl high Mick acid) ... 68.3 parts by Ube Industries, Ltd. (carboxy-terminated Ted pig diethylene en acrylate Roni torr) ... 5.0 parts by weight example 2 ... using casting urethane resin etch and-cable Co. ... Haikyasuto 3070 Haikyasuto liquids a and B in a weight ratio of 1: 1 with calculated, and uniformly mixed at room temperature, a predetermined amount injected on the back side wall portion of the head face of Metaruu Ddokurabu, a constant temperature bath at 60 ° C. in cured by heating for 2 hours.

〔実験結果〕 上記のような合成樹脂材を使用して作成したクラブヘッドを、夫々ウッドゴルフクラブに仕立て、試打テストを行ったところクラブヘッドの重量並びにクラブバランスを略同一にして比較し、5mm以下合成樹脂材で補強したクラブヘッドは、メタルのみのクラブヘッドに比較して5%以上の飛距離の向上が確認出来た。 The club head produced by using Experiment results] The above-described synthetic resin material, tailored to each wood golf club, and compared with the weight and club balance of the club head was subjected to test hitting test to be substantially the same, 5 mm following the club head, which was reinforced with synthetic resin material, improvement of more than 5% of the distance in comparison with the club head of the only metal could be confirmed.

また、打球時の打音も従来のメタルウッド独特の軽い金属音に比較して重く、カーボンヘッドに近い軽妙な打球音を得ることが出来た。 In addition, the slapping sound of the time of hitting the ball even heavier as compared with the conventional metal wood distinctive light metallic sound, was able to get a witty hitting sound close to the carbon head.

〔発明の効果〕 〔Effect of the invention〕

この発明は、上述のように本はのメタルウッドゴルフクラブによれば、中空状のクラブヘッド本体のフェイス部の裏面側の全域にわたり合成樹脂材を板状に密着させたので、少量に限定された金属材料でクラブヘッドを出来るだけ大中空容量にするため薄肉にした場合でも、打球時にフェイス面に凹みなどを生じないような強度を与えることができる。 The present invention, according to the metal wood golf club of the present is as described above, since the synthetic resin material is adhered to the plate over the back side whole area of ​​the face portion of the hollow club head body, is limited to a small amount and a metal material even when thin to only large hollow volume can club head, it is possible to provide strength, such as not to cause such dents on the face surface when hitting. しかも、フェイス部裏面側の全域にわたる合成樹脂を平面状の裏面をもつ略均一厚みにしたので、重心深度に実質的に影響を与えることなく打球時の衝撃をフェイス部全面に均一に分散させ、一層高強度にすることができる。 Moreover, since the term synthetic resin entire area of ​​the face portion back side was substantially uniform thickness with a rear surface of the planar, uniformly disperse the impact of hitting the face portion the entire surface without substantially affecting the depth of the center of gravity, it can be made more high strength.

また、本発明のメタルウッドゴルフクラブヘッドの製造方法によれば、上記板状の合成樹脂材のクラブヘッド内への内貼りを僅か1工程で行うから、上記効果を有するメタルウッドゴルフクラブヘッドの製造を容易にし、 According to the manufacturing method for a metal wood golf club head of the present invention but performed in just one step the inner bonding to the plate-like synthetic resin material in the club head, the metal wood golf club head having the effect to facilitate the production,
生産性を向上することができる。 It is possible to improve the productivity.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

第1図は従来のメタルウッドゴルフクラブヘッドの全体斜視図、第2図は第1図のII−II矢視断面図、第3図〜 Figure 1 is an overall perspective view of a conventional metal wood golf club head, Figure 2 is II-II cross-sectional view taken along Figure 1, Figure 3 -
第6図はこの発明を実施したメタルウッドゴルフクラブヘッドの各断面図、第7図はこの発明のメタルウッドゴルフクラブヘッドの製造方法を示す説明図である。 Figure 6 is the sectional view of metal wood golf club head embodying the present invention, FIG. 7 is an explanatory diagram showing a manufacturing method for a metal wood golf club head of the present invention. 〔符号の説明〕 11……クラブヘッド本体、12……内部、 13……フェイス面、13a……裏面側側壁部、 14……合成樹脂材、15……メタルフェイス部 16……リブ、17……フォーム材 [DESCRIPTION OF REFERENCE NUMERALS] 11 ...... club head body, 12 ...... internal, 13 ...... face surface, 13a ...... rear surface side wall portion, 14 ...... synthetic resin material, 15 ...... metal face portion 16 ...... rib 17 ...... foam material

Claims (4)

    (57)【特許請求の範囲】 (57) [the claims]
  1. 【請求項1】金属材料で中空状に成形したクラブヘッド本体のフェイス部の裏面側に、該裏面側の壁面全域にわたり合成樹脂材を板状に密着させ、該合成樹脂材を平面状の裏面を有する略均一の肉厚にしたメタルウッドゴルフクラブヘッド。 To 1. A back side of the face portion of the club head body molded in a hollow shape by a metal material, is adhered over the wall throughout the back surface side of the synthetic resin material in a plate shape, a planar back surface of said synthetic resin material metal wood golf club head that was the thickness of the substantially uniform with.
  2. 【請求項2】前記フェイス部の裏面側に複数のリブを設け、これらリブを介して前記合成樹脂材を一体的に固着した特許請求の範囲第1項に記載のメタルウッドゴルフクラブヘッド。 Wherein a plurality of ribs on the back side of the face portion, the metal wood golf club head according to paragraph 1 the claims which is fixed integrally with the synthetic resin material through these ribs.
  3. 【請求項3】前記中空状のクラブヘッド本体の内部にフォーム材を充填した特許請求の範囲第1項または第2項に記載のメタルウッドゴルフクラブヘッド。 Wherein the hollow claims filled with foam material in the interior of the club head body of the first term or metal wood golf club head according to the second term.
  4. 【請求項4】金属材料で中空状に成形したクラブヘッド本体を、そのフェイス部を下向きの略水平状態にするように設定し、該クラブヘッド本体のホーゼル部からヘッドの中空部内に注入パイプを挿入し、該注入パイプから液状未硬化の合成樹脂材を前記フェイス部の裏面側の壁面全域にわたるように注入し、該合成樹脂材を液面を平面状態に維持して硬化することにより略均一肉厚の樹脂補強層にするメタルゴルフクラブヘッドの製造方法。 The wherein the club head body molded in a hollow shape by a metal material, set to the face portion in a substantially horizontal state downward, the filler pipe into the hollow portion of the head from the hosel part of the club head body inserted, substantially uniform by injecting to the synthetic resin material of liquid uncured from the infusion pipe over the back side of the wall the whole area of ​​the face portion, cured by maintaining the synthetic resin material of the liquid surface in the planar state method of manufacturing a metal golf club head to the resin reinforcing layer of thickness.
JP13347487A 1987-05-30 1987-05-30 Metal wood golf club head and a method of manufacturing the same Expired - Lifetime JP2584230B2 (en)