JP2022095499A - ポリエステルフィルムの回収方法、回収装置及び機能層除去剤 - Google Patents
ポリエステルフィルムの回収方法、回収装置及び機能層除去剤 Download PDFInfo
- Publication number
- JP2022095499A JP2022095499A JP2020208860A JP2020208860A JP2022095499A JP 2022095499 A JP2022095499 A JP 2022095499A JP 2020208860 A JP2020208860 A JP 2020208860A JP 2020208860 A JP2020208860 A JP 2020208860A JP 2022095499 A JP2022095499 A JP 2022095499A
- Authority
- JP
- Japan
- Prior art keywords
- polyester film
- functional layer
- agent
- cleaning agent
- cleaning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
また、仮に製膜できたとしても得られたフィルムの着色や、異物混入などによる品質の劣化が避けられない。
すなわち、易溶解性樹脂層を有さない、大部分の積層ポリエステルフィルムに用いることはできず、汎用性のない技術である。
上記実情に鑑みて、易溶解性樹脂層を有さない積層ポリエステルフィルムであっても、機能層を剥離でき、基材フィルムを回収することのできるポリエステルフィルムの回収方法を提案することを課題とする。
(1)ポリエステルフィルムの表面に機能層を備える積層ポリエステルフィルムを、酸性度定数(pKa)が8.0以上、20.0以下であるアルコール類を含有する洗浄剤で洗浄し、機能層を除去する、機能層除去工程(A)と、機能層を除去したポリエステルフィルムを回収する、回収工程(B)を有するポリエステルフィルムの回収方法。
(2)前記洗浄剤が水系洗浄剤である上記(1)に記載のポリエステルフィルムの回収方法。
(3)前記洗浄剤が、さらにアルカリ性化剤を含む上記(1)又は(2)に記載のポリエステルフィルムの回収方法。
(4)前記アルカリ性化剤が、アルカリ金属水酸化物を含む上記(3)に記載のポリエステルフィルムの回収方法。
(5)前記アルカリ金属水酸化物が水酸化カリウムを含有する上記(4)に記載のポリエステルフィルムの回収方法。
(6)前記アルコール類を2種類以上併用する上記(1)~(5)のいずれか1つに記載のポリエステルフィルムの回収方法。
(7)前記アルコール類の少なくとも1種類の酸性度定数(pKa)が9.0以上、10.0以下である上記(6)に記載のポリエステルフィルムの回収方法。
(8)前記機能層除去工程(A)における洗浄剤の温度が20℃以上である上記(1)~(7)のいずれか1つに記載のポリエステルフィルムの回収方法。
(9) 上記(1)~(8)のいずれか1つに記載の回収方法により回収したポリエステルフィルムを、原料として少なくとも一部に含むリサイクルポリエステル製品。
(10)洗浄装置を有するポリエステルフィルムの回収装置であって、洗浄装置において、ポリエステルフィルムの表面に機能層を備える積層ポリエステルフィルムを、酸性度定数(pKa)が8.0以上、20.0以下であるアルコール類を含有する洗浄剤で洗浄し、機能層を除去したポリエステルフィルムを回収することを特徴とする、ポリエステルフィルムの回収装置。
(11)前記機能層を除去したポリエステルフィルムに付着した洗浄剤を洗い流すリンス装置をさらに備える上記(10)に記載のポリエステルフィルムの回収装置。
(12)前記洗浄剤が水系洗浄剤であり、前記リンス装置において、水で水系洗浄剤を洗い流す上記(11)に記載のポリエステルフィルムの回収装置。
(13)前記機能層が除去されたポリエステルフィルムを乾燥する乾燥装置を備える上記(10)~(12)のいずれか1つに記載のポリエステルフィルムの回収装置。
(14)前記洗浄装置の前段に巻き出し装置を有する上記(10)~(13)のいずれか1つに記載のポリエステルフィルムの回収装置。
(15)ロールトゥロール方式で回収する上記(14)に記載のポリエステルフィルムの回収装置。
(16)前記洗浄装置の前段に裁断装置をさらに備える上記(10)~(13)のいずれか1つに記載のポリエステルフィルムの回収装置。
(17)ポリエステルフィルムの表面に機能層を備える積層ポリエステルフィルムから機能層を除去するための除去剤であって、酸性度定数(pKa)が8.0以上、20.0以下であるアルコール類を含有する、ポリエステルフィルム用機能層除去剤。
(18)前記除去剤が水系除去剤である上記(17)に記載のポリエステルフィルム用機能層除去剤。
(19)前記除去剤が、さらにアルカリ性化剤を含む上記(17)又は(18)に記載のポリエステルフィルム用機能層除去剤。
(20)前記アルカリ性化剤が、アルカリ金属水酸化物を含む上記(19)に記載のポリエステルフィルム用機能層除去剤。
(21)前記アルカリ金属水酸化物が水酸化カリウムを含有する上記(20)に記載のポリエステルフィルム用機能層除去剤。
(22)前記アルコール類を2種類以上併用することを特徴とする上記(17)~(21)のいずれか1つに記載のポリエステルフィルム用機能層除去剤。
(23)前記アルコール類の少なくとも1種類の酸性度定数(pKa)が9.0以上、10.0以下である上記(22)に記載のポリエステルフィルム用機能層除去剤。
本発明の積層ポリエステルフィルムの回収方法は、ポリエステルフィルムの表面に機能層を備える積層ポリエステルフィルムを、酸性度定数(pKa)が8.0以上、20.0以下であるアルコール類を含有する洗浄剤で洗浄し、機能層を除去する、機能層除去工程(A)と、機能層を除去したポリエステルフィルムを回収する、回収工程(B)を有する。
ここで、機能層除去工程(A)において、酸性度定数(pKa)が8.0以上、20.0以下であるアルコール類を使用することが重要であり、これによって、ポリエステルフィルム上の機能層を効果的に除去することができる。
そして、酸性度定数(pKa)が8.0以上、20.0以下であるアルコール類が、効率よく当該アルコキシドを生成することで、機能層の剥離が容易になったと考えられる。
本発明における積層ポリエステルフィルムとは、基材フィルムであるポリエステルフィルムの表面に樹脂層などの機能層が積層されたものをいう。
ポリエステルフィルムは、単層構造であっても多層構造であってもよい。多層構造の場合、2層構造、3層構造などでもよいし、4層又はそれ以上の多層であってもよく、層数は特に限定されない。また、ポリエステルフィルムは、二軸延伸フィルム等の延伸フィルムであっても未延伸フィルムであってもよい。
上記芳香族ジカルボン酸としては、例えば、テレフタル酸、2,6-ナフタレンジカルボン酸、イソフタル酸、フタル酸などが挙げられる。上記脂肪族グリコールとしては、例えば、エチレングリコール、ジエチレングリコール、プロピレングリコール、ブチレングリコール、1,4-シクロヘキサンジメタノール、ネオペンチルグリコール等を挙げることができる。
ポリエステルはホモポリエステルであっても、共重合ポリエステルであってもよい。また、ポリエステルは、芳香族ジカルボン酸、グリコール以外の第3成分を共重合体成分として含んでもよい。
2種類以上の層が積層されている場合、少なくとも1層が樹脂により構成されている層であることが好ましい。
本発明の方法では、機能層除去工程(A)において、酸性度定数(pKa)が8.0以上、20.0以下であるアルコール類を含有する洗浄剤で洗浄することを特徴とする。
アルコール類の酸性度定数(pKa)が上記範囲内であると、洗浄剤の液性を損ねることなく、アルコキシドが生成されるため、洗浄剤の洗浄能力が向上する。洗浄性の観点から、アルコール類の酸性度定数(pKa)が8.0以上、18.0以下がより好ましく、9.0以上、16.0以下がさらに好ましく、9.0以上、15.6以下の範囲が特に好ましく、9.3以上、15.4以下が最も好ましい。
酸性度定数(pKa)が8.0以上、20.0以下のアルコール類としては、ヘキサフルオロ-2-プロパノール(pKa=9.3)、ベンジルアルコール(pKa=15.4)、メタノール(pKa=15.5)、エタノール(pKa=16.0)、1-プロパノール(pKa=16.1)、2-プロパノール(pKa=17.1)、1-ブタノール(pKa=16.1)、tert-ブタノール(pKa=18.0)等が挙げられる。
これらのうち、前記酸性度定数(pKa)が好適な範囲である、ヘキサフルオロ-2-プロパノール、メチルアルコール、エチルアルコール、プロピルアルコール及びベンジルアルコールがより好ましい。なかでも、洗浄力の高いヘキサフルオロ-2-プロパノールが特に好ましい。
2種類以上のアルコール類を併用する場合は、洗浄能力を調整する観点から、酸性度定数(pKa)が9.0以上、10.0以下のアルコール類を少なくとも1種類含むことが好ましく、とりわけ、ヘキサフルオロ-2-プロパノール(pKa=9.3)とメチルアルコール、ヘキサフルオロ-2-プロパノールとエチルアルコール及びヘキサフルオロ-2-プロパノールとベンジルアルコールの併用が好ましい。なかでも、低揮発性及び使用可能な温度範囲の観点から、ヘキサフルオロ-2-プロパノールとベンジルアルコールの併用が特に好ましい。
また、上記以外のフェノール類あるいは上記好適なアルコール類以外のアルコール類を併用してもよく、具体的には、以下のものが例示される。
また、(a)成分中の、酸性度定数(pKa)が8.0以上、20.0以下のアルコール類の含有量としては、50~100質量%であることが好ましく、60~100質量%であることがより好ましく、70~100質量%であることがさらに好ましい。
(アルカリ性化剤)
アルカリ性化剤(以下、「(b)成分」とも記す)は、洗浄液をアルカリ性とするものであり、アルカリ剤とも呼べる。アルカリ性化剤としては、無機アルカリ性化剤であっても、有機アルカリ性化剤であってもよい。
界面活性剤とは、上記成分(a)及び/又は(b)並びにその他任意に添加される添加剤等を可溶化する成分であり、代表的には、後述する化合物が挙げられる。
酸化防止剤としては、特に限定されず、アミン系酸化防止剤、フェノール系酸化防止剤等を用いることができる。
防錆剤としては、クロム酸塩、モリブデン酸塩、亜硝酸ナトリウム等の無機化合物が挙げられる。
pH調整剤としては乳酸、二酸化炭素、コハク酸、グルコン酸、クエン酸、クエン酸三ナトリウム、リンゴ酸、リン酸、等が挙げられる。
防腐剤としてはパラベン系、安息香酸、安息香酸ナトリウム、ソルビン酸、プロピオン酸塩系、デヒドロ酢酸、二酸化硫黄及びピロ亜硫酸ナトリウム系等が挙げられる。
粘度調整剤としては、高分子化合物、層状無機粒子などが挙げられる。
消泡剤としては、フッ素系化合物、シリコーン系化合物、ポリエーテル系化合物、アセチレングリコール系化合物やEDTAに代表されるキレート剤等が挙げられる。
本発明に係る機能層除去工程は、前記洗浄剤を用いて、積層フィルムの機能層を除去する工程である。除去の方法としては、例えば、洗浄剤の入った洗浄槽に浸漬する浸漬法、溶液状態の洗浄剤を塗布する塗布法、溶液状態の洗浄剤又は気化した洗浄剤を吹き付ける吹き付け法などが挙げられる。これらのうち、機能層への洗浄剤の浸透性の点から、浸漬法が好ましい。
また、洗浄剤の温度の上限値としては、洗浄剤を溶液状態で用いる場合には、沸点以下の温度が好ましい。本願の好適な態様である水系洗浄剤の場合は、100℃以下が好ましく、90℃以下がより好ましい。
なお、浸漬法以外においても洗浄時の洗浄液の温度は、上記と同様である。また、浸漬法における剥離洗浄では、加水分解反応を進める目的として、マイクロ波照射を行ってもよい。
また、機能層除去工程から後述するリンス工程において、積層ポリエステルフィルムから効率良く機能層を除去する目的で、ロールブラシ、超音波、マイクロ/ナノバブル、水流、圧縮冷気などの物理的手段を備えた設備を設けてもよい。
前記機能層除去工程(A)の後に、基材フィルムであるポリエステルフィルムを回収する。回収工程の前段で、後述するリンス工程、及び乾燥工程を有することが好ましい。回収の方法としては、廃材である積層ポリエステルフィルムの形状に応じて、適当な方法を選択することができる。
本発明では、機能層除去工程(A)の後、回収工程(B)の前に、洗浄剤を洗い流すリンス工程を有することが好ましい。具体的には、リンス液により、機能層を除去したポリエステルフィルムに付着した洗浄剤を洗い流す工程を指す。
リンス工程の後には、乾燥工程を経ることが好ましい。乾燥工程によって、ポリエステルフィルム上に残存した洗浄剤及び/又はリンス液を除去できる。なお、リンス工程が省略される場合には、乾燥工程は、機能層除去工程(A)の後に行われるとよい。
本発明の回収方法により得られたポリエステルフィルムは、ポリエステル原料として利用でき、いわゆるリサイクルポリエステル製品として、再利用することができる。具体的には、回収したポリエステルはペレット化して、ペレット状のポリエステル(ポリエステル製品)として保管することができる。また、回収されたポリエステルは、溶融押出し等によってポリエステルフィルムなどの各種のポリエステル製品に成形することもできる。
なお、回収されたポリエステルは、その製造容易性から、一旦ペレット化した後に、各種製品に成形することが好ましい。
本発明の別の態様によれば、ポリエステルフィルムの表面に機能層を備える積層ポリエステルフィルムから機能層を除去するための除去剤(以下「本除去剤」ともいう)が提供される。
本発明に係るポリエステルフィルム用機能層除去剤は、上述したポリエステルフィルムの回収方法における機能層除去工程(A)で使用される洗浄剤を、前記ポリエステルフィルムから機能層を除去するために使用するものである。
本除去剤の具体的態様及び好ましい態様は、上記洗浄剤と同じであり、これらを全て援用することができる。
本除去剤は、ポリエステルフィルムから機能層を容易に除去することができ、積層ポリエステルフィルムから効率的にポリエステルフィルムを回収することができる。
本発明に係るポリエステルフィルムの回収装置は、洗浄装置を有する。回収装置は、洗浄装置にて洗浄され、機能層を除去したポリエステルフィルムを回収する。
塊状の場合には、ベルトコンベヤなどの搬送装置により、所定の回収位置に機能層を除去したポリエステルフィルムを搬送させて回収してもよい。
塊状の場合は、裁断装置を有していることが好ましい。裁断によって、廃材はフレーク状になり、前述のように、洗浄工程がより効率的になる。
洗浄装置は、酸性度定数(pKa)が8.0以上、20.0以下であるアルコール類を含有する洗浄剤で洗浄する装置である。典型的には、洗浄槽に上記洗浄剤を満たした洗浄槽が挙げられ、ここに廃材である積層ポリエステルフィルムを導入し、浸漬して洗浄する。その他、溶液状態の洗浄剤を塗布する塗布装置、溶液状態又は気化した洗浄剤や、洗浄剤のミストを形成してミストを吹き付ける吹付装置などがある。
リンス装置は、洗浄剤にて機能層を除去した後に、ポリエステルフィルムに付着した洗浄剤を洗い流すための装置である。具体的には、リンス液を吹き付ける吹付装置、リンス液に浸漬させる浸漬装置などが挙げられる。上述のように、洗浄剤として水系洗浄剤を用いることで、リンス工程で水を用いることができ、安全性が高く、また防爆装置などが不要であることからコスト面でも好ましい。
乾燥装置は、機能層が剥離され、洗浄剤が洗い流されたポリエステルフィルムを乾燥するためのものであり、乾燥条件については、前述の通りである。乾燥装置としては、赤外線ヒーター、オーブン、熱風乾燥機、及びマイクロ波加熱乾燥機などが挙げられる。乾燥装置における乾燥工程を経て、ポリエステル基材は回収される。なお、リンス装置が省略される場合にも、乾燥装置は、機能層が剥離されたポリエステルフィルムを乾燥するとよい。
(1)浸漬試験
各実施例及び比較例で調製した洗浄剤を30mlの水槽に入れ、積層フィルムを浸漬させた。洗浄剤の温度、浸漬時間、およびサンプルサイズは、表に記載の通りである。
(2-1)目視
(粘着層を有する積層ポリエステルフィルム、及びハードコート層を有する積層ポリエステルフィルム)
浸漬した積層フィルムを取り出して表面を目視観察し、以下の基準で評価した。
◎(very good);機能層が溶解又は剥離されており、基材であるポリエステルフィルムに大きな損傷がなく、実用上特に好ましい。
○(good);機能層が一部溶解又は剥離しており、実用上問題ない。
△(fair);機能層のごく一部が溶解又は剥離している。
×(bad);機能層が残ったままであり、実用上問題がある。
(シリコーン離型層を有する積層ポリエステルフィルム)
洗浄後の積層フィルムの表面を、蛍光X線分析装置(XRF、(株)島津製作所製「XRF-1800」)を用いてSi元素の定量分析を行った。
洗浄前の積層ポリエステルフィルム表面のSi元素量を100%、積層フィルムの機能層が塗工されていないプレーンフィルムのSi元素量を0%とすることで、機能層の除去率を測定した。
◎(very good);除去率90~100%
○(good);除去率70~89%
×(bad);除去率0~69%
ポリエステル1gを精秤し、フェノール/テトラクロロエタン=50/50(質量比)の混合溶媒100mlを加えて溶解させ、30℃で測定した。
次の(I)~(III)の機能層を有する積層ポリエステルフィルムを、試料として用意した。
(I)積層フィルム(アクリル系粘着層を有する積層ポリエステルフィルム);
市販品(日榮新化(株)製「PET75-H120(10)ブルー」)、ポリエチレンテレフタレートフィルムの厚み;75μm、アクリル系粘着層の厚み;10μm
下記手順にてアクリル系ハードコート層を有する積層ポリエステルフィルムを得た。
(アクリル系ハードコート溶液の調製)
ジペンタエリスリトールヘキサアクリレート24質量部、2-ヒドロキシ-3-フェノキシプロピルアクリレート6質量部、光重合開始剤(商品名:Omnirad 184、IGM Resins B.V.製)1.5質量部、トルエン70質量部の混合塗液とし、アクリル系ハードコート溶液を得た。
(アクリル系ハードコートフィルムの調製)
ポリエチレンテレフタレートフィルム;市販品(三菱ケミカル(株)製「ダイヤホイル」)上に、上記アクリル系ハードコート溶液を乾燥膜厚が約9μmとなるよう塗布し、紫外線を照射して硬化させ、アクリル系ハードコート層を有する積層ポリエステルフィルムを得た。
(a)成分としてベンジルアルコール40質量部、キシレノール10質量部、(b)成分として水酸化カリウム5質量部、その他の成分として水を45質量部となるように混合し、洗浄剤(pH=13以上)を調製した。
積層フィルム(I)~(III)を用いて、表1に記載の条件で洗浄性評価を実施した。結果を表1に示す。
(a)成分としてベンジルアルコール40質量部、プロピレングリコール1質量部、(b)成分として水酸化カリウム5質量部、水酸化ナトリウム5質量部及びモノエタノールアミン19質量部、その他の成分として水を30質量部となるように混合し、洗浄剤(pH=13以上)を調製した。
積層フィルム(I)~(III)を用いて、表1に記載の条件で洗浄性評価を実施した。結果を表1に示す。
積層フィルム(III)を浸漬時間1分、温度条件60℃で洗浄し、シリコーン離型層を除去したポリエステルフィルムの極限粘度を測定した結果、極限粘度は0.67であり、洗浄前後でのポリエステルフィルムの極限粘度は変化していなかった。
(a)成分としてベンジルアルコール16質量部、(b)成分として水酸化カリウム5質量部、水酸化ナトリウム5質量部、及びジエタノールアミン10質量部、その他の成分として水を64質量部となるように混合し、洗浄剤(pH=13以上)を調製した。
積層フィルム(I)及び(III)を用いて、表1に記載の条件で洗浄性評価を実施した。結果を表1に示す。
(a)成分としてベンジルアルコール95質量部、(b)成分として水酸化カリウム5質量部となるように混合し、洗浄剤(pH=13以上)を調製した。
積層フィルム(I)及び(III)を用いて、表1に記載の条件で洗浄性評価を実施した。結果を表1に示す。
(a)成分としてメタノール95質量部、(b)成分として水酸化カリウム5質量部となるように混合し、洗浄剤(pH=13以上)を調製した。
積層フィルム(III)を用いて、表1に記載の条件で洗浄性評価を実施した。結果を表1に示す。
(a)成分としてエタノール95質量部、(b)成分として水酸化カリウム5質量部となるとなるよう水に溶解し、洗浄剤を調製した。
積層フィルム(I)及び(III)を用いて、表1に記載の条件で洗浄性評価を実施した。結果を表1に示す。
(a)成分としてベンジルアルコール33.8質量部、ヘキサフルオロ-2-プロパノール3.8質量部、及びプロピレングリコール2.9質量部、(b)成分として水酸化カリウム5質量部、水酸化ナトリウム5質量部、及びモノエタノールアミン17.9質量部、その他の成分として水を31.6質量部となるように混合し、洗浄剤を調製した。
積層フィルム(III)を用いて、表1に記載の条件で洗浄性評価を実施した。結果を表1に示す。
(a)成分としてベンジルアルコール28.1質量部、ヘキサフルオロ-2-プロパノール9.4質量部、及びプロピレングリコール2.9質量部、(b)成分として水酸化カリウム5質量部、水酸化ナトリウム5質量部、及びモノエタノールアミン17.9質量部、その他の成分として水を31.6質量部となるように混合し、洗浄剤を調製した。
積層フィルム(III)を用いて、表1に記載の条件で洗浄性評価を実施した。結果を表1に示す。
(a)成分としてベンジルアルコール18.8質量部、ヘキサフルオロ-2-プロパノール18.8質量部、及びプロピレングリコール2.9質量部、(b)成分として水酸化カリウム5質量部、水酸化ナトリウム5質量部、及びモノエタノールアミン17.9質量部、その他の成分として水を31.6質量部となるように混合し、洗浄剤を調製した。
積層フィルム(III)を用いて、表1に記載の条件で洗浄性評価を実施した。結果を表1に示す。
(b)成分として、水酸化カリウム30質量部、その他の成分として水を70質量部となるように混合し、洗浄剤を調製した。積層フィルム(I)及び(III)を用いて、表1に記載の条件で洗浄性評価を実施した。結果を表1に示す。
温度条件を第1表に記載のように変更したこと以外は、比較例1と同様に洗浄性評価を実施した。結果を表1に示す。
試料を5分間洗浄剤に浸漬し、(株)ミツトヨ社製「シックネスゲージ ID-C112X/1012X」によって厚みを測定することで基材の厚み変化を測定した。
厚み変化が3μm以上あった場合をA、厚み変化が3μm未満であった場合をBとした。
実施例1と同じ組成の洗浄剤を用いて、表1に記載の条件で基材フィルム(IV)及び基材フィルム(V)の洗浄試験を行い、洗浄後の厚みを測定した。結果を表1に示す。
実施例2と同じ組成の洗浄剤を用いて、表1に記載の条件で基材フィルム(IV)及び基材フィルム(V)の洗浄試験を行い、洗浄後の厚みを測定した。結果を表1に示す。
洗浄剤におけるアルコール類の最良の形態の確認のために、実施例2、7、8及び9において、洗浄温度を40℃、浸漬時間を1.2分に洗浄条件を変更し、以下の基準にて洗浄評価を行った。結果を表2に示す。
なお、上記と同様に、洗浄後の積層フィルムの表面について、蛍光X線分析装置を用いてSi元素の定量分析を行うことで洗浄評価を行った。
機能層の除去率は、以下の基準で判断した。
○(good);除去率50~100%
△(fair);除去率0~49%
また、実施例2の結果から、本発明の方法によれば、機能層の除去工程(洗浄工程)前後でのポリエステルフィルムの極限粘度(IV)が低下しないため、回収したポリエステルフィルムを原料とするリサイクルポリエステル製品も、機械的物性等に優れる可能性が高い。
さらに、実施例7、8及び9の結果から、本発明の方法によれば、酸性度定数(pKa)が8.0以上、20.0以下であるアルコール類を2種類以上併用し、その少なくとも1種類の酸性度定数(pKa)が9.0以上、10.0以下であることで、フィルムに影響を及ぼす可能性が低い、より低温かつより短時間での機能層剥離も可能であることが分かった。
Claims (23)
- ポリエステルフィルムの表面に機能層を備える積層ポリエステルフィルムを、酸性度定数(pKa)が8.0以上、20.0以下であるアルコール類を含有する洗浄剤で洗浄し、機能層を除去する、機能層除去工程(A)と、機能層を除去したポリエステルフィルムを回収する、回収工程(B)を有するポリエステルフィルムの回収方法。
- 前記洗浄剤が水系洗浄剤である請求項1に記載のポリエステルフィルムの回収方法。
- 前記洗浄剤が、さらにアルカリ性化剤を含む請求項1又は2に記載のポリエステルフィルムの回収方法。
- 前記アルカリ性化剤が、アルカリ金属水酸化物を含む請求項3に記載のポリエステルフィルムの回収方法。
- 前記アルカリ金属水酸化物が水酸化カリウムを含有する請求項4に記載のポリエステルフィルムの回収方法。
- 前記アルコール類を2種類以上併用することを特徴とする請求項1~5のいずれか1項に記載のポリエステルフィルムの回収方法。
- 前記アルコール類の少なくとも1種類の酸性度定数(pKa)が9.0以上、10.0以下である請求項6に記載のポリエステルフィルムの回収方法。
- 前記機能層除去工程(A)における洗浄剤の温度が20℃以上である請求項1~7のいずれか1項に記載のポリエステルフィルムの回収方法。
- 請求項1~8のいずれか1項に記載の回収方法により回収したポリエステルフィルムを、原料として少なくとも一部に含むリサイクルポリエステル製品。
- 洗浄装置を有するポリエステルフィルムの回収装置であって、洗浄装置において、ポリエステルフィルムの表面に機能層を備える積層ポリエステルフィルムを、酸性度定数(pKa)が8.0以上、20.0以下であるアルコール類を含有する洗浄剤で洗浄し、
機能層を除去したポリエステルフィルムを回収することを特徴とする、ポリエステルフィルムの回収装置。 - 前記機能層を除去したポリエステルフィルムに付着した洗浄剤を洗い流すリンス装置をさらに備える請求項10に記載のポリエステルフィルムの回収装置。
- 前記洗浄剤が水系洗浄剤であり、前記リンス装置において、水で水系洗浄剤を洗い流す請求項11に記載のポリエステルフィルムの回収装置。
- 前記機能層が除去されたポリエステルフィルムを乾燥する乾燥装置を備える請求項10~12のいずれか1項に記載のポリエステルフィルムの回収装置。
- 前記洗浄装置の前段に巻き出し装置を有する請求項10~13のいずれか1項に記載のポリエステルフィルムの回収装置。
- ロールトゥロール方式で回収する請求項14に記載のポリエステルフィルムの回収装置。
- 前記洗浄装置の前段に裁断装置をさらに備える請求項10~13のいずれか1項に記載のポリエステルフィルムの回収装置。
- ポリエステルフィルムの表面に機能層を備える積層ポリエステルフィルムから機能層を除去するための除去剤であって、
酸性度定数(pKa)が8.0以上、20.0以下であるアルコール類を含有する、ポリエステルフィルム用機能層除去剤。 - 前記除去剤が水系除去剤である請求項17に記載のポリエステルフィルム用機能層除去剤。
- 前記除去剤が、さらにアルカリ性化剤を含む請求項17又は18に記載のポリエステルフィルム用機能層除去剤。
- 前記アルカリ性化剤が、アルカリ金属水酸化物を含む請求項19に記載のポリエステルフィルム用機能層除去剤。
- 前記アルカリ金属水酸化物が水酸化カリウムを含有する請求項20に記載のポリエステルフィルム用機能層除去剤。
- 前記アルコール類を2種類以上併用することを特徴とする請求項17~21のいずれか1項に記載のポリエステルフィルム用機能層除去剤。
- 前記アルコール類の少なくとも1種類の酸性度定数(pKa)が9.0以上、10.0以下である請求項22に記載のポリエステルフィルム用機能層除去剤。