JP2019075387A - バインダー組成物、非水電解質二次電池用電極および非水電解質二次電池 - Google Patents
バインダー組成物、非水電解質二次電池用電極および非水電解質二次電池 Download PDFInfo
- Publication number
- JP2019075387A JP2019075387A JP2019029431A JP2019029431A JP2019075387A JP 2019075387 A JP2019075387 A JP 2019075387A JP 2019029431 A JP2019029431 A JP 2019029431A JP 2019029431 A JP2019029431 A JP 2019029431A JP 2019075387 A JP2019075387 A JP 2019075387A
- Authority
- JP
- Japan
- Prior art keywords
- electrode
- vinylidene fluoride
- binder composition
- fluoride polymer
- active material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本実施形態に係るバインダー組成物は、電池が有する電極であって、集電体上に電極活物質を含む電極合剤層が形成されてなる電極において、電極活物質を集電体に結着させるために用いられるものである。バインダー組成物には、2種類のフッ化ビニリデン系重合体が含まれている。便宜上、本明細書等では、この2種類について、「第1のフッ化ビニリデン系重合体」および「第2のフッ化ビニリデン系重合体」と称する。また、本明細書等では、「第1のフッ化ビニリデン系重合体と第2のフッ化ビニリデン系重合体との混合物」を単に「ブレンド物」とも称する。なお、本実施形態に係るバインダー組成物においては、所望の効果を阻害しない限り、さらに別の重合体を含んでいてもよい。
第1のフッ化ビニリデン系重合体は、1.7dl/g以上の固有粘度を有するフッ化ビニリデン系重合体である。
[第2のフッ化ビニリデン系重合体]
第2のフッ化ビニリデン系重合体は、(メタ)アクリル酸を単量体単位として含むフッ化ビニリデン系重合体である。第2のフッ化ビニリデン系重合体は、単量体単位としてフッ化ビニリデンの他に(メタ)アクリル酸を含んでいればよく、他の単量体単位が含まれていてもよい。また、アクリル酸およびメタクリル酸両方の単量体単位を含んでいてもよい。中でも、(メタ)アクリル酸とフッ化ビニリデンとの共重合体であることが好ましい。中でも、アクリル酸とフッ化ビニリデンとの共重合体であることがより好ましい。なお、本明細書中において「(メタ)アクリル酸」は、アクリル酸およびメタクリル酸のいずれかを意味するものである。
本実施形態に係るバインダー組成物は、第1のフッ化ビニリデン系重合体と第2のフッ化ビニリデン系重合体とを混合することにより得られる。バインダー組成物の第1のフッ化ビニリデン系重合体の混合量と第2のフッ化ビニリデン系重合体の混合量との比率は、重量比で75:25〜25:75であることが好ましく、70:30〜30:70であることがより好ましく、60:40〜40:60であることがさらに好ましい。
本実施形態に係るバインダー組成物は、本実施形態に係るバインダー組成物を用いた電極合剤から形成される電極合剤層を有する電極において、電極合剤層と集電体との高い接着性すなわち、高い剥離強度を得ることができる。また、本発明に係るバインダー組成物を用いて得られた電極合剤層を有する電極では、その電極表面上に共重合体の凝集物が生じることを抑制することができる。
本実施形態における電極合剤は、バインダー組成物に、電極活物質と非水溶媒とを含ませたものである。この電極合剤を集電体上に塗布して電極合剤層を形成することにより、電極を作製することができる。電極合剤は、スラリー状であり、非水溶媒の量を調節することによって、所望の粘度に調整することができる。
本実施形態における電極合剤において用いられる非水溶媒としては、フッ化ビニリデン系重合体を溶解できる溶媒であれば特に限定されるものではない。非水溶媒としては、例えばN−メチル−2−ピロリドン(NMP)、ジメチルホルムアミド、N,N−ジメチルアセトアミド、N,N−ジメチルスルホキシド、ヘキサメチルホスホアミド、ジオキサン、テトラヒドロフラン、テトラメチルウレア、トリエチルホスフェート、トリメチルホスフェート、アセトン、メチルエチルケトン、およびテトラヒドロフランなどが挙げられる。これらの非水溶媒は、単独で用いてもよいし、二種類以上を混合した混合溶媒として用いてもよい。電極合剤において用いられる非水溶媒は、中でも、N−メチル−2−ピロリドン、N,N−ジメチルホルムアミドおよびN,N−ジメチルアセトアミドなどの含窒素系有機溶媒が好ましく、N−メチル−2−ピロリドンがより好ましい。
本実施形態における電極合剤において用いられる電極活物質は、上述したように、本実施形態に係る電極合剤を負極用の電極合剤とする場合には、負極用の電極活物質、すなわち負極活物質を用いればよく、本実施形態に係る電極合剤を正極用の電極合剤とする場合には、正極用の電極活物質、すなわち正極活物質を用いればよい。
本実施形態における電極合剤は、さらに導電助剤を含んでいてもよい。導電助剤は、LiCoO2等の電子伝導性の小さい活物質を使用する場合に、電極合剤層の導電性を向上する目的で添加するものである。導電助剤としては、例えば、カーボンブラック、カーボンナノチューブ、黒鉛微粉末および黒鉛繊維等の炭素物物質、ならびにニッケルおよびアルミニウム等の金属微粉末または金属繊維を用いることができる。
本実施形態における電極合剤は、上述の成分以外の他の成分を含んでいてもよい。他の成分としては、例えば、ポリビニルピロリドンなどの顔料分散剤等を挙げることができる。
図1を参照して、本実施形態に係る電極に関して以下に説明する。図1は、本実施形態における電極の断面図である。図1に示すように、電極10は、集電体11、電極合剤層12aおよび12bを有しており、集電体11上に電極合剤層12aおよび12bが形成されている。電極10は、上述したように、正極用の電極合剤を用いて電極合剤層12aおよび12bが得られる場合には正極となり、負極用の電極合剤を用いて電極合剤層12aおよび12bが得られる場合には負極となる。
図2を参照して、本実施形態に係る電池について以下に説明する。図2は、非水電解質二次電池の分解斜視図である。電池100は、正極1、負極2、セパレータ3および金属ケーシング5を有している。具体的には、電池100は、正極1と負極2との間にセパレータ3を配置した積層体を渦巻き状に巻き回した発電素子が、金属ケーシング5中に収容されている構造を有している。ここで、正極1または負極2は、図1における電極10と同様のものである。セパレータ3としては、ポリプロピレンおよびポリエチレン等の高分子物質の多孔性膜などの公知の材料を用いることができる。
本発明に係るバインダー組成物は、上記課題を解決するために、電極活物質を当該電極活物質が塗布される集電体に結着させるために用いられるバインダー組成物であって、固有粘度が1.7dl/g以上の第1のフッ化ビニリデン系重合体と、(メタ)アクリル酸を単量体単位として含む第2のフッ化ビニリデン系重合体とを含んでいるバインダー組成物である。
固有粘度(インヘレント粘度)ηiを算出するために、重合体80mgを20mlのN,N−ジメチルホルムアミドに溶解することによって重合体溶液を作製する。当該重合体溶液の粘度ηを、30℃の恒温槽内においてウベローデ粘度計を用いて測定する。固有粘度ηiは、当該粘度ηを用いて下記式によって求められる。
上記式において、η0は溶媒であるN,N−ジメチルホルムアミドの粘度、Cは0.4g/dlである。
次に、得られた電極の表面の観察方法について以下に説明する。製造した電極を、2cm×2cmに切削し、切削電極表面範囲内での直径1mm以上または長さ1mm以上の凝集物ならびに直径0.5mm以上または長さ0.5mm以上の凝集物の存在数を観察した。存在数は、切削電極4枚を目視で観察し、1枚当たりの凝集物の存在数を算出することで決定した。凝集物の有無は、表面上にフッ化ビニリデン系重合体の凝集物の存在が直径1mm以上または長さ1mm以上の凝集物が平均3個/枚以上確認される場合、もしくは直径0.5mm以上または長さ0.5mm以上の凝集物が平均5個/枚以上確認される場合は、共重合体の凝集物があると判断した。
[第1のフッ化ビニリデン系重合体:フッ化ビニリデン単独重合体(PVDF)]
第1のフッ化ビニリデン系重合体として、固有粘度1.7dl/gのPVDF(株式会社クレハ製 KF#1700)を使用した。
内容量2リットルのオートクレーブに、イオン交換水900g、ヒドロキシプロピルメチルセルロース0.4g、ブチルペルオキシピバレート2g、フッ化ビニリデン396g、およびアクリル酸の初期添加量0.2gの各量を仕込み、50℃に加熱した。重合中に圧力を一定に保つ条件で、アクリル酸を含む1重量%アクリル酸水溶液を反応容器に連続的に供給した。得られた重合体スラリーを脱水、乾燥してVDF/AA共重合体を第2のフッ化ビニリデン系重合体として得た。アクリル酸は、初期に添加した量を含め、全量4gを添加した。得られたVDF/AA共重合体の固有粘度は、2.5dl/gであった。
PVDFをN−メチル−2ピロリドン(以下、NMP)に溶解し、5重量%濃度のフッ化ビニリデン重合体溶液を作製した。同様の手法でVDF/AA共重合体の5重量%濃度溶液も作製した。
得られた電極合剤を、集電体である厚さ15μmのアルミ箔上にバーコーターで塗布し、これを恒温槽を用いて、窒素雰囲気下にて110℃で30分間一次乾燥を行い、次いで窒素雰囲気下にて130℃で2時間二次乾燥して、乾燥合剤目付け量がおよそ150g/m2の電極を作製した。
第1のフッ化ビニリデン系重合体を固有粘度2.1dl/gのPVDF(株式会社クレハ製 KF#7200)に変更した以外は、実施例1と同様にして電極を作製した。
第1のフッ化ビニリデン系重合体を固有粘度3.1dl/gのPVDF(株式会社クレハ製 KF#7300)に変更した以外は、実施例1と同様にして電極を作製した。
PVDFとVDF/AA共重合体との割合を25:75とした以外は、実施例3と同様にして電極を作製した。
PVDFとVDF/AA共重合体との割合を75:25とした以外は、実施例3と同様にして電極を作製した。
第1のフッ化ビニリデン系重合体として、固有粘度3.1dl/gのPVDF(株式会社クレハ製 KF#4300)を用い、PVDFとVDF/AA共重合体との割合を3:2とし、さらに、電極合剤の作製時に導電助剤としてカーボンブラック(SP;Timcal Japan社製 SuperP(登録商標) Li、平均粒子径40nm、比表面積60m2/g)を電極活物質に対して2重量部添加した以外は、実施例1と同様にして電極を作製した。
SPの代わりに導電助剤としてカーボンナノチューブ(CNT;平均直径15nm、比表面積200m2/g)を用いた以外は、実施例6と同様にして電極を作製した。
第2のフッ化ビニリデン系重合体を作製する際に、ブチルペルオキシピバレートの量およびアクリル酸の初期添加量を、それぞれ6gおよび0.8gに変更した以外は実施例3と同様にして電極を作製した。得られたVDF/AA共重合体の固有粘度は、1.5dl/gであった。
第2のフッ化ビニリデン系重合体を作製する際に、アクリル酸の初期添加量を0.8gとした以外は実施例3と同様にして電極を作製した。このとき得られたVDF/AA共重合体の固有粘度は3.0dl/gであった。
第1のフッ化ビニリデン系重合体を固有粘度1.1dl/gのPVDF(株式会社クレハ製 KF#1100)に変更した以外は、実施例1と同様にして電極を作製した。
第2のフッ化ビニリデン系重合体を用いずに、固有粘度3.1dl/gのPVDF(株式会社クレハ製 KF#7300)のみを用い、電極合剤の作製時に導電助剤としてSPを電極活物質に対して2重量部添加した以外は、実施例1と同様にして電極を作製した。
第1のフッ化ビニリデン系重合体を用いずに、VDF/AA共重合体のみを用い、電極合剤の作製時に導電助剤としてSPを電極活物質に対して2重量部添加した以外は、実施例1と同様にして電極を作製した。
導電助剤としてSPの代わりにCNTを用いた以外は、比較例2と同様にして電極を作製した。
導電助剤としてSPの代わりにCNTを用いた以外は、比較例3と同様にして電極を作製した。
VDF/AA共重合体を、固有粘度が2.1dl/gのカルボキシル基含有フッ化ビニリデン系重合体に代えた以外は実施例3と同様にして電極を作製した。
固有粘度が1.7dl/gであるPVDF(株式会社クレハ製 KF#1700)のみを用い、第2のフッ化ビニリデン系重合体を用いなかった以外は、実施例1と同様にして電極を作製し、剥離強度を測定した。
固有粘度が2.1dl/gであるPVDF(株式会社クレハ製 KF#7200)のみを用い、第2のフッ化ビニリデン系重合体を用いなかった以外は、実施例1と同様にして電極を作製した。
固有粘度が3.1dl/gであるPVDF(株式会社クレハ製 KF#7300)のみを用い、第2のフッ化ビニリデン系重合体を用いなかった以外は、実施例1と同様にして電極を作製した。
固有粘度が2.5dl/gであるVDF/AA共重合体のみを用い、第1のフッ化ビニリデン系重合体を用いなかった以外は、実施例1と同様にして電極を作製した。
第1のフッ化ビニリデン系重合体を用いずに、実施例8で調製した固有粘度が1.5dl/gであるVDF/AA共重合体のみを用いた以外は、実施例1と同様にして電極を作製した。
第1のフッ化ビニリデン系重合体を用いずに、実施例9で調製した固有粘度が3.0dl/gであるVDF/AA共重合体のみを用いた以外は、実施例1と同様にして電極を作製した。
[電極構造体における電極合剤層の接着性および凝集物生成の評価1]
実施例1〜7、および比較例1〜6で得られた電極におけるアルミ箔と電極合剤層との接着力は、塗工により形成した電極の上面をプラスチックの厚板と貼り合わせ、JIS K6854−1に準じて引張試験機(ORIENTEC社製「STA−1150 UNIVERSAL TESTING MACHINE」)を使用し、ヘッド速度10mm/分で90°剥離強度として評価した。プラスチックの厚板は、アクリル樹脂製であり、厚さ5mmである。各実施例および各比較例における剥離強度を測定した。また、各実施例および各比較例の電極合剤層における凝集物の生成を観察した。結果を表1に示す。
[電極の製造2]
(実施例10)
電極活物質としてリチウム−ニッケル−コバルト−マンガン複合酸化物(NCM111;Li1.00Ni0.33Co0.33Mn0.33O2、平均粒子径6μm)を用いた以外は実施例6と同様にして電極を作製した。
電極活物質としてNCM111(Li1.00Ni0.33Co0.33Mn0.33O2、平均粒子径6μm)を用いた以外は比較例2と同様にして電極を作製した。
電極活物質としてNCM111(Li1.00Ni0.33Co0.33Mn0.33O2、平均粒子径6μm)を用いた以外は比較例3と同様にして電極を作製した。
電極活物質としてリチウム−コバルト複合酸化物(LCO;LiCoO2、セルシードC5H、日本化学工業製、平均粒子径5μm)を用いた以外は実施例6と同様にして電極を作製した。
電極活物質としてLCO(LiCoO2、セルシードC5H、日本化学工業製、平均粒子径5μm)を用いた以外は比較例2と同様にして電極を作製した。
電極活物質としてLCO(LiCoO2、セルシードC5H、日本化学工業製、平均粒子径5μm)を用いた以外は比較例3と同様にして電極を作製した。
[電極構造体における電極合剤層の接着性および凝集物生成の評価2]
上記[電極構造体における電極合剤層の接着性および凝集物生成の評価1]と同様にして、実施例10、11および比較例13〜16における剥離強度を測定した。また電極合剤層における凝集物の生成を観察した。結果を表2に示す。
2 負極
3 セパレータ
5 金属ケーシング
10 電極
11 集電体
12a 電極合剤層
12b 電極合剤層
100 電池
Claims (8)
- 電極活物質を当該電極活物質が塗布される集電体に結着させるために用いられるバインダー組成物であって、
前記バインダー組成物は、固有粘度が1.7dl/g以上の第1のフッ化ビニリデン系重合体と、アクリル酸またはメタクリル酸を単量体単位として含む第2のフッ化ビニリデン系重合体と、導電助剤と、を含んでおり、
前記第1のフッ化ビニリデン系重合体は、フッ化ビニリデンのみを単量体単位として含むものであり、
前記導電助剤はカーボンナノチューブである
ことを特徴とするバインダー組成物。 - 上記第2のフッ化ビニリデン系重合体の固有粘度が1.0dl/g以上であることを特徴とする請求項1に記載のバインダー組成物。
- 上記第1のフッ化ビニリデン系重合体は、固有粘度が2.1dl/g以上であることを特徴とする請求項1または2に記載のバインダー組成物。
- 上記第1のフッ化ビニリデン系重合体と、上記第2のフッ化ビニリデン系重合体との混合比が、重量比で75:25〜25:75であることを特徴とする請求項1から3のいずれか1項に記載のバインダー組成物。
- 非水溶媒および上記電極活物質を含むことを特徴とする請求項1から4のいずれか1項に記載のバインダー組成物。
- 上記電極活物質は正極材料であることを特徴とする請求項5に記載のバインダー組成物。
- 集電体と集電体上に形成されている電極合剤層とを有する非水電解質二次電池用電極であって、
上記電極合剤層は、請求項1から6のいずれか1項に記載のバインダー組成物を用いて作製された層であることを特徴とする非水電解質二次電池用電極。 - 請求項7に記載の非水電解質二次電池用電極を備えていることを特徴とする非水電解質二次電池。