JP2018125002A - Selection method of writing member for touch panel pen, touch panel system, writing member for touch panel pen, touch panel, and display device - Google Patents

Selection method of writing member for touch panel pen, touch panel system, writing member for touch panel pen, touch panel, and display device Download PDF

Info

Publication number
JP2018125002A
JP2018125002A JP2018018512A JP2018018512A JP2018125002A JP 2018125002 A JP2018125002 A JP 2018125002A JP 2018018512 A JP2018018512 A JP 2018018512A JP 2018018512 A JP2018018512 A JP 2018018512A JP 2018125002 A JP2018125002 A JP 2018125002A
Authority
JP
Japan
Prior art keywords
touch panel
pen
average
panel pen
friction force
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2018018512A
Other languages
Japanese (ja)
Other versions
JP6984458B2 (en
Inventor
周望 田谷
Chikamochi Taya
周望 田谷
智洋 小川
Tomohiro Ogawa
智洋 小川
陽亮 高山
Yosuke Takayama
陽亮 高山
淳 辻本
Jun Tsujimoto
淳 辻本
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dai Nippon Printing Co Ltd
Original Assignee
Dai Nippon Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to JP2017018894 priority Critical
Priority to JP2017018894 priority
Application filed by Dai Nippon Printing Co Ltd filed Critical Dai Nippon Printing Co Ltd
Publication of JP2018125002A publication Critical patent/JP2018125002A/en
Application granted granted Critical
Publication of JP6984458B2 publication Critical patent/JP6984458B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a selection method of a writing member for a touch panel pen for improving efficiency of product design and quality control of a writing member.SOLUTION: A touch panel pen is fixed to a surface of a writing member for a touch panel pen while the touch panel pen is in contact at an angle of 60 degrees. While applying a normal load of 100 gf to the touch panel pen, dynamic frictional force in a moving direction applied to the touch panel pen when the writing member for a touch panel pen is moved for a length of 40 mm for one way at a speed of 14 mm/sec is measured at an interval of 0.001 sec, and the average of the dynamic frictional force is calculated at each 0.001 sec. Further, residual frictional force in the moving direction applied to the touch panel pen is measured at an interval of 0.001 sec, and the average of the residual frictional force is calculated at each 0.001 sec. A writing member in which the average of dynamic frictional force and the average of residual frictional force satisfy a relationship of "0.45<average of residual frictional force/average of dynamic frictional force" is selected as the writing member for a touch panel pen.SELECTED DRAWING: None

Description

本発明は、タッチパネルペン用筆記性部材の選別方法、タッチパネルシステム、タッチパネルペン用筆記性部材、タッチパネル及び表示装置に関する。   The present invention relates to a method for selecting a writable member for a touch panel pen, a touch panel system, a writable member for a touch panel pen, a touch panel, and a display device.

近年、タッチパネルは多くの携帯情報端末に搭載されるようになったこともあり、流通量が増加している。タッチパネルの表面には、種々の目的のために表面保護シートが貼着される場合がある。   In recent years, touch panels have been installed in many portable information terminals, and the distribution volume has increased. A surface protective sheet may be attached to the surface of the touch panel for various purposes.

従来主流であった抵抗膜式タッチパネルは、指やペンで繰り返し打点するような操作を行うことから、表面保護シートには高度な耐擦傷性が求められていた。
一方、現在の主流である静電容量式タッチパネルの表面保護シートには、指で操作する際の滑り性が求められている。従来の抵抗膜式は、複数個所を同時に検知できないため、画面上で指を動かすことはなかったものの、静電容量式タッチパネルは、複数個所を同時に検知可能であり、画面上で指を動かす操作が多いためである。
また、抵抗膜式及び静電容量式に共通して、タッチパネル用の表面保護シートには、指で操作した際の指紋の付着を抑制したり、付着した指紋を拭取りやすくする性能が求められている。
Conventionally, the resistance film type touch panel, which has been the mainstream, performs an operation of repeatedly hitting with a finger or a pen, and thus the surface protection sheet is required to have high scratch resistance.
On the other hand, the surface protection sheet of a capacitive touch panel, which is currently the mainstream, is required to have slipperiness when operated with a finger. The conventional resistive film type cannot detect multiple locations at the same time, so it does not move the finger on the screen, but the capacitive touch panel can detect multiple locations simultaneously, and moves the finger on the screen. This is because there are many.
In addition, in common with the resistive film type and the capacitive type, the surface protective sheet for touch panel is required to have the performance of suppressing the adhesion of fingerprints when operated with a finger or facilitating wiping off the adhered fingerprints. ing.

上記のようなタッチパネル用の表面保護シートとしては、例えば、特許文献1〜2が提案されている。   For example, Patent Documents 1 and 2 have been proposed as surface protective sheets for touch panels as described above.

特開2015−114939号公報JP2015-114939A 特開2014−109712号公報JP 2014-109712 A

静電容量式タッチパネルは、静電容量の変化を計測して触れた箇所を認識することから、接触物には一定の導電性が必要である。このため、静電容量式タッチパネルの出現当初は、指での操作性のみが検討されており、タッチパネルペンにより文字や絵を描くなどの筆記性は検討されていなかった。抵抗膜式タッチパネルにおいても、タッチパネルペンを用いた際の操作は打点が主流であり、文字や絵を描く際の筆記性は重視されていなかった。
しかし、近年、静電容量式タッチパネルや電磁誘導型タッチパネルに入力可能なタッチパネルペンが提案され始めたこと、タッチパネルペンによる文字入力や描画に対応したアプリケーションが増加してきたことから、タッチパネル用の表面保護シートには、タッチパネルペンでの良好な筆記感が求められている。
しかしながら、従来提案された特許文献1〜2のタッチパネル用の表面保護シートは、タッチパネルペンでの筆記感について何ら検討していない。さらに、近年、紙に鉛筆で筆記しているような高レベルな筆記感が求められるようになってきている。
Since the capacitive touch panel recognizes a touched place by measuring a change in capacitance, the contact object needs to have a certain conductivity. For this reason, at the beginning of the appearance of the capacitive touch panel, only operability with a finger was considered, and writing properties such as drawing characters and pictures with a touch panel pen were not considered. Also in the resistive touch panel, the operation when using the touch panel pen is mainly performed by dots, and the writing property when drawing characters and pictures is not emphasized.
However, in recent years, touch panel pens that can be input to capacitive touch panels and electromagnetic induction touch panels have begun to be proposed, and the number of applications that support character input and drawing using touch panel pens has increased. The sheet is required to have a good writing feeling with a touch panel pen.
However, the conventionally proposed surface protective sheets for touch panels of Patent Documents 1 and 2 do not consider any writing feeling with a touch panel pen. Furthermore, in recent years, a high level of writing feeling, such as writing on a paper with a pencil, has been demanded.

本発明は、高レベルの筆記感を得ることができるタッチパネルペン用筆記性部材の選別方法、タッチパネルシステム、タッチパネルペン用筆記性部材、タッチパネル及び表示装置を提供することを課題とする。   An object of the present invention is to provide a method for selecting a writable member for a touch panel pen, a touch panel system, a writable member for a touch panel pen, a touch panel, and a display device capable of obtaining a high level of writing feeling.

本発明者らは上記課題を解決すべく鋭意研究した結果、動摩擦力と、タッチパネルペンの操作を一旦停止した際の残留摩擦力との関係が高レベルな筆記感に大きな影響を与えることを見出し、上記課題を解決するに至った。
本発明は、以下[1]〜[5]のタッチパネルペン用筆記性部材の選別方法、タッチパネルシステム、タッチパネルペン用筆記性部材、タッチパネル及び表示装置を提供する。
As a result of diligent research to solve the above problems, the present inventors have found that the relationship between the dynamic friction force and the residual friction force when the operation of the touch panel pen is temporarily stopped has a great influence on a high level of writing feeling. The above problems have been solved.
The present invention provides a touch panel pen writable member selection method, a touch panel system, a touch panel pen writable member, a touch panel, and a display device according to [1] to [5] below.

[1]下記条件1−1を満たすものをタッチパネルペン用筆記性部材として選別する、タッチパネルペン用筆記性部材の選別方法。
<条件1−1>
タッチパネルペン用筆記性部材の表面に対してタッチパネルペンを60度の角度で接触させた状態で固定し、前記タッチパネルペンに垂直荷重100gfをかけながら、前記タッチパネルペン用筆記性部材を14mm/秒の速度で片道40mmの長さを移動させた際の前記タッチパネルペンにかかる前記移動方向の動摩擦力を0.001秒間隔で測定し、0.001秒ごとの動摩擦力の平均を算出する。
さらに、前記タッチパネルペン用筆記性部材の片道40mmの長さの移動が完了した後に、前記タッチパネルペンにかかる垂直荷重100gfを保持し、前記タッチパネルペン用筆記性部材の表面に対して前記タッチパネルペンを60度の角度で接触させたままの状態とする。この状態において、前記タッチパネルペンにかかる前記移動方向の残留摩擦力を0.001秒間隔で測定し、0.001秒ごとの残留摩擦力の平均を算出する。
前記動摩擦力の平均と前記残留摩擦力の平均とが「0.45<残留摩擦力の平均/動摩擦力の平均」の関係を示す。
[2]表面にタッチパネルペン用筆記性部材を有するタッチパネルと、タッチパネルペンとからなるタッチパネルシステムであって、上記条件1−1を満たすタッチパネルシステム。
[3]上記条件1−1を満たす表面を有するタッチパネルペン用筆記性部材。
[4]表面に筆記性部材を有するタッチパネルであって、前記筆記性部材として、上記[3]に記載のタッチパネルペン用筆記性部材の上記条件1−1を満たす側の面がタッチパネルの表面を向くように配置してなるタッチパネル。
[5]表示素子上にタッチパネルを有する表示装置であって、前記タッチパネルが上記[4]に記載のタッチパネルである、タッチパネル付きの表示装置。
[1] A method for selecting a writable member for a touch panel pen, wherein a material satisfying the following condition 1-1 is selected as a writable member for a touch panel pen.
<Condition 1-1>
The touch panel pen is fixed in a state where it is in contact with the surface of the writable member for touch panel pens at an angle of 60 degrees, and the writable member for touch panel pens is 14 mm / second while applying a vertical load of 100 gf to the touch panel pen. The moving frictional force in the moving direction applied to the touch panel pen when moving a length of 40 mm one way at a speed is measured at 0.001 second intervals, and the average of the dynamic frictional force every 0.001 second is calculated.
Furthermore, after the movement of the length of the one-way 40 mm of the touch panel pen writing member is completed, a vertical load of 100 gf is applied to the touch panel pen, and the touch panel pen is held against the surface of the touch panel pen writing member. The contact is made at an angle of 60 degrees. In this state, the residual friction force in the moving direction applied to the touch panel pen is measured at intervals of 0.001 seconds, and the average of the residual friction forces every 0.001 seconds is calculated.
The average of the dynamic friction force and the average of the residual friction force indicate a relationship of “0.45 <average of residual friction force / average of dynamic friction force”.
[2] A touch panel system comprising a touch panel having a writable member for a touch panel pen on the surface and a touch panel pen, which satisfies the above condition 1-1.
[3] A writable member for a touch panel pen having a surface satisfying the above condition 1-1.
[4] A touch panel having a writable member on the surface, wherein the surface of the touch panel pen writable member according to [3] that satisfies the above condition 1-1 is the surface of the touch panel as the writable member. Touch panel arranged to face.
[5] A display device having a touch panel on a display element, wherein the touch panel is the touch panel according to [4].

本発明のタッチパネルペン用筆記性部材の選別方法は、タッチパネルペンによる筆記試験を行わなくても、高レベルな筆記感が得られる筆記性部材を選別することができ、筆記性部材の製品設計、品質管理を効率よくすることができる。また、本発明のタッチパネルシステム、タッチパネルペン用筆記性部材、タッチパネル及び表示装置は、高レベルな筆記感を付与することができる。   The method for selecting a writable member for a touch panel pen according to the present invention can select a writable member that provides a high level of writing feeling without performing a writing test with a touch panel pen. Quality control can be made efficient. Moreover, the touch panel system, the writable member for a touch panel pen, the touch panel, and the display device of the present invention can impart a high level of writing feeling.

本発明のタッチパネルペン用筆記性部材の一実施形態を示す断面図である。It is sectional drawing which shows one Embodiment of the writable member for touchscreen pens of this invention. 本発明のタッチパネルペン用筆記性部材の他の実施形態を示す断面図である。It is sectional drawing which shows other embodiment of the writable member for touch-panel pens of this invention. 摩擦力の測定方法を説明する概略図である。It is the schematic explaining the measuring method of frictional force. タッチパネルペンの直径Dの算出方法を説明する図である。It is a figure explaining the calculation method of the diameter D of a touch-panel pen. 平均傾斜角θaの算出方法を説明する図である。It is a figure explaining the calculation method of average inclination-angle (theta) a. 本発明のタッチパネルの一実施形態を示す断面図である。It is sectional drawing which shows one Embodiment of the touchscreen of this invention. 本発明のタッチパネルの他の実施形態を示す断面図である。It is sectional drawing which shows other embodiment of the touchscreen of this invention.

以下、本発明のタッチパネルペン用筆記性部材の選別方法、タッチパネルシステム、タッチパネルペン用筆記性部材、タッチパネル及び表示装置の実施の形態を説明する。   Hereinafter, embodiments of the method for selecting a writable member for a touch panel pen, a touch panel system, a writable member for a touch panel pen, a touch panel, and a display device according to the present invention will be described.

[タッチパネルペン用筆記性部材の選別方法]
本発明のタッチパネルペン用筆記性部材の選別方法は、下記条件1−1を満たすものをタッチパネルペン用筆記性部材として選別するものである。
<条件1−1>
タッチパネルペン用筆記性部材の表面に対してタッチパネルペンを60度の角度で接触させた状態で固定し、前記タッチパネルペンに垂直荷重100gfをかけながら、前記タッチパネルペン用筆記性部材を14mm/秒の速度で片道40mmの長さを移動させた際の前記タッチパネルペンにかかる前記移動方向の動摩擦力を0.001秒間隔で測定し、0.001秒ごとの動摩擦力の平均を算出する。
さらに、前記タッチパネルペン用筆記性部材の片道40mmの長さの移動が完了した後に、前記タッチパネルペンにかかる垂直荷重100gfを保持し、前記タッチパネルペン用筆記性部材の表面に対して前記タッチパネルペンを60度の角度で接触させたままの状態とする。この状態において、前記タッチパネルペンにかかる前記移動方向の残留摩擦力を0.001秒間隔で測定し、0.001秒ごとの残留摩擦力の平均を算出する。
前記動摩擦力の平均と前記残留摩擦力の平均とが「0.45<残留摩擦力の平均/動摩擦力の平均」の関係を示す。
[Selection method of writable material for touch panel pen]
The selection method of the writable member for touch-panel pens of this invention selects what satisfies the following conditions 1-1 as a writable member for touch-panel pens.
<Condition 1-1>
The touch panel pen is fixed in a state where it is in contact with the surface of the writable member for touch panel pens at an angle of 60 degrees, and the writable member for touch panel pens is 14 mm / second while applying a vertical load of 100 gf to the touch panel pen. The moving frictional force in the moving direction applied to the touch panel pen when moving a length of 40 mm one way at a speed is measured at 0.001 second intervals, and the average of the dynamic frictional force every 0.001 second is calculated.
Furthermore, after the movement of the length of the one-way 40 mm of the touch panel pen writing member is completed, a vertical load of 100 gf is applied to the touch panel pen, and the touch panel pen is held against the surface of the touch panel pen writing member. The contact is made at an angle of 60 degrees. In this state, the residual friction force in the moving direction applied to the touch panel pen is measured at intervals of 0.001 seconds, and the average of the residual friction forces every 0.001 seconds is calculated.
The average of the dynamic friction force and the average of the residual friction force indicate a relationship of “0.45 <average of residual friction force / average of dynamic friction force”.

なお、60度とは、タッチパネルペン用筆記性部材の表面と平行な方向を0度として、表面に対して60度傾いていることを意味する。   60 degrees means that the direction parallel to the surface of the writable member for a touch panel pen is inclined at 60 degrees with respect to the surface, with the direction parallel to the surface being 0 degrees.

図1及び図2は、本発明のタッチパネルペン用筆記性部材10の一実施形態を示す断面図である。図1及び図2のタッチパネルペン用筆記性部材10は、基材1の一方の面に樹脂層2を有している。
本発明のタッチパネルペン用筆記性部材は、一方の表面が条件1−1を満たしていてもよいし、両方の表面が条件1−1を満たしていてもよい。
以下、タッチパネルペン用筆記性部材のことを「筆記性部材」、条件1−1を満たす表面のことを「筆記面」と称する場合がある。
FIG.1 and FIG.2 is sectional drawing which shows one Embodiment of the writable member 10 for touchscreen pens of this invention. 1 and 2 has a resin layer 2 on one surface of a substrate 1.
One surface of the writable member for a touch panel pen of the present invention may satisfy the condition 1-1, or both surfaces may satisfy the condition 1-1.
Hereinafter, a writable member for a touch panel pen may be referred to as a “writing member”, and a surface satisfying the condition 1-1 may be referred to as a “writing surface”.

<筆記面>
本発明のタッチパネルペン用筆記性部材の選別方法は、上記条件1−1を満たす表面を有するものをタッチパネルペン用筆記性部材として選別するものである。以下、条件1−1の設計の技術思想について説明する。
<Writing surface>
The selection method of the writable member for touch-panel pens of this invention selects what has the surface which satisfy | fills the said conditions 1-1 as a writable member for touch-panel pens. Hereinafter, the technical idea of the design under Condition 1-1 will be described.

文字を書いたり、図形を描いたりする際には、一瞬筆記を停止した後に再始動する場合が多い。例えば、筆記方向を転換する際には、通常は一瞬筆記を停止してから筆記方向を転換する。筆記を一瞬停止した後に再始動する際の筆記感には静摩擦力が大きく関連していると考えられるが、本発明者らの検討では、両者に十分な相関関係が見られない場合が散見された。   When writing letters or drawing figures, there are many cases where writing is stopped for a moment and then restarted. For example, when changing the writing direction, the writing direction is usually changed after the writing is stopped for a moment. The frictional force is considered to be greatly related to the feeling of writing when the writing is stopped for a moment and then restarted, but in our study, there are some cases where there is no sufficient correlation between the two. It was.

条件1−1の「残留摩擦力の平均(以下、「Fre」と称する場合がある。)」は、筆記性部材の移動が完了した後に、タッチパネルペンの荷重条件及び筆記性部材へのタッチパネルへの接触条件を保持した状態において、タッチパネルペンにかかる前記移動方向の摩擦力を示している。Freは、一瞬筆記を停止する際のペン先の止まりやすさや、タッチパネルペンを再始動する際に要する臨界的な力を示していると考えられる。つまり、Freは、一瞬筆記を停止する動作及び再始動する動作における筆記感(以下、「再始動時の筆記感」と称する場合がある。)に大きく影響すると考えられる。しかし、Freを調整したのみでは、再始動時の筆記感を十分にできない場合があった。
本発明者らは鋭意検討した結果、人間は一連の動作の際に直前の感覚を残しており、それ故、一瞬筆記を停止して再始動する際の筆記感には直前の動摩擦力が大きく影響していることを見出した。そして、Freと動摩擦力とを関連付けることにより、再始動時の筆記感を良好にすることができ、ひいては高レベルの筆記感を付与し得ることを見出した。
Condition 1-1 “Average of residual frictional force (hereinafter may be referred to as“ F re ”)” indicates the load condition of the touch panel pen and the touch panel to the writable member after the movement of the writable member is completed. In the state where the contact condition is maintained, the frictional force in the moving direction applied to the touch panel pen is shown. Fre is considered to indicate the ease of stopping the pen tip when stopping writing for a moment and the critical force required when restarting the touch panel pen. That is, Fre is considered to greatly affect the writing feeling in the operation of stopping writing for a moment and the operation of restarting (hereinafter sometimes referred to as “writing feeling at restart”). However, there are cases where the feeling of writing at the time of restart cannot be sufficiently achieved only by adjusting Fre .
As a result of diligent study, the present inventors have left the immediately preceding sensation during a series of movements. Therefore, the immediately preceding dynamic friction force is large in the writing sensation when writing is stopped and restarted for a moment. I found out that it was influencing. Then, it has been found that by associating Fre and dynamic friction force, the writing feeling at the time of restart can be improved, and as a result, a high level of writing feeling can be imparted.

条件1−1では、Freと、動摩擦力の平均(以下、「F」と称する場合がある。)の関係式「Fre/F」が0.45超であることを要求している。
re/Fが0.45以下であることは、Fに比べてFreが小さ過ぎることを意味する。この場合、筆記を停止する際にペンの駆動力を0近傍に調整する動作が非常に困難となり、ペン先が止まり難くなったり、ペンが滑ると感じられるようになり、思い通りの位置と方向に筆記方向を転換しにくくなる。したがって、Fre/Fが0.45以下の場合、再始動時の筆記感を良好にすることができず、高レベルの筆記感を付与できない。
Condition 1-1 demands that the relational expression “F re / F k ” of F re and the average of dynamic friction forces (hereinafter sometimes referred to as “F k ”) exceeds 0.45. Yes.
It F re / F k is 0.45 or less means that F re is too small as compared with F k. In this case, when stopping writing, it becomes very difficult to adjust the pen driving force to near zero, the tip of the pen becomes difficult to stop or the pen feels slipping, and the position and direction as expected. It becomes difficult to change the writing direction. Therefore, when Fre / Fk is 0.45 or less, the writing feeling at the time of restart cannot be improved, and a high level writing feeling cannot be imparted.

なお、Fre/Fが大き過ぎると、筆記を一瞬停止して再始動する際の負荷が重く感じられることがある。このため、再始動時の筆記感をより良好にする観点から、条件1−1において、Fre/Fは、0.60以上1.50以下であることが好ましく、0.65以上1.40以下であることがより好ましく、0.90以上1.35以下であることがさらに好ましい。 In addition, when Fre / Fk is too large, the load at the time of stopping and restarting writing may be felt heavy. For this reason, from the viewpoint of making the writing feeling at the time of restart better, in condition 1-1, F re / F k is preferably 0.60 or more and 1.50 or less, and 0.65 or more and 1. More preferably, it is 40 or less, and further preferably 0.90 or more and 1.35 or less.

本発明の筆記性部材の選別方法は、下記条件1−2を満たすものを選別することが好ましい。条件1−2を満たすことにより、条件1−1を満たすことにより得られる再始動時の筆記感をより良好にすることができる。
<条件1−2>
残留摩擦力の平均が1.0gf以上25.0gf以下。
In the method for selecting a writable member of the present invention, it is preferable to select one that satisfies the following condition 1-2. By satisfying the condition 1-2, the writing feeling upon restart obtained by satisfying the condition 1-1 can be further improved.
<Condition 1-2>
The average residual friction force is 1.0 gf or more and 25.0 gf or less.

残留摩擦力の平均(Fre)は、1.5gf以上23.0gf以下であることがより好ましく、2.0gf以上20.0gf以下であることがさらに好ましい。 The average residual friction force (F re ) is more preferably 1.5 gf or more and 23.0 gf or less, and further preferably 2.0 gf or more and 20.0 gf or less.

本発明の筆記性部材の選別方法は、下記条件1−3を満たすものを選別することが好ましい。条件1−3を満たすことにより、連続して筆記する際の筆記感を良好にしやすくできるとともに、ペン先の摩耗を抑制しやすくできる。
<条件1−3>
動摩擦力の平均が1.0gf以上32.0gf以下。
In the method for selecting a writable member of the present invention, it is preferable to select one that satisfies the following conditions 1-3. By satisfying the condition 1-3, it is possible to easily improve the writing feeling when writing continuously, and to suppress wear of the pen tip.
<Condition 1-3>
The average dynamic friction force is 1.0 gf or more and 32.0 gf or less.

動摩擦力の平均(F)は、2.0gf以上25.0gf以下であることがより好ましく、2.5gf以上15.0gf以下であることがさらに好ましい。 The average dynamic friction force (F k ) is more preferably 2.0 gf or more and 25.0 gf or less, and further preferably 2.5 gf or more and 15.0 gf or less.

本発明の筆記性部材の選別方法は、下記条件1−4を満たすものを選別することが好ましい。条件1−4を満たすことにより、連続して筆記する際の筆記感を良好にしやすくできるとともに、ペン先の摩耗を抑制しやすくできる。
<条件1−4>
動摩擦力の標準偏差が0.5gf以上18.0gf以下。
In the method for selecting a writable member of the present invention, it is preferable to select one that satisfies the following conditions 1-4. By satisfying Condition 1-4, it is possible to easily improve the writing feeling when writing continuously, and to suppress wear of the pen tip.
<Condition 1-4>
The standard deviation of dynamic friction force is 0.5gf or more and 18.0gf or less.

動摩擦力の標準偏差(以下、「σF」と称する場合がある。)は、0.001秒ごとに測定した動摩擦力から算出したものである。σFは、0.7gf以上10.0gf以下とすることがより好ましく、1.0gf以上5.0gf以下とすることがさらに好ましい。 The standard deviation of dynamic friction force (hereinafter sometimes referred to as “σF k ”) is calculated from the dynamic friction force measured every 0.001 seconds. σF k is more preferably 0.7 gf or more and 10.0 gf or less, and further preferably 1.0 gf or more and 5.0 gf or less.

本発明において、F及びFreは、15個のサンプルを各1回ずつ測定した際の平均値とする。また、本発明において、Fre/Fは、15個のサンプルを各1回ずつ測定して各サンプルのFre/Fを算出し、20サンプルのFre/Fを平均した値とする。また、本発明において、σFは、60個のサンプルのFを各1回ずつ測定した際の標準偏差とする。 In the present invention, F k and F re are average values when 15 samples are measured once. Further, in the present invention, F re / F k is the 15 samples was calculated F re / F k of each sample was measured one time each, a value obtained by averaging the F re / F k of 20 samples To do. In the present invention, σF k is a standard deviation when F k of 60 samples are measured once.

図3は、動摩擦力及び残留摩擦力の測定方法を説明する概略図である。
図3では、タッチパネルペン200は筆記性部材10に接触した状態で保持具84によって固定されている。また、保持具84の上部には重り83を乗せるための土台85が付属されている。土台85上には重り83が乗せられており、該重りによってタッチパネルペンに垂直荷重がかけられている。筆記性部材10は可動台82上に固定されている。
摩擦力の測定時には、タッチパネルペンが上記のように固定された状態で、筆記性部材10が固定された可動台82を、筆記性部材とタッチパネルペンとの成す角の鋭角方向側(図3の右側)に所定の速度で移動する。この際、タッチパネルペン200には、可動台82の移動方向に動摩擦力が生じ、各時間の動摩擦力を算出できる。また、筆記性部材10の移動を完了した後の摩擦力である残留摩擦力を測定できる。
図3に示す測定が可能な装置としては、新東科学社製の商品名HEIDON−18L、HEIDON−14DRが挙げられる。
FIG. 3 is a schematic diagram illustrating a method for measuring dynamic friction force and residual friction force.
In FIG. 3, the touch panel pen 200 is fixed by the holder 84 in a state where the touch panel pen 200 is in contact with the writable member 10. A base 85 for placing a weight 83 is attached to the upper portion of the holder 84. A weight 83 is placed on the base 85, and a vertical load is applied to the touch panel pen by the weight. The writable member 10 is fixed on the movable table 82.
When measuring the frictional force, with the touch panel pen fixed as described above, the movable table 82 to which the writable member 10 is fixed is placed on the acute angle direction side (in FIG. 3) between the writable member and the touch panel pen. Move to the right) at a predetermined speed. At this time, a dynamic friction force is generated in the touch panel pen 200 in the moving direction of the movable table 82, and the dynamic friction force for each time can be calculated. Moreover, the residual friction force which is a friction force after completing the movement of the writable member 10 can be measured.
Examples of the apparatus capable of measurement shown in FIG. 3 include trade names HEIDON-18L and HEIDON-14DR manufactured by Shinto Kagaku Co., Ltd.

なお、本発明において、F、Fre等の摩擦力に関するパラメータは、下記(A)〜(E)のように測定することが好ましい。
(A)0点補正
タッチパネルペン用筆記性部材の表面に対してタッチパネルペンを60度の角度で接触させた状態で固定し、タッチパネルペンに垂直荷重100gfをかける。この状態のまま(筆記性部材は動かさない)、100m秒静置し、タッチパネルペンの鋭角方向に生じた摩擦力を0.001秒間隔で測定する。計測時間1m秒〜100m秒の間の摩擦力の最大値を、摩擦力の全計測値(1m秒の摩擦力〜残留摩擦力の測定終了の摩擦力までの全ての摩擦力の測定値)から引いた値を各時間の摩擦力として、0点補正する。後述の(C)〜(E)は0点補正した摩擦力に基づいて算出している。
(B)実測時間
0点補正する前の計測時間1m秒〜100m秒の摩擦力の標準偏差の3倍を「閾値」とする。上記(A)の100m秒静置の後、さらに500m秒静置した後に、筆記性部材を固定した可動台を14mm/秒の速度で、筆記性部材とタッチパネルペンとの成す角の鋭角方向側に移動させ、タッチパネルペンの鋭角方向の摩擦力を0.001秒間隔で測定する。筆記性部材の移動開始後に閾値を最初に超えた時間を「実測開始」の時間とする。
(C)最大摩擦力Fmax
実測開始から1500m秒以内の最大摩擦力から最大摩擦力Fmaxを算出する。
(D)動摩擦力
最大摩擦力Fmaxが発生した時間を第1ピーク時間とする。
実測を開始した時間から、筆記性部材の40mmの長さの移動が完了する時間までの摩擦力の平均を暫定平均摩擦力とする。第1ピーク時間から30m秒経過後に、[暫定平均摩擦力+(最大摩擦力×0.1)]を超える摩擦力が最初に発生した時間を第2ピーク時間とする。
第2ピーク時間から500m秒経過した時間を動摩擦力の測定開始時間、筆記性部材の40mmの長さの移動が完了する時間を動摩擦力の測定終了時間として、各時間の動摩擦力を測定し、動摩擦力の平均(F)、動摩擦力の標準偏差(σF)を算出できる。
(E)残留摩擦力
筆記性部材の片道40mmの長さの移動が完了した後に、タッチパネルペンにかかる垂直荷重100gfを保持し、タッチパネルペン用筆記性部材の表面に対してタッチパネルペンを60度の角度で接触させたままの状態とする。この状態において、タッチパネルペンにかかる鋭角方向の摩擦力(残留摩擦力)を測定する。残留摩擦力の測定時間は、筆記性部材の片道40mmの長さの移動が完了してから500m秒経過後を測定開始時間として、そこから400m秒後を測定終了時間とする。各時間の残留摩擦力から、残留摩擦力の平均(Fre)を算出する。
In the present invention, it is preferable to measure parameters relating to frictional forces such as F k and F re as shown in the following (A) to (E).
(A) 0 point correction The touch panel pen is fixed in a state where it is in contact with the surface of the writable member for the touch panel pen at an angle of 60 degrees, and a vertical load of 100 gf is applied to the touch panel pen. In this state (the writable member does not move), it is left to stand for 100 milliseconds, and the frictional force generated in the acute angle direction of the touch panel pen is measured at intervals of 0.001 seconds. The maximum value of the friction force between the measurement time of 1 msec to 100 msec is calculated from all the measurement values of the friction force (measurement values of all friction forces from the friction force of 1 msec to the friction force at the end of the measurement of the residual friction force). The subtracted value is used as the frictional force for each time, and zero correction is performed. The following (C) to (E) are calculated based on the frictional force corrected by 0 points.
(B) Actual measurement time Three times the standard deviation of the frictional force of the measurement time 1 ms to 100 ms before the zero point correction is set as the “threshold value”. After standing for 100 msec in the above (A) and then for 500 msec, the movable table with the writable member fixed at the speed of 14 mm / sec, the acute angle direction side of the angle formed by the writable member and the touch panel pen And the frictional force in the acute angle direction of the touch panel pen is measured at 0.001 second intervals. The time when the threshold value is first exceeded after the start of the movement of the writable member is set as the “measurement start” time.
(C) Maximum friction force F max
The maximum friction force F max is calculated from the maximum friction force within 1500 milliseconds from the start of measurement.
(D) Dynamic friction force The time when the maximum friction force Fmax occurs is defined as the first peak time.
The average of the frictional force from the time when the actual measurement is started to the time when the movement of the 40 mm length of the writable member is completed is defined as the provisional average frictional force. The time when the first frictional force exceeding [provisional average frictional force + (maximum frictional force × 0.1)] after 30 milliseconds has elapsed from the first peak time is defined as the second peak time.
Measure the dynamic friction force at each time, with the time when 500 msec elapsed from the second peak time as the measurement start time of the dynamic friction force, the time when the movement of the 40 mm length of the writable member is completed as the measurement end time of the dynamic friction force, The average (F k ) of the dynamic friction force and the standard deviation (σF k ) of the dynamic friction force can be calculated.
(E) Residual friction force After completing the movement of the 40 mm length of the writable member, the vertical load 100 gf applied to the touch panel pen is held, and the touch panel pen is held at 60 degrees with respect to the surface of the writable member for the touch panel pen. Keep in contact at an angle. In this state, the frictional force (residual frictional force) in the acute angle direction applied to the touch panel pen is measured. The measurement time of the residual friction force is defined as the measurement start time after 500 msec from the completion of the movement of the 40 mm length of the writable member, and the measurement end time after 400 msec. From the residual friction force at each time, an average (F re ) of the residual friction force is calculated.

なお、筆記性部材の表面及びタッチパネルペンのペン先に油脂(例えば、人間の指から筆記性部材の表面に転写した指紋成分)が付着していると、摩擦力に影響を与える可能性がある。このため、摩擦力の測定は、筆記性部材の表面及びタッチパネルペンのペン先に油脂が付着しないようにして実施することが好ましい。また、筆記性部材の表面及びタッチパネルペンのペン先に油脂が付着した場合には、筆記性部材の表面及びタッチパネルペンのペン先の形状、物性に影響を与えない範囲で脱脂処理を行った後に摩擦力を測定することが好ましい。   In addition, if oils and fats (for example, a fingerprint component transferred from the human finger to the surface of the writable member) adhere to the surface of the writable member and the pen tip of the touch panel pen, there is a possibility of affecting the frictional force. . For this reason, it is preferable to carry out the measurement of the frictional force so that oils and fats do not adhere to the surface of the writable member and the pen tip of the touch panel pen. In addition, when oils and fats adhere to the surface of the writable member and the pen tip of the touch panel pen, after degreasing the surface of the writable member and the shape and physical properties of the pen tip of the touch panel pen It is preferable to measure the frictional force.

条件1−1及びその他の条件の判定に用いるタッチパネルペンは特に限定されず、市販のタッチパネルペンの中から適宜選択できる。
なお、タッチパネルペンのペン先の材料が筆記性部材の表面凹凸に嵌まり込まない場合、条件1−1を満たす筆記性部材が設計しにくくなる。このため、条件1−1等の判定に用いるタッチパネルペンは、ペン先が一定の柔軟性を有することが好ましい。しかし、ペン先に柔軟性を有する材料のみから形成した場合、フィルムの凸形状部の食い込み部分でペン先が摩耗するため寿命が短くなったり、ペン先が筆記性部材の表面凹凸から離れにくくなる場合がある。したがって、条件1−1等の判定に用いるタッチパネルペンは、ペンの先端領域が、少なくとも2つの領域を有することが好ましい。具体的には、ペンの先端領域が、少なくとも、変形を促進する領域(i)と、硬さを付与する領域(ii)とを有することが好ましい。また、変形を促進する領域(i)と、硬さを付与する領域(ii)とは、規則的又はランダムに混在していることが好ましい。領域(i)と、領域(ii)とが混在した構成としては、例えば、多孔質の構成(空気孔が変形を促進する領域(i)となる)、硬い素材の中に柔らかい素材が混在している構成等が挙げられる。
変形を促進する領域(i)としては、例えば、空気孔、空洞部、柔らかい素材等が挙げられる。柔らかい素材のヤング率は1.0GPa以下であることが好ましく、0.6GPa以下であることがより好ましい。
硬さを付与する領域(ii)としては、ヤング率1.2GPa以上の素材が挙げられる。硬さを付与する領域(ii)の素材のヤング率は2.0GPa以上であることが好ましく、2.5GPa以上であることがより好ましい。なお、筆記性部材の摩耗を抑制する観点からは、硬さを付与する領域(ii)の素材のヤング率は5.0GPa以下であることが好ましく、4.0GPa以下であることがより好ましく、3.5GPa以下であることがさらに好ましい。
領域(i)と領域(ii)との体積比は、98:2〜70:30であることが好ましく、95:5〜75:25であることがより好ましく、90:10〜80:20であることがさらに好ましい。
ヤング率Eの測定時の雰囲気は、温度は23℃±5℃、湿度40〜65%とする。また、ヤング率Eの測定開始前に、測定サンプルを23℃±5℃、湿度40〜65%の雰囲気に10分以上放置するものとする。
先端領域とは、タッチパネルペンのペン先から1.5mm以内の範囲をいうものとする。
The touch panel pen used for determination of Condition 1-1 and other conditions is not particularly limited, and can be appropriately selected from commercially available touch panel pens.
In addition, when the material of the nib of a touch-panel pen does not fit in the surface unevenness | corrugation of a writable member, it becomes difficult to design the writable member which satisfy | fills conditions 1-1. For this reason, as for the touch-panel pen used for determination of conditions 1-1 etc., it is preferable that a pen point has a certain softness | flexibility. However, if the nib is made of only a flexible material, the nib wears out at the biting portion of the convex part of the film, so the life is shortened or the nib is difficult to separate from the surface irregularities of the writable member. There is a case. Therefore, in the touch panel pen used for determination of the condition 1-1 or the like, it is preferable that the tip end region of the pen has at least two regions. Specifically, it is preferable that the tip region of the pen has at least a region (i) that promotes deformation and a region (ii) that imparts hardness. Further, it is preferable that the region (i) for promoting deformation and the region (ii) for imparting hardness are mixed regularly or randomly. Examples of the configuration in which the region (i) and the region (ii) are mixed include, for example, a porous configuration (the air hole becomes the region (i) that promotes deformation), and a soft material mixed in a hard material. The structure etc. which are are mentioned.
Examples of the region (i) that promotes deformation include air holes, cavities, and soft materials. The Young's modulus of the soft material is preferably 1.0 GPa or less, and more preferably 0.6 GPa or less.
Examples of the region (ii) to which hardness is imparted include materials having a Young's modulus of 1.2 GPa or more. The Young's modulus of the material in the region (ii) to which hardness is imparted is preferably 2.0 GPa or more, and more preferably 2.5 GPa or more. In addition, from the viewpoint of suppressing the wear of the writable member, the Young's modulus of the material for imparting hardness (ii) is preferably 5.0 GPa or less, more preferably 4.0 GPa or less, More preferably, it is 3.5 GPa or less.
The volume ratio of region (i) to region (ii) is preferably 98: 2 to 70:30, more preferably 95: 5 to 75:25, and 90:10 to 80:20. More preferably it is.
The atmosphere at the time of measuring the Young's modulus E is a temperature of 23 ° C. ± 5 ° C. and a humidity of 40 to 65%. Before starting the measurement of Young's modulus E, the measurement sample is left in an atmosphere of 23 ° C. ± 5 ° C. and humidity of 40 to 65% for 10 minutes or more.
The tip region refers to a range within 1.5 mm from the pen tip of the touch panel pen.

また、条件1−1等の判定に用いるタッチパネルペンは、ペン先の直径が0.3〜2.5mmであることが好ましく、0.5〜2.0mmであることがより好ましく、0.7〜1.7mmであることがさらに好ましい。
ペン先の直径Dは、ペン軸に対して垂直方向側からタッチパネルペンを撮像した写真を基準として算出する。図4は、ペン軸に対して垂直方向側からタッチパネルペンを撮像した際のタッチパネルペンの外形を点線で表示したものである。図4(a)に示すように、該写真に対して、該写真の頂点を通り、かつ該写真からはみ出ない円を重ね合わせた際に、最大となる円の直径をペン先の直径Dとする。ただし、図4(b)に示すように、該写真が斜面を有し、かつ該斜面のペン軸に対する角度が40〜90度であれば、該斜面をはみ出して該円を重ね合わせてもよい。
Moreover, as for the touchscreen pen used for determination of conditions 1-1 etc., it is preferable that the diameter of a pen point is 0.3-2.5 mm, It is more preferable that it is 0.5-2.0 mm, 0.7 More preferably, it is -1.7 mm.
The diameter D of the pen tip is calculated based on a photograph of the touch panel pen taken from the direction perpendicular to the pen axis. FIG. 4 shows the outline of the touch panel pen displayed as a dotted line when the touch panel pen is imaged from the side perpendicular to the pen axis. As shown in FIG. 4 (a), when a circle that passes through the top of the photograph and does not protrude from the photograph is superimposed on the photograph, the diameter of the largest circle is the diameter D of the pen tip. To do. However, as shown in FIG. 4B, if the photograph has an inclined surface and the angle of the inclined surface with respect to the pen axis is 40 to 90 degrees, the circle may be overlapped by protruding the inclined surface. .

また、本発明の筆記性部材の選別方法は、下記条件2−1を満たすものをタッチパネルペン用筆記性部材として選別することが好ましい。
<条件2−1>
ヘイズが25.0%以上
Moreover, as for the selection method of the writable member of this invention, it is preferable to select as a writable member for touch panel pens that satisfy the following conditions 2-1.
<Condition 2-1>
Haze is 25.0% or more

ヘイズを25.0%以上とすることにより、ギラツキ(映像光に微細な輝度のばらつきが見える現象)を抑制しやすくできる。
ギラツキ抑制の観点から、ヘイズは35.0%以上であることがより好ましく、45.0%以上であることがさらに好ましい。また、表示素子の解像性の低下の抑制の観点から、ヘイズは90.0%以下であることが好ましく、70.0%以下であることがより好ましく、67.0%以下であることがさらに好ましく、60.0%以下であることがよりさらに好ましい。
ヘイズ及び後述の全光線透過率を測定する際は、筆記性部材の筆記面(上記条件1−1を満たす面)とは反対側の表面から光を入射するものとする。筆記性部材の両面が筆記面の場合、光入射面はどちらの面であってもよい。なお、本明細書において、ヘイズ及び全光線透過率は、15個のサンプルを各1回ずつ測定した際の平均値とする。
By setting the haze to 25.0% or more, it is possible to easily suppress glare (a phenomenon in which minute variations in luminance are seen in video light).
From the viewpoint of suppressing glare, the haze is more preferably 35.0% or more, and further preferably 45.0% or more. Further, from the viewpoint of suppressing a decrease in resolution of the display element, the haze is preferably 90.0% or less, more preferably 70.0% or less, and 67.0% or less. More preferably, it is more preferably 60.0% or less.
When measuring the haze and the total light transmittance described later, light is incident from the surface opposite to the writing surface of the writable member (the surface satisfying the above condition 1-1). When both surfaces of the writable member are writing surfaces, the light incident surface may be either surface. In this specification, the haze and the total light transmittance are average values when 15 samples are measured once each.

また、本発明の筆記性部材の選別方法は、下記条件2−2を満たすものをタッチパネルペン用筆記性部材として選別することが好ましい。
<条件2−2>
JIS K7361−1:1997の全光線透過率が87.0%以上
Moreover, it is preferable that the selection method of the writable member of this invention selects what satisfies the following conditions 2-2 as a writable member for touch panel pens.
<Condition 2-2>