JP2017139118A - 非水電解液二次電池の製造方法 - Google Patents
非水電解液二次電池の製造方法 Download PDFInfo
- Publication number
- JP2017139118A JP2017139118A JP2016018809A JP2016018809A JP2017139118A JP 2017139118 A JP2017139118 A JP 2017139118A JP 2016018809 A JP2016018809 A JP 2016018809A JP 2016018809 A JP2016018809 A JP 2016018809A JP 2017139118 A JP2017139118 A JP 2017139118A
- Authority
- JP
- Japan
- Prior art keywords
- positive electrode
- mass
- battery
- phosphate
- secondary battery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】非水電解液二次電池の製造方法は、正極製造ステップ(S01)と、電極群構成ステップ(S03)と、電解液調製ステップ(S04)と、ケース収容ステップ(S05)とを備える。正極製造ステップ(S01)では、リン酸トリフェニルおよびリン酸ジフェニルの少なくとも一方を合計で8質量%以上12質量%以下含有する正極合材層を含む、正極を製造する。電極群構成ステップ(S03)では、正極および負極を含む電極群を構成する。電解液調製ステップ(S04)では、シクロトリホスファゼンを5質量%以上8質量%以下含有する電解液を調製する。ケース収容ステップ(S05)では、電極群および電解液を電池ケースに収容することにより、非水電解液二次電池を製造する。
【選択図】図1
Description
正極製造ステップでは、リン酸トリフェニルおよびリン酸ジフェニルの少なくとも一方を合計で8質量%以上12質量%以下含有する正極合材層を含む、正極を製造する。
電極群構成ステップでは、正極および負極を含む電極群を構成する。
電解液調製ステップでは、シクロトリホスファゼンを5質量%以上8質量%以下含有する電解液を調製する。
ケース収容ステップでは、電極群および電解液を電池ケースに収容することにより、非水電解液二次電池を製造する。
図1は、本実施形態の製造方法の概略を示すフローチャートである。本実施形態の製造方法は、正極製造ステップ(S01)と、負極製造ステップ(S02)と、電極群構成ステップ(S03)と、電解液調製ステップ(S04)と、ケース収容ステップ(S05)とを備える。以下、各ステップを説明する。
正極製造ステップ(S01)では、リン酸トリフェニルおよびリン酸ジフェニルの少なくとも一方を合計で8質量%以上12質量%以下含有する正極を製造する。
O=P(OC6H5)3 ・・・(I)
によって表すことができる。
O=P(OH)(OC6H5)2 ・・・(II)
によって表すことができる。
導電材 :4〔質量%〕
バインダ :3〔質量%〕
リン酸エステル化合物:X〔質量%〕(ただし、8≦X≦12である)。
負極製造ステップ(S02)では、負極を製造する。負極は従来公知の方法で製造することができる。たとえば、負極活物質およびバインダを含有する負極スラリーを調製し、該負極スラリーを負極集電体の表面に塗工し、乾燥させることにより、負極を製造することができる。本実施形態の負極は、たとえば帯状のシート部材である。
電極群構成ステップでは、正極および負極を含む電極群を構成する。
電解液調製ステップ(S04)では、シクロトリホスファゼンを5質量%以上8質量%以下含有する電解液を調製する。
ケース収容ステップ(S05)では、電極群および電解液を電池ケースに収容する。
図2は、本実施形態に係る非水電解液二次電池の構成の一例を示す概略図である。以下のようにして、図2に示される電池100(18650サイズの円筒形非水電解液二次電池)を製造した。電池100の定格容量は、500mAhである。
1.正極製造ステップ(S01)
以下の材料を準備した。
正極活物質:LiNi1/3Co1/3Mn1/3O2
導電材 :アセチレンブラック
バインダ :PVdF
リン酸エステル化合物:リン酸トリフェニル
溶媒 :NMP
正極集電体:Al箔(厚さ=15μm)。
以下の材料を準備した。
負極活物質:天然黒鉛(D50=10μm)
バインダ :CMCおよびSBR
溶媒 :水
負極集電体:Cu箔(厚さ=10μm)。
巻取装置を用いて、セパレータ30を挟んで、正極10と負極20とを積層し、さらに巻回することにより、円柱状の電極群80を構成した。
非プロトン性有機溶媒に、支持電解質塩およびホスファゼン化合物を分散させることにより、電解液を調製した。電解液組成は次のとおりである。
非プロトン性有機溶媒:[EC:EMC:DMC=3:4:3(体積混合比)]
支持電解質塩 :LiPF6(1mоl/l)
ホスファゼン化合物 :シクロトリホスファゼン(5質量%)。
円筒形の電池ケース50(直径=18mm、高さ=65mm)を準備した。電池ケース50に、電極群80を収容し、電極群80を電池ケース50内の所定の位置に溶接した。さらに所定量の電解液を電池ケース50に入れ、電池ケース50を密閉した。以上より、非水電解液二次電池を製造した。
下記表1に示すように、リン酸トリフェニルを増量することを除いては、実施例1と同様にして、実施例2および3に係る電池を製造した。今回の実験では、導電材およびバインダの質量混合比、ならびに正極活物質およびリン酸エステル化合物の質量混合比の合計を一定とした。すなわち正極において、各成分の質量混合比は「正極活物質:導電材:バインダ:リン酸エステル化合物=(93−X):4:3:X」である(表1に示すように、ここでは0≦X≦15である;以下同様である)。
リン酸トリフェニルに代えて、リン酸ジフェニルを用いることを除いては、実施例1〜3と同様にして、実施例4〜6に係る電池を製造した。
下記表1に示すように、正極におけるリン酸トリフェニルまたはリン酸ジフェニルの含有量、および電解液におけるシクロトリホスファゼンの含有量を変更することを除いては、実施例1〜6と同様にして、実施例7〜12ならびに比較例1〜8に係る電池を製造した。
以下のようにして、上記で製造された各電池の性能を評価した。以下の説明において、電流レートの単位「C」は、電池の定格容量を1時間で放電しきる電流レートを示すものとする。
3.0〜4.1Vの電圧範囲で定電流充放電を行い、初期容量(放電容量)を測定した。結果を上記表1に示す。
60℃に設定された恒温槽内に電池を配置した。3.0〜4.1Vの電圧範囲において、2Cの電流レートで充放電を500サイクル繰り返した。500サイクル後の放電容量を、初期容量で除することにより、容量維持率(百分率)を求めた。結果を上記表1に示す。
25℃に設定された恒温槽内に電池を配置した。電池のSOC(State Of Charge)を60%に調整した。次いで下記のパルス充電およびパルス放電の組み合わせを1サイクルとして、パルス充放電サイクルを3000サイクル繰り返した。
パルス充電:電流=10C、充電時間=80秒、上限電圧=4.3V
パルス放電:電流=2C、放電時間=400秒、下限電圧=2.5V。
Thermal Hazard Technology社製のARC(Accelerating Rate Calorimeter)を用いて、電池の熱安定性を評価した。「ARC」とは、試料を断熱状態で段階的に加熱することにより、試料を自己発熱させ、自己発熱速度を測定する装置である。
Temperature Range:80〜350℃
Temperature Step:5℃
Wait Time:20min
Temp. Rate Sensitivity:0.02℃/min
Calculation Step temp.:0.2℃。
上記表1に示されるように、正極におけるリン酸トリフェニルまたはリン酸ジフェニルの含有量が8質量%以上12質量%以下であり、かつ電解液におけるシクロトリホスファゼンの含有量が5質量%以上8質量%以下である、実施例では、かかる条件を満たさない比較例に比し、熱安定性が高く、なおかつハイレートパルスサイクルに伴う抵抗増加率が低い電池を製造することができた。
Claims (1)
- リン酸トリフェニルおよびリン酸ジフェニルの少なくとも一方を合計で8質量%以上12質量%以下含有する正極合材層を含む、正極を製造するステップと、
前記正極および負極を含む電極群を構成するステップと、
シクロトリホスファゼンを5質量%以上8質量%以下含有する電解液を調製するステップと、
前記電極群および前記電解液を電池ケースに収容することにより、非水電解液二次電池を製造するステップと、を備える、非水電解液二次電池の製造方法。