JP2017105493A - Resin film for packaging and packaging body - Google Patents
Resin film for packaging and packaging body Download PDFInfo
- Publication number
- JP2017105493A JP2017105493A JP2015239996A JP2015239996A JP2017105493A JP 2017105493 A JP2017105493 A JP 2017105493A JP 2015239996 A JP2015239996 A JP 2015239996A JP 2015239996 A JP2015239996 A JP 2015239996A JP 2017105493 A JP2017105493 A JP 2017105493A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- packaging
- resin film
- sealant layer
- surface layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、被包装物を包装するための包装用樹脂フィルム及び該包装用樹脂フィルムを用いて被包装物を包装した包装体に関するものであり、特に食品を包装するための包装用樹脂フィルム及び包装体に関するものである。 TECHNICAL FIELD The present invention relates to a packaging resin film for packaging an article to be packaged and a packaging body in which the article to be packaged is packaged using the packaging resin film, and in particular, a packaging resin film for packaging food and It relates to a package.
食品等を包装するための包装用樹脂フィルムには、商品名などの他、消費期限、賞味期限、製造所固有番号、内容量、ロット番号等、法令上または管理上必要な情報が印刷される。これら情報は、概して食品を包装用樹脂フィルムにより包装する直前に、包装用樹脂フィルムの表面に印刷される。しかしながら、包装用樹脂フィルムにより食品を包装した包装体が搬送される際、包装体表面が外部から摩擦を受けることにより、印刷された情報が消失する場合がある。また、包装用樹脂フィルムにより食品を包装した包装体が調理場に置かれた際、油脂類が印刷のインク成分を溶解することにより、印刷された情報が消失する場合がある。 In addition to product names, information required by law and management is printed on packaging resin films for packaging food, etc. . Such information is generally printed on the surface of the packaging resin film immediately before the food is packaged with the packaging resin film. However, when a packaging body in which food is packaged by the packaging resin film is conveyed, the printed information may be lost due to friction on the surface of the packaging body from the outside. Moreover, when the package body which packaged the food with the resin film for packaging is put in the cooking place, the printed information may be lost due to the fats and oils dissolving the printing ink components.
ここで、特許文献１には、外部からの摩擦等による印字の消失を防止するために、基材層、絵柄印刷層、印刷下地層及びシーラント層を順次貼り合わせた包装用積層小袋材について提案されている。印刷下地層はレーザ光による印字可能な白色インキからなる層であり、この印刷下地層にレーザ光を照射することにより包装用積層小袋材に文字等が印刷される。 Here, Patent Document 1 proposes a laminated pouch material for packaging in which a base material layer, a pattern printing layer, a printing base layer, and a sealant layer are sequentially bonded in order to prevent loss of printing due to external friction or the like. Has been. The printing base layer is a layer made of white ink that can be printed with laser light. By irradiating the printing base layer with laser light, characters and the like are printed on the laminated pouch material for packaging.
また、特許文献２には、表層とシール層との間に、酸化チタンを着色剤として用いた白色インキ層を設け、白色インキ層にレーザ光を照射して黒変させることにより印字する包装フィルムへのレーザマーキング方法について記載されている。 Patent Document 2 discloses a packaging film in which a white ink layer using titanium oxide as a colorant is provided between a surface layer and a seal layer, and printing is performed by irradiating the white ink layer with a laser beam to turn black. The laser marking method is described.
特許文献１及び２記載の包装用樹脂フィルムにおいては、外部からの摩擦等による印字の消失を防止することができるが、表層とシーラント層との間に印刷層を設ける必要があるため、包装用樹脂フィルムの薄化が求められているにもかかわらず、包装用樹脂フィルムの厚さは増大する。 In the packaging resin films described in Patent Documents 1 and 2, it is possible to prevent the disappearance of printing due to external friction or the like, but it is necessary to provide a printing layer between the surface layer and the sealant layer. Despite the demand for thin resin films, the thickness of packaging resin films increases.
また、包装用樹脂フィルムにおいては、被包装物を遮視する不透明性も求められているが、包装用樹脂フィルムを薄くすると、被包装物が透けるという問題があった。 In addition, the packaging resin film is also required to have opaqueness that shields the object to be packaged. However, if the packaging resin film is thin, there is a problem that the object to be packaged is transparent.
本発明の目的は、表層とシーラント層との間に印刷層を設けなくとも、外部からの摩擦等により消失しない文字等をレーザマーキングすることができ、且つ被包装物を遮視することができる包装用樹脂フィルム及び該包装用樹脂フィルムを用いて被包装物を包装した包装体を提供することである。 The object of the present invention is to allow laser marking of characters that do not disappear due to external friction or the like without providing a printing layer between the surface layer and the sealant layer, and to shield the object to be packaged. It is providing the packaging body which packaged the to-be packaged object using the resin film for packaging and this resin film for packaging.
本発明の包装樹脂フィルムは、少なくとも表層及びシーラント層を有し、被包装物を包装するための包装用樹脂フィルムであって、前記表層は、前記シーラント層を視認可能な視認部を有し、前記シーラント層は、ＴｉＯ2を含有し、前記被包装物を遮視する着色がなされていることを特徴とする。 The packaging resin film of the present invention has at least a surface layer and a sealant layer, and is a packaging resin film for packaging an object to be packaged, wherein the surface layer has a visual recognition part capable of visually recognizing the sealant layer, The sealant layer contains TiO 2 and is colored to obscure the package.
また、本発明の包装用樹脂フィルムは、前記表層を介してレーザ光を照射し前記ＴｉＯ2を発色させることにより任意の文字、図形及び記号の少なくとも１つが表示される表示部を有し、前記表示部は、前記視認部を介して視認可能であることを特徴とする。 Further, the packaging resin film of the present invention has a display unit on which at least one of arbitrary characters, figures and symbols is displayed by irradiating a laser beam through the surface layer to develop the TiO 2 color, The display unit is visible through the viewing unit.
また、本発明の包装用樹脂フィルムは、前記着色が白色であることを特徴とする。 The packaging resin film of the present invention is characterized in that the coloring is white.
また、本発明の包装用樹脂フィルムは、シーラント層が直鎖状低密度ポリエチレン（ＬＬＤＰＥ）層または無延伸ポリプロピレン（ＣＰＰ）層であることを特徴とする。 The packaging resin film of the present invention is characterized in that the sealant layer is a linear low density polyethylene (LLDPE) layer or an unstretched polypropylene (CPP) layer.
また、本発明の包装用樹脂フィルムは、前記表層がポリエチレンテレフタレート（ＰＥＴ）層、ナイロン層、ポリエチレン（ＰＥ）層及びポリプロピレン（ＰＰ）層のなかの１つからなる単層、または２つ以上からなる積層であることを特徴とする。 In the packaging resin film of the present invention, the surface layer is a single layer composed of one of a polyethylene terephthalate (PET) layer, a nylon layer, a polyethylene (PE) layer, and a polypropylene (PP) layer, or two or more layers. It is the lamination | stacking which becomes.
また、本発明の包装用樹脂フィルムは、前記被包装物が食品であることを特徴とする。 The packaging resin film of the present invention is characterized in that the package is a food.
また、本発明の包装用樹脂フィルムは、前記食品が穀粉、穀粉調製品、冷凍食品または乾麺であることを特徴とする。 The packaging resin film of the present invention is characterized in that the food is flour, flour preparation, frozen food or dry noodles.
また、本発明の包装用樹脂フィルムは、前記表示部が前記食品の商品名、消費期限、賞味期限、製造所固有番号、内容量、ロット番号及びその他法令上または管理上必要な情報の少なくとも１つを表示することを特徴とする。 Further, in the packaging resin film of the present invention, the display unit has at least one of the product name of the food, the expiration date, the expiration date, the unique number of the factory, the content volume, the lot number, and other information required by law or management. It is characterized by displaying one.
また、本発明の包装体は、本発明の包装用樹脂フィルムを用いて前記被包装物を包装することを特徴とする。 Moreover, the package of this invention packages the said to-be packaged object using the resin film for packaging of this invention, It is characterized by the above-mentioned.
本発明によれば、表層とシーラント層との間に印刷層を設けなくとも、外部からの摩擦等により消失しない文字等をレーザマーキングすることができ、且つ被包装物を遮視することができる包装用樹脂フィルム及び該包装用樹脂フィルムを用いた包装体を提供することができる。 According to the present invention, even if a printing layer is not provided between the surface layer and the sealant layer, it is possible to laser-mark characters and the like that do not disappear due to external friction or the like, and it is possible to shield the packaged item. A packaging resin film and a packaging body using the packaging resin film can be provided.
以下、図面を参照して本発明の実施の形態に係る包装体について説明する。図１は、実施の形態に係る包装体の概略構成を示す図である。この実施の形態に係る包装体２は、包装用樹脂フィルム４を用いて被包装物を包装する横ピロー包装体であって、図１に示すように、包装用樹脂フィルム４により被包装物を包装する際、まず包装用樹脂フィルム４の幅方向の両端部４ａをシールし、次に筒状になった包装用樹脂フィルム４の両側４ｂをシールすることにより作製される横ピロー包装体である。 Hereinafter, a package according to an embodiment of the present invention will be described with reference to the drawings. Drawing 1 is a figure showing the schematic structure of the package concerning an embodiment. The packaging body 2 according to this embodiment is a horizontal pillow packaging body that wraps an object to be packaged using the packaging resin film 4, and the packaging object film 4 is wrapped with the packaging resin film 4 as shown in FIG. When packaging, it is a horizontal pillow package produced by first sealing both end portions 4a in the width direction of the packaging resin film 4 and then sealing both sides 4b of the packaging resin film 4 in a cylindrical shape. .
なお、この実施の形態においては、包装体２として横ピロー包装体を例に挙げて説明するが、横ピロー包装体以外の包装体、例えば四方シールの包装体、三方シールの包装体、スタンディングパウチ、またはスパウトパウチ等にも本発明を適用することができる。また、被包装物としては、例えば小麦粉などの穀粉や、ホットケーキミックスやお好み焼きミックス等の穀粉調製品、冷凍食品、若しくはパスタ、素麺、冷麦、うどん、そば等の乾麺類が挙げられる。 In this embodiment, a horizontal pillow package will be described as an example of the package 2, but a package other than the horizontal pillow package, such as a four-side seal package, a three-side seal package, and a standing pouch. The present invention can also be applied to spout pouches and the like. Examples of the package include flour such as wheat flour, flour preparations such as hot cake mix and okonomiyaki mix, frozen foods, and dry noodles such as pasta, raw noodles, cold wheat, udon and soba.
図２及び図３は、被包装物を包装するための包装用樹脂フィルム４の構成を説明するための図である。包装用樹脂フィルム４は、図２及び図３に示すように、表層６及びシーラント層８を有し、包装体２の表面側（外側）となる表層６と包装体２の裏面側（内側）となるシーラント層８とを貼り合わせて構成されている。表層６は、例えばポリエチレンテレフタレート（ＰＥＴ）層、ナイロン層、ポリエチレン（ＰＥ）層及びポリプロピレン（ＰＰ）層のなかの１つからなる単層であり、被包装物の性質、耐熱性、印刷適性、耐油性、ガスバリア性などに応じて適切に選択される。なお、表層６は単層であるが、例えばポリエチレンテレフタレート（ＰＥＴ）層、ナイロン層、ポリエチレン（ＰＥ）層及びポリプロピレン（ＰＰ）層のなかの２つ以上からなる積層を表層として用いてもよい。 FIG.2 and FIG.3 is a figure for demonstrating the structure of the resin film 4 for packaging for packaging a to-be-packaged item. The packaging resin film 4 has a surface layer 6 and a sealant layer 8 as shown in FIGS. 2 and 3, and the surface layer 6 that becomes the front surface side (outside) of the packaging body 2 and the back surface side (inside) of the packaging body 2. And a sealant layer 8 to be formed. The surface layer 6 is a single layer composed of, for example, one of a polyethylene terephthalate (PET) layer, a nylon layer, a polyethylene (PE) layer, and a polypropylene (PP) layer, and the properties, heat resistance, printability, It is appropriately selected according to oil resistance, gas barrier properties, and the like. In addition, although the surface layer 6 is a single layer, you may use the lamination | stacking which consists of 2 or more of a polyethylene terephthalate (PET) layer, a nylon layer, a polyethylene (PE) layer, and a polypropylene (PP) layer as a surface layer, for example.
また、表層６は、シーラント層８を視認可能な視認部１０を有している。視認部１０は着色されていないため、視認部１０を介してシーラント層８（後述する表示部１２）を視認することができる。なお、この実施の形態においては、視認部１０を構成する領域以外の領域は着色されているが、着色されていなくてもよい。 Further, the surface layer 6 has a visual recognition part 10 through which the sealant layer 8 can be visually recognized. Since the visual recognition part 10 is not colored, the sealant layer 8 (display part 12 described later) can be visually recognized through the visual recognition part 10. In this embodiment, the region other than the region constituting the visual recognition unit 10 is colored, but it may not be colored.
シーラント層８は、例えば直鎖状低密度ポリエチレン（ＬＬＤＰＥ）層または無延伸ポリプロピレン（ＣＰＰ）層からなり、被包装物の性質、ヒートシール性、シール強度、耐衝撃性などに応じて適切に選択される。シーラント層８の融点は表層６の融点より低いため、所定の温度で包装用樹脂フィルム４を加熱すると、表層６が融けずにシーラント層８のみが融ける。シーラント層８のみが融けることを利用して、包装用樹脂フィルム４により被包装物を包装する際、包装用樹脂フィルム４の幅方向の両端部４ａを加熱し融けた後シールし、筒状になった包装用樹脂フィルム４の両側４ｂを加熱し融けた後シールすることにより包装体２が作製される。 The sealant layer 8 is made of, for example, a linear low density polyethylene (LLDPE) layer or an unstretched polypropylene (CPP) layer, and is appropriately selected according to the properties of the package, heat sealability, seal strength, impact resistance, etc. Is done. Since the melting point of the sealant layer 8 is lower than the melting point of the surface layer 6, when the packaging resin film 4 is heated at a predetermined temperature, only the sealant layer 8 melts without melting the surface layer 6. Utilizing the fact that only the sealant layer 8 is melted, when packaging an object to be packaged with the packaging resin film 4, both end portions 4a in the width direction of the packaging resin film 4 are heated and melted, and then sealed to form a cylinder. The package 2 is produced by heating and melting both sides 4b of the resulting packaging resin film 4 and then sealing.
また、シーラント層８は、ＴｉＯ2（酸化チタン）を含有し、被包装物を遮視する着色がなされている。即ち、シーラント層８は、ＴｉＯ2を含有しているため白色である。したがって、包装体２内に収容されている被包装体を、包装体２の外側から視認することはできない。 The sealant layer 8 contains TiO 2 (titanium oxide) and is colored so as to obscure the package. That is, the sealant layer 8 is white because it contains TiO 2 . Therefore, the packaged body accommodated in the package 2 cannot be viewed from the outside of the package 2.
また、表層６を介してシーラント層８にレーザ光を照射し、シーラント層８に含まれるＴｉＯ2を発色させることにより、シーラント層８に任意の文字、図形及び記号（以下、文字等という。）を表示させることができる。ＴｉＯ2は、レーザ光を照射すると白色から黒色（灰色を含む）に色調変化する。したがって、図３に示すように、シーラント層８にレーザ光を照射し、ＴｉＯ2を白色から黒色１４に変化させることにより文字等がレーザマーキングされる。即ち、シーラント層８に含まれるＴｉＯ2は、被包装物を遮視するための白色顔料として機能するとともに、シーラント層８に表示される文字等をレーザマーキングするための着色剤として機能する。 Further, the sealant layer 8 is irradiated with laser light through the surface layer 6 to develop TiO 2 contained in the sealant layer 8, thereby causing the sealant layer 8 to have arbitrary characters, figures, and symbols (hereinafter referred to as “characters”). Can be displayed. TiO 2 changes its color tone from white to black (including gray) when irradiated with laser light. Therefore, as shown in FIG. 3, a laser beam is irradiated on the sealant layer 8 to change the TiO 2 from white to black 14, so that characters and the like are laser-marked. That is, TiO 2 contained in the sealant layer 8 functions as a white pigment for shielding the packaged object, and also functions as a colorant for laser-marking characters and the like displayed on the sealant layer 8.
具体的には、シーラント層８は、文字等の少なくとも１つが表示される所定領域である表示部１２を有し、表示部１２には、文字等の少なくとも１つがレーザマーキングされ表示される。表示部１２は、図２及び図３に示すように、表層６とシーラント層８とを貼り合わせた際に表層６の視認部１０に対応する領域（視認部１０の下面と貼り合わされる領域）に形成される。なお、視認部１０及び表示部１２は、シーラント層８がシールとして機能する領域（４ａ，４ｂ）以外に配置される。 Specifically, the sealant layer 8 includes a display unit 12 that is a predetermined area in which at least one character or the like is displayed. At least one of the character or the like is laser-marked and displayed on the display unit 12. As shown in FIGS. 2 and 3, the display unit 12 is an area corresponding to the visual recognition part 10 of the surface layer 6 (an area bonded to the lower surface of the visual recognition part 10) when the surface layer 6 and the sealant layer 8 are bonded together. Formed. In addition, the visual recognition part 10 and the display part 12 are arrange | positioned except the area | region (4a, 4b) where the sealant layer 8 functions as a seal | sticker.
表示部１２は、視認部１０を介して包装体２の外側から視認可能である。表示部１２は、文字等として例えば被包装物である食品の商品名などの他、消費期限、賞味期限、製造所固有番号、内容量、ロット番号等、法令上または管理上必要な情報の少なくとも１つ（以下、消費期限等という。）を表示する。なお、表示部１２が消費期限等以外の文字等を表示してもよい。 The display unit 12 is visible from the outside of the package 2 through the visual recognition unit 10. The display unit 12 includes at least information necessary for legal or administrative purposes, such as a product name of a food that is a packaged item, etc. as a character, etc., as well as a expiration date, a shelf life, a unique number of a factory, an internal volume, a lot number, etc. One (hereinafter referred to as expiration date, etc.) is displayed. The display unit 12 may display characters other than the expiration date.
表示部１２に表示される文字等は、包装用樹脂フィルム４により被包装物を包装した包装体２が作製される直前に、表層６（視認部１０）を介してレーザ光を照射し、シーラント層８に含まれるＴｉＯ2を発色させることによりレーザマーキングされる。したがって、包装用樹脂フィルム４により被包装物を包装した包装体２が作製されるときまで印字することができない消費期限等を表示するのに適している。 Characters and the like displayed on the display unit 12 are irradiated with laser light through the surface layer 6 (visual recognition unit 10) immediately before the package 2 in which an article to be packaged is wrapped with the packaging resin film 4, and the sealant. Laser marking is performed by coloring TiO 2 contained in the layer 8. Therefore, it is suitable for displaying the expiration date or the like that cannot be printed until the package 2 in which the package object is packaged by the packaging resin film 4 is produced.
この実施の形態に係る包装体２によれば、表層６とシーラント層８との間に印刷層を設けなくとも、シーラント層８に含まれるＴｉＯ2を発色させることにより表示部１２に文字等をレーザマーキングし、表層６の視認部１０を介して、レーザマーキングされた文字等を視認することができる。したがって、包装体２の外側からの摩擦やインク成分の溶解などによる文字等の滲み、擦れ、崩れ、消失等を防止することができる。また、ＴｉＯ2を発色させることにより文字等をレーザマーキングするため、刻印の文字等と比較して、印字検査装置等による印字検査容易な文字等を表示することができる。 According to the package 2 according to this embodiment, even if a printing layer is not provided between the surface layer 6 and the sealant layer 8, characters or the like are displayed on the display unit 12 by coloring the TiO 2 contained in the sealant layer 8. Laser marking is performed, and laser-marked characters and the like can be visually recognized through the visual recognition portion 10 of the surface layer 6. Accordingly, it is possible to prevent bleeding, rubbing, collapsing, disappearance, and the like of characters due to friction from the outside of the package 2 or dissolution of ink components. In addition, since characters and the like are laser-marked by coloring TiO 2 , it is possible to display characters and the like that can be easily inspected by a print inspection device or the like as compared with engraved characters and the like.
また、表層６とシーラント層８との間に印刷層を設ける必要がないため、包装用樹脂フィルム４の厚さを薄くすることができる。更に、シーラント層８がＴｉＯ2を含有する白色であるため、包装体２内に収容された被包装体を遮視することができる。 Moreover, since it is not necessary to provide a printing layer between the surface layer 6 and the sealant layer 8, the thickness of the packaging resin film 4 can be reduced. Furthermore, since the sealant layer 8 is white containing TiO 2 , the packaged body accommodated in the package 2 can be shielded.
なお、上述の実施の形態においては、表層６及びシーラント層８からなる包装用樹脂フィルム４を例に挙げて説明したが、例えば図４に示すように、表層６とシーラント層８との間に少なくとも１つの中間層１６を有する包装用樹脂フィルム４０を用いてもよい。この場合には、表層６だけでなく中間層１６にもシーラント層８（表示部１２）を視認可能な視認部１８を設ける。 In the above-described embodiment, the packaging resin film 4 including the surface layer 6 and the sealant layer 8 has been described as an example. However, as illustrated in FIG. 4, for example, between the surface layer 6 and the sealant layer 8. A packaging resin film 40 having at least one intermediate layer 16 may be used. In this case, the visual recognition part 18 which can visually recognize the sealant layer 8 (display part 12) is provided not only on the surface layer 6 but also on the intermediate layer 16.
（実施例１）
表層として厚さ２０μｍのＯＰＰ（延伸ポリプロピレン）及びシーラント層として厚さ３０μｍの乳白ＬＬＤＰＥ（直鎖状低密度ポリエチレン）からなる包装用樹脂フィルムに、レーザマーカ（オムロン社製：ＭＸ−Ｚ２０００Ｇ）を用いてレーザマーキング（出力：８０％、パルス周波数：１００ｋＨｚ、加工速度：１０００ｍｍ／ｓ）を行った。なお、シーラント層は、ＴｉＯ2（酸化チタン）を含有しており、ＴｉＯ2（酸化チタン）により乳白色に着色されている。シーラント層（ＬＬＤＰＥ）に含まれるＴｉＯ2の量は約５．５％であった。これは、包装用樹脂フィルム（ＯＰＰ及びＬＬＤＰＥ）を燃焼させ灰にし、その灰からＴｉ（チタン）を抽出し、抽出したＴｉがすべてＴｉＯ2で存在したと仮定して、抽出したＴｉの重量からＴｉＯ2の重量を算出する。そして、算出したＴｉＯ2の重量を燃焼させた包装用樹脂フィルムのシーラント層の重量で割った値である。また、レーザマーキングのためのレーザ照射時間を（１）０．６秒、（２）１．２秒、（３）１．８秒、（４）２．４秒と変化させて、塗り潰し条件を太線：１０本、線幅：０．５ｍｍ、線間隔：０．０５ｍｍとし、文字条件を文字幅：４ｍｍ、高さ：４ｍｍ、文字間隔：１ｍｍ、ＬＭフォント使用として印字を行った。図５に（１）〜（４）のすべての場合における印字結果を示す。なお、図５の上から順に（１）、（２）、（３）、（４）の場合における印字結果を示している。図５に示すように、（１）〜（４）のすべての場合において容易に判読可能な印字がなされた。
Example 1
A laser marker (manufactured by OMRON Corporation: MX-Z2000G) is used on a packaging resin film composed of OPP (stretched polypropylene) having a thickness of 20 μm as a surface layer and milk white LLDPE (linear low density polyethylene) having a thickness of 30 μm as a sealant layer. Laser marking (output: 80%, pulse frequency: 100 kHz, processing speed: 1000 mm / s) was performed. The sealant layer contains TiO 2 (titanium oxide) and is colored milky white with TiO 2 (titanium oxide). The amount of TiO 2 contained in the sealant layer (LLDPE) was about 5.5%. This is because the packaging resin films (OPP and LLDPE) are burned into ash, Ti (titanium) is extracted from the ash, and all the extracted Ti is present in TiO 2. The weight of TiO 2 is calculated. Then, a value obtained by dividing the weight of the sealant layer of the calculated packaging resin film the weight of TiO 2 is burned with. Also, the laser irradiation time for laser marking is changed to (1) 0.6 seconds, (2) 1.2 seconds, (3) 1.8 seconds, (4) 2.4 seconds, and the filling conditions are changed. Printing was performed using 10 thick lines, line width: 0.5 mm, line spacing: 0.05 mm, and character conditions of character width: 4 mm, height: 4 mm, character spacing: 1 mm, using LM font. FIG. 5 shows the printing results in all cases (1) to (4). In addition, the printing results in the cases of (1), (2), (3), and (4) are shown in order from the top of FIG. As shown in FIG. 5, in all cases (1) to (4), easily readable prints were made.
（実施例２）
実施例１で使用した包装用樹脂フィルムに、レーザマーカ（オムロン社製：ＭＸ−Ｚ２０００Ｇ）を用いてレーザマーキング（出力：８０％、パルス周波数：７０ｋＨｚ、加工速度：５００ｍｍ／ｓレーザ照射時間：１．２秒）を行った。なお、塗り潰し条件及び文字条件は実施例１と同様の条件である。図６に印字結果を示す。但し、図６に示す黒枠は別途印刷したものであって上述のレーザマーキングによるものではない。図６に示すように、容易に判読可能な印字がなされた。
(Example 2)
Laser marking (output: 80%, pulse frequency: 70 kHz, processing speed: 500 mm / s laser irradiation time) using a laser marker (manufactured by OMRON: MX-Z2000G) on the packaging resin film used in Example 1. 2 seconds). The filling condition and the character condition are the same as those in the first embodiment. FIG. 6 shows the printing result. However, the black frame shown in FIG. 6 is printed separately and is not based on the laser marking described above. As shown in FIG. 6, the print was easily readable.
また、出力のみを変化させて、出力以外の条件は上述と同様の条件で印字を行った。出力が８０，７０％の場合においては容易に判読可能な印字がなされた。一方、出力が６０％の場合においては判読可能であるが濃度が薄く読み取り困難な印字がなされた。なお、出力が４０，２０％の場合における印字は判読不能であった。 Further, only the output was changed, and printing was performed under the same conditions as described above except for the output. When the output was 80, 70%, easily readable printing was made. On the other hand, when the output was 60%, printing was possible, but the density was low and difficult to read. It should be noted that the printing when the output was 40, 20% was unreadable.
また、パルス周波数のみを変化させて、パルス周波数以外の条件は上述と同様の条件で印字を行った。パルス周波数が１００，９０，７０，６０ｋＨｚの場合においては容易に判読可能な印字がなされた。一方、パルス周波数が５０ｋＨｚの場合においては判読可能であるが濃度が薄く読み取り困難な印字がなされた。なお、パルス周波数が３０，２０ｋＨｚの場合における印字は判読不能であった。 Further, only the pulse frequency was changed, and printing was performed under the same conditions as described above except for the pulse frequency. When the pulse frequency was 100, 90, 70, or 60 kHz, easy-to-read printing was performed. On the other hand, when the pulse frequency was 50 kHz, printing was possible, but the density was low and difficult to read. Note that the printing when the pulse frequency was 30, 20 kHz was unreadable.
また、加工速度のみを変化させて、加工速度以外の条件は上述と同様の条件で印字を行った。加工速度が５００ｍｍ／ｓの場合においては容易に判読可能な印字がなされた。一方、加工速度が７００，９００ｍｍ／ｓの場合においては判読可能であるが濃度が薄く読み取り困難な印字がなされた。なお、加工速度が１１００ｍｍ／ｓの場合における印字は判読不能であった。 Further, only the processing speed was changed, and printing was performed under the same conditions as described above except for the processing speed. When the processing speed was 500 mm / s, easy-to-read printing was performed. On the other hand, when the processing speed was 700,900 mm / s, printing was possible with a low density but difficult to read. Note that the printing when the processing speed was 1100 mm / s was unreadable.
（比較例）
実施例１で使用した包装用樹脂フィルムに代えて、表層として厚さ２０μｍのＯＰＰ（延伸ポリプロピレン）及びシーラント層として厚さ３０μｍのＬＬＤＰＥ（直鎖状低密度ポリエチレン）からなる包装用樹脂フィルムに、実施例１と同様の条件でレーザマーキングを行った。なお、シーラント層は、ＴｉＯ2（酸化チタン）を含有しておらず、透明である。図７に（１）〜（４）のすべての場合における印字結果を示す。なお、図７の上から順に（１）、（２）、（３）、（４）の場合における印字結果を示している。図７に示すように、（１）〜（４）のすべての場合において印字されなかった。
(Comparative example)
Instead of the packaging resin film used in Example 1, a packaging resin film composed of 20 μm thick OPP (stretched polypropylene) as a surface layer and 30 μm thick LLDPE (linear low density polyethylene) as a sealant layer, Laser marking was performed under the same conditions as in Example 1. The sealant layer does not contain TiO 2 (titanium oxide) and is transparent. FIG. 7 shows printing results in all cases (1) to (4). In addition, the printing results in the cases (1), (2), (3), and (4) are shown in order from the top of FIG. As shown in FIG. 7, printing was not performed in all cases (1) to (4).
以上より、ＴｉＯ2を含有し、ＴｉＯ2により着色されているシーラント層を有する包装用樹脂フィルムに、レーザマーキングによる印字は可能であるといえる。 From the above, it can be said that printing by laser marking is possible on a packaging resin film containing a sealant layer containing TiO 2 and colored with TiO 2 .
２…包装体、４…包装用樹脂フィルム、６…表層、８…シーラント層、１０…視認部、１２…表示部。 DESCRIPTION OF SYMBOLS 2 ... Packaging body, 4 ... Resin film for packaging, 6 ... Surface layer, 8 ... Sealant layer, 10 ... Visual recognition part, 12 ... Display part.
Claims (9)
前記表層は、前記シーラント層を視認可能な視認部を有し、
前記シーラント層は、ＴｉＯ2を含有し、前記被包装物を遮視する着色がなされていることを特徴とする包装用樹脂フィルム。 A packaging resin film for packaging a packaged article, having at least a surface layer and a sealant layer,
The surface layer has a visual recognition part capable of visually recognizing the sealant layer,
The packaging resin film, wherein the sealant layer contains TiO 2 and is colored so as to obscure the packaged object.
前記表示部は、前記視認部を介して視認可能であることを特徴とする請求項１記載の包装用樹脂フィルム。 The sealant layer has a display unit on which at least one of arbitrary characters, figures, and symbols is displayed by irradiating a laser beam through the surface layer to develop the TiO 2 color.
The packaging display resin film according to claim 1, wherein the display unit is visible through the visual recognition unit.