JP2016124870A - 含水ゲル組成物 - Google Patents
含水ゲル組成物 Download PDFInfo
- Publication number
- JP2016124870A JP2016124870A JP2015252536A JP2015252536A JP2016124870A JP 2016124870 A JP2016124870 A JP 2016124870A JP 2015252536 A JP2015252536 A JP 2015252536A JP 2015252536 A JP2015252536 A JP 2015252536A JP 2016124870 A JP2016124870 A JP 2016124870A
- Authority
- JP
- Japan
- Prior art keywords
- mass
- water
- less
- component
- gel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
さらに、特許文献3には、特定の鉱物と、ポリアクリル酸及び/又はその塩とを含有し、含水率が60重量%以上である含水パップ剤組成物が開示されており、裏ジミを低減しつつ皮膚への粘着性の付与を試みている。
(A)水 50質量%以上95質量%以下
(B)カルボキシメチルセルロース又はその塩を80質量%以上含むアニオン性水溶性高分子化合物
(C)アニオン性官能基とイオン架橋を形成する架橋剤
(D)下記一般式(1)で示されるノニオン性水溶性高分子化合物 2.5質量%以上8質量%以下
を含有する含水ゲル組成物に関する。
また、本発明は、次の成分(A)〜(D):
(A)水 50質量%以上95質量%以下
(B)カルボキシメチルセルロース又はその塩を80質量%以上含むアニオン性水溶性高分子化合物
(C)アニオン性官能基とイオン架橋を形成する架橋剤
(D)下記一般式(1)で示されるノニオン性水溶性高分子化合物 2.5質量%以上8質量%以下
を混合して未架橋ゲル原液を作製し、次いで片面を剥離可能なフィルムとし、他面を剥離可能なフィルム又は基材層として未架橋ゲル原液をシート化する、含水ゲル組成物の製造方法に関する。
本発明の含水ゲル組成物は、成分(A)として、水を50質量%以上95質量%以下含有する。このように、高い含有量で水が存在することから、使用場面においてみずみずしい肌触りを良好に発揮することができ、また適度な柔軟性を発揮して皮膚への優れた追随性を付与することもできる。成分(A)の含有量は、優れた使用感を付与する観点から、本発明の含水ゲル組成物中に、50質量%以上であって、好ましくは60質量%以上であり、より好ましくは65質量%以上であり、さらに好ましくは70質量%以上であり、ことさらに好ましくは75質量%以上である。また、成分(A)の含有量は、ゲルの安定性を確保する観点から、本発明の含水ゲル組成物中に、95質量%以下であって、好ましくは92質量%以下であり、より好ましくは90質量%以下であり、さらに好ましくは85質量%以下である。そして、成分(A)の含有量は、本発明の含水ゲル組成物中に、50質量%以上95質量%以下であって、好ましくは60〜92質量%であり、より好ましくは65〜92質量%であり、さらに好ましくは70〜90質量%であり、ことさらに好ましくは75〜85質量%である。
エーテル化度=(162×Y)/(10,000−80×Y)
有機酸の含有量は、効果的にゲルの安定性の向上に寄与する観点から、本発明の含水ゲル組成物中に、好ましくは0.1〜0.7質量%であり、より好ましくは0.3〜0.5質量%である。
なお、疎水性繊維の素材としては、ポリエチレンテレフタレート(PET)、ポリエチレン(PE)、ポリプロピレン(PP)等のポリオレフィン、ポリウレタン等の疎水性ポリマーからなる繊維が挙げられる。
[1]次の成分(A)〜(D):
(A)水 50質量%以上95質量%以下
(B)カルボキシメチルセルロース又はその塩を80質量%以上含むアニオン性水溶性高分子化合物
(C)アニオン性官能基とイオン架橋を形成する架橋剤
(D)下記一般式(1)で示されるノニオン性水溶性高分子化合物 2.5質量%以上8質量%以下
を含有する含水ゲル組成物。
[2]成分(A)の含有量は、好ましくは60質量%以上であり、より好ましくは65質量%以上であり、さらに好ましくは70質量%以上であり、ことさらに好ましくは75質量%以上であり、好ましくは92質量%以下であり、より好ましくは90質量%以下であり、さらに好ましくは85質量%以下である上記[1]の含水ゲル組成物。
[4]成分(B)に含まれるカルボキシメチルセルロース又はその塩の、1質量%水溶液としたときの25℃における粘度は、好ましくは1,500〜10,000mPa・sであり、より好ましくは2,500〜7,000mPa・sである上記[1]〜[3]いずれか1の含水ゲル組成物。
[5]カルボキシメチルセルロース又はその塩の含有量は、成分(B)中に、好ましくは80質量%以上であり、より好ましくは90質量%以上であり、さらに好ましくは95質量%以上であり、好ましくは100質量%以下である上記[1]〜[4]いずれか1の含水ゲル組成物。
[6]成分(B)の含有量は、好ましくは2.2質量%以上であり、より好ましくは2.7質量%以上であり、さらに好ましくは3質量%以上であり、好ましくは6質量%以下であり、より好ましくは5質量%以下であり、さらに好ましくは4質量%以下である上記[1]〜[5]いずれか1の含水ゲル組成物。
[8]成分(C)の含有量は、好ましくは0.01質量%以上であり、より好ましくは0.05質量%以上であり、さらに好ましくは0.1質量%以上であり、好ましくは2質量%以下であり、より好ましくは1質量%以下であり、さらに好ましくは0.4質量%以下である上記[1]〜[7]いずれか1の含水ゲル組成物。
[9]成分(B)と成分(C)の質量比((B)/(C))は、好ましくは3以上であり、より好ましくは15以上であり、さらに好ましくは20以上であり、好ましくは60以下であり、より好ましくは40以下であり、さらに好ましくは30以下である上記[1]〜[8]いずれか1の含水ゲル組成物。
[11]成分(D)の含有量は、好ましくは3質量%以上であり、より好ましくは4質量%以上であり、8質量%以下であって、好ましくは7質量%以下であり、より好ましくは6質量%以下である上記[1]〜[10]いずれか1の含水ゲル組成物。
[12]成分(B)と成分(D)の質量比((B)/(D))は、好ましくは0.4以上であり、より好ましくは0.5以上であり、さらに好ましくは0.6以上であり、好ましくは1.7以下であり、より好ましくは1.2以下であり、さらに好ましくは0.9以下である上記[1]〜[11]いずれか1の含水ゲル組成物。
[14]有機酸の含有量は、好ましくは0.1〜0.7質量%であり、より好ましくは0.3〜0.5質量%である上記[13]の含水ゲル組成物。
[15]成分(B)及び成分(D)以外の水溶性高分子化合物の含有量は、好ましくは1質量%以下であり、より好ましくは0.5質量%以下であり、さらに好ましくは0.2質量%以下であり、或いは好ましくはデンプン、グアーガム、及びキサンタンガムを含有しない上記[1]〜[14]いずれか1の含水ゲル組成物。
[16]厚みが、好ましくは0.1mm以上、より好ましくは0.3mm以上であり、さらに好ましくは0.5mm以上であり、また、好ましくは4mm以下であり、より好ましくは3mm以下であり、さらに好ましくは2以下である上記[1]〜[15]のいずれか1の含水ゲル組成物。
[17]さらに、基材層として好ましくは不織布、織布、編布、又は紙に積層したものであり、より好ましくは不織布に積層したものである上記[1]〜[16]いずれか1の含水ゲル組成物。
[18]不織布が、好ましくは親水性繊維を含み、より好ましくはレーヨン、コットン、キュプラ、麻、ウール、シルク、アセテート、セルロース、木材パルプ、非木材パルプの繊維;ポリビニルアルコール、ポリエチレングリコール、酢酸セルロース、ポリアクリルアミド、メラミン樹脂、ナイロン、親水性ポリウレタンの親水性ポリマーからなる繊維;親水化処理した疎水性ポリマーからなる繊維;疎水性ポリマーからなる疎水性部と親水性部とを備える複合繊維から選択される1種又は2種以上を含むものである上記[17]の含水ゲル組成物。
[19]不織布中の親水性繊維の含有量が、不織布中に好ましくは20質量%超であり、より好ましくは30質量%以上であり、さらに好ましくは40質量%以上であり、殊更に好ましくは50質量%以上であり、また、好ましくは100質量%以下であり、より好ましくは95質量%以下であり、さらに好ましくは90質量%以下である上記[18]の含水ゲル組成物。
[20]上記[1]〜[19]いずれか1の含水ゲル組成物を基材層に積層してなる冷却用貼付シート。
[21]基材層に積層することによる、上記[1]〜[19]いずれか1の含水ゲル組成物の冷却用貼付シート製造のための使用。
[22]上記成分(A)、(B)、(C)及び(D)を混合して未架橋ゲル原液を作製し、次いで片面を剥離可能なフィルムとし、他面を剥離可能なフィルム又は基材層として未架橋ゲル原液をシート化する含水ゲル組成物の製造方法。
[23]上記シート化する方法が、片面を剥離可能なフィルムとし、他面を剥離可能なフィルム又は基材層として未架橋ゲル原液を挟み込んだ後、展延する方法、或いは剥離可能なフィルム上に未架橋ゲル原液を塗工し、剥離可能なフィルム又は基剤層を積層する方法である上記[22]の含水ゲル組成物の製造方法。
[24]未架橋ゲル原液を、好ましくは0.1〜5mmの厚みに展延又は塗工する上記[23]の含水ゲル組成物の製造方法。
[25]未架橋ゲル原液を、好ましくは30〜60℃の加温下で1〜8日間熟成させる上記[22]〜[24]のいずれか1の含水ゲル組成物の製造方法。
[26]基材層として好ましくは不織布、織布、編布、又は紙に積層する、より好ましくは不織布に積層する、上記[22]〜[25]のいずれか1の含水ゲル組成物の製造方法。
表1〜3に示す処方にしたがい、下記方法により含水ゲル組成物を含む貼付剤を作製した。
具体的には、まずグリセリン、パラオキシ安息香酸メチルを加温溶解させたプロピレングリコール、カルボキシメチルセルロースナトリウム、乾燥水酸化アルミニウムゲルとの混合液を混練機に投入し、次にコハク酸水溶液を添加して、未架橋ゲル原液を調製した。次いで、得られた未架橋ゲル原液を、ポリエチレンテレフタレート(PET)フィルムに挟み込み、ベーカー式アプリケーターによってゲル原液の厚さを0.8mmに調整して展延した。次いで一方のPETフィルムを剥離し、展延したゲル層に不織布(パルプ:PET=80質量%:20質量%、坪量=20g/m2、エアレイド製 厚さ:0.22mm)をゲル層に張り合わせて、シート状の貼付剤にした。得られた貼付剤をアルミピローに封入して密封した後、50℃で2日間熟成し、未架橋ゲル原液中の架橋反応を進行させてゲルを形成した。架橋後のゲル層を備えた貼付剤を型抜きして、試験片を得た(50mm×100mm)。
得られた試験片を用い、下記方法にしたがって各評価を行った。
結果を表1〜3に示す。
得られた貼付剤の試験片を額に貼付した際の使用感について、5名の評価者により次の基準により評価し、その平均値を四捨五入して評価値とした。
5:みずみずしく、全くべたつかない
4:みずみずしく、僅かにべたつく
3:少しべたつく
2:乾いているが、べたつく
1:乾いているが、顕著にべたつく
粘着性は、JIS Z 0237(2009年改訂版)の「傾斜式ボールタック」を参考とし、次に記載する方法にて試験を行った。水平面に対して30°傾けたポリエチレン板上に、前記で得られた貼付剤の試験片(100mm×50mm)を貼り付けた。この試験片の上部に、材質がJIS G 4805(2008年改訂版)に規定された高炭素クロム軸受鋼鋼材で、JIS B 1501(2009年改訂版)で定められたボール大きさのうち、「呼び」が1/8インチのボールを置き、重力により転がせ、置いた場所から50mm〜100mmの間の50mmを通過した時間を測定した。本測定による時間は貼付剤の肌への貼りつき具合の指標となるが、時間が長過ぎるとべたつきが高くなり、肌触りの点で好ましくない。好ましくは200秒未満であり、より好ましくは5秒以上120秒未満であり、更に好ましくは10秒以上60秒未満である。
得られた貼付剤の試験片を額の肌に貼付し、眉間を上下に1cm、5回(1回/1秒)動かした際のシートの追随性について、次の基準により評価した。5名の評価者により行い、その平均値を四捨五入して評価値とした。
5:抵抗感なくしっかり追随する
4:少し抵抗感を感じるが追随する
3:抵抗感を感じるが追随する
2:少しでも動くと抵抗感を感じ、追随せず剥がれやすい
1:少しでも動くと抵抗感を強く感じ、追随せず剥がれやすい
得られた貼付剤の試験片を、50℃1ヵ月保存した後のゲルの保形性について、次の基準により評価した。5名の評価者により行い、その平均値を四捨五入して評価値とした。
5:弾性を有し非常に保形性が高い
4:弾性を有し保形性が高い
3:弾性はあるが保形性が若干低く少し柔らかい
2:弾性は少しある程度で保形性が低く柔らかい
1:弾性が無くゲルの保形性が無い
実施例1、比較例4、5及び6にて得られた貼付剤の試験片に、次の素材組成の不織布をそれぞれ積層した貼付剤の試験片を作製した。
・不織布1 PET:パルプ=80:20(質量比)のエアレイド不織布(厚み0.22mm、坪量20g/m2)
・不織布2 上層部がレーヨン:パルプ:PP+PET:PVA=37:32:28:3(質量比)、下層部がPET+PE:パルプ:PVA=82:14:4(質量比)の湿式二層不織布(厚み0.13mm、坪量24g/m2)
作製した試験片を50℃で1ヶ月保存した後に、不織布の含水ゲルに接する面と反対側の面への含水ゲルの染み出しを、次の基準にて評価した。
結果を表4に示す。
5:不織布の面に全く染み出しが確認できない
4:不織布の面の1/4以上に染み出しが確認できる。
3:不織布の面の半分以上に染み出しが確認できる。
2:不織布の面の3/4以上に染み出しが確認できる。
1:不織布の全面に染み出しが確認できる。
前記実施例にて作製したシート状の貼付剤の厚みを、JIS K6402:1976準拠の定圧厚み測定器PG−11J(テクロック社)を用い、加圧荷重3.7gf/cm2にて測定した。その結果、実施例1〜23、比較例1〜6の含水ゲル組成物を含む貼付剤の厚みは、1.3±0.3mmであった。また、不織布層から含水ゲル層のみを剥がし、含水ゲル層の厚みを測定したところ、1.1±0.3mmであった。
また、表4の結果によれば、本発明の含水ゲル組成物は、吸水性繊維に積層しても長期間染み出すことがなく、幅広い素材との組み合わせが可能であることがわかる。
Claims (8)
- 成分(C)が、多価金属化合物、並びに一分子内に一価のカチオン元素及び/又はアミノ基を2個以上有するカチオン性化合物から選ばれる1種又は2種以上である請求項1に記載の含水ゲル組成物。
- 成分(B)及び成分(D)以外の水溶性高分子化合物の含有量が、1質量%以下である請求項1又は2に記載の含水ゲル組成物。
- 成分(B)と成分(C)の質量比((B)/(C))が、3以上60以下である請求項1〜3のいずれか1項に記載の含水ゲル組成物。
- 成分(D)が、ポリビニルアルコール、ポリビニルピロリドン、及びポリアクリルアミドから選ばれる1種又は2種以上である請求項1〜4のいずれか1項に記載の含水ゲル組成物。
- 成分(B)の含有量が、2.2質量%以上6質量%以下である請求項1〜5のいずれか1項に記載の含水ゲル組成物。
- 厚みが0.1mm以上4mm以下である請求項1〜6のいずれか1項に記載の含水ゲル組成物。
- 次の成分(A)〜(D):
(A)水 50質量%以上95質量%以下
(B)カルボキシメチルセルロース又はその塩を80質量%以上含むアニオン性水溶性高分子化合物
(C)アニオン性官能基とイオン架橋を形成する架橋剤
(D)下記一般式(1)で示されるノニオン性水溶性高分子化合物 2.5質量%以上8質量%以下
を混合して未架橋ゲル原液を作製し、次いで片面を剥離可能なフィルムとし、他面を剥離可能なフィルム又は基材層として未架橋ゲル原液をシート化する、含水ゲル組成物の製造方法。