JP2016075748A - Heat shrinkable cylindrical label, and vessel having label - Google Patents

Heat shrinkable cylindrical label, and vessel having label Download PDF

Info

Publication number
JP2016075748A
JP2016075748A JP2014204727A JP2014204727A JP2016075748A JP 2016075748 A JP2016075748 A JP 2016075748A JP 2014204727 A JP2014204727 A JP 2014204727A JP 2014204727 A JP2014204727 A JP 2014204727A JP 2016075748 A JP2016075748 A JP 2016075748A
Authority
JP
Japan
Prior art keywords
heat
print layer
layer
label
shrinkable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2014204727A
Other languages
Japanese (ja)
Other versions
JP6513922B2 (en
Inventor
原田 雅史
Masafumi Harada
雅史 原田
祐司 大矢
Yuji Oya
祐司 大矢
Original Assignee
株式会社フジシール
Fuji Seal Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社フジシール, Fuji Seal Inc filed Critical 株式会社フジシール
Priority to JP2014204727A priority Critical patent/JP6513922B2/en
Publication of JP2016075748A publication Critical patent/JP2016075748A/en
Application granted granted Critical
Publication of JP6513922B2 publication Critical patent/JP6513922B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a heat shrinkable cylindrical label having a sufficient hologram-like appearance even after heat shrinkage.SOLUTION: A heat shrinkable cylindrical label 1 of the present invention includes: a cylindrical film formed in a cylindrical shape so that the rear surface of the heat shrinkable film 3 defines the inner surface of the cylindrical shape; and a decorative printing layer 4 disposed on at least one of the front side and rear side of the cylindrical film. The decorative printing layer 4 includes a tabular thin piece containing a metal or semimetal and having a plurality of irregularities on one surface.SELECTED DRAWING: Figure 5

Description

本発明は、ホログラム調の外観を有する熱収縮性筒状ラベル及びそれが装着されたラベル付き容器に関する。   The present invention relates to a heat-shrinkable cylindrical label having a hologram-like appearance and a labeled container to which the heat-shrinkable cylindrical label is attached.

従来、熱収縮性フィルムを筒状に形成した熱収縮性筒状ラベルが多様な用途に用いられている。なお、熱収縮性筒状ラベルは、シュリンクラベル、シュリンクチューブなどとも呼ばれる。
前記熱収縮性筒状ラベルは、商品名などの文字、装飾的な模様などのデザインを表示するための装飾媒体として利用されている。また、装飾効果を高めるため、ホログラム調の外観を有する熱収縮性筒状ラベルも知られている。ここで、ホログラム調の外観とは、光の干渉縞によって視覚上虹色のように見える外観をいう。
従来、ラベルにホログラム調の外観を付与する方法としては、ホログラム箔転写シートをラベルに転写する方法が知られている(特許文献1)。前記ホログラム箔転写用シートは、剥離層を有するシートと、前記剥離層の表面に積層され且つホログラム調の表面凹凸を有する樹脂層と、この樹脂層の表面に積層されたアルミニウム蒸着膜と、このアルミニウム蒸着膜の表面に積層された接着剤層と、を有する。この転写シートの接着剤層をラベルに接着し、剥離層を有するシートを引き剥がすことにより、ラベルにホログラム箔が転写される。
しかしながら、熱収縮性筒状ラベルに前記ホログラム箔を転写した場合には、熱収縮性筒状ラベルを被着体に装着した後に、ホログラム効果が消失する又は非常に小さくなるという問題点がある。ホログラム効果が消失する理由は、明確ではないが、次のように推定される。熱収縮性筒状ラベルは、加熱して熱収縮させることにより被着体に装着されるラベルであり、前記ホログラム箔が転写された熱収縮性筒状ラベルを熱収縮させると、ホログラム箔もそれに追従して収縮させられるので、樹脂層の表面の凹凸が乱れ、ホログラム調の外観を消失する又はその外観が見え難くなる。
Conventionally, a heat-shrinkable cylindrical label in which a heat-shrinkable film is formed in a cylindrical shape has been used for various applications. The heat-shrinkable cylindrical label is also called a shrink label, a shrink tube, or the like.
The heat-shrinkable cylindrical label is used as a decoration medium for displaying a character name such as a product name and a design such as a decorative pattern. In order to enhance the decorative effect, a heat-shrinkable cylindrical label having a hologram-like appearance is also known. Here, the hologram-like appearance means an appearance that visually looks like a rainbow color due to interference fringes of light.
Conventionally, as a method of imparting a hologram-like appearance to a label, a method of transferring a hologram foil transfer sheet to a label is known (Patent Document 1). The hologram foil transfer sheet includes a release layer, a resin layer laminated on the surface of the release layer and having hologram-like surface irregularities, an aluminum vapor deposition film laminated on the surface of the resin layer, And an adhesive layer laminated on the surface of the aluminum deposited film. By adhering the adhesive layer of the transfer sheet to the label and peeling off the sheet having the release layer, the hologram foil is transferred to the label.
However, when the hologram foil is transferred to a heat-shrinkable cylindrical label, there is a problem that the hologram effect disappears or becomes very small after the heat-shrinkable cylindrical label is attached to the adherend. The reason for the disappearance of the hologram effect is not clear, but is estimated as follows. The heat-shrinkable cylindrical label is a label attached to the adherend by heating and heat-shrinking. When the heat-shrinkable cylindrical label to which the hologram foil is transferred is heat-shrinked, the hologram foil is also moved to it. Since it is made to follow and contract, the irregularities on the surface of the resin layer are disturbed, and the hologram-like appearance disappears or the appearance becomes difficult to see.

特開2003−320795号公報JP 2003-320795 A

本発明の目的は、熱収縮させた後も良好なホログラム調の外観を有する熱収縮性筒状ラベル及びその熱収縮性筒状ラベルが容器に熱収縮装着されたラベル付き容器を提供することである。   An object of the present invention is to provide a heat-shrinkable cylindrical label having a good hologram-like appearance even after heat-shrinking and a labeled container in which the heat-shrinkable cylindrical label is heat-shrink mounted on the container. is there.

本発明者らは、鋭意研究した結果、複数の凹凸を有する板状の薄片を含む印刷層を形成することにより、上記目的を達成できる熱収縮性筒状ラベルに想到した。   As a result of diligent research, the present inventors have come up with a heat-shrinkable cylindrical label that can achieve the above object by forming a printing layer including a plate-like thin piece having a plurality of irregularities.

本発明の熱収縮性筒状ラベルは、熱収縮性フィルムの裏面が内側となるように筒状に形成された筒状フィルムと、前記筒状フィルムの表面側及び裏面側の少なくとも一方側に設けられた装飾印刷層と、を有し、前記装飾印刷層が、金属又は半金属を含み且つ一方面に複数の凹凸を有する板状薄片を含んでいる。   The heat-shrinkable cylindrical label of the present invention is provided on at least one side of a tubular film formed in a tubular shape so that the back surface of the heat-shrinkable film is inside, and the front surface side and the back surface side of the tubular film. The decorative printed layer, and the decorative printed layer includes a plate-shaped flake including a metal or a semimetal and having a plurality of irregularities on one surface.

本発明の好ましい熱収縮性筒状ラベルは、前記板状薄片が、金属蒸着薄片を含む。
本発明の好ましい熱収縮性筒状ラベルは、前記装飾印刷層が、筒状フィルムの裏面側に設けられており、その装飾印刷層の裏面側に、白色着色剤を含む背景印刷層が設けられている。
In a preferred heat-shrinkable cylindrical label of the present invention, the plate-like flakes include metal-deposited flakes.
In a preferable heat-shrinkable cylindrical label of the present invention, the decorative print layer is provided on the back side of the cylindrical film, and a background print layer containing a white colorant is provided on the back side of the decorative print layer. ing.

本発明の別の局面によれば、ラベル付き容器を提供する。
本発明のラベル付き容器は、三次元曲面部を有する容器と、前記三次元曲面部を含んで前記容器に熱収縮装着された上記熱収縮性筒状ラベルと、を有し、前記装飾印刷層の設けられた領域が前記三次元曲面部に装着されている。
According to another aspect of the present invention, a labeled container is provided.
The container with a label of the present invention includes a container having a three-dimensional curved surface portion, and the heat-shrinkable cylindrical label that is heat-shrink-mounted on the container including the three-dimensional curved surface portion, and the decorative print layer The region provided with is attached to the three-dimensional curved surface portion.

本発明の熱収縮性筒状ラベルは、複数の凹凸を有する板状薄片を含む装飾印刷層が設けられているので、熱収縮させた後も良好なホログラム調の外観を有する。
かかる熱収縮性筒状ラベルが容器の三次元曲面部に熱収縮装着されたラベル付き容器は、見る角度によって色彩が大きく変化するホログラム調の外観を有し、装飾性に優れているものである。
The heat-shrinkable cylindrical label of the present invention is provided with a decorative print layer including a plate-shaped flake having a plurality of irregularities, and thus has a good hologram-like appearance even after heat-shrinking.
A labeled container in which such a heat-shrinkable cylindrical label is heat-shrink mounted on the three-dimensional curved surface portion of the container has a hologram-like appearance in which the color changes greatly depending on the viewing angle, and is excellent in decorativeness. .

本発明の熱収縮性筒状ラベルを構成するラベル形成用基材を裏面側から見た正面図。The front view which looked at the base material for label formation which comprises the heat-shrinkable cylindrical label of this invention from the back surface side. 図1のII−II線で切断した横断面図。The cross-sectional view cut | disconnected by the II-II line | wire of FIG. 図1のIII−III線で切断した横断面図。The cross-sectional view cut | disconnected by the III-III line of FIG. 本発明の熱収縮性筒状ラベルの斜視図。The perspective view of the heat-shrinkable cylindrical label of this invention. 同熱収縮性筒状ラベルを上方から見た平面図。The top view which looked at the heat-shrinkable cylindrical label from the upper direction. 図4のVI−VI線で切断した横断面図(シール部の横断面図)。The cross-sectional view cut | disconnected by the VI-VI line of FIG. 4 (cross-sectional view of a seal part). 板状薄片を一方面側から見た平面図。The top view which looked at the plate-shaped thin piece from the one surface side. (a)は、板状薄片の一方面の一部分を拡大した平面図であって、1つの実施形態に係る凹凸形状を示す平面図、(b)は、同(a)のVIIIb−VIIIb線で切断した断面図、(c)は、凹凸形状の変形例を示す断面図。(A) is the top view which expanded a part of one side of a plate-shaped thin piece, Comprising: The top view which shows the uneven | corrugated shape which concerns on one embodiment, (b) is a VIIIb-VIIIb line | wire of the (a). Sectional drawing which cut | disconnected, (c) is sectional drawing which shows the modification of uneven | corrugated shape. (a)は、板状薄片の一方面の一部分を拡大した平面図であって、更なる変形例に係る凹凸形状を示す平面図、(b)は、同(a)のIXb−IXb線で切断した断面図。(A) is the top view which expanded a part of one side of a plate-shaped thin piece, Comprising: The top view which shows the uneven | corrugated shape which concerns on the further modification, (b) is the IXb-IXb line | wire of the (a). Sectional drawing which cut | disconnected. (a)は、本発明の第1例に係るラベル付き容器の正面図、(b)は、第2例に係るラベル付き容器の正面図。(A) is a front view of the labeled container which concerns on the 1st example of this invention, (b) is a front view of the labeled container which concerns on a 2nd example. (a)は、本発明の第3例に係るラベル付き容器の正面図、(b)は、第4例に係るラベル付き容器の正面図。(A) is a front view of the labeled container which concerns on the 3rd example of this invention, (b) is a front view of the labeled container which concerns on a 4th example.

以下、本発明の実施形態について図面を参照しながら説明する。
ただし、本明細書において、「裏面」とは、筒状ラベルを形成したときにその筒状内側となる面をいい、「表面」とは、前記裏面の反対面(他方の面)を指し、筒状ラベルを形成したときにその筒状外側となる面をいう。筒状内側は、筒状ラベルの径内方向を意味し、筒状外側は、筒状ラベルの径外方向を意味する。
また、本明細書において、「横方向」は、ラベル形成用基材の1つの方向であって、この基材が筒状ラベルに形成されたときにはその筒状ラベルの周方向に相当し、「縦方向」は、基材の面内で前記横方向と略直交する方向をいう。
なお、各図において表された形状、大きさ、各層の厚み及びそれらの相対的な比率などは、実際の寸法とは異なっていることに留意されたい。
Hereinafter, embodiments of the present invention will be described with reference to the drawings.
However, in the present specification, the “back surface” refers to a surface that becomes the inside of the cylinder when the cylindrical label is formed, and the “front surface” refers to the opposite surface (the other surface) of the back surface, When a cylindrical label is formed, the surface which becomes the cylindrical outer side is said. The cylindrical inner side means the inner radial direction of the cylindrical label, and the cylindrical outer side means the outer radial direction of the cylindrical label.
In the present specification, the “lateral direction” is one direction of the base material for label formation, and corresponds to the circumferential direction of the cylindrical label when the base material is formed on the cylindrical label. The “longitudinal direction” refers to a direction substantially orthogonal to the lateral direction in the plane of the substrate.
It should be noted that the shape, size, thickness of each layer, the relative ratio thereof, and the like shown in each drawing are different from actual dimensions.

[1つの実施形態]
図1は、本発明の筒状ラベルを形成するために用いられる、ラベル形成用基材を裏面側から見た正面図であり、図2及び図3は、その基材の各部で切断した断面図である。図4は、本発明の熱収縮性筒状ラベルの斜視図であり、図5は、その熱収縮性筒状ラベルを上方から見た平面図であり、図6は、その熱収縮性筒状ラベルのシール部を切断した断面図である。
本発明の熱収縮性筒状ラベル1は、後述するラベル形成用基材2を筒状に形成したものである。
一般に、熱収縮性筒状ラベルは、容器などの被着体に対する装着方法に従って、予め筒状に形成された熱収縮性筒状ラベルと、被着体に装着すると同時に筒状に形成される熱収縮性筒状ラベルと、に大別できる。これらの熱収縮性筒状ラベルは、いずれも熱収縮性フィルムを有する基材を筒状に形成した筒状フィルムからなる点において共通しているが、その違いは、被着体に装着される前から筒状となっているか、又は、被着体に装着する前には葉状の基材の状態であって、被着体に装着すると同時に筒状となる点である。本発明の熱収縮性筒状ラベル1は、前記2つのいずれのタイプでもよい。
以下、図面などを含めて前者のタイプの熱収縮性筒状ラベル1について説明する。
[One Embodiment]
FIG. 1 is a front view of a label-forming base material used to form the cylindrical label of the present invention as viewed from the back side, and FIGS. 2 and 3 are cross-sections cut at each part of the base material. FIG. 4 is a perspective view of the heat-shrinkable cylindrical label of the present invention, FIG. 5 is a plan view of the heat-shrinkable cylindrical label from above, and FIG. 6 is the heat-shrinkable cylindrical label. It is sectional drawing which cut | disconnected the seal part of the label.
The heat-shrinkable cylindrical label 1 of the present invention is obtained by forming a label-forming substrate 2 described later in a cylindrical shape.
Generally, a heat-shrinkable cylindrical label is a heat-shrinkable cylindrical label formed in advance in a cylindrical shape according to a mounting method for an adherend such as a container, and heat that is formed in a cylindrical shape at the same time as being attached to the adherend. It can be roughly divided into a shrinkable cylindrical label. These heat-shrinkable cylindrical labels are common in that they are made of a tubular film in which a base material having a heat-shrinkable film is formed into a tubular shape, but the difference is attached to the adherend. It is cylindrical from the front, or is in a state of a leaf-like base material before being attached to the adherend, and becomes cylindrical at the same time as being attached to the adherend. The heat-shrinkable cylindrical label 1 of the present invention may be any of the two types.
Hereinafter, the former type of heat-shrinkable cylindrical label 1 will be described with reference to the drawings.

(ラベル形成用基材)
ラベル形成用基材2は、熱収縮性筒状ラベル1を構成する基本部材である。
前記ラベル形成用基材2は、図1乃至図3に示すように、平面視矩形状の熱収縮性フィルム3と、金属又は半金属を含み且つ一方面に複数の凹凸を有する板状薄片を含む装飾印刷層4と、を有し、好ましくは、デザインを表示したデザイン印刷層5をさらに有し、より好ましくは、背景印刷層6をさらに有する。前記ラベル形成用基材2は、必要に応じて、前記熱収縮性フィルム3、装飾印刷層4、デザイン印刷層5及び背景印刷層6以外の他の機能層を有していてもよい。前記他の機能層としては、表面保護層、滑り層などが挙げられる。
このラベル形成用基材2の裏面が内側となるように、これを筒状にして、その第1側端部21の表面側に第2側端部22を重ねて接着することにより、図4乃至図6に示すような、本発明の熱収縮性筒状ラベル1が得られる。
なお、機械的生産過程では、ラベル形成用基材は、通常、複数のラベル形成用基材が連続的に繋がった長尺状の基材連続体として製造される。使用に際して、その連続体を所定長さに切断することにより、個々のラベル形成用基材2が得られる。
(Base material for label formation)
The label-forming substrate 2 is a basic member constituting the heat-shrinkable cylindrical label 1.
As shown in FIGS. 1 to 3, the label-forming substrate 2 includes a heat-shrinkable film 3 having a rectangular shape in plan view, and a plate-like piece containing a metal or a semimetal and having a plurality of irregularities on one surface. A decorative print layer 4 including, preferably a design print layer 5 displaying a design, and more preferably a background print layer 6. The label-forming substrate 2 may have a functional layer other than the heat-shrinkable film 3, the decorative print layer 4, the design print layer 5, and the background print layer 6 as necessary. Examples of the other functional layers include a surface protective layer and a sliding layer.
By making this into a cylindrical shape so that the back surface of the label forming substrate 2 is inside, the second side end portion 22 is overlapped and bonded to the surface side of the first side end portion 21, whereby FIG. Thru | or FIG. 6, the heat-shrinkable cylindrical label 1 of this invention is obtained.
In the mechanical production process, the label forming substrate is usually manufactured as an elongated substrate continuous body in which a plurality of label forming substrates are continuously connected. In use, each label-forming substrate 2 is obtained by cutting the continuous body into a predetermined length.

(熱収縮性フィルム)
前記熱収縮性フィルム3としては、その裏面側に設けられた層を筒状ラベルの外側から視認するために透明なフィルムが用いられる。なお、本明細書において、ある部材が「透明」とは、その部材の表面側からその部材の裏面側に設けられた層の色彩及び表示を視認できる程度の透光性を有することをいう。前記熱収縮性フィルム3の全光線透過率は、例えば、70%以上であり、好ましくは80%以上であり、より好ましくは90%以上である。前記全光線透過率は、JIS K7105(プラスチックの光学的特性試験方法)に準拠した測定法によって測定される値をいう。
前記熱収縮性フィルム3は、熱収縮性を有していることを条件として、例えば、自己伸縮性も有してもいてもよく、或いは、自己伸縮性を有していなくてもよい。自己伸縮性は、フィルムに拡張力を加えるとそのフィルムが伸び、その拡張力を解除するとフィルムがほぼ元の寸法に戻る性質をいう。
(Heat shrinkable film)
As the heat-shrinkable film 3, a transparent film is used in order to visually recognize the layer provided on the back surface side from the outside of the cylindrical label. In addition, in this specification, a certain member is "transparent" means that it has translucency of the grade which can visually recognize the color and display of the layer provided in the back surface side of the member from the surface side of the member. The total light transmittance of the heat-shrinkable film 3 is, for example, 70% or more, preferably 80% or more, and more preferably 90% or more. The total light transmittance refers to a value measured by a measuring method based on JIS K7105 (plastic optical property testing method).
The heat-shrinkable film 3 may have, for example, self-stretching property or may not have self-stretching property on the condition that it has heat-shrinking property. Self-stretchability refers to the property that when an expansion force is applied to the film, the film stretches, and when the expansion force is released, the film returns to its original size.

前記熱収縮性は、所要温度(例えば、70℃〜100℃)に加熱されると収縮する性質をいう。熱収縮性フィルム3は、横方向(横方向は、筒状フィルムに形成した際に、周方向となる)に少なくとも熱収縮し、必要に応じて、縦方向にも若干熱収縮又は熱伸張し得るものでもよい。
熱収縮性フィルム3の横方向における熱収縮率は、被着体に密着させることができる程度以上であれば特に限定されず、例えば、90℃に加熱した際の横方向における熱収縮率は、30%以上であり、好ましくは40%以上、より好ましくは50%以上である。なお、熱収縮性フィルム3が縦方向にも若干熱収縮又は熱伸張する場合、その90℃に加熱した際の縦方向における熱収縮率は、例えば、−3%〜15%である。前記縦方向の熱収縮率のマイナスは、熱伸張を意味する。前記90℃に加熱した際の熱収縮率は、加熱前のフィルムの長さ(元の長さ)と、フィルムを90℃の温水中に10秒間浸漬した後のフィルムの長さ(浸漬後の長さ)の割合であり、下記式に代入して求められる。
式:熱収縮率(%)=[{(横方向(又は縦方向)の元の長さ)−(横方向(又は縦方向)の浸漬後の長さ)}/(横方向(又は縦方向)の元の長さ)]×100。
The heat shrinkability refers to a property of shrinking when heated to a required temperature (for example, 70 ° C. to 100 ° C.). The heat-shrinkable film 3 is at least heat-shrinked in the horizontal direction (the horizontal direction is the circumferential direction when formed into a tubular film), and is slightly heat-shrinked or stretched in the vertical direction as necessary. You may get it.
The heat shrinkage rate in the horizontal direction of the heat-shrinkable film 3 is not particularly limited as long as it can be adhered to the adherend. For example, the heat shrinkage rate in the horizontal direction when heated to 90 ° C. is It is 30% or more, preferably 40% or more, more preferably 50% or more. In addition, when the heat-shrinkable film 3 is slightly heat-shrinked or stretched in the vertical direction, the heat shrinkage rate in the vertical direction when heated to 90 ° C. is, for example, −3% to 15%. The minus of the thermal contraction rate in the longitudinal direction means thermal expansion. The heat shrinkage rate when heated to 90 ° C. is the length of the film before heating (original length) and the length of the film after being immersed in warm water of 90 ° C. for 10 seconds (after immersion). Length) and is obtained by substituting into the following equation.
Formula: heat shrinkage rate (%) = [{(original length in horizontal direction (or vertical direction)) − (length after immersion in horizontal direction (or vertical direction))} / (horizontal direction (or vertical direction) ) Original length)] × 100.

熱収縮性フィルム3は、装飾印刷層が設けられる面が高い平滑性を有するものが好ましい。平滑性が高い熱収縮性フィルム3を用いることにより、板状薄片が配向し易くなり、熱収縮性筒状ラベルが良好なホログラム調の外観を呈する。詳しくは、装飾印刷層4に含まれる複数の板状薄片は、その一方面を装飾印刷層4の表面に対して平行又は鋭角状に傾斜し且つその装飾印刷層4の厚み方向に積み重なって配向していると考えられ、前記のように平滑性の高い面に装飾印刷層4を設けることにより、板状薄片の配向が乱れ難くなり、その結果、良好なホログラム調の外観を呈する熱収縮性筒状ラベルが得られる。   The heat-shrinkable film 3 preferably has high smoothness on the surface on which the decorative print layer is provided. By using the heat-shrinkable film 3 having high smoothness, the plate-like flakes are easily oriented, and the heat-shrinkable cylindrical label exhibits a good hologram-like appearance. Specifically, the plurality of plate-like flakes included in the decorative print layer 4 are oriented so that one surface thereof is inclined parallel or acute to the surface of the decorative print layer 4 and stacked in the thickness direction of the decorative print layer 4. By providing the decorative printing layer 4 on the surface having high smoothness as described above, the orientation of the plate-like flakes is hardly disturbed, and as a result, the heat shrinkability that exhibits a good hologram-like appearance. A cylindrical label is obtained.

前記熱収縮性フィルム3の材質は、特に限定されず、例えば、ポリエチレンテレフタレートなどのポリエステル系樹脂、ポリプロピレン、環状オレフィンなどのオレフィン系樹脂、スチレン−ブタジエン共重合体などのスチレン系樹脂、塩化ビニル系樹脂などの熱可塑性樹脂を含む延伸フィルムが挙げられる。また、熱収縮性フィルム3は、単層構造でもよく、複層構造でもよい。平滑性が高く、印刷溶剤耐性に優れていることから、少なくとも装飾印刷層の設けられる面がポリエステル系樹脂層で構成された熱収縮性フィルムが好ましい。また、熱収縮後でも板状薄片の配向が比較的崩れにくいことから、収縮曲線が緩やかであるポリスチレン系樹脂層又はポリオレフィン系樹脂層を含む熱収縮性フィルムを用いることが好ましい。これらの事項を考慮して、特に、熱収縮性フィルム3は、表裏面層にポリエステル系樹脂層を有し、且つ中間層にポリスチレン系樹脂層又はポリオレフィン系樹脂層を有する異種積層フィルムが好ましい。
前記矩形状の熱収縮性フィルム3は、縦方向に沿う第1側端部21と、この第1側端部21に横方向において対向する、縦方向に沿う第2側端部22と、をそれぞれ有する。前記第1側端部21は、熱収縮性フィルム3の1つの側端部において上縁から下縁にまで縦方向に延びる帯状領域である。前記第2側端部22は、熱収縮性フィルム3のもう1つの側端部において上縁から下縁にまで縦方向に延びる帯状領域である。前記第1側端部21及び第2側端部22は、筒状フィルム(筒状ラベル)を形成する際に重ね合わせて接着される、シール部を構成する。
前記第1側端部21及び第2側端部22の横幅は、それぞれ特に限定されないが、通常、3mm〜20mmであり、好ましくは5mm〜15mmである。前記横幅とは、横方向における長さである。
The material of the heat-shrinkable film 3 is not particularly limited, and examples thereof include polyester resins such as polyethylene terephthalate, olefin resins such as polypropylene and cyclic olefin, styrene resins such as styrene-butadiene copolymer, and vinyl chloride. The stretched film containing thermoplastic resins, such as resin, is mentioned. The heat-shrinkable film 3 may have a single layer structure or a multilayer structure. A heat-shrinkable film in which at least the surface on which the decorative printing layer is provided is composed of a polyester resin layer is preferable because of its high smoothness and excellent printing solvent resistance. In addition, since the orientation of the plate-like flakes is relatively difficult to break even after heat shrinkage, it is preferable to use a heat shrinkable film including a polystyrene resin layer or a polyolefin resin layer having a gentle shrinkage curve. Considering these matters, the heat-shrinkable film 3 is particularly preferably a heterogeneous laminated film having a polyester resin layer on the front and back layers and a polystyrene resin layer or a polyolefin resin layer on the intermediate layer.
The rectangular heat-shrinkable film 3 includes a first side end portion 21 along the vertical direction and a second side end portion 22 along the vertical direction that opposes the first side end portion 21 in the horizontal direction. Have each. The first side end 21 is a band-like region extending in the vertical direction from the upper edge to the lower edge at one side end of the heat-shrinkable film 3. The second side end 22 is a band-like region extending in the vertical direction from the upper edge to the lower edge at the other side end of the heat-shrinkable film 3. The said 1st side edge part 21 and the 2nd side edge part 22 comprise the seal | sticker part which overlap | superposes and adhere | attaches, when forming a cylindrical film (tubular label).
The lateral widths of the first side end portion 21 and the second side end portion 22 are not particularly limited, but are usually 3 mm to 20 mm, preferably 5 mm to 15 mm. The horizontal width is a length in the horizontal direction.

(装飾印刷層)
装飾印刷層4は、後述する板状薄片を含む印刷層である。本発明の熱収縮性筒状ラベル1は、前記装飾印刷層4が設けられているので、熱収縮前後において、ホログラム調の外観を有する。
装飾印刷層4は、熱収縮性フィルム3の表面側及び裏面側の少なくとも一方側に設けられ、好ましくは、熱収縮性フィルム3の表面側又は裏面側の何れか一方側に設けられる。
熱収縮性フィルム3を通じて装飾印刷層4を見た方が良好なホログラム調の外観を呈することから、前記装飾印刷層4は、熱収縮性フィルム3の裏面側に設けられていることが好ましい。特に、板状薄片が配向し易くなることから、熱収縮性フィルム3の表面及び裏面の少なくとも一方に接して設けられ、好ましくは、熱収縮性フィルム3の裏面に接して設けられる。
(Decorative printing layer)
The decorative print layer 4 is a print layer including a plate-shaped flake described later. Since the decorative print layer 4 is provided, the heat-shrinkable cylindrical label 1 of the present invention has a hologram-like appearance before and after heat shrinkage.
The decorative print layer 4 is provided on at least one side of the front surface side and the back surface side of the heat shrinkable film 3, and preferably provided on either the front surface side or the back surface side of the heat shrinkable film 3.
It is preferable that the decorative print layer 4 is provided on the back side of the heat-shrinkable film 3 because a better hologram-like appearance is obtained when the decorative print layer 4 is viewed through the heat-shrinkable film 3. In particular, since the plate-like flakes are easily oriented, they are provided in contact with at least one of the front and back surfaces of the heat-shrinkable film 3, and preferably provided in contact with the back surface of the heat-shrinkable film 3.

装飾印刷層4は、ホログラム調の外観を見せたい領域に設けられる。従って、装飾印刷層4は、熱収縮性フィルム3の所望の領域に設けられ、例えば、熱収縮性フィルム3の全体に設けられていてもよく、或いは、その一部分に設けられていてもよい。もっとも、シール部はフィルム同士を直接接着することによって強固となるので、シール部を構成するフィルム重ね合わせ面には、装飾印刷層が設けられていないことが好ましい。詳しくは、装飾印刷層4は、熱収縮性フィルム3の上縁と、下縁と、第1側端縁(第1側端部21側の側縁21a)と、第2側端部22の境界線22bと、によって囲われる領域内(以下、この領域を特定領域という場合がある)に設けられている。装飾印刷層4は、前記特定領域内の全体に設けられていてもよく、又は、その特定領域内の一部分に設けられていてもよい。好ましくは、図示のように、装飾印刷層4は、前記特定領域内の一部に設けられる。
例えば、図示例では、前記特定領域内の一部に装飾印刷層4が設けられ、その領域内の一部には、装飾印刷層が設けられていない部分39(以下、非装飾印刷部という)が存在する。その非装飾印刷部39は、前記特定領域内の1箇所に形成されていてもよく、独立した2箇所以上に形成されていてもよい。
The decorative print layer 4 is provided in an area where it is desired to show a hologram-like appearance. Therefore, the decorative print layer 4 is provided in a desired region of the heat-shrinkable film 3, and may be provided on the entire heat-shrinkable film 3, or may be provided on a part thereof. However, since the seal portion is strengthened by directly bonding the films together, it is preferable that the decorative print layer is not provided on the film overlapping surface constituting the seal portion. Specifically, the decorative print layer 4 includes an upper edge, a lower edge, a first side edge (a side edge 21a on the first side edge 21 side), and a second side edge 22 of the heat shrinkable film 3. And the boundary line 22b (hereinafter, this region may be referred to as a specific region). The decorative print layer 4 may be provided in the entire specific area, or may be provided in a part of the specific area. Preferably, as illustrated, the decorative print layer 4 is provided in a part of the specific area.
For example, in the illustrated example, a decorative print layer 4 is provided in a part of the specific area, and a part 39 in which the decorative print layer is not provided (hereinafter referred to as a non-decorative print part). Exists. The non-decorative printing part 39 may be formed at one place in the specific area, or may be formed at two or more independent places.

装飾印刷層4は、不透明でもよいが、好ましくは光透過性を有する。前記光透過性は、装飾印刷層4を通じて、その裏面側に設けられた色彩を視認できる性質をいう。例えば、装飾印刷層4は、例えば、その全光線透過率(JIS K7105)が50%以上、好ましくは60%以上の光透過性を有する。前記装飾印刷層4の全光線透過率は、装飾印刷層4を積層した熱収縮性フィルム3を用いて測定した値である。
装飾印刷層4の厚みは、適宜設定できるが、前記光透過性を有する装飾印刷層4の厚みは、例えば、0.5μm〜5μmである。
The decorative print layer 4 may be opaque, but preferably has light transparency. The light transmissive property refers to the property that the color provided on the back side of the decorative printed layer 4 can be visually recognized. For example, the decorative print layer 4 has a light transmittance of, for example, a total light transmittance (JIS K7105) of 50% or more, preferably 60% or more. The total light transmittance of the decorative print layer 4 is a value measured using the heat-shrinkable film 3 on which the decorative print layer 4 is laminated.
Although the thickness of the decorative print layer 4 can be set as appropriate, the thickness of the decorative print layer 4 having light transmittance is, for example, 0.5 μm to 5 μm.

装飾印刷層4は、複数の板状薄片と、バインダー樹脂と、を含み、必要に応じて、各種の添加剤を含む。装飾印刷層4は、複数の板状薄片が、前記バインダー樹脂中においてその装飾印刷層4の面方向に略均一に分散している。このように面方向に板状薄片が略均一に分散していることにより、熱収縮性筒状ラベルを熱収縮させた後も板状薄片の凹凸が消失し難くなる。なお、複数の板状薄片は、装飾印刷層4の厚み方向にも略均一に分散していることが好ましいが、厚み方向においては、不均一であってもよい。   The decorative print layer 4 includes a plurality of plate-shaped flakes and a binder resin, and includes various additives as necessary. In the decorative print layer 4, a plurality of plate-like flakes are dispersed substantially uniformly in the surface direction of the decorative print layer 4 in the binder resin. As described above, since the plate-like flakes are substantially uniformly dispersed in the surface direction, the unevenness of the plate-like flakes hardly disappears even after the heat-shrinkable cylindrical label is heat-shrinked. The plurality of plate-like flakes are preferably dispersed substantially uniformly in the thickness direction of the decorative print layer 4, but may be non-uniform in the thickness direction.

板状薄片7は、図7に示すように、金属又は半金属を含む板状のものであって、その一方面に複数の凹凸を有する板状である。前記凹凸は、板状薄片7の固有の形状でもよく、或いは、板状薄片7に付加された何らかの物質に基づいていてもよいが、好ましくは、板状薄片7の固有の形状である。
前記金属としては、金、銀、銅、チタン、アルミニウム、錫、亜鉛、クロム、ニッケル、マグネシウム、ガリウムなどが挙げられる。半金属は、金属と非金属の中間的性質を示すものをいう。半金属としては、例えば、ケイ素、ビスマス、ゲルマニウムなどが挙げられる。板状薄片は、金属、半金属若しくはこれらの2種以上の複合物、又は、これらの金属、半金属若しくは複合金の酸化物、硫化物、酸化炭化物若しくは酸化窒化物などから形成されている。板状薄片は、好ましくは金属から形成され、より好ましくはアルミニウムから形成される。板状薄片は、板状の薄いものであり、その製法は、特に限定されないが、容易に凹凸を形成できることから、蒸着膜を砕いた蒸着薄片であることが好ましく、金属蒸着膜を砕いたものがより好ましく、凹凸形状が付与された金属蒸着膜を砕いた蒸着薄片がさらに好ましい。
前記板状薄片7は、前記金属など又は金属の酸化物などからなるが、その表面が薄く透明な樹脂層などの被覆層によって被覆されていてもよい。ただし、板状薄片7が前記被覆層で被覆されている場合でも、前記凹凸形状は板状薄片7に基づく(つまり、前記複数の凹凸は、板状薄片7の固有の形状である)ことが好ましい。
As shown in FIG. 7, the plate-like thin piece 7 is a plate-like material containing a metal or a semimetal, and has a plate shape having a plurality of irregularities on one surface thereof. The unevenness may be a shape unique to the plate-like thin piece 7 or may be based on some substance added to the plate-like thin piece 7, but is preferably a shape unique to the plate-like thin piece 7.
Examples of the metal include gold, silver, copper, titanium, aluminum, tin, zinc, chromium, nickel, magnesium, and gallium. A metalloid refers to an intermediate property between metal and nonmetal. Examples of the semimetal include silicon, bismuth, and germanium. The plate-like flakes are made of metal, metalloid, or a composite of two or more of these, or an oxide, sulfide, oxycarbide, or oxynitride of these metal, metalloid, or composite gold. The plate-like flakes are preferably made of metal, more preferably aluminum. The plate-shaped flake is a thin plate-like material, and its production method is not particularly limited, but since it can easily form irregularities, it is preferably a vapor-deposited flake obtained by crushing a vapor-deposited film, and a metal vapor-deposited film is crushed Is more preferable, and vapor deposition flakes obtained by crushing a metal vapor deposition film provided with an uneven shape are more preferable.
The plate-like flake 7 is made of the metal or the like, or a metal oxide, but the surface thereof may be covered with a coating layer such as a transparent resin layer. However, even when the plate-like thin piece 7 is covered with the coating layer, the uneven shape may be based on the plate-like thin piece 7 (that is, the plurality of unevenness is a shape unique to the plate-like thin piece 7). preferable.

板状薄片7の厚みは、特に限定されず、例えば、10nm〜1000nmであり、好ましくは、50nm〜800nmである。
板状薄片7の平面視形状は、略矩形状、鱗片状、略円形状などの定形でもよく、不定形でもよい。図示例の板状薄片7は、不定形であり、従って、装飾印刷層4は、様々な平面視形状の板状薄片7が含まれている。
板状薄片7の面積(平面視形状の面積)は、特に限定されず、例えば、5平方μm〜2000平方μmである。なお、不定形な板状薄片7においては、前記面積範囲に含まれないものもある。
板状薄片7のアスペクト比は、特に限定されず、例えば、2〜1000である。
ただし、前記アスペクト比は、[板状薄片の平面視に於ける最大長さ/板状薄片の厚み]で求められる。
また、板状薄片7の平面視に於ける最大長さ:幅長さは、例えば、1:1〜10:1である。板状薄片7の平面視における最大長さは、板状薄片7をその一方面に対する垂線方向から見て、最大幅となる箇所での長さをいう(図7に、符号W1で示す)。板状薄片7の平面視における幅長さは、板状薄片7の面内で前記最大長さの箇所に対して直交する方向における板状薄片の最大長さをいう(図7に、符号W2で示す)。
The thickness of the plate-shaped thin piece 7 is not specifically limited, For example, it is 10 nm-1000 nm, Preferably, it is 50 nm-800 nm.
The planar view shape of the plate-like thin piece 7 may be a regular shape such as a substantially rectangular shape, a scale shape, or a substantially circular shape, or may be an irregular shape. The plate-like flakes 7 in the illustrated example are indeterminate, and therefore the decorative print layer 4 includes the plate-like flakes 7 having various shapes in plan view.
The area (area in plan view) of the plate-like thin piece 7 is not particularly limited, and is, for example, 5 square μm to 2000 square μm. In addition, in the irregular plate-shaped thin piece 7, there are some which are not included in the said area range.
The aspect ratio of the plate-shaped flake 7 is not particularly limited and is, for example, 2 to 1000.
However, the aspect ratio is obtained by [maximum length in plan view of plate-like flakes / thickness of plate-like flakes].
Moreover, the maximum length: width length in the planar view of the plate-shaped thin piece 7 is 1: 1 to 10: 1, for example. The maximum length of the plate-like thin piece 7 in a plan view refers to the length at the location where the plate-like thin piece 7 becomes the maximum width when viewed from the direction perpendicular to the one surface (indicated by reference numeral W1 in FIG. 7). The width in the plan view of the plate-like thin piece 7 is the maximum length of the plate-like thin piece in the direction orthogonal to the location of the maximum length in the plane of the plate-like thin piece 7 (refer to W2 in FIG. 7). ).

板状薄片7は、少なくとも一方面に複数の凹凸が形成されている。従って、板状薄片7は、例えば、図8(b)及び図9(b)に示すように、その一方面及び反対面の双方面に複数の凹凸が形成されていてもよく、或いは、図8(c)に示すように、その一方面のみに複数の凹凸が形成されていてもよい。
凹凸は、相対的は概念であり、一方面に形成された凹部72の底を基準面とした場合、それよりも突出している箇所が凸部71である。図8(b)及び図9(b)のように、双方面に凹凸が形成されている場合において、一方面の凸部71に対応して反対面において凹部74が形成され且つ一方面の凹部72に対応して反対面において凸部73が形成されていてもよく、或いは、特に図示しないが、一方面の凸部71と反対面の凹部74が対応していなくてもよい。
The plate-shaped thin piece 7 has a plurality of irregularities formed on at least one surface. Accordingly, the plate-like thin piece 7 may have a plurality of irregularities formed on both one side and the opposite side as shown in FIGS. 8B and 9B, for example. As shown in FIG. 8 (c), a plurality of irregularities may be formed only on one surface thereof.
The unevenness is a concept in terms of relatives, and when the bottom of the concave portion 72 formed on one surface is used as a reference surface, the portion that protrudes more than that is the convex portion 71. As shown in FIG. 8B and FIG. 9B, when the concave and convex portions are formed on both surfaces, the concave portion 74 is formed on the opposite surface corresponding to the convex portion 71 on the one surface and the concave portion on the one surface. The convex portion 73 may be formed on the opposite surface corresponding to 72, or the convex portion 71 on one surface and the concave portion 74 on the opposite surface may not correspond to each other, although not particularly illustrated.

凸部71の平面視形状は、特に限定されず、例えば、図8(a)に示すように、平面視略円形状でもよく、図9(a)に示すように、平面視略矩形状でもよく、その他、図示しないが、所望の形状でもよい。なお、本明細書において、略円形状は、真円状の他、楕円状及びオーバル状を含む意味であり、略矩形状は、長方形状及び正方形状の他、少なくとも1つの角が直角でない四角形を含む意味である。
板状薄片7の複数の凸部71は、規則的に配列されていてもよく、不規則に配列されていてもよいが、好ましくは、規則的に配列される。
また、複数の板状薄片7は、その凸部71の平面視形状が同じでもよいし、異なっていてもよい。凸部71の平面視形状が異なる複数の板状薄片7は、例えば、平面視略円形状の凸部を有する板状薄片と、平面視略矩形状の凸部を有する板状薄片とが混在している場合などが挙げられる。
The planar view shape of the convex portion 71 is not particularly limited, and may be, for example, a substantially circular shape in plan view as shown in FIG. 8A, or a substantially rectangular shape in plan view as shown in FIG. In addition, although not shown, a desired shape may be used. In the present specification, the substantially circular shape means an elliptical shape and an oval shape in addition to a perfect circular shape, and the substantially rectangular shape is a rectangular shape and a square shape, and at least one corner is not a right angle. It means to include.
The plurality of convex portions 71 of the plate-like thin piece 7 may be regularly arranged or irregularly arranged, but is preferably arranged regularly.
Moreover, the planar view shape of the convex part 71 may be the same, and the some plate-shaped thin piece 7 may differ. The plurality of plate-like flakes 7 having different projections 71 in plan view include, for example, a mixture of plate-like slices having projections that are substantially circular in plan view and plate-like slices having projections that are substantially rectangular in plan view. This is the case.

前記板状薄片7は、表面に凹凸が形成され且つその表面に剥離剤が塗布された支持板の表面に、アルミニウムを蒸着し、そのアルミニウム蒸着膜を支持板の表面から剥離した後、任意に粉砕することにより得ることができる。なお、得られたアルミニウム蒸着膜には、前記支持板の表面の凹に対応する凸部と、支持板の表面の凸に対応する凹部が形成され、そのアルミニウム蒸着膜を粉砕することにより、上記凸部71及び凹部72を有する板状薄片7が得られる。
前記アルミニウムに代えて、任意の金属又は半金属を用いることにより、アルミニウム以外の金属又は半金属の蒸着膜を得ることができ、また、必要に応じて、酸素含有ガスなどの反応ガスと共に前記金属などを蒸着することにより、金属又は半金属の酸化物などからなる蒸着膜を得ることができる。これを粉砕することにより、金属又は半金属の酸化物や硫化物からなる板状薄片、アルミニウム以外の金属又は半金属からなる板状薄片を形成できる。
The plate-like flake 7 is formed by depositing aluminum on the surface of the support plate having irregularities formed on the surface and having a release agent applied on the surface, and then separating the aluminum vapor deposition film from the surface of the support plate. It can be obtained by grinding. In the obtained aluminum vapor deposition film, a convex portion corresponding to the concave portion on the surface of the support plate and a concave portion corresponding to the convex portion on the surface of the support plate are formed. The plate-shaped thin piece 7 which has the convex part 71 and the recessed part 72 is obtained.
By using any metal or metalloid instead of aluminum, it is possible to obtain a metal or metalloid vapor deposition film other than aluminum, and, if necessary, the metal together with a reaction gas such as an oxygen-containing gas. By evaporating the above, it is possible to obtain a deposited film made of a metal or metalloid oxide. By pulverizing this, a plate-shaped flake made of a metal or metalloid oxide or sulfide, or a plate-shaped flake made of a metal other than aluminum or a metalloid can be formed.

前記バインダー樹脂としては、特に限定されないが、例えば、アクリル樹脂、ウレタン樹脂、ニトロセルロースやセルロース・アセテート・ブチレートなどのセルロース系樹脂、塩化ビニル樹脂、酢酸ビニル樹脂、ポリエステル樹脂などの熱可塑性樹脂などが挙げられる。バインダー樹脂は、1種単独で又は2種以上を併用できる。好ましくは、ウレタン樹脂及びセルロース系樹脂の少なくとも何れであり、より好ましくは、ガラス転移温度が0度以下のウレタン樹脂が用いられる。
前記添加剤として、例えば、顔料などの着色剤、沈降防止剤、滑剤、分散安定剤、充填剤、酸化防止剤、紫外線吸収剤、帯電防止剤、難燃剤などが挙げられる。
The binder resin is not particularly limited, and examples thereof include acrylic resins, urethane resins, cellulose resins such as nitrocellulose and cellulose acetate butyrate, thermoplastic resins such as vinyl chloride resins, vinyl acetate resins, and polyester resins. Can be mentioned. Binder resin can be used alone or in combination of two or more. Preferably, it is at least one of a urethane resin and a cellulose resin, and more preferably, a urethane resin having a glass transition temperature of 0 ° C. or less is used.
Examples of the additive include colorants such as pigments, anti-settling agents, lubricants, dispersion stabilizers, fillers, antioxidants, ultraviolet absorbers, antistatic agents, and flame retardants.

前記板状薄片7の含有量は、特に限定されないが、余りに少ないとホログラム調の外観を十分に有さないことから、装飾印刷層4の全体を100質量%とした場合に、1質量%以上が好ましく、3質量%以上がより好ましく、5質量%以上がさらに好ましい。
また、前記板状薄片7の含有量の上限は、特に限定されず、装飾印刷層4の全体を100質量%とした場合に、例えば、50質量%である。もっとも、余りに多くの板状薄片7を含有させると、装飾印刷層の光透過性が低下するので、上記光透過性を有する装飾印刷層4を形成する場合には、板状薄片7の含有量は、装飾印刷層4の全体を100質量%とした場合に、例えば、30質量%以下であり、好ましくは20質量%以下である。
The content of the plate-like flakes 7 is not particularly limited, but if it is too small, it does not have a hologram-like appearance sufficiently. Therefore, when the total decorative printing layer 4 is 100% by mass, it is 1% by mass or more. Is preferably 3% by mass or more, and more preferably 5% by mass or more.
Moreover, the upper limit of content of the said plate-shaped flake 7 is not specifically limited, For example, when the whole decoration printing layer 4 is 100 mass%, it is 50 mass%. However, if too much plate-like flakes 7 are contained, the light transmittance of the decorative print layer is lowered. Therefore, when the decorative print layer 4 having the light transmittance is formed, the content of the plate-like flakes 7 is included. Is, for example, 30% by mass or less, preferably 20% by mass or less, when the total decorative printing layer 4 is 100% by mass.

前記装飾印刷層4の形成方法は、特に限定されず、装飾印刷層形成材料を、公知の印刷法、塗工法などによって熱収縮性フィルム3に塗布し、固化させることによって形成できる。
装飾印刷層形成材料は、前記板状薄片7、バインダー樹脂及び任意の添加剤を含み、必要に応じてこれらを溶解させる溶剤を含んでいてもよい。装飾印刷層4はこのような形成材料を塗布した後、乾燥固化して形成され得る。
前記溶剤は、特に限定されず、酢酸エチル、酢酸プロピル、酢酸ブチルなどのエステル類;メタノール、エタノール、イソプロピルアルコール、ブタノールなどのアルコール類;アセトン、メチルエチルケトンなどのケトン類;トルエンなどの炭化水素類;これらの混合溶媒などが挙げられる。
所望の領域に容易に装飾印刷層4を形成できることから、装飾印刷層形成材料を公知の印刷法にて塗布し、装飾印刷層4を形成することが好ましい。
The method for forming the decorative print layer 4 is not particularly limited, and the decorative print layer forming material can be formed by applying the decorative print layer forming material to the heat-shrinkable film 3 by a known printing method, coating method or the like and solidifying it.
The decorative printed layer forming material contains the plate-like flakes 7, the binder resin, and optional additives, and may contain a solvent for dissolving them as necessary. The decorative printed layer 4 can be formed by applying such a forming material and then drying and solidifying it.
The solvent is not particularly limited, and esters such as ethyl acetate, propyl acetate, and butyl acetate; alcohols such as methanol, ethanol, isopropyl alcohol, and butanol; ketones such as acetone and methyl ethyl ketone; hydrocarbons such as toluene; These mixed solvents are mentioned.
Since the decorative print layer 4 can be easily formed in a desired region, it is preferable to form the decorative print layer 4 by applying a decorative print layer forming material by a known printing method.

(デザイン印刷層)
デザイン印刷層5は、商品名、絵柄、成分表示、注意書きなどの各種デザイン表示が表された印刷層である。デザイン印刷層5は、従来公知の印刷インキを用いて形成できる。なお、図2及び図3において、デザイン印刷層を、塗潰しを含んだ細斜線で示している。デザイン印刷層5は、その全部又は一部が光透過性を有していてもよく、又は、全部が不透明でもよい。なお、デザイン印刷層5の光透過性は、上記装飾印刷層4の光透過性と同義である(上記装飾印刷層4の光透過性の欄の説明において、装飾印刷層4をデザイン印刷層5に読み替えるものとする)。
(Design printing layer)
The design print layer 5 is a print layer on which various design displays such as a product name, a pattern, a component display, and a notice are displayed. The design print layer 5 can be formed using a conventionally known printing ink. In FIG. 2 and FIG. 3, the design print layer is indicated by a thin oblique line including filling. The design printing layer 5 may be entirely or partially light transmissive, or may be entirely opaque. The light transmittance of the design print layer 5 is synonymous with the light transmittance of the decorative print layer 4 (in the description of the light transmittance column of the decorative print layer 4, the decorative print layer 4 is referred to as the design print layer 5). To be read as).

デザイン印刷層5は、デザイン表示を見せたい領域に設けられる。従って、デザイン印刷層5は、熱収縮性フィルム3の所望の領域に設けられる。デザイン印刷層5は、熱収縮性フィルム3の全体に設けられていてもよいが、上記装飾印刷層4と同様の理由から特定領域内の全体又は一部分に設けられる。
デザイン印刷層5は、熱収縮性フィルム3の裏面側に設けられていてもよく、熱収縮性フィルム3の表面側に設けられていてもよい。デザインが傷付き難くなることから、デザイン印刷層5は、図2及び図3に示すように、熱収縮性フィルム3の裏面側に設けられていることが好ましい。
The design print layer 5 is provided in an area where it is desired to show the design display. Therefore, the design print layer 5 is provided in a desired region of the heat-shrinkable film 3. The design print layer 5 may be provided on the entire heat-shrinkable film 3, but for the same reason as the decorative print layer 4, it is provided on the whole or part of the specific region.
The design print layer 5 may be provided on the back surface side of the heat-shrinkable film 3 or may be provided on the front surface side of the heat-shrinkable film 3. The design printing layer 5 is preferably provided on the back surface side of the heat-shrinkable film 3 as shown in FIGS.

デザイン印刷層5が裏面側に設けられる場合において、デザイン印刷層5は、図2及び図3に示すように、(1)非装飾印刷部39における熱収縮性フィルム3の裏面に接して設けられていてもよく、或いは、(2)装飾印刷層4の裏面に接して設けられていてもよく、或いは、(3)熱収縮性フィルム3と装飾印刷層4の間に設けられていてもよい。デザイン印刷層5は、前記(1)乃至(3)から選ばれる少なくとも1つの態様により、熱収縮性フィルム3に設けられる   In the case where the design print layer 5 is provided on the back surface side, the design print layer 5 is provided in contact with the back surface of the heat-shrinkable film 3 in the non-decorative print portion 39 as shown in FIGS. Or (2) may be provided in contact with the back surface of the decorative print layer 4, or (3) may be provided between the heat-shrinkable film 3 and the decorative print layer 4. . The design print layer 5 is provided on the heat-shrinkable film 3 according to at least one aspect selected from the above (1) to (3).

前記(1)のデザイン印刷層5が非装飾印刷部39における熱収縮性フィルム3の裏面に接して設けられる場合、そのデザイン印刷層5の裏面側には、後述する背景印刷層6が設けられていてもよく(図2参照)、或いは、背景印刷層が設けられていなくてもよい(図示せず)。前記(1)の場合、非装飾印刷部39においては通常のデザイン表示(通常のデザイン表示は、ホログラム調の外観を伴わないデザイン表示。以下、同様)を視認できる。   When the design printing layer 5 of (1) is provided in contact with the back surface of the heat-shrinkable film 3 in the non-decorative printing portion 39, a background printing layer 6 described later is provided on the back surface side of the design printing layer 5. May be provided (see FIG. 2), or the background print layer may not be provided (not shown). In the case of (1), the non-decorative printing unit 39 can visually recognize a normal design display (a normal design display is a design display without a hologram-like appearance; the same applies hereinafter).

前記(2)のデザイン印刷層5が装飾印刷層4の裏面に接して設けられる場合にも、そのデザイン印刷層5の裏面側には、後述する背景印刷層6が設けられていてもよく(図2参照)、或いは、背景印刷層が設けられていなくてもよい(図示せず)。デザイン表示が綺麗に見るので、デザイン印刷層5の裏面側には背景印刷層6が設けられていることが好ましい。
ただし、(2)の態様の場合、デザイン表示を筒状ラベルの外側から視認するため、装飾印刷層4は光透過性を有するものが用いられる。前記(2)の場合、筒状ラベルの外側から見たときに、デザイン表示がホログラム調の外観を伴って視認される。前記(1)と前記(2)の態様を併用することにより、通常のデザイン表示とホログラム調の外観を伴ったデザイン表示を視認できる熱収縮性筒状ラベルを構成できる。かかる通常のデザイン表示とホログラム調の外観を伴ったデザイン表示とを併有する熱収縮性筒状ラベルは、ホログラム調の外観が際立つので好ましい。
Even when the design print layer 5 of the above (2) is provided in contact with the back surface of the decorative print layer 4, a background print layer 6 described later may be provided on the back surface side of the design print layer 5 ( 2) or a background print layer may not be provided (not shown). Since the design display is clearly seen, it is preferable that a background print layer 6 is provided on the back side of the design print layer 5.
However, in the case of the mode (2), in order to visually recognize the design display from the outside of the cylindrical label, the decorative print layer 4 having light permeability is used. In the case of (2), the design display is visually recognized with a hologram-like appearance when viewed from the outside of the cylindrical label. By using the aspects (1) and (2) in combination, a heat-shrinkable cylindrical label that can visually recognize a normal design display and a design display with a hologram-like appearance can be configured. A heat-shrinkable cylindrical label having both such a normal design display and a design display with a hologram-like appearance is preferable because the hologram-like appearance stands out.

前記(3)のデザイン印刷層5が熱収縮性フィルム3と装飾印刷層4の間に設けられている場合にも、そのデザイン印刷層5の裏面側には、後述する背景印刷層6が設けられていてもよく(図2参照)、或いは、背景印刷層が設けられていなくてもよい(図示せず)。(3)の態様の場合であって、デザイン印刷層5が光透過性を有する場合、ホログラム調の外観を伴ったデザイン表示を視認できる。もっとも、前記(2)と(3)の態様を比べると、前記(2)の態様の方が、デザイン表示がより印象強いホログラム調に見えるようになる。また、(3)の態様の場合であって、デザイン印刷層5が不透明である場合には、通常のデザイン表示を視認でき、そのデザイン表示の周辺がホログラム調に見えるようになる。
デザイン印刷層5の厚みは、特に限定されないが、例えば、0.1μm〜5μm程度である。
Even when the design print layer 5 of the above (3) is provided between the heat-shrinkable film 3 and the decorative print layer 4, a background print layer 6 described later is provided on the back side of the design print layer 5. It may be provided (see FIG. 2) or the background print layer may not be provided (not shown). In the case of the aspect (3), when the design print layer 5 has light transmittance, a design display with a hologram-like appearance can be visually recognized. Of course, when the aspects (2) and (3) are compared, the aspect (2) makes the design display look more holographic. In the case of the mode (3), when the design print layer 5 is opaque, a normal design display can be visually recognized, and the periphery of the design display can be seen as a hologram.
Although the thickness of the design print layer 5 is not specifically limited, For example, it is about 0.1 micrometer-5 micrometers.

(背景印刷層)
背景印刷層6は、無模様一色又は無模様多色の印刷層である。背景印刷層6は、不透明であることが好ましい。なお、本明細書において、不透明とは、全く光を通さない場合の他、その裏面側の表示又は色彩が若干透けて見える場合を含む意味である。
この無模様一色の印刷層としては、例えば、白色着色剤を含む印刷層(通常、この印刷層は白色を呈する)、銀色着色剤を含む印刷層(通常、銀色を呈する)、黒色着色剤を含む印刷層、白色、銀色及び黒色以外の色彩の着色剤(例えば、赤色など。以下、特定色という)を含む印刷層などが挙げられる。無模様多色の印刷層としては、例えば、無模様銀色と無模様白色が塗り分けられ又は塗重ねられた印刷層、特定色と白色、銀色又は黒色とが塗り分けられ又は塗重ねられた印刷層、特定色が2種以上塗り分けられ又は塗重ねられた印刷層、特定色が2種以上と白色、銀色及び黒色から選ばれる2種以上とが塗り分けられ又は塗重ねられた印刷層などが挙げられる。
(Background printing layer)
The background print layer 6 is a non-pattern single-color or non-pattern multi-color print layer. The background print layer 6 is preferably opaque. In the present specification, the term “opaque” means not only the case where light is not transmitted at all, but also the case where the display or color on the back side is slightly transparent.
As this patternless one-color print layer, for example, a print layer containing a white colorant (usually this print layer exhibits white), a print layer containing a silver colorant (usually silver), and a black colorant And a printing layer containing a colorant having a color other than white, silver and black (for example, red, etc., hereinafter referred to as a specific color). Examples of the non-patterned multi-color printing layer include, for example, a printing layer in which a non-patterned silver color and a non-patterned white are separately applied or overlaid, and a specific color and white, silver or black are separately or overprinted. Layers, printing layers in which two or more specific colors are painted or overlaid, printing layers in which two or more specific colors are coated with two or more selected from white, silver and black, etc. Is mentioned.

背景印刷層6は、好ましくは、装飾印刷層4の裏面に積層される。背景印刷層6は、装飾印刷層4の裏面全体に重ねて設けられていてもよく、装飾印刷層4の裏面の一部分に設けられていてもよい。好ましくは、背景印刷層6は、少なくとも装飾印刷層4の裏面全体に重ねて設けられる。   The background print layer 6 is preferably laminated on the back surface of the decorative print layer 4. The background print layer 6 may be provided so as to overlap the entire back surface of the decorative print layer 4, or may be provided on a part of the back surface of the decorative print layer 4. Preferably, the background print layer 6 is provided so as to overlap at least the entire back surface of the decorative print layer 4.

さらに、装飾印刷層4の裏面に背景印刷層6が設けられる場合、その背景印刷層6は、デザイン印刷層5が設けられた領域及びデザイン印刷層5が設けられていない領域の何れか一方又は双方に設けられていてもよいが、少なくともデザイン印刷層5が設けられていない領域において装飾印刷層4の裏面に背景印刷層6が設けられている領域を有する(装飾印刷層4と背景印刷層6が重なる領域を有する)ことが好ましい。この重なる領域においては、後述するように、装飾印刷層4に背景印刷層6が相乗して、優れたホログラム調の外観を呈し、かかる効果をより顕著に奏することから、その背景印刷層6が白色着色剤を含む印刷層であることがより好ましく、白色顔料を含む白色印刷層であることが特に好ましい。
また、背景印刷層6は、非装飾印刷部39における熱収縮性フィルム3の裏面の全部又は一部に対応して積層されていてもよい。非装飾印刷部39に対応して背景印刷層6を設ける場合、その非装飾印刷部39における熱収縮性フィルム3の裏面の全部又は一部には、上記デザイン印刷層5が設けられていることが好ましい。なお、前記非装飾印刷部39に対応するフィルムの裏面全部にデザイン印刷層5が設けられる場合には、そのデザイン印刷層5の裏面に背景印刷層6が設けられ、裏面の一部にデザイン印刷層5が設けられる場合には、そのデザイン印刷層5の裏面及びフィルムの裏面に背景印刷層6が設けられることが好ましい。もっとも、デザイン印刷層が全く設けられていない非装飾印刷部のフィルムの裏面に背景印刷層を設けてもよい(図示せず)。
Furthermore, when the background print layer 6 is provided on the back surface of the decorative print layer 4, the background print layer 6 is either one of an area where the design print layer 5 is provided and an area where the design print layer 5 is not provided. Although it may be provided on both sides, at least an area where the design print layer 5 is not provided has a region where the background print layer 6 is provided on the back surface of the decorative print layer 4 (the decorative print layer 4 and the background print layer). 6 has an overlapping region). In this overlapping region, as will be described later, the background print layer 6 synergizes with the decorative print layer 4 to exhibit an excellent hologram-like appearance, and this effect is more prominent. A printing layer containing a white colorant is more preferred, and a white printing layer containing a white pigment is particularly preferred.
The background print layer 6 may be laminated corresponding to all or part of the back surface of the heat-shrinkable film 3 in the non-decorative print portion 39. When the background print layer 6 is provided corresponding to the non-decorative printing portion 39, the design print layer 5 is provided on all or part of the back surface of the heat-shrinkable film 3 in the non-decorative printing portion 39. Is preferred. When the design printing layer 5 is provided on the entire back surface of the film corresponding to the non-decorative printing portion 39, the background printing layer 6 is provided on the back surface of the design printing layer 5, and the design printing is performed on a part of the back surface. When the layer 5 is provided, the background print layer 6 is preferably provided on the back surface of the design print layer 5 and the back surface of the film. But you may provide a background printing layer in the back surface of the film of the non-decorative printing part in which the design printing layer is not provided at all (not shown).

前記背景印刷層6は、例えば、白色顔料などの着色剤を含む着色インキをベタ状に又は適宜な箇所にスポット的に塗布することにより形成できる。白色顔料としては、例えば、酸化チタン、亜鉛華、炭酸カルシウム、クレー、アルミナホワイトなどを用いることができるが、装飾印刷層4に背景印刷層6が相乗して特に優れたホログラム調の外観を呈することから、白色顔料は酸化チタンを含むことが好ましい。例えば、前記白色着色剤を含む印刷層は、その印刷層全体を100質量%とした場合に、酸化チタンを30質量%〜80質量%含んでいるものが好ましい。
背景印刷層6の厚みは、特に限定されないが、例えば、1μm〜5μm程度である。
The background print layer 6 can be formed, for example, by applying a color ink containing a colorant such as a white pigment in a solid form or in a spot-like manner at an appropriate location. As the white pigment, for example, titanium oxide, zinc white, calcium carbonate, clay, alumina white, and the like can be used. The background print layer 6 and the background print layer 6 are synergistic to exhibit a particularly excellent hologram-like appearance. Therefore, the white pigment preferably contains titanium oxide. For example, the print layer containing the white colorant preferably contains 30% by mass to 80% by mass of titanium oxide when the entire print layer is 100% by mass.
Although the thickness of the background printing layer 6 is not specifically limited, For example, it is about 1 micrometer-5 micrometers.

(熱収縮性筒状ラベル)
ラベル形成用基材2の第1側端部21の表面及び第2側端部22の裏面の少なくともいずれか一方に接着剤、粘着剤又は溶剤(以下、接着剤、粘着剤又は溶剤を「接着剤等」と記す場合がある)を塗布し、ラベル形成用基材2を丸めて筒状にし、第1側端部21の表面に第2側端部22の裏面に重ね合わせ、その重ね合わせ部分の全部又は一部を前記接着剤等を介して接着してシール部を形成することにより、図4乃至図6に示すような熱収縮性筒状ラベル1が得られる。なお、溶剤は、熱収縮性フィルム3が溶剤接着可能な材質の場合に用いることができる。前記第1及び第2側端部21,22の重ね合わせ構成からなるシール部の重ね合わせ面(第1側端部21の表面及び第2側端部22の裏面)は、何れもフィルム面であるため、強固に接着したシール部を構成できる。
上記熱収縮性筒状ラベル1は、例えば、熱収縮性フィルム3を筒状に形成した筒状フィルムの裏面に、順に、デザイン印刷層5、装飾印刷層4及び背景印刷層6が設けられている領域を有する。
本発明の熱収縮性筒状ラベル1は、様々な被着体に装着して使用される。被着体は、特に限定されないが、代表的には、飲料、調味料、化粧品、シャンプーなどが収納された容器である。特に、化粧品などの比較的高額な商品に、本発明の熱収縮性筒状ラベル1を装着することにより、その高額な商品のイメージに合致し、商品価値を高めることができる。容器の材質は、特に限定されず、代表的にはポリエチレンテレフタレート製容器などの比較的薄肉の可撓性を有する合成樹脂製容器を例示できるが、ガラス製、金属製などであってもよい。
熱収縮性筒状ラベル1を被着体に被せた後、加熱することにより、熱収縮性筒状ラベル1が熱収縮して被着体に装着される。
(Heat-shrinkable cylindrical label)
Adhesive, pressure-sensitive adhesive or solvent (hereinafter referred to as adhesive, pressure-sensitive adhesive or solvent) is adhered to at least one of the front surface of the first side end portion 21 and the back surface of the second side end portion 22 of the substrate 2 for label formation. The label-forming substrate 2 is rolled into a cylindrical shape, and is superposed on the surface of the first side end portion 21 on the back surface of the second side end portion 22. The heat-shrinkable cylindrical label 1 as shown in FIGS. 4 to 6 is obtained by forming a seal portion by bonding all or part of the portion through the adhesive or the like. In addition, a solvent can be used when the heat-shrinkable film 3 is a material that can be bonded to a solvent. The overlapping surfaces (the surface of the first side end portion 21 and the back surface of the second side end portion 22) of the seal portion composed of the overlapping configuration of the first and second side end portions 21 and 22 are both film surfaces. As a result, a tightly bonded seal portion can be configured.
In the heat-shrinkable cylindrical label 1, for example, a design print layer 5, a decorative print layer 4, and a background print layer 6 are provided in this order on the back surface of a tubular film in which the heat-shrinkable film 3 is formed into a tubular shape. Have an area.
The heat-shrinkable cylindrical label 1 of the present invention is used by being attached to various adherends. The adherend is not particularly limited, but is typically a container in which beverages, seasonings, cosmetics, shampoos, and the like are stored. In particular, by attaching the heat-shrinkable cylindrical label 1 of the present invention to a relatively expensive product such as cosmetics, the product value can be increased in accordance with the image of the expensive product. The material of the container is not particularly limited. Typically, a relatively thin flexible synthetic resin container such as a polyethylene terephthalate container can be exemplified, but it may be made of glass or metal.
After covering the adherend with the heat-shrinkable cylindrical label 1, the heat-shrinkable tubular label 1 is thermally contracted and attached to the adherend.

図10及び図11は、容器に熱収縮性筒状ラベルが熱収縮装着されたラベル付き容器を示している。
図10において、容器9は、下方から順に、胴部91と、肩部92と、蓋部93と、を有する。この胴部91は、外周長が大きい2つの大径部911,911と、その2つの大径部911,911の間に外周長が小さい小径部912と、を有する。また、肩部92は、上方に向かうに従って外周長が次第に小さくなるように形成されている。図10の容器9の胴部91及び肩部92の横断面形状は、略円形状であるが、その横断面形状が略矩形状などでもよい。
大径部911から小径部912の間における胴部91の外形は、三次元曲面状を成しており、この部分は、三次元曲面部となっている。肩部92の外形も三次元曲面状を成しており、この肩部92も三次元曲面部となっている。
図10(a)のラベル付き容器11において、熱収縮性筒状ラベル1は、大径部911及び小径部912を含む胴部91に熱収縮装着されている。従って、熱収縮性筒状ラベル1の装飾印刷層4が設けられた領域が、容器9の三次元曲面部に密着して装着されている。
図10(b)のラベル付き容器12において、熱収縮性筒状ラベル1は、大径部911及び小径部912を含む胴部91及び肩部92に熱収縮装着されている。従って、熱収縮性筒状ラベル1の装飾印刷層4が設けられた領域が、容器9の三次元曲面部に密着して装着されている。
10 and 11 show a labeled container in which a heat-shrinkable cylindrical label is heat-shrink mounted on the container.
In FIG. 10, the container 9 includes a trunk portion 91, a shoulder portion 92, and a lid portion 93 in order from the bottom. The body portion 91 includes two large diameter portions 911 and 911 having a large outer peripheral length, and a small diameter portion 912 having a small outer peripheral length between the two large diameter portions 911 and 911. Further, the shoulder portion 92 is formed so that the outer peripheral length gradually decreases as it goes upward. Although the cross-sectional shape of the trunk | drum 91 and the shoulder part 92 of the container 9 of FIG. 10 is substantially circular shape, the cross-sectional shape may be substantially rectangular shape.
The outer shape of the body portion 91 between the large diameter portion 911 and the small diameter portion 912 has a three-dimensional curved surface shape, and this portion is a three-dimensional curved surface portion. The outer shape of the shoulder 92 is also a three-dimensional curved surface, and the shoulder 92 is also a three-dimensional curved surface.
In the container 11 with the label of FIG. 10A, the heat-shrinkable cylindrical label 1 is heat-shrinkably attached to a body portion 91 including a large-diameter portion 911 and a small-diameter portion 912. Therefore, the region provided with the decorative print layer 4 of the heat-shrinkable cylindrical label 1 is attached in close contact with the three-dimensional curved surface portion of the container 9.
In the labeled container 12 in FIG. 10B, the heat-shrinkable cylindrical label 1 is heat-shrinkably mounted on the body 91 and the shoulder 92 including the large-diameter portion 911 and the small-diameter portion 912. Therefore, the region provided with the decorative print layer 4 of the heat-shrinkable cylindrical label 1 is attached in close contact with the three-dimensional curved surface portion of the container 9.

図11において、容器9は、下方から順に、胴部91と、肩部92と、蓋部93と、を有する。この胴部91は、直胴状(直胴状は、上下方向において、その外周長が殆ど変わらない形状)である。また、肩部92は、上方に向かうに従って外周長が次第に小さくなり、肩部92は、三次元曲面部となっている。図11の容器9の胴部91及び肩部92の横断面形状は、略円形状であるが、その横断面形状が略矩形状などでもよい。
図11(a)のラベル付き容器13において、熱収縮性筒状ラベル1は、胴部91及び肩部92に熱収縮装着されている。従って、熱収縮性筒状ラベル1の装飾印刷層4が設けられた領域が、容器9の三次元曲面部に密着して装着されている。
図11(b)のラベル付き容器14において、熱収縮性筒状ラベル1は、胴部91のみに熱収縮装着されている。従って、このラベル付き容器14においては、熱収縮性筒状ラベル1が容器9の三次元曲面部には装着されていない。
In FIG. 11, the container 9 includes a trunk portion 91, a shoulder portion 92, and a lid portion 93 in order from the bottom. The body portion 91 has a straight body shape (a straight body shape has a shape in which the outer circumferential length hardly changes in the vertical direction). Further, the shoulder portion 92 gradually decreases in outer peripheral length as it goes upward, and the shoulder portion 92 is a three-dimensional curved surface portion. Although the cross-sectional shape of the trunk | drum 91 and the shoulder part 92 of the container 9 of FIG. 11 is a substantially circular shape, the cross-sectional shape may be a substantially rectangular shape.
In the labeled container 13 in FIG. 11A, the heat-shrinkable cylindrical label 1 is heat-shrinkably attached to the body portion 91 and the shoulder portion 92. Therefore, the region provided with the decorative print layer 4 of the heat-shrinkable cylindrical label 1 is attached in close contact with the three-dimensional curved surface portion of the container 9.
In the labeled container 14 of FIG. 11B, the heat-shrinkable cylindrical label 1 is heat-shrinkably attached only to the body 91. Therefore, in this labeled container 14, the heat-shrinkable cylindrical label 1 is not attached to the three-dimensional curved surface portion of the container 9.

本発明の熱収縮性筒状ラベル1は、その外側から装飾印刷層4を視認でき、虹色の如きホログラム調の外観を有する。特に、装飾印刷層4が光透過性を有し且つその装飾印刷層4の裏面側に設けられた背景印刷層6が白色着色剤を含む印刷層である場合には、白色着色剤が装飾印刷層4を透過した光をより多く反射するので、装飾印刷層4のホログラム調外観に白色感が加わり、両層が重なっている範囲においては、優れたホログラム調の外観を有する。このホログラム調の外観は、熱収縮性筒状ラベル1を熱収縮させる前及び熱収縮させた後も同様に有する。本発明の熱収縮性筒状ラベル1が熱収縮させた後もホログラム調の外観を有する理由は、明確ではないが、本発明者らは、熱や熱収縮性フィルムの収縮応力によって板状薄片7の凹凸が消失し難いためと推定している。
また、本発明のラベル付き容器11乃至14は、熱収縮性筒状ラベル1のホログラム調の外観により、装飾性に優れている。特に、三次元曲面部を含んで熱収縮性筒状ラベル1が装着されているラベル付き容器11乃至13は、装飾印刷層4の設けられた領域が三次元曲面状を成し、見る角度によって色彩が大きく変化するホログラム調の外観を呈するので好ましい。
The heat-shrinkable cylindrical label 1 of the present invention can visually recognize the decorative print layer 4 from the outside, and has a rainbow-like hologram appearance. In particular, when the decorative print layer 4 is light transmissive and the background print layer 6 provided on the back side of the decorative print layer 4 is a print layer containing a white colorant, the white colorant is decoratively printed. Since more light transmitted through the layer 4 is reflected, a white feeling is added to the hologram-like appearance of the decorative print layer 4, and the hologram-like appearance is excellent in the range where both layers overlap. This hologram-like appearance is also present before and after the heat-shrinkable cylindrical label 1 is heat-shrinked. Although the reason why the heat-shrinkable cylindrical label 1 of the present invention has a hologram-like appearance even after heat-shrinking is not clear, the present inventors have not been able to obtain plate-like flakes due to heat or shrinkage stress of the heat-shrinkable film. It is estimated that the unevenness of 7 is difficult to disappear.
Further, the labeled containers 11 to 14 of the present invention are excellent in decorativeness due to the hologram-like appearance of the heat-shrinkable cylindrical label 1. In particular, in the labeled containers 11 to 13 including the three-dimensional curved surface portion to which the heat-shrinkable cylindrical label 1 is attached, the region provided with the decorative printing layer 4 forms a three-dimensional curved surface, and depends on the viewing angle. This is preferable because it has a hologram-like appearance in which the color changes greatly.

1 熱収縮性筒状ラベル
2 基材
3 熱収縮性フィルム
4 装飾印刷層
5 デザイン印刷層
6 背景印刷層(白色の印刷層)
7 板状薄片
9 容器
11,12,13,14 ラベル付き容器
DESCRIPTION OF SYMBOLS 1 Heat-shrinkable cylindrical label 2 Base material 3 Heat-shrinkable film 4 Decoration printing layer 5 Design printing layer 6 Background printing layer (white printing layer)
7 Plate-shaped flake 9 Container 11, 12, 13, 14 Container with label

Claims (4)

  1. 熱収縮性フィルムの裏面が内側となるように筒状に形成された筒状フィルムと、
    前記筒状フィルムの表面側及び裏面側の少なくとも一方側に設けられた装飾印刷層と、を有し、
    前記装飾印刷層が、金属又は半金属を含み且つ一方面に複数の凹凸を有する板状薄片を含む、熱収縮性筒状ラベル。
    A cylindrical film formed in a cylindrical shape so that the back side of the heat-shrinkable film is inside,
    A decorative printing layer provided on at least one side of the front side and the back side of the tubular film,
    The heat-shrinkable cylindrical label, wherein the decorative print layer includes a plate-shaped flake containing a metal or a semimetal and having a plurality of irregularities on one surface.
  2. 前記板状薄片が、金属蒸着薄片を含む、請求項1に記載の熱収縮性筒状ラベル。   The heat-shrinkable cylindrical label according to claim 1, wherein the plate-like flakes include metal-deposited flakes.
  3. 前記装飾印刷層が、筒状フィルムの裏面側に設けられており、その装飾印刷層の裏面側に、白色着色剤を含む背景印刷層が設けられている、請求項1または2に記載の熱収縮性筒状ラベル。   The heat according to claim 1 or 2, wherein the decorative print layer is provided on the back side of the tubular film, and a background print layer containing a white colorant is provided on the back side of the decorative print layer. Shrinkable cylindrical label.
  4. 三次元曲面部を有する容器と、前記三次元曲面部を含んで前記容器に熱収縮装着された請求項1乃至3のいずれか一項に記載の熱収縮性筒状ラベルと、を有し、
    前記装飾印刷層の設けられた領域が前記三次元曲面部に装着されている、ラベル付き容器。
    A container having a three-dimensional curved surface part, and the heat-shrinkable cylindrical label according to any one of claims 1 to 3, wherein the heat-shrinkable cylindrical label is attached to the container including the three-dimensional curved surface part,
    A labeled container in which a region provided with the decorative print layer is attached to the three-dimensional curved surface portion.
JP2014204727A 2014-10-03 2014-10-03 Heat-shrinkable cylindrical label and labeled container Active JP6513922B2 (en)